CA2546806A1 - Foam cushion backing suitable for use in carpets and carpet tile products - Google Patents

Abstract

The present invention pertains to foam cushion backings comprising at least one homogeneously branched ethylene polymer (HBEP) or a substantially linear ethylene polymer (SLEP). More particularly, the present invention pertains to foam cushion backings suitable for use in carpets and carpet tile products.
The present invention further pertains to foam cushion-backed carpet and carpet tile products. The present invention further pertains to methods of making such foam cushion backings and carpet and carpet tiles as described herein.

Description

CARPET STRUCTURE WITH PLASTOMERIC FOAM BACKING
FIELD OF THE INVENTION
The present invention pertains to foam cushion backings. More particularly, the present invention pertains to foam cushion backings suitable for use in carpets and carpet tile products. The present invention further pertains to foam cushion-backed carpet and carpet tile products. The present invention further pertains to methods of malting such foam cushion backings and carpet and carpet tiles as described herein.
1o BACKGROUND OF THE INVENTION
Foam cushions are commonly used as backings for carpet or carpet tile products. When cushion-backed, carpets and carpet tiles may wear longer than products that do not have these backings. In particular, when stress is applied to carpet face yarn affixed to a carpet or carpet tile product having a cushioned backing, such as 15 by walking, rolling or by placing heavy obj ects on the surface, the load is transferred from the carpet face to the cushioned backing. Thus, the cushioned backing will bear the majority of the load and the carpet face will generally not show wear as quicltly as products not having a cushion backing. As such, a cushion backing system engineered to absorb that force can greatly increase the appearance retention of the carpet or carpet 2o tile, thus increasing its usable life and lowering the overall cost to the consumer.
Additionally, since a cushion-backed carpet or carpet tile product can absorb the load applied by a person's wallting or standing, the person's fatigue can be lessened. This mattes cushion-baclted carpet or carpet tile products especially beneficial in locations where persons walk or stand for extended periods such as, for example, offices, malls, 25 airports etc.
However, when repeated stresses are placed on a carpet or carpet tile structure, such as by walking, standing, rolling or the placing of heavy obj ects on the surface, some foam bacltings can have a tendency to collapse. When this happens, a baclting will no longer have significant cushioning properties. Aperson walking or standing on 3o the carpet or carpet tile for extended periods may experience increased fatigue because of the loss of cushioning in the backing material. This, in turn, will normally lead to #245780 more wear to the face fibers because the stress applied will no longer be transferred to the backing. Delamination i. e., separation of one or more of the individual layers of the carpet or carpet tile product may also increase.
Polyurethanes are widely used in the preparation of foam cushion-backed carpet and carpet tiles. Application of a polyurethane cushion backing to a carpet or carpet tile generally enhances the longevity of the product and can decrease fatigue in a person walking or standing thereon.
However, carpet and carpet tile products backed with polyurethane are generally not readily recyclable using low cost methods. That is, a polyurethane-backed carpet or 1o carpet tile product generally must first be separated from the carpet face and primary backing prior to recycling so as to be able to obtain value from the components for later use to prepare products from such recycled materials. The potential uses for a heterogeneous mixture of recycled polymeric materials i.e., unseparated materials, are generally quite limited in that desirable products are difficult to obtain from such materials. For example, while a recyclable carpet or carpet tile may be obtained from the use of a polyethylene face fiber, a polyethylene primary backing and an ethylene-containing adhesive material, when such carpet has a polyurethane foam cushion backing, the foam cushion backing is not readily compatible with the other materials.
This generally results in an adverse affect on the mechanical properties (e.g., tensile and 2o impact strength) and aesthetic properties of any articles formed from such a mixture.
While the various components can be separated from each other prior to use in a recycled product, the separation process generally takes considerable time and energy to undertake.
In light of the above, it would be beneficial to a obtain foam cushion backing for application to a carpet or carpet tile product, where such backing does not comprise polyurethane. It would be further desirable to have a carpet or carpet tile product having such a foam cushion backing, where such product exhibits durability and comfort underfoot.
#245780 SUMMARY OF THE INVENTION
The present invention pertains to foam cushion backings. More particularly, the present invention pertains to foam cushion backings suitable for use in carpets and carpet tile products. The foam cushion backings herein are prepared from homogenously branched ethylene polymers or substantially linear ethylene polymers.
The foam cushion backings may contain a resilient material. The present invention further pertains to foam cushion-backed carpet and carpet tile products. The carpets and carpet tiles can comprise a secondary backing material. The present invention further relates to methods of making such foam cushion backings and carpet and carpet 1o tiles as described herein.
Additional advantages of the invention will be set forth in part in the detailed description, which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the appended claims. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory aspects of the invention, and are not restrictive of the invention, as claimed.
