CA2518837C - Cementitious compositions containing interground cement clinker and zeolite - Google Patents
Cementitious compositions containing interground cement clinker and zeolite Download PDFInfo
- Publication number
- CA2518837C CA2518837C CA002518837A CA2518837A CA2518837C CA 2518837 C CA2518837 C CA 2518837C CA 002518837 A CA002518837 A CA 002518837A CA 2518837 A CA2518837 A CA 2518837A CA 2518837 C CA2518837 C CA 2518837C
- Authority
- CA
- Canada
- Prior art keywords
- base grind
- composition
- zeolite
- interground
- grind
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Methods and compositions for wellbore treating fluids, especially cementitious compositions that include interground cement clinker and zeolite, with and without gypsum.
Description
Cementitious Compositions Containing Interground Cement Clinker and Zeolite Background The present application relates generally to compositions for sealing a subterranean zone penetrated by a wellbore.
Zeolites are known to be pozzolanic materials and may be activated with alkali or Portland cement in the presence of sufficient water. In most cases, it is possible to accelerate or retard the setting time by using conventional cement additives. However, further properties of a zeolite-containing composition such as compressive strength development, early strength, rheology, and density, for example, are of industrial concern.
Conventionally, a wellbore is drilled using a drilling fluid that is continuously circulated down a drill pipe, through a drill bit, and upwardly through the wellbore to the surface. The next operation usually involves running a pipe string, e.g., casing, into the wellbore, and then cleaning out the wellbore, after which primary cementing operations are typically performed. The pipe is cemented in the wellbore by placing a cement slurry in the annulus between the pipe and the walls of the wellbore. The cement slurry sets into a hard impermeable mass, and is intended to bond the pipe to the walls of the wellbore whereby the annulus is sealed and fluid communication between subterranean zones or to the surface by way of the annulus is prevented.
During any of the above or other operations performed in the wellbore, a number of problems can occur, including difficulty in removing portions of drilling fluid, deposits of filter cake, or inability to achieve a satisfactory bond between the pipe and the walls of the wellbore.
The present embodiments provide zeolite-containing cementitious compositions having enhanced performance in terms of rheological properties and compressive strength. In particular, such compositions are useful in the construction industry and in well cementing.
Brief Description of the Drawings FIG. 1. is a graph of mean particle size as a function of grind time for a composition of 60% cement clinker interground with 40% zeolite (w/w);
FIG. 2. is a graph of percent volume as a function of particle size at various grinding times for a composition of 60% cement clinker interground with 40% zeolite (w/w);
FIG. 3. is a graph of percent volume as a function of particle size at various grinding times for a composition of 60% cement clinker interground with 40% zeolite (w/w);
Zeolites are known to be pozzolanic materials and may be activated with alkali or Portland cement in the presence of sufficient water. In most cases, it is possible to accelerate or retard the setting time by using conventional cement additives. However, further properties of a zeolite-containing composition such as compressive strength development, early strength, rheology, and density, for example, are of industrial concern.
Conventionally, a wellbore is drilled using a drilling fluid that is continuously circulated down a drill pipe, through a drill bit, and upwardly through the wellbore to the surface. The next operation usually involves running a pipe string, e.g., casing, into the wellbore, and then cleaning out the wellbore, after which primary cementing operations are typically performed. The pipe is cemented in the wellbore by placing a cement slurry in the annulus between the pipe and the walls of the wellbore. The cement slurry sets into a hard impermeable mass, and is intended to bond the pipe to the walls of the wellbore whereby the annulus is sealed and fluid communication between subterranean zones or to the surface by way of the annulus is prevented.
During any of the above or other operations performed in the wellbore, a number of problems can occur, including difficulty in removing portions of drilling fluid, deposits of filter cake, or inability to achieve a satisfactory bond between the pipe and the walls of the wellbore.
The present embodiments provide zeolite-containing cementitious compositions having enhanced performance in terms of rheological properties and compressive strength. In particular, such compositions are useful in the construction industry and in well cementing.
Brief Description of the Drawings FIG. 1. is a graph of mean particle size as a function of grind time for a composition of 60% cement clinker interground with 40% zeolite (w/w);
FIG. 2. is a graph of percent volume as a function of particle size at various grinding times for a composition of 60% cement clinker interground with 40% zeolite (w/w);
FIG. 3. is a graph of percent volume as a function of particle size at various grinding times for a composition of 60% cement clinker interground with 40% zeolite (w/w);
FIG. 4. is a micrograph of a composition of 60% cement clinker interground with 40%
zeolite (w/w);
FIG. 5. is a micrograph of a composition of 60% cement clinker interground with 40%
zeolite (w/w);
FIG. 6. is a comparison graph of percent volume as a function of particle size for various compositions that include one or more of clinker, zeolite, and gypsum;
FIG. 7. is a comparison graph of percent volume as a function of particle size for various compositions that include one or more of clinker, zeolite, and gypsum;
and FIG. 8. is a comparison graph of compressive strength versus time for various compositions that include one or more of clinker, zeolite, gypsum and cement.
Description Interground zeolite and cement clinker compositions are provided herein for use as a cementitious composition in cementing operations. Additional compositions are provided in which gypsum is interground with zeolite and cement clinker.
Intergrinding zeolite and cement clinker was found to provide a bimodal distribution of particle size in the grind, and increased strength properties of the subsequent cementitious set material as compared to blending separately-ground material, particularly at longer set times.
The increased compressive strength of the interground set material was not observed when hand-ground gypsum was added to the slurry of interground clinker and zeolite material.
Class C cement is essentially ground clinker and gypsum, and slurries of such cement blended with zeolite, while producing early compressive strengths comparable to that of the interground material, does not provide later compressive strengths comparable to that of the interground material.
Increased flow, i.e., better rheology, was observed in those samples lacking gypsum.
Gypsum serves the function of a retarder and in its absence, the aluminate phase hydration reactions appear to occur rapidly. Zeolite has a retarding effect also, however, zeolite appears to provide better results in terms of rheology.
The high compressive strengths at longer set times and the greater flow characteristics of the interground clinker and zeolite material combines two desirable characteristics of a cementitious composition in one material.
The term "cementitious," as used herein, means having the properties of cement. The cementitious materials are suitable for a broad range of cementing applications, in particular, as a replacement for hydraulic cement where cement is to be set in a water environment, for control of timing of strength development, for applications where flowability is particularly desired, and where low density slurries are desired.
.A process of performing a cementing operation in a subterranean zone penetrated by a wellbore is an embodiment of the present invention. The process comprises placing a gypsum-free cementitious composition into the subterranean zone and allowing the cementitious composition to set therein. The gypsum-free cementitious composition is also an embodiment of the present invention and comprises a carrier fluid, and a base grind comprising cement clinker interground with zeolite. The interground base grind has a bimodal distribution of particle size, and has an exterior surface area greater than 10,000 cm2/g. The cementing operation may be primary cementing or remedial cementing, for example. The gypsum-free cementitious composition may include in the base grind a first pozzolan interground therewith, a first and second pozzolan interground therewith, or a first, second and third pozzolan interground therewith, each pozzolan comprising fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan such as volcanic ash, or a combination thereof When a pozzolan is interground in the base grind, the pozzolan is present in an amount to replace less than 100% of the zeolite of the base grind.
According to one aspect of the present disclosure, the base grind comprises at least 10% to about 50% by weight of pozzolan.
According to another general aspect, the cementitious composition comprises an accelerator in the amount of 0.5% to 10% by weight of the base grind.
In accordance with a still further general aspect, the base grind comprises between from about 2% to 7% by weight of the accelerator.
In accordance with a still further aspect, the process comprises forming the cementitious composition to form a foamed cementitious composition.
A further embodiment of the present invention includes gypsum in the base grind. In this embodiment, the process of performing a cementing operation in a subterranean zone penetrated by a wellbore comprises placing a gypsum-containing cementitious composition into the subterranean zone and allowing the cementitious composition to set therein. The gypsum-containing cementitious composition is also an embodiment of the present invention 3a and comprises a carrier fluid, and a base grind comprising cement clinker interground with zeolite and gypsum wherein the amount of zeolite is greater than 5% to about 95% by weight of the base grind. The interground base grind has a bimodal distribution of particle size and, in a certain embodiment, has an exterior surface area greater than 10,000 cm2/g. The cementing operation may be primary cementing or remedial cementing, for example.
A gypsum-free interground composition is a further embodiment of the present invention. The gypsum-free interground composition comprises a base grind comprising cement clinker interground with zeolite. The interground composition has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 emZ/g.
zeolite (w/w);
FIG. 5. is a micrograph of a composition of 60% cement clinker interground with 40%
zeolite (w/w);
FIG. 6. is a comparison graph of percent volume as a function of particle size for various compositions that include one or more of clinker, zeolite, and gypsum;
FIG. 7. is a comparison graph of percent volume as a function of particle size for various compositions that include one or more of clinker, zeolite, and gypsum;
and FIG. 8. is a comparison graph of compressive strength versus time for various compositions that include one or more of clinker, zeolite, gypsum and cement.
Description Interground zeolite and cement clinker compositions are provided herein for use as a cementitious composition in cementing operations. Additional compositions are provided in which gypsum is interground with zeolite and cement clinker.
Intergrinding zeolite and cement clinker was found to provide a bimodal distribution of particle size in the grind, and increased strength properties of the subsequent cementitious set material as compared to blending separately-ground material, particularly at longer set times.
The increased compressive strength of the interground set material was not observed when hand-ground gypsum was added to the slurry of interground clinker and zeolite material.
Class C cement is essentially ground clinker and gypsum, and slurries of such cement blended with zeolite, while producing early compressive strengths comparable to that of the interground material, does not provide later compressive strengths comparable to that of the interground material.
Increased flow, i.e., better rheology, was observed in those samples lacking gypsum.
Gypsum serves the function of a retarder and in its absence, the aluminate phase hydration reactions appear to occur rapidly. Zeolite has a retarding effect also, however, zeolite appears to provide better results in terms of rheology.
The high compressive strengths at longer set times and the greater flow characteristics of the interground clinker and zeolite material combines two desirable characteristics of a cementitious composition in one material.
The term "cementitious," as used herein, means having the properties of cement. The cementitious materials are suitable for a broad range of cementing applications, in particular, as a replacement for hydraulic cement where cement is to be set in a water environment, for control of timing of strength development, for applications where flowability is particularly desired, and where low density slurries are desired.
.A process of performing a cementing operation in a subterranean zone penetrated by a wellbore is an embodiment of the present invention. The process comprises placing a gypsum-free cementitious composition into the subterranean zone and allowing the cementitious composition to set therein. The gypsum-free cementitious composition is also an embodiment of the present invention and comprises a carrier fluid, and a base grind comprising cement clinker interground with zeolite. The interground base grind has a bimodal distribution of particle size, and has an exterior surface area greater than 10,000 cm2/g. The cementing operation may be primary cementing or remedial cementing, for example. The gypsum-free cementitious composition may include in the base grind a first pozzolan interground therewith, a first and second pozzolan interground therewith, or a first, second and third pozzolan interground therewith, each pozzolan comprising fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan such as volcanic ash, or a combination thereof When a pozzolan is interground in the base grind, the pozzolan is present in an amount to replace less than 100% of the zeolite of the base grind.
