CA1193389A - Copolyester-carbonates containing aliphatic diol co- monomers - Google Patents

Copolyester-carbonates containing aliphatic diol co- monomers

Info

Publication number
CA1193389A
CA1193389A CA000412197A CA412197A CA1193389A CA 1193389 A CA1193389 A CA 1193389A CA 000412197 A CA000412197 A CA 000412197A CA 412197 A CA412197 A CA 412197A CA 1193389 A CA1193389 A CA 1193389A
Authority
CA
Canada
Prior art keywords
composition
alkylene radical
chloride
radical
carboxylic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CA000412197A
Other languages
French (fr)
Inventor
Niles R. Rosenquist
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Application granted granted Critical
Publication of CA1193389A publication Critical patent/CA1193389A/en
Expired legal-status Critical Current

Abstract

Abstract of the Disclosure Copolyester-carbonate resins, and articles molded therefrom, exhibiting improved processability comprising the reaction product of; (i) at least one dihydric phenol; (ii) a carbonyl halide carbonate precursor;
(iii) at least one difunctional carboxylic acid or a reactive derivative thereof; and (iv) at least one bishaloformate represented by the general formula

Description

~L'r3~3~

~ CL 3572 COPOLYESTER-CARBONATES CONT~INING
ALIP~TIC DI~L CO-MONOMERS

BACKGROUND OF THE INVEN~ION

Copolyester-carbonates are well known thermo-plastic materials which, due to their many excellent properties, find use in many commercial and industrial applications. These copolyester-carbonates exhibit, for example, excellent properties oE toughness, Elexibility, impact resistance, and high heat distortion temperatures.
The copolyester-carbonates, as described in U.S. Patent No. 3,169,121, are generally prepared by the reaction of a dihydric phenol, a carbonate precursor, and a di-functional carboxylic acid. ~lowever, due to theirrelatively high melt viscosities the copolyester-carbonates are generally difficult to process, even at high temperatures. It would thus be very advantageous if a copolyester-carbonate could be provided which retained al] of the other advantageous properties of copolyester-carbonates and was also easier to process, :i.e., exhibited lower melt viscosities.
It is, therefore, an object of th:is invention to provide copolyester-carbonate resins which exhibit improved processability and which simultaneously retain all of the other advantageous properties of copolyester-,. ~ _ j~ ~
.., ~3~
- 2 8C~,-3572 carbonates.
DESCRIPTION OF T~IE IN~TENTION
It has been discovered that copolyester-carbonates can be obtained which exhibit improved processability while simultaneously generally retaining all of their other advantageous properties such as toughness, impact strength, flexibility, hiyh heat distortion temperatures, and the like.
These copolyester-carbonate resins are comprised of the polymerized reaction products of (i) a dihydric phenol; (ii) at leas-t one difunctional carboxylic acld or a reactive derivative thereof;
(iii) a carbonyl halide carbonate precursor; and (iv) at least one par-ticular bishaloformate, in minor amounts, represented by the general formula O O
Il ~1 I. X-C-O-(R~-O-C-X

wherein.X rPpr~ n~ a halogen radical and R represents an alkylene radical. The resultant copolyester-carbonates exhibit lowered melt. viscosities, thereby rendering them easier to process, while simultarleously generally retaining the other advantageous properties of the copolyester-carbonate resins.
Briefly stated, the copolyester-carbonates of this invention comprise recurring carbonate groups o Il (-O-C-O-) and carboxylate groups F~

o (--C~o--) and aromatic carbocycllc groups in the linear polymer chain~ in which at least some of the carboxylate groups and at least some of the carbonate groups are bonded directly to ring carbon atoms of the aromatic carbocyclic groups.
In the bishaloEormates of ~ormula I the preferred halide radical is the chloride radical. The alkylene radicals represented by R are those alkylene radicals containing -from 2 to about 20 carbon atoms.
These alkylene radicals can be either straight chain alkylene radicals or branched alkylene radicals. If the alkylene radicals are branched chain alkylene radicals it is preferred that branching occur at the beta carbon 1~ atom. Preferred beta branched chain alkylene radicals are those wherein branching occurs at both beta carbon atoms when more than one beta carbon a-tom is present.
More preferred branched chain alkylene radicals are those where both beta carbon atoms, if more than one beta carbon atom is present, contain two branching groups.
Some illustrative non-limiting examples of straight chain alkylene radicals include ethylene, propylene, butylene, pentylene, octylene, amylene, and the like.
Some illustrative non-limlting examples o~
branched chain alkylene radicals include C H CH

