CA1280586C

CA1280586C - Method of reducing fluid loss in cement compositions which may contain substantial salt concentrations

Info

Publication number: CA1280586C
Application number: CA000532545A
Authority: CA
Inventors: Jerry Dale Childs; Slaton Eugene Fry; Lance Everett Brothers; Donald Wayne Lindsey
Original assignee: Halliburton Co
Current assignee: Halliburton Co
Priority date: 1986-05-13
Filing date: 1987-03-19
Publication date: 1991-02-26
Anticipated expiration: 2008-02-26
Also published as: US4676317A; EP0245930B1; DE3769199D1; ES2021357B3; EP0245930A2; NO871361D0; NO173820B; NO871361L; EP0245930A3; NO173820C

Abstract

METHOD OF REDUCING FLUID LOSS
IN CEMENT COMPOSITIONS WHICH MAY
CONTAIN SUBSTANTIAL SALT CONCENTRATIONS
Abstract of the Disclosure Cementing compositions having improved fluid loss capabilities for use in oil, gas, water and other well cementing operations are disclosed. Such compositions are comprised of water, hydraulic cement and a fluid-loss addi-tive comprising a graft polymer comprised of a backbone of lignin, lignite, derivatized cellulose and various synthetic polymers selected from the group consisting of polyvinyl alcohol, polyethylene oxide, polypropylene oxide and polyethyleneimine. The grafted pendant groups comprise at least one member selected from the group of homopolymers, copolymers and terpolymers of 2-acrylamido-2-methylpropane-sulfonic acid, acrylonitrile, N,N-dimethylacrylamide, acry-lic acid, N,N-dialkylaminoethylmethacrylate and their salts.
The backbone comprises from about 5 to about 95 percent by weight of the graft polymer, and the pendant groups can comprise from about 5 to about 95 percent by weight of the graft polymer.

Description

l~so~a6 85.194 METHOD OF REDUCING FLUID LOSS
IN CEMENT COMPOSITIONS WHICH MAY
CONTAIN SUBSTANTIAL SALT CONCENTRATIONS
Field of the Invention The present invention relates to an aqueous cementing composition and method of using same in cementing oil and gas wells and the like. More particularly, the pre-sent invention concerns incorporation of a grafted polymer prepared by the polymerization of monomers or salts of mono-mers of N,N-dimethylacrylamide, 2-acrylamido-2-methylpropane-~ul~onic acid and acrylonitrlle having a lignin or lignite or other backbone in a hydraulic cement which may contain ~ ~~
substantial salt concentrations for the purpose of reducing fluld 1088 during cementing operations.
Certain polymer compoAitions have long been recognized by those skllled in the art of cementing wells in the p-troleum industry as comentlng additives useful ln reducing fluid loss from a slurry of cement and water to the surrounding environment, such as, the formation. These com-positions are commonly referred to as "fluid loss additives."
Discussions of the use of fluid-lo~s additives in well cementing compositions and their importance may be ~ o found in the following articles :
:
A. Carter, Greg and Slagle, Knox, "A Study of Completion Practices to Minimize Gas Communica-tion", Society of Petroleum Engineers Paper No.
,~ ~,., ' ' .
.

, .
' o~

3164, November 1970:
B. Christian, W. w., Chatterji, Jiten, and O~troot, Warren, "Gas Leakage in Primary Cementing - A Field Study and Laboratory Investigation", Society of Petroleum Engineers Paper No. 5517, October, 1975;
C. Cook, C. and Cunningham, W., "Filtrate Control: A
Key in Successful Cementing Practices", Journal of Petroleum Technoloqy, August 1977, page 951;

