CA2230761C

CA2230761C - Method of forming improved apertured films, resultant apertured films, and absorbent products incorporating resultant apertured films

Info

Publication number: CA2230761C
Application number: CA002230761A
Authority: CA
Inventors: William A. James; William G.F. Kelly; Charles James Shimalla
Original assignee: McNeil PPC Inc
Current assignee: Johnson and Johnson Consumer Inc
Priority date: 1995-09-01
Filing date: 1996-08-27
Publication date: 2007-08-07
Anticipated expiration: 2016-08-27
Also published as: HUP9901669A2; ES2180795T3; JP4302184B2; US6240817B1; CN1200018A; US6022607A; CO4790143A1; WO1997009018A1; ATE220528T1; NZ318589A; NO980832D0; PT847266E; MX9801712A; CZ56598A3; CN1152652C; HUP9901669A3; EP0847266B1; TW381054B; DE69622411D1; BR9610265A

Abstract

An apertured film for use as a topsheet in absorbent products wherein the film is apertured and includes a plurality of micro-holes and a plurality of large-sized holes. A method of forming the film is disclosed, as well as an absorbent product incorporating the apertured film as a topsheet.

Description

-~-= METHOD OF FORMING IMPROVED PsPERTUR]ED FILMS, RESULTANT APERTURED FII.MS, AND ABSORBENT
PRODUCTS INCORPORATING RESULTA] 1T APERTURED FILMS
Field Of The Invention This invention relates to apertured films having priinary utility as a cover member for an absorbent article, and ito methods and apparatus for forming such apertured fi!lms.

Background Of The Invention For many years it has been commein to use nonwoven fabrics as a cover member, or facing layer, for products that are adapted to receive body discharges, such as disposable diapers, sanitary napkins, adult incontinent devices, wound dressings and the Iike. Such fabrics have typically been formed by air-laying, carding, spun bonding and the like, and it is known to post-treat such fabrics to provide strength and integrity, as by the application of binders or fiber entanglement, either mechanically or by the application of fluid forces. Since such fabrics are often formed of hydrophobic material, it is also known to post-treat such fabrics with surface active agents to promote the passage of body discharges through the fabric.
Such fabrics have, or are perceived to have, desiirable characteristics such as breathability, drapeability, softness, and pleasanit hand and tactile impression.
One of the drawbacks associated vaith facing layers formed of a nonwoven fabric is that liquid such as urine, menses, wound exudates, and the like that passes through the facing layer and into the absorbent core has a tendency to strike back through the facing layer, particularly under pressure and when the liquid in the absorbent core approaches the volumetric storage capacity of the core. For this reason, and other reasons, it has been known in the past to utilize apertured plastic films as the facing layer in absorbent articles.

The following list includes disclosures of such apertured films in issued U.S. and foreign patents and published patent applications.
U.S. Patent No. 3,632,269 - Doviak et al.
U.S. Patent No. 3,929,135 - Thompson et al.
U.S. Patent No. 4,324,276 - Mullane U.S. Patent No. 4,351,784 - Thomas et al.
U.S. Patent No. 4,381,326 - Kelly U.S. Patent No. 4,456,570 - Thomas et al.
U.S. Patent No. 4,535,020 - Thomas et al.
U.S. Patent No. 4,690,679 - Mattingly et al.
U.S. Patent No. 4,839,216 - Curro et al.
U.S. Patent No. 4,950,264 - Osborn U.S. Patent No. 5,009,653 - Osborn U.S. Patent No. 5,112,690 - Cohen et al.
U.S. Patent No. 5,342,334 - Thompson et al.
U.S. Patent No. 5,352,217 - Curro U.S. Patent No. 5,368,910 - Langdon U.S. Patent No. 5,368,926 - Thompson et al.
U.S. Patent No. 5,376,439 - Hodgson et al.
U.S. Patent No. 5,382,245 - Thompson et al.
U.S. Patent No. 5,382,703 - Nohr et al.
U.S. Patent No. 5,383,870 - Takai et al.

U.S. Patent No. 5,387,209 - Yamamoto et al. EP 0 304 617 - Suda et al.

EP 0 432 882 A2 - Shipley EP 0 598 204 Al - Garavaglia et al.
EP 0 626 158 Al - Coles et al.
EP 0 626 159 A1 - Taki et al.
EP 0 640 328 - Tanaka et al.
JP 3-286762 A - Yamamoto et al.
WO 92/18078 Al - Colbert WO 93/15701 Al - Turi et al.
WO 94/18926 Al - Perry WO 94/22408 Al - Langdon WO 94128846 Al - Steiger et al.
WO 95/00093 A2 - Osborn et al.
While certain of such apertured films have functioned reasonably well for their intended purposes, the vast majority of such filFns have actual and perceived major deficiencies. For example, even though such apertured films may permit fluid to readily lpass therethrough, and may minimize strike-back of such fluid, such apertured fdms nevertheless tend to have the appearance, feel and hand of a film, 'ratlaer than a fabric. Such fiIm-like characteristics are considered as a negative by the consumer, and thus absorbent products with apertured films as a facing layer have not met with widespread consumer acceptance.
Major improvements for apertured f"zlm facing layers for absorbent products are disclosed in commonly assigned, copending U.S.
patent application Serial Nos. 08/417,404 and 08/417,408 to Turi et al. filed April 5, 1995 as a continuation and a division of Serial No. 08/004,379, filed January 14, 1993 as a continuation of Serial No. 07/744,744, filed August 14, 1991 (corresponding to publication WO 93/15701 Al on the above list).
In the above-mentioned Turi et al. applications, ain apertured film, and methods and apparatus for forming the film, are disclosed which impart to the film physical characteristics like those of nonwoven fabrics. This is accomplished by supporting a film formed of stretchable thermoplastic polymeric material on localized support regions of a backing member, and S directing a fluid in the form of high pressure, small diameter columnar jets against the upper surface of the film, so that unsupported portions of the film are directed downwardly between the support regions to cause the formation of micro-holes and fiber-like elements (fibrils) thereabout to impart to the apertured film physical characteristics of appearance, softness, feel and hand, like those of a nonwoven fabric. While such apertured films are a marked improvement over prior art apertured films, it is desired to provide further improvements in such apertured filsns, as by improving the ability of such films to pass viscous fluids, such as menses.
For use of apertured films as topsheets for sanitary napkins, clean-dry properties are very much desired. This means that the sanitary napkin should appear clean and dry to the user even after it has accepted a flow of inenstrual fluid. There are many factors affecting the clean-dry properties of a sanitary napkin, including the aperture characteristics and open area of the napkin cover material. There is a trade-off in the effects of the film aperture size and open area on clean-dry properties. On the one hand, large apertures allow the fluid to be more rapidly transtnitted to the absorbent core. On the other hand, apertures that are too large permit the fluid to be transported back through the topsheet from the absorbent core (a phenomenon sometimes referred to as "strike back") and to contact the wearer. Furthermore, large open areas tend to allow the stain on the absorbent core of the napkin to be visible through the topsheet and give the wearer the perception that the product has not kept her clean. To exhibit both clean and dry properties, a topsheet must have a carefully balanced combination of aperture size and open area: large enough apertures to rapidly accept a flow of menstrual fluid and to allow it to pass through to the napkin's absorbent core, but small enough to mask the stain on the underlying absorbent core to give the wearer the perception of cleanliness.
Surnmary Of The Inventiqn In accordance with one aspect of the present invention, apertured films of the type disclosed in the above-mentioned Turi et al.
patent applications are improved by providing such fil~ns with larger apertures and a sufficient open area so that viscous fluids, such as menses, can flow readily through the film. These improved properties are imparted to the film by subjecting the film to fluid forces in the form of columnar streams or jets from at least two sets of orifices, the orifices oir one set having a diameter greater than ten mils, and the fluid supplied to ithe orifices having a relatively low pressure less than about 500 psig, and the orifices of at least one other set having a diameter of less than or equal to tein mils and the fluid supplied thereto having a relatively high pressure greater than about 500 psig. The present invention can be practiced with selective variation of the sequence to which the film is subjected to fluid forces from the low and high pressure orifices, that is, first low pressure then high pressure, or 17irst high pressure then low pressure, or other combinations or vai-iations.
The apertures are, for the most part, irregular in shape and size. They are measured by various techniques that approximate the diameter, which may be expressed as equivalent hydraulic diameter (EI-ID) or equivalent circular diameter (ECD). The resulting apertured film has a combination of large sized apertures having average EHD's of from about 7 mils to about 30 mils, and small sized apertures having average EHD's of from about 1 mit to about 7 mils. Such apertured fi.ims have an open area in the range of from about 3 96 to about 13 96 .
The improved apertured film of the present invention is preferably formed on a backing member like that shown in Figures 17-19 of the above-mentioned Turi et al. applications, which results in the fitm having a series of generally parallel ridges formed by generally vertically oriented side walls which define a series of generally parallel valleys. The film thus includes generally parallel alternating solid or closed portions of the film separated by apertured or open portions of the film, that contain the aforementioned combination of large and small sized apertures. Both size apertures are formed as a result of elongating and drawing the stretchable material between the localized support regions of the backing member as a result of the application of fluid pressure, and as the film elongates it undergoes thinning until it finally reaches the point of rupturing (i.e., splitting and fibrillating) to form the above-mentioned apertures.
As with apertured films disclosed in the Turi et al. applications, the apertures are surrounded by a network of fiber-like elements or micro-strips of drawn plastic material. Such drawn fiber-like elements (fibrils) cooperate with the apertures to provide the apertured film with physical characteristics similar to those of nonwoven fabrics. The fiber like elements have lengths. varying from about 0.005 inch (0.013 cm) to about 0.05 inch (0.127 cm), widths ranging from about 0.001 inch (0.003 cm) to about 0.035 inch (0.089 cm), and thicknesses ranging from about 0.00025 inch (0.0006 cm) to about 0.002 inch (0.005 cm).
In accordance with the present invention, apertured films of the type disclosed in the above mentioned Turi et al. applications are modified so as to provide the film with improved fluid distribution properties in the region of the film which have been subjected to stretching, by downward deflection of the film into the recessed region of'the support member, during formation of the film.
The method for forming an apertu;eed fi.lm from a stretchable thermoplastic polymeric material in accordance with the invention comprises the steps of providing a starting flm comprising said stretchable thermoplastic polymeric material and having an upper surface and a lower surface. A backing member comprising localized support regions for supporting the starting film is provided. The backing member has recessed zones into which the film may be deformed by the application thereto of fluid forces. Means for allowing said applied fluid to be transported away from the backing member are provided.
The starting film on the backing member has portions of the lower surface of the film being in contact with the support regions of the backing member. The upper surface of the film faces away from the backing member.
A fluid in the form of columnar sti-eams from at least two sets of orifices is directed against the upper surface of the starting film in a zone of contact, i.e., a zone in which the film is subjected to the forces from the fluid streams. The orifices of the first set each have a diameter greater than ten mils and the fluid supplied thereto has a pressure less than 500 psig. to cause the formation of large sized holes in said starting film. The orifices of the second set each have a diameter less than or equal to ten mils and the = 25 fluid supplied thereto has a pressure of at least 500 psig. to cause the formation of micro-holes in the starting film.