BRIEF DESCRIPTION OF THE DRAWINGS
2o Figure 1 shows an aspect of the present invention having a non-woven backing attached thereto.
Figure 2 shows an aspect of the present invention having a capcoat applied thereto.
DETAILED DESCRIPTION OF THE INVENTION
The present invention may be understood more readily by reference to the following detailed description of the invention and the examples provided herein. It is to be understood that this invention is not limited to the specific methods, formulations, and conditions described, as such may, of course, vary It is also to be understood that #245780 the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting.
In this specification and in the claims that follow, reference will be made to a number of terms, which shall be defined to have the following meaungs.
The singular forms "a," "an," and "the" include plural referents unless the context clearly dictates otherwise.
Ranges may be expressed herein as from "about" one particular value and/or to "about" or another particular value. When such a range is expressed, another aspect 1o includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent "about,"
it will be understood that the particular value forms another aspect.
"Optional" or "optionally" means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where 15 said event or circumstance occurs and instances where it does not. For example, the phrase "optionally comprising water" means that the composition may comprise water and that the description includes both compositions comprising water and compositions without water.
"Carpet" and "carpet tile" are used herein in the manner as would be recognized 2o by one of ordinary skill in the art. The definition of carpet and carpet tiles herein does not include products that would be known to one of ordinary slcill in the art as "resilient flooring." As an example, products that fall under the category of resilient flooring include, but are not limited to, linoleum, vinyl tiles, cork tiles, rubber tiles and floor mats.
25 Throughout this application, where patents are referenced, the disclosures of these patents in their entireties are hereby incorporated by reference into this disclosure.
Throughout this application, where ASTM methods are referenced, the disclosures of each of these ASTM methods are hereby incorporated by reference in their entireties into this disclosure.
3o In a first aspect, the invention pertains to a foam cushion backing suitable for use in a carpet or carpet tile product. Still further, the present invention pertains to #245780 carpet and carpet tile products having such a foam cushion backing. In a further aspect, the foam cushion backing is formed from a polymer composition having certain polymeric and other ingredients.
In one aspect, the polymer composition used to prepare the foam cushion comprises an ethylene polymer, in particular, a homogenously branched ethylene polymer. The term "homogeneously branched ethylene polymer" ("HBEP") means an ethylene interpolymer in which the comonomer is randomly distributed within a given polymer molecule and wherein substantially all of the polymer molecules have the same ethylene to comonomer molar ratio. The term more specifically refers to an ethylene 1o interpolymer that is characterized by a relatively high short chain branching distribution index (SCBDI) or composition distribution branching index (CDBI). That is, the interpohymer has a SCBDI greater than or equal to about 50 %, or greater than or equal to about 70 %, or greater than or equal to about 90 %, and generally lacks a measurable high density (crystalline) polymer fraction. SCBDI is defined as the weight %
of the polymer molecules having a comonomer content within 50 % of the median total molar comonomer content and represents a comparison of the monomer distribution in the interpolymer to the monomer distribution expected for a Bernoullian distribution. The SCBDI of an interpohymer can be readily calculated from data obtained from techniques known in the art, such as, for example, temperature rising elution fractionation (abbreviated herein as "TREF") as described, for example, by Wild et al., Journal of Polymer Science, Poly Phys. Ed., Vol. 20, p. 441 (1982), or in U.S. Patent.
No.
4,798,081, or by L. D. Cady, "The Role of Comonomer Type and Distribution in LLDPE Product Performance," SPE Regional Technical Conference, Quaker Square Hilton, Akron, Ohio, October 1-2, pp.107-119 (1985). The monomer distribution of the interpolymer and SCBDI may also be determined using 13C NMR analysis in accordance with techniques described in U.S. Patent. No. 5,292,845 and by J.
C.
Randall in Rev. Macromol. Chem. Phys., C29, pp. 201-317.
In addition to refernng to a homogeneous (or narrow) short branching distribution, the terns "HBEP" also means the interpolymer does not have substantial long chain branching. That is, the ethylene interpolymer has an absence of long chain branching and a linear polymer backbone in the conventional sense of the terns "linear."
#245780 However, the term "HBEP" does not refer to high pressure branched polyethylene which is known to those skilled in the art to have numerous long chain branches.
HBEP can be made using polymerization processes (e.g., those described by Elston in U.S. Patent. No. 3,645,992) which provides a uniform (narrow) short branching distribution (i. e., are homogeneously branched). In his polymerization process, Elston uses soluble vanadium catalyst systems to make such polymers, however others such as Mitsui Chemical Corporation, Exxon Chemical Corporation and Dow Chemical Company have used so-called single site catalyst systems to make polymers having a similar homogeneous structure. HBEPs suitable for use herein can be prepared in 1o solution, slurry or gas phase processes using hafnium, zirconium and vanadium catalyst systems. Ewen et al. in U.S. Patent. No. 4,937,299 describes a method of preparation using metallocene catalysts.
