CA2514101A1 - Structural reinforcement article and process for prepareation thereof - Google Patents
Structural reinforcement article and process for prepareation thereof Download PDFInfo
- Publication number
- CA2514101A1 CA2514101A1 CA002514101A CA2514101A CA2514101A1 CA 2514101 A1 CA2514101 A1 CA 2514101A1 CA 002514101 A CA002514101 A CA 002514101A CA 2514101 A CA2514101 A CA 2514101A CA 2514101 A1 CA2514101 A1 CA 2514101A1
- Authority
- CA
- Canada
- Prior art keywords
- article
- film
- expandable material
- mold
- expandable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The invention is a process for the preparation of article comprising placing a film (27) on each inner surface of each part of a two part mold (21, 22);
placing an article (26) in the mold (20) with film (27) located between the surface of the mold and the article (26) such that there is a sma space (29) between the article and the surface of the mold; closing the mold the article;
injecting between the film and the article an expandable plastic material (12) under conditions that the article (26) is coated with the expandable material (12) and the expandable material does not expand; removing the plastic article with the expandable material coated thereon with the two films attached to the expandable plastic material. In another embodiment the invention is an article comprising a shaped plastic article; an expandable material coated in the shaped plastic article; and a film covering the material coated shaped plastic article. In another embodiment the invention is a method of reinforcing a structural member which comprises inserting an article according to this invention into a cavity of the structural member and heating the structural member and the article to a temperature at which the expandable plastic material expands and the film or the expandable material bonds to the inner surface of the structural member so as to fix the location of the article in the structural member.
placing an article (26) in the mold (20) with film (27) located between the surface of the mold and the article (26) such that there is a sma space (29) between the article and the surface of the mold; closing the mold the article;
injecting between the film and the article an expandable plastic material (12) under conditions that the article (26) is coated with the expandable material (12) and the expandable material does not expand; removing the plastic article with the expandable material coated thereon with the two films attached to the expandable plastic material. In another embodiment the invention is an article comprising a shaped plastic article; an expandable material coated in the shaped plastic article; and a film covering the material coated shaped plastic article. In another embodiment the invention is a method of reinforcing a structural member which comprises inserting an article according to this invention into a cavity of the structural member and heating the structural member and the article to a temperature at which the expandable plastic material expands and the film or the expandable material bonds to the inner surface of the structural member so as to fix the location of the article in the structural member.
Description
STRUCTURAL REINFORCEMENT ARTICLE AND PROCESS FOR PREPARATION
THEREOF
This invention relates to an article coated with an expandable composition, such as a structural reinforcement article which is adapted to reinforce a stntctmal member, such as a structural member of an automobile, a house or my constntction which includes structural members designed to give structural integrity to the construction. In another embodiment the invention is a process for preparing an article coated with an expandable composition. In yet another embodiment the invention is a method of reinforcing a structural member using the structural reinforcement articles of the invention.
The automotive industry is under regulatory pressure to reduce average fuel consumption and improve he crashworthiness of vehicles. To improve fuel consumption lighter and thinner materials are being used. Unfortwzately, this reduces the structural integrity of parts of an automobile. To compensate automobile producers place structural reinforcing members into hollow structural members, such as A and B pillars of automobiles. Structural reinforcing members and their use in automobiles are described in Thum US
5,194,199; I~eller US Patent 6,146,565; Wycech US Patent 6,165,588; Hopton et al. US Patent 6,199,940; Barz US 6,131,897 and Sheldon et. al, US Patent Application 2002/0160130, all incorporated herein by reference. These structural reinforcing articles generally comprise some structural part, which gives the reinforcing articles shape and strength, which structural part is based on a light weight metal or a rigid plastic. The structural part is coated with an expandable composition, which expands when heated to a certain temperature. Typically the expandable composition expands to contact the imzer walls of the stuuctural member being supported.
Upon expansion, the expandable composition functions to hold the structural reinforcing member in place permanently by adhering to the imler wall of the stmctural member or by friction because the expanded composition is wedged tightly in position. The expanded composition also helps transfer a load from sheet metal to imler reinforcement to sheet metal.
The expandable composition is applied to the stntctural part of the structural reinforcing member by conventional means lmown m the art, such as hand applied sheets of epoxy, compression molding, resin transfer molding and injection molding. Some of the expandable materials exhibit adhesive properties at elevated temperatures.
This is desirable for affixing the expandable composition to the structural part of the structural reinforcing member.
The adhesive properties can cause problems in manufacturing of the stnictural reinforcing member because it can be difficult to remove the stmctural reinforcing member with the expandable materials deposited thereon from the mold. In order to pump the expandable material and apply it, it is necessary to heat the expandable material and the mold to facilitate application. Thereafter to prevent, or reduce adhesion to the mold, the mold is cooled prior to opening the mold. Even when cooled some of the expaizdable materials will still adhere to the mold, forcing an operator to manually remove some of the expandable material.
Heating the mold to application temperature and then cooling before attempting to remove the coated stnictural reinforcing member results in long processes, up to an hour per part per mold. In high vohune parts manufacture this results in the need for large amount of capital to keep up with the demand for the part. In addition to the long cycle times there are post process steps that may need to take place to make a tack free part including but not limited to dusting.of the surface of the expandable material with a material which renders the surface tack free such as glass balloons.
What is needed is a part that can be manufactured in an efficient manner with low part residence times in molds and little or no post molding processing steps. What is also needed is a process, which can produce expa~idable material coated articles, such as structural reinforcing members, in a cost efficient manner maximizing the productivity of tools used to manufacture the parts.
The invention is a process for the preparation of cuticle comprising placing a film on the top imler and bottom imzer half of a insert molding tool; placing an article in the mold with film located between the surface of the mold and the article;
closing the mold the article such that there is a small space between the article and the surface of the mold;
injecting between the film and the article an expandable material under conditions that the article is coated with the expaazdable material and the expandable material does not expand;
removing the plastic article with the expandable material coated thereon with the film attached to the expandable material. Preferably, when the article is placed in the mold, there is a small
THEREOF
This invention relates to an article coated with an expandable composition, such as a structural reinforcement article which is adapted to reinforce a stntctmal member, such as a structural member of an automobile, a house or my constntction which includes structural members designed to give structural integrity to the construction. In another embodiment the invention is a process for preparing an article coated with an expandable composition. In yet another embodiment the invention is a method of reinforcing a structural member using the structural reinforcement articles of the invention.
The automotive industry is under regulatory pressure to reduce average fuel consumption and improve he crashworthiness of vehicles. To improve fuel consumption lighter and thinner materials are being used. Unfortwzately, this reduces the structural integrity of parts of an automobile. To compensate automobile producers place structural reinforcing members into hollow structural members, such as A and B pillars of automobiles. Structural reinforcing members and their use in automobiles are described in Thum US
5,194,199; I~eller US Patent 6,146,565; Wycech US Patent 6,165,588; Hopton et al. US Patent 6,199,940; Barz US 6,131,897 and Sheldon et. al, US Patent Application 2002/0160130, all incorporated herein by reference. These structural reinforcing articles generally comprise some structural part, which gives the reinforcing articles shape and strength, which structural part is based on a light weight metal or a rigid plastic. The structural part is coated with an expandable composition, which expands when heated to a certain temperature. Typically the expandable composition expands to contact the imzer walls of the stuuctural member being supported.
Upon expansion, the expandable composition functions to hold the structural reinforcing member in place permanently by adhering to the imler wall of the stmctural member or by friction because the expanded composition is wedged tightly in position. The expanded composition also helps transfer a load from sheet metal to imler reinforcement to sheet metal.
The expandable composition is applied to the stntctural part of the structural reinforcing member by conventional means lmown m the art, such as hand applied sheets of epoxy, compression molding, resin transfer molding and injection molding. Some of the expandable materials exhibit adhesive properties at elevated temperatures.
This is desirable for affixing the expandable composition to the structural part of the structural reinforcing member.
The adhesive properties can cause problems in manufacturing of the stnictural reinforcing member because it can be difficult to remove the stmctural reinforcing member with the expandable materials deposited thereon from the mold. In order to pump the expandable material and apply it, it is necessary to heat the expandable material and the mold to facilitate application. Thereafter to prevent, or reduce adhesion to the mold, the mold is cooled prior to opening the mold. Even when cooled some of the expaizdable materials will still adhere to the mold, forcing an operator to manually remove some of the expandable material.
