CA1255106A

CA1255106A - Abrasive products

Info

Publication number: CA1255106A
Application number: CA000477988A
Authority: CA
Inventors: Richard P. Burnand
Original assignee: De Beers Industrial Diamond Division Pty Ltd
Current assignee: De Beers Industrial Diamond Division Pty Ltd
Priority date: 1984-03-30
Filing date: 1985-03-29
Publication date: 1989-06-06
Also published as: JPS6133865A; DE3511284A1; DE8509236U1; SE8501570L; FR2561969B1; CH666649A5; AT386558B; GB2158086A; GB8508295D0; SE462021B; DE3546783C2; DE3511284C2; JPH0732985B2; ATA92585A; BE902072A; GB2158086B; FR2561969A1; US4793828A; SE8501570D0

Abstract

A B S T R A C T

An abrasive tool having a working portion which includes an abrasive insert which is exposed to high temperatures during manufacture or use of the tool. Examples of such tools are dressing or turning tools and surface set or impregnated drill bits. The tools are characterised by the abrasive insert comprising a mass of diamond particles present in an amount of 80 to 90 percent by volume of the insert and a second phase present in an amount of 10 to 20 percent by volume of the insert, the mass of diamond particles containing substantial diamond-to-diamond bonding to form a coherent skeletal mass and a second phase consisting essentially of silicon, the silicon being in the form of silicon and/or silicon carbide. These abrasive inserts have been found to have substantial strength due, at least in part, to the diamond-to-diamond bonding and to be capable of withstanding temperatures of 1200°C under a vacuum 10 Torr or better or inert or reducing atmosphere without significant graphitisation of the diamond occurring.

Description

~ZS~i~06 -- 2 ~

BACKGROVND OF TH~ INV~NTION

This invention relates to abrasive products.

Abrasive compacts are well known in the art and are used extensively in industry for the abrading of various workpieces. They consist 5 essentially of a mass of abrasive particles present in an amount of at least 70 percent, preferably 80 to 90 percent, by volume of the compact bonded into a hard conglomerate. Compacts are polycrystalline masses and can replace single large crystals in many applications. The abrasive particles of compacts are invariably 10 ultra-hard abrasi~es such as diamond and cubic boron nitride.

Abrasive compacts generally contain a second phase or bonding ma-trix which contains a catalyst (also known as a solvent) useful in synthesising the particles. In the case of cubic boron nitride, examples of suitable catalysts are aluminium or an alloy of aluminium 15 with nickel, cobalt, iron, manganese or chromium. In the case of diamond, examples of suitable catalysts are metals of Group VIII of the Periodic Table such as cobalt, nickel or iron or an alloy containing such a metal.
t"~
~1 ~

i.~..

--` ` ` ' , . .
, ~ ~' ' ' . ' ': ' `.
~' .: .:

'~

~Z5~ 06 As is known in the art, diamond and cubic boron nitride compacts are manufactured under conditions of temperature and pressure at which the abrasive particle is crystallographically stable.

Abrasive compacts may be bonded directly to a tool or shank for use.
5 Alternatively, they may be bonded to a backing such as a cemented carbide backing prior to being mounted on a tool or shank. Such backed compacts are also known in the art as composite abrasive compacts.

United States Patent Specification No. 4,224,380 describes a method 10 of leaching out a substantial quantity of the catalyst from a diamond compact. The product so produced comprises self-bonded diamond particles comprising between about 70 percent and 95 percent by volume of the product, a metallic phase infiltrated substantially uniformly throughout the product, the phase comprising between about 15 0,05 percent and 3 percent by volume of the product, and a network of interconnected, empty pores dispersed throughout the product and defined by the particles and the metallic phase, the pores comprising between 5 percent and 30 percent by volume of the product. Leaching may be achieved by placing a diamond compact in a hot concentrated 20 nitric-hydrofluoric acid solution for a period of time. This treatment with the hot acid leaches out the catalyst phase leaving behind a skeletal diamond structure. The leached product is said to be thermally more stable than the unleached product.