Still further, the polymer composition comprises a substantially linear ethylene polymer ("SLEP"). "SLEPs" are a type of HBEP and are disclosed in U.S. Patent.
Nos.
5,272,236 and 5,278,272, the disclosures of which are incorporated herein in their entireties by this reference for SLEP's and the methods of making the same.
Such polymers are available are available from The Dow Chemical Company as AFFINITYTM polyolefin plastomers and from Dupont Dow Elastomers JV as ENGAGETM polyolefm elastomers.
2o More particularly, as used herein, "SLEP" refers to homogeneously branched ethylene/cx olefin interpolymers that have a narrow short chain branching distribution and contain long chain branches as well as short chain branches attributable to homogeneous comonomer incorporation. The long chain branches are of the same structure as the baclcbone of the polymer and are longer than the short chain branches.
The polymer backbone of substantially linear-olefin polymers is substituted with an average of 0.01 to 3 long chain branch/1000 carbons. SLEPs can have certain processing advantages for use in the present invention. When those advantages are desired, suitable SLEPs for use in the invention are substituted with from 0.01 long chain branch/1000 carbons to 1 long chain branch/1000 carbons, and more preferably 3o from 0.05 long chain branch/1000 carbons to 1 long chain branches/1000 carbons.

Long chain branching is defined herein as a chain length of at least 6 carbons, above which the length cannot be distinguished using 13C nuclear magnetic resonance spectroscopy. Long chain branches are of greater length than the short chain branches resulting from comonomer incorporation.
The presence of long chain branching can be determined in ethylene homopolymers by using 13C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method described by Randall (Rev. Macromol. Chem. Phys., C29, V 2&3, p. 285-297). As a practical matter, current 13C nuclear magnetic resonance spectroscopy cannot determine the length of a long chain branch in excess of six carbon 1o atoms. However, there are other known techniques useful for determining the presence of long chain branches in ethylene polymers, including ethylene/1-octene interpolymers.
Two such methods are gel permeation chromatography coupled with a low angle laser light scattering detector (GPC-LALLS) and gel permeation chromatography coupled with a differential viscometer detector (GPC-1~V). The use of these techniques for long 15 chain branch detection and the underlying theories have been well documented in the literature. See, for example, Zimm, G H. and Stockmayer, W. H., J. Chem.
Phys., 17, 1301 (1949) and Rudin, A., Modern Methods of Polymer Characterization, John Wiley & Sons, New York (1991) pp. 103-112.
Included among HBEPs suitable for use in the present invention are SLEPs due 2o to their improved melt extrusion processability and unique rheological properties as described by Lai et al. in U.S. Patent. Nos. 5,272,236 and 5,278,272, the disclosures of which are included in their entireties by this reference.
SLEPs differ from the class of polymers conventionally known as HBEPs, for example, by Elston in U.S. Patent. No. 3,645,992, in that substantially linear ethylene 25 polymers do not have a linear polymer backbone in the conventional sense of the term "linear."
The SLEPs that may be used in the present invention may be characterized as having (a) a melt flow ratio, ho /I2.5.63, (b) a molecular weight distribution, MW /M", as determined by gel permeation chromatography and defined by the equation:
(MW/M") 30 (ho /I2)-4.63, (c) a gas extrusion rheology such that the critical shear rate at onset of surface melt fracture for the substantially linear ethylene polymer is at least about 50 #245780 greater than the critical shear rate at the onset of surface melt fracture for a linear ethylene polymer, wherein the SLEP and the linear ethylene polymer comprise the same comonomer or comonomers, the linear ethylene polymer has an Iz, MW /M" and density within ten % of the SLEP and wherein the respective critical shear rates of the SLEP
and the linear ethylene polymer are measured at the same melt temperature using a gas extrusion rheometer, (d) preferably a single differential scanning calorimetry, DSC, melting peak between -30 and 150 °C., and (e) a short chain branching distribution index greater than about 50 %.
The SLEPs that may be used in this invention are homogeneously branched 1o interpolymers and essentially lack a measurable "high density" fraction as measured by the TREF technique (i.e., have a narrow short chain distribution and a high SCBD
index). The SLEPs generally do not contain a polymer fraction with a degree of branching less than or equal to 2 niethyls/1000 carbons. The "high density polymer fraction" can also be described as a polymer fraction with a degree of branching less than about 2 methyls/1000 carbons.
