CA1321688C - Polyimide gas separation membranes - Google Patents

Polyimide gas separation membranes

Info

Publication number
CA1321688C
CA1321688C CA000549790A CA549790A CA1321688C CA 1321688 C CA1321688 C CA 1321688C CA 000549790 A CA000549790 A CA 000549790A CA 549790 A CA549790 A CA 549790A CA 1321688 C CA1321688 C CA 1321688C
Authority
CA
Canada
Prior art keywords
productivity
hours
selectivity
solution
films
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CA000549790A
Other languages
French (fr)
Inventor
Richard Allen Hayes
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
EIDP Inc
Original Assignee
LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude, EI Du Pont de Nemours and Co filed Critical LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
Application granted granted Critical
Publication of CA1321688C publication Critical patent/CA1321688C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

TITLE
POLYIMIDE GAS SEPARATION MEMBRANES
ABSTRACT OF THE DISCLOSURE
Semi-flexible aromatic polyimides, prepared by polycondensation of dianhydrides with diamines having alkyl substituents on all ortho positions to the amine functions, or with mixtures of diamines, some components having substituents on all positions ortho to the amine functions, are disclosed.
Membranes formed from this class of polyimides have improved environmental stability and superior gas permeability. The range of gas permeation properties observed allows for the tailoring of membrane material for widely diverse gas separations. The high permeabilities of some gases from multicomponent mixtures is due to the optimization of the molecular free volume in the polymer.

Description

~ 321~88 o POLYIMIDE GAS SEPARATION MEMBRANES
BACKGROUND OF THE INVENTION
Field of the Invention The present invention relates to certain substituted aromatic polyimide separation membranes particularly useful for separating gases and the process of using them.
Prior Art U.S. Patent 3,822,202 and U.S. 3,899,309 disclose aromatic polyimide gas separation membranes in which the molecular structure is such that the molecules in the polymer are unable to pack densely, and, therefore, have high gas permeation rates.
U.S. Patent 4,113,628 and U.K. 1,435,151 of Du Pont, published 1976 May 12, disclose aromatic polyimide gas separation membranes prepared from polyamide acid membranes.
EPO 132,221 of Ciba Geigy, published 1985 January 23, and EPO 141,781 of Ciba Geigy, published 1985 May 15, discloses substituted aromatic polyimides and photochemically crosslinked compositions thereof, but not for use as gas separation membranes.
U.S. Patent 4,370,290, U.S. 4,460,526, U.S.
4,474,662, U.S. 4,512,893, U.K. 2,098,994 of Ube Industries, published 1982 December 01, U.K.
2,101,137 of Ube Industries, published 1983 January 12, and U.K. 2,102,333 of Ube Industries, published 1983 February 02, discloses microporous aromatic polyimide membranes and the process from which they are prepared.

1321~88 U.S. Patent 4,486376 and U.K. 2,104,832 of Ube Industries, published 1983 March 16, disclose gas separation membranes made from a microporous aromatic polyimide support treated with modifying agents.
U.S. Patent 4,378,324, U.S. 4,440,643, U.S.
4,474,858, U.S. 4,485,056, U.S. 4,528,004, U.K.
2,102,726 of Ube Industries published 1983 February 09, U.K. 2,104,411 of Ube Industries, published 1983 March 09, and U.K. 2,104,905 of Ube Industries, published 1983 March 16, disclose gas separation membranes made from a microporous aromatic polyimide support coated with an aromatic polyamide acid or aromatic polyimide.
U.S. 4,378,400 and EPO 43,265 of Ube Industries, published 1982 January 06, disclose aromatic polyimide gas separation membranes in which the molecular structure is such that the molecules in the polymer can pack densely.
U.S. 4,578,166 discloses polymers comprising as the essential component a saturated linear polyester or polyamide and copolymerized therewith benzophenone tetracarboxylic groups which are crosslinked by irradiation.
EP0 113,574 of Sumitomo Electric, published 1984 July 18, discloses gas separation membranes made from aromatic polyetherimides.
EP0 143,552 of Nitto Electric, published 1985 June 05, discloses gas separation membranes made from a microporous aromatic polyimide support coated with a crosslinked silicone resin film.
EP0 125,908 of Exxon Research and Engineering, published 1984 November 21, discloses aromatic polyimide reverse osmosis membranes.

1 3 ~

SUMMARY OF THE INVENTION
Canadian patent application Serial No 534,692 of R.A. Hayes filed 1986 April 14, discloses aromatic polyimide gas separation membranes in which the monomeric diamines were rigid and substituted on essentially all of the positions ortho to the amino substituents and the monomeric acid anhydride groups were essentially all attached to rigid aromatic moieties exhibited extremely high permeation rates to gases. The present invention relates to aromatic polyimide gas separation membranes in which some of the before described rigidity is relaxed through use of acid anhydride groups which are essentially attached to less rigid aromatic diamines, and/or unsubstituted diamines. Through controlled reduction of the rigidity, polyimide gas separation membranes which have improved selectivities~

.... . . .

.' : ~ . :

:

132~ ~8 to gases while still maintaining high permeation to gases are available to effectively separate several combinations of gases.
DETAILED DESCRIPTION
The present invention relates to the discovery that aromatic polyimides derived from diamines having substitutents on all positions ortho to the amine functions or from mixtures of aromatic diamines, some components having substitutents on all positions ortho to the amine functions, exhibit exceptional gas permeability. The selectivity of one gas over other gases in a multicomponent gas mixture can be controlled through choice of the amounts of aromatic diamines having substitutents on all positions ortho to the amine functions and/or the amounts of structurally-nonrigid dianhydrides utilized in the polyimide preparation while maintaining exceptional gas permeability. The high permeability of these membranes is believed to be due to the high molecular free volume in the polymer structure resulting from the rigid nature of the rotationally hindered polymer chains.
Generally, extremely high gas permeation through dense polymeric membranes is found only with low glass transition temperature (Tq) materials, such as silicone rubbers and a few polyolefin polymers.
The low Tg materials are generally only useful as the dense separating layer in composite membranes, where a supporting porous membrane substructure provides structural integrity.
High Tg polymeric materials, found in the prior art, generally do not possess extremely high gas permeabilities. Examples reported involve mostly unsubstituted, or partially substituted, polymers ~ 32~8~

subject to for~ing a close chain packing during fabrication and/or subsequent operation.
The aforementi~ C~dian patent application Serial Nb. 534,692 discloses that arRmatic polyimide gas separation membranes in which the monomeric dlamines were rigid and substituted on essentially all of the positions ortho to the amino substituents and the monomeric acid anhydride groups were essentially all attached to rigid aromatic moieties exhibited extremely high permeation rates to gases. The present invention, through the controlled addition of less chain rigidity, allows for an improved selectivity while still maintaining high permeability to gases.
The present invention circumvents the above shortcomings and provides exceptionally high permeability dense membranes using high Tg aromatic polyimides containing the repeating unit:

O O O O
l~
C C C C
/\ /\ / \ /\
~Art--~N R Nt--tAr't--~N R' Nt C C C C
Il ~I 11 11 where -Ar- is ~ X~X2 Xl X2 Xl X3 z -.; ;., ~
:. ,. :. . :, :

~ :;' ` ~321~8~

or mixtures thereof, -R- is ~ ~ ~ C

or mixtures thereof, -Ar'- is 10 ~ , ~ ~ ~

R"
~ ~

or mixtures thereof, R' is ~ ~,R"~

or mixtures thereof, and -R~- is .---C-- , --O-- , --S-- , --S-- , --C--(X)n ~0, where n = O to 4, alkylene radicals of 1 to 3 carbon atoms or mixtures thereof, 1321~88 -X, -Xl, -X2, and -X3 are independently alkyl groups having 1 to 6 carbon atoms preferably methyl or ethyl, or aromatic groups of 6 to 13 carbon atoms, Z is -H, -X, -Xl, -X2, or -X3 W is S% to 100%, Q is 5% to 100%, Y is 100% minus W
V is 100% minus V
Y plus V is at least 5%, preferably 10 to 50%.
The multiple substitutions ortho to the amines in the above illustrated structures sterically restricts free rotation around the imide linkage. These amines in combination with structurally rigid dianhydrides form rigid polyimides. The incorporation of flexible units such as R' for dianhydrides and/or -Ar'- for diamines, allows for the partial relaxation of this rigidity which may lead to lowered molecular free volume in the polymer. This relaxation promotes greater selectivity for the permeation of certain gases from multicomponent gas mixtures through the membrane. At comparable gas selectivities, membranes of the polyimides disclosed herein have generally higher gas permeation rates than other polymers disclosed in the prior art. By varying the amount of relaxation in the polymers of this invention, membranes can be tailored for a wide range of gas separations with exceptional gas productivity.
As preferred examples, some of the fully cyclized polyimides of this invention are soluble in ordinary organic solvents. This is a great advantage for the ease of fabrication of industrially useful membranes. Further, the polyimides reported in this invention range from extremely soluble to insoluble.

: -, . : - . ~
. ., ;,~ . :

132~88 The soluble polyimides can be solution cast on porous solvent resistant substrates to serve as the dense separating layer of a composite membrane; or they can be solution cast as dense or asymmetric films.
Insoluble examples can be cast into membranes from their polyamic acid form and subsequently chemically or thermally cyclized.
The polyimides described in this invention have high inherent thermal stabilities. They are generally stable to 400 C in air or inert atmospheres.
The glass transition temperatures of these polyimides are generally above 300-C. The high temperature characteristics of these polyimides can help to prevent the membrane compaction problems observed in other polymers at even moderate temperatures.
The present invention finds use in recovery of hydrogen in refinery and ammonia plants; separation of carbon monoxide from hydrogen in syngas systems;
separation of carbon dioxide or hydrogen sulfide from hydrocarbons; enrichment of oxygen and nitrogen from air for increased combustion or inerting streams, respectively.
EXAMPLES
Example 1 To a 50-C stirred solution of 2,4,6-trimethyl-1,3-phenylenediamine (30.01g, - -0.20 mol) in ~-methylpyrrolidone t600 ml) under an inert atmosphere was added 3,3',4,4'-benzophenonetetracarboxylic dianhydride (3.22g, 0.01 mol). After stirring 0.5 hours, 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione 132~88 C\ / I~
~c ~~C ' I~ ~l O o (84.36g, 0.19 mol), was added in eight portions, the last portion ~eing washed in with 200 ml _-methyl 10 pyrrolidone. The yellow solution was stirred at 50C
overnight, then a solution of acetic anhydride (75.8 mol, 0.80 mol) and triethylamine (223.9 ml, 0.81 mol) was rapidly added and the resulting reaction solution stirred for 2 hours. The reaction solution was precipitated in methanol. The resulting white solid was collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 5 hours and at 250C for 2 hours to give 104.37g white product.
Films were cast from a 15% solution, (based on weight) of the above polymer in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 80-C with a 15-mil (3.8xlO-4m) knife gap. The films were dried on the plate at 80'C for 25 minutes, cooled to room temperature, stripped off the plate and dried in a vacuum oven at room temperature overnight and at 120DC
for 4 hours. The films were then tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2kPa), 25-C. Results are reported below:
2 Productivity: 8,900 centiBarrer 2/N2 Selectivity: 3.5 and 2 Productivity: 12,000 centiBarrer 35 2/N2 Selectivity: 3.5 .

~ -Du Pont TEFLON~ dry lubricant contains a fluorccarbon telomer which reduces the adhesion of the membrane to the glass plate.
A centiBarrer is the number of cubic centimeters of gas passed by the membrane at standard temperature and pressure times the thickness of the membrane in centimeters times 10-12 divided by the permeating area of the membrane in square centimeters times the time in seconds times the partial pressure difference across the membrane in cm Hg, i.e., cm3 (STP)-cm centiBarrer = lo-12 __________________ cm2 - sec - cmHg The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity:29,300 centiBarrer 20 N2 Productivity:2,270 centiBarrer C2 Productivity:84,600 centiBarrer He/N2 Selectivity: 13 C02/N2 Selectivity: 37.3 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
H2 Productivity: 32,230 centiBarrer H2/CH4 Selectivity: 9.5 Example 2 To a stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol) in N-methyl pyrrolidone (600 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (6.44g, 0.02 mol, washed in with 50 ml N-methyl pyrrolidone). After the .: :

1321~88 solution was stirred for 0.75 hours, 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (79.92g, 0.18 mol), was added in seven portions, the last portion being washed in with 150 ml N-methyl pyrrolidone. The yellow reaction solution was stirred for 2 hours. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added to the reaction solution and the resulting yellow solution stirred for 2 hours. The reaction solution was precipitated in methanol. The resulting white solid was collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours, and at 250C for 3 hours to give 119.5g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 75C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 75 C for 25 minutes, cooled to room temperature, stripped off the plate, and dried in a vacuum oven at room temperature overnight and at 120C
for 4 hours. The films were then tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 k Pa), 25-C. Results are reported below:
2 Productivity: 8,300 centiBarrer 2/N2 Selectivity: 3.9 The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 k Pa), at 25DC.
Results are reported below:

- . .