United States Patent No. 4,124,401 describes and claims a 25 polycrystalline diamond body comprised of a mass of diamond crystals adherently bonded together by a silicon atom-containing bonding medium comprised of silicon carbide and a carbide and/or silicide of a metal component which forms a silicide with silicon, the diamond crystals ranging in size from 1 micron to about 1 000 microns, the .

;, .
.

.. ~
: . - .
.'` ~

~55 density of the cryst~ls ranging from at least about 70 percent by volume up to at least about 90 percent by volume of said body, said silicon atom-containing bonding medium being present in an amount ranging up to about 30 percent by volume of said body, said bonding 5 medium being distributed at least substantially uniformly throughout the body, the portio~ of the bonding medium in contact with the surfaces of the diamond crystals being at least in a major amount silicon carbide and the diamond body being at least substantially pore-free. The metal component for the diamond body is selected 10 from a wide group of metals consisting of cobalt, chromium, iron, hafnium, manganese, molybdenum, niobium, nickel, palladium, platinum, rhenium, rhodiwn, ruthenium, tantalum, thorium, titanium, urani~n, vanadiunl, tungsten, yttrium, zirconium and alloys thereof. The polycrystall~ne diamond ~ody is made under relatively mild hot 1~ pressing conditions and such that diamond intergro~th will not occur.

United States Patent No. 4,151,686 describes a polycrystalline diamond body similar to that of United States Patent No. 4,124,401 save that the bonding medium is comprised of silicon carbide and elemental silicon ~nd the density of diamond crystals in the body 20 ranges from 80 percent by volume to about 95 percent by volume of the body. ~lo-reover, the polycrystalline abrasive bodies of this ~nited States patent are made under higher applied pressure conditions, i.e.
applied pressures of at least about 25 kilobars. The abrasive bodies are said to be useful on an abrasive cutting tool, noz~le or other 25 wear-resistant part.

United States Patent No. 3,234,321 describes diamond compacts having a second phase of titanium, vanadium, zirconium, chromium or silicon or an alloy of any of these metals with nickel, manganese or iron.
The compacts are made by mixing the diamond particles with the metal, 30 in powdered form, and subjecting the mixture to elevated conditions of temperature and pressure. One e~ample uses silicon as the metal I :!

.`'"' ~"' ~' ''~
:' ' '' ''.'"'' ": : .
' ' ' . . . ' ' ' ~2~

in an amount of 31,5 volume percent. The patent suggests that the compact may be suitably shaped and mounted for cutting and abrading hard materials.

The complete specification of South African Patent No. 84/0053 5 describes an abrasive body which has high strength and an ability to withstand high temperatures making it suitable as a tool insert for dressing tools and surface set drill bits. The body comprises a mass of diamond particles present in an amount of 80 to 90 percent by volume of the body and a second phase present in an amount of 10 to 10 20 percent by volume of the body, the mass of diamond particles containing substantial diamond-to-diamond bonding to form a coherent skeletal mass and the second phase containing nickel and silicon, the nickel being in the form of nickel and/or nickel silicide and the silicon being in the form of silicon, silicon carbide and/or nickel 15 silicide. The abrasive bodies are made under conditions of elevated temperature and pressure suitable for diamond compact manufacture.

SUMMARY OF THE INVENTION

According to the present invention there is provided an abrasive tool having a working port,on which includes an abrasive insert held 20 therein, that insert being exposed to a high temperature during manufacture or use of the tool and comprising a mass of diamond particles present in an amount of 80 to 90 percent by volume of the insert and a second phase present in an amoun~ of 10 to 20 percent by volume of the insert, l;he mass of diamond particles containing 25 substantial diamond-to-diamond bonding to form a coherent, skeletal mass and the second phase consisting essentially of silicon, the silicon being in the form of silicon and/or silicon carbide.
Typically, the abrasive tool will be such that the abrasive insert is exposed to a temperature above 8500C during manufacture or use of the 30 tool.