The film is removed from the contact zone, and the now-apertured film is removed from the backing member.

According to one aspect of the present invention, there is provided a method for forming an apertured film from a stretchable thermoplastic polymeric material comprising: a) providing a starting film comprising said stretchable thermoplastic polymeric material having an upper surface and a lower surface; b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces; and means for allowing said applied fluid to be transported away from said backing member; c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member; d) forming irregular size micro-holes and large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from at least two sets of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, the orifices of the first set having a diameter greater than ten mils and the fluid supplied thereto having a pressure less than 500 psig. to cause said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions, the orifices of the second set having a diameter less than or equal to ten mils and the fluid supplied thereto having a pressure of at least 500 psig., to cause said starting film to rupture into a multiplicity of said micro-holes in said starting film between said -8a-localized support regions; e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

According to another aspect of the present invention, there is provided a method for formin(g an apertured film from a stretchable thermoplastic polymeric material comprising: a) providing a starting film comprising said stretchable thermoplastic polymeric material and having an upper surface and a lower surface; b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces, and means for allowing said applied fluid to be transported away from said backing member, c) a supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member; d) forming irregular large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a first set of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices in said first set having a diameter greater than or equal to ten mils and the fluid supplied thereto causing said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions; forming irregular size micro-holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a second set of orifices against the upper surface of said starting film in a zone of -8b-contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices in said second set having a diameter less than or equal to ten mils and the fluid emitted therefrom causing said starting film to rupture into a multiplicity of said micro-holes in said starting film between said localized support regions, said micro-holes being defined by fibrils of said thermoplastic material; e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.
According to still another aspect of the present invention, there is provided a method for forming an apertured film from a stretchable thermoplastic polymeric material comprising: a) providing an embossed starting film comprising said stretchable thermoplastic polymeric material having an upper surface and a lower surface; b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces; and means for allowing said applied fluid to be transported away from said backing member; c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member;
d) forming irregular size micro-holes and large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from at least two sets of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, the orifices of the first set having a diameter greater than ten mils and -8c-the fluid supplied thereto having a pressure less than 500 psig. to cause said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions, the orifices of the second set having a diameter less than or equal to ten mils and the fluid supplied thereto having a pressure of at least 500 psig., to cause said starting film to rupture into a multiplicity of said micro-holes in said starting film between said localized support regions; e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

According to yet another aspect of the present invention, there is provided an apertured film formed from a starting film of stretchable thermoplastic polymeric material, and having a given thickness dimension comprising:
a plurality of apertures extending through the thickness dimension of said film, said plurality of apertures including first and second groups of apertures, and the apertures of said first group having a size greater than the size of the apertures in said second group, the apertures of said first and second groups being defined by fibrils formed from said thermoplastic polymeric material, said first and second groups of apertures having been produced by the process of subjecting unsupported portions of the polymeric material to columnar streams of pressurized fluid directed at said material in a zone of contact to cause the material to stretch between localized support regions over recessed zones wherein the first group of apertures comprises irregular holes formed by the columnar streams from a first set of orifices and wherein the second group of apertures comprises irregular holes formed by the columnar streams from a second set of smaller orifices, said material adjacent each said aperture having been thinned relative to -8d-the portions of said material which have not been thinned, said thinned material having irregular curving portions formed free of contact with said localized support regions.

According to a further aspect of the present invention, there is provided an absorbent product comprising: an absorbent core having oppositely facing major surfaces, and an apertured film covering at least one of said major surfaces, said apertured film having an outwardly facing body contacting side and an opposite side facing inwardly toward said core, said apertured film being formed from a starting film of stretchable thermoplastic polymeric material, and having a given thickness dimension, said apertured film having a plurality of apertures extending through the thickness dimension of said film, said plurality of apertures including first and second groups of apertures, and the apertures of said first group having a size greater than the size of the apertures in said second group, the apertures of said first and second groups being defined by fibrils formed from said thermoplastic polymeric material, said first and second groups of apertures having been produced by the process of subjecting unsupported portions of the polymeric material to columnar streams of pressurized fluid directed at said material in a zone of contact to cause the material to stretch between localized support regions over recessed zones wherein the first group of apertures comprises irregular holes formed by the columnar streams from a first set of orifices and wherein the second group of apertures comprises irregular holes formed by the columnar streams from a second set of smaller orifices, said material adjacent each said aperture having been thinned relative to the portions of said material which have not been thinned, said thinned material having -8e-irregular curving portions formed free of contact with said localized support regions.

According to yet a further aspect of the present invention, there is provided a method for forming an apertured film from a stretchable thermoplastic polymeric material comprising: a) providing a starting film comprising said stretchable thermoplastic polymeric material and having an upper surface and a lower surface; b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces, and means for allowing said applied fluid to be transported away from said backing member; c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backin(g member and with the upper surface of said film facing away from said backing member; d) forming irregular size holes having an average EHD of about 7 to 30 mils in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a first set of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices having a diameter greater than or equal to ten mils and the fluid supplied thereto causing said starting film to rupture into a multiplicity of said holes in said starting film between said localized support regions; e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

Other features and advantages of the present invention will become readily apparent from the following -8f-detailed description, the accompanying drawings, and the appended claims.