The substantially linear ethylene interpolymers that may be used in the present invention are interpolymers of,ethylene with at least one C3-Cao a olefin and/or C4 -Cis diolefm. Copolymers of ethylene and a olefin of C3-C2o carbon atoms can be used.
The term "interpolymer" is used herein to indicate a copolymer, or a terpolymer, or the like, where, at least one other comonomer is polymerized with ethylene to make the interpolymer. Suitable unsaturated comonomers useful for polymerizing with ethylene include, for example, ethylenically unsaturated monomers, conjugated or non-conjugated dimes, polyenes, etc. Examples of such comonomers include C3-Czo a olefins as propylene, isobutylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-heptene, 1-octene, 1-nonene, 1-decene, 1,9-decadiene and the like. Other suitable monomers include styrene, halo- or alkyl-substituted styrenes, tetrafluoroethylene, vinylbenzocyclobutane, 1,4-hexadiene, 1,7-octadiene, and cycloalkenes, e.g., cyclopentene, cyclohexene and cyclooctene.
SLEPs are known to have excellent processability, despite having a relatively 3o narrow molecular weight distribution (for purposes of this invention, the MW/Mn ratio is generally less than about 3.0, or less than about 2.5, and or less than about

2).
#245780 Surprisingly, unlike homogeneously and heterogeneously branched linear ethylene polymers, the melt flow ratio (ho /I2) of substantially linear ethylene polymers can be varied essentially independently of the molecular weight distribution, MW /Mn.
Accordingly, a particularly suitable ethylene a olefin polymer for use in the present invention can be a SLEP.
The teen "heterogeneously branched linear ethylene polymer" is used herein in the conventional sense in reference to a linear ethylene interpolymer having a comparatively low short chain branching distribution index. That is, the interpolymer has a relatively broad short chain branching distribution. Heterogeneously branched linear ethylene polymers have a SCBDI less than about 50 % and more typically less than about 30 %. HBEPs and SLEPs also differ from the class of polymers known conventionally as heterogeneously branched traditional Ziegler polymerized linear ethylene interpolymers, for example, ultra low density polyethylene ("ULDPE"), very low density polyethylene ("VLDPE"), linear low density polyethylene ("LLDPE") medium density polyethylene ("MDPE") or high density polyethylene ("HDPE") made, for example, using the technique disclosed by Anderson et al. in U.S. Patent.
No.
4,076,698, in that substantially linear ethylene interpolymers are homogeneously branched interpolymers. In one aspect, VLDPE, ULDPE, LLDPE, MDPE and HDPE
are not used as the primary ethylene components in the foam cushion backings of the 2o present invention (although such materials may be used as a component in any adhesive polymers or resilient materials utilized herein as discussed below). Further, in accordance with the present invention, the polymer composition does not comprise more than 20 % by weight of heterogeneously branched linear ethylene polymers, as measured by the total weight of the polymer composition. Still further, heterogeneously branched linear ethylene polymers do not comprise the primary ethylene component in the foam cushion backings of the present invention (although such materials may be used in small amounts as a component in any adhesive polymers and/or resilient materials utilized herein as discussed below).
HBEPs and SLEPs also differ significantly from the class known as free-radical 3o initiated highly branched high pressure low density ethylene homopolymer and ethylene interpolymers such as, for example, ethylene-acrylic acid (EAA) copolymers and #zas~so ethylene-vinyl acetate (EVA) copolymers, in that substantially linear ethylene polymers do not have equivalent degrees of long chain branching and are made using single site catalyst systems rather than free-radical peroxide catalyst systems. In accordance with the present invention, the polymer composition does not comprise more than 20 % by 5 weight of free-radical initiated highly branched high pressure low density ethylene homopolymer and ethylene interpolymers, as measured by the total weight of the polymer composition, exclusive of any adhesive polymer and/or resilient material that contains such homopolymers and interpolymers (as discussed in more detail below).
Put another way, the polymer composition used in the foam cushion backings of to the present invention can be characterized as having: a) a HBEP or SLEP
component;
b) optionally, a resilient material component; c) optionally, an adhesive polymer component; and d) optionally, a component comprising additional materials, such as filler, etc. In accordance with this description, component a) does not comprise more than 20 % by weight of free-radical initiated highly branched high pressure low density ethylene homopolymer and ethylene interpolymers or non-SLEP or non-HBEP
polymer, as measured by the total weight of the polymer composition.
In a further aspect, the ethylene polymer of component a) of the polymer composition consists essentially of HBEP and/or SLEP, exclusive of any ethylene-containing adhesive polymer in the composition. Still further, component a) of the 2o polymer composition of the present invention comprises at least about 80 %
by weight of HBEP as measured by weight of the composition. Still further, component a) of the polymer composition comprises HBEP in at least about 80, 85, 90, 95, 97, 98, or 99 by weight of the polymer composition, where any value can comprise an upper or a lower endpoint, as appropriate.
