CA2067806C - Gypsum-containing fire-resistant structural fiberboard - Google Patents

Abstract

An isometric view of fire door construction (60) comprising gypsum fiberboard panels (62) having a density of at leat 60 lbs/ft3, a flexural strength of at least 30 lbs (1/2) inch thick material), and a screw holding capacity of at least 400 lbs. Said panel has a composition comprising 65 wt % to 90 wt % gypsum dihydrate, 7 wt % to 30 wt % paper fiber, and a performance booster selected from inorganic fiber, clay, vermiculite, and binder polymer. The honeycomb structure (66) is surrounded at the door perimeter by gypsum fiberboard edge banding (65) with a preferred density of 65 lbs/ft3 and a screw holding capacity of at least 600 lbs/ft3.

Description

~WO91/057~ 2 ~ 6 7 ~ ~ 6 PCT/US90/0s867 GYP8UM-CONTAINING FIRE-R~8I8TANT
_-.~u~.uKAL ~ k~Pn Field of the Invention This invention relates generally to fire-resistant structures, and more particularly, to mineral-containing compositions for providing superior fire resistance and high strength constructions.

Background of the Invention Fire-resistant boards and panels, as used in residential, commercial, and industrial applications, are typically employed to provide fire protection between different zones of a structure, and particularly to isolate high fire risk areas of a building from the remainder of the structure, such as the garage from the living quarters of a dwelling. They may be incorporated into fire doors, which often include facings on the two major planar surfaces and a core which may be solid or include some hollow space.
Fire doors usually are not capable of indefinitely withstanding the high temperature conditions of a fire, but rather, are designed to maintain the integrity of the fire wall for a limited time to permit the occllpAnts of a building to escape and to delay the spread of the fire until fire control equipment can be brought to the scene. Various tests have been devised for determining the reliability of fire doors which are based, in part, on such factors as the time ~ 206'78 O6 that a given door can withstand a certain temperature while maintaining its integrity. One such test is the ASTM E-152 fire test, which requires a door to maintain its integrity for periods ranging up to 1.5 hours while withstanding progressively higher temperatures within the range of 1750~F to 1800~F and the 5 erosive effects of a high pressure fire hose at the conclusion of the fire exposure.
Considerations in fire door design, in addition to retarding the advance of a fire, include the cost of raw materials and the cost of fabrication.
Furthermore, the weight of the door is important, both from the standpoint of ease in handling and the cost of transportation. The strength of the door is also a 10 significant factor, since fire doors must pass the previously noted fire and water stream test as well as have the requisite structural strength to withstand normal use and abuse. Finally, fire doors must provide support and split-resistance in loc~li7e.1 areas where hinges, knobs, and locks are mounted.
While in the main, commercial fire-resistant materials, such as those described in Hashimoto et al., U.S. Patent No. 4,174,230, Vogt, U.S. Patent No. 4,840,688, Porter et al., U.S. Patent No. 2,076,349, and Lehnert et al., U.S.
Patent No. 4,748,771 are known to possess certain mechanical and fire-resistant properties which are acceptable in fire doors, they often require expensive, heavy, potentially hazardous additives, and relatively complicated constructions to 20 achieve those properties. Thus, there is a need for a composition and structure which includes safe and inexpensive components from which superior fire doors and other structural panels can be made.

~_ 2a 2 0 5 7 8 ~ 6 Summary of the Invention This invention provides fire-resistant structures suitable for use in fire door applications. The structures have at least a 20 minute ASTM E-152 fire5 test rating and include a gypsum fiberboard composition having a density of at ~ W O 91/05744 2 0 6 7 8 ~ 6 PC~r/US90/05867 least about 60 lbs/ft3, a flexural strength of at least 30 lbs (1/2 inch thick material), and a screw-holding capacity of at least about 400 lbs. The composition of this structure contains a substantially uniform distribution of solids including about 65 wt.% to about 90 wt.% set gypsum dihydrate, about 7 wt.~6 to about 30 wt.% paper fiber, and about 1.5 wt.%
to about 35 wt.% of one or more performance boosters selected from inorganic fiber, clay, vermiculite, and binder polymer.
This composition is prepared with a quantity of water substantially in excess of that required to completely hydrate the gypsum-containing starting ingredient.
Accordingly, practical and economical fire-resistant structures are provided which have excellent fire-resistance characteristics, as well as important and desirable environmental benefits. The gypsum fiberboard of this invention is both safe and effective for use in structural elements subject to high temperatures. It can be produced relatively in~Ypencively and can be incorporated into fire doors, beam and girder insulation and fire walls without excessive weight additions. The gypsum fiberboards of the present invention can include scrap or waste materials, which can provide further cost incentives to manufacturers, as well as satisfy a current need for the recycling of building debris and flue slag. -In another aspect of this invention, gypsum fiberboards are employed in a variety of economical constructions for obtaining multiple fire ratings. For instance, fire door designs are provided for obtaining 45 minute, 60 minute, and 90 minute ASTM E-152 fire test labels.
The disclosed gypsum fiberboards can be separated by spacing means, such as paper-containing honeycomb-like structures, for uniformly supporting the fiberboards and for producing an overall light weight core. This invention therefore not only provides economical fire doors, but also a fiexibie manufacturing method which is capable of producing multiple layers of preferred fiberboard formulations in varying thicknesses for different fire rating requirements.

