CA2132595A1 - Polyol Composition Having Good Flow and Water Blown Rigid Polyurethane Foams Made Thereby Having Good Dimensional Stability - Google Patents

Polyol Composition Having Good Flow and Water Blown Rigid Polyurethane Foams Made Thereby Having Good Dimensional Stability

Info

Publication number
CA2132595A1
CA2132595A1 CA2132595A CA2132595A CA2132595A1 CA 2132595 A1 CA2132595 A1 CA 2132595A1 CA 2132595 A CA2132595 A CA 2132595A CA 2132595 A CA2132595 A CA 2132595A CA 2132595 A1 CA2132595 A1 CA 2132595A1
Authority
CA
Canada
Prior art keywords
polyol composition
good
polyol
dimensional stability
rigid polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA2132595A
Other languages
French (fr)
Other versions
CA2132595C (en
Inventor
Thomas L. Fishback
Curtis J. Reichel
Thomas B. Lee
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF Corp
Original Assignee
Thomas L. Fishback
Curtis J. Reichel
Thomas B. Lee
Basf Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Thomas L. Fishback, Curtis J. Reichel, Thomas B. Lee, Basf Corporation filed Critical Thomas L. Fishback
Publication of CA2132595A1 publication Critical patent/CA2132595A1/en
Application granted granted Critical
Publication of CA2132595C publication Critical patent/CA2132595C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A polyol composition is provided which when reacted with and organic isocyanate, has good flow characteristics and makes an all water blown rigid polyurethane foam having good dimensional stability at low core densities of 1.1 pcf to 2.0 pcf. The polyol composition has a polyol component which must have present a polyoxyalkylene polyether polyol having an equivalent weight of 130 or less, an average functionality of 3.1 or greater, and a hydroxyl number of 400 or more, a polyoxyalkylene polyether polyol having an average functionality from 1.5 to 3.1 and a viscosity of less than 800 cP at 25°C, and a polyoxyalkylene polyether polyol having an average functionality of greater than 3.1 and an equivalent weight of greater than 130. The polyol composition also has water as the blowing agent, and further contains a blow catalyst, a delayed action gel catalyst, and preferably a cure catalyst and a surfactant.
CA002132595A 1993-09-22 1994-09-21 Polyol composition having good flow and water blown rigid polyurethane foams made thereby having good dimensional stability Expired - Lifetime CA2132595C (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/125,070 1993-09-22
US12507093A 1993-09-23 1993-09-23

Publications (2)

Publication Number Publication Date
CA2132595A1 true CA2132595A1 (en) 1995-03-23
CA2132595C CA2132595C (en) 1999-03-16

Family

ID=22418061

Family Applications (1)

Application Number Title Priority Date Filing Date
CA002132595A Expired - Lifetime CA2132595C (en) 1993-09-22 1994-09-21 Polyol composition having good flow and water blown rigid polyurethane foams made thereby having good dimensional stability

Country Status (2)

Country Link
US (2) US5686500A (en)
CA (1) CA2132595C (en)