--CH2 - CH -- C~I2 - CH - CH2 ~;

~3,38~

Cl 2H5 ~ 2H5 -CH2 - C - CH2 - C - CH2 ~ ;

-CH - C - CH

CH - C - CH2 - CH2 ~ C~I2 -CH2 ~ CEI CH2 ~ ;

Cl2H5 C14H9 -CH2 ~ CH - CEI2 - CH2 - C - CH2 ~ ;
~ .n 3 C3E~7 CH3 2 - CH ~ CH2 ~ CH ~ CH2 ~ ;

C~4Hg C12H5 CIH3 Ci3~7 -CH2 - C~ - CH2 - CH2 - CH2 - CH - CH2 - ~C - CH2 - ; and the ~ 5 - 8CL-3572 like.
The bishaloformates of Formula I are known compounds which are generally commercially available or which may be readily prepared by known methods.
One method of preparing these bishaloformates involves reacting a diol represented by the formula HO-(R)-OH

wherein R is as defined above, with a carbonyl halide represented by the formula 1 0 ~C~
X X
wherein X represents a halide radical, preferably the chloride radical. In thi.s reaction one mole of the diol is reacted with two moles of the carbonyl halide to produce the bishaloformate of Formu].a I.
The dihydric phenols that may be employed in the practice of this invention are any of the well known dihydric phenols. Illustrative of these dihydric phenols are those disclosed in United States Patent Numbers 3,028,365; 2,999,835; 3,030,331 and
3,169,121.
In general these dihydric phenols are represented by the general formula (Y)m ~ ~Rl~ - 1 m II. HO - - A E A OH
- t - - s - - u "~

~ CL-357~

in which A is an aromatic group such as phenylene, bi-phenylene, naphthylene, anthrylene, etc. E may be an alkylene or alkylidene groLlp such as me-thylene, ethylene, propylene, propylidene, isopropylidene, butylene, butyl-idene, isobutylidene, amylene, isoamylene, amylidene,isoamylidene, etc. Where E is an alkylene or alkylidene group it may also consist of two or more alkylene or alkylidene groups connected by a non- alkylene or non-alkylidene group such as an aromatic linkage, a tertiary amino linkage, an ether linkage, a carbonyl linkage, a silicon-containiny linkage, or by a sulfur containing linkage such as sulfide, sulfoxide, sulfone, etc. In addition, E may be a cycloaliphatic group (e.g. cyclopentyl, cyclohexyl); a sulfur~containing lin-kage such as sulfide, sulfoxide or sulfone; an etherlinkage; a carbonyl group; a tertiary nitrogen group;
or a silicon-containing linkage such as silane or siloxy. Rl is hydrogen or a monovalent hydrocarbon group such as alkyl (methyl, ethyl, propyl, etc.), cycloaliphatic (cyclopentyl, cyclohexyl, etc.), aryl (phenyl, naphthyl, etc.), or aralkyl (benzyl, ethyl-phenyl, etc.). Y may be an inorganic atom such as chlorine, bromine, fluorine, etc; an inorganic group such as the nitro group, etc.; an organic group such as R above, or an oxy group such as ORl, it being only necessary that Y be inert to and unaffected by the reactants and the reaction conditions. The letter m is any whole number from and including zero through the number of posi~ions on A available for ~ubstitution;
p is any whole number from and including zero through .~

the number of available positions on E; t is a whole number equal to at least one; s is either zero or one; and u may be any whole number including zero~
In the dihydric phenol compound represented by Formula II above, when more than one Y substituent is present, they may be the same or differen-t. The same is true for the Rl substituen-t. Where s is zero in Formula II and u is not zero, the aromatic rlngs are directly joined with no intervening alkylene or other bridge. The positions of the hydroxyl groups and Y on the aromatic nuclear residues A
can be varied in the ortho, meta, or para positions and the groupings can be in a vicinal, asymmetrical or symmetrical relationship, where two or more ring carbon atoms of the aromatic hydrocarbon residue are substi.tuted with Y and hydroxyl group.
Preferred dihydric phenols, for the purposes of the instant invention, are those represented by the general fo.rmula (~)m (~)m (R )p III. HO { ~ E - ~ OH

