CA2225072C - Fiber reinforced aluminum matrix composite - Google Patents
Fiber reinforced aluminum matrix composite Download PDFInfo
- Publication number
- CA2225072C CA2225072C CA002225072A CA2225072A CA2225072C CA 2225072 C CA2225072 C CA 2225072C CA 002225072 A CA002225072 A CA 002225072A CA 2225072 A CA2225072 A CA 2225072A CA 2225072 C CA2225072 C CA 2225072C
- Authority
- CA
- Canada
- Prior art keywords
- matrix
- fibers
- aluminum
- composite material
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
A composite metal matrix formed of polycrystalline .alpha.-Al2O3 fibers encapsulated within a matrix of substantially pure elemental aluminum, or an alloy elemental aluminum and up to about 2 % copper is disclosed. The resulting materials are characterized by their high strength and low weight are particularly well suited for applications in various industries including high voltage power transmission.
Description
FIBER REINFORCED ALUMTNUM MATRIX COMPOSTTE
Government License Rights The U.S. Government Iias a paid-up license in this invention and the right in limited circumstances to require the patent owner to license others on reasotiable terms as provided for by the terms of contract No. MDA 972-90-C-0018 awarded by the Defense Advanced Research Projects Agency (DARPA).
Field of the Invention The present invention pertains to composite materials of ceramic fibers within in an aluminum matrix. Such materials are well-suited for various applications in which high strength, low weight materials are required.
Background of the Invention Continuous fiber reiniorced aluniinum matrix cotnposites (CF-AMCs) offer exceptional specific properties when compared to conventional alloys and to particulate metal matrix composites. The longitudinal stiffness of such composite materials is typically three times that of conventional alloys, and the specific strength of such composites is typically twice tiiat of high-strength steel or aluininum alloys. Furthermore, for niany applications, CF-AMCs are particularly attractive when compared to graphite-polymer coniposites due to their more moderate anisotropy in properties, particularly their high strength in directions different that those of the fiber axes. Additionally, CF-AMCs offer substantial improvements in allowable service temperature ranges and do not suffer from environmental problems typically encountered by polynieric matrix composites.
Such problems include delaminatio*i and degradation in hot and humid environments, particulai-ly when exposed to ultraviolet (UV) radiation.
Despite their numerous advantages, known CF-E~J'VICs suffer drawbacks which have hampered their use in many engineering applications. CF-AMCs generally feature high modulus or high strength, but seldoni combine both properties. This featui=e is taught in Table V of R.B. B'rlagat, "C.asting Fiber--l-Reinforced Metal Matrix Composites", in Metal Matrix Composites: Processing and Interfaces, R.K. Everett and R.J. Arsenault Eds., Academic Press, 1991, pp. 43-82.
In that reference, properties listed for cast CF-AMC only combine a strength in excess of 1 GPa with a modulus in excess of 160 GPa in high-strength carbon-reinforced aluminum, a composite which suffers from low transverse strength, low compressive strength, and poor corrosion resistance. At the present time, the most satisfactory approach for producing CF-AMCs in which high strength in all directions is combined with a high modulus in all directions is with fibers produced by chemical vapor deposition. The resulting fibers, typically boron, are very expensive, too large to be wound into preforms having a small-radius of curvature, and chemically reactive in molten aluminum. Each of these factors significantly reduces the processability and commercial desirability of the fiber.
Furthermore, composites such as aluminum oxide (alumina) fibers in aluminum alloy matrices suffer from additional drawbacks during their manufacture.
In particular, during the production of such composite materials, it has been found to be difficult to cause the matrix material to completely infiltrate fiber bundles.
Also, many composite metal materials known in the art suffer from insufficient long-term stability as a result of chemical interactions which can take place between the fibers and the surrounding matrix, resulting in fiber degradation over time. In still other instances, it has been found to be difficult to cause the matrix metal to completely wet the fibers. Although attempts have been made to overcome these problems (notably, providing the fibers with chemical coatings to increase wetability and limit chemical degradation, and using pressure differentials to assist matrix infiltration) such attempts have met with only limited success. For example, the resulting matrices have, in some instances, been shown to have decreased physical characteristics. Furthermore, fiber coating methods typically require the addition of several complicated process steps during the manufacturing process.
In view of the above, a need exists for ceramic fiber metal composite materials that offer improved strength and weight characteristics, are free of long term degradation, and which may be produced using a minimum of process steps.
Government License Rights The U.S. Government Iias a paid-up license in this invention and the right in limited circumstances to require the patent owner to license others on reasotiable terms as provided for by the terms of contract No. MDA 972-90-C-0018 awarded by the Defense Advanced Research Projects Agency (DARPA).
Field of the Invention The present invention pertains to composite materials of ceramic fibers within in an aluminum matrix. Such materials are well-suited for various applications in which high strength, low weight materials are required.
Background of the Invention Continuous fiber reiniorced aluniinum matrix cotnposites (CF-AMCs) offer exceptional specific properties when compared to conventional alloys and to particulate metal matrix composites. The longitudinal stiffness of such composite materials is typically three times that of conventional alloys, and the specific strength of such composites is typically twice tiiat of high-strength steel or aluininum alloys. Furthermore, for niany applications, CF-AMCs are particularly attractive when compared to graphite-polymer coniposites due to their more moderate anisotropy in properties, particularly their high strength in directions different that those of the fiber axes. Additionally, CF-AMCs offer substantial improvements in allowable service temperature ranges and do not suffer from environmental problems typically encountered by polynieric matrix composites.
Such problems include delaminatio*i and degradation in hot and humid environments, particulai-ly when exposed to ultraviolet (UV) radiation.
Despite their numerous advantages, known CF-E~J'VICs suffer drawbacks which have hampered their use in many engineering applications. CF-AMCs generally feature high modulus or high strength, but seldoni combine both properties. This featui=e is taught in Table V of R.B. B'rlagat, "C.asting Fiber--l-Reinforced Metal Matrix Composites", in Metal Matrix Composites: Processing and Interfaces, R.K. Everett and R.J. Arsenault Eds., Academic Press, 1991, pp. 43-82.
In that reference, properties listed for cast CF-AMC only combine a strength in excess of 1 GPa with a modulus in excess of 160 GPa in high-strength carbon-reinforced aluminum, a composite which suffers from low transverse strength, low compressive strength, and poor corrosion resistance. At the present time, the most satisfactory approach for producing CF-AMCs in which high strength in all directions is combined with a high modulus in all directions is with fibers produced by chemical vapor deposition. The resulting fibers, typically boron, are very expensive, too large to be wound into preforms having a small-radius of curvature, and chemically reactive in molten aluminum. Each of these factors significantly reduces the processability and commercial desirability of the fiber.
Furthermore, composites such as aluminum oxide (alumina) fibers in aluminum alloy matrices suffer from additional drawbacks during their manufacture.
In particular, during the production of such composite materials, it has been found to be difficult to cause the matrix material to completely infiltrate fiber bundles.
Also, many composite metal materials known in the art suffer from insufficient long-term stability as a result of chemical interactions which can take place between the fibers and the surrounding matrix, resulting in fiber degradation over time. In still other instances, it has been found to be difficult to cause the matrix metal to completely wet the fibers. Although attempts have been made to overcome these problems (notably, providing the fibers with chemical coatings to increase wetability and limit chemical degradation, and using pressure differentials to assist matrix infiltration) such attempts have met with only limited success. For example, the resulting matrices have, in some instances, been shown to have decreased physical characteristics. Furthermore, fiber coating methods typically require the addition of several complicated process steps during the manufacturing process.
In view of the above, a need exists for ceramic fiber metal composite materials that offer improved strength and weight characteristics, are free of long term degradation, and which may be produced using a minimum of process steps.
Summary of the Invention According to one aspect of the present invention, there is provided a composite material comprising a plurality of continuous polycrystalline a-A1203 fibers having an average tensile strength of at least about 2.8 GPa contained within a matrix selected from the group consisting of an aluminum matrix and a matrix of an alloy of aluminum and up to about 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrices contain less than 0.05 percent by weight impurities, based on the total weight of said matrices, wherein said matrix being free of material phases or domains capable of the enhancing brittleness of said matrix, and wherein said composite material has an average tensile strength of greater than 1.17 GPa.
According to a further aspect of the present invention, there is provided a wire comprising a composite material as defined herein.
According to another aspect of the present invention, there is provided an overhead high voltage power transmission cable which comprises a plurality of wires as described herein.
According to yet another aspect of the present invention, there is provided a method of making continuous composite wire, said method comprising: melting a metallic matrix material selected from the group consisting of aluminum and an alloy of aluminum with up to 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrix material contain less than 0.05 percent by weight impurities, based on the total weight of said matrix materials, to provide a contained volume of melted metallic matrix material; imparting ultrasonic energy to cause vibration of said contained volume of melted metallic matrix material; immersing a plurality of continuous polycrystalline a-A1z03 fibers having an average tensile strength of at least about 2.8 GPa into said contained volume of melted metallic matrix material while maintaining said vibration to permit the melted metallic matrix material to infiltrate into and coat said plurality of fibers such that an infiltrated, coated plurality of fibers is provided;
and withdrawing said infiltrated, coated plurality of fibers from said contained volume of melted metallic matrix material under conditions which permit the melted metallic matrix material to solidify to provide a wire as described herein.
The present invention relates to continuous fiber aluminum matrix composites having wide industrial applicability. Embodiments of the present invention pertain to continuous fiber aluminum matrix composites having continuous high-strength, high-stiffness fibers contained within a matrix material that is free of contaminants likely to cause brittle intermetallic compounds or phases, or segregated domains of contaminant material at the matrix/fiber interface. The matrix material is selected to have a relatively low yield-strength whereas the fibers are selected to have a relatively high tensile strength.
Furthermore, the materials are selected such that the fibers are relatively chemically inert both in the molten and solid phases of the matrix.
