CA2107495C - Solubilized anionic polymerization initiators and products therefrom - Google Patents

Solubilized anionic polymerization initiators and products therefrom Download PDF

Info

Publication number
CA2107495C
CA2107495C CA002107495A CA2107495A CA2107495C CA 2107495 C CA2107495 C CA 2107495C CA 002107495 A CA002107495 A CA 002107495A CA 2107495 A CA2107495 A CA 2107495A CA 2107495 C CA2107495 C CA 2107495C
Authority
CA
Canada
Prior art keywords
group
carbon atoms
general formula
alkyls
initiator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CA002107495A
Other languages
French (fr)
Other versions
CA2107495A1 (en
Inventor
David F. Lawson
Mark L. Stayer, Jr.
H. James Harwood
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bridgestone Corp
Original Assignee
Bridgestone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corp filed Critical Bridgestone Corp
Publication of CA2107495A1 publication Critical patent/CA2107495A1/en
Application granted granted Critical
Publication of CA2107495C publication Critical patent/CA2107495C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The present invention is directed toward anionic polymerization initiators which are soluble in acyclic alkane solvents. The initiators include a solubilized lithio amine having the general formula (A)Li(SOL)y. SOL is a solubilizing component and A is an alkyl, dialkyl or cycloalkyl amine radical or a cyclic amine and y is from about 1 to 4. The invention is also directed toward polymers and other products made using the initiator, and methods therefor. Further, the invention contemplates a polymer, a polymer composition and products therefrom, which include a functional group from the reaction product of an amine and an organolithium compound. The resulting polymers may be terminated with a terminating, coupling or linking agent, which may provide the polymer wtih a multifunctionality.

Description

SOLUBILIZED ANIONIC POLYMEItIZATION INITIATORS
AND I'RODUCTS TIIEREI{ ROM

TGCIINICAL FIELD
The subject invention relates to anionic polymerizations resulting in diene polymer and copolymer elasl:omers. More particularly, the present invention relates to polymerization employing a solubilized aniine initiator. Specifically, the invention relates to a solubilized lithium amine initiator whicli is soluble in acyclic alkane solvents, and which will reproducibYy polymerize monomers in a controllable and narrow mqlecular weight distribution range.

BACKGROUND ART
When conducting polymerizations on a commercial basis, it is important to utilize process conditions and components which will allow the molecular weight of the end products to be narrowly and reproducibly defined. The characteristics of a given polymer and its usefulness are dependent, among other things, upon its molecular weight. Hence, it is desirable to be able to predict with some certainty the molecular weight of the end product of the polymerization. When the molecular weight is not narrowly definable, or is not reproducible on a systematic basis, the process is not commercially viable.
In the art, it is desirable to produce elastomeric compounds exhibiting reduced hysteresis characteristics. Such elastomers, when compounded to form articles such as tires, power belts and the like, will show an increase in rebound, a decrease in rolling resistance and will have less heat build-up when mechanical stresses are applied.
A major source of hysteretic power loss has been establislied to be due to the section of the polymer chain froni the last cross link of the vulcanizate to the end of the polymer chain. This free end cannot be involved in an efficient elastically recoverable process, and as a result, any energy transmitted to this section of the cured sample is lost as heat. It is known in the art that this type of mechanism can be reduced by preparing higher inolecular weight polymers which will have fewer end groups.
However, this procedure is not useful because processability of the rubber with compounding ingredients and during shaping operations decreases rapidly with incrcasing molccular wcight.

9203023 FIR.P.US0069 It is difficult to obtain consistent properties, such as a reduction in hysteresis properties, if the polymer cannot be controllably reproduced in a narrow molecular weight range distribution. See, for example, U.S. Pat. No. 4,935,471, in which some polymers are prepared with a heterogeneous mixture of certain secondary amines, including lithium pyrrolidide.. Polymers made in this manner have widely variable molecular weights, broad polydispersities, and their functional terminations tend to reproduce erratically, giving rise to poorly reproducible hysteresis reduction results.
A major drawback with many of these known initiators, is that they are not soluble in acyclic alkanes, such as hexane. Polar solvents have heretofore been employed including the polar organic etllers such as dimethyl or diethyl ether, tetrahydrofuran, tetramethylethylenediamine, or diethylene glycol methyl ether (diglyme).
The present invention provides novel initiators for anionic polymerization, which are soluble in acyclic alkanes. The invention provides for the incorporation of a functionality from the initiator to be incorporated at the head and tail of the polymer chain. The invention provides for efficient:, controllable and reproducible polymerizations, with the preparation of well defined end-products of a relatively narrow molecular weight range distribution.

DiscLosuRE OF 'IIIE INVENTION
It is therefore, an object of the present invention to provide an anionic polymerization initiator which is soluble in acyclic alkanes.
It is a further object of the present invention to provide a method of preparing such an anionic polymerization initiator.
It is still a further object of the invention to provide an initiator which will reproducibly result in a polymer within a narrow, predictable molecular weight range.
It is another object of the present invention to provide elastomers formed with such a polymcrization initiator.
It is also an object of certain embodiments of the present invention to provide diene polymers and copolymers having reduced hysteresis characteristics.
It is a further object of the present invention to provide vulcanizable elastomeric ooinpauxls of diene polymers and copolymers having reduced hysteresis characteristics.
9203023 FIR.P.US0069 Still anothcr object of the present invention is to provide an improved tire formed from an clastomer as described hereinabove.
At least one or rriore of these objects together with the advantages thereof over the existing art, which shall become apparent from the specification which follows, are accomplished by the invention as hereinafter described and claimed.
In gcneral, according to the present invention, an anionic polymerization initiator which is soluble in acyclic alkane solvents, comprises a solubilized lithio amine having the general formula (A)Li(SOL)y where y is from about I to about 3; SOL is a solubilizing component selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof; and, A
is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula N-and cyclic amines having the general formula where RI is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from I to about 12 carbon a.toms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups.

There is also provided a metliod of preparing an anionic polymerization initiator, which method comprises the steps of reacting an organolithium compound with a functionalizing agent in the presence of a solubilizing agent; the functionalizing agent 9203023 FLR.P.US0069 being selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula Rl N-and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from I to about 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylend group having from about 3 to about 7 methylene groups; and, the solubilizing agent is selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof.
A method of preparing an anionic polymerization initiator comprises the steps of reacting an organolithium compound with a functionalizing agent to form a reaction product. The functionalizing agent is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula N-and cyclic amines having the general formula I--/

where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to about 12 carbon atoms, and R2 is selected from the group consisting of an 9203023 FIR.P.US0069 alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups. The method also comprises the step of reacting the reaction product with a solubilizing agent selected froni the group consisting of hydrocarbons, ethers, amines or mixtures thereof.
A functionalized polymer comprises a polymer chain carrying at least one functional group A wherein A is derived from a polymerization initiator having the general formula (A)Li(SOL)y where y is of from about I to about 3; SOL is a solubilizing component selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof; and, A is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula N-i Rl and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to about 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups.
A method of forming a functionalized polymer, according to the invention, comprises the steps of forming a solution of one or more anionically polymerizable monomers in an alkane solvent; and, polymerizing the monomers in the presence of an 9203023 FIR.P.US0069 initiator which is soluble in the alkane solvent. The initiator comprises a solubilized lithio amine having the general formula (A)Li(SOL)y where y is from about 1 to about 3; SOL is a solubilizing component selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof; and, A
is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula RI
N-and cyclic amines having the general formula ~./

where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to about 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups.
A vulcanizable elastomeric compound having reduced hysteresis properties comprises an elastomeric polymer having chains carrying at least one functional group A, wherein A is derived from a polymerization initiator having the general formula (A)Li(SOL)y where y is of from about I to about 3; SOL is a solubilizing component selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof; and, A is 9203023 FIR.P.US0069 selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general forniula Rl N-and cyclic amines having the general formula /---I

where Rl is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to about 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups; and from about 5 to 80 parts by weight of carbon black, per 100 parts of the polymer.