wherein Y, E, Rl, m and p are as defined above.
Some nonlimiting illustrative examples of the preferred dihydric phenols of Formula III include 2,2-bis-(4-hydroxyphenyl)-propane;
1,1-bis-(4-hydroxyphenyl)-ethane;
1,3-bis-(3-methyl-4-hydroxyphenyl~-propane;
2,2-bis-(3-isopropyl-4-hydroxyphenyl~-proparle;

2,2-bis-~4-hydroxyphenyl) pentane; and the like.
Mixtures of two or more of the dihydric phenols can also be employe~ and where dihydric phenol is mentioned herein, mixtures of such material are eon-sidered to be included.
In general, any difunctional carboxylic acidconventionally used in the preparation of linear polyesters may be used for the preparation o~ the copolyester-carbonates of the present invention.
Generally, the carboxylie acids whieh may be used include the aliphatic carboxylic acids, aliphatic-aromatic earboxylic acids, and aromatic carboxylic aeids. These acids are described in United States Patent Number 3,169,121, which issued February g, 1965 to Goldberg.
The acids which may be used generally con~orm to the formula IV. R3--~R2 ~coo~l wherein R2 ls an alkylene, al]cylidene or cyclo-aliphatic group in the same manner as set out above Eor E in Formula II; an al]cylene, alkylidene or cycloaliphatic group containing ethylenic unsat-uration; an aromatie radical such as phenylene, naphthylene, biphenylene, substituted phenylene, and the like; two or more aromatic groups connected through non-aromatic linkages such as those defined by E in Formula II; an aral]cyl radical such as tolylene, xylene, and the like. R3 is either a carboxyl or a hydroxyl group. The letter q is one where R3 is a hydroxyl group and either zero or one where R is 3~3~

a carboxyl group.
Preferred difunctional carboxylic acids are the aromatic dicarboxylic acids, i.e., those wherein q is 1, R3 is a carboxyl group, and R2 is an aromatic radical such as phenylene, naphthylene~ biphenylene, substituted phenylene, and the like. The preferred aromatic carboxylic acids are those represented by the general formula (Y)m HOOC
~'~
V~ ~ OOH

wherein ~ c~nd m are as defined above.
Mixtures of -these difunctional carboYylic acids can also be employed and where difunctional carboxylic acid is mentioned herein, mixtures of such materials are considered to be included.
Preferred aromatic dicarboxylic acids, for the purposes of the present invention, are isophthalic acid, terephthalic acid, and mixtures of isophthalic acid and terephtha]ic acid. Particularly useEul are mixtures of isophthalic acid and terephthalic acid. In these mixtures the weight ratio of terephthalic acid to isophthalic acid is generally in -the range of from about 10:1 to about 1:10.
Rather than using the difunctional carboxylic acids per se it is possible, and some-times even preferred, to utilize their reactive derivatives such as the acid halides. The acid chlorides are the preferred reactive derivatives of the difunctional carboxylic acids. Thus, 3~

- 10 - 8CLr357 for example, instead of using terephthalic acid, isophthalic acid, or mixtures of isophthalic acid and terephthalic acid; terephthaloyl chloride, isophthaloy]
chloride, or mixtures of isophthaloyl chloride and tere-phthaloyl chlo~ide may be employed.
The carbonyl halides utilized as the carbonateprecursors in the instant invention are carbonyl chloride, carbonyl bromide, or mixtures thereof.
Carbonyl chloride, also known as phosgene, is the preferred carbonyl halide.
The amount of -the bishaloformate of Formula I
employed is a processability improving amount. By processability improving amount is meant an amount effective to improve the processability of the copolyester-carbonate resin, i.e., reduce the melt viscosity of the resin, but insufficient to significantly adversely affect the other advantageous properties o~ the resin, particularly the heat distortion temp-erature. Generally, this amount ranges fxom about 1 to about 10 mole percent, based on the amount of dihydric phenol employed, and preferably from about 2 to about 8 mole percent. In general iE the amount of the bishaloformate employed is less than about one mole percent there is no significant decrease in the melt viscosity, i.e., there is no significant im-provement in the processability of the resin. If more than about 10 mole percent of the bishaloformate of Formula I is present the other properties of the resin, particularly the heat distortion temperature, begin to 3Q be significantly adversely af-fected.