WO91/057~ 2 0 6 7 8 0 6 PCT/US90/05867 The fiberboard structures of this invention preferably do not include paper facing sheets, such as those normally employed with ordinary paper-surfaced gypsum wallboard. In wallboard composites, the paper facings of two or more wallboards are usually adhesively bonded together for laminating the different components together. Paper facing, however, is very susceptible to humidity changes in the atmosphere, which can adversely affect the laminated components. Additionally, during a fire, water driven off from the chemically combined gypsum, weakens the paper, causing delamination and premature failure. Paper facing is also known to char away, leaving little, if any, adhesive bonds between the layers of a composite member.
Since the bonded fiberboards of this invention lS preferably do not have paper facing sheets, they are more stable throughout a wide range of changing humidities, making them attractive in even the most damp applications. Moreover, the intimate contact between the paper fibers and set gypsum in the composition of this invention can withstand a far higher temperature before evidencing deterioration of the adhesive bonds between the gypsum fiberboard layers than is the case for delamination of adhesively secured wallboards.
The unfaced gypsum fiberboards of this invention also provide a unique advantage over pressed perlite cores since less glue is required during lay up due to the lower surface porosity of the fiberboard structure. Smaller glue requirements lower manufacturing costs and provide a more economical fire door and other structures.
A further advantage of this invention is the simplification and structural improvement of the disclosed edge hAn~ing versus tripartite and other laminated systems of the prior art. The gypsum fiberboard structures and doors of this invention do not require any particular edge system.
Th~ir composit.Gn alone can provide superior split resistance and screw-holding capacity. These fiberboards can also be readily machined for providing relief designs, such as those found in panel doors.

~WO9l/057~ 2 0 6 ~ ~ O fi PCT/US90/OS867 Finally, the fiberboard compositions of this invention provide excellent fire protection to structural members, such as steel and wood beams. This invention includes structures for substantially containing such beams within a fiberboard casing to protect them from flames and accelerated damage during a fire. The casings are easy to apply and are environmentally safe, making them an attractive alternative to asbestos.

Brief DescriDtion of the Drawinqs The accompanying drawings illustrate preferred embodiments of the invention as well as other information pertinent to the disclosure, and in which:
FIG. 1: is a flow diagram which illustrates the process of this invention by which gypsum-containing fiberboards are made;
FIG. 2: is a graphical illustration of the effect of one of the components in a preferred fiberboard composition of this invention on one of the processing steps;
FIG. 3: is a graphical illustration of the flexural strength of fiberboards of this invention as a function of the density of the material;
FIG. 4: is a graphical illustration of the screw-holding capacity of fiberboards of this invention as a function of the density of the material;
FIG. 5: is a top view of one of the preferred fire doors of this invention;
FIG. 6: is a front cross-sectional view taken along line 6-6 of the fire door of FIG. 5;
FIG. 7: is a front elevational view of another fire door within the scope of this invention;
FIG. 8: is an isometric view of a corner of the fire door of FIG. 7 with portions broken away; and - FIG. 9: is an isometric view of prererred steel beam fire protection structure with sections peeled away to reveal its integral parts.

WO91/057~ 2 0 6 ~ 8 0 6 PCT/US90/05867 Detailed Description of the Invention Fire-resistant structures, such as fire doors and structural beam insulators, are provided by this invention which include one or more gypsum fiberboards having a density of at least about 60 lbs/ft3, a flexural strength of at least about 30 lbs (1/2 inch thick material), and a screw-holding capacity, defined below, of at least about 400 lbs. These fiberboards contain about 65 wt.% to about 90 wt.% set gypsum dihydrate and about 7 wt.% to about 30 wt.% paper fiber and about 1.5 wt.% to about 35 wt.% performance booster. When incorporated into structures, the fiberboards of this invention, whether they be in the form of panels, boards, skins, cores, or other structural members, are designed to provide at least a 20 minute ASTM E-152 fire test rating.
In a more specific embodiment of this invention, a 20 minute fire door is provided which includes at least a pair of unfaced gypsum fiberboard panels containing a composition comprising about 75 wt.% to about 90 wt.% set gypsum dihydrate, about 10 wt.% to about 17 wt.% paper fiber, and about 1.5 wt.% to about 35 wt.% of a performance booster selected from inorganic fiber, clay, vermiculite, and binder polymer. The gypsum fiberboard panels of this embodiment have a flexural strength of at least about 30 lbs (1/2 inch thick material), a screw-holding capacity of at least 400 lbs, and a wood-like veneer disposed substantially over the core. Other fire-resistant structures are provided by this invention which will pass at least 45, 60, and 90 minute ASTM E-152 fire tests.

Fiberboard Construction The gypsum-containing fiberboard layers of this invention should be fire resistant yet po~s~C~ a high degree of structural integrity. They must provide superior screw-holding for attached door hardware and have exceptional overall strength.
The preferred fiberboard panels of this invention have a density of at least about 60 lbs/ft3, a flexural 7 2 0 6 7 8 n 6 strength of at least 30 lbs (1/2 inch thick material), and a screw-holding capacity, measured as defined hereinafter, of at least about 400 lbs. The fiberboard panels do not require a paper facing, which is desirably absent to promote fire and water resistance properties. The composition of the preferred fiberboard panels is a 5 uniform distribution of solids, which includes by weight, about 65% to about 90% set gypsum dihydrate, about 7% to about 30% cellulosic fiber, and prererably about 1.5%
to about 35% of one or more performance boosters selected from inorganic fiber, clay, vermiculite, and binder polymer.
One of the essential constituents of the gypsum containing fiberboard 10 panels of the present invention is calcium sulfate dihydrate. This constituent is derived from the hydration of any form of calcium sulfate which is preferably in non-fibrous form and which is capable of reacting with water to form set gypsum, that is, calcium sulfate dihydrate. Thus, the calcium sulfate can be in anhydrous form or in the hemihydrate form. It is believed that the hemihydrate form of 15 calcium sulfate will be used most widely. Of the "alpha" and "beta" forms of the hemihydrate, use of the latter is preferred. The hemihydrate can be produced from the naturally-occurring gypsum mineral by heating, or calcining, the dihydrate.
For many applications, it is not important to inquire into the crystalline form of the hemihydrate; however, with respect to fiberboard panels of 20 this invention, a preference is made. It is known that calcium sulfate hemihydrate can exist in two different crystalline forms, namely a non-fibrous form and a fibrous form, for example, elongated needles, such as the fibrous alpha-calcium sulfate C

~_ 7a 2~ 678 n 6 hemihydrate disclosed in U.S. Patent No. 4,239,716. In the practice of this invention, there is used a non-fibrous form of calcium sulfate capable of reacting with water to form set gypsum. It should be understood, however, that a minor amount of a 5 fibrous form of gypsum can be used as an optional constituent.