According to one aspect of the present disclosure, the base grind comprises at least 10% to about 50% by weight of pozzolan.
According to another general aspect, the cementitious composition comprises an accelerator in the amount of 0.5% to 10% by weight of the base grind.
In accordance with a still further general aspect, the base grind comprises between from about 2% to 7% by weight of the accelerator.
In accordance with a still further aspect, the process comprises forming the cementitious composition to form a foamed cementitious composition.
A further embodiment of the present invention includes gypsum in the base grind. In this embodiment, the process of performing a cementing operation in a subterranean zone penetrated by a wellbore comprises placing a gypsum-containing cementitious composition into the subterranean zone and allowing the cementitious composition to set therein. The gypsum-containing cementitious composition is also an embodiment of the present invention 3a and comprises a carrier fluid, and a base grind comprising cement clinker interground with zeolite and gypsum wherein the amount of zeolite is greater than 5% to about 95% by weight of the base grind. The interground base grind has a bimodal distribution of particle size and, in a certain embodiment, has an exterior surface area greater than 10,000 cm2/g. The cementing operation may be primary cementing or remedial cementing, for example.
A gypsum-free interground composition is a further embodiment of the present invention. The gypsum-free interground composition comprises a base grind comprising cement clinker interground with zeolite. The interground composition has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 emZ/g.
An interground composition comprising gypsum is an embodiment of the present invention. The composition comprises a base grind of cement clinker interground with zeolite and gypsum wherein the amount of zeolite is greater than 5% to about 95% by weight of the base grind. The interground composition has a bimodal distribution of particle size and, in certain embodiments, the interground composition has an exterior surface area greater than 10,000 cm2/g.
Base Grind and Intergrinding: The term "base grind" as used herein means the components that are interground together. For gypsum-free embodiments, the base grind comprises cement clinker and zeolite. For embodiments containing gypsum, the base grind comprises cement clinker, zeolite and gypsum. The base grind in either case may also include one or more pozzolans. The amount of a component of a base grind is based on the weight percent of the base grind.
The term "intergrinding" or "interground" as used herein means using a rod mill or a ball mill, for example, as known by one of ordinary skill in the art to reduce the particle size of the components of the base grind to achieve an exterior surface area and particle size that provides unexpected properties of rheology and compressive strength in a subsequent slurry made therefrom as compared to those properties of a blended composition having the same components. Base grinds of embodiments of the compositions of the present invention have an exterior surface area greater than 10,000 cm2/g or an exterior surface area ranging between any of and including any of 10,100 cm2/g, 10,500 cm2/g, 11,000 cm2/g, 11,500 cm2/g, 12,000 cm2/g, 12,500 cm2/g, 13,000 cm2/g, 13,500 cm2/g, 14,000 cm2/g, 14,500 cm2/g, 15,000 cm2/g, 15,500 cm2/g, and 16,000 cm2/g. Such grinds unexpectedly have a bimodal distribution of particle size as described herein. A mean particle size is between about 10 and 30 microns.
For a base grind of 40% zeolite and 60% cement clinker (w/w) having an exterior surface area of about 14,000 cm2/g, a smaller peak of the bimodal curve has a peak particle size of about 4 microns and the larger peak of the bimodal curve has a peak particle size of about 18 microns.
External surface area is measured using a MASTERSIZER 2000 laser particle size analyzer (Malvern Instruments Ltd., Malvern, UK) according to the manufacturer's instructions. Exterior surface area was determined by laser during the particle size analysis for determining mean and cumulative particle size. Surface area may also be determined using air permeability or nitrogen adsorption, light extinction, light scattering methods, or X-ray methods, techniques that are well known to those of ordinary skill in the art.
Zeolites: Zeolites are porous alumino-silicate minerals that may be either a natural or manmade material. Manmade zeolites are based on the same type of structural cell as natural zeolites, and are composed of aluminosilicate hydrates having the same basic formula as given below. It is understood that as used herein, the term "zeolite" means and encompasses all natural and manmade forms of zeolites. All zeolites are composed of a three-dimensional framework of Si04 and A104 in a tetrahedron, which creates a very high surface area. Cations and water molecules are entrained into the framework. Thus, all zeolites may be represented by the crystallographic unit cell formula:
M./n[(AlO2)a(SiO2)b] - xH2O.
M represents one or more cations such as Na, K, Mg, Ca, Sr, Li or Ba for natural zeolites and NH4, CH3NH3, (CH3)3NH, (CH3)4N, Ga, Ge and P for manmade zeolites; n represents the cation valence; the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5; and x represents the moles of water entrained into the zeolite framework.
Zeolites for use in the compositions of the present embodiments include analcime (hydrated sodium aluminum silicate), bikitaite (lithium aluminum silicate), brewsterite (hydrated strontium barium calcium aluminum silicate), chabazite (hydrated calcium aluminum silicate), clinoptilolite (hydrated sodium aluminum silicate), faujasite (hydrated sodium potassium calcium magnesium aluminum silicate), harmotome (hydrated barium aluminum silicate), heulandite (hydrated sodium calcium aluminum silicate), laumontite (hydrated calcium aluminum silicate), mesolite (hydrated sodium calcium aluminum silicate), natrolite (hydrated sodium aluminum silicate), paulingite (hydrated potassium sodium calcium barium aluminum silicate), phillipsite (hydrated potassium sodium calcium aluminum silicate), scolecite (hydrated calcium aluminum silicate), stellerite (hydrated calcium aluminum silicate), stilbite (hydrated sodium calcium aluminum silicate) or thomsonite (hydrated sodium calcium aluminum silicate), or combinations thereof. In certain embodiments of the invention, the zeolites for use herein include chabazite, clinoptilolite, or a combination thereof.
For the compositions of the present embodiments, zeolite is a component of a base grind. For compositions that are gypsum-free, the amount of zeolite in the base grind is between 0% and 100% by weight. For compositions of the present embodiments that contain gypsum, the amount of zeolite in the base grind is from about 5% to 95% by weight. In additional embodiments of the compositions, zeolite is present in an amount ranging between any of and including any of 10%, 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80%, or 90%
by weight of the base grind.
Cement Clinker.= Cement clinker is the main component in portland cement and is produced by the heat treatment of the raw materials limestone, clay minerals and metals. In general, limestone (calcium carbonate) and clay (containing silicon, aluminum, and iron) in about a 2:1 weight ratio are heated in a kiln. A mixture of several products termed "cement clinker" forms due to chemical reactions that result from the heating process.
Suitable cement clinker for use in the compositions of the present embodiments include Portland cement clinker for each of ASTM Type I, IA, II, III, and V cements, API cement clinker for each of Class A, C, G and H cements and Canadian Type 10 cement clinker. Other suitable cement clinkers include those having high sulfate or moderate sulfate resistance, and those that are non sulfate resistant. In the manufacture of cement, cement clinker is ground with gypsum (hydrated calcium sulfate).
Cement clinker is present in a base grind of the compositions of the present embodiments in an amount of from about 5% to about 95% by weight of the base grind. In embodiments of the invention, cement clinker is present in the base grind in an amount ranging between any of and including any of 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, and 95% by weight of the base grind.
Gypsum: According to certain embodiments, gypsum (hydrated calcium sulfate) is interground with zeolite and pozzolan in the base grind of the compositions.
Gypsum may be present in an amount of from greater than 0% to about 10% by weight of base grind. In further embodiments, gypsum is present in the base grind in an amount ranging between any of and including any of 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, 3.0%, 3.5%, 4.0%, 4.5%, 5.0%, 5.5%, 6.0%, 6.5%, 7.0%, 7.5%, 8.0%, 8.5%, 9.0%, 9.5%, and 10.0% by weight of clinker in the base grind.
A suitable gypsum product is commercially available from Lehigh Inland Cement Limited (Edmonton, Alberta, Canada).
Further Pozzolans as Components of the Base Grind.= Further pozzolans may be included in the base grind such as fly ash (Class C or Class F), slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, a natural pozzolan, or a combination thereof.
The amount of pozzolan present in the base grind replaces zeolite in the base grind in an amount of less than 100% of the zeolite. The amount of each component in such a binary, ternary, or quatemary base grind can be increased or decreased depending upon the properties desired in the product in terms of rheology, improved early strength, compressive strength development, light weight or a combination thereof. Fly ash is commercially available from Ashcor Technologies Limited (Calgary, Alberta, Canada); slag is commercially available from Holcim (Calgary, Alberta, Canada); fumed silica is commercially available from Fritz Industries (Mesquite, Texas, USA) and Elkem Group (Oslo, Norway); diatomaceous earth is commercially available from Western Pozzolan Corp. (Doyle, Nevada, USA);
calcined shale is commercially available from TXI (Houston, Texas, USA); metakaolin is commercially available from ISG Resources (South Jordan, Utah, USA) and Advanced Cement Technologies, LLC. (Blaine, Washington, USA); and rice husk ash is commercially available from Hi Rise Exports Private Ltd. (Calcutta, India) and Kittiya (U-Thaimai, Utaitanee, Thailand).
Optional Additives: Additives known to those of ordinary skill in the art may be included in the cementitious compositions of the present invention. Additives are typically dry blended with the base grind after the base grind is interground or may be added to a cementitious slurry. An additive may comprise an accelerator, a retarder, an activator, a defoamer, silica, a fluid loss control additive, a flow enhancing agent, a dispersant, an extender, a lost circulation control agent, a gas migration agent, an expansive agent, a weight altering agent for increasing or decreasing density or for changing the water requirement, or a combination thereof, for example. Selection of the type and amount of additive largely depends on the nature and composition of the set composition, and those of ordinary skill in the art will understand how to select a suitable type and amount of additive for compositions herein.
Suitable activator additives are catalysts for the setting reaction and may be one or more of lime, lime hydrate, calcium hydroxide, calcium chloride, sodium silicate, sodium fluoride, sodium silicofluoride, magnesium silicofluoride, zinc silicofluoride, sodium carbonate, potassium carbonate, sodium hydroxide, potassium hydroxide, sodium sulfate, or hydrates thereof, for example.
Suitable setting accelerators increase the rate of the setting reaction and include sodium chloride, sodium sulfate, sodium aluminate, sodium carbonate, calcium sulfate, calcium carbonate, aluminum sulfate, potassium sulfate, potassium carbonate and alums, or a combination thereof, for example.
Base Grind and Intergrinding: The term "base grind" as used herein means the components that are interground together. For gypsum-free embodiments, the base grind comprises cement clinker and zeolite. For embodiments containing gypsum, the base grind comprises cement clinker, zeolite and gypsum. The base grind in either case may also include one or more pozzolans. The amount of a component of a base grind is based on the weight percent of the base grind.