Heating the mold to application temperature and then cooling before attempting to remove the coated stnictural reinforcing member results in long processes, up to an hour per part per mold. In high vohune parts manufacture this results in the need for large amount of capital to keep up with the demand for the part. In addition to the long cycle times there are post process steps that may need to take place to make a tack free part including but not limited to dusting.of the surface of the expandable material with a material which renders the surface tack free such as glass balloons.
What is needed is a part that can be manufactured in an efficient manner with low part residence times in molds and little or no post molding processing steps. What is also needed is a process, which can produce expa~idable material coated articles, such as structural reinforcing members, in a cost efficient manner maximizing the productivity of tools used to manufacture the parts.
The invention is a process for the preparation of cuticle comprising placing a film on the top imler and bottom imzer half of a insert molding tool; placing an article in the mold with film located between the surface of the mold and the article;
closing the mold the article such that there is a small space between the article and the surface of the mold;
injecting between the film and the article an expandable material under conditions that the article is coated with the expaazdable material and the expandable material does not expand;
removing the plastic article with the expandable material coated thereon with the film attached to the expandable material. Preferably, when the article is placed in the mold, there is a small
2 space between the article and the surface of the mold; with the space between the article and the mold created from crush stand offs on the article and or the over molding tool.
In another embodiment the invention is an al-ticle comprising a shaped article; an expandable material coated in the shaped article; and a film covering the expandable material coated shaped article.
In another embodiment the invention is a method of reinforcing a structural member which comprises inserting an article according to.this invention into a cavity of the structural member and heating the structural member and the article to a temperature at which the expandable material expands and the film or the expandable material bonds to the inner surface of the stl-uctural member so as to permanently fix the article in the structural member.
The process of the invention allows the preparation of an article coated with an expandable material in an efficient manner allowing tools to cycle with a hold time of 5 minutes or less, and more preferably as low as 60 to 90 seconds per part.
In another embodiment the invention is a method of molding with a film in which the melting point of the film is lower than the temperature of the molding tool during molding operations. The film with the low melting point is placed on top of another film with a melting point above the molding temperature of the tool dluing molding operations. The film with the high melting point is referred to as the cal-rier film. The film with the low melting point is referred to as the leave-on film. This two film combination is placed on the top half and bottom half of the tool. The carrier film and leave-on film are placed into the tool together with the carrier film closest to the tool and the leave-on film closest to the open cavity portion of the tool. The two film combination can be placed into the tool as one piece, with the two film combination folded over with the insert in the middle of the film or the two film combination cari be placed in the tool as two separate film pieces. The carrier film allows the use of a leave-on film with a melting temperatlue lower then the temperature needed to process the expandable material. Preferably, the carrier film and the leave-on film are separated after removal from the mold. The removed carrier flllll call thereafter be discarded.
Figure 1 shows a cross-sectional view of a stmctu ral reinforcing member.
Figure 2 illustrates an apparatus used.to perform the process of the invention.
Figure 3 shows a cross-sectional view of a structural reinforcing member with a three layer fihn.
This invention relates to a process for efficiently applying an expandable material to a shaped article in an efficient malmer and to the article so prepared. Shaped article as used herein means any article which is formed into a shape near its' final use shape.
Generally, the article can be fabricated from any lmown.material, such as plastic, metal, ceramic, glass and the life. In applications where weight is a l~ey factor, such as where the shaped article is used in an automobile, lighter materials such as plastics are preferably used.
The plastic material may be nylon, styrenic, polyolefm, such as polyethylene or polypropylene, polycarbonate, polyester, polyurethane, polyepoxide, poyurea, polyphenylene sulfide, polyetherimide, toughened plastics such as ABS (acrylonitrile-butadiene-styrene) or previously mentioned materials containing elastomers such as styrene-all~adiene blocl~
copolymers, ethylene-octene copolymers and the life, and blends thereof, such as a polycarbonate-ABS
blends. The rigid plastic shaped articles can be solid or hollow with hollow shaped articles preferred for applications where weight is a critical factor. hl allotheT
elllbOdllllellt the Shaped article is foam. Foamed articles are preferably solid and provide lower density and higher strength. Preferably the shaped foamed articles are prepared from foam which can withstand the time and temperatures to which the expandable material must be exposed to expand.
Preferably, the foam is based on polystyrene, polyurethane, polyurea or epoxy resins; more preferably on polyurethanes, polytzreas, epoxy reS111S alld most preferably polyurethanes.. In a preferred embodiment the foam used is a foam described in the Allen, U.S.
6,423~755B1, incorporated herein by reference.
The shaped article can be used in any application where it is necessary to hold the article into place permanently in another structure. Such applications include in transpol-tation vehicles, such at automobiles, light tmclcs, heavy-duty trucl~s and busses, rail cars, aircraft; buildings, appliances and heavy machinery. Preferal?ly, the at-ticles of the invention are used to reinforce sti-nctural members. A structural member is a part of a structure, as described above, which supports or protects the structure. In this embodiment, the articles of the invention are structural reinforcing members, which means that they are used to structurally strengthen the structure and integrity of the structural member into which they are inserted.
Generally, the structural reinforcing members are inserted into hollow cavities of the structural member to improve the structural integrity of the structural member.
Preferably the structural reinforcing members are used in buildings or vehicles, preferably vehicles, such as automobiles and light trucl~s. The articles of the invention may further comprise a weans of locating and holding the article into a cavity until exposed to conditions such that the expandable material expands to hold the article in place. The means of locating and holding the article in place can be means which function to locate and/or hold the article in place prior to expansion of the expandable material. Such means include shaped standoffs or projections, tabs affixed to the part by mechanical affixing means (screws, nails, clips and the life), pressure sensitive adhesives, magnets and the life.
The expandable material useful in the invention can be any material which expands under controlled conditions and which does not expand under conditions of application to the part as described herein. In a preferred embodiment the expandable material exhibits adhesive properties under controlled conditions. It is also preferred that the expandable material is dry and not tacl~y to the touch at ambient conditions to facilitate shippiyg and handling. In the preferred embodiment, the expandable material is a polyneric material, and more preferably an expandable adhesive. A typical expandable adhesive includes a polymeric base material, such as an epoxy resin or ethylene-based polymer which, when compounded with appropriate ingredients (typically a blowing and curing agents), expands a~ld cures in a reliable and predictable manner upon the application of heat. The expandable adhesive will also crosslinc upon curing rendering the material incapable of fiu-ther flow or shape change.
Any material that is heat-activated and expands and cores in a predictable and reliable manner under appropriate conditions, while meeting stnictural requirements, for the selected application can be used. Other useful materials include polyolefins, copolymers and terpolymers with at least one monomer type an alpha-olefin, phenol/fonnaldehyde materials, phenoxy materials, and polyurethane materials with high glass transition temperature such as disclosed in U.S. 5,766,719; U.S. 5,755,486, U.S. 5,575526; U.S. 5,932,680, all incorporated by reference.
In a preferred embodiment, the expandable adhesive is a material comprising a) a 1-part epoxy resin; b) a viscosity increasing agent; and c) not greater than 25 parts by weight of an inorganic filler, based on 100 pans of the epoxy resin. The expandable material that is used to coat the article is prepared as a 1-part epoxy resin formulation.
Preferred epoxy resins include diglycidyl ethers of bisphenol A and bisphenol F, as well as oligomers of diglycidyl ethers of bisphenol A and bisphenol F, either alone or in combination. More preferably, the epoxy resin is a mixture of diglycidyl ether of bisphenol A and an oligomer of diglycidyl ether of bisphenol A. The epoxy resin preferably constitutes from 40 weight percent to 80 weight percent of the total materials used to male the expandable adhesive. The viscosity increasing agent is a material that increases the viscosity of the blend used to male the expandable adhesive. The viscosity increasing agent is preferably used as a fine powder (volume mean average <200 p,m) and preferably has a T~ of at least 70°C, more preferably at least 100°C.
Examples of preferred polymeric viscosity increasing agents include polymeric acrylates and methaciylates, more preferably polymethylmethacrylate (PMMA), most preferably a carboxylic acid functionalized PMMA, such as the conunercially available DegalanTM 4944F
PMMA
(available from Rohm America). The polymeric viscosity increasing agent is used in an effective amount to control release of gas from the blowing agent so as to reduce cell size in the resultant cured resin. The concentration of the polymeric viscosity increasing agent is preferably at least 2, more preferably at least 5, and most preferably at least 10 weight percent;
and preferably not more than 40 weight percent, more preferably not more than 30 weight percent, and most preferably not more than 20 weight percent, based on the total materials used to male the expandable adhesive. The polymerization of the epoxy resin is catalyzed by an effective amount of a polymerizing promoting catalyst, preferably from 0.1 weight percent to 2 weight percent, based on the total materials used to male the expandable adhesive. Preferable catalysts include, but are not restricted to amides, blocked amines, areas and imidazoles. An example of a preferred catalyst is Acclerine CEL 2191 (1-(2-(2-hydroxbenzamido)ethyl)-2-(2-hydroxyphenyl-2-imidazoline, which has the following chemical stmcture:
G
The preparation of this catalyst is described by Bagga in U.S. Patent 4,997,951, which description is incorporated herein by reference.
