CA2128912A1 - Modified phenol-aldehyde resin and binder system - Google Patents
Modified phenol-aldehyde resin and binder systemInfo
- Publication number
- CA2128912A1 CA2128912A1 CA002128912A CA2128912A CA2128912A1 CA 2128912 A1 CA2128912 A1 CA 2128912A1 CA 002128912 A CA002128912 A CA 002128912A CA 2128912 A CA2128912 A CA 2128912A CA 2128912 A1 CA2128912 A1 CA 2128912A1
- Authority
- CA
- Canada
- Prior art keywords
- aldehyde
- resin
- phenol
- phenolic compound
- modifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
MODIFIED PHENOL-ALDEHYDE RESINS AND BINDER SYSTEM
ABSTRACT OF THE DISCLOSURE
A process for the production of a modified phenol-aldehyde resin which may form a binder system when combined with a curing agent which includes an additional source of an aldehyde, e.g., a phenol-formaldehyde resin. The inventive phenol-aldehyde resin may be modified with compounds from one of the following classes: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. The resin and adhesive are useful in the production of a wood composite (such as plywood, oriented strandboard, or fiberboard).
ABSTRACT OF THE DISCLOSURE
A process for the production of a modified phenol-aldehyde resin which may form a binder system when combined with a curing agent which includes an additional source of an aldehyde, e.g., a phenol-formaldehyde resin. The inventive phenol-aldehyde resin may be modified with compounds from one of the following classes: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. The resin and adhesive are useful in the production of a wood composite (such as plywood, oriented strandboard, or fiberboard).
Description
-MODIFIED PHENOL-ALDEHYDE RESIN AND BINDER SYSTEM
BACKGROUND OF THE INVENTION
Field of the Invention The invention relates generally to the production of a modified phenol-aldehyde resin, and more particularly to the preparation and use of a modified phenol-aldehyde resin which utilizes an additional source of aldehyde, e.g., a phenol-formaldehyde resin, as a curing agent. The invention further relates to the use of such a cured resin as a binder in a process for the production of wood composites, e.g., plywood or fiberboard.
Description of Related Technolo~y Various processes may be used to produce wood composites depending on the desired final product which is desired. Synthetic resins, such as phenol-formaldehyde resins, are often used as binders in the manufacture of wood composites such as man-made pressed wood boards (e.g., waferboard, oriented strandboard ("OSB"), or fiberboard). Such wood composites may be formed in de~ired shapes and sizes depending on the intended use. Fiberboard, for example, may be made by various known processes including "dry" processes (e.g., a process comprising application of resin by a blender or by a blow line application), "wet"
processes, or "wet-dry" processes. Various known phenol-formaldehyde resins may also be utilized as binders in the manufacture of other wood composites such as plywood.
Several useful processes are described (for example, for the production of plywood and fiberboard) in U.S. Patent No. 4,961,795, the disclosure of which ~-is incorporated herein by reference.
Various fast-curing phenol-formaldehyde resins have been utilized as binders in the manufacture of wood composites. Typical fast curing phenol-formaldehyde resins have (a) a high molar ratio of formaldehyde to phenol and (b) a high caustic content ~,,. ~ .
~128912 in order to accelerate the curing process. However, such fast-curing resins are undesirable due to (a) high levels of free formaldehyde emission during pres~ing and (b~ the high caustic content which negatively impacts the resistance of the final product to moisture.
It is therefore desirable to produce a binder resin which (a) has a relatively fast cure time and/or (b) is resistant to high levels of moisture. In addition, it is desirable to produce a binder system in which undesirable amounts of formaldehyde will not be released into the atmosphere upon pressing. It is further desirable to produce a binder system which is convenient to use in a process such as the those described above.
SUM~RY OF THE INVENTION
It is an object of the invention to overcome one or more of the problems described above.
Accordingly, the invention provides a process for producing a modified phenol-aldehyde resin (e.g., a phenol-formaldehyde resin) useful in the production of wood composites, e.g., waferboard. The resin is preferably modified with a compound from one of the following classes: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines, including combinations thereof.
According to one feature of the invention, the inventive modified phenol-aldehyde resin is combined with a source of aldehyde (e.g., formaldehyde or a formaldehyde derivative) to form a binder system.
In a preferred embodiment of the invention, a binder system iB provided by supplying the modified phenol-aldehyde resin in combination with a curing agent which i8 an organic resin comprising formaldehyde.
In a further embodiment of the invention, the modified phenol-aldehyde resin is combined with a curing agent and cellulosic material (e.g., wood wafers) to form a mat. The mat is cured under heat and pressure to fonm a wood composite. Alternatively, the ': :
':
: . .
inventive resin may be combined with a curing agent and utilized as a binder in the manufacture of plywood.
Other objects and advantages of the invention will be apparent to those skilled in the art from the following detailed description, taken in conjunction with the appended claims.
DETAILED DESCRIPTION OF A PREFERR~D EMBODIMENT
According to the invention, a modified phenol-aldehyde resin is produced by first condensing phenol and an aldehyde in the presence of an alkaline cataly3t. The condensation product of phenol and the aldehyde is then further condensed with a modifier selected from one of the following (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. The resin may be incorporated with a curing agent (e.g., a phenol-formaldehyde resin) which provides a further source of aldehyde. The combination of the inventive resin and curing agent may comprise a binder system which is preferably blended with a cellulosic material (e.g., wood wafers or fibers) and formed into a wood composite, e.g., waferboard, fiberboard, or particleboard.
According to a preferred embodiment of the inventive process, formaldehyde (or a formaldehyde derivative or other aldehyde) and phenol (or a phenol derivative) are condensed, preferably at a temperature of about 65-70C, in a reactor in the presence of an alkaline catalyst (e.g., caustic) to achieve methylolation of phenol. Useful catalysts include those known in the art, for example, sodium hydroxide or potassium hydroxide. The reference herein to "phenol" denotes phenol derivatives, as well as phenol itself (i.e., hydroxybenzene). Derivatives of phenol include, for example, substituted phenols. Thus, the reference herein to "formaldehyde" does not limit the invention to formaldehyde, but denotes derivatives of formaldehyde, as well as formaldehyde itself, other aldehydes and derivatives of other aldehydes.
Derivatives of formaldehyde include, for example, paraformaldehyde and hexamethylenetetramine. The ratio ~'` ' . - . -; ~ - : . . .............................. .