The term "intergrinding" or "interground" as used herein means using a rod mill or a ball mill, for example, as known by one of ordinary skill in the art to reduce the particle size of the components of the base grind to achieve an exterior surface area and particle size that provides unexpected properties of rheology and compressive strength in a subsequent slurry made therefrom as compared to those properties of a blended composition having the same components. Base grinds of embodiments of the compositions of the present invention have an exterior surface area greater than 10,000 cm2/g or an exterior surface area ranging between any of and including any of 10,100 cm2/g, 10,500 cm2/g, 11,000 cm2/g, 11,500 cm2/g, 12,000 cm2/g, 12,500 cm2/g, 13,000 cm2/g, 13,500 cm2/g, 14,000 cm2/g, 14,500 cm2/g, 15,000 cm2/g, 15,500 cm2/g, and 16,000 cm2/g. Such grinds unexpectedly have a bimodal distribution of particle size as described herein. A mean particle size is between about 10 and 30 microns.
For a base grind of 40% zeolite and 60% cement clinker (w/w) having an exterior surface area of about 14,000 cm2/g, a smaller peak of the bimodal curve has a peak particle size of about 4 microns and the larger peak of the bimodal curve has a peak particle size of about 18 microns.
External surface area is measured using a MASTERSIZER 2000 laser particle size analyzer (Malvern Instruments Ltd., Malvern, UK) according to the manufacturer's instructions. Exterior surface area was determined by laser during the particle size analysis for determining mean and cumulative particle size. Surface area may also be determined using air permeability or nitrogen adsorption, light extinction, light scattering methods, or X-ray methods, techniques that are well known to those of ordinary skill in the art.
Zeolites: Zeolites are porous alumino-silicate minerals that may be either a natural or manmade material. Manmade zeolites are based on the same type of structural cell as natural zeolites, and are composed of aluminosilicate hydrates having the same basic formula as given below. It is understood that as used herein, the term "zeolite" means and encompasses all natural and manmade forms of zeolites. All zeolites are composed of a three-dimensional framework of Si04 and A104 in a tetrahedron, which creates a very high surface area. Cations and water molecules are entrained into the framework. Thus, all zeolites may be represented by the crystallographic unit cell formula:
M./n[(AlO2)a(SiO2)b] - xH2O.
M represents one or more cations such as Na, K, Mg, Ca, Sr, Li or Ba for natural zeolites and NH4, CH3NH3, (CH3)3NH, (CH3)4N, Ga, Ge and P for manmade zeolites; n represents the cation valence; the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5; and x represents the moles of water entrained into the zeolite framework.
Zeolites for use in the compositions of the present embodiments include analcime (hydrated sodium aluminum silicate), bikitaite (lithium aluminum silicate), brewsterite (hydrated strontium barium calcium aluminum silicate), chabazite (hydrated calcium aluminum silicate), clinoptilolite (hydrated sodium aluminum silicate), faujasite (hydrated sodium potassium calcium magnesium aluminum silicate), harmotome (hydrated barium aluminum silicate), heulandite (hydrated sodium calcium aluminum silicate), laumontite (hydrated calcium aluminum silicate), mesolite (hydrated sodium calcium aluminum silicate), natrolite (hydrated sodium aluminum silicate), paulingite (hydrated potassium sodium calcium barium aluminum silicate), phillipsite (hydrated potassium sodium calcium aluminum silicate), scolecite (hydrated calcium aluminum silicate), stellerite (hydrated calcium aluminum silicate), stilbite (hydrated sodium calcium aluminum silicate) or thomsonite (hydrated sodium calcium aluminum silicate), or combinations thereof. In certain embodiments of the invention, the zeolites for use herein include chabazite, clinoptilolite, or a combination thereof.
For the compositions of the present embodiments, zeolite is a component of a base grind. For compositions that are gypsum-free, the amount of zeolite in the base grind is between 0% and 100% by weight. For compositions of the present embodiments that contain gypsum, the amount of zeolite in the base grind is from about 5% to 95% by weight. In additional embodiments of the compositions, zeolite is present in an amount ranging between any of and including any of 10%, 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80%, or 90%
by weight of the base grind.
Cement Clinker.= Cement clinker is the main component in portland cement and is produced by the heat treatment of the raw materials limestone, clay minerals and metals. In general, limestone (calcium carbonate) and clay (containing silicon, aluminum, and iron) in about a 2:1 weight ratio are heated in a kiln. A mixture of several products termed "cement clinker" forms due to chemical reactions that result from the heating process.
Suitable cement clinker for use in the compositions of the present embodiments include Portland cement clinker for each of ASTM Type I, IA, II, III, and V cements, API cement clinker for each of Class A, C, G and H cements and Canadian Type 10 cement clinker. Other suitable cement clinkers include those having high sulfate or moderate sulfate resistance, and those that are non sulfate resistant. In the manufacture of cement, cement clinker is ground with gypsum (hydrated calcium sulfate).
Cement clinker is present in a base grind of the compositions of the present embodiments in an amount of from about 5% to about 95% by weight of the base grind. In embodiments of the invention, cement clinker is present in the base grind in an amount ranging between any of and including any of 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, and 95% by weight of the base grind.
Gypsum: According to certain embodiments, gypsum (hydrated calcium sulfate) is interground with zeolite and pozzolan in the base grind of the compositions.
Gypsum may be present in an amount of from greater than 0% to about 10% by weight of base grind. In further embodiments, gypsum is present in the base grind in an amount ranging between any of and including any of 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, 3.0%, 3.5%, 4.0%, 4.5%, 5.0%, 5.5%, 6.0%, 6.5%, 7.0%, 7.5%, 8.0%, 8.5%, 9.0%, 9.5%, and 10.0% by weight of clinker in the base grind.
A suitable gypsum product is commercially available from Lehigh Inland Cement Limited (Edmonton, Alberta, Canada).
Further Pozzolans as Components of the Base Grind.= Further pozzolans may be included in the base grind such as fly ash (Class C or Class F), slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, a natural pozzolan, or a combination thereof.
The amount of pozzolan present in the base grind replaces zeolite in the base grind in an amount of less than 100% of the zeolite. The amount of each component in such a binary, ternary, or quatemary base grind can be increased or decreased depending upon the properties desired in the product in terms of rheology, improved early strength, compressive strength development, light weight or a combination thereof. Fly ash is commercially available from Ashcor Technologies Limited (Calgary, Alberta, Canada); slag is commercially available from Holcim (Calgary, Alberta, Canada); fumed silica is commercially available from Fritz Industries (Mesquite, Texas, USA) and Elkem Group (Oslo, Norway); diatomaceous earth is commercially available from Western Pozzolan Corp. (Doyle, Nevada, USA);
calcined shale is commercially available from TXI (Houston, Texas, USA); metakaolin is commercially available from ISG Resources (South Jordan, Utah, USA) and Advanced Cement Technologies, LLC. (Blaine, Washington, USA); and rice husk ash is commercially available from Hi Rise Exports Private Ltd. (Calcutta, India) and Kittiya (U-Thaimai, Utaitanee, Thailand).
Optional Additives: Additives known to those of ordinary skill in the art may be included in the cementitious compositions of the present invention. Additives are typically dry blended with the base grind after the base grind is interground or may be added to a cementitious slurry. An additive may comprise an accelerator, a retarder, an activator, a defoamer, silica, a fluid loss control additive, a flow enhancing agent, a dispersant, an extender, a lost circulation control agent, a gas migration agent, an expansive agent, a weight altering agent for increasing or decreasing density or for changing the water requirement, or a combination thereof, for example. Selection of the type and amount of additive largely depends on the nature and composition of the set composition, and those of ordinary skill in the art will understand how to select a suitable type and amount of additive for compositions herein.
Suitable activator additives are catalysts for the setting reaction and may be one or more of lime, lime hydrate, calcium hydroxide, calcium chloride, sodium silicate, sodium fluoride, sodium silicofluoride, magnesium silicofluoride, zinc silicofluoride, sodium carbonate, potassium carbonate, sodium hydroxide, potassium hydroxide, sodium sulfate, or hydrates thereof, for example.
Suitable setting accelerators increase the rate of the setting reaction and include sodium chloride, sodium sulfate, sodium aluminate, sodium carbonate, calcium sulfate, calcium carbonate, aluminum sulfate, potassium sulfate, potassium carbonate and alums, or a combination thereof, for example.
Suitable retarders slow the setting time of a cementitious composition, thereby allowing for control of the setting time of such a composition. Controlling the setting time is desirable to allow flexibility to adjust to wellbore conditions, or to adjust for adequate removal of drilling or spacer fluids. Suitable retarders include a lignosulfonate, an organic acid having an a-hydroxy group such as citric acid, tartaric acid or gluconic acid, salts thereof, or a combination thereof, for example. Further suitable carboxylic acids that retard the setting time include carboxylic acids such as malic acid, lactic acid, combinations thereof, as well as alkaline earth metal salts thereof such as calcium, potassium, or barium salts, and the like. The salt of the organic acid may have a cation containing an element of the periodic chart listed in Group I or in Group II.
Suitable defoamers or dispersants include polypropylene glycol, polypropylene glycol on diatomaceous earth, or a mixture of polypropylene glycol, olefm oil and hydrophobically modified silica, salts of sulfonated naphthalene-formaldehyde condensate, salts of sulfonated naphthalene-formaldehyde condensates combined with polyvinylpyrolidone, salts of sulfonated melamine-formaldehyde condensates, salts of polyether polycarboxylate, sulfonic-acid esters, carbohydrate esters or modified lignosulfonates, for example. A salt may be a calcium salt or a sodium salt or a combination thereof.
Carrier Fluids: Carrier fluids suitable for use in compositions of the present embodiments include aqueous fluids, oil-based and synthetic-based fluids, emulsions, or mixtures thereof.
Exemplary aqueous fluids include but are not limited to water and water-based gels.
When the carrier fluid comprises water, the water can be fresh water, unsaturated salt solution, including brines and seawater, and saturated salt solution. Exemplary oil-based fluids include but are not limited to canola oil, kerosene, diesel oil, fish oil, mineral oil, sunflower oil, corn oil, soy oil, olive oil, cottonseed oil, peanut oil and paraffin. Exemplary synthetic-based fluids include but are not limited to esters, olefins or ethers, e.g., esters having a C2-C12 alcohol portion and a C16-C24 carboxylic acid portion, olefms having a C6-C18 linear internal portion, or ethers having a C6-C24 portion.
