CA2396494A1 - Amine organoborane complex polymerization initiators and polymerizable compositions - Google Patents

Amine organoborane complex polymerization initiators and polymerizable compositions Download PDF

Info

Publication number
CA2396494A1
CA2396494A1 CA002396494A CA2396494A CA2396494A1 CA 2396494 A1 CA2396494 A1 CA 2396494A1 CA 002396494 A CA002396494 A CA 002396494A CA 2396494 A CA2396494 A CA 2396494A CA 2396494 A1 CA2396494 A1 CA 2396494A1
Authority
CA
Canada
Prior art keywords
amine
complex
organoborane
composition
polymerization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA002396494A
Other languages
French (fr)
Inventor
Mark F. Sonnenschein
Steven P. Webb
Nelson G. Rondan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CA2396494A1 publication Critical patent/CA2396494A1/en
Abandoned legal-status Critical Current

Abstract

The invention is an amine-organoborane complex wherein the organoborane is a trialkyl borane and the amine is an amine having an amidine structural component; an aliphatic heterocycle having at least one nitrogen in the heterocyclic ring wherein the heterocyclic compound may also contain one or more nitrogen atoms, oxygen atoms, sulfur atoms, or double bonds in the heterocycle; a primary amine which in addition has one or more hydrogen bond accepting group wherein there is at least two carbon atoms, preferably three , between the primary amine and the hydrogen bond accepting group, such that d ue to inter- or intramolecular interactions within the complex the strength of the B-N bond is increased; or a conjugated imine. Preferred hydrogen bond accepting groups include the following: a secondary amine, a tertiary amine, an ether, a halogen, a polyether group or a polyamine group. The complexes o f the invention are used in polymerizable compositions, adhesive compositions and coatings compositions containing compounds having moieties which polymerise under free radical polymerization conditions.