~3~

~ 8CL-3572 The copolyester-carbona-tes of the instant invention, when a dicarboxylic acid or its reactive derivative is utilized, generally contain repeating units represented by the structures ~o O ( )m (Rl)p (Y)m .. ..
VI~ _--C~O--(R~--O--C-O -- A --~ E A O --~ t s u /0 (Y)m (Rl)p (Y)m VII. --C--O-- A E A O
t s ll / (Y)m ~(Rl) ~ (Y)m ,. .. ..
VIII.-- C-(R )q~C~O-- A E A O ~--~ ~ t s u wherein Y, R, Rl, R , A, E, t, s, u, m, p and q are as defined above. Structure VI will be present in minor amounts, depending upon the amount of the bishaloformate of Formula I utilized.
In the case where the preferred dihydric phenol of Formula III is emp]oyed~ and wherein the dicarboxylic acid is a mi~ture of terephthalic acid and isophthalic acid (or in the case of the reactive derivatives thereof, isophthaloyl chloride and terephthaloyl chloride) the copolyester-carbonate resin contains repeating units represented by the structures `~`

3~

(Y)m ( )m ( IX. -----C--O--(R)--O--C--O{O}E--~ O --~ (R ) p ~ \
X. ---- C --O ~--E ~ O

p XI. ----C ~ C-O--~O)--~ E --~ O --; and m (~ )m ~II. ~-- C --(0~ (I )p --O}

wherein Y, E, R1, R, p and m are as defined above.
Structure IX will be pxesent in minor amounts, depend-ing on the amount of the bishaloformate of Formula I
employed.
It has ~een found that a copolyester-carbonate resin which contains structu:res IX~II, i.e., one which is the reaction product of (i) at least one bishaloformate of Formula I; (ii) at least one di-hydric phencl of Formula III; (i.ii) terephthalic acid or a reactive derivative thereo-E such as terephthaloyl chloride; (iv) isophthalic acid or a reactive deriv-ative thereof such as isophthaloyl chloride; and (v) a carbonyl halide such as phosgene, exhibits particularly excellent all around properties such as impact strength, lS toughness, flexibility, high heat distortion temp--eratures, and ease of processability, and is particularly preferred.
One of the methods for preparing the copol.yester-carbonates of this invention, ~hen employing phosgene as the carbonyl halide carbonate precursor, involves first introducing the diacid chlorides and the bishalo-formate, dissolved in a suitable solvent, into a reacti.on mixture containing a dihydric phenol, an acid acceptor, and a catalyst. Upon completion of the i.ntroduction of the diacid halides and the bis-haloformate, preferably bischloroformate, phosgene is introduced into the reaction mixture in sufficient quantity to bring about reaction of substantially all of the remaining aromatic hydroxy groups. A particularly useful me-thod, and one ~hich results in copolyester-carbonates of yenerally excellent properties, lnvolves ,~
1. ~