Tlle epoxy resin is expanded to a desired volume in the presence of an effective amount of a blowing agent, preferably from 0.5 weight percent to 10 weight percent, based on the total materials used to male the expandable adhesive. Preferred blowing agents are heat activatable at a temperature of 100°C or greater, more preferably at 120°C or greater; and even more preferably 150°C or greater, and most preferably 1G0°C or greater and preferably not greater than 200°C. Examples of suitable blowing agents include those described by Fului in U.S. 6,040,350, column 4, lines 25-30, which section is incorporated herein by reference. An example of a preferred commercially available blowing agent is Celogen AZTM
azodicarbonamide (from Crompton). The epoxy resin is cured using an effective amount of a curing agent, preferably from 2 to 10 weight percent, based on the total materials used to male the expandable adhesive. Examples of suitable curing agents include those described by Fulcui in column 4, line 66-67 and column 5, lines 1-9, which sections are incorporated herein by reference. The expandable adhesive may also include organic filler such as a polyethylene.
copolymer or an inorganic filler such as calcium carbonate. The amount of inorganic filler is preferably not greater than 25 parts by weight, more preferably not greater than 15 parts by weight, and most preferably not greater than 10 parts by weight, relative to l00 parts by weight of the expandable adhesive.
A preferred expandable adhesive is prepared by combining and mixing the epoxy resin, the blowing agent, the catalyst, the curing agent, the viscosity increasing agent, and optionally the inorganic and organic fillers at a temperature above ambient temperature, preferably from 30°C to 50°C for 15 minutes to 2 hours.
Entrapped air is removed ira vacuo.
The preferred cured (expanded) adhesive has a Young's modulus of at least 500 MPa, more preferably at least 700 MPa, and host preferably of at least 1000 MPa at 100 percent expansion. Furthel~nore, the prefelTed cured adhesive has su lprisingly small voids, preferably with a number weighted mean diameter of less than lOOO x.111, more preferably less than 500 p,m, and most preferably less than 100 l.~m. Consequently, the adhesion of the SFI
(structural foam insert) to the automotive structure is strong and durable.
The expandable material must also be capable of being plunped at temperature below the temperature at which the expandable material expands. This is to facilitate injection of the expandable material into the mold.
Alternatively the expandable material can be a material without adhesive properties. This is enabled when the film functions to bond the expandable material coated structural reinforcement member to the structural member. Airy polymeric material, which can be expanded under controlled conditions and can be applied to the structural reinforcement yember, can be used in this embodiment, examples include polyvinyl chloride (PVC), Poly Methyl Methacrylate (PMMA), phenoxy thermoplastics which further contain blowing agents.
The film used in thlS 111Ve11t1011 Call be any film, Whlch Call retalll 1tS
StrLlCtural integrity when exposed to the conditions of applying the expandable material to the plastic article, and will not adhere to the hold sw-face under such conditions. There are two general types of films used. In one embodiment, the film does not have any adhesive character and is simply used to allow easy removal.of the part from the mold. In another embodiment, the film has adhesive character under conditions where the expandable material expands.
In this embodiment the expandable material does not require adhesive character.
In the embodiment wherein the film does not require adhesive character, the film is preferably a low surface energy film; preferably a polyolefin , such as high density polyethylene, low density polyethylene, fluorinated polyethylene or polypropylene.
Alternatively, the film can be a high surface energy film coated with a low surface energy coating, for instance polyester coated with a low surface energy coating. In the embodiment where the film provides adhesion to the sti2lctural member, ally film, which provides adhesion at the temperature of expansion of the. expandable material, cal be used. In olle embodiment the film can be a corona treated polyolefln. In another embodiment the film can be a multilayer film with a layer on the outside which demonstrates adhesive character under conditions of expansion of the expandable material. The adhesive layer could be ethylene vinyl acetate or an ethylene acrylic acid co-polymer layer. Alterlatively the film can fiuzction as a hot melt adhesive under conditions of expansion. Where the f11111 fLl11Ct10115 aS a hot melt adhesive it is desirable that the expandable material have adhesive properties also.
In another embodiment the film can be sprayed or coated on the mold prior to placing the article into the mold. Water based highmolecular weight epoxy resins are useful in this embodiment, for example EPI-REZTM 3540 water based epoxy. The water-based epoxy is contacted with the mold and the water is flashed off such that a film is formed on the mold.
Thereafter the article is placed in the mold.
Molds used to prepare the articles of the invention are generally insert molds wherein an article is placed into the cavity of the tool. With the mold closed an outer shell cavity is created which is close to the size of the article being coated. The holds have at least one injection port to inject the expandable material into the mold. The molds need to have the capability to heat the expandable material and the article to facilitate application of the expandable material to the article. Generally the molds need to have the capability to be heated to a temperature high enough that the expandable material can be processed or flows and below the temperature at which the expandable material expands, such temperatures are 90°C or greater, and preferably 150°C or less and more preferably 130°C
or less.
In the process of the invention, the film is applied to the mold as described;
the article is placed in the mold with the film between the mold and the article.
The expandable adhesive is then injected into the hot mold (90°C to 150°C, preferably to 150°C) that surrounds and conforms to the shape of the article to achieve tlzicl~rless of adhesive over article ranging f10111 1 lrlln to 4 lxlln, the thiclmess can vary across the surface of the articles. The article is left in the mold fox sufficient time to achieve a coating of the desired thicla-less on the article. If the expandable material is thermoplastic in nature thl5 15 SLlfflClellt. If the coating is a liquid thernoset material, such as a paste epoxy, the material may need to be heated for an additional period of time to gel the expandable material to achieve the desired integrity of the coating.
Generally the residence time of the al-ticle in the mold is 6 hinutes or less, preferably 3 minutes or less, and most preferably 90 seconds or less.
After the article is removed from the mold, the article is cooled. Generally, the hold can ilmnediately be cycled, that is another of the described process can be started.
There are two types of film that would require deflhning. The first is a film that would be removed and under that would be the expandable material. The second would be the multi-layer film using the carrier and leave-on fiI111. Both types of film can be defihned or removed after cooling to or below ambient or it can be Ieft on the article until just before inserting it in the cavity of the structural member. For the first filly it is advantageous to leave the film on until just before insertion into the cavity of the stl-uctural member to facilitate handling and exposureof operators to uncured expandable material. If the film has adhesive properties, such as the leave-on film, it can be left on the article when it is inserted in the cavity of the structural member. In the embodiment where the film is entirely removed after molding, it is desirable to coat the part with a coating which renders the surface of the part non-taclcy.
The coating is generally a particulate material of a relatively small size.
Any coating which renders the surface non-tacl~y may be used. Preferable coating materials include calcium carbide,, glass balloons and the life.
In one embodiment, two films may be used. One film is an adhesive film (leave-on,fllm) and the second is a carrier film which does not have adhesive properties. In one embodiment, the carrier film does not adhere to the adhesive (or leave-on) film. The films typically are arranged in the mold with the carrier film located adjacent to the mold and the adhesive film located adjacent to the part. Preferably, the carrier film has a relatively high melting temperature of 130°C or greater, and preferably 160°C or greater. The carrier film can be prepared from any material which can maintain its integrity under molding conditions..
Ful-ther, it is preferable that the carrier film not adhere in a significant way to the mold under holding conditions. Preferably, the carrier f111111S prepared fiom a relatively non-polar polymeric material. Preferred polymeric materials are polyolefins or blends containing a volumetric majority of a polyolefin. Preferred polyolefins are polypropylene and polyethylene.
A preferred polyethylene is low density polyethylene. Alternatively, the film could be a fluorinated polyethylene or silicon coated polyester. Most preferably, the carrier layer is a homopolymer polypropylene. The thicl~rless of the carrier fihn is chosen to allow the carrier film to maintain its integrity dining molding. Maintain its integrity means the film continues to stay in film form and can be handled in film form. Preferably, the carrier layer has a thicl~rless of 2 mils 0.0051 (mm) or greater and more preferably 2.5 mils (0.0645 mm) or greater.
Preferably, the carrier layer has a thicl~less of 8 mil (0.20 mm) or less, more preferably 6 mil (0.15 mm) or less and most preferably 3 mil (0.076 mm) or less.