: `
. , ~ ,.. .

~ ~.

1321~88 He Productivity:28,530 centiBarrer N2 Productivity:1,800 centiBarrer C2 Productivity:129,000 centiBarrer He/N2 Selectivity: 16 C02/N2 Selectivity: 72 Example 3 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol~ in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (9.21g, 0.03 mol). After stirring at 50~C for 0.3 hours, 5,5'-2,2,2-trifluoro-2-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (76.lg, 0.17 mol, added in four portions, last portion washed in with 150 ml N-methyl pyrrolidone) was added and the resulting reaction solution stirred at 50C overnight. A
solution of acetic anhydride (78.5 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting yellow solution stirred at 50C for 2 hours. The reaction solution was precipitated in methanol, the white solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at lOO-C for 3 hours and at 220~C for 3 hours to give 104.2g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90-C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature, and dried in a vacuum oven at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120C
for 4 hours. The films were then consecutively tested :

:

13211~88 for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
He ~roductivity: 28,660 centiBarrer N2 Productivity: 1,540 centiBarrer C2 Productivity: 121,650 centiBarrer He/N2 Selectivity: 19 C02/N2 Selectivity: 79 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
H2 Productivity: 21,420 centiBarrer H2/CH4 Selectivity: 14 Example 4 To a 50'C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (16.1g, 0.05 mol) and the resulting yellow solution stirred for 0.5 hours.
5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (66.6g, 0.15 mol, in four portions, last portion washed in with 150 ml N-methyl pyrrolidone) was added to give a light yellow solution. After stirring overnight at 50 C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting reaction solution stirred at 50C
for 2 hours. The reaction solution was precipitated in methanol, the resulting solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours and at 200-C for 3 hours. The product was an off-white solid (102.3g).

.

;

' 1321~88 Films of the above polymer were cast from a 15~ polymer solution (based on weight) in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.
The films were stripped off the plate and further dried in a vacuum oven at 120C for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 k Pa), 25 C. Results are reported below:
15 He Productivity:26,520 centiBarrer N2 Productivity:2,640 centiBarrer C2 Productivity:90,320 centiBarrer He/N2 Selectivity: 10 C02/N2 Selectivity: 34 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
H2 Productivity: 22,080 centiBarrer H2/CH4 Selectivity: 15 The above films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 k Pa), 25C. Results are reported below:
2 Productivity: 5,900 centiBarrer 2/N2 Selectivity: 4.0 0 Example 5 To a 50-C, stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (32.2g, 0.10 mol). After stirring for 2 hours at 50C, 5,5'-2,2,2-trifluoro-1-,, . :~

1321~88 (trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedio-ne (44.4g, 0.10 mol, added in four portions, last portion washed in with 150 ml N-methyl pyrrolidone) was added to the slightly yellow reaction solution.
The reaction solution was allowed to stir at 50C
overnight. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, O.Bl mol) was added as rapidly as possible to the rapidly stirred reaction solution at 50-C. After stirring for 2 hours, the reaction solution was precipitated in methanol. The resulting white solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at 100C
for 3 hours and at 220-C for 3 hours to give 96.9g product.
Films of the above polymer were cast from a -15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON¢ dry lubricant at 90-C with a 15 mil (3.8 x 10-4) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.
The films were stripped off the plate and further dried in a vacuum oven at 120-C for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 k Pa), 25 C. Results are reported below:
He Productivity:17,930 centiBarrer N2 Productivity:713 centiBarrer C2 Productivity:46,680 centiBarrer He/N2 Selectivity: 25 CO2/N2 Selectivity: 66 1321~8~

Films of the above polymer were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 k Pa), 25 C. ~esults are reported below:
2 Productivity: 3,800 centiBarrer 2/N2 Selectivity: 4.2 Films of the above polymer were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25-C. Results are reported below:
H2 Productivity: 10,600 centiBarrer H2/CH4 Selectivity: 20.0 To a 50 C stirred solution of 2,3,5,6-tetramethyl-1,4-phenylene diamine (32.86g, 0.20 mol) in N-methyl pyrrolidone (500 ml) under an inert atmosphere was sequentially added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (3.22g, 0.01 mol) and 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzo-furanedione (84.36g, 0.19 mol, added in four portions,last portion washed in with 250 ml N-methyl pyrrolidone~ and the resulting yellow solution was stirred overnight at 50-C. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added to the reaction solution. After stirring at 50-C for 2 hours, the yellow reaction solution was precipitated in methanol.
The resulting white solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at lOO-C for 4 hours and at 250 C for 3 hours to give 112g product.
Films of the above polymer were cast from a 12.5% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 85-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the ' ~

1321$8~

plate at 85~C for 25 minutes, coole~ to room temperature and dried in a vacuum ov at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120~C
for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
lo He Productivity:39,600 centiBarrer N2 Productivity:3,500 centiBarrer C2 Productivity:230,900 centiBarrer He/N2 Selectivity: 11 C02/N2 Selectivity: 66 Films of the above polymer were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 k Pa), 25-C. Results are reported below:
2 Productivity: 14,100 centiBarrer 2/N2 Selectivity: 3.4 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25~C. Results are reported below:
H2 Productivity: 33,980 centiBarrer H2/CH4 Selectivity: 6.8 Example 7 To a 50-C stirred solution of 2,4,6-trimethyl-1-3-phenylene diamine (30.01g, 0.20 mol) in _-methyl pyrrolidone (500 ml) under an inert atmosphere was sequentially added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (3.22g, 0.01 mol) and 1,2,4,5-benzenetetracarboxylic dianhydride (41.44g, 0.19 mol, added in four portions). After stirring overnight at 50C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting orange solution stirred for 2 hours 13216~