3~

mixing -the compound or compounds of Formula I with the dicarboxylic acid or the reactive derivative thereof such as the diacid chloride and gradually adding this mixture to the reaction mixture before the introduction of phosgene has commenced.
A suitable acid acceptor may be either organic or inorganic in nature. A suitable organic acid acceptor is a tertiary amine and includes such materials as pyridine, triethylamine, dimethylaniline, tributyl-amine, and the like. The inorganic acid acceptor maybe one which can be either a hydroxide, a carbonate, a bicarbonate, a phosphate, or an alkali or alkaline earth metal hydroxide.
The catalysts present in the reaction mixture may be any of the suitable catalysts that aid the poly-merization reaction between the dihydric phenol, phosgene, and the dicarboxylic acid or its reactive derivative.
Suitable catalysts include, but are not limited to, tertiary amines, secondary amines, quaternary ammonium compounds, quaternary phosphonium compounds, amidines, and the like.
Also present in the reac-tion mixture i~ a mol-ecular weight regulator. These molecular weight regulators, or chain terminators, are generally well known and include such compounds as phenol, tertiarybutyl phenoll and the like.
The temperature at which the reaction proceeds may vary from below 0C. to above 100C. The reaction proceeds satisfactorily at temperatures from room temperature (25C.) to 50C. Since -the :reaction is exothermic, the rate o~ dicarboxylic acid or its reactive ~ ~ ~q`~ ~ 8CL-3572 derivative addition, or the rate of phosgene addition may be used to control the reaction temperature.
The copolyester-carbonate resins of the instant invention may optionally contain various known and commonly utilized additives such as antio~ida.nts;
antistatic agents; glass fibers, impact modifiers;
ultraviole-t radiation absorbers such as the benzophenones and the benzotriazoles; fillers; plast.icizers; mold release agents; hydrolytic stabilizers such as the epoxides disclosed in U.S. Patents 3r489,716, issued January 13, 1970 to Calkins; 4,138,379, issued February 6, 1979 to Scott et al and 3,839,247, issued October 1, 1974 to Bialous et al; color stabilizers such as the organophosphites disclosed in U.S. Patents 3,305,520, issued February 21, lg67 to Fritz et al and
4,118,370, issued October 3, 1978 to Sannes et al; and flame retardants.
Some particularly useful flame retardants are the alkali metal salts of sulfonic acids and the alkaline metal salts of sulfonic acids. These types of 1ame retardants are dlscl~sed in U~S. Patents 3,933,734, issued ~anuary 20, 1976; 3,948,851, issued April 6, 1976;
3,926,908, issued December 16, 1975; 3,919,167, issued November 11, 1975; 3,909,490, issued September 30, 1975;
3,953,396, issued April 27, 1976; 3,931,100, issued January 6, 1976; 3,97~,024, issued August 31, 1976;
3,953,39g, issued May 4, 1976; 3,917,559, issued November 4, 1975; 3,951,910, issued April 20, 1976 and 3,940 ! 366 ! issued February 24, 1976, all to Victor Mark.
~ KlPTION OF THE PR~ EMBODI~ENT
The following examples are set forth to further illustrate the present invention and are not to be construed as limi~ing ~he invention thereto. Unless otherwise specific, where parts or percents are men-tioned, they are parts or percents by we.ight.

~3~3~

- 16 - ~CL-3572 EXAMPL~ 1 This e~ample illustrates a copolyester carbonate resin not containing the bishaloformate o~ the instant invention and thus falling outside the scope of the present invention.
To a reactor fitted with a mechanical agitator are charged 8 liters of deionized water, 16 liters of methylene chloride, 1,910 grams (8.36 moles) of bisphenol A, 24 milliliters of triethylamine, 3.4 grams of sodium gluconate, and 65 grams (0.~3 mole) o~ p-tertiary butyl phenol molecular weight regulator.
This mixture is stirred and to the stirred mixture are added, over a 15 minute period, a mixture of 890 grams oE terephthaloyl chloride and 160 grams of isophthaloyl chloride as a 25 weight ~ solids solution in methylene chloride. During the acid chloride addition the pH is maintained in the range of 9.0 to 10.0 by the addition of 25~ aqueous sodium hydroxlde.
The resulting reaction mixture is then phosgenated by the addition of phosgene at the rate of 36 grams per minute for 15 minutes wlth the p~l controlled at 10.0 to 11 b~ the addition oE the aqueous sodium hydroxide.
After phosgenation is terminated 2 liters of methylene chloride are added, the brine layer is separated by centrifuge and the resin solution is washed with aqueous acid and with water. The resin is steam precipitated and dried in a nitrogen fluid bed at approximately 240F. To this resin product are added minor amounts (about 0.1 part by weight per hundred parts by weight of resin) of a phosphite !~

~33~
~ 17 - 8CL-3572 color stabillzer and an epoxy stabilizer. This stabili~ed resin product is -then fed to an extruder operating at a ~emperature of about 600F. to extrude the resin into strands and the ex-truded strands are chopped into pellets~ The pellets are then injection molded at a~out 650F. into test samples measuring about 2 1/2" x 1/2" x 1/8".
The following examples illustrate copolyester-carbonate resins of the ins-tant invention.