The second film is an adhesive or leave-on film. The leave-on film functions to protect the surface of the part during handling and transpol-t. It also prevents contact of anyone who handles the part with the adhesive coated oil the pact. The leave-on film may also serve the fiulction of an adhesive which aids in bonding the part in place in the structural member which is reinforced. Alternatively, the leave-on film melts wider automobile paint oven conditions allowing the adhesive coated on the part to read tluough the film to bond to the inside surface of the structural member reinforced. Preferably, the leave-on film is tacl~y at elevated temperatures, but not tacky at ambient temperatures, 15 to 35°C. Preferably, the film is taclLy or melts at the temperatures of an automotive paint oven. The leave-on layer may also be corona treated to improve bonding to the adhesive on the part during holding. The leave-on film can be prepared from any polymeric material which provides the propel-ties discussed hereinbefore. Preferably, the leave-on film comprises a polymer which contains polar functional groups, such as carboxylic acid, acetate, hydroxyl and the life. In another embodiment, the leave-on film comprises a blend of a polymer, with functional groups and a non-polar polymer for instance a polyolefn-1, copolyester or copolyalnide, a polyolefin.
Preferred polar group containing polymers include ethylene vinyl acetates, ethylene ethyl acrylates, malefic anhydride grafted polyolefins, allcylene acrylic acids (such as ethylene acrylic acid) blends thereof and the lilce. The leave-on film is preferably thicl~
enough to render the surface of the part non-taclcy under ambient conditions. Preferably, the thiclmess of the leave-on f11111 1S 0.1 mils (0.003 lrlln) or greater and most preferably 0.411111 (0.01016 lnm or greater).
Preferably, the leave-on film is 4 mils (0.1 mn) or less, more preferably 2 W
ils (0.0051 mm) or less and most preferably 0.8 mils (0.020 mm) or less.
In one embodiment, the two films can be formed as a single two-layer film and used as such in the preparation of the part. In this embodiment, the carrier portion of the film must be removable from the part after fabrication and the leave-on film is left behind. In this embodiment, the two layer film is placed in the mold, the mold is closed, and the adhesive is injected between the part and film. After the part is removed fiom the mold, the carrier film is removed and the leave-on fihn is left behind.
In another embodiment, the film can comprise tluee layers; the caiTier film, the leave-on film and an adhesion layer located between the two layers which function to adhere the two layers together. The adhesion properties of the intermediate layer are preferably sufficient to hold the layers together during processing, but not so strong as to prevent the carrier film from being removed. Preferably, the intermediate film has a relatively strong adhesive bond with the.carrier film and a relatively wear adhesive formed with.the leave-on film so as to allow removal of the intermediate f11111 Wlth the carrier layer.
The intermediate film can be prepared from any polymer which forms an adhesive bond with both the carrier and leave-on fihxis and which allows the caiTier film to be removed. Preferably, the intermediate layer is prepared from a non-polar polymer. Preferred polymers used are polyolefins, with homopolymer polypropylenes preferred. The intermediate film has sufficient thicl~ness to hold the two other layers together during handling. Preferably, the intermediate layer has a thicl~ness of 0.2 mils (0.0051 mm) or greater. Preferably, the intermediate layer has a thiclmess of 1 mil (0.025 mm) or less thicl~ and more preferably 0.4 mil (0.010 mm) thiclcness or less.
The films can be fabricated by well-lmown teclmziques such as multilayer coextrusions, casting or blown film processes.
The resultant article is affixed within a cavity of a stn.~ctwal member so as to create a gap between the article and the structural ll1e111ber Of 1-1n111 to 4-smm. The structure is then exposed to conditions at which the expandable material cures, preferably to temperatures of 140°C or greater, more preferably 150°C or greater, most preferably 160°C or greater, and preferably less than 205°C and more preferably less than 200°C, preferably for a time of 15 minutes. or more and preferably 25 minutes or more. In the embodiment where the structure is an automobile the expandable material is expanded during the e-coat process, with residual e-coat liquid escaping through the gaps between article and the structural member. Finally, the e-coat and expandable adhesive are cured at a suitable curing temperature, preferably between 150°C and 200°C.
Figure 1 shows a cross-sectional view of a portion of stmctural reinforcing member, (10). The structural reinforcing member has a film (11) adhered to an expandable material layer (12) coated onto a shaped rigid foam structure (13).
Figure 2 illustrates a partially closed apparatus (20) for perfomning the process of the invention. The apparatus (20) comprises two halves of a mold (21 and 22) which when closed forms a cavity (23). The. apparatus further comprises an injection nozzle (24)' having a central tube (25) adapted for injectiizg expandable material into the mold cavity.(23). A part (26) located in the mold cavity (23) are two film portions (27) located between the part (26) and the halves of the mold (21 and 22). To seal between the inj ectioii nozzle (24) and the film portions (27), several methods can be used, such as 0 rings (28) as illustrated here or soft defomnable seals, the film (27) itself squeezed between the mold (21 and 22) and the injection nozzle (24). There are 0 rings (28) located the injectioy nozzle (24). The 0 rings (28) seal the film (27) so that any injected material stays between the film portions (27) and part (26).
Located between the part (26) and the walls of the mold halves (21 and 22) layered with the film (27) is a gap (29) which is large enough to accommodate a coating of expandable material. .
Figure 3 is similar to Figure 1 except a three-layer film (11) is used. The figure illustrates a cross-sectional view of a stmctural reinforcing member (10)..
The structural reinforcing member (10) has a film (11) adhered to an expandable material layer (12) coated onto a rigid foam stuucture (13). The film (11) comprises tluee.layers, a leave-on layer (14) adjacent to the expandable material layer (12); an adhesion layer (15) located between the leave-on film layer and a carrier film layer (16) wherein the carrier film layer (16) is located as the outside film layer.
1.3 The process of the invention can be described in the context of Figure 2. The apparatus or mold (20) is opened and film (27) is placed in each mold half (21 and 22). A part (26) is placed in the cavity (23) of one of the mold halves (22). The other mold half (21) is closed so that the two mold halves (21 and 22) surround the part (26) with film (27) surrounding the part (26) and located between the part (26) and the mold halves (21 and 22).
There is a gap (28) between the part (26) and the mold halves (21 and 22) layered with he film (27). The film (27) is sealed by 0 rings (28) the injection nozzle (24). The mold is heated to the desired temperature (90°C to 150°C). Expandable material is injected into the gap (29) between the part (26) and film (27) through the tube (25) of the injection nozzle (24), until the entire gap (29) is filled. If the expandable material needs to the part (26), the part (26) with the injected epoxy is maintained in the mold cavity (23) lllltll the expandable material gels.
Thereafter the mold half (21) is opened to open the mold cavity (23). The part (26) with expandable material coated thereon and film (27) adhered to the expandable material is removed from the mold, and it is coated. The apparatus (20) is now ready to repeat the process.
Specific Embodiments The following examples are included to illustrate the invention and are not meant to limit the scope of the claims. Unless otherwise stated all parts and percentages are by weight.
To automate the process and allow for multiple molds to feed from one gun, a sheet separator is needed. This is a reusable or disposable piece that keeps the sheets separated for the gun to enter but allows the mold to be closed without the gun in place. A temporary plug maybe used after the gun is removed to prevent black flow of the expandable coating fiom leaving the mold. The gun can now be transferred to the next 11101d which is already closed and ready to be filled.
BETAMATETM73607 adhesive comprises a mixture of 30 to 40 percent by weight of a Bisphenol A based liquid epoxy resin having an epoxy equivalent weight of 181, 15 to 25 percent by weight of a blend of a high viscosity advanced liquid epoxy resin based on Bisphenol A having an epoxy equivalent weight of 230 to 250 and a solid advanced epoxy resin based on Bisphenol A having an epoxy equivalent weight of 675 to 750;
polymethyl methacrylate as a gelling agent, dicydicyanamide as a curing agent and a mixture of phenyldimethyl urea and a modified benzamide (MMB 2191 available from Celerity LLC as catalysts and as a blowing agent azodicarbonalnide.
XUS 66185 film comprises three layer a 0.8 mil (0.02032 lnln) layer of ethylene acrylic acid available from The Dow Chemical Company, a film of the trademarl~
PRIMACORTM 3330, an intermediate layer of 0.3 mils (0.00762 nun) of a homopolymer polypropylene and 2.5 mil (0.0635 nnn) layer of a copolymer of polypropylene blended with a minor amount of polyethylene available from The Dow Chemical Company under the designation DC783.00, XV661.