at 50C. The reaction solution was recipitated in methanol. The resulting orange soli( ~A~as collected by filtration, washed with methanol, and Iried in a vacuum oven at room temperature overnight, at 100C
for 3 hours and at 250C for 3 hours to give 67.lg product.
Films of the above polymer were cast from a 10% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont ~eflon~ dry lubricant at 80C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 80 C for 30 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.
The films wre stripped off the plate and further dried in a vacuum oven at 120C for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity:10,800 centiBarrer N2 Productivity:814 centiBarrer C2 Productivity:38,140 centiBarrer He/N2 Selectivity: 13 C02/N2 Selectivity: 47 25 and He Productivity:10,500 centiBarrer N2 Productivity:580 centiBarrer C2 Productivity:123,500 centiBarrer He/N2 Selectivity: 18 C02/N2 Selectivity: 213 The above films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 450 psig 3.1 kPa, 25C. Results are reported below:
2 Productivity: 3,100 centiBarrer 2/N2 Selectivity: 4.1 132~8~ -The above films were tested for mixed gas /CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
H2 Productivity: 21,960 centiBarrer H2/CH4 Selectivity: 9 Example 8 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (6.44g, 0.02 mol) and the resulting solution stirred for 0.75 hours. At 50C
1,2,4,5-benzenetetracarboxylic dianhydride (39.3g, 0.18 mol, added in 4 portions, last portion washed in with 150 ml N-methyl pyrrolidone) was added with stirring and the orange reaction solution stirred overnight at 50 C. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was added as fast as possible to the rapidly stirring 50C reaction solution. A solid precipitated, but slowly went back into solution.
After stirring at 50C for 2 hours, the orange reaction solution was precipitated in methanol. The resulting yellow solid was collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours and at 230C for 3 hours. This gave 68.5g product as a yellow-orange solid.
Films of the above polymer were cast from a 12.5% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont Teflon~ dry lubricant at 90-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature, and dried in a vacuum oven at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120DC for 4 hours.
The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity:22,730 centiBarrer N2 Productivity:1,400 centiBarrer C2 Productivity:118,600 centiBarrer He/N2 Selectivity: 16.2 C02/N2 Selectivity: 85 The above films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 kPa), 25-C. Results are reported below:
2 Productivity: 7,900 centiBarrer 2/N2 Selectivity: 3.9 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25C. Results are reported below:
H2 Productivity: 23,600 centiBarrer H2/CH4 Selectivity: 9.2 Example 9 To a 50-C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.01g, 0.20 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (9.21g, 0.029 mol). After the yellow solution had stirred for 0.50 hours, 1,2,4,5-benzenetetracarboxylic dianhydride (37.4g, 0.17 mol, added in four portions, last portion washed in with 150 ml ~-methyl pyrrolidone) was added and the resulting orange raction solution was stirred at 50C
overnight. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was added as fast as possible to the rapidly stirring 50c ~ ' .

reaction solution. A solid precipitated, but went back into solution after ~ minutes. The resulting orange reaction solution was stirred at 50-C for 2 hours and then precipitated in methanol. The off-white solid was collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours and at 220C for 3 hours to give 69.4g of an orange product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90 C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90'C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120C
for 4 hours. The films were then tested for mixed gas 20 H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 -k Pa), 25C. Results are reported below:
H2 Productivity: 24,050 centiBarrer H2/CH4 Selectivity: 8 The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25-C. The results are reported below:
He Productivity:28,800 centiBarrer N2 Productivity:2,080 centiBarrer 30 C2 Productivity:163,600 centiBarrer He/N2 Selectivity: 14 C02/N2 Selectivity: 79 -Example 10 To a stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.05g, 0.20 mol) in N-methyl pyrrolidone (450 ml) at room temperature under a :

nitrogen atmosphere was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (16.11g, 0.05 mol, washed in with N-methyl pyrrolidone (50 ml)). After stirring at room temperature for 0.5 hours, 1,2,4,5-benzene-tetracarboxylic dianhydride (32.72g, 0.15 mol, washed in with N-methyl pyrrolidone (100 ml)) was added and the yellow solution allowed to stir for 2 hours. A
solution of acetic anhydride (75.84 ml, 0.80 mol) and triethylamine (112.94 ml, 0.80 mol) was added as fast as possible with fast stirring. A white solid precipitated, but went back into solution to form a viscous golden-yellow solution. After stirring 2 hours, the reaction solution was precipitated in methanol, the resulting off-white solid collected by filtration, and dried in vacuo overnight at room temperature, for 4 hours at 100C, and for 3 hours and at 240C to give product. (69.3g).
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 80DC with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 80-C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120C
for 4 hours. The films were then tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 k Pa), 25-C. Results are reported below:
H2 Productivity: 10,170 centiBarrer H2/CH4 Selectivity: 20.4 The above films were tested for mixed gas CO2/CH4 (50/50) (mole) permeabilities at 245 psig _ (1.7 k Pa), 25-C. Results are reported below:
3~

132~88 C2 Productivity: 9,517 centiBarrer C02/CH4 Selectivity: 30 The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25 C. The results are reported below:
He Productivity:7,450 centiBarrer N2 Productivity:200 centiBarrer C2 Productivity:37,700 centiBarrer He/N2 Selectivity: 37 C02/N2 Selectivity: 187 Exam~le 11 To a stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.05g, 0.20 mol) in N-methyl pyrrolidone (500 ml) was added 3,3',4,4'-benzophenone tetracarboxylic dianhydride (32.22g, 0.10 mol, washed in with 100 ml N-methyl pyrrolidone) at room temperature under an inert atmosphere. The slightly yellow solution was stirred for 0.5 hours and then 1,2,4,5-benzenetetracarboxylic dianhydride (21.8g, 0.10 mol, washed in with N-methyl pyrrolidone (100 ml)) was added. The yellow solution turned more viscous and was stirred for 2 hours at room temperature. A solution of acetic anhydride (75.84 ml, 0.80 mol) and triethylamine (112.94 ml, 0.80 mol) was rapidly added with fast stirring, causing a small amount of white solid to precipitate. As the solid redissolved, the solution became viscous and orange-yellow. After stirring for 2 hours, the reaction solution was precipiated from methanol, the white solid collected by filtration, and the reaction product washed with methanol. The solid was dried in vacuo overnight at room temperature, 3 hours at lOO~C
and 3 hours at 220~C to give 73.6g product.

