CA2505594A1 - Reinforced wallboard - Google Patents

Reinforced wallboard Download PDF

Info

Publication number
CA2505594A1
CA2505594A1 CA 2505594 CA2505594A CA2505594A1 CA 2505594 A1 CA2505594 A1 CA 2505594A1 CA 2505594 CA2505594 CA 2505594 CA 2505594 A CA2505594 A CA 2505594A CA 2505594 A1 CA2505594 A1 CA 2505594A1
Authority
CA
Canada
Prior art keywords
wallboard
wallboard core
additive
core
cellulose ether
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA 2505594
Other languages
French (fr)
Other versions
CA2505594C (en
Inventor
Christopher D. Tagge
Jacob Freas Pollock
Lennard Torres
David S. Soane
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Placo SAS
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/351,675 external-priority patent/US6841232B2/en
Application filed by Individual filed Critical Individual
Publication of CA2505594A1 publication Critical patent/CA2505594A1/en
Application granted granted Critical
Publication of CA2505594C publication Critical patent/CA2505594C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A reinforced wallboard core is prepared from a slurry comprising a mixture of .beta.-calcium sulfate hemihydrate, a cellulose ether additive other than CMC
and an amount of water that is sufficient to form a slurry and resulting in a wallboard density of less than 0.8 g/cc. The .beta.-calcium sulfate hemihydrate is hydrated by the water forming a wallboard core reinforced by the cellulose ether additive. The cellulose ether, having a molecular weight of at least about 20,000 and a viscosity grade of at least about 100 cps, is selected to give the reinforced wallboard core improved nail pull resistance and greater flexural strength than unreinforced wallboard of the same density.
The reinforced wallboard core may be used for reduced-paper wallboard and/or for lightweight wallboard, for example.

Claims (55)