~ ", ~ ."

:
, . .:

.. ':. ~ ., ` `

~2~i106 DESCRIPTION OF THE DRAI~INGS

Figure 1 is a fragmentary side view of a dressing tool of the invention;
Figure 2 is a perspective view of a surface set drill bit of the 5 invention;
Figure 3 is a perspective view of a portion of the cutting face of the bit of Figure 2;
Figure 4 is a perspective view of another embodiment of a surface set drill bit of the invention; and 10 Figure 5 illustrates graphically the results obtained in a comparative test.

DETAILED DESCRIPTION OF THE INVENTION

An essential feature of the abrasi~e tool of the invention is that the working portion includes at least one abrasive insert having the 15 characteristics specified above. Such inserts have been found not only to have substantial strength due, at least in part, to the substantial diamond-to-diamond bonding but also to be capable of withstanding a temperature of 1200C under a vacuum of 10-4 Torr or better or an inert or a reducing atmosphere without significant 20 graphitisation of the diamond occurring. The strength of the inserts and their ability to withstand high temperatures makes them ideal as cutting elements or tool inserts for tools where high temperatures are generated during use thereof, as for example in dressing or turning tools, or where high temperatures are required during 25 manufacture of the tool, as for example in surface set or impregnated drill bits.

The silicon second phase in the abrasive insert is uniformly distributed through the coherent~ skeletal diamond mass. The second phase, as stated above, consists essentially of silicon, the silicon ~Z5~ 6 being in the form of silicon and/or silicon carbide. This means that any other components will be present in the second phase in trace amounts only.

The abrasive inserts used in the invention may take on a variety of S shapes depending on the use to which they are put. Examples of suitable shapes are disc, triangular, cube, rectangular and he~agonal. These shapes will generally be cut, for example using laser cutting, from a large'abrasive body produced in a manner described fully below. The inserts may also be of irregular shape 10 which may be produced by crushing the large abrasive body.

The abrasive inserts may be provided with a thin metal or alloy coat prior to insertion into the working portion of the tool. The metal - coat, for e~ample, may be a chromium or titanium coat which has been found to be particularly suitable for impregnated drill bits.

15 The inserts used in the abrasive tools of the inven-tion are manufactured using temperatures and pressures in the diamond stable region of the carbon phase diagram. In particular, ~he inserts are produced from abrasire bodies produced by placing a mass of diamond particles in a reaction vessel, placing a mass of silicon in contact 20 with the mass of diamond particles, placing the loaded reaction vessel in the reaction zone of a high temperature/high pressure apparatus, subjecting the contents of the reaction vessel to conditions of elevated temperature and pressure in the diamond stable region of the carbon phase diagram for a time sufficient to praduce 25 the body and recovering the body from the reaction zone. The preferred conditions of elevated temperature and pressure are temperatures in the range 1400 to 1600C and pressures in the range 50 to 70 kilobars. These elevated conditions of temperature and pressure will be maintained for a time sufficient to produce the 30 body. Typically, these elevated conditions of temperature and .~;

pressure are maintained for a period of 5 to 20 minutes. The silicon may be provided in the form of a powder or in the form of a sheet or foil. It should be added that in order to achieve suitable diamond-to-diamond bonding it has been found preferable to infiltrate the 5 silicon into the diamond mass during manufacture of the body. The diamond-to-diamond bonding is primarily physical diamond-to-diamond interlocking and bonding created by plastic deformation of the diamond particles during manufacture of the element.

The reaction vessel ln which the diamonds and silicon are placed may 10 be made of molybdenum, tantalum, titanium or like high melting, carbide-forming metal. It is believed that confining the mass of diamond and silicon within such reaction vessel during manufacture contributes to the excellent diamond-to-diamond bonding which is achieved.