Brief Description Of The Drawings FIG. 1 is a schematic side elevational view of a production line for forming apertured film in accordance with the present invention;

FIG. 2 is a schematic side elevational view, on an enlarged scale, of the unwind section of the apparatus for producing the apertured film of the present invention;

FIG. 3 is an enlarged side elevational view of the aperturing section of the apparatus used to form the apertured film of the present invention;

FIG. 4 is an enlarged side elevational view of the dewatering section of the apparatus used to form the apertured film of the present invention;

FIG. 5 is an enlarged side elevational view of the drying section of the apparatus used to form the apertured film of the present invention;

FIG. 6 is an enlarged side elevational view of the slitter/rewinder section of the apparatus used to form the apertured film of the present invention;

FIG. 7A is a schematic view of an orifice strip used in the apparatus to form one of the apertured films of the present invention;

WO 97/09018 PCT/iJS96/13796 FIGS. 7B, C, D and E are enlarged views of orifice patterns which can be used in the apparatus to form the apertured films of the present invention;
FIG. 8 is an exploded perspective view of a starting film positioned on a backing member for processing in accordance with the present invention;
FIG. 9 is a top plan view of the backing member shown in the lower portion of FIG. 8;
FIG. 10 is an enlarged cross-sectional view taken along line 10-10 of FIG. 9;
FIGS. 11A-D are views similar to FIG. 10 showing sequential stages in the drawing of the starting film to form apertures in accordance with the teachings of the present invention;
FIG. 12 is a photograph in top plan of an apertured film formed in accordance with the present invention at a magnification of 7.5 times;
FIG. 13 is an end elevational view of the apertured film of FIG. 12;
FIG. 14 is an end elevational view of the apertured film of FIG. 12 at a magnification of 15 times;
FIG. 15 is a top plan view of another apertured film formed in accordance with the teachings of the present invention at a nnagnification of 7.5 times;
FIG. 16 is an end elevational view of the apertured film of = 25 FIG. 15;
FIG. 17 is an end elevational view of the apertured film of FIG. 15 at a magnification of 15 times;

FIGS. 18A and B are photographs taken at a magnification of X of apertured flm formed in accordance with the invention, formed from an embossed starting fi~im having the female side thereof against the associated forming member, wherein the film was subjected to aperturing by 5 a sequence of three orifice strips, the first having relatively large orifices in accordance with FIG. 7D, and the second and third having relatively small orifices in accordance with FIG. 7A (FIG. 18A being the side thereof against which the water jets were directed, FIG. 18B being the side thereof positioned against the associated forming member);
10 FIGS. 18C and D are photographs taken at a magnification of 10 X of apertured film formed in accordance with the invention, formed from an embossed starting film having the female side thereof against the associated forming member, wherein the film was subjected to aperturing by a single orifice strip having relatively large orifices in accordance with FIG.
7D (FIG. 18C.showing the side thereof against which the water jets were directed, FIG. 18D showing the side thereof positioned against the associated forming member);
FIG. 19 is a block diagram showing the various steps of the process for producing the apertured film in accordance with the present invention;
FIG. 20 is a perspective view of a sanitary napkin comprised of an apertured film according to the present invention; and FIG. 21 is a view, partially in section, taken along line 21-21 of FIG. 20;
FIG. 22 is a graph depicting aperture size distribution in a sample of apertured film made at 875 psig. on an apparatus using three -li-orifice strips each having a plurality of orifices, all of the orifices being mils in diameter;
= FIG. 23 is a graph depicting aperture size distribution in a sample of apertured film made on an apparatus comprising a single orifice strip having a plurality of orifices each 20 mils in diameter, said orifice strip being shown in FIG. 7C;
FIG. 24 is a graph depicting aperture size distribution in a sample of apertured film made on an apparatus comprising a first orifice strip (shown in FIG. 7C) having a plurality of orifices, all of which have a diameter of 20 mils, and a second orifice strip, downstream of the first strip, wherein the second strip (shown in FIG. 7A) has a plurality of orifices all of which have a diameter of 5 mils;
FIG. 25 is a graph depicting aperture size distribution in a sample of apertured fitm made in accordance with the invention; and 15. FIG. 26 is a graph depicting the results of comparison in which the spacing of the orifices comprising the orifice strip is varied.

Description Of The Preferred Embodiments While the present invention is susceptible of embodiment in various forms, there is shown in the drawings and will hereinafter be described presently preferred embodiments, witl;- the understanding that the present disclosure is to be considered as an exenlplification of the invention, and is not intended to limit the invention to the specific embodiments illustrated.
Referring now to the drawings, FIG. 1 is a schematic, side elevational view of one embodiment of a production line that may be utilized to produce apertured films in accordance with the teachings of -the present invention. As is indicated by the direction arrow, the process flow proceeds from right to left in FIG. 1. As is shown in FIG. 1, the production line hai five major stations; a film unwinding station 30, an aperturing station 40, a dewatering station 50, a drying station 60, and a slitting, rewinding, and surfactant application station 70.
As shown in FIG. 2 in the film unwinding station, two rolls 31 of slarting film material 33 are mounted for rotation on frame F. The film from rolls 31 is fed over guide rollers and into festoon 32 which has an automatic (closed loop) tension control system. Film 33, under suitable tension, e.g., between 0.1 to 1 pound per linear inch, emerges from festoon 32, and proceeds to the aperturing station 40.
While many different starting film materials are suitable for use in the present invention, one of the preferred materials is a polyethylene film commercially available from Exxon Chemical under product designation EMB-631. This film is an embossed, white pigmented polyethylene filni.
The polyethylene component consists of a blend of 40% by weight low density polyethylene and 60% by weight linear low density polyethylene.
The film has 6.5 % by weight titanium dioxide.
The starting ftlm is embossed with a diamond pattern at 165 lines per inch to provide on one side of the film, referred to as the male side, a plurality of discontinuous observable protrusions separated by a continuous, interconnected grooved pattern. The other side of the embossed starting film, referred to as the female side, has a plurality of observable, cupped recesses separated by a continuous, interconnected rib pattern. The cupped recesses in the female side of the film are in respective registration with the protrusions on the male side of the film. The starting film is electrostatically treated with a corona discharge treatment on one side, preferably the male side. The film has an ultimate tensile strength of 1750 grams in the machine direction (with 500% elongation at break), and 1300 grams in the cross direction (with 650% elongation at break), as determined using ASTM test D-882.
The process for making the film of the invention may be either batch or continuous, generally similar to the batch and continuous processes disclosed in co-pending Serial No. 08/417,404. The preferred embodiment is a continuous apparatus, as further disclosed herein.
With reference to FIG. 3, the film 33 from the unwind station is shown entering aperturing station 40 at the right hand side thereof.
Aperturing station 40 includes a honeycomb-type support drum 41 rotatably mounted on a frame F1. The drum 41 has a thr-ee-dimensional backing or forrning member, described in detail hereinafter, mounted on its outer peripheral surface. Four water jet manifolds 42 are also supported on frame Fl and four suction slots, one for each manifold. 42, are provided interiorly of the support drum, as ~is also hereinafter described in detail. The suction slots are mounted within the drum and are aligned with the water jet manifolds located outside of the drum. Each waiter jet manifold comprises a metallic strip, hereinafter sometimes referred to as an orifice strip, having a plurality of orifices having predetermined size and spacing. Specific examples of such orifice strips are described in 'more detail hereinafter. A
given manifold 42 may comprise one or more orifice strips. The orifice size preferably remains constant for each strip. However, the orifice size may vary on a given strip. The distance between the lower surface of the orifice strip and the outer surface of the backing member of the aperturing drum is preferably in the range of between 0.50 to 1.0 inches.

Hot water under pressure is pumped to the manifolds 42, and the pressurized water exits through the plurality of orifices in the orifice strip in the form of columnar water jets. The water pressure in each manifold 42 may be separately regulated. The entering film 33 is trained over a guide roller 43, and then over the outer periphery of the three dimensional forming member mounted over the support drum 41. The columnar streams of water exiting the orifice strips impinge on the film and cause the film to deflect downwardly into the recessed regions of the backing member mounted on the support drum, thereby causing the film to stretch and rupture into a multiplicity of irregular size holes. The now-apertured film 44 emerges from aperturing station 40 at the left-hand side thereof and passes to dewatering section 50.
As is shown in FIG. 4, in the dewatering section 50, two dewatering drums 51 are mounted for rotation on firame F3. Drums 51 have a honeycomb configuration, and each drum has two vacuum slots associated therewith, capable of drawing vacuum up to 7 inches Hg. Twelve air knives 52 are provided, six air knives being provided for each drum 51. The suction slots associated with the dewatering drums 51 are located internally of the drums, whereas air knives 52 are located outside of the dnims 51.
Excess water is removed from the apertured film by the impingement of high velocity air from knives 52 and by suction through the suction slots in drums 51. Air knives 52 operate at an air temperature range between about 150 -180 F. Total air flow through the twelve air knives 52 is between about 1,000 to about 2,000 cubic feet per minute per linear foot of apertured film width. The dewatered film 53 emerges from the dewatering station 50, at the left-hand side thereof, and passes to the drying section.

With reference to FIG. 5, the air drying station 60 is illustrated as including two vacuum drums 61 mounted on ;frame F4. Each drum 61 has a suction slot, which has an arc of 300 around the drum. Twenty air knives 62 are positioned outwardly of each vacuum drum 61 and the air knives 62 operate at a temperature between 150 -180 F. The combined air flow for all forty air knives 62 is between about 5,000 to about 7,000 cfm per linear foot of apertured film width. The pressure drop caused by the vacuum in drums 61 is about 2 inches of water measured across the film. The dried fnlm 63 emerges from drying section 60 at the left-hand side thereof and passes to slitter/rewinder section 70.