.., ., 2l289l~
of aldehyde to phenol i~ preferably in the range of about 1.2 to about 2.0 moles aldehyde per mole phenol, more preferably about 1.3 to about 1.6 moles aldehyde per mole phenol, and most preferably about 1.4 moles aldehyde per mole phenol.
Although higher level~ of caustic may be utilized (especially for plywood applications), caustic is preferably added to the reaction mixture at about 0.1 to about 0.2 moles sodium hydroxide per mole of phenol. Such an amount of caustic preferably assures very beneficial wet properties of wood composites (e.g., tolerance to moisture), while allowing for sufficiently rapid cure. More caustic can be used to accelerate the resin cure process; however, a high caustic content may result in undesirable properties in the final product, including higher water absorption rates and thickness swell of the final wood composite ~;
product.
Following the condensation reaction between phenol and an aldehyde, the reactor is preferably heated to about 90C and held at this temperature to obtain a polymer of desired chain length. The desired chain length of the polymer, which varies depending upon the reactants and reaction conditions, will generally be based on a measurement of the viscosity of the initial condensation product, which may be referred to as a "PF pre-polymer."
An amount of a modifier (e.g., resorcinol) is added to this initial condensation product, preferably without the addition of further caustic, followed by continuation of the reaction until a desired chain length (e.g., a desired viscosity) is reached to produce what may be referred to as a "PRF pre-polymer"
or "PRF resin." The inventive resin is also referred to herein as a modified phenol-formaldehyde resin. The compounds which may be reacted with the phenol-formaldehyde pre-polymer include three classes of compounds: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. Examples of dihydroxybenzenes include resorcinol, hydroquinone, and catechol. Examples of aminophenols include ortho-~ 2~28912 hydroxyaniline, meta-hydroxyaniline, and para-hydroxyaniline. Examples of phenylenediamines include ortho-phenylenediamine, meta-phenylenediamine, and para-phenylenediamine. When resorcinol i9 referred to herein (e.g., in the examples or preferred ratios described below), any compound in these three classes may be utilized as an alternative to resorcinol, including combinations thereof. Thus, when the term "PRF resin" or "PRF pre-polymer" is used herein, this refers not only to a resin or pre-polymer including resorcinol, but includes any of the compounds described above. ~esorcinol, however, is the preferred compound.
The above-described sequential condensation reactions preferably use a molar ratio of phenol to resorcinol of about 1 to about 10 moles phenol per mole resorcinol, and more preferably about 5 to about 10 moles phenol per mole resorcinol. The ratio of formaldehyde to total phenolic compounds (i.e., phenol plus resorcinol) is preferably about 1 to about 1.8 ~ -~
20 moles formaldehyde per mole phenolics, more preferably --~
about 1.1 to about 1.4 moles formaldehyde per mole phenolics, and most preferably about 1.2 moles formaldehyde per mole phenolics (i.e., the molar ratio of formaldehyde to phenol plu9 resorcinol may be greater than 1).
Following the condensation of resorcinol (or one of the other suitable compounds described above), the reactor is cooled to ambient temperature for storage. The product resin, which may be referred to as a "PRF resin," is generally stable at ambient temperature for at least one month. The inventive PRF
resin is preferably utilized in conjunction with a curing agent (described below) as a blnder system in the manufacture, for example, of waferboard, fiberboard (e.g., medium density fiberboard or hardboard), oriented strandboard, plywood, and particleboard. In the binder system, the inventive resin exhibits very fast cure and excellent tolerance to high levels of moisture.
As stated above, the formaldehyde component of the inventive resin is not limited to formaldehyde '.-, ' ' - ~ :, .
i~self, but encompasses any formaldehyde derivative and other aldehydes or derivatives thereof which are known in the art to be useful in conjunction with phenol-formaldehyde resins. For example, the following 5 aldehydes are useful as the formaldehyde component of the invention: acetaldehyde,`glyoxal, and furaldehyde.
However, formaldehyde is the preferred aldehyde. Thus, it is understood tha~ when the formaldehyde component of the resin is referred to herein, this refers to 10 formaldehyde, formaldehyde derivatives, and other aldehydes.
In addition, although phenol itself is preferably utilized in order to produce a resin which can be made economically on a commercial scale, many 15 other compounds are useful as the phenol or phenol derivative of the present invention. Such useful phenols include substituted phenols such as cresols and 5 xylenols. Therefore, it is also understood that when the phenol component of the resin is referred to 20 herein, this refers to both phenol itself and phenol derivatives.
As is known in the art, a variety of modifiers may be incorporated into the phenol-resorcinol-formaldehyde resin in order to modify its 25 properties. These modifiers include, for example:
urea, melamine, lignins, tannins, sugars, starches, glycols, polyols, and mixtures thereof. The proportion of modifier incorporated into the resin typically ranges from about 5 to about 35 weight percent based 30 upon the phenolic component.
The inventive PRF resin produced by the above-described process may be satisfactorily utilized in any process that utilizes a conventional hot press.
For example, the inventive PRF resin preferably is able 35 to be cured while using an additional source of aldehyde in press cycles not longer than those typically observed for isocyanate resins, while at the same time the inventive resin yields a substrate with better weatherability properties.
Although the resin may be cured by itself at high temperatures, the cure rate of the resin is preferably accelerated by addition to the PRF resin of a source of further formaldehyde or other aldehyde.
The PRF resin and the source of further formaldehyde may be applied as a two-component binder system.
However, it must be emphasized that the PRF resin in combination with a PF resin (as a curing agent) can be easily spray-dried by a process known in the art and used as a one-component system. Any source of formaldehyde or other aldehyde may be used to accelerate the cure of the PRF resin.