D. Smith, Dwight, Cementinq: SPE MonograPh Volume 4, published by Millet the Printer, Inc., Dallas, Texas, 1976.
An example of a fluid loss additive for use in an acidizing or fracturing composition is found in U.S. Patent No. 4,107,057. In the '057 patent a copolymer of a sulfonic-acid modified acrylamide and a polyvinyl cross-linking agent is employed.
In the oil well cementing art, a variety of poly-mers have been disclosed as useful fluid loss additives for hydraulic oil well cements. For example, U.S. Patent No.
4,015,991 discloses such a fluid loss additive for a hydraulic cement slurry consisting of hydrolyzed copolymers of acrylamide ~AM) and 2-acrylamido-2-methylpropanesulfonic acid (AMPS~). However, these AM/AMPS~ copolymers are useful only in operations where the bottom hole circulating temper-ature (BHCT) ranges from 90 to 125F, whereas BHCT rangesencountered in such operations are often outside such a 80~,~6 range. Still further, these copolymers have a salt tolerance of only up to about 10% by weight of water.
The temperature limitations of the AM/AMPS~ copoly-mers, that is, loss of usefulness above about 125F. ~HCT, are believed to be the result of hydrolysis of the amide groups. The carboxylate groups formed by such hydrolysis convert the copolymers to materials which function to retard the setting of the cement and to reduce the compressive strength of the set cement. Further, in the lower portion of the above-mentioned temperature range (between 90 and 100F.1 the AM/AMPS~ is less effective as a fluid loss addi-tive, requiring inclusion of larger amounts of such additive than at higher temperatures. The inclusion of sufficiently large amount of additive to create an acceptable fluid loss composition often creates viscosity and pumpability problems, since the addition of such copolymer directly affects the resultant slurry rheology. Copolymers of acry-lamide and AMPS~ exhibit high viscosity and poor mixability, resulting in cement slurries having poor pumpability charac-teristics during cementing operations. Mixability is a sub-jective term used to describe how well the components in the cement composition wet and mix with each other, as well as the energy required to create a generally homogeneous slurry.
Industry desires a fluid loss additive that has as little effect on compressive strength, set time, viscosity ~'~8~36 and thickening time as possible; is salt tolerable, that is, does not exhibit substantial loss of effectiveness in the presence of salt; and is chemically stable during cementing operations. Further, such desired fluid loss additive should be compatible with as many other additives and environmental conditions as possible, should be soluble in cement slurries at normal ambient temperatures encountered in oil well cementing operations, as well as continue to provide fluid-loss characteristics over a broad temperature range and at the high pH of the cementing compositions.
U.S. Patent No. 4,515,635 discloses the use of copolymers of N,N-dimethylacrylamide (NNDMA) and AMPS~
having monomer ratios of NNDMA to AMPS~ of 1:4 to 4:1 and selected molecular weights as fluid loss additives for cement compositions. As illustrated in the patent, however, the copolymer fails to provide desired levels of fluid loss control even at relatively high concentrations to cements containing substantial salt concentrations.
It would be desirable to provide additives for use in reducing fluid loss in cement compositions, and particu-larly, those containing substantial salt concentrations where the bottom hole circulating temperatures may range from about 100F to in excess of about 400F without adver-sely affecting thickening time, compressive strength or other properties of the cement composition.

1'~8()~6 Summary of the Invention Cementing compositions having improved fluid loss capabilities for use in elevated temperature environments in oil, gas and wa~er well cementing operations are disclosed.
More particularly, such compositions are comprised of water, hydraulic cement and a fluid-loss additive comprising a graft polymer comprised of a backbone of lignin or lignite having pendant groups, preferably comprising at least one member selected from the group of homopolymers, copolymers and terpolymers of 2-acrylamido-2-methylpropanesulfonic acid, acrylonitrile and N,N-dimethylacrylamide and their salts. The backbone also can comprise a derivatized cellu-lose or various synthetic polymers selected from the group consisting of polyvinyl alcohol, polyethylene oxide, poly-propylene oxide and polyethyleneimine. The pendant groups also can include acrylic acid, N,N-dialkylaminoethylmeth-acrylate and their salts. The alkyl groups in the N,N-dialkylaminoethylmethacrylate being selected from methyl, ethyl and propyl radicals.
The backbone compound comprises from about 5 to about 95 percent by weight of the graft polymer, and the pendant groups comprise from about 5 to about 9S percent by weight of the graft polymer.
In a preferred composition of the fluid-loss addi-tive, the backbone comprises from about 20 to about 40 per-cent by weight of the graft polymer and the pendant groups ~;~8~5~36 comprise 2-acrylamido-2-methylpropanesulfonic acid, acrylo-nitrile and N,N-dimethylacrylamide in a mole ratio of from about 1:0:0 to about 3:3:1.
The polymers and salts of the polymers comprising the fluid-loss additive used in the present invention are relatively stable to hydrolysis over a wide range of tem-perature and pH. Such polymers and salts of the copolymers may be admixed in solid form with any dry hydraulic oil field cement or may be added at the time the cement slurry is being prepared, either to the mixing water or to the slurry. ~dditionally, methods of cementing a conduit in a borehole penetrating an earthen formation by introducing such a cementing composition into the space between such conduit and formation are disclosed.
So that the above-recited features, advantages and objects of the invention, as well as others which will become apparent, are attained and can be understood in detail, more particular description of the invention is set forth below with respect to typical embodiments thereof, but the described embodiments should not be considered limiting of its scope, for the invention may admit to other equally effective embodiments which will be apparent from the description to one of ordinary skill in the art.

Description of the Preferred Embodiments New cementing compositions and methods of using i~a~)5~36 same in oil, gas and water well cementing operations are disclosed. Such compositions are comprised of water, hydraulic cement, a graft polymer having a backbone comprising a lignin or lignite and pendant groups comprising homopolymers, copolymers or terpolymers of at least one member selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid (hereinafter referred to as "AMPS~n ~ a registered trademark of The Lubrizol Corporation);
acrylonitrile (hereinafter referred to as "ACN");
N,N-dimethylacrylamide (hereinafter referred to as "NNDMA");
acrylic acid (hereinafter referred to as "AA"); N,N-dimethyl-aminoethylmethacrylate (hereinafter referred to as "DMAEMA") and their salts. The backbone also can comprise derivatized cellulose, polyvinyl alcohol, polyethylene oxide, polypropy-lene oxide and polyethyleneimine.
The backbone of the graft polymer comprises from about 5 to about 95 percent by weight of the fluid-loss additive on a dry basis. Preferably, the backbone comprises from about 10 to about 50 and, most preferably, from about 20 to about 40 percent by weight of the fluid-loss additive on a dry basis. The pendant groups can comprise from about 5 to about 95 percent by weight of the fluid-loss additive on a dry basis. Preferably, the pendant groups comprise from about 50 to about 90 and, most preferably, from about 60 to about 80 percent by weight of the fluid-loss additive on a dry basis.