W O 91/05744 P(~r/US90/05867 ~_ 2~67~

As mentioned above, one of the advantages of the present invention is that waste-type materials can be used in fabricating the fiberboard panels. For example, there can be used as the source of the calcium sulfate the material known as "desulfurized by-product gypsum" which is produced by the desulfurization of flue gas. Another example of a waste- or scrap-type material that can be used in the practice of the present invention is scrap gypsum wallboard, which can be used as a source of both calcium sulfate and the paper constituent of the fiberboard. For this purpose, scrap paper-faced gypsum wallboard can be ground into suitably small particles which are procefiFe~ in water under pressure and in the presence of a crystal modifier to form non-fibrous calcium sulfate hemihydrate. Scrap gypsum wallboard can also be transformed into a suitable material for use in the practice of the present invention by grinding and calcining it at atmospheric pressure. Sufficient water can be used to form the desired pulp-type material from which the-product is conveniently made. This invention can employ any of the above-disclosed individual sources of calcium sulfate, but a mixture of the different sources of calcium sulfate can also be used.
In the use of an aqueous dispersion to make the gypsum-containing fiberboard panels the non-fibrous calcium sulfate generally will comprise between about 53% and about 78% by weight of the total solids, preferably between about 55% and about 70% by weight, ~epen~ing upon the specific application for the resultant building material. For example, in a building board to be employed as edge hAn~ing in a fire door, the non-fibrous calcium sulfate content of the dispersion may be in the range of about 54% to about 62% by weight of the solids. On the other hand, in a building panel to be used as the facing on a fire door or as a girder insulation panel, the calcium sulfate content of the dispersion may lie between about 60% and about 80~ by weight of the solids.
The gypsum dihydrate content of the preferred fiberboard panels of this invention will be approximately ~, W O 91/05744 2 ~ ~ 7 ~ ~ ~ PC~r/US90/05867 18.5% greater than the non-fibrous calcium sulfate content of the compositions from which they are made, the difference representing the added water of hydration in the set gypsum dihydrate. That is, by weight, the set gypsum will preferably comprise between about 65% and about 90%, preferably between about 70% and about 85% of the overall set composition. In a building board for use as edge banding in a fire door, the set gypsum dihydrate may comprise between about 68% and about 78%
by weight. In a building panel intended for use in fire door facings or as a girder or beam insulation panel, the set gypsum may comprise between about 75% and about 90% by weight.
The compositions of the preferred fiberboard panels of this invention also employ a substantial amount of cellulosic fiber. Cellulosic fiber includes the fibrous component of plants, such as cotton, linen, and flax, for example. Among the various sources of cellulosic fiber, paper stock is conveniently employed. That is, the solid ~omponent involved in each of the aforesaid aspects of the invention preferably includes by weight about 7% to about 30% paper fiber, preferably about 7% to about 24% paper fiber, more preferably between about 10% and about 17%. Applicant has determined that paper fiber concentrations greater than about 24 wt.% render the fiberboard papery and detract from the overall gypsum properties. It has further been noted that when the concentration of paper fails significantly below about 7%, screw-holding capacity is diminished, necessitating complicated composites for achieving sufficient screw-holding ability for use as edge banding in door applications, see Lehnert et al., U.S. Patent No. 4,748,771, which discloses a wood-polymer-gypsum fiberboard composite for achieving 500 lbs screw-holding capacity, wherein the fiberboard includes paper fibers up to about 1.3 wt.%.
Building materials intended for use in various - specific products may contain somewhat dirferent amounts of paper fiber. For example, a building board int~n~ for use as edge banding in a fire door may contain about 15% paper fiber by weight, while a panel intended to be used as fire 2 ~ 6 7 8 n ~

door facing may contain somewhat less, e.g., about 12% or 13%. The presence of the paper fiber makes it possible to produce building materials having good physical characteristics such as flexural strength, screw and nail holding ability, and surface hardness without having any separate surfacing membrane such as the paper facing 5 on conventional gypsum wallboard.
The paper fiber can be derived from either virgin paper stock, or previously used, waste paper stock can be employed. The source of the paper can be wood, cotton or linen rags, straw, etc., the origin or history of the paper not being important factors. The paper may be a product of the sulfite process, the sulfate 10 (Kraft paper) process, or other processes. Among the types of paper stock that have been successfully employed are virgin and brown Kraft papers, and especially, newsprint. Waste newspaper provides very satisfactorily results, is inexpensive, and its use helps to overcome an environmental pollution problem. And, as mentioned hereinabove, the source of the paper stock can include the paper of ground paper-15 faced gypsum wallboard.
Fiberboard panels and boards within the scope of this inventiondesirably and preferably include one or more performance boosting additives, their specific nature depending to some extent on the intended utility of the final product.
In almost every case, there will be desirably used one or more defoaming agents, 20 dispersants, and accelerators, ingredients which are well known in the art and are employed at low concentration levels, generally each at less than about 1% by weight of the solids. In the aggregate, the performance booster generally will ~~ 10a 2 0 6 7 8 0 6 comprise about 1.5% to about 35% by weight of the solids and will preferably be selected from inorganic fiber, clay, vermiculite, and binder polymer.
Inorganic fiber, as that term is employed herein, includes glass textile fiber and mineral wool. These latter terms are defined in U.S. Patent No. 4,557,973.
Briefly, the term "mineral wool" means glass or other mineral fibers C