The carrier fluid is present in an amount of from about 0.18 cubic meters to about 12 cubic meters of carrier fluid per metric tonne of components of the base grind. In further embodiments, the carrier fluid is present in an amount ranging between any of and including any of 0.2 m3, 0.5 m3, 1.0 m3, 1.5 m3, 2.0 m3, 2.5 m3, 3.0 m3, 3.5 m3, 4.0 m3, 4.5 m3, 5.0 m3, 5.5 m3, 6.0 m3, 6.5 m3, 7.0 m3, 7.5 m3, 8.0 m3, 8.5 m3, 9.0 m3, 9.5 m3, 10.0 m3, 10.5 m3, 11.0 m3, 11.5 m3, and 12.0 m3 of carrier fluid per metric tonne of components of the base grind.
Those of ordinary skill in the art will understand that the carrier fluid for the compositions as provided herein depends upon the properties desired for the compositions, as well as the cost, availability, temperature, stability, viscosity, clarity, and the like of the carrier fluid, and further that non-aqueous carrier fluids are used when the composition is expected to be exposed to an aqueous fluid in the well for the composition to set. For example, such aqueous fluids may come from the cementitious slurry or from the subterranean formation.
Setting Conditions: Setting of the cementitious compositions of the present embodiments may occur under a variety of conditions including variations in time and temperature. In general, the rate of compressive strength development increases with temperature. Setting temperatures of about 0 F to about 572 F (-17.8 C to 300 C) are appropriate for setting of the present compositions. In further embodiments, a temperature ranging between any of and including any of 20 F (-6.7 C), 30 F (-1.1 C), 50 F (10.0 C), 70 F (21.1 C), 90 F (32.2 C), 110 F (43.3 C), 130 F (54.4 C), 140 F
(60.0 C), 150 F
(65.6 C), 160 F (71.1 C), 170 F (76.7 C), 180 F (82.2 C), 190 F (87.8 C), 200 F (93.3 C), 220 F (107.2 C), 250 F (121.1 C), 300 F (148.9 C), 350 F (176.7 C), 400 F (204.4 C), 450 F (232.2 C), 500 F (260 C), and 550 F (287.8 C) is appropriate for setting of the present compositions. A target setting time for a composition of the present embodiments is adjusted to between, for example, one to 14 days, by adjusting the amounts of the components described herein depending upon circumstances surrounding the drilling operations. A target setting time for a cementitious composition of the present invention may be adjusted such that the composition remains fluid for about 0.5 hours to about 8 hours or about 12 hours to allow placement behind casing materials, and then sets within an acceptable time period. The compositions may comprise a slurry density of about 900 kg/m3 to about 2400 kg/m3 or a slurry density ranging between any of and including any of 1000 kg/m3, 1200 kg/m3, 1400 kg/m3, 1600 kg/m3, 1800 kg/m3, 2000 kg/m3, and 2200 kg/m3. In one embodiment, the slurry density is about 1400 kg/m3.
A process of preparing a gypsum-free cementitious composition is an embodiment of the present invention. The process comprises intergrinding a composition comprising cement clinker and zeolite to form a base grind; and mixing the base grind with a carrier fluid to form a slurry. The base grind has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 cm2/g. In a further embodiment, the process includes allowing the slurry to set.
Another embodiment of the present invention is a process of preparing a cementitious composition comprising intergrinding a composition comprising cement clinker, zeolite, and gypsum to form a base grind wherein the zeolite is present in the base grind in an amount of from about 5% to about 95% by weight; and mixing the base grind with a carrier fluid to form a slurry. The base grind has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 cm2/g. In a further embodiment, the process includes allowing the slurry to set.
The following examples are illustrative of the processes and compositions discussed above.
A MASTERSIZER 2000 laser particle size analyzer (Malvern Instruments Ltd., Malvern, UK) was used for determining mean and cumulative particle size according to the manufacturer's instructions. Exterior surface area was determined by laser during the particle size analysis. The specific total exterior and interior surface area was determined by a nitrogen-adsorption analysis using the Brunauer-Emmett-Teller Method, as described by Branauer et al. (J. Am. Chem. Soc., 60, 309-19, 1938).
Slurries in the following examples were prepared, and compressive strength data were determined by Non-Destructive Sonic Testing as set forth in API Specification lOB 22nd Edition, 1997, of the American Petroleum Institute.
Free water data were gathered according to Section 15.5 of Addendum 2 of the API
Specification lOB 22nd Edition, 1997, of the American Petroleum Institute.
Generally, according to the API Specification, 250 ml of each cement composition was poured into its own 250 ml graduated glass cylinder and then sealed with a plastic film wrap to prevent evaporation. A two hour test period was then initiated, in which the graduated cylinders were left standing. After two hours, the free fluid that had gathered on top of each cement composition inside the cylinder was measured. The percent of free fluid was calculated as the measured milliliters of free fluid multiplied by 100 and then divided by the initial 250 milliliters of the cement composition.
Rheology results were obtained generally according to the procedures set forth in Section 12 of the API Specification RP IOB, 22nd Edition, 1997, of the American Petroleum Institute. Viscosity (dial reading) of the cement composition was measured using a Fann Model 35 viscometer. The viscosity was taken as the measurement of the dial reading on the Fann Model 35 at the different rotational speeds of 300 to 3 RPM, and at room temperature.
For example, the Fann Viscometer is rotated at 300 RPM (revolutions per minute) for 60 seconds and a value on the dial is read, the speed is then changed to 200 RPM
and the new value on the dial reading taken. There are a number of theoretical models known to those of ordinary skill in the art that can be used to convert the values from the dial readings at the different RPM's into viscosity (centipoises). In addition, different viscometer models use different RPM values, thus, in some instances, a measurement is not available at a particular RPM value.
EXAMPLE 1. Interground Cement Clinker and Zeolite The present example provides a grind curve of particle size as a function of grind time for a composition of 60% cement clinker interground with 40% zeolite (w/w), designated herein as Composition 1. Cement clinker was obtained from Lehigh Inland Cement Limited (Edmonton, Alberta, Canada). Zeolite (FDP-C661-02, a clinoptilolite) was obtained from C2C
Zeolite Corporation (Calgary, Canada), and mined from near Princeton, British Columbia.
Cement clinker does not include gypsum. Therefore, the composition of the present example does not include gypsum.
Zeolite was dried for at least about 24 hours at 120 C prior to grinding.
Cement clinker was crushed to approximately 10-mesh using a jaw crusher.
Representative 1 kg samples of 60% cement clinker and 40% zeolite (w/w) were dry ground in steel rod mills to determine a grind curve, i.e., a particle size as a function of grind time. A
representative 1 to 2 gram portion of the grind tests was analyzed using a MASTERSIZER 2000 laser particle size analyzer (Malvem Instruments Ltd., Malvem, UK). A mean particle size of 10.1 m was achieved at 74 minutes of grinding time.
Further, the specific surface area of a 2-gram portion from a grind having a mean particle size of 11.1 m was determined by two methods. The specific exterior surface area determined by laser during the particle size analysis (referred to as a "wet process") was 13,100 cm2/g. The specific total exterior and interior surface area determined by the nitrogen-adsorption analysis of the Branauer-Emmett-Teller Method (dry process) was 259,400 cm2/g.
A summary of the grind curve results is set forth in by Table 1 and FIG. 1.
Table 1. Properties of Interground Composition 1 with Increasing Grinding Time Grind Time Mean Particle Size Exterior Surface Exterior and (minutes) (pm) Area - (cm2/g) Interior Surface Area - (cm / ) 29.1 07,800 -17.4 10,100 -40 12.4 11,700 -54 11.1 13,100 259,400 four determinations:
Suitable defoamers or dispersants include polypropylene glycol, polypropylene glycol on diatomaceous earth, or a mixture of polypropylene glycol, olefm oil and hydrophobically modified silica, salts of sulfonated naphthalene-formaldehyde condensate, salts of sulfonated naphthalene-formaldehyde condensates combined with polyvinylpyrolidone, salts of sulfonated melamine-formaldehyde condensates, salts of polyether polycarboxylate, sulfonic-acid esters, carbohydrate esters or modified lignosulfonates, for example. A salt may be a calcium salt or a sodium salt or a combination thereof.
Carrier Fluids: Carrier fluids suitable for use in compositions of the present embodiments include aqueous fluids, oil-based and synthetic-based fluids, emulsions, or mixtures thereof.
Exemplary aqueous fluids include but are not limited to water and water-based gels.
When the carrier fluid comprises water, the water can be fresh water, unsaturated salt solution, including brines and seawater, and saturated salt solution. Exemplary oil-based fluids include but are not limited to canola oil, kerosene, diesel oil, fish oil, mineral oil, sunflower oil, corn oil, soy oil, olive oil, cottonseed oil, peanut oil and paraffin. Exemplary synthetic-based fluids include but are not limited to esters, olefins or ethers, e.g., esters having a C2-C12 alcohol portion and a C16-C24 carboxylic acid portion, olefms having a C6-C18 linear internal portion, or ethers having a C6-C24 portion.
The carrier fluid is present in an amount of from about 0.18 cubic meters to about 12 cubic meters of carrier fluid per metric tonne of components of the base grind. In further embodiments, the carrier fluid is present in an amount ranging between any of and including any of 0.2 m3, 0.5 m3, 1.0 m3, 1.5 m3, 2.0 m3, 2.5 m3, 3.0 m3, 3.5 m3, 4.0 m3, 4.5 m3, 5.0 m3, 5.5 m3, 6.0 m3, 6.5 m3, 7.0 m3, 7.5 m3, 8.0 m3, 8.5 m3, 9.0 m3, 9.5 m3, 10.0 m3, 10.5 m3, 11.0 m3, 11.5 m3, and 12.0 m3 of carrier fluid per metric tonne of components of the base grind.
Those of ordinary skill in the art will understand that the carrier fluid for the compositions as provided herein depends upon the properties desired for the compositions, as well as the cost, availability, temperature, stability, viscosity, clarity, and the like of the carrier fluid, and further that non-aqueous carrier fluids are used when the composition is expected to be exposed to an aqueous fluid in the well for the composition to set. For example, such aqueous fluids may come from the cementitious slurry or from the subterranean formation.
Setting Conditions: Setting of the cementitious compositions of the present embodiments may occur under a variety of conditions including variations in time and temperature. In general, the rate of compressive strength development increases with temperature. Setting temperatures of about 0 F to about 572 F (-17.8 C to 300 C) are appropriate for setting of the present compositions. In further embodiments, a temperature ranging between any of and including any of 20 F (-6.7 C), 30 F (-1.1 C), 50 F (10.0 C), 70 F (21.1 C), 90 F (32.2 C), 110 F (43.3 C), 130 F (54.4 C), 140 F
(60.0 C), 150 F
(65.6 C), 160 F (71.1 C), 170 F (76.7 C), 180 F (82.2 C), 190 F (87.8 C), 200 F (93.3 C), 220 F (107.2 C), 250 F (121.1 C), 300 F (148.9 C), 350 F (176.7 C), 400 F (204.4 C), 450 F (232.2 C), 500 F (260 C), and 550 F (287.8 C) is appropriate for setting of the present compositions. A target setting time for a composition of the present embodiments is adjusted to between, for example, one to 14 days, by adjusting the amounts of the components described herein depending upon circumstances surrounding the drilling operations. A target setting time for a cementitious composition of the present invention may be adjusted such that the composition remains fluid for about 0.5 hours to about 8 hours or about 12 hours to allow placement behind casing materials, and then sets within an acceptable time period. The compositions may comprise a slurry density of about 900 kg/m3 to about 2400 kg/m3 or a slurry density ranging between any of and including any of 1000 kg/m3, 1200 kg/m3, 1400 kg/m3, 1600 kg/m3, 1800 kg/m3, 2000 kg/m3, and 2200 kg/m3. In one embodiment, the slurry density is about 1400 kg/m3.