According to a preferred embodiment of the invention, an organic resin comprising formaldehyde ~-~
(e.g., a fast-curing phenol-formaldehyde resin or a "PF
resin") is utilized as the curing agent. Any organic resin comprising formaldehyde, a formaldehyde derivative, or other aldehydes may be utilized. Thus, when a phenol-formaldehyde resin is referred to herein, reference i5 also made to the other resins described in the preceding sentence. However, a phenol-formaldehyde resin is the preferred curing agent. When using a PF
resin as the curing agent, the weight proportion of the PRF resin to PF resin is preferably about 0.25:1 to about 4:1, and more preferably about 0.6:1 to about 1.5:1. PF resins known in the art as binders in wood composites may be suitably utilized as the source of further formaldehyde. For example, a PF resin having a molar ratio of formaldehyde to phenol of about 2 to !
about 3 moles formaldehyde per mole phenol, and more preferably about 2.4 moles formaldehyde per mole phenol is useful with the invention. Where the source of further formaldehyde is a phenol-formaldehyde resin, the total resulting ratio of phenol to resorcinol (in the complete binder system) is preferably at least about 10 moles phenol per mole resorcinol. In addition, the total molar ratio of formaldehyde to phenol in the complete binder system may be about 1.8 moles formaldehyde per mole phenol.
The use of the above-described resins as curing agents, e.g., a phenol-formaldehyde resin, is beneficial not only because the PF resin functions as a curing agent, but because the PF resin contributes on 2i28912 its own as a binding agent. Because the PF resin is a binding a~ent, this provides a further advantage in that the PF resin preferably reduce the overall cost of the binder system due to the lower cost of phenol-formaldehyde resins.
In addition to phenol-formaldehyde resins, urea-formaldehyde or melamine-formaldehyde resins may be utilized as curing agents with the invention.
Alternatively (although less preferably), the curing agent may be hexamethylenetetramine or paraformaldehyde. Further, combination~ of any of the above-described curing agents may also be utilized.
An example of a preferred embodiment of the invention will now be de~cribed in conjunction with the production of a waferboard product. It is understood, however, that the inventive resin and binder system may be utilized in other processes, for example, in the manufacturing of plywood. According to the example, phenol, formaldehyde and water are first combined in a reaction vessel. The ingredients are mixed, followed by the addition of caustic to the mixture, preferably at a temperature below about 45C, to begin the condensation reaction. Because the reaction is generally highly exothermic, caustic is added slowly, preferably of over a period of time of, for example, about fifteen minutes.
The temperature of the reactants is allowed to increase stepwise until the temperature reaches about 65C. The reaction is preferably paused at previously determined increments, for example at 50C, 55C, and 60C. The temperature of the reaction is then preferably held at about 65C for about thirty minutes. An additional amount of caustic is may next be added, preferably at a temperature below 70C, for example. The reaction temperature is now allowed to increase to about 85C; the reaction mixture is heated, if necessary, to reach this temperature.
The reaction mixture i9 held at this temperature (about 85C) until the mixture reache~ a viscosity of about "B"-"C", as defined by the Gardner viscosity scale. When the reaction mixture attains ~` 212~9~2 this viscosity, resorcinol is added to the reactor, which is held at about 85C until the reactants attain the viscosity o~ about ~E~ F.~ Once the reaction mixture has reached this viscosity, the batch is cooled as fast as possible to about 25C. The reaction mixture need not be cooled prior to the addition of the modifier, e.g., resorcinol; such cooling is necessary in many prior art processes, for example, those processes disclosed in U.S. Patent Nos. 2,489,336 and 2,614,096. The resin is now suitable for pumping to storage.
The PRF resin may be stored as an aqueous liquid. If the resin is to be stored as an aqueous liquid, the resin is preferably not mixed with the phenol-formaldehyde curing agent until immediately prior to use in the manufacturing process, because such a mixture i9 not stable and might result in undesirable curing of the resin. However, if the resin is to be stored as a powder, the resin can be mixed with the phenol-formaldehyde curing agent immediately prior to the spray-drying (wherein the liquid form of the resin is made into a powder form). Although not necessary, both liquids (PRF and PF) may be mixed in-line immediately prior to blending with the cellulosic material, or to spray-drier. They may be al~o mixed in a separate tank before spray-drying or addition to cellulosic material. Such liquid mixture of PRF and PF
curing resin is stable for several hours.
A particular preferred resin formulation which may be used in the preceding example is shown in Table I below. In Table I, the two amounts of caustic soda reflect the above-described stepwise addition of caustic soda. It is understood, however, that many other variations of the inventive procedure are ;
possible~
; , . . . , .. . . ~ , . .. .. ... .
- 10 ~
TABLE I
Weight Percent (Ba~ed on Total ~onceutration Reactant Ingredients) of Solutio~
Phenol 34.22 Pure Formaldehyde 41.26 37 wt.%
Water 12.15 --Caustic soda 2.18 50 wt.%
Caustic soda 2.18 50 wt.~
Resorcinol 8.01 98 wt.%
Total 100.00 A resin produced in accordance with the example described above preferably has the properties outlined in Table II.
TABLE II
Property Value Non-volatiles 49.0-51.0 wt.%
Viscosity 75-150 cps Water Tolerance 250-400 wt.
Gel Time @ 100C > 60 min.
Spec. Grav. @20C about 1.15 g/mL
Free Formaldehyde ~ 0.1 wt.%
The resin produced by the above process may be used as a binder in the production of waferboard such as that described above. In one embodiment of the invention, in the production of waferboard, a liquid form of the resin is added along with a liquid form of a phenol-formaldehyde resin curing agent to wood flakes or wafers in a mixing vessel, followed by mechanical blending of the ingredients. Alternatively, the powder form of this two-component binder system may be added to the wood wafers as a one-component resin. The wood wafers may, for example, have a moisture content of less than about 20 wt.%. Optionally, other materials such as waxes (to improve water resistance and for :. ,. . . ~ . . ~
~ ~ , . ; ........................ , .:..... . - :
sizing properties) may be added to the waferboard, as is known in the art.
The mixed ingredients are formed into a mat and then cured under heat and pressure to form waferboard. As will be apparent to one of ordinary skill in the art, desirable pressing temperatures vary according to various factors, including the following:
the thickness of the board, the type of cellulosic material being pressed, the moisture content of the cellulosic material, the press time, and the type of resin which is utilized. However, for most applications, the press temperature is generally between about 200F and 500F, and preferably greater than 300F. For the production of waferboard as in the above example, the press temperature is preferably greater than 400F.
The moisture content of the cellulosic material (known as "furnish moisture content") is one factor which controls the core temperature of the mat which can be achieved under given press conditions.
Because the inventive resin system is very fast curing, one resulting advantage is that the binder system i3 - ~:
able to be cured at lower core temperatures than fast curing phenol-formaldehyde resins at a given furnish 25 moisture content, or at a furnish higher moisture -content at a given press temperature.