2 0 ~
WO9l/057~ PCT/US90/05867 prepared by attenuating a melt of glass, basalt, blast furnace slag or other vitreous mineral composition from the face of a heated centrifugal rotor or the like. This process is in contrast to that used to produce textile fibers, where the melt is drawn through an orifice. An especially useful and readily available type of mineral wool is glass wool as found in glass wool insulation material. Glass textile fiber and glass wool, jointly or severally, are referred to herein as "siliceous fiber." As employed in this invention, the glass textile fiber generally will be chopped, e.g., the fibers may be about 1/2 inch long.
The fiberboards of this invention preferably include siliceous fiber. Siliceous fiber improves the fire resistance of the building materials and other products of this invention, apparently by decreasing the tendency of the gypsum construction to crack under thermal stress. The siliceous fiber preferably comprises up to about 7% by weight and may include glass textile fiber and, in addition, glass wool, d~pon~;ng upon the specific product. For example, a building board intended for use as edge banding in a fire door preferably inciudes up to about 7% by weight glass textile fiber, most preferably about 2% by weight glass textile fiber, glass wool being unnececs~ry. However, a building panel intended to be used as facing on a fire door preferably 2S includes about 0.8% to about 2% siliceous fiber, most preferably a combination of about 0.4% chopped glass textile fiber and about 0.5% to about 1.5% glass wool by weight.
The performance booster may also include either clay or vermiculite, or both, especially if the intended board or panel requires excellent fire resistance. Both of these materials may be present in amounts up to about 15.0% by weight, preferably up to about 6%, and more preferably about 3% to about 4% by weight of the solids. The clay to be - employed will generally be kaolin clay, which is effective to control the shrinkage of the gypsum-containing construction under extreme heat, for example, ASP 70 Kaolin clay sold by Minerals and Chemicals Philip Corporation. The vermiculite WO9l/0~7~ 2 0 ~ 7 8 0 ~ PCT/US90/05867 should be raw, or unexpanded vermiculite, which swells when heated, helping to control shrinkage of the construction and possible cracking. The requirement for the presence of these materials depends somewhat on the int~n~e~ use for the final product and may not be n~ce~s~ry in, e.g., a panel intended for use as facings in a fire door.
The composition of the preferred fiberboards of this invention, as well as the construction techniques for adhesively bonding the fiberboards together to form various structures, may also employ binder polymer. The binder polymer affects the physical properties of the fiberboard layers, especially their flexural strength, and also permits good fastener retention at lower density. Furthermore, the binder polymer improves the surface characteristics of the board, panel, door, or insulating member such as smoothing the surface and making it easier to finish.
The binder polymer, when present, may comprise up to about 15% by weight of the solids, but preferably about 1% to about 3~ by weight. A number of different polymeric materials may be employed as binder polymer, including homopolymers, such as poly(vinyl acetate) and polyacrylate, as well as copolymers, such as poly(ethylene)-co-(vinyl chloride), poly(styrene)-co-(butadiene), and poly(vinyl acetate)-co-(methyl acrylate). Among the various binder polymer possibilities, esters of poly(vinyl alcohol) are especially effective, and poly(vinyl acetate) homopolymer is preferred.
It is also convenient in most cases to introduce the binder polymer as an aqueous emulsion, many of which are commercially available.
In selecting the binder polymer, thermoplastic resins are preferred since they tend to form a tough, forgiving film, rather than a brittle film, or one which is soft and has a very low tensile strength when applied for joining the surfaces of ~he fiberboards, stiles, and rails.
Thermoplastic resins are also preferred since the heat required to set a thermosetting resin tends to calcine the gypsum in the preferred fiberboard compositions of this ~~ 13 ~678 ~6 invention. One particularly useful resin emulsion, which is suitable for use as the resin polymer of the preferred fiberboard composition and as an adhesive for bonding the various fire door and fire panel elements to one another is UCAR-130poly-(vinyl acetate) polymer by Union Carbide.
The composition for preparing the fiberboard layers of this invention will also include water in an amount in vast excess of that required to react with and hydrate the calcined non-fibrous gypsum. That is, at least about 20-fold excess, and preferably greater than about 25-fold excess amount of water should be present.
Contrary to the conventional wisdom, the excess water provides processing advantages and leads to products which possess superior properties. It is understood, for instance, that water introduced in quantities significantly less than the preferred amounts produces a sluggish mixture which does not provide optimum mixing of the pulp fibers and gypsum stucco. Conventional "wet" applications of about 80%
water, such as that disclosed by Porter and Way, U.S. Patent No. 2,076,349, have been known to produce veins of relatively weak, concentrated gypsum surrounded by stronger, fiber-rich regions in the set composition. These concentrated gypsum regions, being the weakest link of the composite, detract from the overall structural integrity of the product and adversely affect mechanical properties. Such properties are even further reduced when the latest "dry process" technology is employed, see Moslemi, Wood Composites Chemtech, p. 508 (August, 1988). Applicants' preferred ranges of water and pulped paper fiber promote homogeneity of the fiber and gypsum components and subsequently result in higher flexural strength and screw-~ 13a ~ ~) 6 7 8 ~ ~ -holding capacity measurements.
Although the fiberboard compositions of this invention may be formulated in a variety of ways, and any number of different techniques may be 5 employed to produce the panels and boards of this invention, a process which is yrefelled for making these structures is illustrated ~ C~

W O 91/05744 2 ~ S ~ ~ 0 6 PC~r/US90/05867 ~' _ 14 diagrammatically in FIG. 1. With reference to FIG. 1, the paper fiber component, e.g., newspaper, together with water, at least about 20 times as much water by weight as paper, are added to pulper 20, and the mixture is reduced to pulp, producing a substantially homogeneous suspension. Glass wool, if it is specified in the composition, can be separately pulped in at least about 20 times its weight of water and the separately pulped wool and paper combined. Alternatively, the paper and glass wool can be pulped together, if desired, in at least about 20 times their combined weight of water. Any textile glass fiber, clay and vermiculite called for are then added to the pulper and thoroughly mixed and incorporated into the suspension. The suspension is then transferred to tank 21.
As needed and required for the composition, pulped suspension from tank 21 is added to mixer 24, any binder polymer from tank 22 as may be required for the composition is added to mixer 24, and sufficient non-fibrous calcium sulfate to yield the requisite amount of dihydrate when reacted with less than about 5% of the water is added from tank 23 to mixer 24, wherein all the components are mixed and incorporated into the suspension, producing a slurry.
The wet slurry 25, sometimes referred to herein as "gypsum stucco"j is then cast into mold 26, and the slurry is pressed under hydraulic press 27 for dewatering the slurry and for producing a green casting 28. The pressure employed in the hydraulic press 27 determines the density of the final product; densities in the range of about 40 lbs/ft3 to about 75 lbs/ft3 being readily attained. For the fire-resistant applications of this invention, a density of at leas~t about 60 lbs/ft3, preferably above 65 lbs/ft3 is preferred.
The green casting is allowed to set and is then conveyed into oven 29 and the set casting is dried. If desired, dried set casting 30 may be sanded at sanding station 31 to the desired thickness and/or then cut to the desired size with saw 32. It will be evident that the aforesaid steps can be adapted to either a batch or continuous process.