Description

AMINE ORGANOBORANE COMPLEX POLYMERIZATION INITIATORS AND
POLYMERIZABLE COMPOSITIONS
This invention relates to organoborane amine complexes that are useful as free radical polymerization initiators. In another embodiment, this invention relates to polymerizable compositions comprising compounds containing moieties capable of free radical polymerization and organoborane amine complex initiators of the invention. In yet another embodiment the invention relates to adhesive, sealant, coating and ink compositions containing organoborane amine complexes and compounds containing moieties capable of free radical polymerization.
In many practical situations in which compounds are subjected to polymerization or where adhesives are used, it is desirable to have polymerizable compositions and adhesive compositions which can cure on demand. Cure on demand means that the polymerization can be initiated when desired. A significant problem with cure on demand compositions is the stability of the compositions. Many such compositions will begin curing at, or near, ambient temperature or will partially cure at ambient temperature resulting in an increased viscosity causing difficulties in handling and reduced functionality of the polymerizable composition or adhesive composition.
Low surface energy olefins such as polyethylene, polypropylene and polytetrafluroethylene have a variety of attractive properties in a variety of uses, such as for toys, automobile parts and furniture applications. Because of the low surface energy of these plastic materials, it is very difficult to find adhesive compositions which bond to these materials. The commercially available adhesives which are used for these plastics require time consuming or extensive pretreatment of the surface before the adhesive will bond to the surface. Such pretreatments include corona treatment and flame treatment.
The requirement for extensive pretreatment of the surface results in significant limitations to the designers of automobile components, toys and furniture. What is needed is adhesive compositions which are capable of bonding to low surface energy substrates, and bonding low surface energy substrates to other substrates, without the need for extensive or costly pretreatment.
Mottus et al., US Patent 3,275,611 discloses a process for polymerizing olefinic compounds with a catalyst comprising an organoborane compound, a peroxygen compound and an amine. It is disclosed that the organoborane compound and amine may be added to the reaction mixture separately or as a preformed complex, and that the complex is preferred. The presence of the amine in the complex reduces the pyrophoricity of the organoborane in air. Among the amine complexing agents disclosed are pyridine, aniline, toluidine, dimethylbenzylamine, and nicotine. Many of the complexes disclosed in Mottus are pyrophoric at all amine to boron atom ratios. In addition, many of the amine complexes do not display significant adhesive properties when applied to low surface energy substrates.
A series of patents issued to Skoultchi (US Patent Nos. 5,106,928, 5,143,884, 5,286,821, 5,310,835 and 5,376,746) disclose a two-part initiator system that is reportedly useful in acrylic adhesive compositions. The first part of the two-part system includes a stable organoborane-amine complex and the second part includes a destabilizer or activator such as an organic acid or an aldehyde. The organoborane compound of the complex has three ligands which can be selected from Cl_,o alkyl groups or phenyl groups.
Useful amines disclosed include octylamine, 1,6 diaminohexane, diethylamine, dibutylamine, diethylenetriamine, dipropylenediamine, 1,3 propylene diamine, and 1,2 propylene diamine.
The adhesive compositions are disclosed to be useful in structural and semi-structural adhesive applications, such as speaker magnets, metal to metal bonding, automotive glass to metal bonding, glass to glass bonding, circuit board component bonding, bonding select plastics to metal, glass to wood, etc. and for electric motor magnets.
Zharov et al. discloses in a series of US Patents (US 5,539,070; US
5,690,780; and US 5,691,065) polymerizable acrylic compositions which are particularly useful as adhesives wherein organoborane amine complexes are used to initiate cure. The organoboranes used have three ligands attached to the borane atom which are selected from C,_,o alkyl groups and phenyl. The amine is an alkanol amine or a diamine where the first amine group can be a primary or secondary amine and the second amine is a primary amine.
It is disclosed that these complexes are good for initiating polymerization of an adhesive which bonds to low surface energy substrates.
Pocius in a series of patents (US 5,616,796; US 5,6211,43; US 5,681,910; US
5,686,544; US 5,718,977; and US 5,795,657) disclose amine organoborane complexes with a variety of amines such as polyoxyalkylene polyamines and polyamines which are the reaction product of diprimary amines and compound having at least two groups which react with a primary amine.
Many of the complexes disclosed in the Zharov, Skoultchi and Pocius Patents are not stable in compositions containing olefinic unsaturation at, or near, ambient temperatures and thus the complexes disassociate and induce polymerization at, or near, ambient temperature with time. This instability at, or near, ambient temperature can result in polymerization before desired and can result in compositions which are unsuitable for the desired use.
Therefore, there is a need for initiator systems for free radical polymerization which are safe to handle, not pyrophoric, which can be used to form cure on demand polymer systems or can be used in adhesive systems which cure on demand. What is further needed are adhesive systems which are capable of bonding to low surface energy substrates, and initiator systems which facilitate such bonding. In addition to such needs, the complexes need to be thermally stable, that is do not disassociate at, or near, ambient temperatures and thereby initiate polymerization before desired. What are further needed are polymer compositions and adhesive systems which are thermally stable at, or near, ambient temperatures and which will undergo polymerization when the user desires.
In one embodiment the invention is an amine organoborane complex wherein the organoborane is a trialkyl borane and the amine is selected from the group of amines having an amidine structural component; aliphatic heterocycles having at least one nitrogen in the heterocyclic ring wherein the heterocyclic compound may also contain one or more nitrogen atoms, oxygen atoms, sulfur atoms, or double bonds in the heterocycle; primary amines which in addition have one or more hydrogen bond accepting groups wherein there are at least two carbon atoms, preferably at least three carbon atoms, between the primary amine and the hydrogen bond accepting group, such that due to inter- or intramolecular interactions within the complex the strength of the B-N bond is increased; and conjugated imines. Preferred hydrogen bond accepting groups include the following:
primary amines, secondary amines, tertiary amines, ethers, halogens, polyethers or polyamines.
Heterocycle as used herein refers to a compound having one or more aliphatic cyclic rings of which one of the rings contains nitrogen. The amidines or conjugated imines can be straight or branched chain or cyclic.
In another embodiment the invention comprises a polymerizable composition which comprises an amine organoborane complex of the invention and one or more of monomers, oligomers or polymers having olefinic unsaturation which are capable of polymerization by free radical polymerization. This composition can undergo polymerization by exposing the composition to temperatures at which the organoborane amine complex undergoes disassociation. In another embodiment the invention is a polymerizable composition which further comprises an effective amount of a compound which causes the complex to disassociate (decomplexing agent), thereby freeing the borane to initiate polymerization of the one or more monomers, oligomers or polymers having olefinic unsaturation. The compound which causes disassociation of the complex is kept separate from the complex until initiation of polymerization is desired. In yet another embodiment the invention is a method of polymerization comprising a contacting of the components of the polymerizable compositions under conditions that the one or more monomers, oligomers or polymers undergo polymerization. The polymerizable composition which contains the decomplexing agent can be cured at any desired temperature, such as at, or near, ambient temperature and below ambient temperature.
The polymerizable compositions of the invention can be used as adhesive, sealant, coating or ink compositions. In one embodiment two or more substrates are bonded together by contacting the components of the adhesive composition of the invention, including the decomplexing agent, together under conditions such that polymerization is initiated; contacting the adhesive composition with the two or more substrates; positioning the two or more substrates such that the adhesive composition is located between the two or more substrates wherein they are in contact with one another; and allowing the adhesive to cure so as to bond the two or more substrates together. The thermally curing compositions of the invention can be used to bond two or more substrates together by contacting the adhesive composition with the substrates such that the adhesive composition is located between the two or more substrates and exposing the adhesive composition to a temperature at which the complex disassociates and initiating the free radical polymerization of the monomer, oligomers, polymers or a mixture thereof.
The complexes of the invention are safe to handle, not pyrophoric, are stable at, or near, ambient temperature and therefore will not initiate polymerization at, or near, ambient temperature in the absence of an initiator that causes the complex to disassociate.
The polymeric compositions of the invention are stable at, or near, ambient temperature and can be cured upon demand by contacting the complex with the compounds which cause disassociation of the complex, or alternatively by heating the polymeric compositions above the thermal disassociation temperature of the complex. Furthermore, the adhesive, sealant, coating and ink compositions of the invention can form good bonds to low surface energy substrates without the need for primers or surface treatment.
The organoborane used in the complex is a trialkyl borane or an alkyl cycloalkyl borane. Preferably such borane corresponds to Formula 1:
B-~ R2 ~ 3 Formula 1 wherein B represents Boron; and RZ is separately in each occurrence a C,_,o alkyl, C3_,o cycloalkyl , or two or more of RZ may combine to form a cycloaliphatic ring.
Preferably RZ
is C,~ alkyl, even more preferably CZ~ alkyl, and most preferably C3~ alkyl.
Among preferred organoboranes are tri-ethyl borane, tri-isopropyl borane and tri-n-butylborane. To prepare thermally stable polymerizable compositions, thermally stable complexes which do not disassociate, at or near, ambient temperature are needed. The key to preparation of such complexes, is the selection of the amine. The desirability of the use of a given amine in an amine/organoborane complex can be calculated from the energy difference between the Lewis acid-base complex and the sum of energies of the isolated Lewis acid (organoborane) and base (amine) known as binding energy. The higher the binding energy the more stable the complex.
Binding Energy =
-(Complex Energy - (Energy of Lewis Acid + Energy of Lewis base)) Such binding energies can be calculated using theoretical ab-initio methods such as the Hartree Fock method and the 3-21G basis set. These computational methods are available commercially employing commercial software and hardware such as SPARTAN
and GAUSSIAN 98 programs with a Silicon Graphics workstation. Amines having amine/organoborane binding energies of ten kilocalories per mol or greater are preferred, amines having a binding energy of 15 kilocalories per mol or greater are more preferred and even more preferred are amines with a binding 20 kilocalories per mol or greater. In the embodiment where polymerization of the compositions of the invention is initiated by use of a decomplexing agent the binding energy of the amine to the organoborane is preferably about 50 kcal/mole or less and most preferably about 30 kcal/mole or less. In the embodiment where polymerization of the compositions of the invention is initiated by use of heat the binding energy of the amine is preferably about 100 kcal/mole or less, more preferably about 80 kcal/mole or less and most preferably about 50 kcal/mole or less.
In one embodiment, the amine comprises a compound having a primary amine and one or more hydrogen bond accepting groups, wherein there are at least two carbon atoms, preferably at least about three, between the primary amine and hydrogen bond accepting groups. Hydrogen bond accepting group means herein a functional group that through either inter- or intramolecular interaction with a hydrogen of the borane-complexing amine increases the electron density of the nitrogen of the amine group complexing with the borane. Preferred hydrogen bond accepting groups include primary amines, secondary amines, tertiary amines, ethers, halogen, polyethers, and polyamines. In a preferred embodiment, the amine corresponds to Formula 2:
NH2 CCH2~C ~R 1~2~X Formula 2 wherein:
Rl is separately in each occurrence hydrogen or a Cl_,o alkyl or C3_,o cycloalkyl;
X is hydrogen bond accepting moiety; a is an integer of 1 to 10; and b is separately in each occurrence an integer of 0 to 1, and the sum of a and b is from 2 to 10.
Preferably R' is hydrogen or methyl. Preferably X is separately in each occurrence a hydrogen accepting moiety with the proviso that when the hydrogen accepting, moiety is an amine it is a tertiary or a secondary amine. More preferably X is separately in each occurrence -N(R8)e, -OR'°, or a halogen wherein R8 is separately in each occurrence Cl_,o alkyl, C3_,o cycloalkyl or -(C(R')z)a-W; R'° is separately in each occurrence, Cl_,o alkyl, Cs-~o cYcloalkyl, or -(C(R')z)a-W; and a is 0, 1, or 2. More preferably X is -N(R$)z or -OR'°.
Preferably, R8 and R'° are Cl~ alkyl or --(C(R')z)a-W, more preferably C,_4 alkyl and most preferably methyl. W is separately in each occurrence hydrogen or C,_lo alkyl or X and more preferably hydrogen or C,~ alkyl. Preferably, a is about 1 or greater and more preferably 2 or greater. Preferably a is about 6 or less, and most preferably about 4 or less.
Preferably, b is about 1. Preferably, the sum of a and b is an integer about 2 or greater and most preferably about 3 or greater. Preferably the sum of a and b are about 6 or less and more preferably about 4 or less. Preferably d is separately in each occurrence an integer of 1 to 4, more preferably 2 to 4, and most preferably 2 to 3. Among preferred amines corresponding to Formula 2 are dimethylaminopropyl amine, methoxypropyl amine, dimethylaminoethylamine, dimethylaminobutylamine, methoxybutyl amine, methoxyethyl amine, ethoxypropylamine, propoxypropylamine, amine terminated polyalkylene ethers (such as trimethylolpropane tris(poly(propyleneglycol), amine terminated)ether), aminopropylmorpholine, isophoronediamine, and aminopropylpropanediamine.
In one embodiment the preferred amine complex corresponds to Formula 3:

Formula 3 R2~B ~ NH2 CCH2~C ~R 1>2-~-wherein Rl, RZ, X, a and b are as defined hereinbefore.
In another embodiment the amine is an aliphatic heterocycle having at least one nitrogen in the heterocycle. The heterocyclic compound may also contain one or more of nitrogen, oxygen, sulfur or double bonds. In addition, the heterocycle may comprise multiple rings wherein at least one of the rings has a nitrogen in the ring.
Preferably the aliphatic heterocylic amine corresponds to Formula 4:

wherein:
X
y Formula 4 3\
JX
R3 is separately in each occurrence hydrogen, a C,_,o alkyl or C3_,o cycloalkyl;
Z is separately in each occurrence oxygen or NR4 wherein R4 is hydrogen, Cl_lo alkyl, or C 6_ ,o aryl or alkaryl;
x is separately in each occurrence an integer of 1 to 10, with the proviso that the total of all occurrences of x should be from 2 to 10; and y is separately in each occurrence 0 or 1.
Preferably, R3 is separately in each occurrence hydrogen or methyl. Preferably Z is NR4.
Preferably, R4 is hydrogen or C,~ alkyl, and more preferably hydrogen or methyl.
Preferably x is from 1 to 5 and the total of all the occurrences of x is 3 to 5. Preferred compounds corresponding to Formula 4 include morpholine, piperidine, pyrolidine, piperazine, 1,3,3 trimethyl 6-azabicyclo[3,2,1] octane, thiazolidine, homopiperazine, aziridine, 1,4-diazabicylo[2.2.2]octane (DABCO), 1-amino-4-methylpiperazine, and 3--g_ pyrroline. Complexes using aliphatic heterocyclic amines preferably correspond to Formula 5:
3\
JX
C R2~~- y Formula 5 3\
JX
wherein R2, R3, Z, x and y are as defined hereinbefore.
In yet another embodiment, the amine which is complexed with the organoborane is an amidine. Any compound with amidine structure wherein the amidine has sufficient binding energy as described hereinbefore with the organoborane, may be used.
Preferable amidine compounds correspond to Formula 6:
6 ~1 R~ ~~Rs ~ 2 C Formula 6 N~
R~
wherein:
R5, R6, and R' are separately in each occurrence hydrogen, a C,_,o alkyl or C3_,o cycloalkyl;
two or more of R5, R6, and R' may combine in any combination to form a ring structure, which may have one or more rings. Preferably R5, R6 and R' are separately in each occurrence hydrogen, C,~ alkyl or CS_6 cycloalkyl. Most preferably R' is H or methyl. In the embodiment where two or more of R5, R6 and R' combine to form a ring structure the ring structure is preferably a single or a double ring structure. Among preferred amidines are 1,8 diazabicyclo[5,4]undec-7-ene; tetrahydropyrimidine; 2-methyl-2-imidazoline; and 1,1,3,3-tetramethylguanidine.

The organoborane amidine complexes preferably correspond to Formula 7:

R~ /NCRs J z C Formula 7 R2~-B ~ N\
R~
wherein Rz, R5, R6 and R' are as defined earlier.
In yet another embodiment, the amine which is complexed with the organoborane is a conjugated imine. Any compound with a conjugated imine structure, wherein the imine has sufficient binding energy as described hereinbefore with the organoborane, may be used. The conjugated imine can be a straight or branched chain imine or a cylic imine. Preferable imine compounds correspond to Formula 8:
Formula 8 NR~ CR9 ~CR9 CR9 ~c wherein Y is independently in each occurrence hydrogen, N(R4)z, OR4, C(O)OR4, halogen or an alkylene group which forms a cyclic ring with an R' or R9. R4 is hydrogen, C,_,o alkyl, or C 6-,o aryl or alkaryl. Preferably R4 is hydrogen or methyl. R' is as described previously. R9 is independently in each occurrence hydrogen, Y, C,_~o alkyl, C3_,o cycloalkyl-, (C(R9)z-(CR9=CR9)~-Y or two or more of R9 can combine to form a ring structure provided the ring structure is conjugated with respect to the double bond of the imine nitrogen;
and c is an integer of from 1 to 10. Preferably, R9 is hydrogen or methyl.
Y is preferably N(R4)z, or OR4, or an alkylene group which forms a cyclic ring with R' or R9. Y is more preferably N(R4)z or an alkylene group which forms a cyclic ring with R' or R9. Preferably, c is an integer of from 1 to 5, and most preferably about 1.
Among preferred conjugated imines useful in this invention are 4-dimethylaminopyridine; 2,3-bis(dimethylamino)cyclopropeneimine; 3-(dimethylamine)acroleinimine; 3-(dimethylamino)methacroleinimine.