The present inverition also provides a tire having decreased rolling resistance resulting from a treadstock containing a vulcanizable elastomeric composition which comprises an elastomeric polymer having chains carrying at least one functional group A wherein A is derived from a polymerization initiator having the general formula (A)Li(SOL)y where y is of from about I to about 3; SOL is a solubilizing component selected from the group consisting of hydrocarbons, ethers, amines or mixtures thereof; and, A is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula N -Rl 9203023 FIR.P.US0069 and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to about 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups; and from about 5 to 80 parts by weight of carbon black, per 100 parts by weight of said polymer.
A vulcanizable rubber composition comprises a polymer carrying at least one amine functional group A, wherein A is derived from the reaction product of an organolithiunl compound and an amine; and a tin-carbon bond.
A multifunctional polymer comprises at least one functional group A, wherein A is derived from the reaction product of an organolithium compound and an amine; and, a tin-carbon bond.
A vulcanizable rubber composition comprises a polymer carrying at least one amine functional group A, wherein A is derived from the reaction product of an organolithium compound and an amine; and a second functional group selected and derived from the group consisting of terminating agents, coupling agents and linking agents.
A tire having at least one vulcanizable elastomeric component comprises a multifunctional polymer having at least one functional group A, wherein A is derived from a polymerization initiator which is the reaction product of an organolithium compound and an amine, wherein the multifunctional polymer has a tin-carbon bond, :25 and from about 5 to 80 parts by weight of carbon black, per 100 parts of the polymer.
A multifunctional polymer comprises at least one functional group A, wherein A is derived from the reaction product of an organolithium compound and an amine; and a second functional group selected and derived from the group consisting of terminating agents, coupling agents and linking agents.
:30 A tire having at least one vulcanizable elastomeric component is also provided, which component comprises a multifunctional polymer having at least one 9203023 FIR.P.US0069 ._' functional group A, wherein A is derived from a polymerization initiator which is the reaction product of an organolithium compound and an amine; the polymer having a second functional group selected and derived from the group consisting of terminating agents, coupling agents and linking agents; and frorn about 5 to 80 parts by weight of carbon black, pcr 100 parts of said polymer.

PREFERRED EMBODIMENT FOR CARRYING OLTr THE INVENTION
As will become apparent from the description which follows, the present invention provides novel polymerization initiators which are soluble in acyclic alkanes, including normal alkanes such as hexane, pentane, heptane, isoheptane, octane, their alkylated derivatives, mixtures thereof, and the like. It has also been discovered herein that certain rubber compositions, vulcanizable elastomeric compositions and articles thereof based upon polymers f:ormed using such initiators, exhibit useful properties, such as for example, reproducible relatively narrow molecular weight ranges.
Furthermore, the polymers according to the invention also contain a functionality from the initiator, which functionality is useful for example, in reducing hysteresis properties.
While the initiators of the present invention are soluble in acyclic alkane solvents, it will be appreciated that the use of the initiators in other solvents is also within the scope of the invention.
The preferred initiator according to the invention, is the reaction product of an amine, an organo lithium and a solubilizing component. The organo lithium and the amine may be reacted in the presence of the solubilizing component or agent, or they may be reacted first and the reaction product thereof subsequently reacted with the solubilizing component. The preferred initiator is therefore, a solubilized lithio amine having the general formula (A)Li(SOL)y where y is from about 1 to about 3. The parentheses of this general formula connote that the formula may include A-Li-SOLy; SOLy-A--Li; or, A-SOLy-Li.

9203023 FIR.P.US0069 lo-(SOL) is a solubilizing component and may be a hydrocarbon, ether, amine or a mixture thereof. It has been discovered that by the presence of the (SOL) coinponent, the initiator is soluble in acyclic alkanes.

Exemplary (SOL) groups include dienyl or vinyl aromatic polymers or copolymers having from 3 to about 300 polymerization units. Such polymers include polybutadiene, polystyrene, polyisoprene and copolymers thereof. Other examples of (SOL) include polar ligands, such as tetrahydrofuran (THF) and tetramethylethylenediamine ('TMEDA).

The (A) component represents the amine functionality, at least one of which is carried by the resulting polymer, such as by being incorporated at the initiation site or head thereof. For example, (A) may be a dialkyl or dicycloalkyl amine radical having the general formula 'R1 N -RI

or a cyclic amine having the general formula In these formulas, Rl is an alkyl, cycloalkyl or aralkyl having from 1 to about 20 carbon atoms, where both Rl groups may be the same or different, and R2 is an alkylene, oxy- or amino-alkylene group having from about 3 to about 7 methylene groups.

Exemplary R 1 groups include methyl, ethyl, butyl, octyl, cyclohexyl, 3-phenyl-i-propyl, isobutyl and the like. Exemplary R2 groups include tetramethylene, hexamethylene, oxydiethylene, N-alkylazadiethylene and the like.

For example, (A) may be derivative of pyrrolidine; piperidine; piperazine;
perhydroazepine, also known as hexamethyleneimine; or 1-azacyclooctane;
including bicyclics such as perhydroisoquinoline, perhydroindole, and the like.
Pyrrolidine, 9203023 FIR.P.USOO69 perhydroazepine and 1-azacyclooctane are preferred. Two preferred pyrrolidine derivatives include perhydroindole and perhydroisoquinoline.
It has been found that when Rl or R2 are a di-t-butyl group, a diisopropyl group or the like, the resulting polymerizations are slow, presumably due to hinderence around the nitrogen at the initiation site. Hence, in a preferred embodiment of the invention, the carbon atoms in Rl and R2 which are bonded to the nitrogen in the amine, are also bonded to three hydrogen atoms.
The initiator according to the present invention can be formed by preparing a solution of the amine component (A), in an anhydrous, aprotic solvent, such as hexane, preferably in the presence of the solubilizing agent or component (SOL), if (SOL) is an ether or an amino compound. To this solution is then added an organolithium catalyst in the same or a similar solvent. The organolithium compound has the general formula RLi where R is selected from the group consisting of alkyls, cycloalkyls, alkenyls, alkynyls, aryls and aralkyls having from 1 to about 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to about 25 units. Typical alkyls include n-butyl, s-butyl, methyl, ethyl, isopropyl and the like. The cycloalkyls include cyclohexyl, menthyl and the like.
The alkenyls include allyl, vinyl and the like. The aryl and aralkyl groups include phenyl, benzyl, oligo(styryl) and the like. Exemplary short chain length polymers include the oligo(butadienyls), oligo(isoprenyls), oligo(styryls) and the like.
If (SOL) is a short chain length polymer, the monomers used to iorm (SOL) are added after the amine and the organolithium are mixed, as will be addressed hereinbelow.
To the solution of the amine and the organolithium, is added a solution of the monomers of the solubilizing component (SOL) in the same or similar solvent, if (SOL) is a polydiene or a polyvinyl aromatic. The three components are allowed to react for up to about one hour at ambient temperature (25 to 30 C), or elevated temperatures up to about 100 C preferably at less than 50 C, and more preferably at less than 38 C, following which the catalyst is ready for use. The initiators according to the present invention are considered to be soluble if they remain in solution within an excess of an acyclic alkane solvent for about 3 or more days.