WO91/057~ 2 ~ C ~ PCT/US90/05867 In the preferred continuous process for manufacturing boards and panels within the scope of the present invention, the aforementioned aqueous dispersion of constituents is formed into a sheet of indefinite length by the use of stAn~Ard paper-making techniques. For example, the aqueous dispersion of constituents can be fed from a head box of the type associated with a paper-making machine to a foraminous moving belt through which water drains as the mass of solids coagulates and sets. The resulting composite sheet is consolidated by passing through press rolls. Heated rollers can also be used to dry the sheet.
The proc~cses of the present invention can be used to make an unsupported (unfaced) fiberboard which has a substantially uniform and homogeneous composition throughout its thickness. The term "unfaced" is used herein to mean that the fiberboard is preferably not faced with a sheet material, for example, the paper or glass fiber mat that is often used as a facing material for gypsum wallboard.
As mentioned above, it is preferred that the fiberboard layers of the present invention have a density of at least about 60 lbs/ft3, but it will be understood that the material can have a density of as low as 40 lbs/ft3 for some applications. In order to achieve flexural strength and screw-holding capacity having the values referred to above (30 lbs and 400 lbs respectively) in building materials having densities below 60 lbs/ft3, there should be included in the composition from which the building material is made relatively high amounts of binder polymer, for example, about 25 wt.% to about 35 wt.% based on solids content. For applications in which such flexural strength charact~eristics and screw-holding capacity are not considered important, the ~ use of such binder polymer can be absent or provided in smaller amounts. The density of the fiberboard can be controlled by the use of pressure in forming the product and/or by the use of a low-density material, for example, eY~An~ed perlite.
Table I presents data obtained in producing building 4 2 ~ 6 7 ~ 0 6 PCT/US90/0~867 materials using the aforesaid batch process and various cellulosic fibers. All samples were pressed at 300 psi in a 4 inch by 4 inch mold. Samples were removed from the mold after pressing, hydrated, and then dried at llO-F. The dried samples were sanded to about 0.3 inches thick, cut to l inch wide by 4 inches long and tested for flexural strength on 3 inch centers. As reported in Table I below, the various cellulosic fibers used in forming the fiberboard panels comprise either wood chips which are pulped (comparative example) or paper stock which is pulped, the paper stock comprising either newspaper, Kraft paper, sulfite paper or paper of the type used to face wallboard. The significant improvements achieved by using the pulp of paper stock relative to the use of wood pulp are evident from the results reported in Table I.

TABLE I: Fiberboard Cellulosic Fiber Source Sample Data -Cellulosic Fiber o Newspaper Kraft Wood Pulp Sulfite Wallboard Weight of Water (g) 500.0 500.0 500.0 500.0 500.0 Weight of fiber material (g) 20.0 20.0 20.0 20.0 20.0 Time to vortex (sec) 24.0 291.0 0.0 191.0 377.0 Weight of Pulp Solution (g) 508.9 505.6 512.3 512.7 511.3 Weight of Gypsum (g) 113.0 113.0 113.0 113.0 113.0 Weight in mold prior to press (g)616.0 611.7 620.3 618.2 614.5 Water/gypsum off before press (g)267.5 265.7 383.9 273.2 289.0 Water/gypsum off during press (g)159.7 158.7 98.7 142.6 137.3 Gypsum lost before press (g) 2.82 5.47 36.59 5.07 1.33 Gypsum lost during press (g) 0.61 0.73 4.02 0.74 0.3 Total water lost during press (g)423.77418.2 441.99 409.99 424.67 Weight of sample-wet (g) 180.98 179.7 126.7 177.28 183.12 Weight of sample-dry (g) 137.74 134.41 84.78 134.71 139.52 ~~
Water lost during drying (g) 43.24 45.29 41.92 42.57 43.6 % mixture actually in sample 97.3 96.6 98.0 97.7 97.1 % total water lost before drying87.8 87.9 98.5 85.1 87.8 % total gypsum lost before drying0.031 0.057 36.7 0.053 0.015 Weight of 1" sample (g) 25.4 24.92 15.59 26.66 24.52 Caliper of 1" sample (in) 0.318 0.321 0.314 0.322 0.319 C
Density of 1" sample (lbs/in3) 73.187 71.731 46.352 76.52 70.498 o Flexural strength (lbs) 40.44 45.3 1.05 50.23 29.67 ~

WO91/057~ 2 ~ 6 7 8 0 S PCT/US90/05867 In contrast to that which has been taught previously in the gypsum arts, such as in U.S. Patent No. 4,557,973, it is not necessary in the process described above to pretreat the glass wool with powdered gypsum prior to its use.
Furthermore, the presence of the vast excess amount of water permits the gypsum slurry to flow out in the mold to a uniform thickness. In pressing the slurry to produce the green casting, care is required in order to prevent geysering, in which streams of slurry suddenly exit the mold with a great deal of force. This can be avoided by applying pressure slowly to the slurry. The amount of binder polymer in the slurry has an effect on the press time as shown in FIG. 2.
The data shown in FIG. 2 were obtained from casting compositions of this invention prepared as set forth in Fiberboard Example 1.