A process of preparing a gypsum-free cementitious composition is an embodiment of the present invention. The process comprises intergrinding a composition comprising cement clinker and zeolite to form a base grind; and mixing the base grind with a carrier fluid to form a slurry. The base grind has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 cm2/g. In a further embodiment, the process includes allowing the slurry to set.
Another embodiment of the present invention is a process of preparing a cementitious composition comprising intergrinding a composition comprising cement clinker, zeolite, and gypsum to form a base grind wherein the zeolite is present in the base grind in an amount of from about 5% to about 95% by weight; and mixing the base grind with a carrier fluid to form a slurry. The base grind has a bimodal distribution of particle size and, in certain embodiments, has an exterior surface area greater than 10,000 cm2/g. In a further embodiment, the process includes allowing the slurry to set.
The following examples are illustrative of the processes and compositions discussed above.
A MASTERSIZER 2000 laser particle size analyzer (Malvern Instruments Ltd., Malvern, UK) was used for determining mean and cumulative particle size according to the manufacturer's instructions. Exterior surface area was determined by laser during the particle size analysis. The specific total exterior and interior surface area was determined by a nitrogen-adsorption analysis using the Brunauer-Emmett-Teller Method, as described by Branauer et al. (J. Am. Chem. Soc., 60, 309-19, 1938).
Slurries in the following examples were prepared, and compressive strength data were determined by Non-Destructive Sonic Testing as set forth in API Specification lOB 22nd Edition, 1997, of the American Petroleum Institute.
Free water data were gathered according to Section 15.5 of Addendum 2 of the API
Specification lOB 22nd Edition, 1997, of the American Petroleum Institute.
Generally, according to the API Specification, 250 ml of each cement composition was poured into its own 250 ml graduated glass cylinder and then sealed with a plastic film wrap to prevent evaporation. A two hour test period was then initiated, in which the graduated cylinders were left standing. After two hours, the free fluid that had gathered on top of each cement composition inside the cylinder was measured. The percent of free fluid was calculated as the measured milliliters of free fluid multiplied by 100 and then divided by the initial 250 milliliters of the cement composition.
Rheology results were obtained generally according to the procedures set forth in Section 12 of the API Specification RP IOB, 22nd Edition, 1997, of the American Petroleum Institute. Viscosity (dial reading) of the cement composition was measured using a Fann Model 35 viscometer. The viscosity was taken as the measurement of the dial reading on the Fann Model 35 at the different rotational speeds of 300 to 3 RPM, and at room temperature.
For example, the Fann Viscometer is rotated at 300 RPM (revolutions per minute) for 60 seconds and a value on the dial is read, the speed is then changed to 200 RPM
and the new value on the dial reading taken. There are a number of theoretical models known to those of ordinary skill in the art that can be used to convert the values from the dial readings at the different RPM's into viscosity (centipoises). In addition, different viscometer models use different RPM values, thus, in some instances, a measurement is not available at a particular RPM value.
EXAMPLE 1. Interground Cement Clinker and Zeolite The present example provides a grind curve of particle size as a function of grind time for a composition of 60% cement clinker interground with 40% zeolite (w/w), designated herein as Composition 1. Cement clinker was obtained from Lehigh Inland Cement Limited (Edmonton, Alberta, Canada). Zeolite (FDP-C661-02, a clinoptilolite) was obtained from C2C
Zeolite Corporation (Calgary, Canada), and mined from near Princeton, British Columbia.
Cement clinker does not include gypsum. Therefore, the composition of the present example does not include gypsum.
Zeolite was dried for at least about 24 hours at 120 C prior to grinding.
Cement clinker was crushed to approximately 10-mesh using a jaw crusher.
Representative 1 kg samples of 60% cement clinker and 40% zeolite (w/w) were dry ground in steel rod mills to determine a grind curve, i.e., a particle size as a function of grind time. A
representative 1 to 2 gram portion of the grind tests was analyzed using a MASTERSIZER 2000 laser particle size analyzer (Malvem Instruments Ltd., Malvem, UK). A mean particle size of 10.1 m was achieved at 74 minutes of grinding time.
Further, the specific surface area of a 2-gram portion from a grind having a mean particle size of 11.1 m was determined by two methods. The specific exterior surface area determined by laser during the particle size analysis (referred to as a "wet process") was 13,100 cm2/g. The specific total exterior and interior surface area determined by the nitrogen-adsorption analysis of the Branauer-Emmett-Teller Method (dry process) was 259,400 cm2/g.
A summary of the grind curve results is set forth in by Table 1 and FIG. 1.
Table 1. Properties of Interground Composition 1 with Increasing Grinding Time Grind Time Mean Particle Size Exterior Surface Exterior and (minutes) (pm) Area - (cm2/g) Interior Surface Area - (cm / ) 29.1 07,800 -17.4 10,100 -40 12.4 11,700 -54 11.1 13,100 259,400 four determinations:
10.1 74 10.8 14,100 -11.0 11.1 ave. 10.8 90 9.0 14,900 -The data of Table 1 and FIG. 1 demonstrate that as grind time increases, the mean particle size decreases and approaches a plateau. Exterior surface area also increases with grind time and approaches a plateau as shown in Table 1.
FIG. 2 shows a cumulative particle size distribution as a function of grinding time of Composition 1. As grind time increases, cumulative particle size distribution becomes more uniform, i.e., narrower or tighter.
FIG. 3 shows the particle size distribution at grinding times of 10 minutes, 20 minutes, 40 minutes, 54 minutes, 74 minutes, and 90 minutes for Composition 1. A
bimodal distribution of particle size is more prominent with increased grinding time.
The peak particle size for the smaller sized peak at a grind time of 74 minutes appears to be about 3.8 m, and the peak particle size for the larger sized peak for the same grind time appears to be about 20 m, while the mean particle size for a 74 minute grind time is 10.1 m. As shown in FIG. 7 and described below, the smaller peak is likely to represent predominantly zeolite and the larger peak is likely to represent predominantly cement clinker.
The specific total exterior and interior surface area of a degassed sample (1.6691 g) ground for 54 minutes (mean particle size of 11.143 m) was determined using the nitrogen-adsorption analysis (a "dry process"). The total surface area was recorded as 259,400 cm2/g as shown in Table 1.
A measurement of the volume of gas adsorbed as a function of pressure was also made using the Brunauer-Emmett-Teller method cited above. As relative pressure is increased on a 54 minute ground sample (mean particle size of 11.1 m), and then subsequently decreased, a gap in the volume of gas adsorbed between relative pressure P/Po values of 0.4 and 0.9 was demonstrated. This gap indicates the presence of internal mesopores in the sample and that the gas takes more time to be released from the internal pores.
A pore volume histogram was also done on a 54 minute ground sample (mean particle size of 11.1 m), by measuring pore volume in cc/g versus pore width in angstroms. A
bimodal distribution of pore sizes was observed.
FIG. 4 and FIG. 5 show micrographs of Composition 1 for a 74 minute grind. The distance between the arrows symbolizes a distance of 100 microns. Measurements of particle size of these samples resulted in a determination of mean particle size as 7.6 pm. The difference between this measurement and that of the particle size analyzer is likely due to a smaller sample size.
The data of the present example demonstrate that an interground composition of zeolite and cement clinker provides a bimodal distribution of particle sizes, that mean particle size decreases with increasing grinding time, that exterior surface area increases with increased grinding time, and that the composition contains internal mesopores that also have a bimodal distribution of pore size.
EXAMPLE 2. Interground vs. Blended, Separately Ground Compositions The present example relates to the properties of interground cement clinker and zeolite as compared to the properties of blended, separately ground cement clinker and zeolite.
The interground cement clinker and zeolite sample for Examples 2 through 4 herein is the 74 minute grind as described in Example 1 and is designated Composition 1.
The blended sample is a mixture of separately ground clinker and separately ground zeolite. Since the bimodal distribution of particle size of Composition 1 has two peaks of about 3.8 pm and about 20 m (likely predominantly zeolite and clinker, respectively) the separately ground clinker was ground to an approximate particle size of about 20 m and the zeolite was separately ground to a particle size of about 5.8 m. The separately ground zeolite has a bimodal distribution of peak particle size of about 3.3 m and 15.1 pm as discussed below for FIG. 7. The separately ground samples were then mixed in a weight/weight ratio of 60% clinker and 40% zeolite. This composition was designated as Composition 2.
Separately ground clinker was designated as Composition 3.
Separately ground zeolite was designated as Composition 4.
Table 2 provides particle size, surface area, and grind time for interground (Composition 1) vs. separately ground (Composition 2) compositions of the present example, for ground 100% clinker (Composition 3), and for ground 100% zeolite (Composition 4). The ground clinker Composition 3 was determined in two separate 1 kg grinds.
Table 2. Properties of Interground Composition 1 and Blended Separately Ground Composition 2.
Composition Sample Particle Size Surface area Grind time No. ( ) (cm2/g) (min) 1 Interground 60% clinker and 10.1 14100 74 40% zeolite 2 Blended (separately ground) 9.8 14900 -60% clinker, 40% zeolite 3 100% ground clinker 18'0' 10200, 10700 105, 105 18.0 4 100% ground zeolite 5.8 19000 130 FIG. 6 provides a comparison of cumulative particle size distribution for Compositions 1-4. The interground clinker and zeolite (Composition 1), and separately ground clinker and zeolite (Composition 2) have essentially identical cumulative particle size distributions, which distribution differs both from that of 100% ground zeolite, and that of 100%
ground clinker.
The essentially identical cumulative particle size distributions indicate that particle size is controlled for further comparison of properties of the two compositions. The data of Table 2 further support this conclusion in that the particle size of the blended sample, while slightly lower than that of the interground sample, nevertheless provides a good control for comparing the two types of compositions.
EXAMPLE 3. Presence or Absence of Gypsum The present example relates to the properties of three compositions:
interground cement clinker and zeolite, Composition 1; interground cement clinker, zeolite, and gypsum, Composition 5; and an interground cement clinker and zeolite composition (i.e., Composition 1) blended with hand-ground gypsum, Composition 7. The hand-ground gypsum had been ground and sieved to a particle size of about 168 m. The amount of each ingredient by weight, the particle size, the surface area, and grind time for Compositions 1, 5, and 7 are provided in Table 3. The amount of gypsum provided the same ratio of clinker to gypsum for Compositions 5 and 7. Duplicate determinations were carried out on Composition 5.