Referring now to FIG. 6, the film 63 from the drying section enters the slitter/rewinder station 70 at the right hand side thereof. A
slitter 71, consisting of spaced score cut type slitting Imives, cuts the dried apertured fiim to the desired width. The dried and slit apertured film then passes to a surfactant applicator 72, where a suitable surfactant, e.g., Tween 20, is applied to the film by kiss-coating. The surfactant is preferably provided in an aqueous solution consisting of about 48.8 1.5 percent surfactant. In an exemplary embodiment of the :invention, the surfactant roller coating speed is L5 3 inches per minute. Preferably, the surfactnnt is applied to the male side of the film. The above-mentioned parameters result in a surfactant solution add-on of 0.25 mg/in2 0.07.
Referring to FIGS. 7A-7E, the columnar jets of water are discharged from one or more orifice strips havin;g a plurality of orifices.
Preferably, the orifices are formed by drilling a precursor metallic strip to form cylindrical holes. However, it is anticipated that holes of various shapes may be used.

FIG. 7A shows an orifice strip 80 for delivering columnar jets of water each having a relatively small cross-section to form micro-holes in the film. The orifices 82 in the manifold have a diameter of 5 mils (.005 inch), and are spaced .020 inch apart. This manifold strip is available from the Nippon Nozzle Co., of Kobe, Japan.
FIGS. 7B-7E show orifice strips for producing columnar jets of water, each having a relatively large cross section, to form large sized holes in the film. FIG. 7B shows an orifice strip having two rows 84, 86 of orifices 84', 86' that are spaced apart on opposite sides of a center tangent line. The orifices in each row have a diameter of 15 mils (.015 inch), and are spaced .022 inch apart, center-to-center. The spacing of the orifices in the top row is offset from the spacing of the orifices in the bottom row by .011 inch. The strip contains 90.9 orifices per inch.
FIG. 7C shows an orifice strip having two rows 88, 90 of orifices 88', 90' that are spaced apart on opposite sides of a center tangent line. The orifices in each row have a diameter of 20 mils (.020 inch), and are spaced .032 inch apart. The spacing of the orifices in the top row is offset from the spacing of the orifices in the bottom row by .016 inch. The strip contains 62.5 orifices per inch.
FIG. 7D shows an orifice strip having two rows 92, 94 of orifices 92', 94' that are spaced apart on opposite sides of a center tangent line. The orifices in each row have a diameter of 25 mils (.025 inch), and are spaced .038 inch apart. The spacing of the orifices in the top row is offset from the spacing of the orifices in the bottom row by .019 inch. The strip contains 52.6 orifices per inch.
FIG. 7E shows an orifice strip for delivering columnar jets of water, each having a relatively large cross-section for forming large sized holes in film. The orifices each have a diameteir of 0.025 inches, and are spaced 0.083 inches, center-to-center. While the orifice strip shown in FIG.
7E is suitable for forniing film in accordance with the present invention, use of orifice strips such as shown in FIG. 7B-7D is presently preferred for use in combination with one or more orifice strips having relatively small orifices for formation of micro-sized holes.
The small orifices (see FIG. 7A) preferably have a diameter under 10 mils. The larger orifices (see FIGS. 7B-7E) preferably have a diameter greater than 10 mils.
An apparatus for making apertured films of the present invention is described in detail in co-pending patent application Serial No.
08/417,404. The apparatus for making the film of the present invention contains certain additional features, including a second set of orifice strips as discussed above with reference to FIGS. 7B-7E. The pressure of the water delivered to the smail orifices is generally greater than 500 psig, preferably on the order of 500-1600 psig or higher. The pressure of water delivered to the large orifices is generally less than 500 psig, preferably on the order of 125-200 psig.
In a preferred embodiment, the aperturing equipment consists of a honeycomb type support drum, a three dimensional forming member, several water jet manifolds, and corresponding suction slots arranged interiorly of and sequentially along a section of the circumference of the drum. The forming member is an engraved sleeve, as shown in FIGS. 8-10, which is mounted onto the honeycomb support da-um. The suction slots are mounted within the drum and they are lined up with the water jet manifolds located outside the drum. Each water jet manifold contains a metallic strip having a plurality of orifices. For a given manifold, the orifice size remains constant throughout the strip. The distance between the orifice strip and the surface of the engraved sleeve is preferably between 0.50 to 1 inch. The manifolds are pressurized by pumping in heated water. The pressurized water exits through the series of orifices in the orifice strip, thus creating substantially columaar water jets. The energy of the columnar hot water jets impinging on the film causes the film to contour toward the surface of the engraved sleeve thereby causing the filrn to stretch and rupture into a multiplicity of irregular size holes. The pressure and temperature of the water supplied to each ma.nifold may be separately regulated. The process parameters are as follows:
Line Speed (yards/min): 50-200 Water Temperature: 155 - 165 F.
Maximum Number of Manifolds Used: 3 Distance between Manifold Strip and Surface of Sleeve: 0.50"-15. 1"
Low Pressure Manifot :
Number of Manifolds: 1 Orifice Size Range (inch): 0.0145 to 0.030 Pressure (psig): 150 t 25 Water Flow: 8.0 2.0 gallons per minute per inch of orifice strip (gpm/in) Suction Slot Vacuum (inch of Hg): 5.0 2.0 (-17 f 10.2 kPa) High ressure Manifold:
Number of Manifolds: Maximum of 2 Orifice Size Range (inch): 0.005 to 0.007 Pressure" (psig): 1,150 t 350 Water Flow: 0.9 0.22 gallons per minute per inch of orifice strip Suction Slot Vacuum (inch of Hg): 5 3 (-17 10.2 kPa) Manifold Usage Sequence:
The pressurized water jet manifolds and their associated orifice strips can be arr=anged in a variety of sequences relative to the direction of continuous travel of the film on the drum. Any of the following five sequences may be used to aperture the film:
1. Low Pressure, High Pressure 2. Low Pressure, High Pressure, High Pressure 3. High Pressure, Low Pressure 4. High Pressure, Low Pressure, High Pressure 5. High Pressure, High Pressure, Low Pressure Referring to FIGS. 8-10, the forming member is a three dimensional surface having a plurality of radially extending support elements that rise from the base of the forming or backing member. These elements are substantially similar to the corresponding elements disclosed in co-pending patent application Serial No. 08/417,404.
FIG. 8 is an exploded perspective view of starting film 100 supported on backing member 102. The starting film may be either embossed or unembossed. Alternatively, a portion 104 of starting fiilm 100 qomprises embossments' 106, and unembossed regions 108 as shown in the upper portion of FIG. 8.
Backing member 102 comprises a base portion 110 having an upper surface 110a and a lower surface 110b. Backing member 102 further comprises a plurality of apertures 112 running ttirough the thickness of base 110 from upper surface 110a to lower surface 1:10b. As will be seen hereinafter, apertures 112 are provided to allow for removal of water during the manufacture of apertured film according to the invention. Backing member 102 also includes a plurality of radially-extending support elements 114. These support elements comprise a base 116 coinciding with the plane of upper surface 110a of portion 110 and a pair of angled side walls 118, 120 (best seen in FIGS. 9 and 10). Side walls 118, 120 extend outwardly from base 116 to meet at a land portion or ridge 122. Support elements 114 are aligned in parallel and spaced equidistantly from one another. They may run either parallel to, perpendicular to, or at any angle to the sides of the backing member. As shown in FIGS. 8 and 9, these support elements 114, when viewed in plan, are generally sinusoidal-like or wavy in configuration. It will be understood that the support elements may be provided in other configurations, e.g., straight-line, zig-zag and the like. A detailed description of the forming member is disclosed in co-pending patent application Serial No. 08/417,404.
Referring to FIGS. 11A-D, the progression of the drawing of the starting film 124 to form apertures in accordance with the teachings of the present invention are shown. Referring to FIG. 11A, the starting film 124 is initially laid on the backing member. Referring to FIG. 11B, the film 124 deforms in response to the application of columnar jets of water and is drawn (i.e., stretched) downwardly and partially into the space between support elements. Referring to FIG. 11C, as the film 124 is drawn, it becomes thinner. Referring to FIG. 11D, as the film is further drawn and becomes thinner, it begins to break apart and form holes 126. This process is further described in co-pending patent application Serial No. 08/417,404, wherein the formation of micro-holes surrounded by micro-strips of film material, or fibrils, is described.

Due to the vertical elements on the forming member, the fim of the present invention is expanded (i.e., is gilren significant dimensionality in the z-direction relative to the original thicDcness of the precursor unapertured film) immediately as it comes off drie process. In some prior art processes, expansion in the z-direction must be accomplished in a separate embossing step (see for exaialpte, U.S. Patent No. 4,609,518). An expanded topsheet limits the contact between the wearer and the absorbent layer and thus enhances the feeling of dryness in products that incorporate it.
In the fiims, absorbent products and methods disclosed herein, the holes in the film include both micro-holes and large sized holes, or may include large sized holes only. It is believed that the niicro-holes are formed primarily from the drawing of film material in response to application of colurnnar jets of water coming from the smaller orifices of the orifice strip discussed above. It is believed that the large sized holes, also formed from the drawing of film material, are formed primar6ly in response to application of the columnar jets of water coming from the larger orifices, rather than the smaller orifices, of the orifice strip discussed above.
The resulting apertured film has a combination of large sized holes or apertures having average EHD's of frorii about 7 mils to about 30 nails, and stnall sized apertures or holes, sometir,gles referred to as micro-sized holes, having average EHD's of from about 1 mil to about 7 mils. Such apertured films have an open area in the range of from about 3% to about 13 96 . It has been found that using orifice strips having orifices whose diameters range from about 10 to 25 mils results in the formation of apertures in the film having an average EHD of ;about 7 mils to about 17 mils. The fibrils surrounding and defining the naicro-hoies and the large sized holes are described in detail in co-pending patent application Serial No.