Certain embodiments of the present invention relate - 3a -to composite materials having continuous tows of polycrystalline a-A1203 fibers having an average tensile strength of about 2.8 GPa contained within a matrix of elemental aluminum having a yield-strength of not greater than about 20 MPa or an alloy of elemental aluminum containing up to about 2% by weight copper (based on the total weight of the matrix) having a yield-strength of not greater than about 90 MPa. Such composite structures offer high strength and low weight, while at the same time avoid the potential for long term degradation. Such composites may also be made without the need for many of the process steps associated with prior art composite materials.
In one embodiment, the continuous fiber aluminum matrix composites of the present invention are formed into wires exhibiting desirable strength-to-weight characteristics and high electrical conductivity. Such wires are well-suited for use as core materials in high voltage power transmission (HVPT) cables, as they provide electrical and physical characteristics which offer improvements over HVPT cables known in the prior art.
One wire according to the present invention comprises a composite material comprising a tow of continuous polycrystalline a-A12O3 fibers within a matrix, wherein the polycrystalline a-A12O3 fibers have an average tensile strength of at least about 2.8 GPa, wherein the matrix is selected from the group consisting of substantially pure elemental aluminum and an alloy of elemental aluminum and up to about 201 by weight copper, based on the total weight of the matrix, and wherein the wire has an average tensile strength of greater than 1.17 GPa (170 ksi) (or even at least 1.38 GPa (200 ksi), or at least 1.72 GPa (250 ksi)).
Another wire according to the present invention comprises a composite material comprising a tow of continuous polycrystalline a-A12O3 fibers within a matrix selected from the group consisting of substantially pure elemental aluminum and an alloy of elemental aluminum and up to about 2o by weight copper, based on the total weight of the matrix, wherein the wire has an average tensile strength of at least 1.17 GPa (170 ksi) (or even at least 1.38 GPa (200 ksi), or at least 1.52 GPa (220 ksi) or at least 1.72 GPa (250 ksi)).
Brief Description of the Drawings FIG. 1 is a schematic representation of an apparatus for producing composite metal matrix wires using ultrasonic energy.
FIGS. 2a and 2b are schematic, cross-sections of two embodiments of overhead high voltage transmission cables having composite metal matrix cores.
FIG. 3 is a chart comparing strength-to-weight ratios for materials of the present invention with other materials.
FIGS. 4a and 4b are graphs comparing projected sag as a function of span length for various cables.
FIG. 5 is a graph showing the coefficient of thermal expansion as a function of temperature for a CF-AMC wire.
According to a further aspect of the present invention, there is provided a wire comprising a composite material as defined herein.
According to another aspect of the present invention, there is provided an overhead high voltage power transmission cable which comprises a plurality of wires as described herein.
According to yet another aspect of the present invention, there is provided a method of making continuous composite wire, said method comprising: melting a metallic matrix material selected from the group consisting of aluminum and an alloy of aluminum with up to 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrix material contain less than 0.05 percent by weight impurities, based on the total weight of said matrix materials, to provide a contained volume of melted metallic matrix material; imparting ultrasonic energy to cause vibration of said contained volume of melted metallic matrix material; immersing a plurality of continuous polycrystalline a-A1z03 fibers having an average tensile strength of at least about 2.8 GPa into said contained volume of melted metallic matrix material while maintaining said vibration to permit the melted metallic matrix material to infiltrate into and coat said plurality of fibers such that an infiltrated, coated plurality of fibers is provided;
and withdrawing said infiltrated, coated plurality of fibers from said contained volume of melted metallic matrix material under conditions which permit the melted metallic matrix material to solidify to provide a wire as described herein.
The present invention relates to continuous fiber aluminum matrix composites having wide industrial applicability. Embodiments of the present invention pertain to continuous fiber aluminum matrix composites having continuous high-strength, high-stiffness fibers contained within a matrix material that is free of contaminants likely to cause brittle intermetallic compounds or phases, or segregated domains of contaminant material at the matrix/fiber interface. The matrix material is selected to have a relatively low yield-strength whereas the fibers are selected to have a relatively high tensile strength.
Furthermore, the materials are selected such that the fibers are relatively chemically inert both in the molten and solid phases of the matrix.
Certain embodiments of the present invention relate - 3a -to composite materials having continuous tows of polycrystalline a-A1203 fibers having an average tensile strength of about 2.8 GPa contained within a matrix of elemental aluminum having a yield-strength of not greater than about 20 MPa or an alloy of elemental aluminum containing up to about 2% by weight copper (based on the total weight of the matrix) having a yield-strength of not greater than about 90 MPa. Such composite structures offer high strength and low weight, while at the same time avoid the potential for long term degradation. Such composites may also be made without the need for many of the process steps associated with prior art composite materials.
In one embodiment, the continuous fiber aluminum matrix composites of the present invention are formed into wires exhibiting desirable strength-to-weight characteristics and high electrical conductivity. Such wires are well-suited for use as core materials in high voltage power transmission (HVPT) cables, as they provide electrical and physical characteristics which offer improvements over HVPT cables known in the prior art.
One wire according to the present invention comprises a composite material comprising a tow of continuous polycrystalline a-A12O3 fibers within a matrix, wherein the polycrystalline a-A12O3 fibers have an average tensile strength of at least about 2.8 GPa, wherein the matrix is selected from the group consisting of substantially pure elemental aluminum and an alloy of elemental aluminum and up to about 201 by weight copper, based on the total weight of the matrix, and wherein the wire has an average tensile strength of greater than 1.17 GPa (170 ksi) (or even at least 1.38 GPa (200 ksi), or at least 1.72 GPa (250 ksi)).
Another wire according to the present invention comprises a composite material comprising a tow of continuous polycrystalline a-A12O3 fibers within a matrix selected from the group consisting of substantially pure elemental aluminum and an alloy of elemental aluminum and up to about 2o by weight copper, based on the total weight of the matrix, wherein the wire has an average tensile strength of at least 1.17 GPa (170 ksi) (or even at least 1.38 GPa (200 ksi), or at least 1.52 GPa (220 ksi) or at least 1.72 GPa (250 ksi)).
Brief Description of the Drawings FIG. 1 is a schematic representation of an apparatus for producing composite metal matrix wires using ultrasonic energy.
FIGS. 2a and 2b are schematic, cross-sections of two embodiments of overhead high voltage transmission cables having composite metal matrix cores.
FIG. 3 is a chart comparing strength-to-weight ratios for materials of the present invention with other materials.
FIGS. 4a and 4b are graphs comparing projected sag as a function of span length for various cables.
FIG. 5 is a graph showing the coefficient of thermal expansion as a function of temperature for a CF-AMC wire.
Detailed Description The fiber reinforced aluminum matrix composites of the present invention comprise continuous fibers of polycrystalline a-A12O3 encapsulated within either a matrix of substantially pure elemental aluminum or an alloy of pure aluminum with up to about 2o by weight copper, based on the total weight of the matrix. The preferred fibers comprise equiaxed grains of less than about 100 nm in size, and a fiber diameter in the range of about 1-50 micrometers. A fiber diameter in the range of about 5-25 micrometers is preferred with a range of about 5-15 micrometers being most preferred.
Preferred composite materials according to the present invention have a fiber density of between about 3.90-3.95 grams per cubic centimeter. Among the preferred fibers are those described in U.S. Patent No. 4,954,462 (Wood et al., assigned to Minnesota Mining and Manufacturing Company, St.
Paul, MN). Such fibers are available commercially under the designation NEXTELTM 610 Ceramic Fibers from the Minnesota Mining and Manufacturing Company, St. Paul, MN. The encapsulating matrix is selected to be such that it does not react chemically with the fiber material (i.e., is relatively chemically inert with respect to the fiber material), thereby eliminating the need to provide a protective coating on the fiber exterior.
As used herein, the term "polycrystalline" means a material having predominantly a plurality of crystalline grains in which the grain size is less than the diameter of the fiber in which the grains are present. The term "continuous" is intended to mean a fiber having a length which is relatively infinite when compared to the fiber diameter.
In practical terms, such fibers have a length on the order of about 15 cm to at least several meters, and may even have lengths on the order of kilometers or more.
In the preferred embodiments, the use of a matrix comprising either substantially pure elemental aluminum, or an alloy of elemental aluminum with up to about 2o by weight copper, based on the total weight of the matrix, has been shown to produce successful composites. As used herein the terms "substantially pure elemental aluminum", "pure aluminum"
and "elemental aluminum" are interchangeable and are intended to mean aluminum containing less than about 0.05% by weight impurities. Such impurities typically comprise first row transition metals (titanium, vanadium, chromium, manganese, iron, cobalt, nickel, and zinc) as well as second and third row metals and elements in the lanthanide series. In one preferred embodiment, the terms are intended to mean aluminum having less than about 0.03% by weight iron, with less than about 0.01% by weight iron being most preferred. Minimizing the iron content is desirable because iron is a common contaminant of aluminum, and further, because iron and aluminum combine to form brittle intermetallic compounds (e.g., A13Fe, Al2Fe, etc.). It is also particularly desirable to avoid contamination by silicon (such as from Si02, which can be reduced to free silicon in the presence of molten aluminum) because silicon, like iron, forms a brittle phase, and because silicon can react with the aluminum (and any iron which may be present) to form brittle Al-Fe-Si intermetallic compounds. The presence of brittle phases in the composite is undesirable, as such phases tend to promote fracture in the composite when subjected to stress. In particular, such brittle phases may cause the matrix to fracture even before the reinforcing ceramic fibers fracture, resulting in composite failure. Generally, it is desirable to avoid substantial amounts of any transition metal, (i.e., Groups IB
through VIIIB of the periodic table), that form brittle intermetallic compounds. Iron and silicon have been particularly specified herein as a result of their commonality as impurities in metallurgic processes.
Each of the first row transition metals described above is relatively soluble in molten aluminum and, as noted, can react with the aluminum to form brittle intermetallic compounds. In contrast, metal impurities such as tin, lead, bismuth, antimony and the like do not form compounds with aluminum, and are virtually insoluble in molten aluminum. As a result, those impurities tend to segregate to the fiber/matrix interface, thereby weakening the composite strength at the interface. Although such segregation may aid longitudinal strength of the ultimate composite by contributing to a global load sharing domain (discussed below), the presence of the impurities ultimately results in a substantial reduction in the transverse strength of the composite due to decohesion at the fiber/matrix interface.