Table 3. Compositions With and Without Gypsum Composition article Siz Surface No. Sample (~) area Grind time (min) (cm/) 1 Interground 60% clinker and 10.1 14,100 74 40% zeolite 5 Interground 55.8% clinker, 40% 10.4, 14,400, 105,105 zeolite and 4.2% gypsum 10.5 14,700 Interground composition 1, blended with hand-ground 7 gypsum 4.52% by weight of 13.0 11,500 -Com osition 1.
The interground Compositions 1 and 5 compare favorably in particle size and surface area. The difference in grind time to achieve a particle size of about 10 microns is likely attributable to different operators and mechanical slippage during the grind.
FIG. 6 provides a comparison of cumulative particle size distribution and FIG. 7 provides a comparison of particle size distribution, each for Compositions 1, 5 and 7. Compositions 1, 5 and 7 have comparable bimodal distributions of particle size which distributions both differ from that of 100% ground zeolite; and that of 100% ground clinker. Therefore, the compositions have essentially identical particle size indicating that particle size is essentially controlled for comparison of further properties of the three compositions.
EXAMPLE 4. Properties of Cementitious Compositions, Interground vs. Blended, and With and Without Gypsum The present example relates to properties of cementitious compositions of interground as compared to separately ground and blended zeolite and cement clinker compositions, with or without gypsum.
The cementitious compositions were formed by mixing the components in the amounts set forth in Table 4 and additives were added by weight of components according to the methods of API Specification RP IOB, 22nd Edition, 1997, of the American Petroleum Institute. Sodium sulfate (Na2SO4) and sodium carbonate (Na2CO3) are commercially available and were obtained from Sodium Solutions (Edmonton, Canada) under the trade names CA-661 and K-35, respectively. A defoamer, containing internal olefin oil, polypropylene glycol, hydrophobically modified silica and diatomaceous earth, is commercially available and was obtained from Halliburton Energy Services (Duncan, OK), under the trade name D-Air 3000. Duplicate determinations of compressive strength were carried out for Compositions 1 and 5.
Table 4. Cementitious Compositions3 Cementitious Components (w/w) Additives (bwoc Composition Class C Clinker, No. cement2 Type 10 Zeolite Gypsum Na2SO4 Na2CO3 D.
_ Interground 60% clinker 1 and 40% zeolite - 4.5% 2.25%
separately separately 2 - ground 60% o%d - 4.5% 2.25%
clinker zeolite - Interground 55.8% type 10 clink5r, 40% 4.5% 2.25%
zeolite, and 4.2% gypsum 6 60.0% - 40% - 4.5% 2.25%
hand-ground, 7 - Interground 60% clinker 4.52% by 4.5% 2.25%
and 40% zeolite weight of interground material5 By weight of total components 2 Class C cement is ground clinker and gypsum in a w/w ratio of about 100:7 3 All cementitious compositions of Table 4 have a slurry density of 1400 kg/m3 4 Cubic meters of water per metric ton of total components as components are set forth in Table 4.
5 The amount of gypsum is about 7% in weight relation to cement clinker. This approximates the amount of gypsum in Class C cement for comparison purposes.
Compressive strength, rheology and free fluid were determined as described above.
Exterior surface area was determined by the laser process as described in Example 1. The temperature for measurement of rheology and free water is at about room temperature in order to simulate manufacturing conditions. The temperature for measurement of compressive strength is somewhat higher in order to simulate downhole conditions where the pumped compositions are warmed by the downhole environment.
A comparison of the compressive strength versus time of setting for the five compositions of Table 4 is provided by FIG. 8 and Table 5. The data obtained from interground Compositions 1, and 5 as compared to blended Compositions 2 and 6 demonstrate that the interground compositions appear to have greater long-term compressive strength than do the blended compositions beginning at a set time of about 40 hours.
Further, the data obtained from interground Composition 5 having gypsum present as compared to the data from interground compositions not having gypsum present 1 demonstrate that the intergrinding without gypsum provides better compressive strength.
A free water test at room temperature and an angle of deviation of zero degrees provided a trace of free water in 250 mL for Compositions 1 and 2 as summarized in Table 5.
Free water excess, i.e., greater than about 2% for downhole applications, indicates separation and likely ensuing problems in a wellbore.
Rheology dial readings were recorded as described above and also at 300, 200, 100, 6 and 3 RPM, then increasing to 6, 100, 200 and then to 300 RPM at 20-second intervals.
Rheological data for the compositions of this example are summarized in Table 5. The data demonstrate that the compositions without gypsum have a greater ability to flow than the compositions with gypsum.
Table 5. Properties of Cementitious Compositions Free Rheology Results Compressive Strength Water Comp Dial Reading, - 22 C - 25 C - 22 C
. No. Time to Time to Final 0.35 MPa 3.5 MPa MPa (psi);
300 200 100 6 3 (50 psi) (500 psi) at 120 h (mL/
RPM RPM RPM RPM RPM Hr: Min Hr: Min 250mL) 50:45 6.20 (900) 1 34/32 30/31 28/29 25/25 25 12:08 (ave) (ave) (ave) Trace 2 29/27 24/22 24/20 13/14 12 11:40 60:21 5.03 (730) Trace 52:31 6.68 (970) 55/58 50/53 44/45 31/27 25 13:02 (ave) (ave) (ave) 0 6 50/43 40/38 33/31 23/22 19 9:51 63:35 5.17 (750) 0 7 43/42 38/38 32/32 22/21 16/16 20:55 70:50 5.17 (750) 0 As a control, neat clinker was blended with water in a beaker. Small clumps of material formed in the bottom of the beaker and generated heat immediately.
After about 30 minutes, the remaining slurry was thick but movable. Class C cement was also prepared.
However, no clumping, heat or increase in consistency occurred in the same time period.
Adding water to the ground clinker produced the same results as adding ground clinker to water.
Other embodiments of the present invention will be apparent to those skilled in the art from a consideration of this specification or practice of the embodiments disclosed herein. However, the foregoing specification is considered merely exemplary of the present invention with the true scope and spirit of the invention being indicated by the following claims.
The references cited herein, to the extent that they provide exemplary procedural or other details supplementary to those set forth herein, are specifically incorporated by reference.
As used herein and unless otherwise indicated, the terms "a" and "an" are taken to mean "one", "at least one" or "one or more".
FIG. 2 shows a cumulative particle size distribution as a function of grinding time of Composition 1. As grind time increases, cumulative particle size distribution becomes more uniform, i.e., narrower or tighter.
FIG. 3 shows the particle size distribution at grinding times of 10 minutes, 20 minutes, 40 minutes, 54 minutes, 74 minutes, and 90 minutes for Composition 1. A
bimodal distribution of particle size is more prominent with increased grinding time.
The peak particle size for the smaller sized peak at a grind time of 74 minutes appears to be about 3.8 m, and the peak particle size for the larger sized peak for the same grind time appears to be about 20 m, while the mean particle size for a 74 minute grind time is 10.1 m. As shown in FIG. 7 and described below, the smaller peak is likely to represent predominantly zeolite and the larger peak is likely to represent predominantly cement clinker.
The specific total exterior and interior surface area of a degassed sample (1.6691 g) ground for 54 minutes (mean particle size of 11.143 m) was determined using the nitrogen-adsorption analysis (a "dry process"). The total surface area was recorded as 259,400 cm2/g as shown in Table 1.
A measurement of the volume of gas adsorbed as a function of pressure was also made using the Brunauer-Emmett-Teller method cited above. As relative pressure is increased on a 54 minute ground sample (mean particle size of 11.1 m), and then subsequently decreased, a gap in the volume of gas adsorbed between relative pressure P/Po values of 0.4 and 0.9 was demonstrated. This gap indicates the presence of internal mesopores in the sample and that the gas takes more time to be released from the internal pores.
A pore volume histogram was also done on a 54 minute ground sample (mean particle size of 11.1 m), by measuring pore volume in cc/g versus pore width in angstroms. A
bimodal distribution of pore sizes was observed.
FIG. 4 and FIG. 5 show micrographs of Composition 1 for a 74 minute grind. The distance between the arrows symbolizes a distance of 100 microns. Measurements of particle size of these samples resulted in a determination of mean particle size as 7.6 pm. The difference between this measurement and that of the particle size analyzer is likely due to a smaller sample size.
The data of the present example demonstrate that an interground composition of zeolite and cement clinker provides a bimodal distribution of particle sizes, that mean particle size decreases with increasing grinding time, that exterior surface area increases with increased grinding time, and that the composition contains internal mesopores that also have a bimodal distribution of pore size.
EXAMPLE 2. Interground vs. Blended, Separately Ground Compositions The present example relates to the properties of interground cement clinker and zeolite as compared to the properties of blended, separately ground cement clinker and zeolite.
The interground cement clinker and zeolite sample for Examples 2 through 4 herein is the 74 minute grind as described in Example 1 and is designated Composition 1.
The blended sample is a mixture of separately ground clinker and separately ground zeolite. Since the bimodal distribution of particle size of Composition 1 has two peaks of about 3.8 pm and about 20 m (likely predominantly zeolite and clinker, respectively) the separately ground clinker was ground to an approximate particle size of about 20 m and the zeolite was separately ground to a particle size of about 5.8 m. The separately ground zeolite has a bimodal distribution of peak particle size of about 3.3 m and 15.1 pm as discussed below for FIG. 7. The separately ground samples were then mixed in a weight/weight ratio of 60% clinker and 40% zeolite. This composition was designated as Composition 2.
Separately ground clinker was designated as Composition 3.
Separately ground zeolite was designated as Composition 4.
Table 2 provides particle size, surface area, and grind time for interground (Composition 1) vs. separately ground (Composition 2) compositions of the present example, for ground 100% clinker (Composition 3), and for ground 100% zeolite (Composition 4). The ground clinker Composition 3 was determined in two separate 1 kg grinds.
Table 2. Properties of Interground Composition 1 and Blended Separately Ground Composition 2.
Composition Sample Particle Size Surface area Grind time No. ( ) (cm2/g) (min) 1 Interground 60% clinker and 10.1 14100 74 40% zeolite 2 Blended (separately ground) 9.8 14900 -60% clinker, 40% zeolite 3 100% ground clinker 18'0' 10200, 10700 105, 105 18.0 4 100% ground zeolite 5.8 19000 130 FIG. 6 provides a comparison of cumulative particle size distribution for Compositions 1-4. The interground clinker and zeolite (Composition 1), and separately ground clinker and zeolite (Composition 2) have essentially identical cumulative particle size distributions, which distribution differs both from that of 100% ground zeolite, and that of 100%
ground clinker.