~305t~6 In a p~eferred composition of the fluid-loss addi-tive, the pendant groups are selected from the group of ~PS~, ACN and NNDMA polymers with the mole ratio of the AMPS~:ACN polymers being in the range of from about 1:0 to about 1:1, and the AMPS~:NNDMA being in the range of from about l:0 to about 6:1. When salt is present in the aqueous fluid with which the cement is prepared or is present in the region to be contacted by the cement, the AMPSX:ACN:NNDMA
mole ratio preferably is in the range of from about 1:0:0 to about 3:3:1 and, most preferably, is in the range of from about 3:2:1 to about 3:3:1. Numerous salts of the graft polymers can be made. The preferred salts being made by neutralization of the acid form of the AMPS~ monomer or the copolymers with an alkaline agent such as a source of sodium, calcium, magnesium, ammonium ions or the like. Such alkaline agents can comprise, for example, sodium hydroxide, calcium hydroxide, ammonium hydroxide, magnesium hydroxide and the like.
The amount of each pendant group polymer present in the fluid loss additive will depend upon the amount of salt present, the temperature level to be experienced, rheologi-cal considerations, the average molecular weight of the polymers and other additives present.
The individual pendant groups comprising consti-tuents of the fluid loss additives of the present invention generally are effective at reducing fluid loss in non-salt ~'~805~3~
g containing cementing compositions. The behavior of the various constituents of the additives, however, in salt-containing cementing compositions are very much different.
The pendant groups comprising constituents of the fluid-loss additives of the present invention are generally ineffective individually at reducing fluid loss even at high concentrations from salt-containing cementing compositions.
However, they demonstrate a surprising ability in com-bination to substantially reduce fluid loss from the salt-containing cement compositions. Such reduction in fluid loss from the cement compositions is substantially in excess of any additive effect which the various compounds comprising the fluid loss additive may experience even when utilized at substantially greater individual concentration levels when admixed with cement and as such is totally unex-pected.
The fluid-loss additives of the present invention containing pendant groups consisting of AMPS~, ACN and NNDMA
are effective in reducing fluid loss from cementing com-positions containing in excess of about 10% salt by weightof water. The fluid loss additives are particularly effec-tive at reducing fluid loss at elevated temperatures, that is, generally above 125F from cementing compositions con-taining in excess of 18% salt by weight of water up to the saturated salt concentration level.
The fluid-loss additive is admixed with the cement ;' ~ .

1'~8()~;~fi in an amount of from about 0.25 to about 5 percent by weight of the cement. Preferably, the fluid-loss additive is admixed with the cement in an amount of from about 0.5 to about 1.5 percent. When the aqueous fluid utilized to pre-pare the cement comprises substantially fresh water, theconcentration preferably is in the range of from about 0.5 to about 1 percent by weight of cement. When salt is pre-sent, the fluid-loss additive preferably is present in an amount of from about 1.0 to about 1.5 percent by weight of cement. While it is to be understood that larger quantities of the fluid-loss additive can be utilized, such use is eco-nomically undesirable.
The cementing compositions of the present invention are useful in oil, gas and water well cementing operations since such compositions have reduced fluid loss to the surrounding formation. Such compositions are used to cement a conduit penetrating a permeable earthen formation via introducing such composition into the space between such conduit and such formation and allowing the composition to harden.

The graft polymers and graft polymer salts used in the present invention may be manufactured in accordance with various well know free-radical techniques. Such methods are described in, for example, the text entitled Block and 25 Graft Polymers by William J. Burland and Allan S. Hoffman, copyright 1960 or Graft CoPolymers by H.A.J. Battaerd and ,., ~7~80586 G. W. Treager, copyright 1967. The initiators employed in the chain transfer rea~tions to produce the graft polymers of ~he present invention can comprise substantially any of the redox couples known to react with carbons bearing heteroatoms or with heteroatoms of nitrogen, oxygen or sulfur present in, for example, the lignite which can comprise the backbone. While various ceric salts and other compounds are useful to effect the free radical initiation required to produce the compounds of the present invention, a potassium persulfate-potassium bisulfite redox system has been employed in the preparation of the various lignite graft polymers. The initiator for the polymeric back-bones comprised a ferrous salt with hydrogen peroxide.
The particular solvent employed in the polymerization reactions was water. However, as is well known by those skilled in the art, any other solvent which will solubilize the reactants to a reasonable extent also may be utilized. While not required to effect graft formation, removal of any free oxygen in the solvent is desirable to improve product yields. Free oxygen can be removed, for example, by bubbling nitrogen gas through the solution of reactants for a period of about one hour or more by which time the nitrogen will effectively displace any dissolved oxygen gas in the solution. The reaction can be effected over a wide temperature range with increased temperature generally accelerating the rate of the reaction. The tem-:

perature of the reaction can be in the range, for example, of from about 40C to the temperature at which solvent reflux is achieved. Satisfactory reactions with lignite backbones were found to occur at a temperature of about 60C.
The lignite which may comprise brown coal, oxidized lignite such as leonardite or any other low rank coal resulting from the alteration of vegetal material is pre-pared for reaction with the various polymers by treatment with caustic or the like. The treatment is effected by con-tacting the lignite with caustic alkali or aqueous ammonia solutions which dissolves or disperses a portion of the lignite into the solution. The solution then may be separated from the remaining solids by filtration or the like. The solution can be concentrated to increase the lignite content or utilized directly in the graft polymeri-zation reaction.
While the exact nature of of the graft polymeriza-tion of the lignite and lignin is unknown, it is believed that the various monomers react at the heteroatom and hydroxyl sites present on the backbone compound to form graft polymers containing various members of the monomers in a random nature. Surprisingly, it has been found that the best results are obtained when the AMPS~, ACN and NNDMA
25 monomers are all admixed with the backbone compound prior to initiation of the polymerization reaction when it is desired )5l36 to produce a fluid-loss additive that exhibits significant salt tolerance in the cement composition.
The salts of the various graft polymers may be pro-duced in accordance with the various well known techniques.
The salt may be formed, for example, by reaction of an alka-line agent with either the AMPS~ monomer or other polymer before polymerization or after. The salt may be formed with any alkaline agent which does not adversely react with the monomers of the polymer or the other constituents present in the cementing composition.
The term "lignite" as used herein in reference to the graft polymer means the aqueous soluble or dispersible product~ resulting from the treatment of a source of lignite material with caustic or aqueous ammonium solutions.
The term "lignin" as used herein in reference to the graft polymer means the aqueous soluble or dispersible products or derivatives resulting from the treatment of a source of lignin material with caustic, sulfites or sulfa-tes, or by alkaline oxidation, such as lignosulfonate and the like produced by the well known processes for production of paper pulp.
The term "cement" as used herein is intended to include those compounds of a cementitious nature which are described as hydraulic cements. Such compounds include, for 25 example, Portland Cement in general and particularly Portland Cements of API Classes G and H, although other API

~'~ao586 classes can be utilized, pozzolan cements, gypsum cements, high alumina content cements, high gel (high clay content) cements, silicate containing cements and high alkalinity cements can be used in various applications of the present invention. ~ortland cements and particularly cements of API
Classes & and H are preferred.
The aqueous fluid utilized in the cement composi-tion can be water from any source provided that it does not contain an excess of any compounds that affect the stability of the cement composition of the present invention. The aqueous fluid can contain various salts such as sodium chloride, potassium chloride, calcium chloride and the like.
Other types of well known and conventional addi-tives also can be incorporated into the cement composition to modify the properties of the composition. Such additi-ves include additional fluid loss additives or viscosifiers, retarders, accelerators, dispersants, weight-adjusting materials or fillers and the like.
Additional fluid-loss additives which may be incor-porated into the cement composition of the present inventioninclude cellulose derivatives such as carboxymethylhydroxy-ethyl cellulose, hydroxyethyl cellulose, modified polysac-charides, polyacrylamides polyaromatic sulfonates, guar gum derivatives, mixtures of such compounds and the like.
Numerous other compounds which may be utilized as additional fluid loss additives are well known by those skilled in QS8~;

cementing technology.
A retarder may be used in the cementing composition when the bottom hole circulating temperature exceeds 100F.
Retarders satisfactory for use in the present invention include those commercially available products commonly uti-lized as retarders. Examples of retarders which can be used to carry out the invention include lignosulfonates, such as calcium lignosulfonate and sodium lignosulfonate, organic acids such as tartaric acid and gluconic acid and mixtures thereof. The amount of retarder required will vary according to the bottom hole circulating temperatures and variations in the makeup of the cement itself. The proper amount of retarder required in any particular case should be determined by running a "thickening time" test for the par-ticular concentration of retarder and cement compositionbeing used. Such tests should be run according to the pre-cedures set by API SPEC 10. Generally speaking, "thickening time n i8 defined in ~PI SPEC 10 as the elapsed time from the time pumping begins until the cement reaches from about 70 to 100 units of consistency. In most appli-cations the amount of retarder, if any, required will not exceed more than about 5.0 percent by weight of the cement composition.
Dispersing agents can be utilized to facilitate using lower quantities of water and to promote higher set cement strength. Friction reducers which promote freer ~8~S85 movement of the unset composition, and allow ease of pumping through the annulus, if present, can be incorporated in the slurry in amounts up to about several percent by weight of dry cement. Some dual function additives, such as ligno-sulfonates which function both as a dispersant and also as aset time retarder, can be incorporated in the slurry where their use would be advantageous for certain cementing situations.
Accelerators, such as the soluble inorganic salts in addition to calcium chloride, can be utilized up to about 8 percent by weight of cement.
The cement composition also may include, in parti-cular applications, foaming agents or defoaming agents which comprise various anionic cationic, nonionic and other sur-face active compounds. The amount of such surface active agents added to the cement composition will typically be in the range of from about 0.1 to about 3 percent by weight of cement. Generally, the selection of such additives will be wit~in the skill of those knowledgeable in cement technology.
Of the various types of fine aggregate or particu-late filler materials which can be used, fly ash, silica flour, fine sand, diatomacious earth, lightweight aggregate and hollow spheres can be cited as typical. The use of these materials is well understood in the art, and so long as they are compatible with the compositions of the inven-tion, they can be employed over wide ranges of concentration.
, ~Z8058~ .