----_ _---_--08/417,404. The fibrils have lengths ranging from about 0.005 inch (0.013 cm) to about 0.05 inch (0.127 cm); widths ranging from about 0.001 inch (0.003 cm) to about 0.035 inch (0.089 cm); and thicknesses ranging from about 0.00025 inch (0.006 cm) to about 0.002 inch (0.005 cm).
Photographs in FIGS. 12-18A, B show the combination of micro-holes and large sized holes of an apertured film made in accordance with the invention.
Photographs in FIGS. 18C, D show large sized holes of an apertured film made in accordance with the invention.
The combination of large sized holes and micro-holes of the dimensions discussed above yield an improvement in the clean and dry properties of the film when used as a topsheet for a sanitary napkin. The resulting open area is in the range of 3 to 13 %. In the prior art film having micro-holes only (see co-pending application Serial No. 08/417,404), when 5 mil diameter columnar jets of water are used, the resulting apertured film has nnicro-holes with an average EHD of 3 mils, and has. an open area of about 3%. The increased aperture size and open area in an apertured film having large sized holes in combination with micro-holes in accordance with the invention provides an improved level of aperture size and open area so as to strike an advantageous balance: large enough apertures to rapidly accept a flow of menstrual fluid and to allow it to pass through to the napkin's absorbent core, but small enough to mask the stain on the absorbent pad to give the consumer the perception of cleanliness. Thus, the absorbent products of the present invention made with the apertured films of the present invention have much improved clean and dry properties.
In a preferred embodiment of the invention, the starting film is apertured by large diameter, low pressure columnar water jets and small diameter, high pressure columnar water jets. This combination of jets at both high and low pressure produces larger apertures and greater open area than fdms made with small diameter high pressure jets alone. Films made by this embodiment also appear softer to the user thanFilms niade only with large diameter, low pressure jets.
FIG. 19 is a block diagram showing the several steps in the process for producing the novel apertured films of the present invention. The first step in the process is to position a piece of thin, stretchable film of thermoplastic polymer material on a backing or support member (Box 1).
The support member with the stretchable film thereon is passed under high pressure fluid ejecting nozzles (Box 2). The preferred fluid is water. The water is transported away from the support member, preferably using a vacuum (Box 3). The ftlm is de-watered, suction being preferred for this purpose (Box 4). The de-watered apertured film is removed from the support member (Box 5). Residual water is removed from the apertured film, e.g., by applying a stream of air thereto (Box 6). Surfactant is next applied to the apertured film (Box 7). The apertured film is then rolled up to await use as is or as a structural component of another product such as a sanitary napkin, disposable diaper or wound dressing (Box 8).
Referring to FIGS. 20 and 21, there is shown a sanitary napkin 130 comprising an absorbent core 132 of wood pulp fibers, a thin, fluid-impermeable barrier film 134 and a covering nuiterial 136 which may be any of the apertured films of the invention. Preferably, the covering filin material has the structure shown and described herein. Barrier fiim 134, which may comprise, e.g., a thin film of polyetlzylene, contacts the lower surface of absorbent core 132 and runs part way up the longitudinal sides of the absorbent core. Covering material 136 has a length somewhat longer than the length of the absorbent core and is wrapped around the absorbent core and barrier film as shown in FIG. 21. The longitudinal edges of the cover material are overlapped and sealed together on the lower surface of the napkin in the usual manner. In the embodiment illustrated, the cover material is sealed to itself at the ends 138, 140 of the sanitary napkin. As illustrated in FIG. 21, sanitary napkin 130 has a layer of adhesive 142 for adhering the napkin to the undergarment of the user. Adhesive 142 is protected prior to use by a removable release strip 144.

E~AMPLE 1 In one embodiment of the apertured film in accordance with the invention, the starting material is an embossed film supplied by Exxon Chemical under the designation EMB-631, and having a thickness of 0.95 mils. This film is corona discharge treated on its male side. The film is placed on the forming member shown in FIGS. 8-10 which is mounted on a support drum as described in co-pending applications Serial Nos. 08/417,404 and 08/417,408 to Turi et at. with the corona-treated male side of the film facing away from the forming member. Two manifolds for directing columnar streams of water at the film were used. The first, or upstream, manifold has the orifice configuration shown in FIG. 7D of the drawings, i.e., there are two offset rows 92, 94 of orifices 92', 94', each of the orifices having a diameter of 0.025 inches. The orifices are spaced a distance of 0.038 inches center-to-center to provide a total of 52.6 holes per inch. The second, or downstream, manifold has the orifice configuration shown in FIG.
7A of the drawings, i.e., there is a single row of orifices each having a diameter of 0.005 inches. These orifices are spaced 0.020 inches on a center-to-center basis. There is a total of 50 such orifices per inch. Water having a temperature of 165 F is supplied at a pressure of 165 psig to the WO 97/09018 PCTlUS96/13796 first manifold. and at a pressure of 1400 psig to the second tvanifold. The fiim is passed under the manifolds at a speed of 435 feet per minute. The suction pressure inside the drum is minus 50 inches of water. The film is dewatered with the apparatus shown in FIG. 4 and is dried with the apparatus shown in FIG. 5. Following drying, the male side of the flnn is kiss-coated with a 48.8% solution of Tween-20 in water to a. solution add-on of 0.25 tng/inZ. Subsequent rolling of the film effects transfer of the surfactant solution from the corona-treated male side to the female side. After the surfactant solution ultimately dries, the film has a bulk surfactant add-on (including all surfaces of the film) of 0.12 mg/in$. The resulting apertured film has an air permeabi;lity of approximately 325 cubic feet per minute per square foot (cfm/ft2) at a pressure differential (AP) of 0.5 inches of water.
The film has a measured open area of 6.24% and an average ECD of 10-11 mils. ECD (Equivalent Circular Diameter) is aimlcuiated aperture diameter tliat is based on a measurement of the area of the aperture. The area is measured using the disclosed hardware and software for measuring EHD in co-pending patent application Serial No. 08/417,404. The formula for ECD
is ECD ='/44 , where A is the measured area of an aperture. There is an n average of 500 apertures per square inch. The bulk thickness is 14.5 miLs.

Another embodiment of the apertured film of the invention was made using the same starting film and forming m!ember as used in Example 1. The line speed was 50 yds/min. Two manifoids for directing columnar streams of water at the film were used. The first, or upstream, manifold has the orifice configuration shown in FIG. 7C of the drawings9 i.e., there are two offset rows 88, 90 of orifices 88', 90', each of the orifices having a diameter of 0.020 inches. The orifices are spaced a distance of 0.032 inches center-to-center to provide a total of 62.5 holes per inch. The second, or downstream, manifold has the orifice configuration shown in FIG. 7A of the drawings, i.e., there is a single row of orifices each having a diameter of 0.005 inches. These orifices are spaced 0.020 inches on a center-to-center basis. There is a total of 50 such orifices per inch. Water having a temperature of 160 F. is supplied at a pressure of 150 psig to the first manifold, and at a pressure of 1500 psig to the second manifold. The drum had a vacuum of 6 inches of Hg (-20.4 kPa).
In the dewatering section, there were six dewatering knives, and a vacuum of 4" of Hg. The air temperature for the first set of air knives was 180 F. The air temperature for the second set of air knives was 120 F. There were two fiIm drying cylinders and each cylinder had five heated air knives. The hot air temperature for the knives was 150 F., and the vacuum was less than 1" of water.
The apertured film produced according to Example 2 was analyzed by microscopy. Open area, hole size distribution and total features (number of holes) were measured by image analysis techniques, with the following results:
Open Area St. E.H.D.* ECD Apetture (mean) Dav. (mean) (mean) St. Dev. Coun.t 6.19% .68 7.61 mils 10.85 mils 10.47 858/sq.in.
mils * EHD is measured as discussed in co-pending patent application Serial No. 08/417,404, which is incorporated by reference.