Among preferred cyclic imines are those corresponding to the following structures N
v R9 R9 R9 ~9 R9 N
~R9 The complexes with the conjugated imines preferably correspond to Formula 9:
C R2~B~--NR~ CR9 ~ CR9 CR9 ~ ~ Formula 9 wherein R2, R',R9, c and Y are as defined hereinbefore.
The molar ratio of amine compound to borane compound in the complex is relatively important. In some complexes if the molar ratio of amine compound to organoborane compound is too low, the complex is pyrophoric. Preferably the molar ratio of amine compound to organoborane compound is from 1.0:1.0 to 3.0:1Ø Below the ratio of about 1.0:1.0 there may be problems with polymerization, stability of the complex and for adhesive uses, adhesion. Greater than about a 3.0:1.0 ratio may be used although there is no A-H ~8EALERB R&0 248 3~~~~ ~ 12/12/01 1 :51PM; j .,~
x s b0043 s beneSt from using a ratio greaxcr than about 3.0:1,0, If too much amine is present, this rnay negatively impact the stability of the adhesive or polymer compositions.
Preferably the t molar ratio of~amine compound to organoborane aompouad is from 2.0:1.0 to 1.0:1Ø
Polymerizable compounds which niay be used in the polymerization compositions of the invention include any monomers, oligotners, polymers or mixtures thertof vsrhich contain olefxnic unsaturation which can polymerlxe by free radical 1 .
polymerizadoa. Such compounds are well known to those skilled in the art.
Mottos, US.
Patent Number 3,275,611, provides a description of such compounds at column 2, line 46 to ooluma 4, lint; 16 [, incorporated herein by referenoel. Among preferred classes of .. .. -10; odmpounds containing olefinic unsaturation are monomers, oligomers, polymers sari mixtures thereof derived from the aaylates and methacrylates; olefnically unsaturated hydrocarbons; for example ethylene, propylene, butylene, isobut3~lene,1-octene, l-dodecene, l-tieptadecene, l-eicoxene; vinyl compounds such as styrene, vinyl pyridine, 5-methyl-2 vinylpyridine, vinyl napthylene, alpha methylstyreae; vinyl and vinylidicne 13 halides; acrylonitrilc and rnethacrylonittile; vinyl acetate and vinyl propionate; vinyl oacyethanol; vinyl trimethylacetate; vinyl hexonate; vinyl laurate; vinyl chloroaoetate; vinyl stearate; methyl vinyl ketoae; vinyl isobutyl ether; vinyl ethyl ether;
compounds tlXat have a plurality of ethylenic bonds such as those having conjugated double bonds such as ;e butadiene, 2,ohlorobutadiene, isoprene. Examples of preferable acrylatcs and methacrylates 20 are disclosed in Skoultchi, US Patent Number 5,286,821 at column 3, lines 50 to column 6, line 12, jinvorpouted herein by reference] and Pocius, tJS Pate~ot Number 5,681,910. at column 9, line 28 to column 12, lice 25 [, incorporated herein by reference].
More preferred ole~nic compounds comprise methyl acrylate, methylmethacrylate, butylaiethacrylate, tert-butylmethacrylate, 2-ethylhexyacxylate, Z-ethylhexylmethacrylate, ethylacrylate, 25 ~ isobornylmctliacrylate, isobornylaerylate, hydroxyethylmethacrylate, glycidylmethacryiate, tetrallydrofurfuryl methacrylate, acrylamide, n-metDylacrylamide, and other similar acrylate cozitaining monomers. Also useful are the class of acrylate ripped polyurethane prepolymers available com~merciaily from several sources, and prepared by reacting an isoeyanate reactive aeryha~te monomer, oligo~oner or polymer, such as a hydroxy acrylate, with an 30 isocyanate functional prepolymer.
. -13-12=1 ~-x(30 rm~f,~e~,o'~+ f~ no, vo~e~ x A-H SEALERS R8D 24B 39' ~,~~; ' ~ 12/ 12101 1 : 51 PM, J ~ y . t .' rn the embodiment where the composition is used as an adhesive, acrylate and/or methacrylate based compounds era preferably used. The most preferred aerylate and methacrylate compounds include methylmethacrylate, butylmethacxylate, 2-ethylhexylmethacxylate, isobornylmethacrylate, Getrahydrofurfuryl methacsylate, and cyclohexylmethyLacthacrylate.
In some embodiments the polymerizable compositions of the invention may further comprise an effective amount of a compound that is reactive with an amine so as to liberate the organoboranc so as to initiate polymerisation (a decomplcxing agent). The amine reactivx compound liberates arganoborane by reacting with the amine,.thereby _ .. .
10~ removing the orgatioborane from chemical attachment with the amine.
Desirable amine reactive compounds are chase materials that can reality form reaction products with amines at or below and more preferably at room temperature about ZO°C to 22°G so as to provide a t composition that can be generally easily used and cured under ambient conditions. General classes of such compounds include acids, aldehydes, isocyanates, acid chlorides, sulphonyl 15 chlorides, matures thereof. Preferred amine reactive compounds are acids.
Both $ronstead and L~ewis acids may be used. Pocius,.~US Patent Number 5,718,977 describes the preferred acid compounds at column 9, line 1 to 15 ~inaorparated herein by reference).
The most preferred acids are acrylic acid and methacrylic acid.
Preferably the amount of polymerizable corapounds in the polymerizable 20~ compositions or adhesive is about 20 percent by weight or greater based on the weight of the total composition, more preferably about 30 percent by weight or greater and most .
preferably about 40 percent by weight or greater. Preferably the amount of polymerizable compounds is about 95 percent by weight or less, preferably about 90 percent by v~reight or less and most preferably about 85 percent by weight or less. The amount of complex used 25~ in the composition can be anyamount sufficient to initiate polymerization once the complex has disassociated at the desired speed of polymerisation. At higher concentration of organoborane; the speed of polymerization is higher. Preferably the amount of organoborane complex is abput D.2 percent by weight or greater based cu the weight of the total composition, preferably about 1.0 percent by weight or greater and most preferably about Z
30 percent by weight or Breater. Preferably the amount of orgaaoborane complex present is about 8 percent by weight or less based on the total weight of composition, preferably about ~.~u .:
CA 02396494 2002-06-14 '~''~1.~.'~~ ~~,, Fm~fanRS~a'it 17.~Q~. 19:42 6 percent by weight or less and most preferably about 4 percent by weight or less. In those embodiments where a decomplexing agent is used, the amount of decomplexing agent (initiator) is that amount which is sufficient to initiate disassociation of the organoborane-amine complex thereby causing the organoborane to initiate polymerization of the olefinically unsaturated compound. Preferably the amount of decomplexing agent is about 1 percent by weight or greater based on the weight of the total composition, more preferably about 1.5 percent by weight or greater and most preferably about 2 percent by weight or greater. Preferably the amount of decomplexing agent is about 8 percent by weight or less based on the weight of the total composition, more preferably about 6 percent by weight or less and most preferably about 4 percent by weight or less.
The organoborane amine complex may be readily prepared using known techniques. Typically, the amine is combined with the organoborane in an inert atmosphere with slow stirring. An exotherm is often observed and cooling of the mixture is, therefore, recommended. If the ingredients have a high vapor pressure, it is desirable to keep the reaction temperature below about 70°C to 80°C. Once the materials are well mixed the complex is permitted to cool to room temperature. No special storage conditions are required although it is preferred that the complex be kept in a capped vessel under an inert atmosphere, in a cool, dark location. Advantageously, the complexes of the invention can be prepared in the absence of organic solvents that would later have to be removed, although they could be prepared in solvent, if so desired. Solvents used in the preparation of the complexes should, preferably, be ones that do not coordinate the amine, preferable solvents are for example, tetrahydrofuran or diethylether, or low molecular weight alkanes such as hexane or heptane.
The invention are air stable. By "air stable" it is meant that when the complexes are stored in a capped vessel at room temperature (about 20°C
to 22°C) and under otherwise ambient conditions (that is, not under a vacuum and not in an inert atmosphere), the complexes remain useful as polymerization initiators for at least about two weeks, although the complexes may be readily stored under these conditions for many months.

By "air stable" it is also meant that the complexes are not pyrophoric. (When a few drops of the complex are placed on a paper towel under ambient conditions, the paper towel does not ignite, char or smoke.) The air stability of the complex is enhanced when the complex is a crystalline material. However, the complexes of the invention are air stable for at least six months even when they are liquids. Liquid complexes are easier to handle and mix than are crystalline complexes.
The polymerizable compositions of the invention can be either one or two-part compositions depending upon the mechanism used to initiate polymerizations. In one embodiment the compositions are two-part compositions in which one-part contains the complexes of the invention and the other part contains the decomplexing agent (initiator).
Polymerization is initiated by contacting the two-parts of the composition. An advantage of this process is that polymerization can be initiated at, or even below, ambient temperatures.
In this embodiment heat may be applied to the polymerizable composition to speed up initiation or polymerization. In another embodiment the polymerization composition may be initiated by heating the composition. In this embodiment no decomplexing agent (initiator) is needed. When polymerization is initiated by heating the composition can be either a one-part or a two-part composition. The primary reason to use a two-part composition is to keep apart components of the composition which may be unstable in the presence of one another. Generally a one-part composition is preferred in this embodiment as the delivery equipment is less complex and costly and the need to properly ratio the components is eliminated.
In the embodiment where heat is used to initiate the cure of the composition, the composition is exposed to a heat source which heats the composition to a temperature at or above the temperature at which the complex used in the composition decomposes to release the organoborane which then initiates free radical polymerization.
Generally the composition is heated to a temperature which is less than the temperature at which the polymer formed undergoes degradation. The temperature at which the complex undergoes disassociation is related to the binding energy of the complex. At higher binding energies of the complex higher temperatures are required to initiate polymerization. In the embodiment where the polymerization is initiated thermally the temperature at which the composition is heated to initiate polymerization is dictated by the binding energy of the complex.

Generally the temperature used to initiate the polymerization by decomplexing the complex is about 30°C or greater and preferably about 50°C or greater.
Preferably the temperature at which thermally initiated polymerization is initiated is about 120°C or less and more preferably about 100°C or less. Any heat source which heats the composition to the desired temperature can be used provided the heat source does not negatively impact the components of the composition or its function. In this manner the composition may be contacted with the substrates either before or after the composition is exposed to heat. If the composition is heated prior to contact with the substrates, the composition should be contacted with the substrates before the composition has polymerized to the point at which the composition is no longer able to adhere to the substrates, this is usually the upper limit on the open time as defined hereinafter. It may be necessary in the thermally initiated reaction to control the oxygen content such that there is adequate oxygen to create favorable conditions for radical formation but not so much as to inhibit the polymerization.
The two-part polymerizable compositions or adhesive compositions of the invention are uniquely suited for use with conventional, commercially available dispensing equipment for two-part adhesives. Once the two-parts have been combined, the composition should be used quickly, as the useful pot life (or open time) may be short depending upon the monomer mix, the amount of complex, and the temperature at which the bonding is to be performed. The adhesive composition is applied to one or both substrates and then the substrates are joined together with pressure to force excess composition out of the bond line. This also has the advantage of displacing composition that has been exposed to air and that may have begun to react. In general, the bonds should be made shortly after the composition has been applied, preferably within about 10 minutes.
The typical bond line thickness is about 0.005 inches (0.13 mm) to about 0.03 inches (0.76 mm). The bonding process can easily be carried out at room temperature and to improve the degree of polymerization it is desirable to keep the temperature below about 40°C, preferably below about 30°C, and most preferably below about 25°C.
The bonds will cure to a reasonable green strength to permit handling of the bonded components within about 2 to 3 hours. Full strength will be reached in about 24 hours under ambient conditions; post-curing with heat (typically about 80°C) may be used if desired.