' 1321~88 Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 75-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 75 C for 25 minutes, then at room temperature for 30 minutes. The films were stripped off the plate and dried at room temperature in a vacuum oven for 4 hours and at 120C in a vacuum oven for 4 hours. The films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 KPa), 25C. Results are reported below:
He Productivity:6,830 centiBarrer N2 Productivity:71 centiBarrer C2 Productivity:12,140 centiBarrer He/N2 Selectivity: 96 C02/N2 Selectivity: 171 and He Productivity:7,500 centiBarrer N2 Productivity:55 centiBarrer C2 Productivity:17,300 centiBarrer He/N2 Selectivity: 136 C02/N2 Selectivity: 315 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25C. The results are reported below:
H2 Productivity: 6,590 centiBarrer H2/CH4 Selectivity: 31 Example 12 To a stirred, 50C solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.0lg, 0.20 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was added 3,3',4,4'-benzophenone tetracraboxylic dianhydride (48.3g, 0.15 mol). After stirring for 0.5 hours, 1,2,4,5-benzene-.

132~ 68~

tetracarboxylic dianhydride (10.9g, 0.05 mol, washedin with 150 ml N-methyl pyrrolidone) was added and the resulting orange solution allowed to stir at 50~C
overnight. A solution of acetic anhydride ~75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was added as rapidly as possible to the rapidly stirring reaction solution and the resulting orange solution was stirred at 50'C for 2 hours. The reaction solution was precipitated in methanol, the off-white solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at lOO C for 3 hours and at 220-C for 3 hours. The off-white product was collected in a 89.8g 5 yield.
Films of the above polymer were cast from a 12.5% polymer solution (based on weight) in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90-C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.
The films were stripped off the plate and further dried in a vacuum oven at 120-C for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25 C. Results are reported below:
He Productivity: 3,680 centiBarrer N2 Productivity: 108 centiBarrer C2 Productivity: 22,010 centiBarrer He/N2 Selectivity: 34 C02/N2 Selectivity: 204 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25-C. The results are reported below:

;
:
:.- -~2 Productivity: 6,850 centiBarrer H2/CH4 Selectivity: 28 Example 13 To a stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (30.05g, 0.2 mol) in ~-methyl pyrrolidone (450 ml) was added 3,3',4,4'-benzophenone tetracraboxylic dianhydride (9.2lg, 0.029 mol) at 50C
under an inert atmosphere. After stirring 30 minutes, 10 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (19.3g, 0.043 mol, in three portions) was added. The yellow solution was stirred at 50 C for 15 minutes after which 1,2,4,5-benzenetetracarboxylic dianhydride (28.04g, 0.129 mol, in three portions, last portion washed in with N-methyl pyrrolidone (300 ml)) was added. The resulting orange-yellow reaction solution was stirred at 50~C under an inert atmosphere overnight. A
solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.80 mol) was added as quickly as possible to the rapidly stirred reaction solution at 50-C and the resulting orange reaction solution was stirred for 2 hours at 50-C. The reaction solution was precipitated in methanol, the resulting white solid collected by filtration, and washed with additional methanol. The white solid was dried in a vaccum oven at ambient temperature overnight, at 120-C for 4 hours and at 260-C for 4 hours to give 77g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90 C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90 C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.

1321~8~

The films were then stripped off the plate and further dried in a vacuum oven at 120C for 4 hours. The films were consecutively tested for pure gas helium, nitrogen and carbon dioxide permeabilities at 400 psig (2.75 kPa), 2SC. Results are reported below:
He Productivity: 22,600 centiBarrer N2 Productivity: 600 centiBarrer C2 Productivity: 91,000 centiBarrer He/N2 Selectivity: 38 C02/N2 Selectivity: 152 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25~C. The results are reported below:
15 H2 Productivity: 25,000 centiBarrer H2/CH4 Selectivity: 6 Example 14 To a 50-C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (28.54g, 0.19 mol) and 1,3-phenylene diamine (1.08g, 0.01 mol) in dimethylsulfoxide (500 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (88.8g, 0.20 mol, added in eight portions, last portion washed in with dimethyl sulfoxide (250 ml)). After stirring overnight at 50~C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added to the reaction solution and the resulting yellow solution stirred at 50 C for 2 hours.
The reaction solution was precipitated in methanol, and the resulting white solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at lOO~C
for 4 hours and at 200~C for 4 hour to give 106.7g product.

, , - '~ ,` ..

Films of the above polymer were cast from a 10% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 85-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 85C for 30 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight.
The films were stripped off the plate and further dried in a vacuum oven at 120C for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25 C. Results are reported below:
15 He Productivity:64,370 centiBarrer N2 Productivity:4,480 centiBarrer C2 Productivity:139,300 centiBarrer He/N2 Selectivity: 14 C02/N2 Selectivity: 31 The above films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig, 25C. The results are reported below:
2 Productivity: 14,900 centiBarrer 2/N2 Selectivity: 3.6 Example 15 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (27.04g, 0.18 mol) and 1,3-phenylene diamine (2.16g, 0.02 mol) in dimethylsulfoxide (600 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzofuranedione (88.8g, 0.20 mol, added in four portions, last portion washed in with 150 ml dimethyl-sulfoxide) and the resulting yellow solution was stirred at 50C overnight. A solution of acetic .
-. :

:: , : ~; .

-.: , : .
1' . - ., anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added to the reaction solution. After stirring at 50C for 2 hours, the reaction solution was precipitated in methanol. The resulting white solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at 100-C for 4 hours and at 240C for 3 hours to give 109.3g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 85C with a 15 mil (3.8 X
10~4m) knife gap. The films were dried on the plate at 8SC for 30 minutes, cooled to room temperature and dried in a vacuum oven at room temperature, and then dried in in a vacuum oven overnight. The films were stripped off the plates and dried in a vacuum oven at 120C for four hours. The films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 kPa), 25C. Results are reported below:
2 Productivity: 8,300 centiBarrer 2/N2 Selectivity: 3.9 The above films were consecutively tested from pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity: 47,800 centiBarrer N2 Productivity: 3,380 centiBarrer C2 Productivity: 74,000 centiBarrer He/N2 Selectivity: 13 CO2/N2 Selectivity: 19 and .

.