Elements from Groups IA and IIA of the periodic table tend to react with the fiber and drastically decrease the strength of the fiber in the composite. Magnesium and lithium are particularly undesirable elements in this regard, due, in part, to the length of time the fibers and the metal must be maintained at high temperatures during processing or in use.
It should be understood that references to "substantially pure elemental aluminum", "pure aluminum", and "elemental aluminum" as used herein, are intended to apply to the matrix material rather than to the reinforcing fibers, since the fibers will likely include domains of iron (and possible other) compounds within their grain structure. Such domains typically are remnants of the fiber manufacturing process and have, at most, negligible effect on the overall characteristics of the resulting composite material, since they tend to be relatively small and fully encapsulated within the grains of the fiber. As such, they do not interact with the composite matrix, and thereby avoid the drawbacks associated with matrix contamination.
The metal matrix used in the composite of the present invention is selected to have a low yield-strength relative to the reinforcing fibers. In this context, yield-strength is defined as the stress at 0.2 s offset strain in a standardized tensile test (described in ASTM tensile standard E345-93) of the unreinforced metal or alloy. Generally, two classes of aluminum matrix composites can be broadly distinguished based on the matrix yield-strength. Composites in which the matrix has a relatively low yield-strength have a high longitudinal tensile strength governed primarily by the strength of the reinforcing fibers. As used herein, low yield-strength aluminum matrices in aluminum matrix composites are defined as matrices with a yield-strength of less than about 150 MPa. The matrix yield-strength is preferably measured on a sample of matrix material having the same composition and which has been fabricated in the same manner as the material used to form the composite matrix. Thus, for example, the yield-strength of a substantially pure elemental aluminum matrix material used in a composite material would be determined by testing the yield-strength of substantially pure elemental aluminum without a fiber reinforcement. In composites with low yield-strength matrices, matrix shearing in the vicinity of the matrix-fiber interface reduces the stress concentrations near broken fibers and allows for global stress redistribution. In this regime, the composite reaches "rule-of-mixtures" strength. Pure aluminum has a yield-strength of less than about 13.8 MPa (2 ksi) and Al-2 wt% Cu has a yield-strength less than about 96.5 MPa (14 ksi).
The low yield-strength matrix composites described above may be contrasted with high yield-strength matrices which typically exhibit lower composite longitudinal strength than the predicted "rule-of-mixtures" strength. In composites having high strength matrices, the characteristic failure mode is a catastrophic crack propagation. In composite materials, high yield-strength matrices typically resist shearing from broken fibers, thereby producing a high stress concentration near any fiber breaks. The high stress concentration allows cracks to propagate, leading to failure of the nearest fiber and catastrophic failure of the composite well before the "rule-of-mixtures" strength is reached. Failure modes in this regime are said to result from "local load sharing". For a metal matrix composite with about 50 volume percent fiber, a low yield-strength matrix produces a strong (i.e., >1.17 CPa (170 ksi)) composite when combined with alumina fibers having strengths of greater than 2.8 GPa (400 ksi). Thus, it is believed that for the same fiber loading, the composite strength will increase with fiber strength.
The strength of the composite may be further improved by infiltrating the polycrystalline a-A12O3 fiber tows with small particles or whiskers or short (chopped) fibers, of alumina. Such particles, whiskers or fibers, typically on the order of less than 20 micrometers, and often submicron, become physically trapped at the fiber surface and provide for spacing between individual fibers within the composite. The spacing eliminates interfiber contact and thereby yields a stronger composite. A discussion of the use of small domains of material to minimize interfiber contact can be found in U.S. Patent No. 4,961,990 (Yamada et al., assigned to Kabushiki Kaisha Toyota Chuo Kenkyusho and Ube Industries, Ltd., both of Japan).
As noted above, one of the significant obstacles in forming composite materials relates to the difficulty in sufficiently wetting reinforcing fibers with the surrounding matrix material. Likewise, infiltration of the fiber tows with the matrix material is also a significant problem in the production of composite metal matrix wires, since the continuous wire forming process typically takes place at or near atmospheric pressure. This problem also exists for composite materials formed in batch processes at or near atmospheric pressure.
The problem of incomplete matrix infiltration of the fiber tow can be overcome through the use of a source of ultrasonic energy as a matrix infiltration aid. For example, U.S. Patent No. 4,779,563 (Ishikawa et al., assigned to Agency of Industrial Science and Technology, Tokyo, Japan), describes the use of ultrasonic wave vibration apparatus for use in the production of preform wires, sheets, or tapes from silicon carbide fiber reinforced metal composites. The ultrasonic wave energy is provided to the fibers via a vibrator having a transducer and an ultrasonic "horn" immersed in the molten matrix material in the vicinity of the fibers. The horn is preferably fabricated of a material having little, if any, solubility in the molten matrix to thereby prevent the introduction of contaminants into the matrix. In the present case, horns of commercially pure niobium, or alloys of 95%
niobium and 5% molybdenum have been found to yield satisfactory results. The transducer used therewith typically comprises titanium.
One embodiment of a metal matrix fabrication system employing an ultrasonic horn is presented in FIG. 1. In that Figure, a tow of polycrystalline a-A1203 fibers 10 is unwound from a supply roll 12 and drawn, by rollers 14, through a vessel 16 containing the matrix metal 18 in molten form.
While immersed in the molten matrix metal 18, the tow 10 is subjected to ultrasonic energy provided by an ultrasonic - lla -energy source 20 which is immersed in the molten metal 18 in the vicinity of a section of the tow 10. The ultrasonic energy source 20 comprises an oscillator 22 and a vibrator 24 having a transducer 26 and a horn 27. The horn 27 vibrates the molten matrix metal 18 at a frequency produced by the oscillator 22 and transmitted to the vibrator 24 and transducer 26. In so doing, the matrix material is caused to thoroughly infiltrate the fiber tow. The infiltrated tow is drawn from the molten matrix and stored on a take-up roll 28.
The process of making a metal matrix composite often involves forming fibers into a"preform". Typically, fibers are wound into arrays and stacked. Fine diameter alumina fibers are wound so that fibers in a tow stay parallel to one another. The stacking is done in any fashion to obtain a desired fiber density in the final composite. Fibers can be made into simple preforms by winding around a rectangular drum, a wheel or a hoop. Alternatively, they can be wrapped onto a cylinder. The multiple layers of fibers wound or wrapped in this fashion are cut off and stacked or bundled together to form a desired shape. Handling the fiber arrays is aided by using water either straight or mixed with an organic binder to hold the fibers together in a mat.
One method of making a composite part is to position the fibers in a mold, fill the mold with molten metal, and then subject the filled mold to elevated pressure. Such a process is disclosed in U.S. Patent No. 3,547,180 entitled "Production of Reinforced Composites". The mold should not be a source of contamination to the matrix metal. In one - llb -embodiment, the molds can be formed of graphite, alumina, or alumina-coated steel. The fibers can be stacked in the mold in a desired configuration; e.g., parallel to the walls of the mold, or in layers arrayed perpendicular to one another, as is known in the art. The shape of the composite material can be any shape into which a mold can be made. As such, fiber structures can be fabricated using numerous preforms, including, but not limited to, rectangular drums, wheel or hoop shapes, cylindrical shapes, or various molded shapes resulting from stacking or otherwise loading fibers in a mold cavity. Each of the preforms described above relates to a batch process for making a composite device. Continuous processes for the formation of substantially continuous wires, tapes, cables and the like may be employed as well.
Typically, only minor machining of the surface of a finished part is necessary. It is possible also to machine any shape from a block of the composite material by using diamond tooling. Thus, it becomes possible to produce many complex shapes.
A wire shape can be formed by infiltrating bundles or tows of alumina fiber with molten aluminum. This can be done by feeding tows of fibers into a bath of molten aluminum.
To obtain wetting of the fibers, an ultrasonic horn is used to agitate the bath while the fibers pass through it.
Fiber reinforced metal matrix composites are important for applications wherein lightweight, strong, high-temperature-resistant (at least about 300 C) materials are needed. For example, the composites can be used for gas - llc -turbine compressor blades in jet engines, structural tubes, actuator rods, I-beams, automotive connecting rods, missile fins, fly wheel rotors, sports equipment (e.g., golf clubs) and power transmission cable support cores. Metal matrix composites are superior to unreinforced metals in stiffness, strength, fatigue resistance, and wear characteristics.
In one preferred embodiment of the present invention, the composite material comprises between about 30-70% by volume polycrystalline a-A1203 fibers, based on the total volume of the composite material within a substantially elemental aluminum matrix. It is preferred that the matrix contains less than about 0.03o by weight iron, and most preferably less than about 0.011i by weight iron, based on the total weight of the matrix. A fiber content of between about 40-60% by volume polycrystalline a-A1203 fibers is preferred.
Such composites, formed with a matrix having a yield-strength of less than about 20 MPa and fibers having a longitudinal tensile strength of at least about 2.8 GPa have been found to have excellent strength characteristics.