The characteristics of the orifice strips used in the experiments described below are shown in Table 1:

Table 1. Characteristics of 01ifice Stricrs Orifice Orifice Number Of Rows Intra-Row Spacing Number Of Orifices Strip Size Of Orifices Per Between Orifices Per Strip Per Inch ID (inches) Orifice Strip (center-to-center, in.) Of Orifice Strip a 0.005 1 0.020 S0 b 0.010 2 0,:015 133 c 0.015 2 0.022 90.9 d 0.020 2 0.032 62.5 e 0.025 2 0.038 52.6 f 0.025 1 0.083 12 Experimentation With Batch Formation Of Films, The batch filan aperturing apparatus used in the experiments reported in Table 2 below was similar to that sh4ywn in FIG. 3 of the drawings. However, only one water manifold 42 was used, and only one of the available vacuum slots was used. Each of the orifice strips labeled "b"
through "f" in Table 1 was in turn mounted in the single water jet manifold and used to make one or more apertured films as shown in Table 2. The starting film and forming member were the same as those used in Example 1.
A piece of starting film was mounted to the outer surface of the forming member by a series of pins projecting from the forming member.
The honeycomb support drum was rotated so that the mounted film was out of line with the single orifice strip. Vacuum was applied to the inside of the honeycomb support drum. Heated, pressurized water was supplied to the manifold. The honeycomb support drum motor was rotated to pass the starting film once under the orifice strip. The resultant film was removed from the forming member and air dried. Process conditions used to make films and the resultant film properties are shown in Table 2 below.

Table 2. Batch Film& ring EXperiments Meaa Equivalent Hydrauiic Water Water Film Open Diameoer Orifice Pressure Temp. Vacueua* Speed Area (BHD)-' Ex.# ID (Pu7 ('F.) (in.Water) (R/aiin) (%)** (amila) 1 b 350 160 60 130 3.6 10.7 2 b 550 160 60 150 6.5 10.3 3 b 1000 160 60 150 8.5 7.7 4 c 200 160 60 1S0 2.9 11.7 25 5 c 400 160 60 150 8.7 16.3 6 c 550 160 60 150 11.7 14.3 7 c 850 160 60 150 11.5 8.7 8 d 160 160 60 150 1.5 11.1 9 d 250 160 60 150 8.1 17.1 10 d 350 160 60 150 9.4 14.7 11 d 550 160 60 150 13.2 13.7 12 e ISO 160 60 150 2.0 10.1 13 e 240 160 60 150 7.4 14.9 14 e 375 160 60 150 12.8 172 14a f 150 160 60 150 3.5 13.0 (1) 14b f 200 160 60 150 5.71 12.8 (1) 14c f 250 160 60 150 6.0 11.5 (1) * vacuum value is inches of water below atmospheric pressure.

** Open Area and EHD were measured according to the method disclosed in co-pen.ding application Serial No.
08/417,404, which is incorporated herein by reference.
(1) = ECD
The data indicate the following trt:nds:
= Increasing the fluid pressure with an orifice strip of a given size increases open area.
= Increasing the orifice diameter increases open area at a given fluid pressure.
Due to stretch of material that oecisrs during the process of forming apertures, the weight per area of the fibcn is reduced to about 0.47 oz/sq.yd, which is 65% of the initial film weight per unit area. When the 0.025 inch diameter orifice strips spaced at 0.038 inch, 0.050 inch, 0.062 inch and 0.075 inch of Table 8 were used, the open area decreased from 13.1% to 12.0, 11.2, and 10.1% respectively.

Eperimentation With Continuous FQrmation OfeEHM
Additional embodiments of films according to the present invention were made using the starting film, fonning member and general procedure of Example 1. The characteristics of the orifice strips used are described in Table 1 above. All of the runs were made using water at 160 F, with the corona treated male side of the starting ftlRn facing away from the forming member. The number of orifice strips used, and their characteristics and processing conditions are shown in the following table:

Table 3. Continuous Film A2ertvring Exveriments Orifice Strip 11 Orifice Strip #'2 Orifice Strip /3 I.ine Orifice Pressure Orifice Pressure Orifice Pressure Speed Experiment A' Strip ID (psi) Strip ID (psi) Strip ID (psi) (R/min) 1S d 150 120 16 d 150 a 1000 120 17 d 150 a 1000 a 1000 120 18 a 1000 120 19 a 1000 a 1000 120 a 875 a 875 a 875 120 21 a 875 a 875 a 875 150 22 a 1000 d 150 120 15 23 a 1000 d 150 a 1000 120 Following air drying, the films were kiss-coated with an aqueous solution of Tween 20 surfactant at a concentration of 48.8% on the corona-treated male side to produce a bulk surfactant add-on of 0.12 mg/in2 20 of film as described hereinabove in connection with Example 1.
The apertured films produced in these experinients were evaluated for air permeability, aperture size, open area, strikethrough and bending length (a measure of film stiffness). Tests were run according to the following methods well known in the art. Air permeability was tested according to ASTM D737. Film aperture size and open area were determined and used to calculate Equivalent Circular Diameter (ECD).
Strikethrough is a measurement of the time required for 5 cc of a test fluid to be absorbed through the film supported on ground fluff wood pulp. The test fluid is a mixture of 75% by weight of defibrinated bovine blood and 25% by weight of a 10% by weight aqueous solution polyvinylpyrrolidone (GAF
Povidone K-90). Bending length in the machine direction (MD) and cross direction (CD) were measured according to ASTM D1388. The properties of the film produced in continuous runs are shown in Tables 4-7 below.
Table 4. Continuous Apgrtured Film P=rties - Air P&rmeability Air Permeability Experiment # CFM/SQFT 0 0.5 in. H20 aP) 139.33 10 16 222.00 17 246.67 18 107.00 19 143.67 173.67 15 21 170.67 22 214.33 23 212.67 The data in Table 4 show that the combination of large 20 diameter and small diameter orifices (experiment<,c 16,17, 22 and 23) produces a more permeable, open film than films made witla small diameter orifices alone (experiments 18-21). It is believed that the use of large diameter orifices, albeit used at lower water pressure, is the primary cause for the creation of large holes. Further, it is believed that the use of smaller diameter orifices is the primary cause for the creation of the smaller micro-holes.

WO 97/09018 PC'd'/US96/13796 Table 5. Continuous Agertured Film Properties - Aperture Size And n Area Average Equivalent EC Standard No. Of Circular Deviation Open Area Apertures/squut Experiment # Diameter (mils) (mils) (96) inch 16.46 10.12 4.55 197 16 8.62 9.22 5.34 515 17 7.48 8.47 5.34 715 10 18 4.65 2.66 2.31 1125 19 4.53 2.65 2.48 1283 4.00 2.25 2.38 1635 21 4.16 2.48 2.53 1519 22 6.49 5.59 4.15 806 15 23 6.88 6.18 4.88 856 The data in Table 5 show that the combination of large diameter and small diameter orifices (experiments 16, 17, 22, and 23) produce a film with larger aperture size and increased open area than fihns 20 made with small diameter orifices alone (experiments 18-21).
FIGS. 22, 23 and 24 are graphs that show the aperture size distribution of films produced in these experiments with a 5 mi3 diameter orifice strip (Experiment No. 20), a 20 mil diameter orifice strip (Experiment No. 15), and the combination of a 20 mil orifice strip followed by a 5 nnil orifice strip (Experiment No. 16), respectively (see Table 3 above). As seen from these graphs, the apertured films produced with orifice strips of different diameters have aperture sizes that reflect the effects of various of the individual orifice diameters. The film (Experiment No. 20) produced with only a 5 mil orifice strip has apertures most of which have a diameter under 10 mils (see FIG 22). The film (Experiment No. 15) produced by a 20 mil orifice strip only has a broader distribution of aperture diameters, with peak concentrations at approximately 9 mils and at approximately 23 muAs (see FIG. 23). The film (Experiment No. 16) produced by a combination of a 5 rnil orifice strip and a 20 nul orifice strip haLs a distribution of hole diameters that is primariiy concentrated under 12 mils, and has slight concentration of holes with a diameter of around 23 mils (see FIG. 24).
These three graphs indicate that the 5 mil orifices create micro-holes primarily, that the 20 mil orifices create larger sized holes primarily, and that a combination of 5 rnil orifices and 20 mil orifices creates a combination of micro-holes and large sized holes. Comparable data is shown in FIG. 25 which shows aperture size distribution in a sample of apertured film having micro-holes and large-sized holes in accordance with the invention that was made on a commercial production line.

Table 6. Continuous Apertured Film Prone~.ties - Strikethrough Tune Experiment # Strikethrough Time (sec) 15 16.3 16 17.6 17 13.5 18 28.8 19 25.6 20 20.2 21 22.9 22 15.8 23 17.10 The data in Table 6 show that either large diameter orifices alone, or the combination of large diameter and small diameter orifices (experiments 15, 16, 17, 22 and 23) produce a film with faster strikethrough times than films made with small diameter orifices alone (experiments 18-21).