Example 1:
175 grams of BETAMATETM 73607 adhesive was applied to a less than 1 mil (0.0254 mm) LDPE (low density polyethylene) film: A second sheet was placed on top of the opposite side of the epoxy forming a sandwich configuration, fihn/epoxy/film.
2 mm spacers were placed around the perimeter of the epoxy in a 25 cm square shape between the two pieces of film to set the epoxy thicl~ness. The sandwich film/epoxy/fihn was placed into a heated press preset to 110°C. The press was then closed sdueezing the epoxy to a thicl~ness of 2-mm.
After 5 minutes the press was then opened and the sheet was easily removed from the metal press. The sheet was cooled to room temperature and the film was then easily removed.
Example 2:
175 grams of BETAMATETM 73607 adhesive was sandwiched between two sheets of a LDPE flhn, 3.5 mil (0.0889 mm) with a corona treatment on one surface of the film. On one side of the epoxy mass tile f11111 with the treatment was placed towards the epoxy and on the opposite side of the epoxy mass the treatment was placed away from the epoxy. The flhn/epoxy/flhn sandwich configuration was heated for S 11111111teS 111 tile heated metal press to fol~rl a 2-mm casting. A 10-cln X I O-Clll 5qllare WaS Cllt out of the 25-cm square casting and placed between hot dip galvaliized (HDG) panels with a 2-nnn air gap, using spacers to form the air gap. The HDG panel/flhn/epoxy/fllm/HDG panel sandwich configuration was than baled for 45 minutes @ 170°C. Each HDG panel was pulled away from the epoxy, the side with the treatment towards the epoxy came off the HDG panel easily, very little to no adhesion was observed between the non treated side of the film and the HDG panel. The treated side of the film bonded to the epoxy and could not be removed. The side with the treatment towards the HDG panel was very difficult to remove from the HDG panel, 100 percent cohesive failure was observed.
Example 3:
A Teflon sheet with an adhesive bacl~ing was adhered to a HDG panel. Two of these Teflon/HDG panels were prepared. Then one coat of water based epoxy, EPI-REZr 3540-WY-55, was brushed onto the Teflon sheets and the watei was allowed to flash off. The BETAMATETM 73607 epoxy adhesive was then applied between the two epoxy-coated panels.
Two imn spacers were placed around the perimeter of the epoxy. This sandwich configuration was then placed. into the heated press at 110°C for 2 minutes, pre-gelling the epoxy into a 2 mm casting. The sandwich configuration was cooled to 55°C. The sandwich configuration was pulled apart and the water-based epoxy and the expandable epoxy were easily pulled away from the HDG panel. The water based epoxy film was bonded to the expandable epoxy surface with a tacl~ free surface.
This pre-gelled epoxy dried with the water based epoxy coating was placed between two HDG panel with 4 mm spacers (that is, 2 mn air gap) and baled at 170°C for 45 minutes. 100 percent cohesive failure was observed between the epoxy and the steel panel.
The water-based epoxy film did not interfere with the adhesion.
Example 4:
A 16" (40.64 cm) square piece of XUS 66185 3 layer film was placed on the bottom half of the heated tool 250°F (121°C) with the caurier layer adjacent to the heated mold, the foam article was placed on top of the leave-on layer of the film and a second piece of the XUS 66185 film was placed on top of the foam part with the carrier layer adjacent to the heated top half of the mold. The mold was then ciosed leaving a 2 to 3 imn gap between the film and the tool. A 132 gram mass of BETAMATETM 73607 expandable adhesive was dispensed and injected into the open area between the foam and the leave-on layer of the film.
The tool was opened after 90 seconds; the foam/epoxy/fihn part was removed.
The multi layer film was adhered to the expandable epoxy. After the part reached ambient temperature the caiTier and B intermediate layer of the film were easily removed from the-part as one layer.
In another embodiment the invention is an al-ticle comprising a shaped article; an expandable material coated in the shaped article; and a film covering the expandable material coated shaped article.
In another embodiment the invention is a method of reinforcing a structural member which comprises inserting an article according to.this invention into a cavity of the structural member and heating the structural member and the article to a temperature at which the expandable material expands and the film or the expandable material bonds to the inner surface of the stl-uctural member so as to permanently fix the article in the structural member.
The process of the invention allows the preparation of an article coated with an expandable material in an efficient manner allowing tools to cycle with a hold time of 5 minutes or less, and more preferably as low as 60 to 90 seconds per part.
In another embodiment the invention is a method of molding with a film in which the melting point of the film is lower than the temperature of the molding tool during molding operations. The film with the low melting point is placed on top of another film with a melting point above the molding temperature of the tool dluing molding operations. The film with the high melting point is referred to as the cal-rier film. The film with the low melting point is referred to as the leave-on film. This two film combination is placed on the top half and bottom half of the tool. The carrier film and leave-on film are placed into the tool together with the carrier film closest to the tool and the leave-on film closest to the open cavity portion of the tool. The two film combination can be placed into the tool as one piece, with the two film combination folded over with the insert in the middle of the film or the two film combination cari be placed in the tool as two separate film pieces. The carrier film allows the use of a leave-on film with a melting temperatlue lower then the temperature needed to process the expandable material. Preferably, the carrier film and the leave-on film are separated after removal from the mold. The removed carrier flllll call thereafter be discarded.
Figure 1 shows a cross-sectional view of a stmctu ral reinforcing member.
Figure 2 illustrates an apparatus used.to perform the process of the invention.
Figure 3 shows a cross-sectional view of a structural reinforcing member with a three layer fihn.
This invention relates to a process for efficiently applying an expandable material to a shaped article in an efficient malmer and to the article so prepared. Shaped article as used herein means any article which is formed into a shape near its' final use shape.
Generally, the article can be fabricated from any lmown.material, such as plastic, metal, ceramic, glass and the life. In applications where weight is a l~ey factor, such as where the shaped article is used in an automobile, lighter materials such as plastics are preferably used.
The plastic material may be nylon, styrenic, polyolefm, such as polyethylene or polypropylene, polycarbonate, polyester, polyurethane, polyepoxide, poyurea, polyphenylene sulfide, polyetherimide, toughened plastics such as ABS (acrylonitrile-butadiene-styrene) or previously mentioned materials containing elastomers such as styrene-all~adiene blocl~
copolymers, ethylene-octene copolymers and the life, and blends thereof, such as a polycarbonate-ABS
blends. The rigid plastic shaped articles can be solid or hollow with hollow shaped articles preferred for applications where weight is a critical factor. hl allotheT
elllbOdllllellt the Shaped article is foam. Foamed articles are preferably solid and provide lower density and higher strength. Preferably the shaped foamed articles are prepared from foam which can withstand the time and temperatures to which the expandable material must be exposed to expand.
Preferably, the foam is based on polystyrene, polyurethane, polyurea or epoxy resins; more preferably on polyurethanes, polytzreas, epoxy reS111S alld most preferably polyurethanes.. In a preferred embodiment the foam used is a foam described in the Allen, U.S.
6,423~755B1, incorporated herein by reference.
The shaped article can be used in any application where it is necessary to hold the article into place permanently in another structure. Such applications include in transpol-tation vehicles, such at automobiles, light tmclcs, heavy-duty trucl~s and busses, rail cars, aircraft; buildings, appliances and heavy machinery. Preferal?ly, the at-ticles of the invention are used to reinforce sti-nctural members. A structural member is a part of a structure, as described above, which supports or protects the structure. In this embodiment, the articles of the invention are structural reinforcing members, which means that they are used to structurally strengthen the structure and integrity of the structural member into which they are inserted.
Generally, the structural reinforcing members are inserted into hollow cavities of the structural member to improve the structural integrity of the structural member.
Preferably the structural reinforcing members are used in buildings or vehicles, preferably vehicles, such as automobiles and light trucl~s. The articles of the invention may further comprise a weans of locating and holding the article into a cavity until exposed to conditions such that the expandable material expands to hold the article in place. The means of locating and holding the article in place can be means which function to locate and/or hold the article in place prior to expansion of the expandable material. Such means include shaped standoffs or projections, tabs affixed to the part by mechanical affixing means (screws, nails, clips and the life), pressure sensitive adhesives, magnets and the life.
The expandable material useful in the invention can be any material which expands under controlled conditions and which does not expand under conditions of application to the part as described herein. In a preferred embodiment the expandable material exhibits adhesive properties under controlled conditions. It is also preferred that the expandable material is dry and not tacl~y to the touch at ambient conditions to facilitate shippiyg and handling. In the preferred embodiment, the expandable material is a polyneric material, and more preferably an expandable adhesive. A typical expandable adhesive includes a polymeric base material, such as an epoxy resin or ethylene-based polymer which, when compounded with appropriate ingredients (typically a blowing and curing agents), expands a~ld cures in a reliable and predictable manner upon the application of heat. The expandable adhesive will also crosslinc upon curing rendering the material incapable of fiu-ther flow or shape change.