Families Citing this family (46)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19649829A1 (en) * 1996-12-02 1998-06-04 Bayer Ag Flexible polyurethane foams and a process for their production
CA2243006A1 (en) * 1997-09-22 1999-03-22 Egils Grinbergs Low density, low water, all mdi flexible foams
DE19746807A1 (en) * 1997-10-23 1999-04-29 Basf Ag Process for the production of polyurethane foams
US6660782B1 (en) * 1998-04-22 2003-12-09 Essex Specialty Products, Inc. Rigid polyurethane foams and method to form said foams using low molecular weight diols and triols
WO2000043431A1 (en) * 1999-01-26 2000-07-27 Accuflex Corporation Plasticized composition
TW444039B (en) * 1999-02-02 2001-07-01 Dow Chemical Co Open-celled polyurethane foams containing graphite which exhibit low thermal conductivity
US6753357B2 (en) * 2001-12-18 2004-06-22 Foam Supplies, Inc. Rigid foam compositions and method employing methyl formate as a blowing agent
JP4154654B2 (en) * 2002-09-13 2008-09-24 アキレス株式会社 Method for producing rigid polyurethane foam
DE10259267A1 (en) * 2002-12-17 2004-07-01 Basf Ag isocyanate adducts
US6846850B2 (en) * 2003-01-22 2005-01-25 Bayer Materialscience Llc Rigid polyurethane foams with improved properties
US7338983B2 (en) * 2004-02-10 2008-03-04 World Properties, Inc. Low density polyurethane foam, method of producing, and articles comprising the same
JP4378624B2 (en) * 2004-02-10 2009-12-09 株式会社イノアックコーポレーション Manufacturing method of sealing member
JP2007525581A (en) * 2004-02-28 2007-09-06 コリア ユニバーシティ インダストリアル アンド アカデミック コラボレイション ファウンデーション Clay-polyurethane nanocomposite and method for producing the same
US7151121B2 (en) * 2004-05-26 2006-12-19 Danisco A/S Polyurethane containing a polyol composition comprising a highly branched polysaccharide, mix and process for preparation thereof
DK1773902T3 (en) * 2004-08-04 2018-02-05 Foam Supplies Inc REACTIVITY DIFFERENCE AND CATALYSTS DEGREE IN POLYURETHAN
US7469437B2 (en) 2005-06-24 2008-12-30 Tempur-Pedic Management, Inc. Reticulated material body support and method
US9315612B2 (en) * 2005-07-27 2016-04-19 Certainteed Corporation Composite material including rigid foam with inorganic fillers
CN1911979B (en) * 2005-08-11 2011-04-20 环球产权公司 Low-density polyurethane foam, production method and product composition
US20070149656A1 (en) * 2005-12-23 2007-06-28 3M Innovative Properties Company Sprayable mining liner composition
US20070222105A1 (en) * 2006-03-24 2007-09-27 Century-Board Usa, Llc Extrusion of polyurethane composite materials
KR101454498B1 (en) * 2007-01-09 2014-10-24 바스프 에스이 Water-blown rigid foams for the insulation of liquefied natural gas tanks
WO2008094238A1 (en) * 2007-01-30 2008-08-07 Dow Global Technologies, Inc. Ortho-cyclohexanediamine-initiated polyols and rigid polyurethane foam made therefrom
KR100969016B1 (en) * 2007-12-13 2010-07-09 현대자동차주식회사 Polyurethane foam for steering wheel having improved water resistance
ATE548401T1 (en) * 2008-03-20 2012-03-15 Basf Se POLYURETHANE SYSTEMS FOR THE PRODUCTION OF POLYURETHANE SANDWICH PARTS AT LOW MOLDING TEMPERATURES
WO2010062636A1 (en) * 2008-10-28 2010-06-03 Therma-Tru Corp Low-density filled polyurethane foam
EP2184305A1 (en) * 2008-11-07 2010-05-12 Bayer MaterialScience AG PIR hard foams, method for their manufacture and application thereof
WO2010066635A1 (en) * 2008-12-10 2010-06-17 Basf Se Water-blown rigid foams with improved mechanical properties at low temperatures
US9481759B2 (en) 2009-08-14 2016-11-01 Boral Ip Holdings Llc Polyurethanes derived from highly reactive reactants and coal ash
US8846776B2 (en) 2009-08-14 2014-09-30 Boral Ip Holdings Llc Filled polyurethane composites and methods of making same
AU2010300146A1 (en) 2009-09-29 2012-04-19 Basf Se Process for producing rigid polyurethane foams
CN102844165B (en) * 2009-12-18 2015-01-28 巴斯夫欧洲公司 Polyurethane composite system having high compressive strength and rigidity
AU2012318528A1 (en) 2011-10-07 2014-05-22 Boral Ip Holdings (Australia) Pty Limited Inorganic polymer/organic polymer composites and methods of making same
CA2838056C (en) 2012-12-21 2021-07-13 Michael L. Jackson Rigid polyurethane foam with high adhesion properties
WO2014168633A1 (en) 2013-04-12 2014-10-16 Boral Ip Holdings (Australia) Pty Limited Composites formed from an absorptive filler and a polyurethane
JP6254447B2 (en) * 2014-02-07 2017-12-27 株式会社ブリヂストン Polyurethane foam
US10138341B2 (en) 2014-07-28 2018-11-27 Boral Ip Holdings (Australia) Pty Limited Use of evaporative coolants to manufacture filled polyurethane composites
US9752015B2 (en) 2014-08-05 2017-09-05 Boral Ip Holdings (Australia) Pty Limited Filled polymeric composites including short length fibers
WO2016118141A1 (en) 2015-01-22 2016-07-28 Boral Ip Holdings (Australia) Pty Limited Highly filled polyurethane composites
WO2016195717A1 (en) 2015-06-05 2016-12-08 Boral Ip Holdings (Australia) Pty Limited Filled polyurethane composites with lightweight fillers
ES2932186T3 (en) 2015-06-18 2023-01-16 Basf Se Procedure for the manufacture of rigid polyurethane foams
US20170267585A1 (en) 2015-11-12 2017-09-21 Amitabha Kumar Filled polyurethane composites with size-graded fillers
JP2017095553A (en) * 2015-11-19 2017-06-01 コベストロ、ドイチュラント、アクチエンゲゼルシャフトＣｏｖｅｓｔｒｏ Ｄｅｕｔｓｃｈｌａｎｄ Ａｇ Method for producing hard polyurethane foam
WO2020002282A1 (en) * 2018-06-28 2020-01-02 Covestro Deutschland Ag Rigid polyurethane foams
US10851196B2 (en) * 2019-04-29 2020-12-01 Covestro Llc Rigid polyurethane foams suitable for use as panel insulation
CN112646121A (en) * 2020-12-11 2021-04-13 淄博汇德聚氨酯制品股份有限公司 Polyurethane rigid foam thermal insulation material, and preparation method and application thereof
US11827735B1 (en) 2022-09-01 2023-11-28 Covestro Llc HFO-containing isocyanate-reactive compositions, related foam-forming compositions and flame retardant PUR-PIR foams