Still further, component a) of the polymer composition of the present invention comprises at least about 80 % by weight of SLEP, exclusive of any ethylene-containing adhesive polymer in the composition. Still further, component a) of the polymer composition comprises SLEP in at least about 80, 85, 90, 95, 97, 98, or 99 %
by weight of the polymer in the polymer composition, where any value can comprise an upper or a lower endpoint, as appropriate.
#245780 Still further, component a) of portion of the polymer composition of the present invention can comprise a mixture of HBEP and SLEP and the amount of HBEP and SLEP in this mixture together comprise at least about 80 % by weight of the polymer composition. Still further, the polymer composition comprises a mixture of HBEP and SLEP in at least about 80, 85, 90, 95 or 97, 98, or 99 % by weight polymer composition, where any value can comprise an upper or a lower endpoint, as appropriate. In such a mixture, the amount of HBEP and SLEP can be individually varied in the amounts of, for example, from about 1, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97 or 98 % by weight, where any value can be 1o used for the individual components, and any value can be used as an upper or a lower endpoint, as appropriate.
The density of the HBEP andJor SLEP can be from about 0.880, 0.890, 0.895, 0.900, 0.905, 0.910, 0.915 or 0.920 g/cc, where any value can comprise an upper or a lower endpoint, as appropriate.
In still a further aspect, the polymer composition used to prepare the foam cushion backing can comprise a resilient material. "Resilient material" means a material that confers some rubber-like characteristics to the foam baclcing.
In some aspects, it has been found that in accordance with the invention, the inclusion of this resilient material can improve the durability of the foam backing, which generally 2o translates into an enhanced durability in a carpet or carpet tile product having such a foam cushion backing affixed thereto. That is, it has been found that the resilient material can enhance the durability of the foam backing by reducing the tendency of the foam bacl~ing to become "dead foam" and/or to become "compressed cells." "Dead foam" means foam that has a substantially reduced rebound after being compressed, such as by walking or other force applied to the surface of the carpet or carpet tile.
"Compressed cells" are defined as foam that has lost its cellular structure and appears more like a hardback. As would be understood by one of ordinary skill in the art, when a foam backing collapses or compresses during use, the carpet or carpet tile product having such a backing will no longer function sufficiently as a cushion material.
3o Rather, the backing material will more closely resemble a hardback material. Such a hardback structure will not provide adequate cushioning for most commercial uses and, t~245780 as such, will be more likely to result in fatigue to a person walking on the carpet or carpet tile and will often result in a delamination of the carpet or carpet tile.
In a significant aspect, the foam cushion backings of the present invention do not include grafted blends of polymers, such as those disclosed in U.S. Patent No.
6,395,791, the disclosure of which is incorporated herein in its entirety by this reference.
Still further, it has been found that, in some aspects, the cushioning of a carpet or carpet tile having the foam cushion backing of the present invention can be enhanced with inclusion of the resilient material. This has been shown, in some aspects, to 1o translate into a carpet or carpet tile product that exhibits enhanced comfort underfoot and decreased fatigue to a person walking or standing on the product.
As such, in a further aspect, the polymer composition used to prepare the foam cushion backings of the present invention comprises one or more of the following resilient materials: ethylene-propylene-dime monomer rubber (EPDM), ethylene-15 propylene monomer ("EPM"), acrylonitrile-butadiene (NBR), styrene-butadiene (SBR), carboxylated NBR and carboxylated SBR.
In a further aspect, thermoplastic elastomers ("TPEs") may be utilized as the resilient material. TPEs are positioned between thermoplastics and elastomers in terms of structure and behavior. Like thermoplastics, TPEs become plastic due to the 2o application of heat, and retain elastic behavior again on cooling. As would be understood by one of ordinary skill in the art, TPEs are elastomeric materials having physical cross-linking, which can be reversed via the further application of heat.
Examples of TPEs that are suitable for use in the present invention are the various Kraton~ polymers, available from Kraton Polymers (Houston, TX). One such Kraton 25 polymer suitable for use herein is believed to be a styrene block copolymer.
Additionally, polymers such as the Buna~ EP (Bayer AG, Pittsburgh, PA) materials may be used as the resilient material. These materials are believed to comprise EPDM and EPM polymers. EPM represents a copolymer prepared from ethylene and propylene monomers, while EPDM denotes a terpolymer based on,three 3o monomers: ethylene, propylene and a non-conjugated dime.