After the wood composite has been pressed, it may be immediately transported for coating, gluing, staining, or other finishing to complete a desired 30 product for commercial use. ~ ;
Boiling Water Gel Time ("BWGT"), which can be used as an indicator of resin activity, helps illustrate the effectiveness of the inventive binder system. A higher BWGT indicates a lower reactivity. A
PRF resin prepared in accordance with the above formulation generall~ has a BWGT of above 60 minutes.
In comparison, a fast curing phenol-formaldehyde resin used as the curing agent for the inventive PRF resin has a BWGT of about 23 minutes. However, when used in combination (i.e., where the PF resin is the curing agent for the PRF resin), at a weight ratio of about . : .- ~ - - -; - - : : ~: :
.
-` 212~912 1:1, the inventive binder system has a BW~T of about 13 to about 14 minutes.
Further, as can be seen from Table III below, the internal bond strength values of the wood composite (tested according to ASTM standards and expressed in psi) are significantly better where the binder is the inventive PRF/PF system than where a fast-curing PF
itself is the binder, for given cure times. (The furnish moisture content of the cellulosic material was about 9 percent and boards made with each type of resin were produced under the same conditions.) Table III
also lists the average, standard deviation, minimum value, and maximum value for each tested resin.
TABLE III
Internal Bond Strength (psi) - 180 Second Cook Time PF ReslnPRF with PF
,~, .. . , , ~ 2128912 PF Re~inPRF With PF
` 70 93 8 1 6 ~
AVG 66 . 891. 6 ~ :
STD. DEV. 14.0 18.7 :
M~X 1 0 012 5 ~:
It was also found that other propertie~ (such as water absorption, thickness swell, one hour boil caliper swell) are much better for the inventive binder 20 system, even at the shorter press times, than for known phenol-formaldehyde resins. The water absorption and thickness swell tests are performed by soaking a board for twenty-four hours at room temperature. In the one ;~
hour board caliper swell test, the boards are boiled 2 5 for one hour, followed ~y measuring the amount of swelling that has taken place. Further, as stated above, free formaldehyde emission out of the press is significantly lower with the inventive resin system than with conventional fast-curing phenol-formaldehyde resins.
The foregoing detailed description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications within the scope of the invention will be apparent to those skilled in the art.
:
BACKGROUND OF THE INVENTION
Field of the Invention The invention relates generally to the production of a modified phenol-aldehyde resin, and more particularly to the preparation and use of a modified phenol-aldehyde resin which utilizes an additional source of aldehyde, e.g., a phenol-formaldehyde resin, as a curing agent. The invention further relates to the use of such a cured resin as a binder in a process for the production of wood composites, e.g., plywood or fiberboard.
Description of Related Technolo~y Various processes may be used to produce wood composites depending on the desired final product which is desired. Synthetic resins, such as phenol-formaldehyde resins, are often used as binders in the manufacture of wood composites such as man-made pressed wood boards (e.g., waferboard, oriented strandboard ("OSB"), or fiberboard). Such wood composites may be formed in de~ired shapes and sizes depending on the intended use. Fiberboard, for example, may be made by various known processes including "dry" processes (e.g., a process comprising application of resin by a blender or by a blow line application), "wet"
processes, or "wet-dry" processes. Various known phenol-formaldehyde resins may also be utilized as binders in the manufacture of other wood composites such as plywood.
Several useful processes are described (for example, for the production of plywood and fiberboard) in U.S. Patent No. 4,961,795, the disclosure of which ~-is incorporated herein by reference.
Various fast-curing phenol-formaldehyde resins have been utilized as binders in the manufacture of wood composites. Typical fast curing phenol-formaldehyde resins have (a) a high molar ratio of formaldehyde to phenol and (b) a high caustic content ~,,. ~ .
~128912 in order to accelerate the curing process. However, such fast-curing resins are undesirable due to (a) high levels of free formaldehyde emission during pres~ing and (b~ the high caustic content which negatively impacts the resistance of the final product to moisture.
It is therefore desirable to produce a binder resin which (a) has a relatively fast cure time and/or (b) is resistant to high levels of moisture. In addition, it is desirable to produce a binder system in which undesirable amounts of formaldehyde will not be released into the atmosphere upon pressing. It is further desirable to produce a binder system which is convenient to use in a process such as the those described above.
SUM~RY OF THE INVENTION
It is an object of the invention to overcome one or more of the problems described above.
Accordingly, the invention provides a process for producing a modified phenol-aldehyde resin (e.g., a phenol-formaldehyde resin) useful in the production of wood composites, e.g., waferboard. The resin is preferably modified with a compound from one of the following classes: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines, including combinations thereof.
According to one feature of the invention, the inventive modified phenol-aldehyde resin is combined with a source of aldehyde (e.g., formaldehyde or a formaldehyde derivative) to form a binder system.
In a preferred embodiment of the invention, a binder system iB provided by supplying the modified phenol-aldehyde resin in combination with a curing agent which i8 an organic resin comprising formaldehyde.
In a further embodiment of the invention, the modified phenol-aldehyde resin is combined with a curing agent and cellulosic material (e.g., wood wafers) to form a mat. The mat is cured under heat and pressure to fonm a wood composite. Alternatively, the ': :
':
: . .
inventive resin may be combined with a curing agent and utilized as a binder in the manufacture of plywood.
Other objects and advantages of the invention will be apparent to those skilled in the art from the following detailed description, taken in conjunction with the appended claims.
DETAILED DESCRIPTION OF A PREFERR~D EMBODIMENT
According to the invention, a modified phenol-aldehyde resin is produced by first condensing phenol and an aldehyde in the presence of an alkaline cataly3t. The condensation product of phenol and the aldehyde is then further condensed with a modifier selected from one of the following (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. The resin may be incorporated with a curing agent (e.g., a phenol-formaldehyde resin) which provides a further source of aldehyde. The combination of the inventive resin and curing agent may comprise a binder system which is preferably blended with a cellulosic material (e.g., wood wafers or fibers) and formed into a wood composite, e.g., waferboard, fiberboard, or particleboard.