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2932621A (en) * 1956-02-07 1960-04-12 Pittsburgh Plate Glass Co Preparation of polyurethane foam utilizing a salt of dimethylethanol amine and a dicarboxylic acid as a catalyst
US3509077A (en) * 1966-07-07 1970-04-28 Allied Chem Rigid polyurethane foams from certain polyether mixtures
US3489698A (en) * 1967-05-03 1970-01-13 Union Carbide Corp Stable emulsions of incompatible polyols containing ethylene oxide-propylene oxide block copolymers as emulsifiers
DE2854384A1 (en) * 1978-12-16 1980-07-03 Bayer Ag METHOD FOR PRODUCING POLYURETHANE PLASTICS
US4456696A (en) * 1981-04-09 1984-06-26 Abbott Laboratories Catalyst for making polyurethanes
US4467089A (en) * 1982-03-04 1984-08-21 Air Products And Chemicals, Inc. Carbamate and carbonate salts of tertiary amines
US4450246A (en) * 1982-10-26 1984-05-22 W. R. Grace & Co. Novel polyurethane catalysts in polyurethane foam process
US4525491A (en) * 1982-12-24 1985-06-25 Asahi Glass Company, Ltd. Process for producing a polyurethane elastomer by reaction injection molding
DE3329452A1 (en) * 1983-08-16 1985-03-07 Bayer Ag, 5090 Leverkusen METHOD FOR PRODUCING CELL-SHAPED POLYURETHANES, IF ANY
JPS6058418A (en) * 1983-09-08 1985-04-04 Toyo Soda Mfg Co Ltd Catalyst for polyurethane exhibiting delayed activity
US4582861A (en) * 1984-11-13 1986-04-15 Air Products And Chemicals, Inc. Delayed action/enhanced curing catalysis in polyurethane systems
USRE33609E (en) * 1987-07-23 1991-06-11 Mobay Corporation Production of polyurethane moldings by the reaction injection molding process
US4792576A (en) * 1987-07-23 1988-12-20 Mobay Corporation Production of polyurethane moldings by the reaction injection molding process
US4742089A (en) * 1987-08-12 1988-05-03 Hitachi, Ltd. Rigid polyurethane foam and process for producing the same
JPH01170612A (en) * 1987-12-26 1989-07-05 Bridgestone Corp Production of polyurethane foam
DE3806476A1 (en) * 1988-03-01 1989-09-14 Bayer Ag METHOD FOR PRODUCING CALINARY POLYURETHANIC SOFT FORMULA MATERIALS WITH EXCELLENT DAWNING PROPERTIES
US4929646A (en) * 1988-04-26 1990-05-29 The Dow Chemical Company Polyurethane foam prepared using high functionality cell openers
US5194175A (en) * 1989-07-24 1993-03-16 Foam Supplies, Inc. Rigid foams, methods for preparation thereof and compositions useful in methods and preparations thereof
JP2854028B2 (en) * 1989-08-02 1999-02-03 武田薬品工業株式会社 Manufacturing method of rigid urethane foam
JP2917319B2 (en) * 1989-10-19 1999-07-12 株式会社ブリヂストン Method for producing low-density flexible polyurethane foam
JPH03199223A (en) * 1989-12-27 1991-08-30 Achilles Corp Polyurethane foam for cushioning material
JPH04126732A (en) * 1990-06-11 1992-04-27 Dainippon Ink & Chem Inc Production of urethane foam
US5248703A (en) * 1992-03-13 1993-09-28 Basf Corporation Rigid polyurethane foams containing lithium salts for energy absorbing applications
TW293827B (en) * 1992-04-20 1996-12-21 Takeda Pharm Industry Co Ltd
US5478494A (en) * 1993-09-22 1995-12-26 Basf Corporation Polyol composition having good flow and formic acid blown rigid polyurethane foams made thereby having good dimensional stability