#245780 Another example of resilient materials that can be used is those supplied by Dow Chemical (Houston, TX) as "Flexomer~" resins. These materials are believed to be VLDPE resins that are flexible such that they can function as impact modifiers when blended with other polymers, such as those used in the polymer compositions herein.
When included in the polymer composition used to prepare the foam cushion backings of the present invention, the resilient material is added to the composition at from about 5 to about 40 % by weight of the polymer composition. Still further, the resilient material is added at from about 15 to about 25 % by weight of the polymer composition. Still further, the resilient material is added at from about greater than 1o about 0, 0.1, 1.0, 3.0, 5.0, 10.0, 15.0, 20.0, 25.0, 30.0, 35.0 or 40.0 %
by weight of the polymer composition, where any value can be used as an upper or lower endpoint, as appropriate. The resilient material may be present with another material, such as an ethylene polymer, to assist in dispersion of the resilient material in the polymer composition.
It should be noted that the foam cushion backings of the present invention need not comprise the resilient material in order to perform suitably for use in carpet and carpet tile products. However, in some circumstances, it has been found beneficial to add the resilient material where enhanced durability and/or comfort underfoot is desired in a product. As would be recognized by one of ordinary skill in the art, customers of 2o carpet and carpet tile products will request varying specifications for these products.
Thus, whether it is desirable to have enhanced durability and/or enhanced comfort underfoot will be dictated by the customers of the carpet and carpet tile products of the present invention. Whether or not to include the resilient material in the polymer compositions of the present invention will thus vary according to the specifications of the customer. As one example, when the carpet tile is intended for use in high traffic areas, such as airports or malls, it may be beneficial to add the resilient material to the polymer composition to enhance the durability of the foam cushion backing and, thus, the carpet or carpet tile itself. The varying of the amount of the resilient material or whether it is to be included at all will not require undue experimentation by one of ordinary skill in the art.
#245780 In a further aspect, the polymer composition used to prepare the foam cushion backings of the present invention comprises an adhesive material. In this aspect, the polymer composition of the present invention further comprises at least one functionalized polyethylene. The term "functionalized polyethylene" herein means a polyethylene incorporating at least one functional group in its polymer structure.
Exemplary functional groups may include, for example, ethylenically unsaturated mono- and di-functional carboxylic acids, ethylenically unsaturated mono- and di-functional carboxylic acid anhydrides, salts thereof and esters thereof. Such functional groups may be grafted to an ethylene homopolymer or an ethylene/a olefin 1o interpolymer, or it may be copolymerized with ethylene and an optional additional comonomer to form an interpolymer of ethylene, the functional comonomer and optionally other comonomer(s).
Generally, examples of such functionalized polyethylene may include:
copolymers of ethylene and ethylenically unsaturated carboxylic acid such as acrylic acid and methacrylic acid; copolymers of ethylene and esters of carboxylic acid such as vinyl acetate; polyethylene grafted with an unsaturated carboxylic acid or a carboxylic acid anhydride, such as malefic anhydride. Specific examples of such functionalized polyethylene may include, ethylene/vinyl acetate copolymer (EVA), ethylene/acrylic acid copolymer (EAA), ethylene/methacrylic acid copolymer (EMAA), salts therefrom (ionomer), various polyethylene grafted with malefic anhydride (MAH) such as MAH-grafted high pressure low density polyethylene, heterogeneously branched linear ethylene/a-olefin interpolymers (which have commonly been referred to as "LLDPE"
and "ULDPE"), homogeneously branched linear ethylene/a olefin interpolymers, substantially linear ethylene/a olefin interpolymers and HDPE. Means for grafting functional groups onto polyethylene are described for example in U.S. Patent.
Nos.
4,762,890, 4,927,888, or 4,950,541, the disclosures of each are incorporated herein in their entireties by this reference.
Two useful functionalized polyethylenes suitable for use in forming the compositions of present invention are ethylene/acrylic acid copolymers and malefic 3o anhydride grafted polyethylene. More specific examples are functionalized polyethylenes that may be used herein are ethylene/acrylic acid copolymers, malefic #245780 anhydride-grafted substantially linear ethylenela olefin interpolymers and malefic anhydride-grafted high density polyethylene.
The amount of the functional group present in the functional polyethylene can vary Typically, the functional group will be present in a graft-type functionalized 5 polyethylene (e.g., the malefic anhydride content in a malefic anhydride-grafted polyethylene) at a level which is at least about 0.1 weight %, or at least about 0.5 weight %. Still further, the functional group will typically be present in a graft-type functionalized polyethylene in an amount less than about 10 weight %, or less than about 5 weight %, or less than about 3 weight %. In contrast, the functional group will 1o typically be present in a copolymer-type functionalized polyethylene (e.g., the acrylic acid content in an ethylene acrylic acid copolymer) from at least about 1.0 weight %, or from at least about 5 weight %, or from at least about 7 weight %, as measured by weight of the polyethylene material to which the graft is made. The functional group will typically be present in a copolymer-type functionalized polyethylene in an amount 15 less than about 40 weight %, or less than about 30 weight %, or less than about 25 weight %.