Fiberboard Exam~le 1 Four casting compositions were prepared containing the following ingredients in parts by weight:

TABLE II: Fiberboard Compositions with Varying 20Polymer Binder Concentrations Ingredient A B C D
gypsum hemihydrate 113 113 113 113 newspaper 20 20 20 20 polymer bindera 0 2.2 4.4 8.7 water 500 500 500 500 ~Polyvinyl acetate (UCAR-130) The newspaper was pulped in a Waring blender; the gypsum and polymer binder were added, and the blended mixture was pressed into 3/4 inch thick slabs at a rate to avoid geysering. Bui~ding materials witnin the scope of this invention, prepared by the process described hereinabove, were tested for flexural strength, as defined by the following pL~edure. These tests generally employed ASTM Method C 473-WO91/057~ 2 0 ~ ~ ~ Q 6 PCT/US90/05867 86a modified in that the specimens were 1/2 inch thick, 1 inchwide, and 4 inches long, with random orientation. In each case, the specimen was supported on bearings 3 inches apart, and the specimen was broken across the 1 inch width.
Evaluation of flexural strength as a function of the density of fiberboards was undertaken, and the results appear in FIG.
3. The flexural strength of fiberboards within the scope of this invention generally should be at least about 30 lbs, preferably at least about 60 lbs (1/2 inch thick sample).
Fiberboards within the scope of this invention were evaluated for screw-holding capacity, as defined by the following procedure. In these tests, a specimen of material to be tested, dried to constant weight and 1/2 inch +/- 1/32 inch thick, at least 9 inches long, and nominally 1 9/16 inches wide, was employed. At midwidth, a 5/32 inch pilot hole was drilled to receive a No. 12 sheet metal screw. With the specimen supported on a wooden block or steel plate and the pilot hole centered over a 5/8 inch hole in the support, the screw was turned until the full shank thickness penetrated the specimen. Force was then applied vertically at the center of the screw, forcing the screw through the specimen, and the force was noted. Evaluation of the screw-holding capacity of fiberboards within the scope of this invention was undertaken, as set forth in Fiberboard Example 2. The results appear in FIG. 4. In general, the screw-holding capacity of a building material within the scope of this invention should be at least about 400 lbs, and in a building board to be used as fire door edge banding, the screw-holding capacity should preferably be at least about 600 lbs, more preferably in excess of about 700 lbs.

Fiberboard Exam~le 2 A casting composition was prepared containing the following ingredients in parts by weight:

TABLE III: Base Casting Composition W O 91/05744 2~8a6 PC~r/US90/05867 ~ , Ingredient Ouantity gypsum hemihydrate 113 newspaper 20 water 500 The newspaper was pulped in a Waring blender; the gypsum was added, and varying amounts of the blended mixture were added to a mold and pressed to 1/2 inch thick slabs.
After curing and drying, the density and screw-holding capacity of each slab was measured.
The screw-holding capacity of the fiberboards of this invention is enhAnce~ through the use of binder polymer as illustrated in Fiberboard Example 3.

Fiberboard Example 3 In each case, the casting composition included 113 g lS calcined non-fibrous gypsum, 20 g paper, 2.2 g glass textile fiber, and 5 g binder polymer.

TABLE IV: Physical Properties of Various Fiberboards Per Binder Polymer Type Binder Polymer Product DensityScrew-Holding Capacity -lbs/ft3 lbs AIRFLEX 4530~ 67.5 749 4500 65.8 670 7522 68.6 730 4514 68.8 689 UCAR-130b 66.6 890 GEN FLO 6500C 68.9 718~
UCAR-376d 71.6 678 UCAR-417' 66.7 650 ~he AIRFLEX products are all ethylene~vinyl chloride bPolyvinyl acetate homopolymer 'Styrene/butadiene dVinyl/acrylic 20678~6 WO91/057~ PCT/US90/05867 'Acrylic Fire Door Constructions Referring now to FIGS. 5-8, there is shown a solid fire-resistant door structure which includes a 90 minute ASTM
E-152 fire test label. This door, shown in both "flush" and "panel" configurations, preferably contains a gypsum fiberboard core having a thickness of about 1.5 inches. The core can contain one or more layers of fiberboard panels of the previously described composition, but preferably includes three 1/2 inch fiberboard panels adhered together with adhesive.
With reference to FIGS. 5 and 6, there is shown in top and front cross-sectional views, a solid fire door construction 40 employing a solid multi-section, fiberboard core. This fire door 40 is preferably about 4 feet wide and 8 feet high, and includes a gypsum fiberboard core having a density of at least about 60 lbs/ft3 and a composition containing about 65 wt.% to about 90 wt.% set gypsum dihydrate and about 7 wt.% to about 30 wt.% paper fiber. The fiberboard core of fire door 40, can include multi-ply fiberboard sections 43, which can be adhered~-along their side edges to provide a complete core with other structural members. The fiberboard compositions can also be employed in both the edge banding 45 used to support the latch mechanism and to provide structural support to the edge of the door, for example the fiberboard vertical stiles and horizontal rails in FIG. 6 (note, that the rails are depicted as two -fiberboard members adhered along their longit~)~inAl length), blocking 44 used to provide further support for a latch as well as the door knob and other hardware. The door facings 42 are preferably made of birch or plywood veneer, 1/8 inch thick, and natural fir strips 41 are preferably adhesively bonded to the stiles.
- Alternatively, this invention contemplates employing a fiberboard core without facings, in which panels may be cut directly into the fiberboard surface without a significant loss in structural properties.

22 20 678~
As described in FIGS. 7 and 8, a light-weight fire door construction 60 having at least a 20 minute ASTM E-152 fire test rating can also be produced, which includes a honeycomb-like structure 66, for example, cardboard honeycomb or plastic foam spacer sheets such as those described in Lehnert and Fowler, U.S. Patent No. 4,811,438, Col. 4, for providing a multiplicity of points for supporting a pair of gypsum fiberboard panels 62. The panels 62 preferably comprise a composition having a density of at least about 60 lbs/ft3, a flexural strength of at least about 30 lbs, and ~re~rably at least about 40 lbs (1/2 inch thick material), and a screw-holding capacity of at least about 400 lbs. The composition of the panels 62 contains a substantially uniform distribution of solids including about 65 wt.% to about 90wt.% set gypsum dihydrate, about 7 wt.% to about 30 wt.% paper fiber, and about 1.5 wt.% to about 35 wt.% of one or more performance boosters selected from inorganic fiber, clay, vermiculite, and binder polymer. In this embodiment, a pair of facings, (not illustrated) preferably 1/8 inch thick plywood skins, can be adhered to thegypsum fiberboard panels 62 to provide an aesthetically appealing surface which can be stained or painted to match or blend with interior furnishings or exterior surface treatments.
The honeycomb-like structure 66 of the preferred light-weight door construction 60 is desirably enclosed around its perimeter with gypsum fiberboard edge banding 65. Although the edge banding 65 can include the same composition as the gypsum fiberboard panels 62, it preferably comprises about 68 wt.% to about 78 wt.% set gypsum dihydrate, about 10 wt.% to about 17 wt.% paper fiber, up to 35 C