According to a preferred embodiment of the inventive process, formaldehyde (or a formaldehyde derivative or other aldehyde) and phenol (or a phenol derivative) are condensed, preferably at a temperature of about 65-70C, in a reactor in the presence of an alkaline catalyst (e.g., caustic) to achieve methylolation of phenol. Useful catalysts include those known in the art, for example, sodium hydroxide or potassium hydroxide. The reference herein to "phenol" denotes phenol derivatives, as well as phenol itself (i.e., hydroxybenzene). Derivatives of phenol include, for example, substituted phenols. Thus, the reference herein to "formaldehyde" does not limit the invention to formaldehyde, but denotes derivatives of formaldehyde, as well as formaldehyde itself, other aldehydes and derivatives of other aldehydes.
Derivatives of formaldehyde include, for example, paraformaldehyde and hexamethylenetetramine. The ratio ~'` ' . - . -; ~ - : . . .............................. .
.., ., 2l289l~
of aldehyde to phenol i~ preferably in the range of about 1.2 to about 2.0 moles aldehyde per mole phenol, more preferably about 1.3 to about 1.6 moles aldehyde per mole phenol, and most preferably about 1.4 moles aldehyde per mole phenol.
Although higher level~ of caustic may be utilized (especially for plywood applications), caustic is preferably added to the reaction mixture at about 0.1 to about 0.2 moles sodium hydroxide per mole of phenol. Such an amount of caustic preferably assures very beneficial wet properties of wood composites (e.g., tolerance to moisture), while allowing for sufficiently rapid cure. More caustic can be used to accelerate the resin cure process; however, a high caustic content may result in undesirable properties in the final product, including higher water absorption rates and thickness swell of the final wood composite ~;
product.
Following the condensation reaction between phenol and an aldehyde, the reactor is preferably heated to about 90C and held at this temperature to obtain a polymer of desired chain length. The desired chain length of the polymer, which varies depending upon the reactants and reaction conditions, will generally be based on a measurement of the viscosity of the initial condensation product, which may be referred to as a "PF pre-polymer."
An amount of a modifier (e.g., resorcinol) is added to this initial condensation product, preferably without the addition of further caustic, followed by continuation of the reaction until a desired chain length (e.g., a desired viscosity) is reached to produce what may be referred to as a "PRF pre-polymer"
or "PRF resin." The inventive resin is also referred to herein as a modified phenol-formaldehyde resin. The compounds which may be reacted with the phenol-formaldehyde pre-polymer include three classes of compounds: (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines. Examples of dihydroxybenzenes include resorcinol, hydroquinone, and catechol. Examples of aminophenols include ortho-~ 2~28912 hydroxyaniline, meta-hydroxyaniline, and para-hydroxyaniline. Examples of phenylenediamines include ortho-phenylenediamine, meta-phenylenediamine, and para-phenylenediamine. When resorcinol i9 referred to herein (e.g., in the examples or preferred ratios described below), any compound in these three classes may be utilized as an alternative to resorcinol, including combinations thereof. Thus, when the term "PRF resin" or "PRF pre-polymer" is used herein, this refers not only to a resin or pre-polymer including resorcinol, but includes any of the compounds described above. ~esorcinol, however, is the preferred compound.
The above-described sequential condensation reactions preferably use a molar ratio of phenol to resorcinol of about 1 to about 10 moles phenol per mole resorcinol, and more preferably about 5 to about 10 moles phenol per mole resorcinol. The ratio of formaldehyde to total phenolic compounds (i.e., phenol plus resorcinol) is preferably about 1 to about 1.8 ~ -~
20 moles formaldehyde per mole phenolics, more preferably --~
about 1.1 to about 1.4 moles formaldehyde per mole phenolics, and most preferably about 1.2 moles formaldehyde per mole phenolics (i.e., the molar ratio of formaldehyde to phenol plu9 resorcinol may be greater than 1).
Following the condensation of resorcinol (or one of the other suitable compounds described above), the reactor is cooled to ambient temperature for storage. The product resin, which may be referred to as a "PRF resin," is generally stable at ambient temperature for at least one month. The inventive PRF
resin is preferably utilized in conjunction with a curing agent (described below) as a blnder system in the manufacture, for example, of waferboard, fiberboard (e.g., medium density fiberboard or hardboard), oriented strandboard, plywood, and particleboard. In the binder system, the inventive resin exhibits very fast cure and excellent tolerance to high levels of moisture.
As stated above, the formaldehyde component of the inventive resin is not limited to formaldehyde '.-, ' ' - ~ :, .
i~self, but encompasses any formaldehyde derivative and other aldehydes or derivatives thereof which are known in the art to be useful in conjunction with phenol-formaldehyde resins. For example, the following 5 aldehydes are useful as the formaldehyde component of the invention: acetaldehyde,`glyoxal, and furaldehyde.
However, formaldehyde is the preferred aldehyde. Thus, it is understood tha~ when the formaldehyde component of the resin is referred to herein, this refers to 10 formaldehyde, formaldehyde derivatives, and other aldehydes.
In addition, although phenol itself is preferably utilized in order to produce a resin which can be made economically on a commercial scale, many 15 other compounds are useful as the phenol or phenol derivative of the present invention. Such useful phenols include substituted phenols such as cresols and 5 xylenols. Therefore, it is also understood that when the phenol component of the resin is referred to 20 herein, this refers to both phenol itself and phenol derivatives.
As is known in the art, a variety of modifiers may be incorporated into the phenol-resorcinol-formaldehyde resin in order to modify its 25 properties. These modifiers include, for example:
urea, melamine, lignins, tannins, sugars, starches, glycols, polyols, and mixtures thereof. The proportion of modifier incorporated into the resin typically ranges from about 5 to about 35 weight percent based 30 upon the phenolic component.
The inventive PRF resin produced by the above-described process may be satisfactorily utilized in any process that utilizes a conventional hot press.
For example, the inventive PRF resin preferably is able 35 to be cured while using an additional source of aldehyde in press cycles not longer than those typically observed for isocyanate resins, while at the same time the inventive resin yields a substrate with better weatherability properties.
Although the resin may be cured by itself at high temperatures, the cure rate of the resin is preferably accelerated by addition to the PRF resin of a source of further formaldehyde or other aldehyde.
The PRF resin and the source of further formaldehyde may be applied as a two-component binder system.
However, it must be emphasized that the PRF resin in combination with a PF resin (as a curing agent) can be easily spray-dried by a process known in the art and used as a one-component system. Any source of formaldehyde or other aldehyde may be used to accelerate the cure of the PRF resin.