The functionalized polyethylene can be present in the polymer composition at from about greater than 0 to about 20 % by weight of the polymer composition.
Still further, the amount of functionalized polyethylene can be from about l, 3, 5, 7, 10, 13, 15, 17 or 20 % by weight of the polymer composition, where any value can be used as an upper or lower endpoint, as appropriate. Further, as would be understood by one of ordinary skill in the art, the amount of functionalized polyethylene added to the polymer compositions of the present invention can vary according to the amount of grafting.
The melt index (Ia) of the functionalized polyethylene may be varied, except to the extent to which it unacceptably affects processability of the inventive composition and physical properties of final product. Generally, the functionalized polyethylene has a melt index of at least about 0.1 g/10 min., or from about 0.2 g/10 min.
Generally, the functionalized polyethylene has a melt index of less than about 500 g/10 min., or less than about 350 g/10 min.
3o In a further aspect, the polymer compositions used to prepare the foam cushion backings of the present invention comprise filler. As would be recognized by one of #245780 ordinary skill in the art, the type of filler used will be selected on the basis of the desired physical properties of the final product. Exemplary fillers include calcium carbonate, barium sulfate, barite, glass fiber and powder, metal powder, alumina, hydrated alumina, clay, magnesium carbonate, calcium sulfate, silica or glass, fumed silica, talc, carbon black or graphite, fly ash, cement dust, feldspar, nepheline, magnesium oxide, zinc oxide, aluminum silicate, calcium silicate, titanium dioxide, titanates, glass microspheres, chalk, and mixtures thereof. Further fillers that may be used include calcium carbonate, barium sulfate, talc, silica/glass, alumina, and titanium dioxide, and mixtures thereof. A particularly suitable filler is calcium carbonate, which 1o is available in the industry as limestone and rockdust.
Likewise, the filler may belong to the class of fillers known as "ignition resistance fillers." Exemplary ignition resistant fillers include antimony oxide, decabromobiphenyl oxide, alumina trihydrate, magnesium hydroxide, borates, and halogenated compounds. Other miscellaneous fillers that may be used include wood fibers/flours/chips, ground rice hulls, cotton, starch, glass fibers, synthetic fibers (e.g., polyolefin fibers) and carbon fibers.
The amount of filler present in the polymer compositions used to prepare the foam backings of the present invention is selected based upon the requirements of the final application. For example, where the polymer composition is applied to a carpet 2o greige good prior to activation of the blowing agent, it may be desirable to limit the amount of filler so as to enhance adhesion of the foam to the greige good. The polymer compositions can have a filler amount of at least about 5 % by weight of the polymer composition. Still further, filler may be present in the polymer composition in at least about 20 % by weight. Still further, the amount of filler in the polymer compositions of the present invention may be from about 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 75 or 80 % by weight of the polymer composition where any value may be used as an upper or a lower endpoint, as appropriate.
In certain aspects, it can be beneficial to use filler that can be characterized as "recycled content." One such example, fly ash, is a residue of coal processing for 3o power generators.
#245780 The polymer compositions of the present invention can comprise other materials such as processing aids, oils, pigments, antimicrobials, tackifiers, chemical flame retardants etc. Whether such materials are to be included will depend substantially on the intended use of the foam cushion backing. When such materials are included, they will be included in the amounts generally used in the art.
In a further aspect, the foam cushion backing has a thickness of from greater than 0.075 inches. Yet still further, the foam cushion has a thickness of not less than about 0.075 inches. Still further, the foam layer has a thickness of from about 0.080, 0.090, 0.100, 0.110, 0.120, 0.140, 0.160, 0.180, 0.200, 0.220, 0.240, 0.260, 0.280 or 0.300 inches, where any value can be used as an upper or a lower endpoint as appropriate. In accordance with these measurements, thickness is measured exclusive of the face, primary baclcing and precoat, that is, the thickness of the greige good is not measured as part of the thickness as specified herein.
In a further aspect, the foam cushion backings have a density of from about 10 to about 30 lbs/ft.3 Still further, the foam cushion backings of the present invention can have a density of from about 7, 10, 13, 15, 17, 20, 23, 25, 27, 30 or 33 lbs/ft.3 where any value can be used as an upper or lower endpoint, as appropriate.