Table 7. Continuous Apertured Film Properties - Film Stiffness Experiment # MD Bending Length (mm) CD Bending Length (mm) 22.8 6 10 16 26.3 6.5 17 22.3 6.5 18 27 6.3 19 26.8 5.5 26 9.5 15 21 25.5 8.5 22 23.5 5.8 23 27.30 8.0 comparable commercial product 21.8 14.8 The data indicate that the MD bending length of the films of experiments 15-23 is comparable to those of other commercial sanitary napkin plastic covers, and that the CD bending length of the films is lower than comparable commercial fdms. Hence, stiffness and expected comfort of the films of the present invention are expected to be comparable or superior to that of other conunercial apertured films.

Resuits of additional experimentation are shown in FIG. 26. In these experiments, the spacing of the orifices was varied to determine the effect on film open area. Two water jet manifolds were used in these experiments. The first, or upstream, manifold llad one orifice strip with two rows of orifices on respective sides of the longitudinal center line of the strip, the two rows of orifices being offset as shown in FIGS. 7I3-7D, i.e., the offset distance was one-half the intra-row, center-to-center spacing of the orifices. All orifices had a diameter of 0.025 iizch. The center-to-center spacing of the orifices for each experiment was varied as reported in Table 8.
The second, or downstream, manifold had one orifice strip with a single row of orifices therein. The orifices each had a diameter of 0.005 inch and were spaced 0.020 inch on a center-to-center basis. Water was supplied to the first manifold at 150 psig. Water was supplied to the second manifold at 1000 psig. The film traveled at 150 ft/min. The drum vacuum was 60 inches water. The following Table 8 indicates the open area, number of apertures per in2, ECD and air permeability for the resulting apertured films.

Table Equivalent Circular Film Large Orifice* Numbet of Diameter, Air Number Spacing, inch Open Area, % Apertures inch Permeabiiiry 24 0.038 13.1 914 0.0099 505 25 0.050 12.0 1136 0.0085 476 26 0.062 11.2 1151 0.0081 465 27 0.075 10.1 1299 0.0072 435 * Two rows of 25 mil diameter orifices.

Air penneability was measured per ASTM D737; results are reported in Table 8 in cubic feet per minute per square foot of film. The air permeabilities of film apertured at 150 psig and 150 ft/min. were 310 cfm/sf for the 25-mil diameter orifice strip (only) (0.038 inch spacing) control, which decreased nearly linearly to 245 cfm/sf for the 0.075 inch spacing.
When the 5-mil diameter strip was added, the air permeability increased to 505 cfrn/sf for the control spacing. There was a nearly linear decrease with spacing to a value to 435 cfm/sf at 0.075 inches. At 150 ft/min., the combination of the large diameter, 25 mil diameter control strip with the 5-mil strip provides about 195 cfrn/sf beyond the measured air permeability of the large hole strip alone. The above data indicates that as large orifice spacing increases, fewer large-sized holes are produced, and the open area is accordingly reduced.
Apertured films made according to co-pending Serial No.
08/417,404 and films of the present invention were tested and compared.
The films were prepared on the continuous production line under the following conditions shown in Table 9.

Table 9. Apertured FilrtPreparatio And Properties Fiim made according to Serial No. 08/4I7.444 Present Inventias Precursor Film Exxon EMB-631 Exxon EMB-631 Forming Member Pattern siausoidal (12 railslin.) sinusoidal (12 railsf"m.) Number of Orifice Strips 3 2 Orifice Strip #1 Pressure (psig) 875 150 Orifice Strip 12 Pressure (psig) 875 1000 Orifice Strip #3 Pressure (psig) 875 Orifice ID a/a/a d/a Orifice size (mils) 5/5/5 20/5 Water Temperature 1580 F. 160= F.
Line Speed (ft./min.) 150 150 Surfactant Treatment Tween 20 Tweea 20 Sanitary napkins *comprising a cover, an absorbent core and a backsheet were prepared using the apertured film:c of Table 10 as coverstock materials. Two different napkin designs were constructed and tested for strikethrough and rewet using synthetic menstrual fluid. Synthetic menstaval fluid was prepared dissolving 0.15 9c polyacrylamiide in isotonic phosphate buffer. Approximately 0.3% Germaben was added to prevent bacterial growth. The pH of the solution was measured as 7.4, and the viscosity at 30 centipoise at one radian per second. Results are shown in Tables 11 and 12 below.

WO 97/09018 PCT/[JS96/13796 Table 10. Strikethroug=_h And Rewet f NalZkins Made With Apertured Fi In c Napkin Design #1 Film made according to Serial No. 08/417,404 Present Invention 5 cc strikethrough time (sec) 68 62 Rewet (g) 0.04 0.02 Table 11. Strikethrough And Rewet Of Napkins Made With Apezlured FIIIU
Napkin Design #2 Fiim made according to Serial No. 08/417,404 Present Invention 5 cc strikethrough time (sec) 39 39 Rewet (g) 0.11 0.05 The data in Table 10 and Table 11 show strikethrough time and rewet absorption. The strikethrough time refers to the time elapsed for absorption of 5 cc of synthedc menstrual fluid, with a lower time being desirable. Rewet absorption refers to the amount of fluid that can be absorbed in a filter paper that is placed in contact with a sanitary napkin that has absorbed 5 cc of fluid in the strikethrough test, with a lower amount of rewet being desirable.
The data demonstrate that the larger open area and aperture size of the films of the present invention give rise to at least equal or faster strikethrough times than the prior art films. However, even though the improved films of the present invention have larger open area and larger average aperture size than the prior art films, the napkins made with the films of the present invention have unexpectedly lower rewet values relative to prior art films.

---=39-Another test used to measure the rate of transport of inenstrual fluid through the apertured film is the "Drop Test". Comparative data for the films of the present invention versus prior art films are shown in Table 12 below.
Table 12. Drop Test Data For Apertured Films On N;
gpkin Design #1 Fiim Made According To Serial No. 08/417,404 Present Invention Absorption Time (sec) (0 ) 27 8 Absorption Time (sec) Drop rolled off 17 (45 transverse tilt) The data in Table 12 refers to the time required for absorption of a drop of synthetic menstrual fluid, with a lower time being desirable. In the first test, the film was level. In the second test, the film was tilted to an angle of 45 . The data further illustrate the superior fluid transport properties of films of the present invention relative to prior art films.
Apertured plastic filins made acco:rding to the present invention exhibit the following characteristics: tactile sofltness; textile-like look and feel; low film stiffness as described in Table 7; aperturing patterns, open areas, and pore sizes ranges as described in Table 5 and Figures 23-26; low basis weight ( S 0.7 oz/yd2); and film/air/synthetic menstrual fluid contact angles on both sides of the film of 570 .
The apertured film of the present invention, with surfactant treatment, offers overall comparable fluid penetration rate (as measured by 5cc synthetic menstrual fluid strikethrough times - test method described in co-pending patent application Serial No. 08/417,404), which is improved over non-surfactant-treated films by approximately 34% in either a pulp absorbent core construction or a peat moss based absorbent construction.

Claims

CLAIMS:

1. A method for forming an apertured film from a stretchable thermoplastic polymeric material comprising:
a) providing a starting film comprising said stretchable thermoplastic polymeric material having an upper surface and a lower surface;

b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces; and means for allowing said applied fluid to be transported away from said backing member;

c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member;

d) forming irregular size micro-holes and large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from at least two sets of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, the orifices of the first set having a diameter greater than ten mils and the fluid supplied thereto having a pressure less than 500 psig. to cause said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions, the orifices of the second set having a diameter less than or equal to ten mils and the fluid supplied thereto having a pressure of at least 500 psig., to cause said starting film to rupture into a multiplicity of said micro-holes in said starting film between said localized support regions;

e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

2. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 1, wherein said first set of orifices have a diameter in the range of about 10 mil to about 30 mils.

3. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 1, wherein said first set of orifices have a diameter in the range of about 15 mils to about 35 mils

4. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 3, wherein said second set of orifices have a diameter in the range of about 1 mils to about 10 mils.

5. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 3, wherein said second set of orifices have a diameter in the range of about 3 mils to about 7 mils.

6. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 5, wherein said fluid emitted from said first set of orifices has a pressure in the range of about 100 psig to about 500 psig.

7. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 5, wherein said fluid emitted from said first set of orifices has a pressure in the range of about 125 psig to about 200 psig.

8. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 7, wherein said fluid emitted from said second set of orifices has a pressure in the range of about 500 psig to about 2000 psig.

9. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 7, wherein said fluid emitted from said second set of orifices has a pressure in the range of about 800 psig to about 1500 psig.

10. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 9, including the further step of providing a third set of orifices, said third set of orifices having a diameter less than or equal to about ten mils, the fluid supplied thereto having a pressure of at least 500 psig.

11. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 10, wherein said third set of orifices have a diameter in the range of about 1 mils to about 10 mils.

12. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 10, wherein said third set of orifices have a diameter in the range of about 3 mils to about 7 mils.

13. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 10 to 12, wherein said fluid supplied to said third set of orifices has a pressure in the range of about 500 psig to about 3000 psig.

14. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 10 to 13, wherein said fluid emitted from said third set of orifices has a pressure in the range of about 800 psig to about 1500 psig.

15. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 14, wherein said micro-holes have an average EHD of about 1 mil to about 7 mils.

16. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 14, wherein said micro-holes have an average EHD of about 2 mils to about 5 mils.

17. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 16, wherein said large sized holes have an average EHD of about 7 mils to about 30 mils.

18. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 17, wherein the fluid from the first set of orifices is directed against the upper surface of said starting film prior to directing the fluid from the second set of orifices.

19. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 18, wherein said micro-holes are defined by fibrils.

20. A method of forming an apertured film from a stretchable thermoplastic polymeric material in accordance with any one of claims 1 to 19, wherein said large sized holes are defined by fibrils.

21. A method for forming an apertured film from a stretchable thermoplastic polymeric material comprising:
a) providing a starting film comprising said stretchable thermoplastic polymeric material and having an upper surface and a lower surface;

b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces, and means for allowing said applied fluid to be transported away from said backing member, c) a supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member;

d) forming irregular large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a first set of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices in said first set having a diameter greater than or equal to ten mils and the fluid supplied thereto causing said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions; forming irregular size micro-holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a second set of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices in said second set having a diameter less than or equal to ten mils and the fluid emitted therefrom causing said starting film to rupture into a multiplicity of said micro-holes in said starting film between said localized support regions, said micro-holes being defined by fibrils of said thermoplastic material;

e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

22. A method for forming an apertured film from a stretchable thermoplastic polymeric material comprising:

a) providing an embossed starting film comprising said stretchable thermoplastic polymeric material having an upper surface and a lower surface;

b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces; and means for allowing said applied fluid to be transported away from said backing member;

c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member;

d) forming irregular size micro-holes and large sized holes in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from at least two sets of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, the orifices of the first set having a diameter greater than ten mils and the fluid supplied thereto having a pressure less than 500 psig. to cause said starting film to rupture into a multiplicity of said large sized holes in said starting film between said localized support regions, the orifices of the second set having a diameter less than or equal to ten mils and the fluid supplied thereto having a pressure of at least 500 psig., to cause said starting film to rupture into a multiplicity of said micro-holes in said starting film between said localized support regions;

e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

23. A method of forming an apertured film in accordance with claim 22, including providing said embossed starting film with corona discharge treatment on one side thereof.

24. A method of forming an apertured film in accordance with claim 22 or 23, including applying a surface active agent to one side of said apertured film.

25. An apertured film formed from a starting film of stretchable thermoplastic polymeric material, and having a given thickness dimension comprising: a plurality of apertures extending through the thickness dimension of said film, said plurality of apertures including first and second groups of apertures, and the apertures of said first group having a size greater than the size of the apertures in said second group, the apertures of said first and second groups being defined by fibrils formed from said thermoplastic polymeric material, said first and second groups of apertures having been produced by the process of subjecting unsupported portions of the polymeric material to columnar streams of pressurized fluid directed at said material in a zone of contact to cause the material to stretch between localized support regions over recessed zones wherein the first group of apertures comprises irregular holes formed by the columnar streams from a first set of orifices and wherein the second group of apertures comprises irregular holes formed by the columnar streams from a second set of smaller orifices, said material adjacent each said aperture having been thinned relative to the portions of said material which have not been thinned, said thinned material having irregular curving portions formed free of contact with said localized support regions.

26. An apertured film in accordance with claim 25, wherein said fibrils have an average length in the range of about 0.005 inch to about 0.05 inch.

27. An apertured film in accordance with claim 25 or 26, wherein said fibrils have an average width in the range of about 0.001 inch to about 0.035 inch.

28. An apertured film in accordance with any one of claims 25 to 27, wherein said fibrils have an average thickness in the range of about 0.00025 inch to about 0.002 inch.

29. An apertured film in accordance with any one of claims 25 to 28, wherein said first group of apertures comprise large sized holes having an average EHD of about 7 mils to about 30 mils.

30. An apertured film in accordance with any one of claims 25 to 28, wherein said first group of apertures comprise large sized holes having an average EHD of about 7 mils to about 20 mils.

31 An apertured film in accordance with any one of claims 25 to 30, wherein said second group of apertures comprise micro-holes having an average EHD of about 1 mil to about 7 mils.

32. An apertured film in accordance with any one of claims 25 to 30, wherein said second group of apertures comprise micro-holes having an average EHD of about 2 mils to about 5 mils.

33. An apertured film in accordance with any one of claims 25 to 32, wherein said starting film has a thickness in the range of about 0.3 mils to about 3.0 mils.

34. An apertured film in accordance with any one of claims 25 to 33, wherein said apertured film has an overall thickness dimension greater than the given thickness dimension of said starting film.

35. An apertured film in accordance with claim 34, wherein said overall thickness dimension of said thermoplastic polymeric material is in the range of about 5 mils to about 40 mils.

36. An absorbent product comprising: an absorbent core having oppositely facing major surfaces, and an apertured film covering at least one of said major surfaces, said apertured film having an outwardly facing body contacting side and an opposite side facing inwardly toward said core, said apertured film being formed from a starting film of stretchable thermoplastic polymeric material, and having a given thickness dimension, said apertured film having a plurality of apertures extending through the thickness dimension of said film, said plurality of apertures including first and second groups of apertures, and the apertures of said first group having a size greater than the size of the apertures in said second group, the apertures of said first and second groups being defined by fibrils formed from said thermoplastic polymeric material, said first and second groups of apertures having been produced by the process of subjecting unsupported portions of the polymeric material to columnar streams of pressurized fluid directed at said material in a zone of contact to cause the material to stretch between localized support regions over recessed zones wherein the first group of apertures comprises irregular holes formed by the columnar streams from a first set of orifices and wherein the second group of apertures comprises irregular holes formed by the columnar streams from a second set of smaller orifices, said material adjacent each said aperture having been thinned relative to the portions of said material which have not been thinned, said thinned material having irregular curving portions formed free of contact with said localized support regions.

37. An absorbent product in accordance with claim 36, wherein said fibrils have a length in the range of about 0.005 inch to about 0.05 inch.

38. An absorbent product in accordance with claim 36 or 37, wherein said fibrils have a width in the range of about 0.001 inch to about 0.035 inch.

39. An absorbent product in accordance with any one of claims 36 to 38, wherein said fibrils have a thickness in the range of about 0.00025 inch to 0.002 inch.

40. An absorbent product in accordance with any one of claims 36 to 39, wherein said first group of apertures comprise large sized holes having an average EHD of about 7 mils to about 30 mils.

41. An absorbent product in accordance with any one of claims 36 to 39, wherein said first group of apertures comprise large sized holes having an average EHD of about 7 mils to about 20 mils.

42. An absorbent product in accordance with any one of claims 36 to 41, wherein said second group of apertures comprise micro-holes having an average EHD of about 1 mil to about 7 mils.

43. An absorbent product in accordance with any one of claims 36 to 41, wherein said second group of apertures comprise micro-holes having an average EHD of about 2 mils to about 5 mils.

44. An absorbent product in accordance with any one of claims 36 to 43, wherein said apertured film has an overall thickness dimension greater than the given thickness dimension of said starting film.

45. An absorbent product in accordance with any one of claims 36 to 44, wherein the apertured film is in direct contact with said at least one major surface of said absorbent core.

46. A method for forming an apertured film from a stretchable thermoplastic polymeric material comprising:

a) providing a starting film comprising said stretchable thermoplastic polymeric material and having an upper surface and a lower surface;

b) providing a backing member comprising localized support regions for supporting said starting film, recessed zones into which the film may be deformed by the application thereto of fluid forces, and means for allowing said applied fluid to be transported away from said backing member;

c) supporting said starting film on said backing member with portions of the lower surface of said film being in contact with the support regions of said backing member and with the upper surface of said film facing away from said backing member;

d) forming irregular size holes having an average EHD of about 7 to 30 mils in said starting film by directing a fluid in the form of substantially non-diverging, columnar streams from a first set of orifices against the upper surface of said starting film in a zone of contact to cause said starting film to stretch between said backing member localized support regions over said recessed zones, said orifices having a diameter greater than or equal to ten mils and the fluid supplied thereto causing said starting film to rupture into a multiplicity of said holes in said starting film between said localized support regions;

e) moving said film from said contact zone; and f) removing said now-apertured film from said backing member.

47. A method for forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 46, wherein said large sized holes have an average EHD in the range of about 7 mils to about 20 mils.

48. A method for forming an apertured film from a stretchable thermoplastic polymeric material in accordance with claim 46 or 47, wherein the pressure of said fluid supplied to said orifices is in the range of about 100 to about 500 psig.