According to a preferred embodiment of the invention, an organic resin comprising formaldehyde ~-~
(e.g., a fast-curing phenol-formaldehyde resin or a "PF
resin") is utilized as the curing agent. Any organic resin comprising formaldehyde, a formaldehyde derivative, or other aldehydes may be utilized. Thus, when a phenol-formaldehyde resin is referred to herein, reference i5 also made to the other resins described in the preceding sentence. However, a phenol-formaldehyde resin is the preferred curing agent. When using a PF
resin as the curing agent, the weight proportion of the PRF resin to PF resin is preferably about 0.25:1 to about 4:1, and more preferably about 0.6:1 to about 1.5:1. PF resins known in the art as binders in wood composites may be suitably utilized as the source of further formaldehyde. For example, a PF resin having a molar ratio of formaldehyde to phenol of about 2 to !
about 3 moles formaldehyde per mole phenol, and more preferably about 2.4 moles formaldehyde per mole phenol is useful with the invention. Where the source of further formaldehyde is a phenol-formaldehyde resin, the total resulting ratio of phenol to resorcinol (in the complete binder system) is preferably at least about 10 moles phenol per mole resorcinol. In addition, the total molar ratio of formaldehyde to phenol in the complete binder system may be about 1.8 moles formaldehyde per mole phenol.
The use of the above-described resins as curing agents, e.g., a phenol-formaldehyde resin, is beneficial not only because the PF resin functions as a curing agent, but because the PF resin contributes on 2i28912 its own as a binding agent. Because the PF resin is a binding a~ent, this provides a further advantage in that the PF resin preferably reduce the overall cost of the binder system due to the lower cost of phenol-formaldehyde resins.
In addition to phenol-formaldehyde resins, urea-formaldehyde or melamine-formaldehyde resins may be utilized as curing agents with the invention.
Alternatively (although less preferably), the curing agent may be hexamethylenetetramine or paraformaldehyde. Further, combination~ of any of the above-described curing agents may also be utilized.
An example of a preferred embodiment of the invention will now be de~cribed in conjunction with the production of a waferboard product. It is understood, however, that the inventive resin and binder system may be utilized in other processes, for example, in the manufacturing of plywood. According to the example, phenol, formaldehyde and water are first combined in a reaction vessel. The ingredients are mixed, followed by the addition of caustic to the mixture, preferably at a temperature below about 45C, to begin the condensation reaction. Because the reaction is generally highly exothermic, caustic is added slowly, preferably of over a period of time of, for example, about fifteen minutes.
The temperature of the reactants is allowed to increase stepwise until the temperature reaches about 65C. The reaction is preferably paused at previously determined increments, for example at 50C, 55C, and 60C. The temperature of the reaction is then preferably held at about 65C for about thirty minutes. An additional amount of caustic is may next be added, preferably at a temperature below 70C, for example. The reaction temperature is now allowed to increase to about 85C; the reaction mixture is heated, if necessary, to reach this temperature.
The reaction mixture i9 held at this temperature (about 85C) until the mixture reache~ a viscosity of about "B"-"C", as defined by the Gardner viscosity scale. When the reaction mixture attains ~` 212~9~2 this viscosity, resorcinol is added to the reactor, which is held at about 85C until the reactants attain the viscosity o~ about ~E~ F.~ Once the reaction mixture has reached this viscosity, the batch is cooled as fast as possible to about 25C. The reaction mixture need not be cooled prior to the addition of the modifier, e.g., resorcinol; such cooling is necessary in many prior art processes, for example, those processes disclosed in U.S. Patent Nos. 2,489,336 and 2,614,096. The resin is now suitable for pumping to storage.
The PRF resin may be stored as an aqueous liquid. If the resin is to be stored as an aqueous liquid, the resin is preferably not mixed with the phenol-formaldehyde curing agent until immediately prior to use in the manufacturing process, because such a mixture i9 not stable and might result in undesirable curing of the resin. However, if the resin is to be stored as a powder, the resin can be mixed with the phenol-formaldehyde curing agent immediately prior to the spray-drying (wherein the liquid form of the resin is made into a powder form). Although not necessary, both liquids (PRF and PF) may be mixed in-line immediately prior to blending with the cellulosic material, or to spray-drier. They may be al~o mixed in a separate tank before spray-drying or addition to cellulosic material. Such liquid mixture of PRF and PF
curing resin is stable for several hours.
A particular preferred resin formulation which may be used in the preceding example is shown in Table I below. In Table I, the two amounts of caustic soda reflect the above-described stepwise addition of caustic soda. It is understood, however, that many other variations of the inventive procedure are ;
possible~
; , . . . , .. . . ~ , . .. .. ... .
- 10 ~
TABLE I
Weight Percent (Ba~ed on Total ~onceutration Reactant Ingredients) of Solutio~
Phenol 34.22 Pure Formaldehyde 41.26 37 wt.%
Water 12.15 --Caustic soda 2.18 50 wt.%
Caustic soda 2.18 50 wt.~
Resorcinol 8.01 98 wt.%
Total 100.00 A resin produced in accordance with the example described above preferably has the properties outlined in Table II.
TABLE II
Property Value Non-volatiles 49.0-51.0 wt.%
Viscosity 75-150 cps Water Tolerance 250-400 wt.
Gel Time @ 100C > 60 min.
Spec. Grav. @20C about 1.15 g/mL
Free Formaldehyde ~ 0.1 wt.%
The resin produced by the above process may be used as a binder in the production of waferboard such as that described above. In one embodiment of the invention, in the production of waferboard, a liquid form of the resin is added along with a liquid form of a phenol-formaldehyde resin curing agent to wood flakes or wafers in a mixing vessel, followed by mechanical blending of the ingredients. Alternatively, the powder form of this two-component binder system may be added to the wood wafers as a one-component resin. The wood wafers may, for example, have a moisture content of less than about 20 wt.%. Optionally, other materials such as waxes (to improve water resistance and for :. ,. . . ~ . . ~
~ ~ , . ; ........................ , .:..... . - :
sizing properties) may be added to the waferboard, as is known in the art.