1~_ 22a 2 0 B 7 8 ~ 6 wt.% binder polymer, up to 7 wt.% inorganic fiber, up to 6 wt.% clay, and up to 6 wt% vermiculite. The preferred edge banding 65 includes a density of at least about 65 lbs/ft3 and a screw-holding capacity of at least about 600 lbs, although densities of 5 up to and exceeding 70 lbs/ft3 and screw-holding capacities in excess of 700 lbs are also suitable for this purpose.

W O 91/05744 2 0 ~ 7 8 0 5 PC~r/US90/05867 The sheets of wood-like material, also referred to as "veneer" or "facing sheets", if employed, are preferably made of thin wood sheets, thin hardboard or plywood having a thickness of approximately 1/8 inch or less. Other sheets of thin material could also be employed for these members, such as metal, or polymers, especially fiber reinforced plastics.
The compositions of the fiberboards will vary according to the required thickness (ntn~, surface finish and mechanical integrity mandated by their end use. Some of the preferred compositions are specified in Table V.

TABLE V: Preferred Fiberboard Compositions With With ~
Without Veneer Veneer Edge Veneer t < 3/8 in. t > 3/8 in. ComDosition Gypsum stucco 77.88% 76.251 78.59/ 80.12~ ~

1/2 in. Long cO
Fiberglass .7% .55% .63% 1.6% ~

Paper Pulped Fibers 9.0% 12.3% 12.82% 14.24%

Resin (wet) 3.4% : 1.84%

Unexpanded Vermiculite 6.4% 2.20%

Pulped Glass Wool 1.56%

ASP Clay 9.02% 10.9% u x ( ~~ 25 70B7~ û6 Generally speaking, panels which do not include plywood or other types of veneer will require additional resin for enabling improved scuff resistance for the exposed surface. Additionally, the resin component can be added to the composition for edge banding applications for improving mechanical properties.
It will be understood, upon inspection of the disclosed fiberboard embodiments, that clay additions will vary depending upon the thickness of the fiberboard used. Clay is also important for obtaining "stand alone" qualities, i.e., the ability of the fiberboard to stand upright after fire has consumed the honeycombcore. These features are important for thicknesses of fiberboards less than about 1/2 inches. (For example, thinner panels, such as those employed for 1/8 inch skins,3/16 inch, and 3/8 inch panels require more clay for resistance to structural cracking, which is partially caused by thermal and pressure changes during fire testing.) While it is known that clay reduces shrinkage, see Green, U.S. Patent No. 3,616,176, it also seems to provide a more rigid panel that resists flexing during handling. This resistance to flexing becomes critical during a fire test for fire doors, as the paper honeycomb burns away, requiring the panels to stand alone over about a 36 inch span, the width of a standard size door. For thin panels, for example, less than about 3/8 inches, the fiberboard composition should contain about 5-15 wt.% clay, and ~reLelably about 9-11 wt.% clay.
Comparative Fire Testing Examples As a further demonstration of the effectiveness of the fiberboard ~~ 25a 2 0 6 7 8 ~ 6 compositions of this invention for use in fire doors, three different fire doors were tested pursuant to ASTM E-152 with temperature readings being made on the unexposed faces at selected time intervals.
The first test door contained a Georgia-Pacific mineral core of the type disclosed in U.S. Patent no. 4,343,127, comprising WO91/057~ 2 G ~ 7 8 0 6 PCT/US90/05867 compressed perlite covered with a wood skin. The second door included the same perlite-core, but the wood skin was replaced with 1/8 inch gypsum fiberboard skins containing 77.88 wt.%
gypsum stucco, .7 wt.% 1/2 inch long fiberglass, 9.0 wt.%
paper pulped fibers, 3.4 wt.% UCAR 130 resin (wet), and 9.02 wt.% ASP clay. In a third door construction, a gypsum fiberboard core was constructed with three 1/2 inch gypsum fiberboard panels containing 80.12 wt.% gypsum stucco, 1.6 wt.% 1/2 inch long fiberglass, 14.24 wt.% paper pulped fibers, 1.84 wt.% uneYpAn~ed vermiculite, and 2.20 wt.% pulped glass wool.
Table VI illustrates the temperature of the unexposed faces of these doors during the fire test. As used in this Table, the symbol "~T" refers to the temperature difference between the unexposed face of the referenced door and the unexposed face of the Perlite Core Woodskin door, at the same Furnace temperature.

TA~LE VI: Fire Test Results in Degrees ~F

Perlite Core Gypsum Fiberboard Core Perlite Core Gypsum Fiberboard Woodskin Unexposed Face Time Furnace Woodskin Skin (Temperature recorded Minutes Tem~erature Unexvosod Face UneYI~os~ Face at 15 min intervals onlY) O Ambient 79~ 70~ 84~
1000~ 80~ 72~
1300~ 102~ 90~
1399~ 156~ 134~ 101~
1462~ 192~ 149~
1510~ 203~ 150-1550~ 214~ 159~ 137~
1584~ 251~ 162~
1613~ 326~ 179~
1638- 422- 220- 170- ~
1661- 422- 219~
1681~ 411~ 223~ C~
1700~ 420~ 239~ ~T 181~ 184~
1718~ 430~
1735~ 439-1765~ 458-~85 1779~ 465~ o 1792~ 472~ 194~ ~T 278~ x WO91/057~ 2 ~ 6 PCT/US90/05867 As the data demonstrates, a 1/8 inch gypsum fiberboard skin applied to each side of a standard commercial fire door, during a standard 1 hour fire test, produced up to a 200-F lower temperature on the un~po-ed face when compared to a wood skin-perlite core commercial door. This temperature gap was further increased when a gypsum fiberboard core was used instead of a perlite core; the temperature of the door having a gypsum fiberboard core had a 278-F lower temperature at a furnace temperature of 1792-F than did the perlite core commercial door.