To illustrate the uni~ue benefits of the method of the present invention and not by way of limltation, the ~ollow~ng example~ are presented.

EXAMPLE I
A number of materials were tested as potential fluld-lo~s additives for cements, including various graft polymers of the present invention. These tests were per-formed at 125F using cement slurries comprising Class H
cement, 0.25~ deEoamer comprlsing trl-n-butylphosphate by weight of cement, 1.0~ fluid-loss additive by weight of cement, and 46% water by weight o~ dry cement. The various additives identified in the following table were mixed into the cement slurries in an atmospheric consistometer which was preheated to test temperature and stirred for twenty minutes. The atmospheric consistometer is a nonpressurized lS devlce that slmulates a cementlng pumplng proce~s via move-ment of the consistometer can about a paddle. Temperature can be varied, but pressure is atmospheric. Fluid 1088 then is measured at 1000 psi through a 325 mesh screen on the U.8. Sieve Series in cc/30 minutes. The foregoing test pro-cedure i5 more fully outlined in API Spec 10, Second ; Edition, June 15, 1984, entitled API S~ecification for Materials and Testinq for Well Cements The results of these fluid-loss tests are provided in Table I. The Table I
test results indicate A

OS~36 that certain admixtures of polymers are effective fluid-loss additives under static conditions at 125F. In general, if a material is ineffective at a low temperature, it is even less effective at more elevated temperatures.

TABLE I
.
Fluid-Loss in Consistometercc/30 min.
Sample Reading 1000 psi and Fluid-Loss Additive 0 min 20 min 325 mesh screen Poly(methylhydrosi2 5 1600 10 loxane)-g-monomethyl-poly(ethylene glycol) Hydroxyethylcellulose- 26 7 450 g-AMPS0 Poly(allylamine-HCl)- 5 8 2600 15 g-AMPS0 Poly(vinyl alcohol)-g- 5 8 32 AMPS~/DMAEMA
Poly(tetraethylene-3 5 2600 pentamine)-g-AMPS~
20 Poly(ethylene glycol)- 2 6 48 g-AMPS~ 0.26:1- -Carboxymethylcellulose- 3 11 84 g-AMPS 3 g: Graft 25 AMPS: 2-acrylamido-2-methylpropanesulfonic acid DMAEMA: N,N-dimethylaminoethylmethacrylate EXAMPLE II
The test procedure of Example I is repeated for the testing of certain materials comprising ungrafted lignites ~80s8~

and lignites grafted with AMPS~, ACN or DMA as potential fluid-loss additives for cements which can contain substan-tial salt concentrations. These tests are performed at 125F using cement slurries comprising Class H cement, 38%
water by weight of cement and 1% fluid-loss additive sample by weight of cement.
The Table II results indicate that certain admix-tures of pendant polymers are effective fluid-loss additives under static conditions in fresh water and salt-containing cements.

1~305~

I~sLE II
Sample Salt, Fluid-Loss in Fluid-Loss % By Cbnsistometer cc/30 min.
Sa~ple A~ditive Mole Ratio Wt. of Reading 1000 psi and No. Liqnite, Wt. ~ AMPS~ A~N nMA Water 0 min 20 min 325 mesh screen 1. 33.3 3.62.651.0 0 4 5 28 2. 33.3 3.62.651.0 18 4 5 40 3. 33.3 3.62.651.0 37.2 4 5 248 4. 33.3 3.62.651.0 sea 4 6 76 water 5. 33.3 2.51.3 1.0 0 3 4 28 6. 33.3 2.51.3 1.0 18 3 5 48 7. 33.3 2.51.3 1.0 37.2 4 5 199 8. 33.3 2.51.3 1.0 sea 4 6 38 water 9. 20 3.11.0 1.3 0 4 5 26 15 10. 20 3.11.0 1.3 18 5 5 80 11. 20 3.11.0 1.3 37.2 4 5 173 12. 20 3.11.0 1.3 sea 5 5 40 water 13. 20 1.7 - 1.0 0 5 5 24 14. 20 1.7 - 1.0 18 4 5 145 20 15. 20 1.7 - 1.0 37.2 4 4 199 16. 20 1.7 - 1.0 sea 5 6 34 water 17. 50 1.0 - - 0 3 6 64-18. 50 1.0 - - 18 3 8 356 19. 50 1.0 - - 37.2 3 8 655 25 20. 50 1.0 - - sea 3 8 185 water 21. 33.3 3.8 - 1.0 0 3 3 60 22. 33.3 3.8 - 1.0 18 3 6 403 23. 33.3 3.8 - 1.0 37.2 3 5 473 24. 33.3 3.8 - 1.0 sea 3 5 - 151 water 30 25. 33.3 2.1 - 1.0 0 3 3 46 26. 33.3 2.1 - 1.0 18 3 5 368 27. 33.3 2.1 - 1.0 37.2 3 5 433 28. 33.3 2.1 - 1.0 sea 3 6 70 water 29. 5.0 2.55 1.3 1.0 0 18 18 20 35 30. 5.0 2.55 1.3 1.0 18 12 12 60 31. 5.0 2.55 1.3 1.0 37.2 10 12 105 32. 5.0 2.55 1.3 1.0 sea 37 25 38 water 33. 33.3 1.20.111.0 0 4 5 24 34. 33.3 1.20.111.0 18 3 4 34 40 35. 33.3 1.20.111.0 37.2 5 5 121 36. 33.3 1.20.111.0 sea 5 6 34 water 35)~;8~