The essentially identical cumulative particle size distributions indicate that particle size is controlled for further comparison of properties of the two compositions. The data of Table 2 further support this conclusion in that the particle size of the blended sample, while slightly lower than that of the interground sample, nevertheless provides a good control for comparing the two types of compositions.
EXAMPLE 3. Presence or Absence of Gypsum The present example relates to the properties of three compositions:
interground cement clinker and zeolite, Composition 1; interground cement clinker, zeolite, and gypsum, Composition 5; and an interground cement clinker and zeolite composition (i.e., Composition 1) blended with hand-ground gypsum, Composition 7. The hand-ground gypsum had been ground and sieved to a particle size of about 168 m. The amount of each ingredient by weight, the particle size, the surface area, and grind time for Compositions 1, 5, and 7 are provided in Table 3. The amount of gypsum provided the same ratio of clinker to gypsum for Compositions 5 and 7. Duplicate determinations were carried out on Composition 5.
Table 3. Compositions With and Without Gypsum Composition article Siz Surface No. Sample (~) area Grind time (min) (cm/) 1 Interground 60% clinker and 10.1 14,100 74 40% zeolite 5 Interground 55.8% clinker, 40% 10.4, 14,400, 105,105 zeolite and 4.2% gypsum 10.5 14,700 Interground composition 1, blended with hand-ground 7 gypsum 4.52% by weight of 13.0 11,500 -Com osition 1.
The interground Compositions 1 and 5 compare favorably in particle size and surface area. The difference in grind time to achieve a particle size of about 10 microns is likely attributable to different operators and mechanical slippage during the grind.
FIG. 6 provides a comparison of cumulative particle size distribution and FIG. 7 provides a comparison of particle size distribution, each for Compositions 1, 5 and 7. Compositions 1, 5 and 7 have comparable bimodal distributions of particle size which distributions both differ from that of 100% ground zeolite; and that of 100% ground clinker. Therefore, the compositions have essentially identical particle size indicating that particle size is essentially controlled for comparison of further properties of the three compositions.
EXAMPLE 4. Properties of Cementitious Compositions, Interground vs. Blended, and With and Without Gypsum The present example relates to properties of cementitious compositions of interground as compared to separately ground and blended zeolite and cement clinker compositions, with or without gypsum.
The cementitious compositions were formed by mixing the components in the amounts set forth in Table 4 and additives were added by weight of components according to the methods of API Specification RP IOB, 22nd Edition, 1997, of the American Petroleum Institute. Sodium sulfate (Na2SO4) and sodium carbonate (Na2CO3) are commercially available and were obtained from Sodium Solutions (Edmonton, Canada) under the trade names CA-661 and K-35, respectively. A defoamer, containing internal olefin oil, polypropylene glycol, hydrophobically modified silica and diatomaceous earth, is commercially available and was obtained from Halliburton Energy Services (Duncan, OK), under the trade name D-Air 3000. Duplicate determinations of compressive strength were carried out for Compositions 1 and 5.
Table 4. Cementitious Compositions3 Cementitious Components (w/w) Additives (bwoc Composition Class C Clinker, No. cement2 Type 10 Zeolite Gypsum Na2SO4 Na2CO3 D.
_ Interground 60% clinker 1 and 40% zeolite - 4.5% 2.25%
separately separately 2 - ground 60% o%d - 4.5% 2.25%
clinker zeolite - Interground 55.8% type 10 clink5r, 40% 4.5% 2.25%
zeolite, and 4.2% gypsum 6 60.0% - 40% - 4.5% 2.25%
hand-ground, 7 - Interground 60% clinker 4.52% by 4.5% 2.25%
and 40% zeolite weight of interground material5 By weight of total components 2 Class C cement is ground clinker and gypsum in a w/w ratio of about 100:7 3 All cementitious compositions of Table 4 have a slurry density of 1400 kg/m3 4 Cubic meters of water per metric ton of total components as components are set forth in Table 4.
5 The amount of gypsum is about 7% in weight relation to cement clinker. This approximates the amount of gypsum in Class C cement for comparison purposes.
Compressive strength, rheology and free fluid were determined as described above.
Exterior surface area was determined by the laser process as described in Example 1. The temperature for measurement of rheology and free water is at about room temperature in order to simulate manufacturing conditions. The temperature for measurement of compressive strength is somewhat higher in order to simulate downhole conditions where the pumped compositions are warmed by the downhole environment.
A comparison of the compressive strength versus time of setting for the five compositions of Table 4 is provided by FIG. 8 and Table 5. The data obtained from interground Compositions 1, and 5 as compared to blended Compositions 2 and 6 demonstrate that the interground compositions appear to have greater long-term compressive strength than do the blended compositions beginning at a set time of about 40 hours.
Further, the data obtained from interground Composition 5 having gypsum present as compared to the data from interground compositions not having gypsum present 1 demonstrate that the intergrinding without gypsum provides better compressive strength.
A free water test at room temperature and an angle of deviation of zero degrees provided a trace of free water in 250 mL for Compositions 1 and 2 as summarized in Table 5.
Free water excess, i.e., greater than about 2% for downhole applications, indicates separation and likely ensuing problems in a wellbore.
Rheology dial readings were recorded as described above and also at 300, 200, 100, 6 and 3 RPM, then increasing to 6, 100, 200 and then to 300 RPM at 20-second intervals.
Rheological data for the compositions of this example are summarized in Table 5. The data demonstrate that the compositions without gypsum have a greater ability to flow than the compositions with gypsum.
Table 5. Properties of Cementitious Compositions Free Rheology Results Compressive Strength Water Comp Dial Reading, - 22 C - 25 C - 22 C
. No. Time to Time to Final 0.35 MPa 3.5 MPa MPa (psi);
300 200 100 6 3 (50 psi) (500 psi) at 120 h (mL/
RPM RPM RPM RPM RPM Hr: Min Hr: Min 250mL) 50:45 6.20 (900) 1 34/32 30/31 28/29 25/25 25 12:08 (ave) (ave) (ave) Trace 2 29/27 24/22 24/20 13/14 12 11:40 60:21 5.03 (730) Trace 52:31 6.68 (970) 55/58 50/53 44/45 31/27 25 13:02 (ave) (ave) (ave) 0 6 50/43 40/38 33/31 23/22 19 9:51 63:35 5.17 (750) 0 7 43/42 38/38 32/32 22/21 16/16 20:55 70:50 5.17 (750) 0 As a control, neat clinker was blended with water in a beaker. Small clumps of material formed in the bottom of the beaker and generated heat immediately.
After about 30 minutes, the remaining slurry was thick but movable. Class C cement was also prepared.
However, no clumping, heat or increase in consistency occurred in the same time period.
Adding water to the ground clinker produced the same results as adding ground clinker to water.
Other embodiments of the present invention will be apparent to those skilled in the art from a consideration of this specification or practice of the embodiments disclosed herein. However, the foregoing specification is considered merely exemplary of the present invention with the true scope and spirit of the invention being indicated by the following claims.
The references cited herein, to the extent that they provide exemplary procedural or other details supplementary to those set forth herein, are specifically incorporated by reference.
As used herein and unless otherwise indicated, the terms "a" and "an" are taken to mean "one", "at least one" or "one or more".
Claims (128)
1. A process of performing a cementing operation in a subterranean zone comprising:
placing a gypsum-free cementitious composition into the subterranean zone, the gypsum-free cementitious composition comprising:
a carrier fluid, and a base grind comprising cement clinker interground with zeolite; and allowing the cementitious composition to set therein.
placing a gypsum-free cementitious composition into the subterranean zone, the gypsum-free cementitious composition comprising:
a carrier fluid, and a base grind comprising cement clinker interground with zeolite; and allowing the cementitious composition to set therein.
2. The process of Claim 1 wherein the cementing operation is primary cementing.
3. The process of Claim 1 wherein the cementing operation is remedial cementing.
4. The process of Claim 1 wherein the base grind comprises from about 5% to about 95%
by weight of zeolite.
by weight of zeolite.
5. The process of Claim 1 wherein the base grind comprises from about 5% to about 50%
by weight of zeolite.
by weight of zeolite.
6. The process of Claim 1 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
7. The process of Claim 4 wherein the base grind further comprises at least one pozzolan selected from the group consisting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan, and combinations thereof.
8. The process of Claim 7 wherein the base grind comprises from about 10% to about 50% by weight of the pozzolan.
9. The process of Claim 7 wherein the base grind comprises at least two pozzolans.
10. The process of Claim 7 wherein the base grind comprises at least three pozzolans.
11. The process of Claim 1 wherein the zeolite is represented by the formula:
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
12. The process of Claim 1 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
13. The process of Claim 1 wherein the base grind has an exterior surface area of greater than 10,000 cm2/g.
14. The process of Claim 1 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
15. The process of Claim 1 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
16. The process of Claim 1 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 to about 12.0 cubic meters of water-based carrier fluid per metric tonne of base grind.
17. The process of Claim 1 wherein the carrier fluid comprises an oil-based carrier fluid.
18. The process of Claim 1 wherein the cementitious composition further comprises an additive selected from the group consisting of an accelerator, a retarder, an activator, a defoamer and combinations thereof.
19. The process of claim 18 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
20. The process of claim 1 wherein the cementitious composition further comprises an accelerator in an amount of from about 0.5% to about 10% by weight of the base grind.
21. The process of claim 18 wherein the base grind comprises from about 2% to about 7%
by weight of the accelerator.
by weight of the accelerator.
22. The process of claim 1 further comprising foaming the cementitious composition to form a foamed cementitious composition.
23. A process of performing a cementing operation in a subterranean zone comprising:
placing a cementitious composition into the subterranean zone, the cementitious composition comprising:
a carrier fluid, and a base grind comprising cement clinker interground with zeolite and gypsum wherein the base grind comprises from about 5% to about 95% by weight of zeolite; and allowing the cementitious composition to set therein.
placing a cementitious composition into the subterranean zone, the cementitious composition comprising:
a carrier fluid, and a base grind comprising cement clinker interground with zeolite and gypsum wherein the base grind comprises from about 5% to about 95% by weight of zeolite; and allowing the cementitious composition to set therein.
24. The process of Claim 23 wherein the cementing operation is primary cementing.
25. The process of Claim 23 wherein the cementing operation is remedial cementing.
26. The process of Claim 23 wherein the base grind comprises from about 10% to about 50% by weight of zeolite.
27. The process of Claim 23 wherein the base grind comprises from about 15% to about 45% by weight of zeolite.
28. The process of Claim 23 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
29. The process of Claim 23 wherein the base grind further comprises at least one pozzolan selected from the group consisting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan and combinations thereof.
30. The process of Claim 29 wherein the base grind comprises from about 10% to about 50% by weight of the pozzolan.
31. The process of Claim 29 wherein the base grind comprises at least two pozzolans.
32. The process of Claim 29 wherein the base grind comprises at least three pozzolans.
33. The process of Claim 23 wherein the zeolite is represented by the formula:
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
34. The process of Claim 23 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
35. The process of Claim 23 wherein the interground base grind has an exterior surface area greater than 10,000 cm2/g.
36. The process of Claim 23 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
37. The process of Claim 23 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
38. The process of Claim 23 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 to about 12.0 cubic meters of water-based carrier fluid per metric tonne of base grind.