The matrix may also be formed from an alloy of elemental aluminum with up to about 2% by weight copper, based on the total weight of the matrix. As in the embodiment in which a substantially pure elemental aluminum matrix is used, composites having an aluminum/copper alloy matrix preferably comprise between about 30-7001 by volume polycrystalline a-A1203 fibers by weight, and more preferably therefore about 40-60o by volume polycrystalline a-A1203 fibers, based on the total volume of the composite. In addition, the matrix - lid -preferably contains less than about 0.03% by weight iron, and most preferably less than about 0.01% by weight iron, based on the total weight of the matrix. The aluminum/copper matrix preferably has a yield strength of less than about 90 MPa, and, as above, the polycrystalline a-A1203 fibers have a longitudinal tensile strength of at least about 2.8 GPa. The properties of two composites, a first with an elemental aluminum matrix, and a second with a matrix of the specified aluminum/copper alloy, each having between about 55-65 vol. %
polycrystalline a-A1203 fibers are presented in Table I below:
- lie -Table I: SUMMARY OF COMPOSITE PROPERTIES
Pure Al Al-2wt%Cu 55-65 vol% A12O3 55-65 vol% A1203 Longitudinal 220 - 260 GPa 220 - 260 GPa Young's Modulus, El,(32 - 38 Msi) (32 - 38 Msi) Transverse = 120 - 140 GPa 150 - 160 GPa Young's Modulus, E22 (17.5 - 20 Msi) (22 - 23 Msi) Shear Modulus, G12 48 - 50 GPa 45 - 47 GPa (6.5 - 7.3 Msi) (6.5 - 6.8 Msi) Shear Modulus, GZi 54 - 57 GPa 55 - 56 GPa (7.8 - 8.3 Msi) (8 - 8.2 Msi) Long. tensile strength 1500 - 1900 MPa 1500 - 1800 MPa Sil, T (220 - 275 ksi) (220 - 260 ksi) Long. compressive 1700 - 1800 MPa 3500 - 3700 MPa strength, S ll ,c (245 - 260 ksi) (500 - 540 ksi) Shear Strength 70 MPa 140 MPa S21- S12 (10 ksi) (20 ksi) at 2% strain Trans. strength S22 110 - 130 MPa 270 - 320 MPa at 1% strain (16 - 19 ksi) (39 - 46 ksi) The properties listed in this table represent a range of mechanical performance measured on composites containing 55-65 vol% NEXTELTm 610 ceramic fibers.
The range is not representative of the statistical scatter.
(2) Index Notation 1= Fiber direction; 2 = Transverse direction; ij:i direction normal to the plane in which the stress is acting, j = stress direction, S = Ultimate strength unless specified.
Preferred composite materials according to the present invention have a fiber density of between about 3.90-3.95 grams per cubic centimeter. Among the preferred fibers are those described in U.S. Patent No. 4,954,462 (Wood et al., assigned to Minnesota Mining and Manufacturing Company, St.
Paul, MN). Such fibers are available commercially under the designation NEXTELTM 610 Ceramic Fibers from the Minnesota Mining and Manufacturing Company, St. Paul, MN. The encapsulating matrix is selected to be such that it does not react chemically with the fiber material (i.e., is relatively chemically inert with respect to the fiber material), thereby eliminating the need to provide a protective coating on the fiber exterior.
As used herein, the term "polycrystalline" means a material having predominantly a plurality of crystalline grains in which the grain size is less than the diameter of the fiber in which the grains are present. The term "continuous" is intended to mean a fiber having a length which is relatively infinite when compared to the fiber diameter.
In practical terms, such fibers have a length on the order of about 15 cm to at least several meters, and may even have lengths on the order of kilometers or more.
In the preferred embodiments, the use of a matrix comprising either substantially pure elemental aluminum, or an alloy of elemental aluminum with up to about 2o by weight copper, based on the total weight of the matrix, has been shown to produce successful composites. As used herein the terms "substantially pure elemental aluminum", "pure aluminum"
and "elemental aluminum" are interchangeable and are intended to mean aluminum containing less than about 0.05% by weight impurities. Such impurities typically comprise first row transition metals (titanium, vanadium, chromium, manganese, iron, cobalt, nickel, and zinc) as well as second and third row metals and elements in the lanthanide series. In one preferred embodiment, the terms are intended to mean aluminum having less than about 0.03% by weight iron, with less than about 0.01% by weight iron being most preferred. Minimizing the iron content is desirable because iron is a common contaminant of aluminum, and further, because iron and aluminum combine to form brittle intermetallic compounds (e.g., A13Fe, Al2Fe, etc.). It is also particularly desirable to avoid contamination by silicon (such as from Si02, which can be reduced to free silicon in the presence of molten aluminum) because silicon, like iron, forms a brittle phase, and because silicon can react with the aluminum (and any iron which may be present) to form brittle Al-Fe-Si intermetallic compounds. The presence of brittle phases in the composite is undesirable, as such phases tend to promote fracture in the composite when subjected to stress. In particular, such brittle phases may cause the matrix to fracture even before the reinforcing ceramic fibers fracture, resulting in composite failure. Generally, it is desirable to avoid substantial amounts of any transition metal, (i.e., Groups IB
through VIIIB of the periodic table), that form brittle intermetallic compounds. Iron and silicon have been particularly specified herein as a result of their commonality as impurities in metallurgic processes.
Each of the first row transition metals described above is relatively soluble in molten aluminum and, as noted, can react with the aluminum to form brittle intermetallic compounds. In contrast, metal impurities such as tin, lead, bismuth, antimony and the like do not form compounds with aluminum, and are virtually insoluble in molten aluminum. As a result, those impurities tend to segregate to the fiber/matrix interface, thereby weakening the composite strength at the interface. Although such segregation may aid longitudinal strength of the ultimate composite by contributing to a global load sharing domain (discussed below), the presence of the impurities ultimately results in a substantial reduction in the transverse strength of the composite due to decohesion at the fiber/matrix interface.
Elements from Groups IA and IIA of the periodic table tend to react with the fiber and drastically decrease the strength of the fiber in the composite. Magnesium and lithium are particularly undesirable elements in this regard, due, in part, to the length of time the fibers and the metal must be maintained at high temperatures during processing or in use.
It should be understood that references to "substantially pure elemental aluminum", "pure aluminum", and "elemental aluminum" as used herein, are intended to apply to the matrix material rather than to the reinforcing fibers, since the fibers will likely include domains of iron (and possible other) compounds within their grain structure. Such domains typically are remnants of the fiber manufacturing process and have, at most, negligible effect on the overall characteristics of the resulting composite material, since they tend to be relatively small and fully encapsulated within the grains of the fiber. As such, they do not interact with the composite matrix, and thereby avoid the drawbacks associated with matrix contamination.
The metal matrix used in the composite of the present invention is selected to have a low yield-strength relative to the reinforcing fibers. In this context, yield-strength is defined as the stress at 0.2 s offset strain in a standardized tensile test (described in ASTM tensile standard E345-93) of the unreinforced metal or alloy. Generally, two classes of aluminum matrix composites can be broadly distinguished based on the matrix yield-strength. Composites in which the matrix has a relatively low yield-strength have a high longitudinal tensile strength governed primarily by the strength of the reinforcing fibers. As used herein, low yield-strength aluminum matrices in aluminum matrix composites are defined as matrices with a yield-strength of less than about 150 MPa. The matrix yield-strength is preferably measured on a sample of matrix material having the same composition and which has been fabricated in the same manner as the material used to form the composite matrix. Thus, for example, the yield-strength of a substantially pure elemental aluminum matrix material used in a composite material would be determined by testing the yield-strength of substantially pure elemental aluminum without a fiber reinforcement. In composites with low yield-strength matrices, matrix shearing in the vicinity of the matrix-fiber interface reduces the stress concentrations near broken fibers and allows for global stress redistribution. In this regime, the composite reaches "rule-of-mixtures" strength. Pure aluminum has a yield-strength of less than about 13.8 MPa (2 ksi) and Al-2 wt% Cu has a yield-strength less than about 96.5 MPa (14 ksi).
The low yield-strength matrix composites described above may be contrasted with high yield-strength matrices which typically exhibit lower composite longitudinal strength than the predicted "rule-of-mixtures" strength. In composites having high strength matrices, the characteristic failure mode is a catastrophic crack propagation. In composite materials, high yield-strength matrices typically resist shearing from broken fibers, thereby producing a high stress concentration near any fiber breaks. The high stress concentration allows cracks to propagate, leading to failure of the nearest fiber and catastrophic failure of the composite well before the "rule-of-mixtures" strength is reached. Failure modes in this regime are said to result from "local load sharing". For a metal matrix composite with about 50 volume percent fiber, a low yield-strength matrix produces a strong (i.e., >1.17 CPa (170 ksi)) composite when combined with alumina fibers having strengths of greater than 2.8 GPa (400 ksi). Thus, it is believed that for the same fiber loading, the composite strength will increase with fiber strength.
The strength of the composite may be further improved by infiltrating the polycrystalline a-A12O3 fiber tows with small particles or whiskers or short (chopped) fibers, of alumina. Such particles, whiskers or fibers, typically on the order of less than 20 micrometers, and often submicron, become physically trapped at the fiber surface and provide for spacing between individual fibers within the composite. The spacing eliminates interfiber contact and thereby yields a stronger composite. A discussion of the use of small domains of material to minimize interfiber contact can be found in U.S. Patent No. 4,961,990 (Yamada et al., assigned to Kabushiki Kaisha Toyota Chuo Kenkyusho and Ube Industries, Ltd., both of Japan).
As noted above, one of the significant obstacles in forming composite materials relates to the difficulty in sufficiently wetting reinforcing fibers with the surrounding matrix material. Likewise, infiltration of the fiber tows with the matrix material is also a significant problem in the production of composite metal matrix wires, since the continuous wire forming process typically takes place at or near atmospheric pressure. This problem also exists for composite materials formed in batch processes at or near atmospheric pressure.
The problem of incomplete matrix infiltration of the fiber tow can be overcome through the use of a source of ultrasonic energy as a matrix infiltration aid. For example, U.S. Patent No. 4,779,563 (Ishikawa et al., assigned to Agency of Industrial Science and Technology, Tokyo, Japan), describes the use of ultrasonic wave vibration apparatus for use in the production of preform wires, sheets, or tapes from silicon carbide fiber reinforced metal composites. The ultrasonic wave energy is provided to the fibers via a vibrator having a transducer and an ultrasonic "horn" immersed in the molten matrix material in the vicinity of the fibers. The horn is preferably fabricated of a material having little, if any, solubility in the molten matrix to thereby prevent the introduction of contaminants into the matrix. In the present case, horns of commercially pure niobium, or alloys of 95%
niobium and 5% molybdenum have been found to yield satisfactory results. The transducer used therewith typically comprises titanium.
One embodiment of a metal matrix fabrication system employing an ultrasonic horn is presented in FIG. 1. In that Figure, a tow of polycrystalline a-A1203 fibers 10 is unwound from a supply roll 12 and drawn, by rollers 14, through a vessel 16 containing the matrix metal 18 in molten form.