Any material that is heat-activated and expands and cores in a predictable and reliable manner under appropriate conditions, while meeting stnictural requirements, for the selected application can be used. Other useful materials include polyolefins, copolymers and terpolymers with at least one monomer type an alpha-olefin, phenol/fonnaldehyde materials, phenoxy materials, and polyurethane materials with high glass transition temperature such as disclosed in U.S. 5,766,719; U.S. 5,755,486, U.S. 5,575526; U.S. 5,932,680, all incorporated by reference.
In a preferred embodiment, the expandable adhesive is a material comprising a) a 1-part epoxy resin; b) a viscosity increasing agent; and c) not greater than 25 parts by weight of an inorganic filler, based on 100 pans of the epoxy resin. The expandable material that is used to coat the article is prepared as a 1-part epoxy resin formulation.
Preferred epoxy resins include diglycidyl ethers of bisphenol A and bisphenol F, as well as oligomers of diglycidyl ethers of bisphenol A and bisphenol F, either alone or in combination. More preferably, the epoxy resin is a mixture of diglycidyl ether of bisphenol A and an oligomer of diglycidyl ether of bisphenol A. The epoxy resin preferably constitutes from 40 weight percent to 80 weight percent of the total materials used to male the expandable adhesive. The viscosity increasing agent is a material that increases the viscosity of the blend used to male the expandable adhesive. The viscosity increasing agent is preferably used as a fine powder (volume mean average <200 p,m) and preferably has a T~ of at least 70°C, more preferably at least 100°C.
Examples of preferred polymeric viscosity increasing agents include polymeric acrylates and methaciylates, more preferably polymethylmethacrylate (PMMA), most preferably a carboxylic acid functionalized PMMA, such as the conunercially available DegalanTM 4944F
PMMA
(available from Rohm America). The polymeric viscosity increasing agent is used in an effective amount to control release of gas from the blowing agent so as to reduce cell size in the resultant cured resin. The concentration of the polymeric viscosity increasing agent is preferably at least 2, more preferably at least 5, and most preferably at least 10 weight percent;
and preferably not more than 40 weight percent, more preferably not more than 30 weight percent, and most preferably not more than 20 weight percent, based on the total materials used to male the expandable adhesive. The polymerization of the epoxy resin is catalyzed by an effective amount of a polymerizing promoting catalyst, preferably from 0.1 weight percent to 2 weight percent, based on the total materials used to male the expandable adhesive. Preferable catalysts include, but are not restricted to amides, blocked amines, areas and imidazoles. An example of a preferred catalyst is Acclerine CEL 2191 (1-(2-(2-hydroxbenzamido)ethyl)-2-(2-hydroxyphenyl-2-imidazoline, which has the following chemical stmcture:
G
The preparation of this catalyst is described by Bagga in U.S. Patent 4,997,951, which description is incorporated herein by reference.
Tlle epoxy resin is expanded to a desired volume in the presence of an effective amount of a blowing agent, preferably from 0.5 weight percent to 10 weight percent, based on the total materials used to male the expandable adhesive. Preferred blowing agents are heat activatable at a temperature of 100°C or greater, more preferably at 120°C or greater; and even more preferably 150°C or greater, and most preferably 1G0°C or greater and preferably not greater than 200°C. Examples of suitable blowing agents include those described by Fului in U.S. 6,040,350, column 4, lines 25-30, which section is incorporated herein by reference. An example of a preferred commercially available blowing agent is Celogen AZTM
azodicarbonamide (from Crompton). The epoxy resin is cured using an effective amount of a curing agent, preferably from 2 to 10 weight percent, based on the total materials used to male the expandable adhesive. Examples of suitable curing agents include those described by Fulcui in column 4, line 66-67 and column 5, lines 1-9, which sections are incorporated herein by reference. The expandable adhesive may also include organic filler such as a polyethylene.
copolymer or an inorganic filler such as calcium carbonate. The amount of inorganic filler is preferably not greater than 25 parts by weight, more preferably not greater than 15 parts by weight, and most preferably not greater than 10 parts by weight, relative to l00 parts by weight of the expandable adhesive.
A preferred expandable adhesive is prepared by combining and mixing the epoxy resin, the blowing agent, the catalyst, the curing agent, the viscosity increasing agent, and optionally the inorganic and organic fillers at a temperature above ambient temperature, preferably from 30°C to 50°C for 15 minutes to 2 hours.
Entrapped air is removed ira vacuo.
The preferred cured (expanded) adhesive has a Young's modulus of at least 500 MPa, more preferably at least 700 MPa, and host preferably of at least 1000 MPa at 100 percent expansion. Furthel~nore, the prefelTed cured adhesive has su lprisingly small voids, preferably with a number weighted mean diameter of less than lOOO x.111, more preferably less than 500 p,m, and most preferably less than 100 l.~m. Consequently, the adhesion of the SFI
(structural foam insert) to the automotive structure is strong and durable.
The expandable material must also be capable of being plunped at temperature below the temperature at which the expandable material expands. This is to facilitate injection of the expandable material into the mold.
Alternatively the expandable material can be a material without adhesive properties. This is enabled when the film functions to bond the expandable material coated structural reinforcement member to the structural member. Airy polymeric material, which can be expanded under controlled conditions and can be applied to the structural reinforcement yember, can be used in this embodiment, examples include polyvinyl chloride (PVC), Poly Methyl Methacrylate (PMMA), phenoxy thermoplastics which further contain blowing agents.
The film used in thlS 111Ve11t1011 Call be any film, Whlch Call retalll 1tS
StrLlCtural integrity when exposed to the conditions of applying the expandable material to the plastic article, and will not adhere to the hold sw-face under such conditions. There are two general types of films used. In one embodiment, the film does not have any adhesive character and is simply used to allow easy removal.of the part from the mold. In another embodiment, the film has adhesive character under conditions where the expandable material expands.
In this embodiment the expandable material does not require adhesive character.
In the embodiment wherein the film does not require adhesive character, the film is preferably a low surface energy film; preferably a polyolefin , such as high density polyethylene, low density polyethylene, fluorinated polyethylene or polypropylene.
Alternatively, the film can be a high surface energy film coated with a low surface energy coating, for instance polyester coated with a low surface energy coating. In the embodiment where the film provides adhesion to the sti2lctural member, ally film, which provides adhesion at the temperature of expansion of the. expandable material, cal be used. In olle embodiment the film can be a corona treated polyolefln. In another embodiment the film can be a multilayer film with a layer on the outside which demonstrates adhesive character under conditions of expansion of the expandable material. The adhesive layer could be ethylene vinyl acetate or an ethylene acrylic acid co-polymer layer. Alterlatively the film can fiuzction as a hot melt adhesive under conditions of expansion. Where the f11111 fLl11Ct10115 aS a hot melt adhesive it is desirable that the expandable material have adhesive properties also.
In another embodiment the film can be sprayed or coated on the mold prior to placing the article into the mold. Water based highmolecular weight epoxy resins are useful in this embodiment, for example EPI-REZTM 3540 water based epoxy. The water-based epoxy is contacted with the mold and the water is flashed off such that a film is formed on the mold.
Thereafter the article is placed in the mold.
Molds used to prepare the articles of the invention are generally insert molds wherein an article is placed into the cavity of the tool. With the mold closed an outer shell cavity is created which is close to the size of the article being coated. The holds have at least one injection port to inject the expandable material into the mold. The molds need to have the capability to heat the expandable material and the article to facilitate application of the expandable material to the article. Generally the molds need to have the capability to be heated to a temperature high enough that the expandable material can be processed or flows and below the temperature at which the expandable material expands, such temperatures are 90°C or greater, and preferably 150°C or less and more preferably 130°C
or less.
In the process of the invention, the film is applied to the mold as described;
the article is placed in the mold with the film between the mold and the article.
The expandable adhesive is then injected into the hot mold (90°C to 150°C, preferably to 150°C) that surrounds and conforms to the shape of the article to achieve tlzicl~rless of adhesive over article ranging f10111 1 lrlln to 4 lxlln, the thiclmess can vary across the surface of the articles. The article is left in the mold fox sufficient time to achieve a coating of the desired thicla-less on the article. If the expandable material is thermoplastic in nature thl5 15 SLlfflClellt. If the coating is a liquid thernoset material, such as a paste epoxy, the material may need to be heated for an additional period of time to gel the expandable material to achieve the desired integrity of the coating.