The mixed ingredients are formed into a mat and then cured under heat and pressure to form waferboard. As will be apparent to one of ordinary skill in the art, desirable pressing temperatures vary according to various factors, including the following:
the thickness of the board, the type of cellulosic material being pressed, the moisture content of the cellulosic material, the press time, and the type of resin which is utilized. However, for most applications, the press temperature is generally between about 200F and 500F, and preferably greater than 300F. For the production of waferboard as in the above example, the press temperature is preferably greater than 400F.
The moisture content of the cellulosic material (known as "furnish moisture content") is one factor which controls the core temperature of the mat which can be achieved under given press conditions.
Because the inventive resin system is very fast curing, one resulting advantage is that the binder system i3 - ~:
able to be cured at lower core temperatures than fast curing phenol-formaldehyde resins at a given furnish 25 moisture content, or at a furnish higher moisture -content at a given press temperature.
After the wood composite has been pressed, it may be immediately transported for coating, gluing, staining, or other finishing to complete a desired 30 product for commercial use. ~ ;
Boiling Water Gel Time ("BWGT"), which can be used as an indicator of resin activity, helps illustrate the effectiveness of the inventive binder system. A higher BWGT indicates a lower reactivity. A
PRF resin prepared in accordance with the above formulation generall~ has a BWGT of above 60 minutes.
In comparison, a fast curing phenol-formaldehyde resin used as the curing agent for the inventive PRF resin has a BWGT of about 23 minutes. However, when used in combination (i.e., where the PF resin is the curing agent for the PRF resin), at a weight ratio of about . : .- ~ - - -; - - : : ~: :
.
-` 212~912 1:1, the inventive binder system has a BW~T of about 13 to about 14 minutes.
Further, as can be seen from Table III below, the internal bond strength values of the wood composite (tested according to ASTM standards and expressed in psi) are significantly better where the binder is the inventive PRF/PF system than where a fast-curing PF
itself is the binder, for given cure times. (The furnish moisture content of the cellulosic material was about 9 percent and boards made with each type of resin were produced under the same conditions.) Table III
also lists the average, standard deviation, minimum value, and maximum value for each tested resin.
TABLE III
Internal Bond Strength (psi) - 180 Second Cook Time PF ReslnPRF with PF
,~, .. . , , ~ 2128912 PF Re~inPRF With PF
` 70 93 8 1 6 ~
AVG 66 . 891. 6 ~ :
STD. DEV. 14.0 18.7 :
M~X 1 0 012 5 ~:
It was also found that other propertie~ (such as water absorption, thickness swell, one hour boil caliper swell) are much better for the inventive binder 20 system, even at the shorter press times, than for known phenol-formaldehyde resins. The water absorption and thickness swell tests are performed by soaking a board for twenty-four hours at room temperature. In the one ;~
hour board caliper swell test, the boards are boiled 2 5 for one hour, followed ~y measuring the amount of swelling that has taken place. Further, as stated above, free formaldehyde emission out of the press is significantly lower with the inventive resin system than with conventional fast-curing phenol-formaldehyde resins.
The foregoing detailed description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications within the scope of the invention will be apparent to those skilled in the art.
:
Claims (38)
1. A method for the preparation of a modified phenol-aldehyde resin, comprising:
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde at a molar ratio of aldehyde to phenolic compound of about 1.2:1 to about 2.0:1, said reaction taking place in the presence of an alkaline catalyst present in an amount of about 0.1 to about 0.2 moles catalyst per mole of said phenolic compound; and (b) reacting a modifier comprising a compound selected from the group consisting of dihydroxybenzenes, aminophenols, and phenylenediamines with the product of step (a) wherein (1) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1 and (2) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1.
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde at a molar ratio of aldehyde to phenolic compound of about 1.2:1 to about 2.0:1, said reaction taking place in the presence of an alkaline catalyst present in an amount of about 0.1 to about 0.2 moles catalyst per mole of said phenolic compound; and (b) reacting a modifier comprising a compound selected from the group consisting of dihydroxybenzenes, aminophenols, and phenylenediamines with the product of step (a) wherein (1) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1 and (2) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1.
2. The method of claim 1 wherein said aldehyde comprises formaldehyde.
3. The method of claim 1 wherein:
said modifier comprises resorcinol.
said modifier comprises resorcinol.
4. The method of claim 1 wherein:
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1:1 to about 1.8:1.
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1:1 to about 1.8:1.
5. The method of claim 4 wherein:
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1:1 to about 1.4:1.
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1:1 to about 1.4:1.
6. The method of claim 5 wherein:
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1.2.
said molar ratio of said aldehyde to the total of said phenolic compound and said modifier is about 1.2.
7. The method of claim 1 wherein:
said molar ratio of aldehyde to said phenolic compound is about 1.3:1 to about 1.6:1.
said molar ratio of aldehyde to said phenolic compound is about 1.3:1 to about 1.6:1.
8. The method of claim 7 wherein:
said molar ratio of aldehyde to said phenolic compound is about 1.4:1.
said molar ratio of aldehyde to said phenolic compound is about 1.4:1.
9. The method of claim 1 wherein:
said molar ratio of said phenolic compound to said modifier is about 5:1 to about 10:1.
said molar ratio of said phenolic compound to said modifier is about 5:1 to about 10:1.
10. A resin made by the method of any one of claims 1-9.
11. The method of claim 1 wherein:
said modified phenol-aldehyde resin is combined with a curing agent comprising a source of an aldehyde to form a binder system useful in the production of a wood composite.
said modified phenol-aldehyde resin is combined with a curing agent comprising a source of an aldehyde to form a binder system useful in the production of a wood composite.
12. The method of claim 11 wherein:
said curing agent is selected from the group consisting of phenol-formaldehyde resins, urea-formaldehyde resins, melamine-formaldehyde resins, hexamethylenetetramine, formaldehyde and paraformaldehyde.
said curing agent is selected from the group consisting of phenol-formaldehyde resins, urea-formaldehyde resins, melamine-formaldehyde resins, hexamethylenetetramine, formaldehyde and paraformaldehyde.
13. The method of claim 11 wherein:
said curing agent is an organic resin comprising an aldehyde.
said curing agent is an organic resin comprising an aldehyde.
14. The method of claim 13 wherein:
said curing agent comprises a phenol-formaldehyde resin.
said curing agent comprises a phenol-formaldehyde resin.