While immersed in the molten matrix metal 18, the tow 10 is subjected to ultrasonic energy provided by an ultrasonic - lla -energy source 20 which is immersed in the molten metal 18 in the vicinity of a section of the tow 10. The ultrasonic energy source 20 comprises an oscillator 22 and a vibrator 24 having a transducer 26 and a horn 27. The horn 27 vibrates the molten matrix metal 18 at a frequency produced by the oscillator 22 and transmitted to the vibrator 24 and transducer 26. In so doing, the matrix material is caused to thoroughly infiltrate the fiber tow. The infiltrated tow is drawn from the molten matrix and stored on a take-up roll 28.
The process of making a metal matrix composite often involves forming fibers into a"preform". Typically, fibers are wound into arrays and stacked. Fine diameter alumina fibers are wound so that fibers in a tow stay parallel to one another. The stacking is done in any fashion to obtain a desired fiber density in the final composite. Fibers can be made into simple preforms by winding around a rectangular drum, a wheel or a hoop. Alternatively, they can be wrapped onto a cylinder. The multiple layers of fibers wound or wrapped in this fashion are cut off and stacked or bundled together to form a desired shape. Handling the fiber arrays is aided by using water either straight or mixed with an organic binder to hold the fibers together in a mat.
One method of making a composite part is to position the fibers in a mold, fill the mold with molten metal, and then subject the filled mold to elevated pressure. Such a process is disclosed in U.S. Patent No. 3,547,180 entitled "Production of Reinforced Composites". The mold should not be a source of contamination to the matrix metal. In one - llb -embodiment, the molds can be formed of graphite, alumina, or alumina-coated steel. The fibers can be stacked in the mold in a desired configuration; e.g., parallel to the walls of the mold, or in layers arrayed perpendicular to one another, as is known in the art. The shape of the composite material can be any shape into which a mold can be made. As such, fiber structures can be fabricated using numerous preforms, including, but not limited to, rectangular drums, wheel or hoop shapes, cylindrical shapes, or various molded shapes resulting from stacking or otherwise loading fibers in a mold cavity. Each of the preforms described above relates to a batch process for making a composite device. Continuous processes for the formation of substantially continuous wires, tapes, cables and the like may be employed as well.
Typically, only minor machining of the surface of a finished part is necessary. It is possible also to machine any shape from a block of the composite material by using diamond tooling. Thus, it becomes possible to produce many complex shapes.
A wire shape can be formed by infiltrating bundles or tows of alumina fiber with molten aluminum. This can be done by feeding tows of fibers into a bath of molten aluminum.
To obtain wetting of the fibers, an ultrasonic horn is used to agitate the bath while the fibers pass through it.
Fiber reinforced metal matrix composites are important for applications wherein lightweight, strong, high-temperature-resistant (at least about 300 C) materials are needed. For example, the composites can be used for gas - llc -turbine compressor blades in jet engines, structural tubes, actuator rods, I-beams, automotive connecting rods, missile fins, fly wheel rotors, sports equipment (e.g., golf clubs) and power transmission cable support cores. Metal matrix composites are superior to unreinforced metals in stiffness, strength, fatigue resistance, and wear characteristics.
In one preferred embodiment of the present invention, the composite material comprises between about 30-70% by volume polycrystalline a-A1203 fibers, based on the total volume of the composite material within a substantially elemental aluminum matrix. It is preferred that the matrix contains less than about 0.03o by weight iron, and most preferably less than about 0.011i by weight iron, based on the total weight of the matrix. A fiber content of between about 40-60% by volume polycrystalline a-A1203 fibers is preferred.
Such composites, formed with a matrix having a yield-strength of less than about 20 MPa and fibers having a longitudinal tensile strength of at least about 2.8 GPa have been found to have excellent strength characteristics.
The matrix may also be formed from an alloy of elemental aluminum with up to about 2% by weight copper, based on the total weight of the matrix. As in the embodiment in which a substantially pure elemental aluminum matrix is used, composites having an aluminum/copper alloy matrix preferably comprise between about 30-7001 by volume polycrystalline a-A1203 fibers by weight, and more preferably therefore about 40-60o by volume polycrystalline a-A1203 fibers, based on the total volume of the composite. In addition, the matrix - lid -preferably contains less than about 0.03% by weight iron, and most preferably less than about 0.01% by weight iron, based on the total weight of the matrix. The aluminum/copper matrix preferably has a yield strength of less than about 90 MPa, and, as above, the polycrystalline a-A1203 fibers have a longitudinal tensile strength of at least about 2.8 GPa. The properties of two composites, a first with an elemental aluminum matrix, and a second with a matrix of the specified aluminum/copper alloy, each having between about 55-65 vol. %
polycrystalline a-A1203 fibers are presented in Table I below:
- lie -Table I: SUMMARY OF COMPOSITE PROPERTIES
Pure Al Al-2wt%Cu 55-65 vol% A12O3 55-65 vol% A1203 Longitudinal 220 - 260 GPa 220 - 260 GPa Young's Modulus, El,(32 - 38 Msi) (32 - 38 Msi) Transverse = 120 - 140 GPa 150 - 160 GPa Young's Modulus, E22 (17.5 - 20 Msi) (22 - 23 Msi) Shear Modulus, G12 48 - 50 GPa 45 - 47 GPa (6.5 - 7.3 Msi) (6.5 - 6.8 Msi) Shear Modulus, GZi 54 - 57 GPa 55 - 56 GPa (7.8 - 8.3 Msi) (8 - 8.2 Msi) Long. tensile strength 1500 - 1900 MPa 1500 - 1800 MPa Sil, T (220 - 275 ksi) (220 - 260 ksi) Long. compressive 1700 - 1800 MPa 3500 - 3700 MPa strength, S ll ,c (245 - 260 ksi) (500 - 540 ksi) Shear Strength 70 MPa 140 MPa S21- S12 (10 ksi) (20 ksi) at 2% strain Trans. strength S22 110 - 130 MPa 270 - 320 MPa at 1% strain (16 - 19 ksi) (39 - 46 ksi) The properties listed in this table represent a range of mechanical performance measured on composites containing 55-65 vol% NEXTELTm 610 ceramic fibers.
The range is not representative of the statistical scatter.
(2) Index Notation 1= Fiber direction; 2 = Transverse direction; ij:i direction normal to the plane in which the stress is acting, j = stress direction, S = Ultimate strength unless specified.
Although suitable for a wide variety of uses, in one embodiment, the composites of the present invention have applicability in the formation of composite matrix wire. Such wires are formed from substantially continuous polycrystalline cx-A1203 fibers contained within the substantially pure elemental aluminum matrix or the matrix formed from the alloy of elemental aluminum and up to about 21 copper by weight described above. Such wires are made by a process in which a spool of substantially continuous polycrystalline a-A1203 fibers, arranged in a fiber tow, is pulled through a bath of molten matrix material. The resulting segment is then solidified, thereby providing fibers encapsulated within the matrix. It is preferred that an ultrasonic horn, as described above, is lowered into the molten matrix bath and used to aid the infiltration of the matrix into the fiber tows.
Composite metal matrix wires, such as those described above, are useful in numerous applications. Such wires are believed to be particularly desirable for use in overhead high voltage power transmission cables due to their combination of low weight, high strength, good electrical conductivity, low coefficient of thermal expansion, high use temperatures, and resistance to corrosion. The competitiveness of composite metal matrix wires, such as those described above for use in overhead high voltage power transmission, is a result of the significant effect cable performance has on the entire electricity transport system.
Cable having lower weight per unit strength, coupled with increased conductivity and lower thermal expansion, provides the ability to install greater cable spans and/or lower tower heights. As a result, the costs of constructing electrical towers for a given electricity transport system can be significantly reduced. Additionally, improvements in the electrical properties of a conductor can reduce electrical losses in the transmission system, thereby reducing the need for additional power generation to compensate for such losses.
As noted above, the composite metal matrix wires of the present invention are believed to be particularly well-suited for use in overhead high voltage power transmission cables. In one embodiment, an overhead high voltage power transmission cable can include an electrically conductive core formed by at least one composite metal matrix wire according to the present invention. The core is surrounded by at least one conductive jacket formed by a plurality of aluminum or aluminum alloy wires. Numerous cable core and jacket configurations are known in the cable art. For example, as shown in FIG. 2a, the cross-section of one overhead high voltage power transmission cable 30 may be a core 32 of nineteen individual aluminum or aluminum alloy wires 38.
Likewise, as shown in FIG. 2b, as one of many alternatives, the cross-section of a difference overhead high voltage power transmission cable 30' may be a core 32' of thirty-seven individual composite metal matrix wires 34' surrounded by a jacket 36' of twenty-one individual aluminum or aluminum alloy wires 38'.
The weight percentage of composite metal matrix wires within the cable will depend upon the design of the transmission line. In that cable, the aluminum or aluminum alloy wires used in the conductive jackets are any of the various materials known in the art of overhead high voltage power transmission, including, but not limited to, 1350 Al or 6201 Al.
In another embodiment, an overhead high voltage power transmission cable can be constructed entirely of a plurality of continuous fiber aluminum matrix composite wires (CF-AMCs). As is discussed below, such a construction is well-suited for long cable spans in which the strength-to-weight ratio and the coefficient of thermal expansion of the cable overrides the need to minimize resistive losses.
Although dependent upon a number of factors, the amount of sag in an overhead high voltage power transmission cable varies as the square of the span length and inversely with the tensile strength of the cable. As may be seen in FIG. 3, CF-AMC materials offer substantial improvements in the strength-to-weight ratio over materials commonly used for cable in the power transmission industry. It should be noted that the strength, electrical conductivity and density of CF-AMC materials and cables is dependent upon the fiber volume in the composite. For FIGS. 3, 4a, 4b, and 5 a 50% fiber volume was assumed, with a corresponding density of about 3.2 gm/cm3 (approximately 0.115 lb/in3), tensile strength of 1.38 GPa (200 ksi), and conductivity of 30o IACS.
As a result of the increased strength of cables containing CF-AMC wires, cable sag can be substantially reduced. Calculations comparing the sags of CF-AMC cables as a function of span length with a commonly used steel standing (ACSR) (31 wt% steel having a core of 7 steel wires surrounded by a jacket of 26 aluminum wires), and an equivalent all-aluminum alloy conductor (AAAC) are shown in FIGS. 4a and 4b.