15 The diamond particles used in the manufacture of the abrasive inserts may vary from coarse to fine particles. Generally the particles wi]l be less than 100 microns in size and typically have a si~e in the range 10 to 75 microns. Preferred si~e is in the range 15 to 30 microns.

20 High temperature/high pressure apparatus is well known in the art -see, for example, U.S. Patent No. 2,941,248.

The abrasive tool may be a dressing or turning tool which comprises a tool shank and an abrasive insert as defined above mounted in one end thereof to present a dressing or turning edge. Figure 1 illustrates 25 an example of a dressing tool. Referring to this Figure, there is shown a dressing tool comprising a shank 10 having a cutting element 12 mounted in one end thereof. The cutting element presents a dressing edge 14. High temperatures are generated at the dressing ' ,,;

.. : . ' '~" '.`: , , ; ~
::' :
.
-: : .

~2~5 edge 14 during use of the tool. However, it has been found that the excellent thermal stability of the cutting element 12 enables the element to withstand these high temperatures.

The abrasive tool may also be a drill bit which comprises a rotatable 5 body having at one end thereof a cutting face, the cutting face including a plurality of abrasive inserts held in a bonding matrix and presenting cutting edges or points for the face. Examples of such drill bits are surface set drill bits and impregnated drill bits.

10 For drill bits, it is preferred that the abrasive inserts are either triangular in section or of block form. When the abrasive inserts are triangular in section. the bases thereof will be embedded in the bonding matrix and the apices thereof and side edges leading therefrom will provide cutting edges. When the abrasive inserts are 15 in block form, which is preferably a cube, the major portion thereof will be embedded in the bonding matrix and the cutting edges will be provided by projecting portions of pyramidal shape.

Figures 2 and 3 illustrate an embodiment of a surface set drill bit (also knowm as a coring bit) of the invention. Referring to -these 20 Figures, there is sholm a surface set drill bit comprising a rotatable core 16 having one end 18 threaded for engagement in a coring drill and a cutting face 20 at the other end thereof. The cutting face 20 comprises a plurality of cutting elemen-ts 22 firmly held in a suitable metal matrix. The cutting elements 22 are each 25 triangular in section, as illustrated in greater detail in Figure 3.
The triangular cutting elements 22 are so mounted in the cutting face 20 that the base of the triangle 24 is embedded in the bonding matrix of the face and the apex 26 stands proud of the general plane of the cutting face. It is this apex and side edges 27 which provide the . ~- .
:, .. :
: . :~

55~(~6 cutting edges. Located immediately behind the triangular abrasive body 22 is a support 30 made of the same metal as that of the cutting face. The direction of rotation of the bit is shown by the arrow.

Figure 4 illustrates another embodiment of a surface set drill bit of 5 the invention. Referring to this Figure, there is shown a surface set drill bit comprising a rotatable core 32 having at one end thereof a cutting face 34. The cutting face 34 comprises a plurality of cutting elements 36 firmly held in a suitable metal matrix. Each cutting element is of cube form, the major portion 38 of which is 10 embedded in the metal matrix. The minor portion 40 of the cube which projects beyond the metal matrix and is of essential pyramidal shape presents a cutting point 42 and cutting edges 44. The direction of rotation of the bit is illustrated by the arrow. As will be demonstrated hereinafter, the cubes, when orientated for corner t5 exposure as illustrated, are more rigidly held within the matrix and, although offering potentially less exposure initially, can withstand more readily the higher point loadings necessary for hard rock fracture than the equivalent pattern setting for triangular elelnents.

In surface set drill bits, the cutting elements are se-t into the 20 cutting face using standard high temperature infiltration techniques.
The excellent thermal stability of the cutting elements of the invention enables them to withstand such temperatures, which generally exceed 8500C, without significant degradation thereof.

The invention is further illustrated by the following example.