When bonding fluoroplastics, it is advantageous to cool the initiator containing part of the two-part composition to 0°C to 5°C before adding the organoborane amine complex. The bond should be made as soon after the composition has been applied as practical; performing the bonding operation at less than about room temperature is also helpful.
The compositions may further comprise a variety of optional additives. One particularly useful additive is a thickener such as medium to high (10,000 to 1,000,000) molecular weight polymethyl methacrylate which may be incorporated in an amount of 10 to 60 weight percent, based on the total weight of the composition. Thickeners may be employed to increase the viscosity of the composition to facilitate application of. the composition.
Another particularly useful additive is an elastomeric material. The materials can improve the fracture toughness of compositions made therewith which can be beneficial when, for example, bonding stiff, high yield strength materials such as metal substrates that do not mechanically absorb energy as easily as other materials, such as flexible polymeric substrates. Such additives can be incorporated in an amount of 5 percent to 35 percent by weight, based on the total weight of the composition. Useful elastomeric modifiers include chlorinated or chlorosulphonated polyethylenes such as HYPALON 30 (commercially available from E. I. Dupont de Nemours & Co., Wilmington, Delaware) and block copolymers of styrene and conjugated dimes (commercially available from Dexco Polymers under the Trademark VECTOR, and Firestone under the Trademark STEREON). Also useful, and even more preferred, are certain graft copolymer resins such as particles that comprise rubber or rubber-like cores or networks that are surrounded by relatively hard shells, these materials often being referred to as "core-shell" polymers. Most preferred are the acrylonitrile-butadiene-styrene graft copolymers available from Rohm and Haas. In addition to improving the fracture toughness of the composition, core-shell polymers can also impart enhanced spreading and flow properties to the uncured composition.
These enhanced properties may be manifested by a reduced tendency for the composition to leave an undesirable "string" upon dispensing from a syringe-type applicator, or sag or slump after having been applied to a vertical surface. Use of more than about 20 percent of a core shell polymer additive is desirable for achieving improved sag-slump resistance. Generally the amount of toughening polymer used is that amount which gives the desired toughness to the polymer or the adhesive prepared.
Another useful adjuvant is a cross-linking agent. Cross-linking agents can be used to enhance the solvent resistance of the adhesive bond or polymer composition, although certain compositions of the invention have good solvent resistance even in the absence of externally added cross-linking agents. Typically employed in an amount of 0.2 to 10 weight percent based on the total weight of the compositions, useful cross-linkers include the various diacrylates referred to above as possible acrylic modifying monomers as well as other materials. Particular examples of suitable cross-linking agents include ethylene glycol dimethacrylate, ethylene glycol diacrylate, triethyleneglycol dimethacrylate, diethylene glycol bismethacryloxy carbonate, polyethylene glycol diacrylate, tetraethylene glycol dimethacrylate, diglycerol diacrylate, diethylene glycol dimethacrylate, pentaerythritol triacrylate, trimethylolpropane triglycidyl ether, trimethylolpropane tris(2-methyl-1-aziridinepropionate, trimethylolpropane trimethacrylate, acrylate tipped polyurethane containing prepolymers, polyether diacrylates and dirnethacrylates.
Peroxides may be optionally included (typically in an amount of about 2 percent by weight or less, based on the total weight of the composition), for example, to adjust the speed at which the compositions polymerize or to complete the polymerization.
Small amounts of inhibitors such as hydroquinone may be used, for example, to prevent or reduce degradation of the olefinic monomers during storage.
Inhibitors may be added in an amount that does not materially reduce the rate of polymerization or the ultimate properties of an adhesive or other composition made therewith, typically 10 to 10,000 ppm based on the weight of the polymerizable monomers.
Other possible additives include non-reactive colorants, fillers (for example, carbon black), etc.
The various optional additives are employed in an amount that does not significantly adversely affect the polymerization process or the desired properties of compositions made therewith.

Polymerizable compositions according to the invention may be used in wide variety of ways, including as sealants, coatings, primers, to modify the surface of polymers, and injection molding resins. They may also be used as matrix resins in conjunction with glass and metal fiber mats such as in resin transfer molding operations. They may further be used as encapsulants and potting compounds such as in the manufacture of electrical components, printed circuit boards. Quite desirably, they provide polymerizable adhesive compositions that can bond a diverse myriad of substrates, including polymers, wood, ceramics, concrete, glass and primed metals. Another desirable related application is their use in promoting adhesion of paints to low surface energy substrates such as polyethylene, polypropylene, polyethyleneterephthalate and polytetrafluoroethylene, and their co-polymers. In this embodiment the composition is coated onto the surface of the substrate to modify the surface to enhance the adhesion of the final coating to the surface of the substrate.
The compositions of the invention can be used in coating applications. In such applications the composition may further comprise a carrier such as water or a solvent.
The coating may further contain additives well known to those skilled in the art for use coatings such as pigments to color the coating, inhibitors and UV stabilizers.
The compositions may also be applied as powder coatings and may contain the additives well known to those skilled in the art for use in powder coatings.
The compositions of the invention can also be used to modify the surface of a polymeric molded part, extruded film or contoured object. Compositions of the invention can also be used to change the functionality of a polymer particle by surface grafting of polymer chains on to the unmodified plastic substrate.
Alternatively, the complexes of the present invention can be dissolved in a variety of solvents including water or organic solvents that provide a non acid containing environment and used as a primer. In this manner the complex containing solution is applied to the surface that is to be used for adhesion, surface modification, or polymerization, and the solvent allowed to dry. The polymerizable monomer is then brought into contact with the complex on the surface and allowed to react for the purpose of promoting adhesion, or surface modification, or for initiating radical polymerization.

Polymerizable compositions of the invention are especially useful for adhesively bonding low surface energy plastic or polymeric substrates that historically have been very difficult to bond without using complicated surface preparation techniques, priming, etc. By low surface energy substrates is meant materials that have a surface energy of about 45 mJ/m2 or less, more preferably about 40 mJ/m2 or less and most preferably about 35 mJ/mz or less. Included among such materials are polyethylene, polypropylene, acrylonitrile-butadiene-styrene, polyamides, syndiotactic polystyrene, olefin containing block co-polymers, and fluorinated polymers such as polytetrafluoroethlene (TEFLON) which has a surface energy of less than about 20 mJ/m2. (The expression "surface energy"
is often used synonymously with "critical wetting tension" by others.) Other polymers of somewhat higher surface energy that may be usefully bonded with. the compositions of the invention include polycarbonate, polymethylmethacrylate, and polyvinylchloride.
The polymerizable compositions of the invention can be easily used as two-part adhesive. The components of the polymerizable compositions are blended as would normally be done when working with such materials. The decomplexing agent is usually included in this blend so as to separate it from the organoborane amine complex, thus providing one-part of the two-part composition. The organoborane amine complex of the polymerization initiator system provides the second part of the composition and is added to the first part shortly before it is desired to use the composition. The complex may be added to the first part directly or it may be pre-dissolved in an appropriate carrier such as methyl methacrylate.
It may be desirable to store the complexes apart from the monomers, oligomers or polymers to inhibit premature polymerization of the monomers, oligomers or polymers. The complexes of this invention have greatly enhanced stability when in the presence of monomers and in the absence of a decomplexing agent, such as an acid, and thus can be stored with the polymerizable components of the composition.
Complexes in which the complexing amine nitrogen atom to boron atom ratio is greater than 1:1 may be sufficiently stable that they can be blended with polymerizable components in useful proportions. However, in such situations, the presence of additional non-polymerizing reactants (for example, the organoborane liberator) may result in other, undesirable affects.