To a reactor fitted with a mechanical agitator are charged 8 liters of deionized water, 16 liters of methylene chloride, 1,910 grams (8.36 moles) of bis-phenol A, 24 milliliters of triethylamine, 3.4 grams of sodium gluconate and 65 grams (0.~3 mole) of p-tertiary butyl phenol. This reaction mixture is stirred and to the stirred mixture are added, over a 15 minute period, a ternary mix-ture of 890 grams of terephthaloyl chloride, 160 grams of isophthaloyl chloride, and 38.2 grams (2 mole %) of the bischloro-formate of 2,2-dimethyl propanediol as a 25 weight solids solution in methylene chloride. During the addition of this ternary mixture the pH is maintained in the range of 9.0 to 10.0 b~ the addition of 25%
aqueous sodium hydroxide. The resulting reaction mixture is then phosgenated by the addition of phosgene at the rate of 36 grams per minute for 15 minutes with the pH controlled at 10 to 11 by the addition of the aqueous sodium hydroxide. After phosgenation is terminated 2 liters of methylene chloride are added, the brine layer is separated by centrifuge and -the resin solution is washed with aqueous acid and with water. The resin is steam precipitated and dried in a nitrogen fluid bed at approximately 240F. To this resin product are added minor amounts (about 0.1 part by weight per hundred parts by weight of resin) of a phosphite color stahilizer and an epoxy hydrolytic stabilizer. This stabilized resin product is then fed to an extruder operating at a temperature of about 600F. to extrude the resin into strands and the extruded strands are chopped into pellets. The pellets are then injection molded at about 650F. into test samples measuring about 2 1/2" x 1/2" x 1/8".

The procedure of E'xample 2 is substantially repeated except that 76.4 grams (4 mole ~) of the bischloroformate of 2,2-dimethyl propane diol are uti]ized in the ternary mixture.
Various physical properties of the resin and the molded sampl~s obtained in Examples 1-3 were determined accordiny to the following test procedures:
~leat Distortion Temperature Under Load (DTUL) of the molded samples was determined accordiny to ASTM D-648, modified to use test samples described above;
Notched Izod (NI) impact on the molded samples was determined according to ASTM D-256;

~, ~33~3~
~ 19 - 8CL-3572 Melt Index (MI) of the resin was determined according to modified ASTM D-123~, condition 0;
the Intrinsic Vi.scosity (IV) of the resin was determined in methylene chloride at 25C.i the Glass Transition Temperature (Tg) was determined in degrees C.; and the Light Transmission of the molded samples, before and after autoclaving at 250~., was determined according to ASTM D-1003.
The results of these tests are set forth in Table I.
As i.llustrated by the data in Table I the Melt Index of the resins of the instant invention, Examples 2 and 3, i9 substantially higher than the Melt Index of the prior art resins, Example 1. This higher Melt Index indicates reduced viscosity of the resin and, therefore, improved processability of the copolyester-carbonate resin. This improvement in processability is achieved without any substantial deterioration of the other advan~ageous physical properties of the copolyester-carbonate resin.
As stated above, the preferred method of preparation of the present copolyester-carbonates involves the reaction of a carbonyl halide such as phosgene with the dihydric phenol of Formula II and a dicarboxylic acid or its reactive derivative and the bishaloformate of Formula I. The proportion of carboxylate and carbonate groups present in the final polymer can be suitably varied by varying the molar ratio of the dihydric phenol to dicarboxylic acid TABLE I

ExampleIntrinsic ViscosityMelt Index Notched Izod D~UL
No.(deciliters/gm~ Equilibration (ft.lb./in.) ~C. at 264 psi) timé at 300GC.
Z min. 12 min.