25 EXA~IPLE

A mass of diamond particles (12,5 g) was placed in a tantalum cup.
A layer of silicon powder (1,36 g) was placed on top of the mass of diamonds and a tantalum ]id placed on the open-end of the cup.

O

~L2~

The loaded cup was placed in the reaction ~one of a conventional high temperature/high pressure apparatus and subjected to 1500C
temperature and 55 kilobars pressure and these conditions were maintained for a period of 10 minutes. Recovered from the reaction 5 7one was a disc-shaped abrasive body which comprised a mass of diamond particles in which there was a substantial amount of diamond-to-diamond bonding forming a coherent, skeletal diamond mass and a second phase containing silicon carbide and a small amount of silicon, uniformly distributed through the diamond mass.

10 The disc-shaped abrasive body was suitably cut by standard laser cutting techniques into a plurality of cubes and triangles. The cubes were mounted in a surface set drill bit of the type illustrated by Figure 4 and the triangular elements ~ere similarly mounted in a surface set drill bit of the same type. Triangular shaped drill 15 inserts produced following the teachings of Uni~ed States Patent Specification No. 4,224,380 were also mounted in a surface set drill bit of the type illustrated by Figure 4. These three drill bits were then used to drill holes in Norite granite and the rate of penetration of each drill bit in relation to the depth drilled was 20 measured at a constantly applied load of lOOOkg. The results illustrated graphically in Figure 5 show the rate of penetration versus depth drilled in Norite granite. It will be noted that the drill bit containing the cube cutting elements produced a far superior overall drilling rate at the same applied load when compared 25 with the drill bits containing the triangular cutting elements.
Furthermore, the overall drilling rate for the drill bit containing silicon-containing triangular cutting elements of the present invention had a superior overall drilling rate when compared with the drill bit incorporating triangles produced following the teachings of 30 United States Patent Specification No. 4,224,380. Norite granite is a very hard material having a uniaxial compressive strength of 277 MPa.

Claims

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:-1.

An abrasive tool having a working portion which includes an abrasive insert held therein, that insert being exposed to a high temperature during manufacture or use of the tool and comprising a mass of diamond particles present in an amount of 80 to 90 percent by volume of the insert and a second phase present in an amount of 10 to 20 percent by volume of the insert, the mass of diamond particles containing substantial diamond-to-diamond bonding to form a coherent skeletal mass and the second phase consisting essentially of silicon, the silicon being in the form of silicon and/or silicon carbide.

2.
An abrasive tool according to claim 1 wherein the insert is exposed to a temperature above 850°C during manufacture or use of the tool.

3.
An abrasive tool according to claim 1 which is a dressing tool comprising a shank and an abrasive insert mounted in one end thereof to present a dressing or turning edge for the tool.

4.
An abrasive tool according to claim 1 which is a turning tool comprising a shank and an abrasive insert mounted in one end thereof to present a dressing or turning edge for the tool.

5.
An abrasive tool according to claim 1 wherein the abrasive insert has a disc, triangular, cube, rectangular, hexagonal or irregular shape.

6.
An abrasive tool of claim 1 which is a drill bit comprising a rotatable body having at one end thereof a cutting face, the cutting face including a plurality of abrasive inserts held in a bonding matrix and presenting cutting edges or points for the face.

7.
An abrasive tool according to claim 6 which is a surface set drill bit.

8.
An abrasive tool according to claim 6 which is an impregnated drill bit.

9.
An abrasive tool according to claim 6 wherein the abrasive inserts are triangular in section, the bases of the triangles being embedded in the bonding matrix and the apices and side edges leading therefrom of the triangles presenting cutting edges.

10 .
An abrasive tool according to claim 6 wherein the abrasive inserts are of block form, the major portion of each being embedded in the bonding matrix and the cutting edge for each being provided by a projecting portion of pyramidal shape.

11 .
An abrasive tool according to claim 10 wherein the abrasive inserts are cubes.