All cables had equivalent electrical conductivity and diameter. FIG. 4a demonstrates that CF-AMC cables provide for a 4001 reduction in tower height as compared to ACSR for spans of about 550 m (about 1800 ft.). Likewise, CF-AMC cables allow for an increase in span length about 25o assuming allowable sags of 15 m (about 50 ft.). Further advantages from the use of CF-AMC cables in long spans are presented in FIG.- 4b. In FIG. 4b, the ACSR cable was 72 wto steel having a core of 19 steel wires surrounded by a jacket of 16 aluminum wires.
The sag of a high voltage power transmission (HVPT) cable at its maximum operating temperature is also dependent upon the coefficient of thermal expansion (CTE) of the cable at its maximum operating temperature. The ultimate CTE of the cable is determined by the CTE and the elastic modulus of both the reinforcing core and the surrounding strands. Within limits, materials with a low CTE and a high elastic modulus are desired. The CTE for the CF-AMC cable is shown in FIG. 5 as a function of temperature. Reference values for aluminum and steel are provided as well.
It is noted that the present invention is not intended to be limited to wires and HVPT cables employing composite metal matrix technology; rather, it is intended to include the specific inventive composite materials described herein as well as numerous additional applications. Thus, the composite metal matrix materials described herein may be used in any of a wide variety of applications, including, but not limited to, flywheel rotors, high performance aerospace components, voltage transmission, or many other applications in which high strength, low density materials are desired.
It should be further noted that although the preferred embodiment makes use of the polycrystalline cx-A1203 fibers described in U.S. Patent No. 4,954,462 currently being marketed under the tradename NEXTELTM 610 by Minnesota Mining and Manufacturing Company of St. Paul, MN, the invention is not intended to be limited to those specific fibers. Rather, any suitable polycrystalline a-A1203 fiber is intended to be included herein as well. It is preferred, however, that any such fiber have a tensile strength at least on the order of that of the NEXTELTM 610 fibers (approximately 2.8 GPa).
In the practice of the invention, the matrix must be chemically inert relative to the fiber over a temperature range between about 20 C-760 C. The temperature range represents the range of predicted processing and service temperatures for the composite. This requirement minimizes chemical reactions between the matrix and fiber which may be deleterious to the overall composite properties. In the case of a matrix material comprising an alloy of elemental aluminum and up to about 2o by weight copper, the as-cast alloy has a yield-strength of approximately 41.4-55.2 MPa (6-8 ksi). In order to increase the strength of this metal alloy, various treatment methods may be used. In one preferred embodiment, once combined with the metallic fibers, the alloy is heated to about 520 C for about 16 hours followed by quenching in water maintained at a temperature of between about 60-100 C. The composite is then placed in an oven and maintained at about 190 C and maintained at that temperature until the desired strength of the matrix is achieved (typically 0-10 days). The matrix has been found to reach a maximum yield-strength of about 68.9-89.6 MPa (10-13 ksi) when it was maintained at a temperature of approximately 190 C for five days. In contrast, pure aluminum that is not specifically heat treated has a yield-strength of approximately 6.9-13.8 MPa (1-2 ksi) in the as-cast state.
ExamUles Objects and advantages of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. All parts and percentages are by weight unless otherwise indicated.
Test Methods Fiber strength was measured using a tensile tester (commercially available as Instron 4201 tester from Instron of Canton, MA) and the test is described in ASTM D 3379-75, (Standard Test Methods for Tensile Strength and Young's Modulus for High Modulus Single-Filament Materials). The specimen gauge length was 25.4 mm (1 inch), the strain rate was 0.02 mm/mm/min.
To establish the tensile strength of a fiber tow, ten single fiber filaments were randomly chosen from a tow of fibers. Each filament was tested to determine its breaking load. At least 10 filaments were tested with the average strength of the filaments in the tow being determined. Each individual, randomly selected fiber had strength ranging from 2.06-4.82 GPa (300-700 ksi). The average individual filament tensile strength ranged from 2.76 to 3.58 GPa (400-520 ksi).
Fiber diameter was measured optically using an attachment to an optical microscope (Dolan-Jenner Measure-Rite Video Micrometer System, Model M25-0002, commercially available from Donal-Jenner Industries, Inc. of Lawrence MA) at x 1000 magnification. The apparatus used reflected light observation with a calibrated stage micrometer.
The breaking stress of each individual filament was calculated as the load per unit area.
The fiber elongation was determined from the load displacement curve and ranged from about 0.55% to about 1.3%.
The average strength of the polycrystalline cx-A1203 fibers used in the working examples was greater than 2.76 GPa (400 ksi)(with 15% standard deviation typical). The higher the average strength of the reinforcing fiber, the higher the composite strength. Composites made according to this embodiment of the present invention has a strength of at least 1.38 GPa (200 ksi)(with 5% standard deviation), and often at least 1.72 GPa (250 ksi)(with 5% standard deviation) when provided with a fiber volume fraction of approximately 60%
(based on the total volume of the composite).
- 18a -Tensile Testing The tensile strength of the composite was measured using a tensile tester (commercially available as an Instron 8562 Tester from Instron Corp. of Canton, MA). This test was carried out substantially as described for the tensile testing of metal foils, i.e., as described in ASTM E345-93, (Standard Test Methods for Tension Testing of Metallic Foil).
In order to perform tensile testing, the composite was made into a plate 15.24 cm x 7.62 cm x 0.13 cm (6"x3"x0.05"). Using a diamond saw, this plate was cut into 7 coupons (15.24 cm x 0.95 cm x 0.13 cm(6"xO.375"xO.05)) which were used for testing.
Average longitudinal strength (i.e., fiber parallel to test direction) was measured at 1.38 GPa (200 ksi) for composites having a matrix of either pure aluminum or pure aluminum with 2% by weight Cu. For composites having a fiber volume content of about 60%, average transverse strength (i.e., fiber perpendicular to the test direction) was 138 MPa (20 ksi) for composites containing pure aluminum and 262 MPa (38 ksi) for composites made with the aluminum/2% copper alloy.
Specific examples of various composites metal matrix fabrications are described below.
Example 1 - Preparation of a fiber-reinforced metal composite A composite was prepared using a tow of NEXTELTM 610 alumina ceramic fibers. The tow contained 420 fibers. The fibers were substantially round in cross-section and had - 18b -average. The average tensile strength of the fibers (measured as described above) ranged from 2.76-3.58 GPa (400-520 ksi).
Individual fibers had strengths ranging from 2.06-4.82 GPa (300-700 ksi).
The fibers were prepared for infiltration with metal by winding the fibers into a"preform". In particular, the fibers were wet with distilled water and wound around a rectangular drum having a circumference of approximately 86.4 cm (34 inches) in multiple layers to the desired preform thickness of approximately 0.25 cm (0.10in).
The wound fibers were cut from the drum and stacked in the mold cavity to produce the final desired preform thickness. A graphite mold in the shape of a rectangular plate was used. Approximately 1300 grams of aluminum metal (commercially available as Grade 99.99% from Belmont Metals of Brooklyn, NY) were placed into the casting vessel.
The mold containing the fibers was placed into a pressure infiltration casting apparatus. In this apparatus, the mold was placed into an airtight vessel or crucible and positioned at the bottom of an evacuable chamber. Pieces of aluminum metal were loaded into the chamber on a support plate above the mold. Small holes (approximately 2.54 mm in diameter) were present in the support plate to permit passage of molten aluminum to the mold below. The chamber was closed and the chamber pressure was reduced to 3 milliTorr to evacuate the air from the mold and the chamber. The aluminum metal was heated to 720 C and the mold (and fibrous preform in it) was heated to at least about 670 C. The aluminum melted at this temperature but remained on the plate above the mold. In order to fill the mold, the power to the heaters was turned ofly and the chamber was pressurized by filling with argon to a pressure of 8.96 MPa (1300 psi). The molten aluminum immediately flowed through the holes in the support plate and into the mold. The temperature was allowed to drop to before venting the chamber to the atmosphere. After the chamber had cooled to room temperature, the part was removed from the mold. The resulting samples had dimensions of 15.2 cm x 7.6 cm x 0.13 cm (6" x 3" x 0.05").
The sample rectangular composite pieces contained 60 volume % fiber.
The volume fraction was measured by using the Archimedes principle of fluid displacement and by examining a photomicrograph of a polished cross-section at 200x magnification.
The part was cut into coupons for tensile testing; it was not machined further. The tensile strength, measured from coupons as described above, was MPa (204 ksi)(Iongitudinal strength) and 140 MPa (20.4 ksi) (transverse strength).
Example 2-Preparation of Metal Matrix Composite Wires The fibers and metal used in this example were the same as those described in Example 1. The alumina fiber was not made into a preform.
Instead, the = 30 fibers (in the form of multiple tows) were fed into a molten bath of aluminum and then onto a take-up spool. The aluminum was melted in an alumina crucible having dimensions of about 24.1 cm x 31.3 cm x 31.8 cm (9.5 "x 12.5 "x12.5 ") (commercially available from Vesuvius McDaniel of Beaver Falls, PA). The temperature of the molten aluminum was approximately 720 C. An alloy of 95% niobium and 5% molybdenum was fashioned into a cylinder having dimensions of about 12.7 cm (5") long x 2.5 cm (1") diameter. The cylinder was used as an ultrasonic horn actuator by tuning to the desired vibration (i.e., tuned by altering the length), to a vibration frequency of about 20.0-20.4 kHz. The amplitude of the actuator was greater than 0.002 cm (0.0008").
The actuator was connected to a titanium waveguide which, in turn, was connected to the ultrasonic transducer. The fibers were infiltrated with matrix material to form wires of relatively uniform cross-section and diameter. Wires made by this process had diameters of about 0.13 cm (0.05").
The volume percent of fiber was estimated from a photomicrograph of a cross section (at 200x magnification) to be about 40 volume %.
The tensile strength of the wire was 1.03 - 1.31 GPa (150-190 ksi).
The elongation at room temperature was approximately 0.7-0.8%.
Elongation was measured during the tensile test by an extensometer.