l f~ ~i~ A-H SEALERS R&D 248 39~'~~u 12/12101 1 :52PM, j "

For a two-part adhesive such as those of the invention to be most easily used in commercial and industrial environments, the ratio at which the two-parts are combinod should be a cotjvenient whole number. This facilitates application of the adhesive with conventional, ~comtnercially available dispensers. Such dispensers are shown in US Patent ~ Nos. 4,538,920 and 5,082,147 j(incorporated herein by reference}] and are available from Conprotec, lnc. (Salem New 3ersey) under the trade name MIK~'AC. Typically, these dispensers use a pair of tubular receptacles arranged side-by-side with eacb tuba being intended to receive one of the two-parts of the adhesive. Two plungers, one for each tuba are simultaneously advanced (for example, manually or by a hand=actuated ratchetixtg 10v mechanism) to evacuate the contents of the tubes into a common, hollow;
elongated mixing cbatrtber that inay also contain a static nnixer to facilitate blending of the two-parts. The blended adhesive is extruded from the mixing chamber onto a substrate. Once the tubes bave been emptied, Lhey can be replaced with fresh tubes and the application process continued.
x5~ : The ratfo at which the twa-parts of the adhesive era combined is cont:olled by the diaraetsr of the tubes. (each plunger is sized to be reosivcd within a tube of fixed diameter, aad'the plungers are advanced into the lobos at the same speed.) A
sirtglo dispenser is often intended for use with a variety of different two-part adhesives and the plungers axe syzed to deliver the two-parts of the adhesive at a convenient mix ratio. Some 20 ~ common mix ratios are 1:1> 2:1, 4:1 and 10:1.
The part of the adhesive or polymerizable compositions of the invention which coptain the amine-organoborane complex preferably displays thermal stability at, or above, room temperature. Thermal stability as used herein menus the amine organoboranc complex does,not disassociate and initiate polymerization of the olefinic unsaturated 25 ~ compounds present in the composition. Thermal stability can be measured by determining the temperature at which the viscosity of the composition begins to increase.
Preferably the temperature al which the viscosity of the composition increases is greater than about 40°C, more preferably greater than about 60°C and most preferably greater than about 80°C. The increase in viscosity indicates that the amine borane complex is disassociated and ' 30' polymerization has been initiated. In the embodiment wherein the composition is used as an ,~ .
adhesive, the adhesive preferably demonstrates a lap shear strength of about 100 psi (6$9 ' -22-CA 02396494 2002-06-14 . , '~''~w~~ ~~~
Fmofanac~a{it l7.llao. 1q:4~ X:.

kPa) or greater, more preferably about 250 psi (1724 kPa) or greater and more preferably about 400 psi (2758 kPa) or greater according to the following test procedure.
The adhesive components are mixed and applied to one or both substrates (1 in x 4 in x 1/8 in (25.4 mm x 101.6 mm x 3.2 mm) polypropylene coupons).
Adhesive thickness is controlled by the addition of a few weight percent of glass beads between 0.005 to 0.030 inches in diameter (0.13 mm to 0.76 mm). The coupons are mated to provide 0.5 inch squared (161 mm2) to 1.0 inch squared (645 mm2) substrate overlap in a lap-shear testing configuration. The samples are held in place with metal binder clips to provide constant force and facilitate the elimination of air bubbles in the adhesive.
The bonded samples were usually cured for at least about 24 hours before being mounted in a tensile testing apparatus fitted with a sample oven. The samples are evaluated at crosshead speeds of 0.05 (0.13 mm) and 0.5 (12.7 mm) inches per minute for room temperature and 110°C
testing conditions, respectively. Maximum load (pounds) to break are recorded and maximum stress (psi) is calculated by dividing this load by the overlap area (inches squared).
Preferably the open time of the adhesive is about 3 minutes or greater, more preferably about 5 minutes or greater, and most preferably about 8 minutes or greater.
Preferably the open time of the adhesive is about 30 minutes or less, more preferably about minutes or less, and most preferably about 20 minutes or less. Open time as used herein 20 is the time between initiation of polymerization and the time at which the adhesive can no longer be applied and used as an adhesive. If the open time is too long, poor bond strength is observed. If the open time is too short, the composition polymerizes before a link up with the substrate can be achieved.
Preferably the polymeric compositions of the invention have a suitable 25 viscosity to allow application. Preferably the compositions have the viscosity of about 100 centipoise or greater, more preferable about 1,000 centipoise or greater and most about 20,000 centipoise or greater. Preferably the adhesive compositions have a viscosity of about 150,000 centipoise or less, more preferably about 100,000 centipoise or less and most preferably about 50,000 centipoise or less.

The following examples are included for illustrative purposes only and are not intended to limit the scope of the claims. Unless otherwise stated all parts and percentages are by weight.
Preparation Of The Organoborane/Amine Complex 50 cc of a 1M solution of organoborane, for example, tributyl borane (TBB) in ether solution (Aldrich), was added to a weighed round bottom flask. The solution was purged with nitrogen. A weighed amount of the amine, for example, pyrrolidine (4.97 g, 1:1.4 molar ratio of boron to amine), was added in small portions to the organoborane solution, maintaining the temperature below 40°C with an external ice bath. The amine was added to make a molar ratio of organoborane to amine of between 1:1 to a 1:3.
The solution was stirred for about 30 minutes and then the solvent was removed on a rotary evaporator at less than 40°C. The weight of the flask and complex were periodically compared to the theoretical weight to assure that the solvent was completely removed. The complex was tested for pyrophoric reactivity by placing a drop on a paper towel and looking for charring of the towel. Some pyrophoric complexes can be made less or non-pyrophoric by adding additional amine (lowering the organoborane:amine molar ratio).
Preparation of Adhesive Compositions Two component (part) adhesives were produced as described below. One component included the organoborane/amine complex (hardener) mixed with an acrylic resin, described below, and an antioxidant. The other component was the acrylic resin with an initiator, for example, acrylic acid, that decomplexes the boron/amine complex when mixed into the other component. The acrylic resin was a mixture of 250 g methylmethacrylate (MMA) and 80 g polymethylmethacrylate (PMMA, 350 K Mw). The MMA and PMMA were stirred or rotated overnight to mix the PMMA into the MMA.
The resulting acrylic resin has a viscosity of about 25,000 centipoise (cP).
The first component (Part I) comprised 135 g acrylic resin, 6.6 g of a hardener, and 82.5 mg BHT. The second component comprised 135 g acrylic resin, 6.6 g acrylic acid (AA), 13.5 g fillers (glass beads, polypropylene ground flakes, etc.) (<10 percent), and 13.5 g tougheners (Stereon 840A block copolymer) (<10 percent)).
The two components of the adhesive composition were formulated to allow for a ratio of 1:1, 1:4, or 1:10 mixture of hardener:initiator, preferably 1:1.
The adhesive may be mixed in the desired ratio in air, in a bag, or through a pressurized gun. The adhesive was applied to a polypropylene test strip 1 inch (25.4 mm) wide with a 1/z inch (12.7 mm) overlap and was tested for adhesive strength as described previously.
Thermal stability testing was performed according to the procedures provided below. The auto-initiation temperature was determined from the point at which the viscosity started to rise, indicating the onset of polymerization of the borane:amine containing resin without initiator. Onset occurred due to thermal destabilization of the boron/amine complex. Viscosity was measured continuously by a Brookfield viscometer (rotating cylinder at 50 rpm) as a function of a constant temperature ramp (about 1°C/min).
The temperature at which the viscosity began to increase was noted and listed as the take off temperature.
In another method the time it took for the viscosity to reach 100 kcPs at ambient temperature (or elevated temperature) was determined by periodic measurement of the viscosity of a hardener and resin over a period of days. This was considered to be the useful lifetime of the resin.
Several complexes were prepared and tested in the composition as described herein. Table 1 contained the results of the testing.
The following abbreviations were used in Table 1.
TBB is tri-n-butyl borane.
DMAPA is dimethylaminopropylamine.
TiBB is triisobutylborane.
DEBM is diethylmethoxyborane.
DEBI is diethylisopropoxy borane.