As stated above, the initiator thus formed may be employed as an initiator to prepare any anion ically-polymerized elastomer, e.g., polybutadiene, polyisoprene and the like, and copolymers thereof with monovinyl aromatics such as styrene, alpha methyl styrene and the like, or trienes such as myrcene. Thus, the elastomers include diene homopolymers and copolymers thereof with monovinyl aromatic polymers. Suitable monomers include conjugated dienes having from about 4 to about 12 carbon atoms and monovinyl aromatic monomers having 8 to 18 carbon atoms and trienes. Examples of conjugated diene monomers and the like useful in the present invention include 1,3-butadiene, isoprene, 1,3-pentadiene, 2,3-dimethyl-l,3-butadiene and 1,3-hexadiene, and aromatic vinyl monomers include styrene, a-methylstyrene, p-methylstyrene, vinyltoluene and vinylnaphthalene. The conjugated diene monomer-and aromatic vinyl monomer are normally used at the weight ratios of 95-50:5-50, preferably 95-65:5-35.
Polymerization is conducted in an acyclic alkane solvent, such as the various hexanes, heptanes, octanes, mixtures thereof, and the like. In order to promote randomization in copolymerization and to control vinyl content, a polar coordinator may be added to the polymerization ingredients. Amounts range between 0 and 90 or more equivalents per equivalent of lithium. The amount depends on the amount of vinyl desired, the level of styrene employed and the temperature of the polymerization, as well as the nature of the specific polar coordinator (modifier) employed.
Compounds useful as. polar coordinators are organic and include tetrahydrofuran (THF), linear and cyclic oligomeric oxolanyl alkanes such as 2-2'-di(tetrahydrofuryl) propane, di-piperidyl ethane, hexamethylphosphoramide, N-N'-dimethylpiperazine, diazabicyclooctane, dimethyl ether, diethyl ether, tributylamine and the like. The linear and cyclic oligomeric oxolanyl alkane modifiers are described in U.S.
Pat. No. 4,429,091, owned by the Assignee of record. Compounds useful as polar coordinators include those having an oxygen or nitrogen hetero-atom and a non-bonded pair of electrons. Other examples include dialkyl ethers of mono and oligo alkylene glycols; "crown" ethers; tertiary amines such as tetramethylethylene diamine (TMEDA);
linear THF oligomers and the like.

A batcli polymerization is usually begun by charging a blend of monomer(s) and an acyclic alkane solvent to a suitable reaction vessel, followed by the addition of the polar coordinator (if employed) and the initiator compound previously described.
The reactants are heated to a temperature of from about 20 to about 200 C, and the polymerization is allowed to proceed for from about 0. 1 to about 24 hours. A
functional amine group is derived from the initiator compound and attaches at the initiation site. Thus, substantially every resulting polymer chain has the following general formula AYLi where A is as described above, and Y is a divalent polymer radical which is derived from any of the foregoing diene homopolymers, monovinyl aromatic polymers, diene/monovinyl aromatic random copolymers and block copolymers. The monomer addition at the lithium end causes the molecular weight of the polymer to increase as the polymerization continues.

To terminate the polymerization, and thus further control polymer molecular weight, a terminating agent, coupling agent or linking agent may be employed, all of these agents being collectively referred to herein as "terminating agents".
Certain of these agents may provide the resulting polymer with a multifunctionality. That is, the polymers initiated according to the present invention, may carry at least one amine functional group A as discussed hereinabove, and may also carry a second functional group selected and derived from the group consisting of terminating agents, coupling agents and linking agents.

Useful terminating, coupling or linking agents include active hydrogen compounds such as water or= alcohol; carbon dioxide; N,N,N',N'-tetradialkyldiamino-benzophenone (such as tetrarriethyldiaminobenzophenone or the like); N,N-dialkylamino-benzaldehyde (such as dimethylaminobenzaldehyde or the like); 1,3-dialkyl-2-imidazolidinones (such as 1,3-dimethyl-2-imidazolidinoneor the like); 1-alkyl substituted pyrrolidinones; 1-aryl substituted pyrrolidinones; dialkyl- and dicycloalkyl-carbodiimides having from about 5 to about 20 carbon atoms; (R3)aZXb;

9203023 FIk.P.US0069 O
~

N CH = O

O
ii R6 N O N=CH-R5 and, R6 N CH = N-R7 where Z is tin or silicon. It is preferred that Z is tin.
R3 is an alkyl having from about 1 to about 20 carbon atoms; a cycloalkyl having from about 3 to about 20 carbon atoms; an aryl having from about 6 to about 20 carbon atoms; or, an aralkyl having from about 7 to about 20 carbon atoms. For example, R3 may- include methyl, ethyl, n-butyl, neophyl, phenyl, cyclohexyl or the l i ke.

X is chlorine or bromine, "a" is from 0 to 3, and "b" is froin about 1 to 4, where a + b = 4.

Each R4 is the same or different and is an alkyl, cycloalkyl or aryl, having from about 1 to about 12 carbon atoms. For example, R4 may include methyl, ethyl, nonyl, t-butyl, phenyl or the like.