Example 3-Composite Metal Matrix Materials Using an AUCu Alloy Matrix This example was carried out exactly as described in Example 1, except that instead of using pure aluminum, an alloy containing aluminum and 2% by weight copper was used. The alloy contained less than about 0.02% by weight iron, and less than about 0.05% by weight total impurities. The yield strength of this alloy ranged from 41.4 - 103.4 MPa (6-15 ksi). The alloy was heat treated according to the following schedule:
520 C for 16 hours followed by a water quench (water temperature ranging from 60 -100 C); and immediately placed into an oven at 190 C and held for 5 days.
The processing proceeded as described for Example 1 to produce rectangular pieces to make coupons suitable for tensile testing except that the metal was heated to 710 C and the mold (with the fibers in it) was heated to greater than 660 C.
_ The composite contained 60 volume % of fiber. The longitudinal strength ranged from 1.38 - 1.86 GPa (200 - 270 ksi) (with the average of 10 measurements of 1.52 GPa (220 ksi)) and the transverse strength ranged from MPa (35 - 48 ksi) (with an average of 10 measurements of 262 MPa (38 ksi)).
Equivalents Various modifications and alterations to this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention. It should be understood that this invention is not intended to be unduly limited by the illustrative embodiments and examples set forth herein and that such examples and embodiments are presented by way of example only with the scope of the invention intended to be limited only by the claims set forth herein as follows.
Composite metal matrix wires, such as those described above, are useful in numerous applications. Such wires are believed to be particularly desirable for use in overhead high voltage power transmission cables due to their combination of low weight, high strength, good electrical conductivity, low coefficient of thermal expansion, high use temperatures, and resistance to corrosion. The competitiveness of composite metal matrix wires, such as those described above for use in overhead high voltage power transmission, is a result of the significant effect cable performance has on the entire electricity transport system.
Cable having lower weight per unit strength, coupled with increased conductivity and lower thermal expansion, provides the ability to install greater cable spans and/or lower tower heights. As a result, the costs of constructing electrical towers for a given electricity transport system can be significantly reduced. Additionally, improvements in the electrical properties of a conductor can reduce electrical losses in the transmission system, thereby reducing the need for additional power generation to compensate for such losses.
As noted above, the composite metal matrix wires of the present invention are believed to be particularly well-suited for use in overhead high voltage power transmission cables. In one embodiment, an overhead high voltage power transmission cable can include an electrically conductive core formed by at least one composite metal matrix wire according to the present invention. The core is surrounded by at least one conductive jacket formed by a plurality of aluminum or aluminum alloy wires. Numerous cable core and jacket configurations are known in the cable art. For example, as shown in FIG. 2a, the cross-section of one overhead high voltage power transmission cable 30 may be a core 32 of nineteen individual aluminum or aluminum alloy wires 38.
Likewise, as shown in FIG. 2b, as one of many alternatives, the cross-section of a difference overhead high voltage power transmission cable 30' may be a core 32' of thirty-seven individual composite metal matrix wires 34' surrounded by a jacket 36' of twenty-one individual aluminum or aluminum alloy wires 38'.
The weight percentage of composite metal matrix wires within the cable will depend upon the design of the transmission line. In that cable, the aluminum or aluminum alloy wires used in the conductive jackets are any of the various materials known in the art of overhead high voltage power transmission, including, but not limited to, 1350 Al or 6201 Al.
In another embodiment, an overhead high voltage power transmission cable can be constructed entirely of a plurality of continuous fiber aluminum matrix composite wires (CF-AMCs). As is discussed below, such a construction is well-suited for long cable spans in which the strength-to-weight ratio and the coefficient of thermal expansion of the cable overrides the need to minimize resistive losses.
Although dependent upon a number of factors, the amount of sag in an overhead high voltage power transmission cable varies as the square of the span length and inversely with the tensile strength of the cable. As may be seen in FIG. 3, CF-AMC materials offer substantial improvements in the strength-to-weight ratio over materials commonly used for cable in the power transmission industry. It should be noted that the strength, electrical conductivity and density of CF-AMC materials and cables is dependent upon the fiber volume in the composite. For FIGS. 3, 4a, 4b, and 5 a 50% fiber volume was assumed, with a corresponding density of about 3.2 gm/cm3 (approximately 0.115 lb/in3), tensile strength of 1.38 GPa (200 ksi), and conductivity of 30o IACS.
As a result of the increased strength of cables containing CF-AMC wires, cable sag can be substantially reduced. Calculations comparing the sags of CF-AMC cables as a function of span length with a commonly used steel standing (ACSR) (31 wt% steel having a core of 7 steel wires surrounded by a jacket of 26 aluminum wires), and an equivalent all-aluminum alloy conductor (AAAC) are shown in FIGS. 4a and 4b.
All cables had equivalent electrical conductivity and diameter. FIG. 4a demonstrates that CF-AMC cables provide for a 4001 reduction in tower height as compared to ACSR for spans of about 550 m (about 1800 ft.). Likewise, CF-AMC cables allow for an increase in span length about 25o assuming allowable sags of 15 m (about 50 ft.). Further advantages from the use of CF-AMC cables in long spans are presented in FIG.- 4b. In FIG. 4b, the ACSR cable was 72 wto steel having a core of 19 steel wires surrounded by a jacket of 16 aluminum wires.
The sag of a high voltage power transmission (HVPT) cable at its maximum operating temperature is also dependent upon the coefficient of thermal expansion (CTE) of the cable at its maximum operating temperature. The ultimate CTE of the cable is determined by the CTE and the elastic modulus of both the reinforcing core and the surrounding strands. Within limits, materials with a low CTE and a high elastic modulus are desired. The CTE for the CF-AMC cable is shown in FIG. 5 as a function of temperature. Reference values for aluminum and steel are provided as well.
It is noted that the present invention is not intended to be limited to wires and HVPT cables employing composite metal matrix technology; rather, it is intended to include the specific inventive composite materials described herein as well as numerous additional applications. Thus, the composite metal matrix materials described herein may be used in any of a wide variety of applications, including, but not limited to, flywheel rotors, high performance aerospace components, voltage transmission, or many other applications in which high strength, low density materials are desired.
It should be further noted that although the preferred embodiment makes use of the polycrystalline cx-A1203 fibers described in U.S. Patent No. 4,954,462 currently being marketed under the tradename NEXTELTM 610 by Minnesota Mining and Manufacturing Company of St. Paul, MN, the invention is not intended to be limited to those specific fibers. Rather, any suitable polycrystalline a-A1203 fiber is intended to be included herein as well. It is preferred, however, that any such fiber have a tensile strength at least on the order of that of the NEXTELTM 610 fibers (approximately 2.8 GPa).
In the practice of the invention, the matrix must be chemically inert relative to the fiber over a temperature range between about 20 C-760 C. The temperature range represents the range of predicted processing and service temperatures for the composite. This requirement minimizes chemical reactions between the matrix and fiber which may be deleterious to the overall composite properties. In the case of a matrix material comprising an alloy of elemental aluminum and up to about 2o by weight copper, the as-cast alloy has a yield-strength of approximately 41.4-55.2 MPa (6-8 ksi). In order to increase the strength of this metal alloy, various treatment methods may be used. In one preferred embodiment, once combined with the metallic fibers, the alloy is heated to about 520 C for about 16 hours followed by quenching in water maintained at a temperature of between about 60-100 C. The composite is then placed in an oven and maintained at about 190 C and maintained at that temperature until the desired strength of the matrix is achieved (typically 0-10 days). The matrix has been found to reach a maximum yield-strength of about 68.9-89.6 MPa (10-13 ksi) when it was maintained at a temperature of approximately 190 C for five days. In contrast, pure aluminum that is not specifically heat treated has a yield-strength of approximately 6.9-13.8 MPa (1-2 ksi) in the as-cast state.
ExamUles Objects and advantages of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. All parts and percentages are by weight unless otherwise indicated.
Test Methods Fiber strength was measured using a tensile tester (commercially available as Instron 4201 tester from Instron of Canton, MA) and the test is described in ASTM D 3379-75, (Standard Test Methods for Tensile Strength and Young's Modulus for High Modulus Single-Filament Materials). The specimen gauge length was 25.4 mm (1 inch), the strain rate was 0.02 mm/mm/min.
To establish the tensile strength of a fiber tow, ten single fiber filaments were randomly chosen from a tow of fibers. Each filament was tested to determine its breaking load. At least 10 filaments were tested with the average strength of the filaments in the tow being determined. Each individual, randomly selected fiber had strength ranging from 2.06-4.82 GPa (300-700 ksi). The average individual filament tensile strength ranged from 2.76 to 3.58 GPa (400-520 ksi).
Fiber diameter was measured optically using an attachment to an optical microscope (Dolan-Jenner Measure-Rite Video Micrometer System, Model M25-0002, commercially available from Donal-Jenner Industries, Inc. of Lawrence MA) at x 1000 magnification. The apparatus used reflected light observation with a calibrated stage micrometer.
The breaking stress of each individual filament was calculated as the load per unit area.
The fiber elongation was determined from the load displacement curve and ranged from about 0.55% to about 1.3%.
The average strength of the polycrystalline cx-A1203 fibers used in the working examples was greater than 2.76 GPa (400 ksi)(with 15% standard deviation typical). The higher the average strength of the reinforcing fiber, the higher the composite strength. Composites made according to this embodiment of the present invention has a strength of at least 1.38 GPa (200 ksi)(with 5% standard deviation), and often at least 1.72 GPa (250 ksi)(with 5% standard deviation) when provided with a fiber volume fraction of approximately 60%
(based on the total volume of the composite).
- 18a -Tensile Testing The tensile strength of the composite was measured using a tensile tester (commercially available as an Instron 8562 Tester from Instron Corp. of Canton, MA). This test was carried out substantially as described for the tensile testing of metal foils, i.e., as described in ASTM E345-93, (Standard Test Methods for Tension Testing of Metallic Foil).
In order to perform tensile testing, the composite was made into a plate 15.24 cm x 7.62 cm x 0.13 cm (6"x3"x0.05"). Using a diamond saw, this plate was cut into 7 coupons (15.24 cm x 0.95 cm x 0.13 cm(6"xO.375"xO.05)) which were used for testing.