1321~88 He Productivity:32,530 centiBarrer N2 Productivity:2,000 centiBarrer C2 Productivity:113,200 centiBarrer He/N2 Selectivity: 16 C02/N2 Selectivity: S7 Exam~le 16 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (25.8g, 0.17 mol) and 1,3-phenylene diamine (3.1g, 0.03 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)-ethylidene-bis-1,3-isobenzofuranedione (88.8g, 0.20 mol, added in four portions, last portion washed in with 150 ml N-methyl pyrrolidone). After stirring overnight at 50 C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting reaction solution was stirred at 50C for 2 hours. The yellow reaction solution was precipitated in methanol and the resulting white solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at lOO C for 3 hours and at 200-C for 3 hours to give 97.0g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90 C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90-C for 25 minutes, cooled to room temperature and then dried in a vacuum oven at room temperature overnight. The films were then stripped off the plate and further dried in a vacuum oven at 120'C for four hours. The films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide .

1321~8~

permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity: 7,240 centiBarrer N2 Productivity: 154 centiBarrer C2 Productivity: 10,541 centiBarrer He/N2 Selectivity: 47 C02/N2 Selectivity: 69 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
H2 Productivity: 5,780 centiBarrer H2/CH4 Selectivity: 49 Example 17 15 To a SO-C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (24.04, 0.16 mol) and 1,3-phenylene diamine (4.33g, 0.04 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)-ethylidene-bis-1,3-isobenzofuranedione (88.8g, 0.20 mol, added in four portions, last portion washed in with 150 ml ~-methyl pyrrolidone). After stirring overnight at 50-C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting yellow reaction solution was stirred at 50C for 2 hours.
The reaction solution was precipitated in methanol and the resulting white solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours and at 240C for 4 hours to give 106.5g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in _-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90C with a 15 mil (3.8 x ' 13216~8 10~4m) knife gap. The films were dried on the plate at 90C for 30 minutes, cooled to room temperature and then dried in a vacuum oven overnight. The films were then stripped off the plate and further dried in a vacuum oven at 120~C for four hours. The films were then tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
2 Productivity: 4,300 centiBarrer 2/N2 Selectivity: 4.1 The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported 15 below:
He Productivity:22,300 centiBarrer N2 Productivity:1,080 centiBarrer C2 Productivity:67,000 centiBarrer He/N2 Selectivity: 21 C~2/N2 Selectivity: 62 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
H2 Productivity: 14,600 centiBarrer H2/CH4 Selectivity: 23 Example 18 To a 50C stirred solution of 2,4,6-tri-methyl-1,3-phenylene diamine (15.04, 0.10 mol) and 1,3-phenylene diamine (10.8g, 0.10 mol) in N-methyl pyrrolidone (350 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bi-s-1,3-isobenzofuranedione (88.8g, 0.20 mol, added in four portions, last portion washed in with 150 ml N-methyl pyrrolidone). After stirring overnight at 50C, a solution of acetic anhydride (75.8 ml, 0.80 ..

.

mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the resulting reaction solution was stirred at 50C for 2 hours. The slightly yellow reaction solution was precipitated in methanol and the resulting white solid collected by filtration, washed with methanol and dried in a vacuum oven at room temperature overnight, at 100DC for 3 hours and at 220C for 4 hours. The product was a white solid (106.8g).
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90 C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature and then dried in a vacuum oven at room temperature overnight. The films were then stripped off the plate and further dried in a vacuum oven at 120C for four hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
He Productivity: 8,300 centiBarrer N2 Productivity: 775 centiBarrer C2 Productivity: 25,000 centiBarrer He~N2 Selectivity: 11 CO2/N2 Selectivity: 32 The above films were tested for mixed gas H2/CH4 (50/50) (mole) permeabilities at 400 psig (2.75 kPa), 25C. Results are reported below:
H2 Productivity: 17,840 centi3arrer H2/CH4 Selectivity: 15 The above films were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 kPa), 25C. Results are reported below:

, ,. :

132~1~88 2 Productivity: 42,200 centiBarrer 2/N2 Selectivity: 3.9 Example 19 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (27.04, 0.18 mol) and 4-aminophenyl sulfone (4.97g, 0.02 mol) in dimethylsulfoxide (600 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-1 (trifluoromethyl)ethylidene-bis-1,3-isobenzo-furanedione (88.8g, 0.20 mol, added in five portions, last portion washed in with 150 ml dimethyl sulfoxide). After stirring overnight at 50 C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and 1 triethylamine (112.9 ml, 0.81 mol) was rapidly added.
The yellow reaction solution was stirred at 50C for 2 hours and then precipitated in methanol. The resulting white solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at 100C for 3 hours and at 250C for 4 hours to give lO9.0g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in ~-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 85-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 85-C for 25 minutes, cooled to room temperature and then dried in a vacuum oven at room temperature overnight. The films were then stripped off the plate and further dried in a vacuum oven at 120-C for four hours. The films were then consecutively tested for mixed gas 2/N2 (21J79) (mole) permeabilities at 300 psig (2 kPa), 25-C. Results are reported below:
2 Productivity:7,800 centiBarrer 2/N2 Selectivity: 3.9 .

.
- ~: :

The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25C. Results are reported 5 below:
He Productivity:26,300 centiBarrer N2 Productivity:1,180 centiBarrer C2 Productivity:126,700 centiBarrer He/N2 Selectivity: 22 CO2/N2 Selectivity: 107 Example 20 To a 50C stirred solution of 2,4,6-trimethyl-1,3-phenylene diamine (27.04, 0.18 mol) and 1,5-naphthalene diamine (3.16g, 0.02 mol) in dimethylsulfoxide (600 ml) under an inert atmosphere was portionwise added 5,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzo-furanedione (88.8g, 0.20 mol, added in six portions, last portion washed in with 150 ml dimethyl sulfoxide). After stirring overnight at 50C, a solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added to form a golden solution. The reaction solution was stirred at 50~C for 2 hours and then precipitated in methanol. The resulting off-white soli~ was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at 100C
for 4 hours and at 240C for 3 hours to give 104.6g product.
3 Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 85-C with a 15 mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 85C for 25 minutes, cooled to room temperature and then dried in a vacuum oven at room temperature ~ 321~