9203023 FIR.P.US0069 R5 is an alkyl, phenyl, alkylphenyl or N,N-dialkylaminophenyl, having from about I to about 20 carbon atoms. For example, R5 may include t-butyl, 2-methyl-4-pentene-2-yl, phenyl, p-tolyl, p-butylphenyl, p-dodecylphenyl, p-diethylaminophenyl, p-(pyrrolidino)phenyl, and the like.
Each R6 is the same or different, and is an alkyl or cycloalkyl having from about 1 to about 12 carbon atoms. Two of the R6 groups may together form a cyclic group. For example, R6 may include methyl, ethyl, octyl, tetramethylene, pentamethylene, cyclohexyl or the like.
R7 may include alkyls, phenyls, alkylphenyls or N,N-dialkylaminophenyls, having from about 1 to about 20 carbon atoms. For example, R7 may include methyl, butyl, phenyl, p-butylphenyl, p-nonylphenyl, p-dimethylaminophenyl, p-diethylaminophenyl, p-(piperidino)phenyl, or the like.
Other examples of useful terminating agents include tin tetrachloride, (Ri)3SnC1, (RI)2SnC12, R1SnC13, carbodiimides, N-methylpyrrolidine, cyclic amides, cyclic ureas, isocyanates, Schiff bases, 4,4'-bis(diethylamino) benzophenone, and the like, where R, is as described hereinabove.
One preferred polymer according to the present invention, is a polymer which includes at least one functional group A as discussed hereinabove, wherein A is derived from the reaction product of an amine and an organolithium compound as also discussed hereinabove. Furthermore, a preferred polymer is multifunctional wherein the polymer also carries a tin-carbon bond, such as may be derived from the terminating, coupling or linking agent. A rubber composition or a vulcanizable rubber composition according to the present invention, may include such a polymer.
The terminating, coupling or linking agent is added to the reaction vessel, and the vessel is agitated for about 1 to about 1000 minutes. As a result, an elastomer is produced having an even greater affinity for compounding materials such as carbon black, and hence, even further reduced hysteresis. Additional examples of terminating agents include those found in U.S. Patent No. 4,616,069.
The polymer may be separated from the solvent by conventional techniques.
These include steam or alcohol coagulation, thermal desolventization, or any other suitable method. Additionally, solvent may be removed from the resulting polymer by drum drying, extruder drying, vacuum drying or the like.
The elastomers of the present invention comprise a plurality of polymers, having a functional group at both the head and tail of the resulting polymer.
Such compounding may result in products exhibiting reduced hysteresis, which means a product having increased rebound, decreased rolling resistance and has less heat build-up when subjected to mechanical stress.
It has also been found, as will be exeniplified hereinbelow, that polymers formed using the initiators of the invention, are reproducibly formable in a relatively narrow range of molecular weights, such that substantially consistently reproducible polymers are possible with a molecular weight range of about 20,000 to about 250,000.
The polymers of the present invention can be used alone or in combination with other elastomers to prepare a product such as a tire treadstock, sidewall stock or other tire component stock c:ompdund. At least one such component is produced from a vulcanizable elastomeric or rubber composition. For example, the polymers according to the invention can be blended with any conventionally employed treadstock rubber which includes natural rubber, synthetic rubber and blends thereof. Such rubbers are well known to those skilled in the art and include synthetic polyisoprene rubber, styrene/butadiene rubber (SBR), polybutadiene, butyl rubber, Neoprene, ethylene/propylene rubber, ethylene/propylene/diene rubber (EPDM), acrylonitrile/butadiene rubber (NBR), silicone rubber, the fluoroelastomers, ethylene acrylic rubber, ethylene vinyl acetate copolymer (EVA), epichlorohydrin rubbers, chlorinated polyethylene rubbers, chlorosulfonated polyethylene rubbers, hydrogenated nitrile rubber, tetrafluoroethylene/propylene rubber and the like. When the polymers of the present invention are blended with conventional rubbers, the amounts can vary widely such as between 1.0 and 99 percent by weight.
The polymers can be compounded with carbon black in amounts ranging from about 5 to about 100 parts by weight, per 100 parts of rubber (phr), with about 5 to about 80 parts being preferred and from about 40 to about 70 phr being more preferred. The carbon blacks may include any of the commonly available, commercially-produced carbon blacks but those having a surface area (EMSA) of at least 9203023 FIR.P.US0069 21 07 49 a TT _~ _~ -20 m2/g and more preferably at least 35 m2/g up to 200 m2/g or higher are preferred.
Surface area values used in this application are those determined by ASTM test using the cetyltrimethyl-arninonium bromide (CTAB) technique. Among the useful carbon blacks are furnace black, channel blacks and lamp blacks. More specifically, examples of the carbon blacks include super abrasion furnace (SAF) blacks, high abrasion furnace (HAF) blacks, fast extrusion furnace (FEF) blacks, fine furnace (FF) blacks, intermediate super abrasion furnace (ISAF) blacks, semi-reinforcing furnace (SRF) blacks, mediuni processing channel blacks, hard processing channel blacks and conducting channel blacks. Other carbon blacks which may be utilized include acetylene blacks. Mixtures of two or more of the above blacks can be used in preparing the carbon black products of the invention. Typical values for surface areas of usable carbon blacks are summarized in the following TABLE I.

TABLE I

CARBON BLACKS

ASTM Surface Area Designation (m2/g) (D-1765-82a) (D-3765) The carbon blacks utilized in the preparation of the rubber compounds of the invention may be in pelletized form or an unpelletized flocculent mass.
Preferably, for more uniform mixing, unpelletized carbon black is preferred. The reinforced rubber 9203023 FIR.P.US0069 compounds can be cured in a conventional manner with known vulcanizing agents at about 0.5 to about 4 phr. For example, sulfur or peroxide-based curing systems may be employed. For a general disclosure of suitable vulcanizing agents one can refer to Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd ed., Wiley Interscience, N.Y.
1982, Vol. 20, pp. 365-468, particularly "Vulcanization Agents and Auxiliary Materials" pp. 390-402. Vulcanizing agents may be used alone or in combination.
Vulcanizable elastomeric or rubber conipositions of the invention can be prepared by compounding or mixing the polymers thereof with carbon black and other conventional rubber additives such as fillers, plasticizers, antioxidants, curing agents and the like, using standard rubber mixing equipment and procedures and conventional amounts of such additives.

General Experimental In order to demonstrate the preparation and properties of the initiators and elastomers according to the present invention, a number of such initiators and elastomers were prepared. A solution of styrene and butadiene monomers in hexane was prepared and was polymerized with the above described initiators. To further show the effectiveness of the invention,, a number of similar monomer solutions were polymerized with a heterogenous mixture of non-solubilized lithium pyrrolidide as an initiator to provide comparative control examples. The non-solubilized lithium pyrrolidides will be discussed first hereinbelow, followed by examples of initiators and elastomers made according to the present invention. As noted above, various techniques known in the art for carrying out polymerizations may be employed without departing from the scope of the present invention.
1. Non-Solubilized Lithium Pyrrolidide Initiation The following examples are included for comparison to the initiators and elastomers prepared according to the invention, which will be exemplified hereinbelow.

9203023 FIR.P.US0069 Experiment No. 1 Initiator Preparation In a small dried and nitrogen purged bottle, 20 ml of a 0.5 M solution of pyrrolidine in hexanes (10 milliequivalent or "meq") was treated with 6.36 ml of a 1.65 M solution of n-butyllithium in hexanes (10.5 meq). The bottle was fitted with a perforated crown seal having a rubber liner. The resulting heterogeneous mixture was agitated gently at room temperature for 16 hours, after which the product was drawn off for use as an initiator. The mixture was shaken vigorously before and while drawing off the samples.
Polymerization The initiator mixture made in the above manner was transferred by syringe to each of two small bottles which were also fitted with a seal as above. The bottles each contained a 75/25 weight percent monomer blend of butadiene/styrene, at 25 weight percent in hexane and a level of 1.0 meq Li/100 grams of monomer. The bottles also contained 0.6 mol of N,N,N',N'-tetramethylethylenediamine (TMEDA) per mol of lithium. The mixtures were agitated at 50 C for 2.5 hours. The reaction resulted in approximately 100 percent conversion of monomer to polymer.
The first bottle of cement, EXAMPLE 1, was then quenched by injection of 1.5 milliliters (ml) of isopropyl alcohol (i-PrOH), and the second bottle of cement, EXAMPLE 2, was treated for an additional 90 minutes at 50 C with 1.15 mol of 4-(N,N-diethylamino) benzaldehyde per mol of lithium. The cement of EXAMPLE 2 was then quenched with 1.5 ml of i-PrOH.
Both cements from EXAMPLE 1 and EXAMPLE 2 were treated with an antioxidant, namely, 2 ml of a mixture containing 2.0 weight percent of dibutyl paracresol (DBPC) and 0.7 weight percent of UOP-88TM, available from Universal Oil Products Co., in hexane. The cements were then coagulated in i-PrOH and drum dried.
The resulting polymers were analyzed, and the characteristics thereof are reported in TABLE II hereinbelow.

TABLL II

Example I Example 2 HNMR 24% styrene 24.8% styrene (0% block styrene) (0% block styrene) Percent of butadiene portion as 1,2 linkages 51.9% 49.4%
GPC (THF solvent) Mn 136365 136697 Mw/Mn 1.35 1.40 Tga -36.5 C -38.8 C
a) glass transition temperature at onset The polymers of' EXAMPLES 1 and 2 were compounded using the rubber recipe reported in TABLE lII hereinbelow.