1. A reinforced wallboard core comprising:
water; and dry ingredients, wherein the dry ingredients comprise .beta.-calcium sulfate hemihydrate powder and a powdered additive and the dry ingredients are mixed together and mixed with the water, forming a slurry and hydrating the .beta.-calcium sulfate hemihydrate powder, wherein the powdered additive is of a cellulose ether other than CMC, and the cellulose ether is selected to have both a viscosity grade of at least about 100 cps and a molecular weight of at least about 20,000, when dried.
2. The wallboard core of claim 1, wherein the cellulose ether is a HPC, a HEC, a MC, a HPMC, a EHEC, a EHPC or a HEMC.
3. The wallboard core of claim 1, wherein the cellulose ether is a HPMC.
4. The wallboard core of claim 1, wherein the cellulose ether is a HEMC.
5. The wallboard core of claim 1, wherein the cellulose ether is a HEC.
6. The wallboard core of claim 1, wherein the wallboard core comprises substantially no clay.
7. The wallboard core of claim 4, wherein the wallboard core comprises substantially no clay.
8. The wallboard core of claim 1, wherein the cellulose ether is a MC.
9. The wallboard core of claim 8, wherein the MC is selected to have a viscosity grade of at least about 400 cps.
10. The wallboard core of claim 1, wherein the amount of water to dry ingredients is selected such that the average density of the wallboard core is less than 0.8 g/cc.
11. The wallboard core of claim 10, wherein the mixing causes dispersion of the powdered additive throughout the .beta.-calcium sulfate hemihydrate powder, whereby the powdered additive is evenly dispersed in the wallboard core.
12. The wallboard core of claim 10, wherein the density of the wallboard core is in a range from 0.45 g/cc to 0.7 g/cc.
13. The wallboard core of claim 1, wherein the percent weight of additive to the .beta.-calcium sulfate hemihydrate powder is at least 0.5 wt%.
14. The wallboard core of claim 13, wherein the additive is selected, and the amount of additive is selected, such that an addition of additive continuously increases the nail pull resistance of the wallboard core.
15. The wallboard core of claim 13, wherein the percent weight of additive to the .beta.-calcium sulfate hemihydrate powder is selected to be no greater than 3 wt%.
16. The wallboard core of claim 1, wherein the degree of substitution of the cellulose ether is less than 1.8.
17. The wallboard core of claim 1, wherein the additive is surface treated to delay dissolution.
18. A wallboard core comprising a .beta.-calcium sulfate hemihydrate powder and an aqueous additive solution, wherein the .beta.-calcium sulfate hemihydrate powder is mixed with the aqueous solution, forming a slurry and hydrating the .beta.-calcium sulfate hemihydrate powder, wherein the aqueous additive solution comprises water and an additive dissolved in the water and the additive is of a cellulose ether other than CMC, and the cellulose ether is selected to have both a viscosity grade of at least about 100 cps and a molecular weight of at least about 20,000, the amount of water being selected such that the wallboard core has a density less than 0.8 g/cc.
19. The wallboard core of claim 18, wherein the cellulose ether is a HEC, a MC, a HPMC, a EHEC, a EHPC or a HEMC, and the cellulose ether is selected to have a viscosity grade of at least about 400 cps.
20. The wallboard core of claim 18, wherein the cellulose ether. is a HPMC.
21. The wallboard core of claim 18, wherein the cellulose ether is a HEMC.
22. The wallboard core of claim 18, wherein the cellulose ether is a HEC.
23. The wallboard core of claim 18, wherein the wallboard has a density in a range from 0.4 g/cc to 0.7 g/cc.
24. The wallboard core of claim 18, wherein the wallboard comprises substantially no clay.
25. The wallboard core of claim 18, wherein the cellulose ether is a MC
having a viscosity grade of at least about 400 cps.
26. The wallboard core of claim 25, wherein the MC has a molecular weight of at least about 40,000.
27. The wallboard core of claim 25, wherein the amount of water is selected such that the wallboard core has a density less than 0.75 g/cc.
28. The wallboard core of claim 18, wherein the cellulose ether is selected to have a viscosity grade less than about 100,000 cps.
29. The wallboard core of claim 18, wherein the percent weight of additive to the .beta.-calcium sulfate hemihydrate powder is at least 0.5 wt%.
30. The wallboard core of claim 29, wherein the additive is selected, and the amount of additive is selected, such that an addition of additional additive continuously increases the nail pull resistance of the wallboard core.
31. The wallboard core of claim 29, wherein the percent weight of additive to the .beta.-calcium sulfate hemihydrate powder is selected to be no greater than 3 wt%.
32. The wallboard core of claim 31, wherein the additive is selected, and the amount of additive is selected, such that an addition of additional additive continuously increases the nail pull resistance of the wallboard core.
33. A wallboard comprising the wallboard core of claim 1 and at least one face sheet.
34. The wallboard of claim 33, wherein the at least one face sheet is paper.
35. The wallboard of claim 34, wherein the paper is fiber reinforced.
36. The wallboard of claim 33, wherein the at least one face sheet is a polymer layer.
37. The wallboard of claim 36, wherein the polymer layer is formed in situ.
38. The wallboard of claim 33, wherein the at least one face sheet is decorative.
39. A process for making a wallboard core comprising:
mixing together a .beta.-calcium sulfate hemihydrate powder and a powdered additive, until the powdered additive is dispersed throughout the .beta.-calcium sulfate hemihydrate powder, wherein the powdered additive is a cellulose ether other than CMC and the cellulose ether has a molecular weight of at least about 20,000 and a viscosity grade of at least about 200 cps;
adding the mixture of the .beta.-calcium sulfate hemihydrate powder and the powdered additive with an amount of water such that the resulting wallboard core has a density less than 0.8 g/cc;
forming a slurry by mixing the mixture of the .beta.-calcium sulfate hemihydrate powder and the powdered additive with the water;
extruding the slurry;
shaping the extrudate into an elongated sheet; and allowing the slurry to set, wherein at least a portion of the .beta.-calcium sulfate hemihydrate powder is hydrated.
40. The process of claim 39, wherein the steps of adding, forming and extruding are continuous.
41. A process for making a wallboard core comprising:
dissolving an additive in water to form an aqueous solution, wherein the additive is a cellulose ether other than CMC and the cellulose ether has a molecular weight of at least about 20,000 and a viscosity grade of at least about 200 cps;
adding an amount of dry ingredients to an amount of the aqueous solution such that the resulting wallboard has a density less than 0.8 g/cc, wherein the dry ingredients include a .beta.-calcium sulfate hemihydrate powder;
forming a slurry by mixing the mixture of the .beta.-calcium sulfate hemihydrate powder and the powdered additive with the water;
extruding the slurry;
shaping the extrudate into an elongated sheet; and allowing the slurry to set, wherein at least a portion of the .beta.-calcium sulfate hemihydrate powder is hydrated.
42. The process of claim 41, wherein the steps of adding, forming and extruding are continuous.
43. The wallboard core of claim 1, wherein the cellulose ether is selected to have both a viscosity grade of at least about 400 cps and a molecular weight of at least about 40,000.
44. The wallboard core of claim 43, wherein the percent weight of cellulose ether to .beta.-calcium sulfate hemihydrate is at least 0.5 wt%.
45. The wallboard core of claim 44, wherein the percent weight fraction of cellulose ether to .beta.-calcium sulfate hemihydrate is less than 3 wt%.
46. The wallboard of claim 33, wherein the at least one face sheet is a glass mat.
47. The wallboard of claim 33, wherein the density of the wallboard is in a range from 0.45 g/cc to 0.7 g/cc.
48. The wallboard core of claim 1, further comprising a fiber reinforcement, wherein the fiber reinforcement is mixed with the dry ingredients.
49. The wallboard core of claim 48, wherein the fiber reinforcement is a cellulose fiber.
50. The wallboard core of claim 48, wherein the fiber reinforcement is one of a glass fiber, a polymer fiber and a carbon fiber.
51. The wallboard core of claim 48, wherein the fiber reinforcement is one of a polyester fiber and a nylon fiber.
52. The wallboard core of claim 48, wherein the fiber reinforcement has an elongated axis and the elongated axis is oriented in the direction of extrusion.
53. The wallboard core of claim 1, wherein the surface of the wallboard core resists the development of mold, showing no signs of mold growth after 24 days of exposure to mold spores within an environment maintained at 90%
humidity and a temperature of 32 °C.
54. The wallboard of claim 33, wherein the surface of the wallboard resists the development of mold, showing no signs of mold growth after 24 days of exposure to mold spores within an environment maintained at 90% humidity and a temperature of 32 °C.
55. A reinforced wallboard core comprising:
water; and dry ingredients, wherein the dry ingredients comprise .beta.-calcium sulfate hemihydrate powder and a powdered additive and the dry ingredients are mixed together and mixed with the water, forming a slurry and hydrating the .beta.-calcium sulfate hemihydrate powder, wherein the powdered additive is of a methyl cellulose, having a degree of substitution in a range from 1.2 to 1.6, the average density of the wallboard core being less than 0.8 g/cc, when dried.
CA 2505594 2002-11-12 2003-10-21 Reinforced wallboard Expired - Lifetime CA2505594C (en)