1 n . 533 0.731 0.779 6.56 163.3 2 0.51~ 0.795 0.837 6.51 163.0 CG
r~

3 0.526 0.393 0.992 6.46 156.~
co tl w ul TABL~ I (cont'd) Example Tg ~ Light Transmitted Initial After Auto-claving for 96 hrs. at 250F.
1 lg~.l 87.9 81.1 2 185.3 85.9 78.8 ~, 3 180.8 36.3 82.4 t~
~n N

3~

or its reactive derivative. :[t is preferred that this molar ratio of dihydric phenol to dicarboxylic acid or its reactive derivative be more than 1, preferably in the range of from about 1.00:0.05 to about 1.00:0.70O
The copolyester-carbonates of the instant invention generally have a weight average molecular welght in the range of rom about 5,000 to about 200,000, preferably in the range of from about 10,000 to about 100,000, and more preferably in the range of from about 25,000 to about 50,000.
The foregoing detailed description has been given for c~earness of understanding only and no unnecessary limitations are to be understood or implied therefrom. The invention is not limited to the exact details shown and described herein, for obvious modifications will occur to those skllled in the art.

Claims (28)

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:
1. A copolyester-carbonate resin composition exhibiting improved processability comprised of the polymerized reaction product of:
(i) at least one dihydric phenol;
(ii) a carbonyl halide carbonate precursor;
(iii) at least one difunctional carboxylic acid or a reactive derivative thereof; and (iv) a processability improving amount of at least one bishaloformate represented by the formula wherein X represents a halide radical and R represents an alkylene radical containing from 2 to about 20 carbon atoms.
2. The composition of claim 1 wherein said bishaloformate is present in an amount of from about one to about 10 mole percent, based on the amount of dihydric phenol present.
3. The composition of claim 2 wherein said alkylene radical is a straight chain alkylene radical.
4. The composition of claim 2 wherein said alkylene radical is a branched chain alkylene radical.
5. The composition of claim 4 wherein branching occurs at the beta carbon atom of said branched alkylene radical.
6. The composition of claim 2 wherein said difunctional carboxylic acid is an aromatic dicarboxylic acid.
7. The composition of claim 2 wherein said reactive derivative of said carboxylic acid is the diacid halide of an aromatic dicarboxylic acid.
8. The composition of claim 7 wherein said diacid halide is a diacid chloride.
9. The composition of claim 2 wherein said carbonyl halide is phosgene.
10. The composition of claim 8 wherein said carbonyl halide is phosgene.
11. The composition of claim 10 wherein said dihydric phenol is bisphenol A.
12. The composition of claim 11 wherein said diacid chloride is a mixture of terephthaloyl chloride and isophthaloyl chloride.
13. The composition of claim 12 wherein said alkylene radical is a beta branched alkylene radical.
14. The composition of claim 18 which further contains a phosphite color stabilizer.
15. The composition of claim 14 which further contains a epoxide hydrolytic stabilizer.
16. The composition of claim 15 which further contains a flame retardant.
17. The composition of claim 2 which further contains a flame retardant amount of at least one flame retardant compound.
18. The composition of claim 1 wherein said halide radical is the chloride radical.
19. The composition of claim 18 wherein said alkylene radical is a branched chain radical.
20. The composition of claim 19 wherein said branched chain alkylene radical is a beta branched alkylene radical.
21. The composition of claim 20 wherein said carbonyl halide is phosgene.
22. The composition of claim 21 wherein said dihydric phenol is bisphenol A.
23. The composition of Claim 22 wherein said difunctional carboxylic acid is selected from isophthalic acid, terephthalic acid, and mixtures thereof.
24. The composition of Claim 23 wherein said difunctional carboxylic acid is a mixture of isophthalic acid and terephthalic acid.
25. The composition of Claim 22 wherein said reactive derivative of said difunctional carboxylic acid is selected from isophthaloyl chloride, terephthaloyl chloride, and mixtures thereof.
26. The composition of Claim 25 wherein said reactive derivative of said difunctional carboxylic acid is a mixture of isophthaloyl chloride and terephthaloyl chloride.
27. The composition of Claim 26 wherein said composition contains a stabilizing amount of a phosphite color stabilizer and a epoxide hydrolytic stabilizer.
28. The composition of Claim 27 wherein said composition contains a flame retardant amount of a flame retardant compound.
CA000412197A 1981-10-16 1982-09-24 Copolyester-carbonates containing aliphatic diol co- monomers Expired CA1193389A (en)