Structural Beam Fire-Resistant Fiberboard Application In conventional methods for fire proofing steel building sections or wooden columns, light-weight fibrous mixtures are sprayed onto the column or beam or multiple layers of a fire rated gypsum wallboard are adhered in a complicated structure. Spraying is sometimes awkward if the steel areas are difficult to reach by the spraying nozzle.
Additionally, since the coating thickness required for adequate fire proofing should be about .75-1 inch, it is usually n~ceC~Ary to apply the spray in multiple applications that require drying between steps. When wallboard is applied around a column or beam, separate metal attachment structures are necessary to secure the wallboard in position.
Alternatively, it is possible to wire tie the first layer or layers of wallboard and then secure final layers with corner beads and angularly-driven nails. This later method is generally deemed cumbersome and does not provide secure attachment of the outer layers of board.
Referring now to FIG. 9, there is shown a preferred fire-resistant structure 80 for encapsulating a beam or column, such as lOW49 steel column 81. In this embodiment, gypsum fiberboard can be applied in a single layer 82 preferab~y with 1.75 inch type S screws 86. The fiberboard composition of this embodiment preferably comprises about 12-17% paper or cellulosic fibers with the remainder being setcalcium sulfate dihydrate. Minor ingredients such as resins, ~ W O 91/05744 2 0 ~ 7 8 ~ 6 PC~r/US90/05867 glass fibers, mineral fibers, accelerators, consistency adjusting ingredients, and other additions as specified previously, may be added to improve the composition. The resulting gypsum fiberboard preferably has a density of about 60-75 lbs/ft3 and is capable of resisting fire and retaining its shape even after a long exposure to temperatures up to 2,000~F. Since the fiberboard has good nail-holding and screw-holding properties, it can be easily applied by attaching individual sections of the board at the corners as illustrated in FIG. 9.
The gypsum fiberboard layer 82 is enclosed in a .5 inch thick wallboard layer 83 which is affixed to the gypsum fiberboard layer 82 preferably with 1.25 inch type S screws 87. Following the attachment of the wallboard layer 83, corner beads 84 can be adhered to the corners of the wallboard layer 83 for added strength, and a layer of joint compound 85 can be applied over the entire surface. This construction is very economical compared to conventional methods of fire proofing steal beams and the like. It is also believed that the fiberboard-containing structure will have exceptional fire ratings.
From the foregoing, it can be realized that this invention provides fire-resistant panels and doors which can be used in combination with known fire door, beam or column elements to provide various constructions, as needed, for different fire ratings at minimal cost. The fiberboard panels of this invention are stable through a wide range of humidities, require less adhesive, require no additional edge system, are machinAhle into contoured configurations, and cost less to manufacture than ~y~m wallboard. The outlined combination of physical properties and materials, when applied to fire door manufacturing, opens up new frontiers of opportunities in door costs and construction designs.
Altnough various embodiments have been illustrated, this was for the purpose of describing and not limiting the invention.
Various modifications, which will become apparent to one skilled in the art, are within the scope of this invention WO91/057~ 2 0 6 7 ~ 0 6 PCT/US90/05867 described in the attached claims.

Claims (10)

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:

1. A fire-resistant structure characterized by a composition having a density of at least 60 lbs/cu. ft. and a screw holding capacity of at least 40 lbs., including by weight:
at least 65% set gypsum dihydrate derived from calcined gypsum;
and paper fibers derived from pulped paper, said fibers being disposed homogeneously throughout said set gypsum dihydrate by mixing said pulped paper and calcined gypsum with a quantity of water in excess of that required to completely hydrate the calcined gypsum.

2. The fire-resistant structure of claim 1, characterized by the composition having a density of at least 70 lbs./ft3, at least a 20 minute ASTM
E-152 fire test rating, a flexural strength of at least 30 lbs. (1/2 inch thick material), and a screw-holding capacity of at least 200 lbs.

3. The fire-resistant structure of claim 1, characterized by the composition containing a uniform distribution of solids including 65 wt.% to 90 wt.% set gypsum dihydrate, 7 wt.% to 30 wt.% paper fiber, and 1.5 wt.% to 35 wt.%
of one or more performance boosters selected from inorganic fiber, clay, vermiculite, and binder polymer.

4. The fire-resistant structure of claim 1, characterized by the composition including 7 wt.% to 24 wt.% paper fiber, 68 wt.% to 78 wt.% set gypsum dihydrate, and up to 35 wt.% binder polymer.

5. The structure of claim 1, characterized by the composition including 10 wt.% to 17 wt.% paper fiber, 0.8 wt.% to 2.0 wt.% siliceous fiber, up to 6 wt.%
clay, up to 6 wt.% vermiculite, and up to 15 wt.% binder polymer.

6. The fire-resistant structure of claim 1, characterized by the composition having a density of at least 65 lbs/ft3, a flexural strength of at least 40 lbs. (1/2 inch thick material), and a new screw-holding capacity of at least 600 lbs.

7. The fire-resistant structure of claim 1, further characterized by a core comprising a pair of gypsum fiberboard panels including said composition, said core comprising spacing means disposed between said gypsum fiberboard panels for providing a multiplicity of supporting points for supporting said panels.

8. The fire-resistant structure of claim 1, further characterized by a core including at least a pair of unfaced gypsum fiberboard panels containing, said composition comprising 75 wt.% to 90 wt.% set gypsum dihydrate, 10 wt.% to 17 wt.% paper fiber, and a wood-like veneer disposed over said core.

9. The fire-resistant structure of claim 1, further characterized by a plurality of gypsum fiberboard panels comprising said composition and disposed to enclose a structural beam member.

10. The fire-resistant structure of claim 1, further characterized by a plurality of gypsum fiberboard panels comprising said composition and being disposed integrally with a steel beam member.