Average longitudinal strength (i.e., fiber parallel to test direction) was measured at 1.38 GPa (200 ksi) for composites having a matrix of either pure aluminum or pure aluminum with 2% by weight Cu. For composites having a fiber volume content of about 60%, average transverse strength (i.e., fiber perpendicular to the test direction) was 138 MPa (20 ksi) for composites containing pure aluminum and 262 MPa (38 ksi) for composites made with the aluminum/2% copper alloy.
Specific examples of various composites metal matrix fabrications are described below.
Example 1 - Preparation of a fiber-reinforced metal composite A composite was prepared using a tow of NEXTELTM 610 alumina ceramic fibers. The tow contained 420 fibers. The fibers were substantially round in cross-section and had - 18b -average. The average tensile strength of the fibers (measured as described above) ranged from 2.76-3.58 GPa (400-520 ksi).
Individual fibers had strengths ranging from 2.06-4.82 GPa (300-700 ksi).
The fibers were prepared for infiltration with metal by winding the fibers into a"preform". In particular, the fibers were wet with distilled water and wound around a rectangular drum having a circumference of approximately 86.4 cm (34 inches) in multiple layers to the desired preform thickness of approximately 0.25 cm (0.10in).
The wound fibers were cut from the drum and stacked in the mold cavity to produce the final desired preform thickness. A graphite mold in the shape of a rectangular plate was used. Approximately 1300 grams of aluminum metal (commercially available as Grade 99.99% from Belmont Metals of Brooklyn, NY) were placed into the casting vessel.
The mold containing the fibers was placed into a pressure infiltration casting apparatus. In this apparatus, the mold was placed into an airtight vessel or crucible and positioned at the bottom of an evacuable chamber. Pieces of aluminum metal were loaded into the chamber on a support plate above the mold. Small holes (approximately 2.54 mm in diameter) were present in the support plate to permit passage of molten aluminum to the mold below. The chamber was closed and the chamber pressure was reduced to 3 milliTorr to evacuate the air from the mold and the chamber. The aluminum metal was heated to 720 C and the mold (and fibrous preform in it) was heated to at least about 670 C. The aluminum melted at this temperature but remained on the plate above the mold. In order to fill the mold, the power to the heaters was turned ofly and the chamber was pressurized by filling with argon to a pressure of 8.96 MPa (1300 psi). The molten aluminum immediately flowed through the holes in the support plate and into the mold. The temperature was allowed to drop to before venting the chamber to the atmosphere. After the chamber had cooled to room temperature, the part was removed from the mold. The resulting samples had dimensions of 15.2 cm x 7.6 cm x 0.13 cm (6" x 3" x 0.05").
The sample rectangular composite pieces contained 60 volume % fiber.
The volume fraction was measured by using the Archimedes principle of fluid displacement and by examining a photomicrograph of a polished cross-section at 200x magnification.
The part was cut into coupons for tensile testing; it was not machined further. The tensile strength, measured from coupons as described above, was MPa (204 ksi)(Iongitudinal strength) and 140 MPa (20.4 ksi) (transverse strength).
Example 2-Preparation of Metal Matrix Composite Wires The fibers and metal used in this example were the same as those described in Example 1. The alumina fiber was not made into a preform.
Instead, the = 30 fibers (in the form of multiple tows) were fed into a molten bath of aluminum and then onto a take-up spool. The aluminum was melted in an alumina crucible having dimensions of about 24.1 cm x 31.3 cm x 31.8 cm (9.5 "x 12.5 "x12.5 ") (commercially available from Vesuvius McDaniel of Beaver Falls, PA). The temperature of the molten aluminum was approximately 720 C. An alloy of 95% niobium and 5% molybdenum was fashioned into a cylinder having dimensions of about 12.7 cm (5") long x 2.5 cm (1") diameter. The cylinder was used as an ultrasonic horn actuator by tuning to the desired vibration (i.e., tuned by altering the length), to a vibration frequency of about 20.0-20.4 kHz. The amplitude of the actuator was greater than 0.002 cm (0.0008").
The actuator was connected to a titanium waveguide which, in turn, was connected to the ultrasonic transducer. The fibers were infiltrated with matrix material to form wires of relatively uniform cross-section and diameter. Wires made by this process had diameters of about 0.13 cm (0.05").
The volume percent of fiber was estimated from a photomicrograph of a cross section (at 200x magnification) to be about 40 volume %.
The tensile strength of the wire was 1.03 - 1.31 GPa (150-190 ksi).
The elongation at room temperature was approximately 0.7-0.8%.
Elongation was measured during the tensile test by an extensometer.
Example 3-Composite Metal Matrix Materials Using an AUCu Alloy Matrix This example was carried out exactly as described in Example 1, except that instead of using pure aluminum, an alloy containing aluminum and 2% by weight copper was used. The alloy contained less than about 0.02% by weight iron, and less than about 0.05% by weight total impurities. The yield strength of this alloy ranged from 41.4 - 103.4 MPa (6-15 ksi). The alloy was heat treated according to the following schedule:
520 C for 16 hours followed by a water quench (water temperature ranging from 60 -100 C); and immediately placed into an oven at 190 C and held for 5 days.
The processing proceeded as described for Example 1 to produce rectangular pieces to make coupons suitable for tensile testing except that the metal was heated to 710 C and the mold (with the fibers in it) was heated to greater than 660 C.
_ The composite contained 60 volume % of fiber. The longitudinal strength ranged from 1.38 - 1.86 GPa (200 - 270 ksi) (with the average of 10 measurements of 1.52 GPa (220 ksi)) and the transverse strength ranged from MPa (35 - 48 ksi) (with an average of 10 measurements of 262 MPa (38 ksi)).
Equivalents Various modifications and alterations to this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention. It should be understood that this invention is not intended to be unduly limited by the illustrative embodiments and examples set forth herein and that such examples and embodiments are presented by way of example only with the scope of the invention intended to be limited only by the claims set forth herein as follows.
Claims (14)
1. A composite material comprising a plurality of continuous polycrystalline .alpha.-Al2O3 fibers having an average tensile strength of at least about 2.8 GPa contained within a matrix selected from the group consisting of an aluminum matrix and a matrix of an alloy of aluminum and up to about 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrices contain less than 0.05 percent by weight impurities, based on the total weight of said matrices, wherein said matrix being free of material phases or domains capable of the enhancing brittleness of said matrix, and wherein said composite material has an average tensile strength of greater than 1.17 GPa.
2. The composite material according to claim 1, wherein said plurality of continuous polycrystalline .alpha.-Al2O3 fibers includes at least one tow of continuous polycrystalline .alpha.-Al2O3 fibers.
3. The composite material according to claim 1 or 2, comprising between about 30-70% by volume of said polycrystalline alpha.-Al2O3 fibers, based on the total volume of said composite material.
4. The composite material according to any one of claims 1 to 3, comprising between about 40-60% by volume of said polycrystalline a-A1203 fibers, based on the total volume of said composite material.
5. The composite material according to any one of claims 1 to 4, wherein said aluminum matrix contains less than about 0.03% by weight iron, based on the total weight of said matrix.
6. The composite material according to any one of claims 1 to 5 having an average tensile strength of at least 1.38 GPa.
7. The composite material according to any one of claims 1 to 5 having an average tensile strength of at least 1.52 GPa.
8. The composite material according to any one of claims 1 to 5 having an average tensile strength of at least 1.72 GPa.
9. The composite material according to any one of claims 1 to 8, wherein said continuous polycrystalline alpha.-Al2O3 fibers are free of an exterior protective coating.
10. The composite material according to any one of claims 1 to 9, wherein said matrix is substantially pure elemental aluminum.
11. The composite material according to claim 10, wherein said matrix has a yield strength of less than about 20 MPa.
12. The composite material according to any one of claims 1 to 9, wherein said matrix is an alloy of aluminum and up to about 2% by weight copper, based on the total weight of said matrix.
13. The composite material according to claim 12, wherein said matrix has a yield strength of less than about 90 MPa.
14. A wire comprising the composite material as defined in any one of claims 1 to 13.
15. An overhead high voltage power transmission cable which comprises a plurality of wires as defined in claim 14.
16. A method of making continuous composite wire, said method comprising:
melting a metallic matrix material selected from the group consisting of aluminum and an alloy of aluminum with up to 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrix material contain less than 0.05 percent by weight impurities, based on the total weight of said matrix materials, to provide a contained volume of melted metallic matrix material;
imparting ultrasonic energy to cause vibration of said contained volume of melted metallic matrix material;
immersing a plurality of continuous polycrystalline a-A1203 fibers having an average tensile strength of at least about 2.8 GPa into said contained volume of melted metallic matrix material while maintaining said vibration to permit the melted metallic matrix material to infiltrate into and coat said plurality of fibers such that an infiltrated, coated plurality of fibers is provided;
and withdrawing said infiltrated, coated plurality of fibers from said contained volume of melted metallic matrix material under conditions which permit the melted metallic matrix material to solidify to provide a wire as defined in
14. A wire comprising the composite material as defined in any one of claims 1 to 13.
15. An overhead high voltage power transmission cable which comprises a plurality of wires as defined in claim 14.
16. A method of making continuous composite wire, said method comprising:
melting a metallic matrix material selected from the group consisting of aluminum and an alloy of aluminum with up to 2% by weight copper, based on the total weight of said alloy matrix, wherein said matrix material contain less than 0.05 percent by weight impurities, based on the total weight of said matrix materials, to provide a contained volume of melted metallic matrix material;
imparting ultrasonic energy to cause vibration of said contained volume of melted metallic matrix material;
immersing a plurality of continuous polycrystalline a-A1203 fibers having an average tensile strength of at least about 2.8 GPa into said contained volume of melted metallic matrix material while maintaining said vibration to permit the melted metallic matrix material to infiltrate into and coat said plurality of fibers such that an infiltrated, coated plurality of fibers is provided;
and withdrawing said infiltrated, coated plurality of fibers from said contained volume of melted metallic matrix material under conditions which permit the melted metallic matrix material to solidify to provide a wire as defined in
claim 14.