TAELE II
~Continued) Sample Salt, Fluid-Loss in Fluid-Loss % By Consistometer cc/30 min.
Sample~dditive Mole Ratio Wt. of Reading 1000 psi and No. Lignite, Wt. ~ AMPS~ ACN nM~ Water 0 min 20 min 325 mesh screen 5 37. 33.3 3.31.3 1.0 0 4 5 32 38. 33.3 3.31.3 1.0 18 3 5 51 39. 33.3 3.31.3 1.037.2 4 7 452 40. 33.3 3.31.3 1.0 sea 4 8 132 water 41. 33.3 3.91.3 1.0 0 4 5 28 10 42. 33.3 3.91.3 1.0 18 3 4 60 43. 33.3 3.91.3 1.037.2 4 6 440 44. 33.3 3.91.3 1.0 sea 4 8 152 water 45. 33.3 4.41.0 1.0 0 4 5 28 46. 33.3 4.41.0 1.0 18 3 4 60 15 47. 33.3 4.41.0 1.037.2 4 8 416 48. 33.3 4.41.0 1.0 sea 5 8 69 water 4~. 33.3 5.51.0 1.0 0 5 6 30 50. 33.3 5.51.0 1.0 18 3 5 84 51. 33.3 5.51.0 1.037.2 3 8 494 20 52. 33.3 5.51.0 1.0 sea 5 9 104 water 53. 33.3 3.91.0 - 0 5 5 64 54. 33.3 3.91.0 - 18 3 5 211 55. 33.3 3.91.0 - 37.2 3 9 655 56. 33.3 3.91.0 - sea 4 8 201 water 25 57. 33.2 1.91.0 - 0 5 6 56 58. 33.2 1.91.0 - 18 4 6 200 59. 33.2 1.91.0 - 37.2 4 10 582 60. 33.2 1.91.0 - sea 4 7 282 water 61. 100 - - - 0 2 6 940 30 62. 100 - - - 18 3 8 1100 63. 100 - - - 37.2 3 3 1700 64. 100 - - - sea 5 5 870 water 8~8~
-2~-EXAMPLE III
The test procedure of Example I is repeated for the com-pounds of Example II at 190F using cement slurries comprising Class H cement, 35~ particulate silica by weight of cement, 0.5%
retarder by weight of cement, 38% water by weight of cement and 1.0% potential fluid-loss additive by weight of cement.
The results of the tests are set forth in Table III.