15. The method of claim 14 wherein:
the weight ratio of said phenol-aldehyde resin to said modified phenol-aldehyde resin is about 0.25:1 to about 4.0:1.
the weight ratio of said phenol-aldehyde resin to said modified phenol-aldehyde resin is about 0.25:1 to about 4.0:1.
16. The method of any one of claims 13-15 wherein:
said binder system is in the form of a powder.
said binder system is in the form of a powder.
17. The method of any one of claims 13-15 wherein:
each of said modified phenol-aldehyde resin and said curing agent is in the form of a liquid.
each of said modified phenol-aldehyde resin and said curing agent is in the form of a liquid.
18. The method of claim 15 wherein:
the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.6:1 to about 1.5:1.
the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.6:1 to about 1.5:1.
19. The method of claim 15 wherein:
the total molar ratio of said phenolic compound to said modifier in said binder system is at least about 10:1.
the total molar ratio of said phenolic compound to said modifier in said binder system is at least about 10:1.
20. A method for the preparation of a binder system useful in the production of a wood composite, comprising:
(a) reacting a phenolic compound and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin; and (c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde to form said binder system.
(a) reacting a phenolic compound and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin; and (c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde to form said binder system.
21. The method of claim 20 wherein:
said organic resin comprises a phenol-formaldehyde resin, and wherein the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.25:1 to about 4.0:1.
said organic resin comprises a phenol-formaldehyde resin, and wherein the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.25:1 to about 4.0:1.
22. The method of claim 21 wherein:
the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.6:1 to about 1.5:1.
the weight ratio of said phenol-formaldehyde resin to said modified phenol-aldehyde resin is about 0.6:1 to about 1.5:1.
23. The method of claim 20 wherein:
(d) the molar ratio of said aldehyde of step (a) to said phenolic compound is about 1.2:1 to about 2.0:1;
(e) said alkaline catalyst is present in an amount of about 0.1 to about 0.2 moles per mole of said phenolic compound;
(f) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1;
and (g) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1.
(d) the molar ratio of said aldehyde of step (a) to said phenolic compound is about 1.2:1 to about 2.0:1;
(e) said alkaline catalyst is present in an amount of about 0.1 to about 0.2 moles per mole of said phenolic compound;
(f) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1;
and (g) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1.
24. The method of claim 23 wherein:
said molar ratio of said phenolic compound to said modifier is about 5:1 to about 10:1.
said molar ratio of said phenolic compound to said modifier is about 5:1 to about 10:1.
25. A binder system made by the method of any one of claims 20-24.
26. A method for the production of a wood composite, comprising:
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin;
(c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde to form a binder system;
(d) combining said binder system with a cellulosic filler;
(e) forming the product of step (d) into a mat; and (f) pressing said mat under heat to form a wood composite.
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin;
(c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde to form a binder system;
(d) combining said binder system with a cellulosic filler;
(e) forming the product of step (d) into a mat; and (f) pressing said mat under heat to form a wood composite.
27. The method of claim 26 wherein:
said mat has a moisture content of less than about 20 wt.%.
said mat has a moisture content of less than about 20 wt.%.
28. The method of claim 26 wherein:
said aldehyde of step (a) comprises formaldehyde.
said aldehyde of step (a) comprises formaldehyde.
29. The method of claim 26 wherein:
said modifier comprises resorcinol.
said modifier comprises resorcinol.
30. The method of claim 26 wherein:
said wood composite is selected from the group consisting of waferboard, fiberboard, oriented strandboard, and particleboard.
said wood composite is selected from the group consisting of waferboard, fiberboard, oriented strandboard, and particleboard.
31. A wood composite made by the method of any of claims 26-30.
32. A method for the production of a wood composite, comprising:
(a) reacting a phenolic compound comprising phenol or a phenol derivative and an aldehyde at a molar ratio of aldehyde to phenolic compound of about 1.2:1 to about 2.0:1, said reaction taking place in the presence of an alkaline catalyst present in an amount of about 0.1 to about 0.2 moles per mole of said phenolic compound; and (b) reacting a modifier comprising a compound selected from the groups consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) wherein (1) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1 and (2) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1;
(c) combining the product of step (b) with a phenol-aldehyde resin and a cellulosic filler;
(d) forming the product of step (c) into a mat; and (e) pressing said mat under to form a wood composite.
(a) reacting a phenolic compound comprising phenol or a phenol derivative and an aldehyde at a molar ratio of aldehyde to phenolic compound of about 1.2:1 to about 2.0:1, said reaction taking place in the presence of an alkaline catalyst present in an amount of about 0.1 to about 0.2 moles per mole of said phenolic compound; and (b) reacting a modifier comprising a compound selected from the groups consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) wherein (1) the molar ratio of said phenolic compound to said modifier is about 1:1 to about 10:1 and (2) the molar ratio of said aldehyde to the total of said phenolic compound and said modifier is greater than about 1:1;
(c) combining the product of step (b) with a phenol-aldehyde resin and a cellulosic filler;
(d) forming the product of step (c) into a mat; and (e) pressing said mat under to form a wood composite.
33. The method of claim 32 wherein:
said modifier comprises resorcinol.
said modifier comprises resorcinol.
34. The method of claim 32 wherein:
said aldehyde of step (a) comprises formaldehyde.
said aldehyde of step (a) comprises formaldehyde.
35. The method of claim 32 wherein:
said mat is pressed at greater than about 300°F.
said mat is pressed at greater than about 300°F.
36. A method for the production of plywood, comprising:
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin;
(c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde and an extender to form a binder system;
(d) placing said binder system on a wood panel;
(e) curing the product of step (d) under heat and pressure.
(a) reacting a phenolic compound comprising a phenol or a phenol derivative and an aldehyde in the presence of an alkaline catalyst;
(b) reacting a modifier comprising a compound selected from the group consisting of (1) dihydroxybenzenes, (2) aminophenols, and (3) phenylenediamines with the product of step (a) to form a modified phenol-aldehyde resin;
(c) combining said modified phenol-aldehyde resin with a curing agent which comprises an organic resin comprising an aldehyde and an extender to form a binder system;
(d) placing said binder system on a wood panel;
(e) curing the product of step (d) under heat and pressure.
37. The method of claim 36 wherein:
said aldehyde of step (a) comprises formaldehyde.
said aldehyde of step (a) comprises formaldehyde.
38. The method of claim 36 wherein:
said modifier comprises resorcinol.
said modifier comprises resorcinol.