Generally the residence time of the al-ticle in the mold is 6 hinutes or less, preferably 3 minutes or less, and most preferably 90 seconds or less.
After the article is removed from the mold, the article is cooled. Generally, the hold can ilmnediately be cycled, that is another of the described process can be started.
There are two types of film that would require deflhning. The first is a film that would be removed and under that would be the expandable material. The second would be the multi-layer film using the carrier and leave-on fiI111. Both types of film can be defihned or removed after cooling to or below ambient or it can be Ieft on the article until just before inserting it in the cavity of the structural member. For the first filly it is advantageous to leave the film on until just before insertion into the cavity of the stl-uctural member to facilitate handling and exposureof operators to uncured expandable material. If the film has adhesive properties, such as the leave-on film, it can be left on the article when it is inserted in the cavity of the structural member. In the embodiment where the film is entirely removed after molding, it is desirable to coat the part with a coating which renders the surface of the part non-taclcy.
The coating is generally a particulate material of a relatively small size.
Any coating which renders the surface non-tacl~y may be used. Preferable coating materials include calcium carbide,, glass balloons and the life.
In one embodiment, two films may be used. One film is an adhesive film (leave-on,fllm) and the second is a carrier film which does not have adhesive properties. In one embodiment, the carrier film does not adhere to the adhesive (or leave-on) film. The films typically are arranged in the mold with the carrier film located adjacent to the mold and the adhesive film located adjacent to the part. Preferably, the carrier film has a relatively high melting temperature of 130°C or greater, and preferably 160°C or greater. The carrier film can be prepared from any material which can maintain its integrity under molding conditions..
Ful-ther, it is preferable that the carrier film not adhere in a significant way to the mold under holding conditions. Preferably, the carrier f111111S prepared fiom a relatively non-polar polymeric material. Preferred polymeric materials are polyolefins or blends containing a volumetric majority of a polyolefin. Preferred polyolefins are polypropylene and polyethylene.
A preferred polyethylene is low density polyethylene. Alternatively, the film could be a fluorinated polyethylene or silicon coated polyester. Most preferably, the carrier layer is a homopolymer polypropylene. The thicl~rless of the carrier fihn is chosen to allow the carrier film to maintain its integrity dining molding. Maintain its integrity means the film continues to stay in film form and can be handled in film form. Preferably, the carrier layer has a thicl~rless of 2 mils 0.0051 (mm) or greater and more preferably 2.5 mils (0.0645 mm) or greater.
Preferably, the carrier layer has a thicl~less of 8 mil (0.20 mm) or less, more preferably 6 mil (0.15 mm) or less and most preferably 3 mil (0.076 mm) or less.
The second film is an adhesive or leave-on film. The leave-on film functions to protect the surface of the part during handling and transpol-t. It also prevents contact of anyone who handles the part with the adhesive coated oil the pact. The leave-on film may also serve the fiulction of an adhesive which aids in bonding the part in place in the structural member which is reinforced. Alternatively, the leave-on film melts wider automobile paint oven conditions allowing the adhesive coated on the part to read tluough the film to bond to the inside surface of the structural member reinforced. Preferably, the leave-on film is tacl~y at elevated temperatures, but not tacky at ambient temperatures, 15 to 35°C. Preferably, the film is taclLy or melts at the temperatures of an automotive paint oven. The leave-on layer may also be corona treated to improve bonding to the adhesive on the part during holding. The leave-on film can be prepared from any polymeric material which provides the propel-ties discussed hereinbefore. Preferably, the leave-on film comprises a polymer which contains polar functional groups, such as carboxylic acid, acetate, hydroxyl and the life. In another embodiment, the leave-on film comprises a blend of a polymer, with functional groups and a non-polar polymer for instance a polyolefn-1, copolyester or copolyalnide, a polyolefin.
Preferred polar group containing polymers include ethylene vinyl acetates, ethylene ethyl acrylates, malefic anhydride grafted polyolefins, allcylene acrylic acids (such as ethylene acrylic acid) blends thereof and the lilce. The leave-on film is preferably thicl~
enough to render the surface of the part non-taclcy under ambient conditions. Preferably, the thiclmess of the leave-on f11111 1S 0.1 mils (0.003 lrlln) or greater and most preferably 0.411111 (0.01016 lnm or greater).
Preferably, the leave-on film is 4 mils (0.1 mn) or less, more preferably 2 W
ils (0.0051 mm) or less and most preferably 0.8 mils (0.020 mm) or less.
In one embodiment, the two films can be formed as a single two-layer film and used as such in the preparation of the part. In this embodiment, the carrier portion of the film must be removable from the part after fabrication and the leave-on film is left behind. In this embodiment, the two layer film is placed in the mold, the mold is closed, and the adhesive is injected between the part and film. After the part is removed fiom the mold, the carrier film is removed and the leave-on fihn is left behind.
In another embodiment, the film can comprise tluee layers; the caiTier film, the leave-on film and an adhesion layer located between the two layers which function to adhere the two layers together. The adhesion properties of the intermediate layer are preferably sufficient to hold the layers together during processing, but not so strong as to prevent the carrier film from being removed. Preferably, the intermediate film has a relatively strong adhesive bond with the.carrier film and a relatively wear adhesive formed with.the leave-on film so as to allow removal of the intermediate f11111 Wlth the carrier layer.
The intermediate film can be prepared from any polymer which forms an adhesive bond with both the carrier and leave-on fihxis and which allows the caiTier film to be removed. Preferably, the intermediate layer is prepared from a non-polar polymer. Preferred polymers used are polyolefins, with homopolymer polypropylenes preferred. The intermediate film has sufficient thicl~ness to hold the two other layers together during handling. Preferably, the intermediate layer has a thicl~ness of 0.2 mils (0.0051 mm) or greater. Preferably, the intermediate layer has a thiclmess of 1 mil (0.025 mm) or less thicl~ and more preferably 0.4 mil (0.010 mm) thiclcness or less.
The films can be fabricated by well-lmown teclmziques such as multilayer coextrusions, casting or blown film processes.
The resultant article is affixed within a cavity of a stn.~ctwal member so as to create a gap between the article and the structural ll1e111ber Of 1-1n111 to 4-smm. The structure is then exposed to conditions at which the expandable material cures, preferably to temperatures of 140°C or greater, more preferably 150°C or greater, most preferably 160°C or greater, and preferably less than 205°C and more preferably less than 200°C, preferably for a time of 15 minutes. or more and preferably 25 minutes or more. In the embodiment where the structure is an automobile the expandable material is expanded during the e-coat process, with residual e-coat liquid escaping through the gaps between article and the structural member. Finally, the e-coat and expandable adhesive are cured at a suitable curing temperature, preferably between 150°C and 200°C.
Figure 1 shows a cross-sectional view of a portion of stmctural reinforcing member, (10). The structural reinforcing member has a film (11) adhered to an expandable material layer (12) coated onto a shaped rigid foam structure (13).
Figure 2 illustrates a partially closed apparatus (20) for perfomning the process of the invention. The apparatus (20) comprises two halves of a mold (21 and 22) which when closed forms a cavity (23). The. apparatus further comprises an injection nozzle (24)' having a central tube (25) adapted for injectiizg expandable material into the mold cavity.(23). A part (26) located in the mold cavity (23) are two film portions (27) located between the part (26) and the halves of the mold (21 and 22). To seal between the inj ectioii nozzle (24) and the film portions (27), several methods can be used, such as 0 rings (28) as illustrated here or soft defomnable seals, the film (27) itself squeezed between the mold (21 and 22) and the injection nozzle (24). There are 0 rings (28) located the injectioy nozzle (24). The 0 rings (28) seal the film (27) so that any injected material stays between the film portions (27) and part (26).
Located between the part (26) and the walls of the mold halves (21 and 22) layered with the film (27) is a gap (29) which is large enough to accommodate a coating of expandable material. .
Figure 3 is similar to Figure 1 except a three-layer film (11) is used. The figure illustrates a cross-sectional view of a stmctural reinforcing member (10)..
The structural reinforcing member (10) has a film (11) adhered to an expandable material layer (12) coated onto a rigid foam stuucture (13). The film (11) comprises tluee.layers, a leave-on layer (14) adjacent to the expandable material layer (12); an adhesion layer (15) located between the leave-on film layer and a carrier film layer (16) wherein the carrier film layer (16) is located as the outside film layer.