80~

TAELE III
Sample Salt, Fluid-Loss in Fluid-Loss % By Consistometer cc/30 min.
Sample Additive Mole Ratio Wt. of Reading 1000 psi and No. Liqnite, Wt. ~ AMPS~ ACN nMA Water 0 min 20 min 325 mesh screen 1 33.3 3.62.651.0 0 4 10 73 2 33.3 3.62.651.0 18 6 11 107 3. 33.3 3.62.651.0 37.2 7 6 50 4. 33.3 3.62.651.0 sea 6 12 77 water 33.3 2.51.3 1.0 0 5 8 82 10 6 33.3 2.51.3 1.0 18 9 10 128 7. 33.3 2.51.3 1.0 37.2 7 5 40 8. 33.3 2.51.3 1.0 sea 6 7 160 water 9 20 3.11.0 1.3 0 5 9 78 3.11.0 1.3 18 7 7 117 15 11. 20 3.11.0 1.3 37.2 8 5 30 12. 20 3.11.O 1.3 sea 7 11 138 water 13. 20 1.7 - 1.0 0 5 10 112 14. 20 1.7 - 1.0 18 7 8 99 1.7 - 1.0 37.2 7 6 46 20 16 20 1.7 - 1.0 sea 6 11 135 water 17. 50 1.0 - - 0 5 8 77 18 50 1.0 - - 18 7 15 270 19 50 1.0 - - 37.2 8 8 52 20. 50 1.0 - - sea 5 10 110 water 25 21 33.3 3.8 - 1.0 0 4 8 110 22 33.3 3.8 - 1.0 18 7 9 240 23 33.3 3.8 - 1.0 37.2 7 8 104 24 33.3 3.8 - 1.0 sea 5 8 100 water 25. 33.3 2.1 - 1.0 0 5 8 78 30 26. 33.3 2.1 - 1.0 18 6 8 300 27. 33.3 2.1 - 1.0 37.2 6 6 108 28. 33.3 2.1 - 1.0 sea 5 9 89 water 29. 5.0 2.55 1.3 1.0 0 17 13 22 5.0 2.55 1.3 1.0 18 15 10 24 35 31 5.0 2.55 1.3 1.0 37.216 10 14 32. 5.0 2.55 1.3 1.0 sea 23 21 28 water 33. 33.3 1.20.111.0 0 6 16 46 34 33.3 1.20.111.0 18 5 14 62 33.3 1.20.111.0 37.2 7 6 28 40 36. 33.3 1.20.111.0 sea 7 20 50 water ~ 8 6 T~ELE III
tcontinued) Sample Salt, Fluid-Loss in Fluid-Loss % By Consistometercc/30 min.
SampleA~ditive Mole Ratio Wt. of Reading1000 psi and No. Liqnite, Wt. % AMYS~ A~N nM~ Water 0 min 20 min 325 mesh screen 5 37. 33.3 3.3 1.3 1.0 0 6 14 70 38. 33.3 3.3 1.3 1.0 18 6 11 64 39. 33.3 3.3 1.3 1.037.2 5 7 46 40. 33.3 3.3 1.3 1.0 sea 4 16 110 water 41. 33.3 3.9 1.3 1.0 0 6 12 51 10 42. 33.3 3.91.3` 1.0 18 5 11 72 43. 33.3 3.9 1.3 1.037.2 5 8 42 44. 33.3 3.9 1.3 1.0 sea 6 18 99 water 45. 33.3 4.4 1.0 1.0 0 5 17 59 46. 33.3 4.4 1.0 1.0 18 6 7 42 15 47. 33.3 4.4 1.0 1.037.2 8 4 20 48. 33.3 4.4 1.0 1.0 sea 7 19 79 water 49. 33.3 5.5 1.0 1.0 0 6 20 59 50. 33.3 5.5 1.0 1.0 18 7 7 50 51. 33.3 5.5 1.0 1.037.2 6 5 20 20 52. 33.3 5.5 1.0 1.0 sea 6 17 96 water 53. 33.3 3.9 1.0 - 0 6 16 58 54. 33.3 3.9 1.0 - 18 6 8 54 55. 33.3 3.9 1.0 - 37.2 5 5 30 56. 33.3 3.9 1.0 - sea 6 15 160 water 25 57- 33.2 1.9 1.0 - 0 6 16 64 58. 33.2 1.9 1.0 - 18 6 7 50 59. 33.2 1.9 1.0 - 37.2 5 5 30 60. 33.2 1.9 1.0 - sea 6 16 148 water 61. 100 - - - 0 7 7 820 30 62. 100 - - - 18 4 7 1400 63. 100 - - - 37.2 3 5 1600 64. 100 - - - sea 4 4 1400 water 65.1 -o- 2.5 1.3 1.0 0 - - 350 66.1 -O- 2.5 1.3 1.037.2 - - 1150 35 67.1 _0_ 2.5 1.3 1.0 sea - - 740 water 68.2 33.3 2.5 1.3 1.0 0 - - 520 69.2 33.3 2.5 1.3 1.037.2 - _ 1130 70.2 33.3 2.5 1.3 1.0 sea - - 710 water 1 Polymerized monomers only, no lignite 40 2 Physical mLxture only - no graft polymerization The results of Tables II and III clearly indicate the advantages of grafting polymer sidechains onto various backbones. The use of lignite as a backbone in the fluid-loss additive is particularly advantageous since fluid-loss 5 control is achieved over a broad range of ionic strengths in the fluids and satisfactory cement slurries can be prepared from sea water which facilitates offshore cementing opera-tions.

EXAMPLE IV
Density segregation and free water studies were 10 conducted on a portion of the cement slurries of Example III
to determine the amount of free water formed and particle settling after a period of standing for two hours. The slurry sample is mixed on the consistometer for 20 minutes and poured directly into a 250 cc graduated cylinder.
15 Percent free water and settling of the slurry was measured after two hours. The sample number corresponds to the sample number for the additive tested in Example III.

~.~8058çi TABLE IV
Free Water Settling Sample No.
Trace 2 Trace 0 Trace 0 4 Trace 0 Trace 30.2 6. 0 4 3.2 Trace 0 8.

12. 4 8 00 13. 00 4 10.6 4.8 0 16 Trace 17. 1 6 520 20. ~ 4 120 21 0.8 4~
22 1.6 0 24 ~ 0 8 4 222s67....................... Trace 60 30 28.

31. 0 0 32.
3533. 1.6 366 356. 0 8 o .

~,~gs)586 TABLE IV
Free Sample Water Settling No. _ 96 37. 1.6 40 38. Trace 00 41. 2.4 329 10 44424 Trace 3.2 422 4467. Trace 0 51 Trace 0 52. Trace 53. Trace 0 0.5 00 56.

57. 0.8 360.8 25 556890-. 4 Solids on the bottom of the graduated cylinder unpenetrable by a metal ruler ~8o~86 ! 28 In oil well cementing operations, it is importan-t that free water values as defined in API
Spec 10, Second Edition, June 15, 1984, previously identified, be maintained at low values. The importance o this parameter is discussed in a paper by Wester, W. w. and Eikerts, J.V. entitled "Flow After Cementing: A Field and Laboratory Study", Society of Petroleum Engineers Paper No. 8259, September 1979. Although API free water values give an indication of particle settling or sedimentation in a cementing slurry, it is possible for certain cementing compositions to have low API free water values and still involve settling. For a ve~tical, uniform sheath oE set cement to be formed in a well bore, particle sedimentation should be minimized in the design of the cementing compositions. As indicated by the data in Table IV, it is possible to design cementing compositions which readily meet the desired low API free water values and minimize particle sedimentation using the additives of the present invention. For those fluid-loss additives identified in Table IV which provide unacceptable API free water values or settling, it is possible in some instances to effect certain cementing composition formulation modifications as is known in the art to combat these problems. These modiflcations can be accompiished while maintaining the highly desirable fluid-loss response properties of the graft polymer comprising the fluid-loss additive of the present invention.