9203023 FIR.P.US0069 TABLE III
COMPOUNDING RECIPE

Mix Parts per Hundred Ingredicnt Order Parts Rubber Polymer 1 100 Naphthenic oil 2 10 Masterbatch Carbon black, N-351 3 55 145-155 C, 60 RPM
ZnO 4 3 Antioxidant 5 1 l.0 Wax blend 6 2 Total Masterbatch: 171 Stearic acid 2 Final Sulfur 1.5 77-93 C, 40 RPM
Accelerator 1 Total Final: 175.5 The compounded polymers were then cured using 1.5 inch x 4 inch x 0.040 inch tensile plaques, for 45 minutes at 300 F (149 C); Dynastat buttons, 50 minutes at 300 F (149 C). The results of ensuing physical tests are reported in TABLE IV.

9203023 FIR.P.US0069 TABLE IV

PIiYSiCAI. TESTS OF COMPOUNDED POLYMERS OF EXAMPLES 1 AND 2 Wt% 1 Hz Dynastat Example M 4 212 Bound tan 8 Ring Stress-Strain, psi.
RT
No. (gum) (cpd) Rubber 50 C M300 T.S. %Eb 1 32 81 28 0.110 2169 2836 419 2 33 84 ca.29 0.107 2177 2327 359 The test results reported in TABLE IV, show that the compounded polymer of EXAMPLE 1 has a tan 6 value about 30 percent below the value expected for an unmodified polymer of this molecular weight, prepared using a typical alkyllithium initiator. However, the polymer of EXAMPLE 2 fails to show any significant reduction in tan S beyond this, despite its having been additionally treated at the tail with a reagent which is known to be effectivc; for reducing tan b. The lack of additional effect was also noted in the bound rubber results, where the result for EXAMPLE 2 was not significantly different from that of EXAMPLE 1.
It was concluded that the polymer cement prepared in this manner, besides having somewhat broadened molecular weight distribution, also did not have sufficient live C-Li chain ends after polymerization to allow for significant reaction with a chain-end functionalizing reagent. Therefore, this method was not highly desirable for synthesis of polymers with optimum properties.

Experiment No. 2 Initiator Preparation A second non-solubilized initiator was prepared. In a clean, stirred, one gallon stainless steel reactor, which had been dried and preconditioned, and then nitrogen purged, was placed 1.22 pounds of anhydrous hexanes, and 5.4 ml of a 0.77 M solution of pyrrolidine in hexanes (4.16 meq). This was treated with 2.69 ml of a 1.58 M solution of n-butyllithiuin in hexanes (4.25 meq), stirring at room temperature 9203023 FIR.P.USOO69 overnight. The resulting heterogeneous mixture was used in situ for the subsequent polynierization.

Polymerization The reactor containing the above initiator mixture was charged with 0.76 pounds of a 34 weight percent blend of styrene and hexanes, 1.28 mmol of TMEDA, and 3.06 pounds of a 25.5 weight percent blend of 1,3-butadiene in hexanes.
The reactor was heated to 46 C and controlled at that temperature for three hours.
A portion of the polymer cement made in this manner was transferred by needle into three small bottles sealed as in Experiment 1 hereinabove. The remainder of the cement was collected in a large glass container, under a nitrogen purge. The cement in the large container, EXAMPLE 3 was quenched by injection with 1.5 ml of isopropyl alcohol (i-PrOH), while the cement in the sniall bottles, EXAMPLE 4 was treated for an additional 2 hours at 50 C with 1.25 mol of 1,3-dimethylimidazolidin-2-one (1,3-DMI) per mol of lithium. The cement of' EXAMPLE 4 was then quenched with 1.5 ml of i-PrOH, and both cement portions were treated with an antioxidant (2 ml of a mixture containing 2.0 wt. percent DBI'C in hexane). The contents of the bottles were combined, and both EXAMPLES 3 and 4 were coagulated separately in i-PrOH
and drum dried. Suitable characterizations were performed, and the results are summarized in TABLE V hereinbelow.

Experiment No. 3 Repeat experiments were run using the same reactor as in Experiment No. 2, employing the same ainount of reagents, reaction t.imes, and temperatures from those of EXAMPLES 3 and 4. The resulting cement was compounded in the recipe of TABLE III hereinabove, and is reported as EXAMPLE 5 hereinbelow. A portion of EXAMPLE 5 was end-linked by reaction with one equivalent of SnC14 per equivalent of lithium, to produce EXAMPLE 6. A cement was also prepared as for EXAMPLE
5, except that the initiator was allowed to form in the reactor for three (3) days instead of overnight. Also, the resulting polymer was compounded in the recipe of TABLE VI
hereinabove, and is reported herein as EXAMPLE 7. A portion of EXAMPLE 7 was 9203023 FIR.P.US0069 treated with 1.25 mole of 4-(N,N-dimethylamino)-benzylidene butylaniline per mole of lithium to produce EXAMPLE 8. The order of addition of polymerization reagents for the run producing EXAMPLI: 7 and 8 were as follows: (1) TMEDA, (2) butadiene blend, (3) styrene blend. The polymeric products were worked up as described for EXAMPLES 3 and 4. Results of their characterization and compounded evaluation are given in TABLE V hereinbelow.
The product polymers were cured using 1.5 inch x 4 inch x 0.040 tensile plaques, for 20 minutes at 165 C; and Dynastat buttons, for 25 minutes and 165 C.
TABLE V hereinbelow lists the characterizations and compounded properties of Examples 5 to 8.

9203023 FIR.P.US0069 0o c0 o -~r C) "0 'T
p N N -'Q: > N v~l M V ~ V U .r M

~D ~D ~t IN , N v 1 Ul M =-' m N N C7\
CL' p; \O \O r- N f3, t~ ~ N N O ~ C~ N p U
~

,1* 00 M cr\
Q ~t p N N N N O > N
O
A. O ~ M M
O 6 N N N N ~ M N O
~=1 F <
~
w O o N
N N ~t N pp [N-O
V1 N N ~ N N M

U
C~C ON I~t N 00 N N Q\ .- Co tn N M

>-a ~
z _ o 0o U M o b M~+
z >~' o w' bA C CZ. z rG

U c 3 0~ ~ o N c~ U
W C~ C7 >8 U G4 U~ E~-~ N
o N
9203023 FIR.P.US0069 00 N >
M N
C) O N

af M O_~ 0 M N O
0 0 a M ~ .D
N '- N C ~j O O -'" U

'C7 :y O M
'-+ N M C) C) ~ ~Cy ~ =~ o o M
U O Q W a) , y cC
$ o a, P. ~
F M o o E r- o a ;= 0 ' E
[ N N t.
_ o N "" ~ 'n g y p bA
~ ~ ~ ~
C7 O v~ .... C .1]
Ri Y C C 2 -l~ 0 ~ C td t~d 3 Y

c~ v, v~ c 0 a~ +t~ ~, o A
d) C:
(j tu o. (X) ~' p o 0 E
L)G ~, a0 on on ~ ~ o o c ~ > > > op E
vi c'f'v a~ O Q Q Q~ g z ~ n ~ v a ~ o V1 p tn 9203023 FIR.P.US0069 TABLE VI

MEDIUM-OIL COMPOUNDING FORMULATION
Mix Parts per In re i n Order Hundred Parts Rubber Polymer 1 100 Carbon black, 145-155 C, 2 54 Masterbatch ZnO 3 3 60 RPM
Stearic acid 4 2 Antioxidant Procesing aids 5 4.25 Aromatic oil 6 27.6 Total. Masterbatch: 190.85 Final Sulfur 2.25 77-93 C, 40 RPM
Accelerator blend 2.15 Total Final: 195.25 The results in T AIILE V show the shortcomings of polymerization with N-lithiopyrrolidide initiators. Although the initiator/monomers charged in runs 3,5 and 7 were the same (1.0 meq of lithium per 100 grams of monomer), the molecular weight of the products ranged frorn 96,000 to 254,000, which is evidence of the highly erratic initiator. The high molecular weight products are indicative of slow initiation relative tovpropagation, presumably due to the heterogenous nature of the system.