1.3 The process of the invention can be described in the context of Figure 2. The apparatus or mold (20) is opened and film (27) is placed in each mold half (21 and 22). A part (26) is placed in the cavity (23) of one of the mold halves (22). The other mold half (21) is closed so that the two mold halves (21 and 22) surround the part (26) with film (27) surrounding the part (26) and located between the part (26) and the mold halves (21 and 22).
There is a gap (28) between the part (26) and the mold halves (21 and 22) layered with he film (27). The film (27) is sealed by 0 rings (28) the injection nozzle (24). The mold is heated to the desired temperature (90°C to 150°C). Expandable material is injected into the gap (29) between the part (26) and film (27) through the tube (25) of the injection nozzle (24), until the entire gap (29) is filled. If the expandable material needs to the part (26), the part (26) with the injected epoxy is maintained in the mold cavity (23) lllltll the expandable material gels.
Thereafter the mold half (21) is opened to open the mold cavity (23). The part (26) with expandable material coated thereon and film (27) adhered to the expandable material is removed from the mold, and it is coated. The apparatus (20) is now ready to repeat the process.
Specific Embodiments The following examples are included to illustrate the invention and are not meant to limit the scope of the claims. Unless otherwise stated all parts and percentages are by weight.
To automate the process and allow for multiple molds to feed from one gun, a sheet separator is needed. This is a reusable or disposable piece that keeps the sheets separated for the gun to enter but allows the mold to be closed without the gun in place. A temporary plug maybe used after the gun is removed to prevent black flow of the expandable coating fiom leaving the mold. The gun can now be transferred to the next 11101d which is already closed and ready to be filled.
BETAMATETM73607 adhesive comprises a mixture of 30 to 40 percent by weight of a Bisphenol A based liquid epoxy resin having an epoxy equivalent weight of 181, 15 to 25 percent by weight of a blend of a high viscosity advanced liquid epoxy resin based on Bisphenol A having an epoxy equivalent weight of 230 to 250 and a solid advanced epoxy resin based on Bisphenol A having an epoxy equivalent weight of 675 to 750;
polymethyl methacrylate as a gelling agent, dicydicyanamide as a curing agent and a mixture of phenyldimethyl urea and a modified benzamide (MMB 2191 available from Celerity LLC as catalysts and as a blowing agent azodicarbonalnide.
XUS 66185 film comprises three layer a 0.8 mil (0.02032 lnln) layer of ethylene acrylic acid available from The Dow Chemical Company, a film of the trademarl~
PRIMACORTM 3330, an intermediate layer of 0.3 mils (0.00762 nun) of a homopolymer polypropylene and 2.5 mil (0.0635 nnn) layer of a copolymer of polypropylene blended with a minor amount of polyethylene available from The Dow Chemical Company under the designation DC783.00, XV661.
Example 1:
175 grams of BETAMATETM 73607 adhesive was applied to a less than 1 mil (0.0254 mm) LDPE (low density polyethylene) film: A second sheet was placed on top of the opposite side of the epoxy forming a sandwich configuration, fihn/epoxy/film.
2 mm spacers were placed around the perimeter of the epoxy in a 25 cm square shape between the two pieces of film to set the epoxy thicl~ness. The sandwich film/epoxy/fihn was placed into a heated press preset to 110°C. The press was then closed sdueezing the epoxy to a thicl~ness of 2-mm.
After 5 minutes the press was then opened and the sheet was easily removed from the metal press. The sheet was cooled to room temperature and the film was then easily removed.
Example 2:
175 grams of BETAMATETM 73607 adhesive was sandwiched between two sheets of a LDPE flhn, 3.5 mil (0.0889 mm) with a corona treatment on one surface of the film. On one side of the epoxy mass tile f11111 with the treatment was placed towards the epoxy and on the opposite side of the epoxy mass the treatment was placed away from the epoxy. The flhn/epoxy/flhn sandwich configuration was heated for S 11111111teS 111 tile heated metal press to fol~rl a 2-mm casting. A 10-cln X I O-Clll 5qllare WaS Cllt out of the 25-cm square casting and placed between hot dip galvaliized (HDG) panels with a 2-nnn air gap, using spacers to form the air gap. The HDG panel/flhn/epoxy/fllm/HDG panel sandwich configuration was than baled for 45 minutes @ 170°C. Each HDG panel was pulled away from the epoxy, the side with the treatment towards the epoxy came off the HDG panel easily, very little to no adhesion was observed between the non treated side of the film and the HDG panel. The treated side of the film bonded to the epoxy and could not be removed. The side with the treatment towards the HDG panel was very difficult to remove from the HDG panel, 100 percent cohesive failure was observed.
Example 3:
A Teflon sheet with an adhesive bacl~ing was adhered to a HDG panel. Two of these Teflon/HDG panels were prepared. Then one coat of water based epoxy, EPI-REZr 3540-WY-55, was brushed onto the Teflon sheets and the watei was allowed to flash off. The BETAMATETM 73607 epoxy adhesive was then applied between the two epoxy-coated panels.
Two imn spacers were placed around the perimeter of the epoxy. This sandwich configuration was then placed. into the heated press at 110°C for 2 minutes, pre-gelling the epoxy into a 2 mm casting. The sandwich configuration was cooled to 55°C. The sandwich configuration was pulled apart and the water-based epoxy and the expandable epoxy were easily pulled away from the HDG panel. The water based epoxy film was bonded to the expandable epoxy surface with a tacl~ free surface.
This pre-gelled epoxy dried with the water based epoxy coating was placed between two HDG panel with 4 mm spacers (that is, 2 mn air gap) and baled at 170°C for 45 minutes. 100 percent cohesive failure was observed between the epoxy and the steel panel.
The water-based epoxy film did not interfere with the adhesion.
Example 4:
A 16" (40.64 cm) square piece of XUS 66185 3 layer film was placed on the bottom half of the heated tool 250°F (121°C) with the caurier layer adjacent to the heated mold, the foam article was placed on top of the leave-on layer of the film and a second piece of the XUS 66185 film was placed on top of the foam part with the carrier layer adjacent to the heated top half of the mold. The mold was then ciosed leaving a 2 to 3 imn gap between the film and the tool. A 132 gram mass of BETAMATETM 73607 expandable adhesive was dispensed and injected into the open area between the foam and the leave-on layer of the film.
The tool was opened after 90 seconds; the foam/epoxy/fihn part was removed.
The multi layer film was adhered to the expandable epoxy. After the part reached ambient temperature the caiTier and B intermediate layer of the film were easily removed from the-part as one layer.
Claims (10)
1 ~An article comprising i) a shaped article;
ii) an expandable material coated in the shaped article;
iii) and a film covering the expandable material coated shaped article.
ii) an expandable material coated in the shaped article;
iii) and a film covering the expandable material coated shaped article.
2. ~An article according to Claim 1 wherein the shaped article comprises a shaped hollow article with a rigid plastic shell or a shaped solid foam plastic article.
3. ~An article according to Claim 1 or 2 wherein the expandable material exhibits adhesive properties under conditions at which the expandable material is expanded.
4. ~An article according to any one of Claims 1 to 3 wherein the film is capable of bonding to surfaces at a temperature above the temperature at which the film covered expandable material coated article is prepared.
An article according to Claim 12 wherein the film bonds to surfaces at a temperature of 160°C to 205°C.
6. ~An article according to Claim 10 wherein the expandable adhesive comprises an epoxy resin based adhesive.
7. ~An article according to Claim 9 wherein the shaped plastic article comprises a solid polyurethane foam.
8. ~A process for the preparation of article comprising a) placing a film on the inner surface of each part of a two pact mold;
b) placing an article in the mold with film located between the surface of the mold and the article;
c) closing the mold the article such that there is a small space between the article and the surface of the mold;
d) injecting between the film and the article an expandable material under conditions that the article is coated with the expandable material and the expandable material does not expand;
e) removing the article with the expandable material coated thereon with the film attached to the expandable material.
b) placing an article in the mold with film located between the surface of the mold and the article;
c) closing the mold the article such that there is a small space between the article and the surface of the mold;
d) injecting between the film and the article an expandable material under conditions that the article is coated with the expandable material and the expandable material does not expand;
e) removing the article with the expandable material coated thereon with the film attached to the expandable material.
9. The process of Claim 8 wherein the film is removed from the expandable material coated plastic article.
10. A method of reinforcing a structural member which comprises inserting an article according to any one of Claims 1 to 7 into a cavity of the structural member and heating the structural member and the article to a temperature at which the expandable material expands and the film or the expandable material bonds to the inner surface of the structural member so as to fix the location of the article in the structural member.