39. The process of Claim 23 wherein the carrier fluid comprises an oil-based carrier fluid.
40. The process of Claim 23 wherein the cementitious composition further comprises an additive selected from the group consisting of an accelerator, a retarder, an activator, a defoamer and combinations thereof.
41. The process of claim 40 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
42. The process of claim 23 wherein the cementitious composition further comprises an accelerator in an amount of from about 0.5% to about 10% by weight of the base grind.
43. The process of claim 40 wherein the base grind comprises from about 2% to about 7%
by weight of the accelerator.
by weight of the accelerator.
44. The process of claim 23 further comprising foaming the cementitious composition to form a foamed cementitious composition.
45. The processs of claim 23 wherein the base grind comprises gypsum at an amount of up to about 10% by weight of the base grind.
46. The process of claim 23 wherein the base grind comprises gypsum at an amount of from about 2% to about 7% by weight of clinker.
47. A process of preparing a gypsum-free cementitious composition comprising:
intergrinding a composition comprising cement clinker and zeolite to form a base grind;
and mixing the base grind with a carrier fluid to form a slurry.
intergrinding a composition comprising cement clinker and zeolite to form a base grind;
and mixing the base grind with a carrier fluid to form a slurry.
48. The process of claim 47 further comprising allowing the slurry to set.
49. The process of Claim 47 wherein the base grind comprises from about 5% to about 95% by weight of zeolite.
50. The process of Claim 47 wherein the base grind comprises from about 5% to about 50% by weight of zeolite.
51. The process of Claim 47 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
52. The process of Claim 49 wherein the base grind further comprises at least one pozzolan selected from the group consisting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan and combinations thereof.
53. The process of Claim 52 wherein the base grind comprises at least two pozzolans.
54. The process of Claim 52 wherein the base grind comprises at least three pozzolans.
55. The process of Claim 47 wherein the zeolite is represented by the formula:
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
56. The process of Claim 47 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
57. The process of claim 47 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 to about 12.0 cubic meters of water-based carrier fluid per metric tonne of base grind.
58. The process of claim 47 wherein the carrier fluid comprises an oil-based carrier fluid.
59. The process of claim 47 further comprising mixing an additive with the base grind, wherein the additive is selected from the group consisting of an accelerator, a retarder, an activator, a defoamer, and combinations thereof.
60. The process of claim 59 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
61. The process of claim 47 further comprising foaming the composition.
62. The process of Claim 47 wherein the base grind has an exterior surface area greater than 10,000 cm2/g.
63. The process of Claim 47 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
64. The process of Claim 47 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
65. A process of preparing a cementitious composition comprising:
intergrinding a composition comprising cement clinker, zeolite, and gypsum to form a base grind wherein the zeolite is present in the base grind in an amount of from about 5% to about 95% by weight; and mixing the base grind with a carrier fluid to form a slurry.
intergrinding a composition comprising cement clinker, zeolite, and gypsum to form a base grind wherein the zeolite is present in the base grind in an amount of from about 5% to about 95% by weight; and mixing the base grind with a carrier fluid to form a slurry.
66. The process of claim 65 further comprising allowing the slurry to set.
67. The process of Claim 65 wherein the base grind comprises from about 5% to about 50% by weight of zeolite.
68. The process of Claim 65 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
69. The processs of Claim 65 wherein the base grind comprises gypsum at an amount of up to about 10% by weight of the base grind.
70. The process of Claim 65 wherein the base grind comprises at least one pozzolan selected from the group consisiting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan and combinations thereof.
71. The process of Claim 70 wherein the base grind comprises at least two pozzolans.
72. The process of Claim 70 wherein the base grind comprises at least three pozzolans.
73. The process of Claim 65 wherein the zeolite is represented by the formula:
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
74. The process of Claim 65 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
75. The process of claim 65 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 to about 12.0 cubic meters of water-based carrier fluid per metric tonne of base grind.
76. The process of claim 65 wherein the carrier fluid comprises an oil-based carrier fluid.
77. The process of claim 65 further comprising mixing an additive with the base grind, wherein the additive is selected from the group consisting of an accelerator, a retarder, an activator, a defoamer and combinations thereof.
78. The process of claim 77 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
79. The process of claim 65 further comprising foaming the composition.
80. The processs of Claim 65 wherein the base grind comprises gypsum at an amount of from about 0% to about 10% by weight of the base grind.
81. The process of claim 65 wherein the base grind comprises gypsum at an amount of from about 2% to about 7% by weight of clinker.
82. The process of Claim 65 wherein the base grind has an exterior surface area greater than 10,000 cm2/g.
83. The process of Claim 65 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
84. The process of Claim 65 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
85. A gypsum-free interground composition comprising a base grind comprising cement clinker interground with zeolite.
86. The gypsum-free interground composition of Claim 85 wherein the base grind comprises from about 5% to about 95% by weight of zeolite.
87. The gypsum-free interground composition of Claim 85 wherein the base grind comprises from about 5% to about 50% by weight of zeolite.
88. The gypsum-free interground composition of Claim 85 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
89. The gypsum-free interground composition of Claim 86 wherein the base grind further comprises at least one pozzolan selected from the group consisting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan and combinations thereof.
90. The gypsum-free interground composition of Claim 89 wherein the base grind comprises from about 10% to about 50% by weight of the pozzolan.
91. The gypsum-free interground composition of Claim 89 wherein the base grind comprises at least two pozzolans.
92. The gypsum-free interground composition of Claim 89 wherein the base grind comprises at least three pozzolans.
93. The gypsum-free interground composition of Claim 85 wherein the zeolite is represented by the formula:
M a/n(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
94. The gypsum-free interground composition of Claim 85 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
95. The gypsum-free interground composition of Claim 85 wherein the base grind has an exterior surface area of greater than about 10,000 cm2/g.
96. The gypsum-free interground composition of Claim 85 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
97. The gypsum-free interground composition of Claim 85 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
98. A cementitious composition comprising:
a gypsum-free interground composition comprising a base grind comprising cement clinker interground with zeolite; and a carrier fluid mixed with the gypsum-free interground composition.
a gypsum-free interground composition comprising a base grind comprising cement clinker interground with zeolite; and a carrier fluid mixed with the gypsum-free interground composition.
99. The cementitious composition of claim 98 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 to about 12.0 cubic meters of water-based carrier fluid per metric tonne of base grind.
100. The cementitious composition of claim 98 wherein the carrier fluid comprises an oil-based carrier fluid.
101. The cementitious composition of claim 98 further comprising an additive selected from the group consisting of an accelerator, a retarder, an activator, a defoamer and combinations thereof.
102. The cementitious composition of claim 101 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
103. The cementitious composition of claim 98 wherein the base grind has an exterior surface area of greater than about 10,000 cm2/g.
104. The cementitious composition of claim 98 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
105. The cementitious composition of claim 98 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
106. An interground composition comprising a base grind of cement clinker interground with zeolite and gypsum wherein the base grind comprises from about 5% to about 95% by weight of the zeolite.
107. The interground composition of Claim 106 wherein the base grind comprises from about 10% to about 50% by weight of zeolite.
108. The interground composition of Claim 106 wherein the base grind comprises from about 15% to about 45% by weight of zeolite.
109. The interground composition of Claim 106 wherein the base grind comprises from about 20% to about 40% by weight of zeolite.
110. The interground composition of claim 106 wherein the base grind comprises gypsum at an amount of up to about 10% by weight of the base grind.
111. The interground composition of claim 106 wherein the base grind comprises gypsum at an amount of from about 2% to about 7% by weight of clinker.
112. The interground composition of Claim 107 wherein the base grind further comprises at least one pozzolan selected from the group consisting of fly ash, slag, diatomaceous earth, fumed silica, calcined shale, metakaolin, rice husk ash, natural pozzolan and combinations thereof.
113. The interground composition of Claim 112 wherein the base grind comprises from about 10% to about 50% by weight of the pozzolan.
114. The interground composition of Claim 112 wherein the base grind comprises at least two pozzolans.
115. The interground composition of Claim 112 wherein the base grind comprises at least three pozzolans.
116. The interground composition of Claim 106 wherein the zeolite is represented by the formula:
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
M a/n[(AlO2)a(SiO2)b] .cndot. xH2O
where M represents one or more cations selected from the group consisting of Na, K, Mg, Ca, Sr, Li, Ba, NH4, CH3NH3, (CH3)3NH, (CH3)4 N, Ga, Ge and P;
n represents the cation valence;
the ratio of b:a is in a range from greater than or equal to 1 and less than or equal to 5;
and x represents the moles of water entrained into the zeolite framework.
117. The interground composition of Claim 106 wherein the zeolite is selected from the group consisting of analcime, bikitaite, brewsterite, chabazite, clinoptilolite, faujasite, harmotome, heulandite, laumontite, mesolite, natrolite, paulingite, phillipsite, scolecite, stellerite, stilbite, and thomsonite.
118. The interground composition of Claim 106 wherein the base grind has an exterior surface area of greater than about 10,000 cm2/g.
119. The interground composition of Claim 106 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
120. The interground composition of Claim 106 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.
121. A cement composition comprising:
an interground composition comprising a base grind of cement clinker interground with zeolite and gypsum wherein the base grind comprises from about 5% to about 95% by weight of zeolite and;
a carrier fluid mixed with the interground composition, the carrier fluid is present from about 0.18 cubic meters to about 12 cubic meters per tonne of the base grind.
an interground composition comprising a base grind of cement clinker interground with zeolite and gypsum wherein the base grind comprises from about 5% to about 95% by weight of zeolite and;
a carrier fluid mixed with the interground composition, the carrier fluid is present from about 0.18 cubic meters to about 12 cubic meters per tonne of the base grind.
122. The cement composition of claim 121 wherein the carrier fluid comprises a water-based carrier fluid in an amount of from about 0.18 cubic meters of water per metric tonne of base grind.
123. The cement composition of claim 121 wherein the carrier fluid comprises an oil-based carrier fluid.
124. The cement composition of claim 121 further comprising an additive selected from the group consisting of an accelerator, a retarder, an activator, a defoamer and combinations thereof.
125. The cement composition of claim 121 wherein the additive comprises an accelerator selected from the group consisting of sodium sulfate, sodium carbonate and combinations thereof.
126. The cement composition of claim 121 wherein the base grind has an exterior surface area of greater than about 10,000 cm2/g.
127. The cement composition of claim 121 wherein the base grind has an exterior surface area of from about 11,000 cm2/g to about 16,000 cm2/g.
128. The cement composition of claim 121 wherein the base grind has an exterior surface area of from about 13,000 cm2/g to about 15,000 cm2/g.