TOB is tri-n-octylborane.
> means the substrate broke during measurement Y means that paper ignited or charred when contacted with the borane:amine.
N means that paper did not ignite, char, smoke, or discolor when contacted by borane:amine.
S1 means that the paper showed slight evolution of smoke or discoloration, but not charring when contacted with borane:amine.

Table 1 Example BoraneAmine Molar Pyro- Take-offLap Shear B:AminephoricTemp (on PP) (C) psi 1 TBB Hexane diamine 1:1 N 44 >444 2 TBB DMAPA 1:1.1 N 52 >900 3 TBB DMAPA 1:1.2 N 53 >655 4 TiBB DMAPA 1:1.25 N 39 >604 TBB DMAPA 1:0.6 N 47 >929 6 TBB Tetramethyl propane1:3 Y 46 192 diamine 7 TPB DMAPA 1:1.1 N >100 0 8 TBB Aminopropyl 1:1.1 N 50 >682 morpholine 9 TBB Cyclohexylamine 1:1.2 s1 20 >933 TBB Aminopropanol 1:1.2 N 20 >624 11 TBB Morpholine 1:1.2 Y 20 >818 12 TBB Ethanolamine 1:1.17 N 42 458 13 TBB Piperidine 1:1.5 N 52 >783 14 TBB Pyrrolidine 1:1.4 N >100 679 DEBM DMAPA 1:1.25 N 68 36 16 DEBI DMAPA 1:1.25 N 77 64 17 TBB Isophorone diamine1:1.36 N 46 >422 >893 18 TBB Methoxypropyl 1:1.36 N 63 >640 amine 19 TBB a-Methyl Benzylamine1:1.6 s1 25 451 TOB DMAPA 1:1.3 N >100 471 Table 1 Continued 21 TBB Aminopropyl propane1:1.2 N 64 >559 diamine 22 TBB Aminoethoxy ethanol1:1.3 N 25 >847 23 TOB Methoxypropyl 1:1.3 N 68 110 amine 24 TOB Aminopropanol 1:1.3 N 53 79 25 TBB Morpholine 1:3 N 42 >878 26 TBB Aminopropanol 1:2 N 60 >419 27 TOB Isophorone diamine1:1.3 N >100 0 28 TBB Diisopropyl amine1:2 Y SO 0 29 TBB Cyclohexylamine 1:2 N 30 508 30 TBB Piperidine 1:2 N 85 >775 31 TBB Aminoethoxy ethanol1:2 N 50 276 32 TBB Pyrrolidine 1:1.4 N >100 >709 33 TiBB Pyrrolidine 1:1.4 N >100 303 34 TBB Piperazine 1:1.3 N 20 >749 35 TBB Methyl pyrrolidinone1:2 Y 20 0 36 TBB Tetrahydro- thiophene1:1.3 N 20 0 37 TBB Diethanol amine 1:2 Y 65 61 38 TBB Triethyl amine 1:2 Y 52 0 39 TBB Dibutylamine 1:1.3 N 50 39 40 TBB Dipropylamine 1:1.3 Y 52 0 41 TBB Dioctylamine 1:1.3 N 58 192 42 TBB Cyclopentyl amine1:1.3 Y 25 >790 43 TBB Cyclopentyl amine1:2 N 25 >940 44 TiBB Isophorone diamine1:1.3 N 25 300 45 TOB Methoxypropyl 1:1.3 N 50/83 amine 46 TBB 1,3,3 trimethyl 1:1.3 N 25/>100>426 6-aza bicyclo [3,2,1]
octane WO 01/44311 PCT/~JS00/33806 Table 1 Continued 47 TBB Dabco 1:1.3 s1 25 >774 48 TBB Diamino maleonitrile1:1.3 Y NA

49 TBB Thiazolidine 1:1.3 Y 25 >725 50 TBB Thiazolidine 1:2 N 25 186 51 TBB Urea 1:1.3 Y NA

52 TBB 1,8 Diaza bicyclo(5,4J1:1.3 N >100 >555 undec-7-ene 53 TBB 4-Dimethylamino 1:3 N 57 >581 pyridine 54 TBB Proline methyl 1:1.3 N 0 ester 55 TBB 4-Bromo piperidine1:1.3 Y 0 56 TBB Acetaldehyde Ammonia1:1.3 s1 67 0 Trimer 57 TBB 1-Amino-4-Methyl 1:1.3 N 25 145 Piperazine 58 TBB Homopiperazine 1:1.3 N 25 638 59 TBB 2-Dimethyl- 1:3 s1 25 0 aminopyridine 60 TBB Pyridine 1:3 N 25 61 TBB Tetraaza adamantine1:2 Y 0 62 TBB Hexylamine 1:1.3 N 45 >885 63 TBB Tetramethylguanidine1:1.3 N 74 >616 64 TBB Tetrahydropyrimidine1:1.3 N 75 >736 65 TBB 2-Methyl2-imidizole1:1.3 N 35 >1000 66 TBB 3-Pyrroline 1:1.3 N 25 247 Table 1 Continued 67 TBB Trimethylolpropane1:1.3 N 42 >620 tris[poly(propylene-glycol), amine terminated]ether (avg mwt=432) 68 TBB Trimethylolpropane1:1.3 Y <25 0 tris (2-methyl-1-aziridinepropionate Binding Energies of Complexes The organoborane/amine binding energies of several of the complexes were calculated using previously described computational methods. Comparison of results of amine/organoborane combinations listed in Table 1 with calculated binding energies in Table 2 revealed that binding energies less than about 10 kcal/mole were pyrophoric, and a high binding energy was correlated with higher thermal performance.
Furthermore the calculated binding energy was correlated with the temperature at which the alkylborane-amine complex spontaneously disassociated. The disassociation temperature was easily determined by the so called "take-off ' temperature provided in Table 1 at which time the polymerization proceeded in the absence of a de-complexing agent. The disassociation temperature may also be determined by differential scanning calorimetry. When applying differential scanning calorimetry, a sample of the complex was placed in a pan and the temperature of the pan was raised. At the same time a reference sample, usually an empty pan, was heated at the exact same rate and the difference in temperature between the sample and the reference was monitored and recorded using a differential amplifier.
When reaction of the complex was observed an exotherm can be observed implying a release of heat due to insertion of oxygen into the alkyl-boron bond. No exotherm was observed when this experiment was performed under strictly inert conditions.