overnight. The films were then stripped off the plate and further dried in a vacuum oven at 120DC for four hours. The films were then tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 300 psig (2 kPa), 25 D C. Results are reported below:
2 Productivity: 10,000 centiBarrer 2/N2 Selectivity: 3.6 and 2 Productivity: 11,000 centiBarrer 2/N2 Selectivity: 3.5 The above films were consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25-C. Results are reported below-He Productivity: 34,000 centiBarrer N2 Productivity: 2,450 centiBarrer C2 Productivity: 125,100 centiBarrer He/N2 Selectivity: 14 C02/N2 Selectivity: 51 Example 21 To a 50C stirred solution of 2,3,5,6-tetra-methyl-1,4-phenylene diamine (29.57g, 0.18 mol) in dimethylsulfoxide (600 ml) under an inert atmosphere at room temperature was added S,5'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene-bis-1,3-isobenzo-furanedione (88.8g, 0.20 mol) and the resulting solution was stirred at 50C for 6 hours. The reaction solution was cooled to room temperature and 1,5-naphthalene diamine (3.16g, 0.02 mol) was added and the resulting reaction solution stirred at room temperature overnight. A solution of acetic anhydride (75.8 ml, 0.80 mol) and triethylamine (112.9 ml, 0.81 mol) was rapidly added and the yellow reaction solution stirred for 2 hours. The reaction solution was precipitated in methanol. The resulting white ., . ~ , ~ ~ .

solid was collected by filtration, washed with methanol, and dried in a vacuum oven at room temperature overnight, at 100 for 3 hours, and at 200C for 4 hours to give 112.3g product.
Films of the above polymer were cast from a 15% polymer solution (based on weight) in N-methyl pyrrolidone onto a glass plate treated with Du Pont TEFLON~ dry lubricant at 90-C with a 15 mil 1 (3.8 x lo-4m) knife gap. The films were dried on the plate at 90C for 25 minutes, cooled to room temperature and dried in a vacuum oven at room temperature overnight. The films were stripped off the plate and further dried in a vacuum oven at 120~C
for 4 hours. The films were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 400 psig (2.75 kPa), 25-C. Results are reported below:
He Productivity: 35,630 centiBarrer N2 Productivity: 2,380 centiBarrer C2 Productivity: 98,900 centiBarrer He/N2 Selectivity: 15 CO2/N2 Selectivity: 42 Example 22 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 1 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50-C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~C
for 0.5 minutes and then precipitated in deionized water for 24 hours, they were placed in isopropanol.
The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD 184 solution in FREON 113 132168~

(1,1,2-trichloro-1,2,2-trifluoroethane) (weight/volume) and dried in a vaccum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity:480 GPU
N2 Productivity:41 GPU
C2 Productivity:1,122 GPU
He/N2 Selectivity: 12 C02/N2 Selectivity: 27 A Gas Permeation Unit (GPU) is the cubic centimeters of gas passed by the membrane at standard temperature and pressure times 10-6 divided by the area of the membrane in square centimeters times the time in seconds times the pressure on the side of the membrane in cm Hg, i.e., GPU = 10-6 x cm3 (STP) cm2-sec(cm Hg) Dow Corning SYLGARD~ 184 is an elastomeric silicone material which thermally cures to a crosslinked silicone material. In the present usage it serves as a sealing agent for membrane imperfections.
The above asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 23C. The results are reported below:
2 Productivity: 170 GPU
2/N2 Selectivity: 3.8 Exam~le 23 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 1 in a ~: . :

. ~ :

N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
for 1.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity:473 GPU
N2 Productivity:46 GPU
C2 Productivity:1,122 GPU
He/N2 Selectivity: 10 CO2/N2 Selectivity: 24 Exam~le 24 Asymmetric membranes were cast from a 20~ by weight solution of the polymer of Example 1 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
for 2.0 minutes and then precipitated in deionized wate~. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 2S~C. The results are reported below:
He Productivity:352 GPU
N2 Productivity:35 GPU
C2 Productivity:873 GPU
He/N2 Selectivity: 10 CO2/N2 Selectivity: 25 Example 25 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example l in a _-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50c for 3.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25-C. The results are reported below:
He Productivity:700 GPU
N2 Productivity:80 GPU
He/N2 Selectivity: 9 The above asymmetric membranes were treated with a 10%
SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in a vacuum even at 50-C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide : - - .-. : :.

, , 132~688 permeabilities at 100 psig (0.69 kPa), 25C. Results are reported below:
He Productivity:340 GPU
N2 Productivity:34 GPU
C2 Productivity:976 GPU
He/N2 Selectivity: 10 CO2/N2 Selectivity: 29 Example 26 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 3 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
for 1.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON0 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25-C. The results are reported below:
He Productivity: 297 GPU
N2 Productivity: 17.3 GPU
C2 Productivity: 629 GPU
He/N2 Selectivity: 17 CO2/N2 Selectivity: 36 The above asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25C. Results are reported below:

2 Productivity: 74 GPU
2/N2 Selectivity: 3.9 Example 27 Asymmetric membranes were cast from a 20~ by weight solution of the polymer of Example 4 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
1 for 2.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD0 184 solution in FREON0 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig ~0.69 kPa), 25C. The results are reported below:
He Productivity:330 GPU
N2 Productivity:23 GPU
25 C2 Productivity:526 GPU
He/N2 Selectivity:14 CO2/N2 Selectivity: 23 The above asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25-C. Results are reported below:
2 Productivity: 86 GPU
2/N2 Selectivity: 3.3 Exam~le 28 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 4 in a N-methyl pyrrolidone:water (97:3) solution (weight) .: :~.

13216~8 onto a glass plate at 50C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
for 3.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25'C. The results are reported below:
He Productivity:490 GPU
N2 Productivity:46 GPU
He/N2 Selectivity: 11 The above asymmetric membranes were treated with a 10%
SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in a vaccum oven at 50DC for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25-C. Results are reported below:
He Productivity:292 GPU
N2 Productivity:19 GPU
C2 Productivity:510 GPU
He/N2 Selectivity:15 C02/N2 Selectivity: 26 The above asymmetric membranes were tested for mixed gas 2/N2 (21/79) tmole) permeabilities at 100 psig (0.69 kPa), 25-C. Results are reported below:
2 Productivity: 62 GPU
` 2/N2 Selectivity: 3.0 Example 29 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 5 in a N-methyl pyrrolidone:water ~97:3) solution (weight) onto a glass plate at 50DC with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C
for 0.5 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the~membranes were dried in a vacuum oven at room temperature overnight. The asymmetric membranes were tested for pure gas helium and nitrogen permeabilities at 100 psig (0.69 kPa), 25 C. The results are reported below:
He Productivity: 502 GPU
N2 Productivity: 37 GPU
He/N2 Selectivity: 14 These last asymmetric membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in a vaccum oven at 50-C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig, 25-C.
Results are reported below:
He Productivity:300 GPU
N2 Productivity:18 GPU
3 C2 Productivity:440 GPU
He/N2 Selectivity: 17 CO2/N2 Selectivity: 25 These treated asymmetric membranes above were also tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25-C. Results are reported below:

,~.