exhibited a tan 6 reduction at 50 C about 31 % lower than that of an unmodifred polymer of similar microstructure anci molecular weight. T'he result of end-linking of the live cement of EXAMPLE 5, via SnC14, leading to EXAMPLE 6 was a further reduction in tan 6, to about 40% of that of an unmodified polymer of the same base (uncoupled) 9203023 FIR.P.US0069 molecular weight. The bound rubber content, which is indicative of the extent of interaction with carbon black, increased appreciably while the GPC showed that percent of the polymer chains were end-linked, an indication that an appreciable fraction of "live" chain-ends were still available for linking.
EXAMPLES 3, 4 and 7, 8 resulted in polymers of such high molecular weight that they were not processable for forniulation in the low oil recipe of TABLE III, but were formulated according to the recipe of TABLE VI, which contains 27 parts per 100 rubber of oil for better processing. The results of the evaluations in TABLE V indicate that these polymers show reduced tan 6, but the 13-16 percent reduction relative to the unmodified SBR elastomers is small compared to that demonstrated in the EXAMPLES 5 and 6. Little change in viscosity occurred upon attempting end-linking with SnCI4, indicating that ttiere was little active C-Li remaining at the chain ends after polynierization in these polymers. The SnC14-treated polymers (EXAMPLES 4 and 8) exhibited' tan S's which were about 75 percent of that of the unmodified samples.

In summary, the results of polymerizations which were initiated using N-l.ithiopyrrolidide as describecl hereinabove, were highly erratic, both with respect to the nature and composition of the product as well as to other characteristics thcreof.

II. Polymerization witli a Solubilized Initiator Experirnent No. 4 Initiator Preparation A dried, stainless steel one gallon reactor under a nitrogen atmosphere, was charged with 1.22 pounds of hexane, and then with 5.4 ml of 0.77 M pyrrolidine in hexane (4.16 mec) followed by 2.7 ml of 1.58 M n-butyllithium in hexane (4.27 meq).
The mixture was stirred overnight at 90 F (32 C). The reactor was then charged with 90 grams of 25.4 weight percent 1,3-butadiene in a hexane solution (423 mmol of butadiene), and the mixture was heated at 110 to 120 F (43 to 49 C) for one hour.
This effectively places a SOL group on the pyrrolidine moiety consisting on average of about 100 parts of 1,3-butacliene.

9203023 FIR.P.US0069 21074 !95 Polymerization There was then charged to the reactor, 0.76 pounds of 33 weight percent styrene in hexane, containing 1.06 mmol of TMEDA, followed immediately by 2.89 pounds of the 25.4 weight percent butadiene/hexane blend. This provided for an initiator to monomer charged ratio of 1.0 meq of lithium per 100 grams of monomer (1.0 meq Li phgm). The polymerization was allowed to continue for 2 hours at (49 C) and the live cement was collected tlirough a twelve gauge stainless steel needle into four small beverage bottles, fitted and purged as described in the preceding examples.
Ttie cements in two of the bottles, EXAMPLE 9, were quenclled by injection with 1.5 ml of i-PrOH, while the cements in the other two bottles, EXAMPLE 10, were treated for an additional two hours at 50 C with 1.2 mol of tributyltin chloride per mol of lithium. The cement of EXAMPLE 10 was then quenched with 1.5 inl of i-PrOH, and both cement portions were treated with an anti-oxidant as in Experiment III
hereinabove. Both EXAMPLES 9 and 10 were coagulated separately in i-PrOH and drum dried. Suitable characterizations were performed, and the results are summarized in TABLE VII hereinbelow.

Experiment No. 5 Initiator Preparation A mixture of 25.1 meq of pyrrolidine and 25.1 meq of n-butyllithium in hexane was stirred under nitrogen over a weekend at room temperature. This was treated with 50.2 meq of THF in hexane, and the resulting mixture was used to initiate the polymerization.
Polymeri=rAttion A dried, stainless steel five gallon reactor under a nitrogen atmosphere, was charged with 8.53 pounds of hexane, 3.17 pounds of 33 weight percent styrene in hexane, 8.78 mmol of TMEDA, followed immediately by 17.89 pounds of a 25.4 weight percent butadiene/hexane blend, and the initiator prepared hereinabove, contained 25.1 meq of lithiuni. The polymerization was run for 2.25 hours at 110 to 120 F (43 to 49 C) and the live cement. was collected through a twelve gauge stainless steel needle 9203023 FIR.P.US0069 into five small beverage bottles, fitted and purged as described in the previous examples, and through a 1/2 inch pipe into two dried and purged large containers under a nitrogen purge.
The cements in the large containers, EXAMPLE 11, were quenched by injection with i-PrOH, while the cements in the bottles, EXAMPLE 12, were treated first for an additional 0.5 hours at 50 C with 0.3 equivalents of tin tetrachloride per mol of lithium, followed by treatment for 2 hours at 50 C with 0.84 mols of 1,3-dimethyl-2-imidazolidinone (1,3-DMI) per mol of lithium. The cement remaining in the reactor, EXAMPLE 13, was treated for about 2 hours at 50 C with 0.8 equivalents of SnC14 per equivalent of lithium. The polymeric products were worked up as described for EXAMPLES 9 and 10 hereinabove. Results of their characterizations and compounded evaluations are given in TABLE VII hereinbelow.

Experiment No. 6 Initiator Preparation A separate portion of the same initiator used in EXAMPLES 11, 12 and 13 was set aside and used two days later as follows, with an estimated concentration of 0.6 meq/ml.

Polymerization The procedure used to polyinerize the basc ceinent of EXAMPLES 11-13 was repeated. The live product cement was collect through a twelve gauge stainless steel needle into five small beverage bottles, fitted and purged as described in the preceding examples and through a 1/2 inch pipe into two dried and purged large containers under a nitrogen purge.
The cements in the large containers in EXAMPLE 14, were quenched by injection with i-PrOH while the cements in the bottle, EXAMPLE 15, were treated first for an additional 0.5 hours at 50 C with 0.3 equivalents of tin tetrachloride per mol of lithium, followed by treatment for 2 hours at 50 (: with 0.85 mol of 1,3-DMI
per mol of lithium. The polymeric products were worked up as described for EXAMPLES 9 and 10, results of their cl-iaracterizations and compounded evaluations are given in TABLE VII hereinbelow.

9203023 FIR.P.US0069 õ~ -' '~ c~ g rn bR ~p [~ -" ~
o o v c-Vl N U1 N M It --~ ~O tr'1 V't M 00 O O M == =-= ~ 0\ %D 0 '"' 1r1 N N M M
E-~

a M VD pp 0 Q+ .-. M O cn 00 a h N ' N N N M M
U
~

N M ~O 00 NV. pp M --~ [~- V) crI
.-i M O cn l~ ~ U O
V1 N ' N =-+ v~ "' N N

O ~' --~ ~'- ' _ ch %~o a t- N 00 v~i N M rn N
a N
a ~
F~ z r~1 0 o ~ v o o C4 M .a.
W
F-U
N 0~ N 0I~ N

[I.

M~+
z a ~ ~E, --, U ~, v z H a z o x o g V) V) oA- 'n U U c 3 a~ a W U
c~/) v~i cn v1 O
.-, .-.
9203023 FIR.P.US0069 210?495 M M y b0 O ~
Q CD N
(U
w cd Q\
b4 N d N C
O O

00 a) (- M .D
N d O O

.~y o a 110-~.