Also Published As

Publication number Publication date
US5798533A (en) 1998-08-25
US5686500A (en) 1997-11-11
CA2132595C (en) 1999-03-16

Similar Documents

Publication Publication Date Title
CA2132595A1 (en) Polyol Composition Having Good Flow and Water Blown Rigid Polyurethane Foams Made Thereby Having Good Dimensional Stability
CA2132597A1 (en) Polyol Composition Having Good Flow and Formic Acid Blown Rigid Polyurethane Foams Made Thereby Having Good Dimensional Stability
CA2206551A1 (en) Three component polyol blend for use in insulating rigid polyurethane foams
KR930012851A (en) Polyol composition
CA2324359A1 (en) Polyurethane prepolymer compositions, foams made therefrom and methods of making each thereof
CA2032737A1 (en) A process for the production of open-cell, cold-formable rigid polyurethane foams and their use for the production of molded articles
CA2363970A1 (en) Sprayable autofrothing polyisocyanate foam and delivery system
AU2002357617A1 (en) Low-resilience flexible polyurethane foam and process for producing the same
CA2182740A1 (en) Insulating rigid polyurethane foams
CA2241627A1 (en) Poly(oxypropylene/oxyethylene) random polyols useful in preparing flexible high resilience foam with reduced tendencies toward shrinkage and foam prepared therewith
CA2165116A1 (en) Dimensionally stable closed cell rigid polyisocyanate based foam prepared from a froth foaming mixture
WO2002050148A3 (en) Polyurethane compositions useful as shock absorbers and a method for their preparation
WO2003051097A3 (en) Rigid foam compositions and methods employing alkyl alkanoates as a blowing agent
TW200516093A (en) Flexible polyurethane foam and process for producing the same
CA2380301A1 (en) Use of low unsaturated polyether polyols in slabstock foam applications
CA2182739A1 (en) A method of making insulating rigid polyurethane foams
EP0822228A3 (en) Recycling of flexible foam to prepare polyether polyols
EP0337614A3 (en) Improved open-celled polyurethane foams
CA2113946A1 (en) Process for making flexible foams
CA2443130A1 (en) Energy absorbing flexible foams produced in part with a double metal cyanide catalyzed polyol
NZ331944A (en) A polyol mixture of an aromatic amine-starter polyether, a sucrose-started polyether and a propylene glycol-started polyether is used for producing hydrocarbon-blown hard polyurethane foams
CA2182741A1 (en) Insulating rigid polyurethane foam compositions
CA2107291A1 (en) A novel polyether polyol, production of a flexible urethane foam and shaped article therefrom
JP2002512277A5 (en)
ATE483741T1 (en) METHOD FOR PRODUCING POLYISOCYANURATE-MODIFIED POLYURETHANE FOAM

Legal Events

Date Code Title Description
EEER Examination request
MKEX Expiry

Effective date: 20140922