~'~8[)~

While that which is considered to be the preferred embodiment of the invention has been described hereinbefore, it is to be understood that modifications and changes can be made in the method of the present invention without depart-5 ing from the spirit or scope of the invention as set forthin the following claims.

Claims

1. A method of cementing a conduit in a borehole penetrating an earthen formation by introducing a cementing composition into the space between said conduit and said formation, said cementing composition comprising:
cement;
an aqueous fluid, and a fluid-loss additive comprising a graft polymer comprising a backbone comprising at least one member selected from the group consisting of lignin, lignite and their salts and a grafted pendant group comprising at least one member selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid, acrylonitrile, N,N-dimethylacrylamide, acrylic acid, N,N-dialkylaminoethylmethacrylate wherein said alkyl radical comprises at least one member selected from the group con-sisting of methyl, ethyl and propyl radicals.

2. The method of claim 1 wherein said backbone of said fluid-loss additive comprises from about 5 to about 95 percent by weight of said fluid-loss additive.

3. The method of claim 1 wherein said pendant groups of said fluid-loss additive comprise from about 50 to about 90 percent by weight of said fluid-loss additive.

4. The method of claim 1 wherein said pendant groups of said fluid-loss additive comprise from about 60 to about 80 percent by weight of said fluid-loss additive.

5. The method of claim 1 wherein said aqueous fluid contains salt.

6. The method of claim 1 wherein said fluid-loss additive is present in said cementing composition in an amount of from about 0.25 percent to about 5 percent by weight of the cement.

7. The method of claim 1 wherein said fluid-loss additive is present in said cementing compositions in an amount of from about 0.5 percent to about 1.5 percent by weight of the cement.

8. The method of claim 1 wherein the pendant groups of said fluid-loss additive comprise at least one member selected from the group consisting of 2-acrylamido-2-methylpropane-sulfonic acid acrylonitrile, N,N-dimethylacrylamide and their salts.

9. The method of claim 1 wherein said pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid, acrylonitrile and N,N-dimethyl-acrylamide or their salts and are present in said graft polymer in a molar ratio in the range of from about 1:0:0 to about 3:3:1, respectively.

10. The method of claim 1 wherein said pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid, acrylonitrile and N,N-dimethyl-acrylamide or their salts and are present in said graft polymer in a molar ratio in the range of from about 3:2:1 to about 3:3:1, respectively.

11. The method of claim 1 wherein the pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid and acrylonitrile or their salts and are present in said graft polymer in a molar ratio in the range of from about 1:0 to about 1:1, respectively.

12. The method of claim 1 wherein the pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid and N,N-dimethylacrylamide or their salts and are present in said graft polymer in a molar ratio in the range of from about 1:0 to about 6:1, respectively.

13. A method of cementing a conduit penetrating a permeable earthen formation comprising:
introducing a cementing composition into the space between said conduit and said formation, said cementing composition comprising:
cement, an aqueous fluid, and a fluid-loss additive comprising a graft polymer comprising a backbone comprising at least one member selected from the group consisting of lignin, lignite, and their salts and a grafted pendant group comprising at least one member selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid, acrylonitrile, N,N-dimethylacrylamide and their salts; and allowing said cementing composition to set within said space.

14. The method of claim 13 wherein said aqueous fluid contains salt.

15. The method of claim 13 wherein the pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid and acrylonitrile or their salts and are present in said graft polymer in a molar ratio in the range of from about 1:0 to about 1:1, respectively.

16. The method of claim 13 wherein the pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid and N,N-dimethylacrylamide or their salts and are present in. said graft polymer in a molar ratio in the range of from about 1:0 to about 6:1, respectively.

17. The method of claim 13 wherein said pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid, acrylonitrile and N,N-dimethylacryl-amide or their salts and are present in said graft polymer in a molar ratio in the range of from about 1:0:0 to about 3:3:1, respectively.

18. A method of cementing a conduit penetrating a permeable earthen formation comprising introducing a cementing composition into the space between said conduit and said formation, said cementing composition comprising:
cement, an aqueous fluid containing salt, a fluid-loss additive comprising a graft polymer comprising a backbone comprising at least one member selected from the group consisting of lignin, lignite and their salts and a grafted pendant group comprising at least one member selected from the group consisting of 2-acrylamido-2-methylpropanesulfonic acid, acrylonitrile, N,N-dimethylacrylamide and their salts; and allowing said cementing composition to set within said space.

19. The method of claim 18 wherein said pendant groups comprise 2-acrylamido-2-methylpropane-sulfonic acid, acrylonitrile and N,N-dimethylacryl-amide or their salts and are present in said graft polymer in a molar ratio in the range of from about 3:2:1 to about 3;3:1, respectively.