E
C M 0~0 h O .-, O "O
u r'' o o > .~e W =y '~
o O .0 w N ~ V
N E
' Nt 00 O M cli O y cv ~ t~
O O
O
N C ~ -0 C

y o w cd p~q x ~' H C G n. ;, E a~
.--~
U Z; a o o $~ i i i Q E
-~ ~ O Q Q Q~ $ Z
Q ~o ~o o ~., 9203023 FIR.P.US0069 Expcriment No. 7 Initiator I'reparation A mixture of 28.6 meq of pyrrolidine, 57.2 mmol of THF, and 29.15 meq of n-butylithium in hexane, was stirred under a nitrogen atmosphere overnight at room temperature. An aliquot from the resulting mixture (about 0.56 milliequivalent (meq) per ml) was used to initiate the polymerization.
A five gallon sta.inless steel reactor was then charged with 6.42 pounds of hexane, 28.6 mol equivalent of the above 0.56 M initiator, and 1.25 pounds of a 24.2 weight percent blend of butadiene and hexane, and the mixture was heated at (35 C) for one hour.

Polymerization There was then charged to the reactor, 3.53 pounds of 34 weight percent styrene in hexane, 9.7 mmol of TMEDA, and 17.85 pounds of the butadiene/hexane blend. This provided for an initiator to monomer charge ratio of 1.05 meq Li phgm, and a monomer ratio of approximately 20 weight percent styrene/80 weight percent butadiene. The polymerization was run for 1.75 hours at 110 to 115 F (43 to 46 C).
The reactor was finally charged with 0.3 pounds of the butadiene/hexane blend, and a 4.1 pound sample of the cement was immediately collected in a large container and quenched by adding i-PrOH, EXAMPLE 16. The contents remaining in the reactor were treated by stirring witti 22.2 ml of 1.0 N SnC14 for 1.5 hours at 100 to 110 F (43 to 46 C), and the cement was dropped under a nitrogen purge into a five gallon canister containing a small amount of i-PrOH EXAMPLE 17.
The cements from EXAMPLES 16 and 17 were treated with an antioxidant as in the immediately preceding experiment, and both samples were coagulated in i-PrOH and drum dried. Suitable characterizations were performed and the results are summarized in TABLE VIII hereinbelow.

9203023 FIR.P.US0069 Experiment No. 8 Initiator Preparation A mixture of 88.8 meq of pyrrolidine, 177.8 mmol of THF, and 89.8 meq of n-butylithium in hexane was stirred under nitrogen overnight at room temperature.
An aliquot from the resulting mixture (approximately 0.57 meq per ml) was used to initiate polymerization.
A five gallon stainless steel reactor was then charged with 6.55 pounds of hexane, 47.1 ml (26.7 meq) of the above 0.57 M initiator, and 1.0 pound of a 24.2 weight percent blend of butadiene in hexane, and the mixture was heated at 100 F
(38 C) for 30 minutes.

Polymerization There was then charged into the reactor, 4.41 pounds of 34 weight percent styrene in hexane, 9.08 nimol of TMEDA, and 17.1 pounds of the butadiene/hexane blend. This provided for ar- initiator to monomer charge ratio of 0.98 meq Li phgm, and a monomer ratio of approximately 25 weight percent styrene/75 weight percent butadiene. The polymerization was run 2.3 hours at 110 to 115 F (43 to 46 C).
The reactor was finally charged with 0.5 pounds of the butadiene/hexane blend, and a 3.5 pound sample of the cement was immediately collected in a large container and quenched by adding i-PrOH, EXAMPLE 18. The contents remaining in the reactor were treated by stirring with 21.0 ml of 1.0 N SnC14 at 115 F (46 C). After reaction, the cement was dropped uncler a nitrogen purge into a five gallon canister containing a small amount of i-PrOH, EXAMPLE 19. The cements were treated with an antioxidant as in the immediately preceding example and both cements from EXAMPLES 18 and 19 were coagulated separately in i-PrOH and then drum dried. Suitable characterizations were performed and the results are summarized in TABLE VIII
hereinbelow.

9203023 FIR.P.US0069 TABLE VIII

SUMMARY OF CI-iARACTERIZATION AND COMPOUNDED PHYSICAL PROPERTIES

Example No. 16 17 18 19 NMR % VINYL b 42.7 43.1 43.4 43.4 % STY 20.4 20.1 24.9 .24.9 DSC Tg1 Cc -47 -46 -45 -45 GPC (THF) Mn x 10-3 1.00 2.41 1.22 --Mw/Mn 1.10 1.48 1.26 --Coupling -- 86% -- 69%

Raw 7 82 20 113 Compound 47 94 61 98 Test Recipe, TABLE NO. III III III IlI

STRESS-STRAIN, TBd 3167 3452 3283 3714 23 C% EBe 447 423 405 409 DYNASTAT 1 HZ, tan 6+50 C 0.100 0.079 0.098 0.092 tan 6-20 C 0.289 0.312 0.495 0.548 a) Mol% of butadiene content as 1,2-linkages b) Onsct of Tg c) Ring stress-strain, 300% modulus, psi d) Ring stress-strain, tensile modulus, psi e) % Elongation at break 9203023 FIR.P.US0069 The product polymers were compounded and tested as indicated in the test recipes show in TABLE III, and cured as above. TABLE VII lists the characterizations and properties of the polymers from EXAMPLES 9-15. TABLE VIII lists the characterizations and compounded properties of EXAMPLES 16-19.
The results in TABLES VII and VIII show the advantages and the desirable results obtained from polymerization with the initiators according to the present invention. In contrast to the results in TABLE V, EXAMPLES 9-19 demonstrate the consistency of diene polymerizations employing these initiators. Namely, the polymerizations show relatively reproducible and predictable molecular weights, with narrow molecular weight distributions, and the polymer cements exhibit better viability of the living C-Li chains for further reactions. The dicapped polymers of EXAMPLES 10, 12, 13 and 17 show exceptionally low hysteresis, at about 40 percent to 50 percent of the values expected for comparable unmodified polymers of the same base molecular weight.
EXAMPLES 6, 10, 12, 13, 17 and 19 also exhibit the advantageous combination of N-Li initiation and end-linking or termination with a tin compound, such as R3SnC1 or SnC14.

The results of polymerizations which were initiated in acyclic alkane solvents using the lithium pyrrolidide as described in the comparative EXAMPLES 1-8, were highly erratic both with respect to the nature and composition of the products as well as their hysteresis behavior. However, when formulated as the N-lithiohydrocarbon amide with near-equivalent amounts of polar ligand or with monomer extension, as exemplified hereinabove, reproducible polymerizations with good molecular weight control, narrow molecular weight distributions, and good preservation of living C-Li ends for further reactions are achieved.

A preferred method of preparing the initiators according to the invention, will now be described. A vessel, such as a small bottle containing a TeflonTM or glass-clad magnetic stirring bar, is dried, sealed, and purged with nitrogen. The following is added by syringe while stirring:
1. 30 mmol anhydrous 2 amine in hydrocarbon solvent, and 2. 60 mmol anhydrous polar solubilizer in hydrocarbon solvent.

3. 30.1 mmol of alkyl lithium in hydrocarbon solvent is added by syringe at once, with stirring, while taking precaution for back-pressures.