:

2 Productivity: 140 GPU
2/N2 Selectivity: 4.1 Example 30 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 5 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~C
for 1.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50~C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity:307 GPU
N2 Productivity:22.4 GPU
25 C2 Productivity:502 GPU
He~N2 Selectivity: 14 CO2/N2 Selectivity: 22 Example 31 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 5 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50-C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~C
for 2.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were ~:
.

1321~88 placed in isopropanol. The isopropanol was replaced ~ith fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD0 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity: 223 GPU
N2 Productivity:14.6 GPU
C2 Productivity: 56~ GPU
He/N2 Selectivity: 15 CO2/N2 Selectivity:39 Example 32 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 5 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50OC
for 3.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weightfvolume) and dried in vacuum oven at 50-C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 2S-C. The results are reported below:

:
:~ , , ~ ., .

132~688 He Productivity:215 GPU
N2 Productivity:11.3 GPU
C2 Productivity:483 GPU
He/N2 Selectivity: 19 C02/N2 Selectivity: 43 Example 33 Asymmetric membranes were cast from a 20~ by weight solution of the polymer of Example 6 in a N,N-dimethyl formamide:formamide (95:S) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50C for 2.0 minutes and then precipitated in water. After the resulting white asymmetric membranes had sat in slowly running warm water for 2 hours, they were placed in isopropanol for 1 hour. The membranes were dried in a vacuum oven overnight. The asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25DC.
The results are reported below:
2 Productivity: 300 GPU
2/N2 Selectivity: 3.2 Example 34 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 13 in a _-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50 C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~c for 0.5 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The asymmetric membranes were then consecutively tested for pure gas `J

13216~8 helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity:293 GPU
N2 Productivity:22 GPU
C2 Productivity:416 GPU
He/N2 Selectivity: 13 CO2/N2 Selectivity: 19 The above asymmetric membranes were treated with a 10%
SYLGARD~ 184 solution in FREON 113 (weight/volume) and dried in a vaccum oven at 50C for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide 15 permeabilities at 100 psig (0.69 kPa), 25DC. Results are reported below:
He Productivity:237 GPU
N2 Productivity: 15.6 GPU
C2 Productivity: 438 GPU
He/N2 Selectivity: 15 CO2/N2 Selectivity: 28 The above treated asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25-C. Results are reported below:
2 Productivity: 68 GPU
2/N2 Selectivity: 3.8 Example 35 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 19 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50-C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~C
for 0.5 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced - 132168~-with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes we:re dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD~ 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50c for 16 hours. The asymmetric membranes were then consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity:493 GPU
N2 Productivity:21.8 GPU
C2 Productivity:756 GPU
He/N2 Selectivity: 23 15 C02/N2 Selectivity: 35 The above treated asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig (0.69 kPa), 25 C. Results are reported below:
2 Productivity: 105 GPU
2/N2 Selectivity: 4.5 Example 36 Asymmetric membranes were cast from a 20% by weight solution of the polymer of Example 19 in a N-methyl pyrrolidone:water (97:3) solution (weight) onto a glass plate at 50-C with a 15-mil (3.8 x 10~4m) knife gap. The films were dried on the plate at 50~C
for 1.0 minutes and then precipitated in deionized water. After the resulting white asymmetric membranes had sat in deionized water for 24 hours, they were placed in isopropanol. The isopropanol was replaced with fresh isopropanol after 6 hours. After 24 hours in isopropanol the membranes were dried in a vacuum oven at room temperature overnight. The membranes were treated with a 10% SYLGARD 184 solution in FREON~ 113 (weight/volume) and dried in vacuum oven at 50C for 16 hours. The asymmetric membranes were then : 49 consecutively tested for pure gas helium, nitrogen, and carbon dioxide permeabilities at 100 psig (0.69 kPa), 25C. The results are reported below:
He Productivity: 500 GPU
N2 Productivity: 25.7 GPU
C2 Productivity: 802 GPU
He/N2 Selectivity: 20 C02/N2 Selectivity: 31 10 The above asymmetric membranes were tested for mixed gas 2/N2 (21/79) (mole) permeabilities at 100 psig, (0.69 kPa), 25C. Results are reported below:
2 Productivity: llO GPU
2/N2 Selectivity: 3.9 and 2 Productivity: 118 GPU
2/N2 Selectivity: 3.9 .
- .

, ~, .

:

Claims (7)

1. A gas separation membrane formed of an aromatic polyimide comprising units of the formula where -Ar- is or mixtures thereof, -R- is , , or mixtures thereof, -Ar'- is , , or mixtures thereof, ?? is , or mixtures thereof, and -R"- is , -O- , -S- ,, , , where n = 0 to 4, alkylene radicals of 1 to 3 carbon atoms or mixtures thereof, -X, -X1, -X2, and -X3 are independently alkyl groups having 1 to 6 carbon atoms preferably methyl or ethyl, or aromatic groups of 6 to 13 carbon atoms, Z is -H, -X, -X1, -X2, or -X3 W is 5% to 100%
Q is 5% to 100%
Y is 100% minus W
V is 100% minus V
Y plus V is at least 5%.
2. The membrane of Claim 1 wherein Y plus V
is 10 to 50%.
3. The membrane of Claim 2 wherein -X, -X1, -X2, or -X3 are -CH3 or -C2H5.
4. The membrane of Claim 3 wherein Y is 0.
5. A process of separating two or more gases using the permselective membrane of Claim 1.
6. The process of Claim 5 wherein -X, -X1, -X2, or -X3 are -CH3 or -C2H5.
7. The process of Claim 6 wherein R is , or mixtures thereof.
CA000549790A 1986-10-27 1987-10-20 Polyimide gas separation membranes Expired - Fee Related CA1321688C (en)