Table 2 Example Lewis Amine Binding Energy Acid (kcal/mole) 2 TBB DMAPA cyclic 20.4 2 TBB DMAPA linear 15.9 25 TBB morpholine 12.8 32 TBB pyrrolidine 15.4 17 TBB isophorone diamine cis 15.1 17 TBB isophorone diamine trans 15.3 18 TBB methoxypropylamine cyclic 20.1 18 TBB methoxypropylamine, linear 15.4 21 TBB aminopropylpropanediamine 18.3 38 TBB triethylamine 0.0 47 TBB Dabco 10.2 53 TBB 4-dimethylaminopyridine 16.2 60 TBB pyridine 8.7 TBB dimethylaminoethylamine 18.8 TBB dimethylaminobutylamine 21.9 TBB propylamine 15.8 Table 2 Continued TBB acetamidine 19.2 TBB guanidine 21.0 TBB cyclopropeneimine 17.0 TBB tetramethyldiaminocyclopropene23 imine TBB 3-N-methyl-3,4,5,6- 16.4 tetrahydropyrimidine TBB pyrazole 10.2 ' TBB 3-aminopyrazole 13.1 I

TBB aziridine 18.0 TBB methylaziridine 14.9 TBB azetidine 17.9 TBB methylazetidine 12.2 TBB formaldimine 13.2 TBB benzaldimine 11.5 TBB 3,4,5,6-tetrahydropyridine 12.2 TBB 5,6-dihydropyridine 13.1 TBB cyclohexanone imine 12.8 TBB 2-aminopropanol 15.8 TBB 1,4-dihydropyrrole 15.0 WO 01/44311 PCT/i1S00/33806 Table 2 Continued TBB N-Methyl Tetrahydropyrimidine 16.4 TBB 1-azabutadiene 13.8 TBB 4-N,N-dimethylamino-1-azabutadiene 19.5 ~B 4-Methoxy-1-azabutadiene 16.2 Tgg 4-Chloro-1-azabutadiene 11.0 Tgg 1-Azahexatriene 15.0 Among other compounds for which the binding energy is calculated, are those illustrated below with their calculated binding energies adjacent.
N
11.3 N
17.9 NMe2 Me0 N
9.76 N 15.01 \ Me H

Claims (10)

WHAT IS CLAIMED IS:
1. An organoborane/amine complex wherein the organoborane is a trialkyl borane or an alkyl cycloalkyl borane and the amine is selected from the group of amines having aliphatic heterocycles having at least one nitrogen in the heterocyclic ring wherein the heterocyclic compound may also contain one or more nitrogen atoms, oxygen atoms, sulfur atoms, or double bonds in the heterocycle; primary amines which have one or more hydrogen bond accepting groups wherein there is an alkylene chain of at least two carbon atoms between the primary amine and the hydrogen bond accepting group and the hydrogen accepting group is a polyether or halogen; and straight or branched chain or cycloaliphatic conjugated imines wherein the cycloaliphatic conjugated imine has only one nitrogen atom;
isophorone diamine or aminopropyl morpholine.
2 A complex according to Claim 1 wherein the complex of the organoborane and the primary amine corresponds to the formula the organoborane heterocylic amine complex corresponds to the formula and the organoborane conjugated imine complex corresponds to the formula wherein B is boron;
R1 is separately in each occurrence hydrogen, a C1-10 alkyl or C3-10 cycloalkyl;
R2 is separately in each occurrence a C1-10 alkyl, C3-10 cycloalkyl or two or more of R2 may combine to form a cycloaliphatic ring structure;
R3 is separately in each occurrence hydrogen, a C1-10 alkyl or C3-10 cycloalkyl;
R4 is separately in each occurrence hydrogen, C1-10 alkyl, C3-10 cycloalkyl, C6-10 aryl or alkaryl;
R7 is separately in each occurrence hydrogen, C1-10alkyl, C3-10cycloalkyl, or two or more of R7 combine to form a ring structure which can be a single ring or a multiple ring structure and the ring structure can include one or more of nitrogen, oxygen or unsaturation in the ring structure;
R9 is independently in each occurrence hydrogen, C1-10 alkyl or C3-10cycloalkyl, Y, -(C(R9)2-(CR9=CR9)e- Y or two or more of R9 can combine to form a ring structure, or one or more of R9 can form a ring structure with Y provided the ring structure is conjugated with respect to the double bond of the imine nitrogen;
X is a polyether or halogen;
Y is independently in each occurrence hydrogen, N(R4)2, OR4, C(O)OR4, a halogen or an alkylene group which forms a cyclic ring with R7 or R9;
Z is separately in each occurrence oxygen or NR4;
a is separately in each occurrence an integer of from 1 to 10;
b is separately in each occurrence 0 or 1; with the proviso that the sum of a and b should be from 2 to 10;
c is separately in each occurrence an integer of from 1 to 10;
x is separately in each occurrence an integer of 1 to 10, with the proviso that the total of all occurrences of x is from 2 to 10; and y is separately in each occurrence 0 or 1.
3. A complex according to Claim 2 comprising an aliphatic heterocylic amine wherein the amine is a five or six membered heterocylic compound.
4. A.polymerixable composition comprising a) an organoborane/amine complex wherein the organoborane is a trialkyborane or an alkyl cycloalkyl borane and the amine is selected from the group of amines having aliphatic heterocycles having at least one nitrogen in the heterocyclic ring wherein the heterocyclic compound may also contain one or more nitrogen atoms, oxygen atoms, sulfur atoms, or double bonds in the heterocycle; primary amines which have one or more hydrogen bond accepting groups wherein there is an alkylene chain of an alkylene chain of at least two carbon atoms between the primary amine and the hydrogen bond accepting group, and the hydrogen accepting groug is an ether, polyether or halogen;
conjugated imine; isophorone diamine or aminopropylmorpholine;
b) one or more of monomers, oligomers or polymers having olefinic unsaturation which is capable of polymerization by free radical polymerization; and c) an effective amount of a compound which causes the complex to disassociate freeing the borane to initiate polymerization of the one or more monomers, oligomers or polymers having olefinic unsaturation;
wherein the compound which causes disassociation of the complex is kept separate from the complex until initiation of polymerization is desired.
5. A polymerizable composition according to Claim 4 wherein the one of more monomers, oligomers, and polymers have acrylate or methacrylate functionality.
6. A polymerizable composition according to Claims 4 or 5 wherein the compound which causes disassociation of the complex is an acid, aldehyde, isocyanate, acid chloride, or sulphonyl chloride, or a mixture thereof.
7. A method of polymerization comprising a. contacting the components of the polymerizable composition of any one of Claims 4 to 6 under conditions such that the one of more monomers, oligomers, or polymers undergo polymerization.
8. A method of bonding two or more substrates together which comprises a. contacting the components of the composition of any one of Claims 4 to 6 together under conditions such that polymerization is initiated;

b. contacting the adhesive composition with the two or more substrates;

c. positioning the two or more substrates such that the adhesive composition is located between the two or more substrates wherein they are in contact with one another, and d. allowing the adhesive to cure so as to bind the two or more substrates together.
9. A method of modifying the surface of a low surface energy polymer by contacting a composition according to any one of Claims 4 to 6 with at least a portion of the surface of thelow surface energy polymer and causing the complex to disassociate thereby initiating polymerization of the monomer, oligomers, polymers or mixture thereof such that the polymer formed is on the surface of the low surface energy polymer.
10. A method of coating a substrate which comprises contacting the components of the composition according to any one of Claims 4 to 6;
contacting the contacted composition with one or more surfaces of a substrate; and curing the coating composition.
CA002396494A 1999-12-17 2000-12-14 Amine organoborane complex polymerization initiators and polymerizable compositions Abandoned CA2396494A1 (en)