The solution will heat and develop pressure immediately, but will soon begin to cool back down. When larger amounts of reagent are prepared, e.g. 250-300 mmol in large bottles or 0.5-1.5 mol in reactors, best results are obtained when chilled or cold water cooling is used to keep the peak temperature at about 38 C or below. The normal procedure has been to allow the mixture to stir ovenight at room temperature before using. However, the reaction is essentially complete within minutes. The mixture should be clear, straw-yellow, without significant precipitation. Light-to-moderate haziness or cloudiness does not appear to affect activity. Anhydrous conditions are required. (SOL)/hydrocarbon solvent solutions with less than 30 ppm of water give best results. Initiator reagents can be stored under positive nitrogen pressures for periods of up to several weeks at room temperature (25-27 C). N-Lithio pyrrolidine/2THF
solutions prepared and stored in this manner at about 0.5M - 1.5M in hexanes are stable for periods of about three to four weeks, and are effective initiators for diene and/or vinylaromatic (co) poly merizations, giving polymers with excellent properties. N-Lithio perhydroazepine/2THF solutions prepared and stored in this manner at about 0.3M -0.9M in hexanes are stable for at least several days, and can also be used with good results in polymerizations.
It should now be clear from the foregoing examples and specification disclosure, that initiators according to the present invention are useful for the anionic polymerization of diene monomers. Reproducible polymerization of such polymers within a relatively narrow molecular weight range is achieved, and the resulting polymers also exhibit good preservation of live C-Li ends, when compared to the non-solubilized initiators heretofore known in the art.
It is to be understood that the invention is not limited to the specific initiator reactants, nionomers, terminators, polar coordinators or solvents disclosed herein, except as otherwise stated in the specification. Similarly, the examples have been provided merely to demonstrate practice of the subject invention and do not constitute 9203023 FIR.P.US0069 limitations of the invention. Those skilled in the art may readily select other monomers and process conditions, accor=ding to the disclosure made hereinabove.
Thus, it is believed that any of the variables disclosed herein can readily be determined and controlled without departing from the scope of the invention herein disclosed and described. Moreover, the scope of the invention shall include all modifications and variations that fall within the scope of the attached claims.

9203023 FIR.P.USOOG9

Claims (13)

1. An anionic polymerization initiator soluble in acyclic alkane solvents, comprising:

a solubilized lithio amine having the general formula (A)Li(SOL)y where y is from 1 to 3; SOL is a hydrocarbon solubilizing component selected from the group consisting of dienyl polymers, vinyl aromatic polymers and copolymers having from 3 to 300 polymerization units; and A is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls and aralkyls having from 1 to 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- and amino-alkylene group having from 3 to 7 methylene groups.
2. An anionic polymerization initiator, as set forth in claim 1, wherein the carbon atoms in R1 which are bonded to the nitrogen in the amine, are also bonded to a total of at least three hydrogen atoms.
3. An anionic polymerization initiator, as set forth in claim 1, wherein SOL
is selected from the group consisting of polybutadiene, polystyrene, polyisoprene and copolymers thereof.
4. An anionic polymerization initiator, as set forth in claim 1, wherein A is selected from the group consisting of pyrrolidine; piperidine; piperazine;
perhydroazepine; 1-azacyclooctane; and derivatives thereof.
5. An anionic polymerization initiator, as set forth in claim 4, wherein said pyrrolidine derivative is selected from the group consisting of perhydroindole and perhydroisoquinoline.
6. An anionic polymerization initiator, as set forth in claim 1, wherein A is selected from the group consisting of di-n-alkylamines, wherein the alkyl group has from 2 to 5 carbon atoms.
7. An anionic polymerization initiator, as set forth in claim 1, wherein said lithio amine has the formula A-SOL y-Li, A is pyrrolidine and y is 1.
8. A method of preparing an anionic polymerization initiator comprising the step of:
reacting an organolithium compound, having the formula RLi where R is selected from the group consisting of alkyls, alkenyls, alkynyls, cycloalkyls, aryls and aralkyls having from 1 to 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to 25 units, with a functionalizing agent in the presence of a solubilizing agent selected from the group consisting of dienyl aromatic polymers, vinyl aromatic polymers and copolymers having from 3 to 300 polymerization units, said functionalizing agent being selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls or aralkyls having from 1 to 12 carbon atoms, and R2 has from 3 to 7 methylene groups and is selected from the group consisting of an alkylene, oxy- and amino-alkylene groups.
9. A method of preparing an anionic polymerization initiator comprising the steps of:
reacting an organolithium compound, having the formula RLi where R is selected from the group consisting of alkyls, alkenyls, alkynyls, cycloalkyls, aryls and aralkyls having from 1 to 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to 25 units, with a functionalizing agent to form a reaction product, said functionalizing agent being selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls and aralkyls having from 1 to 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- and amino-alkylene group having from 3 to 7 methylene groups; and, reacting said reaction product with a hydrocarbon solubilizing agent selected from the group consisting of dienyl aromatic polymers, vinyl aromatic polymers and copolymers having from 3 to 300 polymerization units.
10. A method of forming a functionalized polymer, comprising the steps of:
forming a solution of one or more anionically polymerizable monomers in an alkane solvent; and, polymerizing said monomers in the presence of an initiator which is soluble in said alkane solvent; said initiator comprising:

a solubilized lithio amine having the general formula (A)LI(SOL)y where y is from 1 to 3;SOL is a hydrocarbon solubilizing component selected from the group consisting of dienyl aromatic polymers, vinyl aromatic polymers and copolymers having from 3 to 300 polymerization units; and, A is selected from the group consisting of alkyl, dialkyl and cycloalkyl amine radicals having the general formula and cyclic amines having the general formula where R1 is selected from the group consisting of alkyls, cycloalkyls and aralkyls having from 1 to 12 carbon atoms, and R2 is selected from the group consisting of an alkylene, oxy- and amino-alkylene group having from 3 to 7 methylene groups.
11. A method, as set forth in claim 10, comprising the further step of reacting said polymer with a functional group selected and derived from the group consisting of terminating agents, coupling agents and linking agents, such that the resulting polymer is multifunctional.
12. A method, as set forth in claim 11, wherein said terminating agent, coupling and linking agents are selected from the group consisting of carbon dioxide;
N,N,N',N'-tetraalkyldiaminobenzophenones; N,N-dialkylaminobenzaldehydes; 1,3-dialkylimidazolidinones; 1-alkyl substituted pyrrolidinones; 1-aryl substituted pyrrolidinones; dialkyl- and dicycloalkyl-carbodiimides having from 5 to 20 carbon atoms; (R3)a ZX b;

where Z is tin or silicon; R3 is selected from the group consisting of alkyls having from 1 to 20 carbon atoms, cycloalkyls having from 3 to 20 carbon atoms, aryls having from 6 to 20 carbon atoms and aralkyls having from 7 to 20 carbon atoms; X is chlorine or bromine; a is an integer from 0 to 3 and b is an integer from 1 to 4 where a + b = 4; each R4 is the same or different and is selected from the group consisting of alkyls, cycloalkyls and aryls, having from 1 to 12 carbon atoms;
R5 is selected from the group consisting of t-alkyls, phenyls, alkylphenyls and N,N-dialkylaminophenyls, having from 4 to 20 carbon atoms; each R6 is the same or different, and is selected from the group consisting of alkyls and cycloalkyls having from 1 to 12 carbon atoms, or the two R6 groups together form a cyclic group;
and, R7 is selected from the group consisting of alkyls, phenyls, alkylphenyls and N,N-dialkylaminophenyls having from 1 to 20 carbon atoms.
13. A method, as set forth in claim 12, wherein the two R6 groups together form a cyclic group.
CA002107495A 1992-10-02 1993-10-01 Solubilized anionic polymerization initiators and products therefrom Expired - Lifetime CA2107495C (en)