As would be recognized by one of ordinary skill in the art, density is a measure of the amount of material per unit weight in the foam cushion backings. For example, 2o foam density can be varied by changing the filler load and by the % gas (e.g., amount of blowing agent) in the polymer composition. Up to a point, depending on the circumstances, more density generally means that there is more cushioning material available to do the work of protecting the carpet and providing comfort underfoot. It follows that density will be a factor in the expected performance of carpet cushion, with higher density generally relating to better performance that may be desirable under some circumstances.
It is also to be recognized that the density and thickness of the foam can be varied to affect properties in the final product. Still further, it will be recognized that it may be beneficial in some instances to reduce the weight of the final carpet or carpet 3o tile product. For example, the thickness of the product can be minimized by reducing weight per square yard of the foam or by increasing the density of the foam.
In a busy #245780 office corridor that receives high traffic, the carpet and cushion will be subjected to significant demands, justifying a higher performance, high-density cushion for long-term retention of properties. In contrast, an executive conference room that receives little traffic, requires a luxurious feel underfoot, and has a need for castered chairs to be reasonably movable. In this case, a lower density may be sufficient.
In a ftirther aspect, carpet and carpet tiles having the foam cushion backing of the present invention affixed thereto exhibit excellent compression set values. As would be understood by one of ordinary skill in the art, compression set relates to the performance of a cushion in situations in which heavy objects will be periodically 1o moved (e.g. repositioning of furniture such as a desk). Products with high compression set will generally leave noticeable, long-term indentations in the carpet or carpet tile products. In particular aspects of the present invention, the compression set of the backings herein can be from about 1 to about 20 %, where the % refers to the recovery of the backing after a 3" x 3" sample is compressed at 25 % for 22 hours, where the temperature is at ambient (about 75 °F). Still further, the compression set of the backings is from about 1, 3, 5, 7, 10, 13, 15 or 20 %, where compression set is measured in accordance with the parameters herein, and where any value can form an upper or a lower endpoint as appropriate.
Still further, the cushioned backings of the present invention have a compression 2o resistance. As would be recognized by one of skill in the art, a compression resistance relates to how a cushion will feel underfoot, as well as the ability of the cushion to provide support without "bottoming out." The ability of a cushion to support traffic without bottoming out can be important in achieving long term carpet appearance retention. In one aspect, the cushion bacl~ings of the present invention have a compression resistance of from about 5 to about 25 psi where 3" x 3" sample of backing is compressed across the thiclcness for 1 minute and the force to recover the thickness is measured in psi, where the temperature is at ambient (about 75 °F). Still further, the compression resistance of the backings herein is from about 5, 7, 10, 13, 15, 17 or 20 psi, where compression resistance is measured in accordance with the 3o parameters herein, and where any value can form an upper or a lower endpoint as appropriate, where the temperature is at ambient (about 75 °F).
#245780 As would be recognized by one of ordinary skill in the art, the various properties of cushion backings for carpets and carpet tiles may be measured in various ways depending on the chemical composition of the backing system. For example, there are different ASTM methodologies depending on whether the backing is polyurethane, rubber, olefin polymers or blends of olefin polymers.
ASTM test 3575 can be used to measure the properties of the foam cushion backings herein. When Suffix B of this test is used to measure compression set of the foams herein, the compression set is from about 8 to 20 % or from about 8, 10, 12, 14, 16, 18 or 20 %, where any value can be used as the upper or lower endpoint, as 1o appropriate. When Suffix D of this test is used to measure compression resistance, the compression resistance of the foam of this invention is from about 18 to about 32 psi.
Still further, the compression resistance is from about 18, 20, 22, 24, 26, 28, 30 or 32 psi when measured in accordance with ASTM 3575 Suffix D, where any value can form and upper or a lower endpoint, as appropriate.
The polymeric components of the polymer composition can be supplied as pellets. Such pellets are normally mixed together in the presence of the other ingredients (e.g. filler, blowing agent, processing aids etc.) prior to melting of the polymer composition. Alternatively, the polymer composition can be mixed in any manner that would be deemed acceptable by one of ordinary skill in the art.
Such 2o methods may include blending, mixing, extrusion etc.
As would be recognized, greige goods generally comprise a carpet fiber tufted into a primary backing. A "precoated greige good" is a greige good to which an adhesive material ("precoat") has been applied to the back surface so as to secure the carpet fibers to the primary backing material.
The face fiber or yarn used in forming the pile of the greige goods used herein is typically made of any one of a number of types of fiber, e.g., nylon, acrylics, polypropylene, polyethylene, polyamides, polyesters, wool, cotton, rayon and the like.
Primary backings for the greige goods herein may be woven or non-woven fabrics made of one or more natural or synthetic fibers or yarns, such as jute, wool, 3o polypropylene, polyethylene, polyamides, polyesters and rayon. Films of synthetic #245780 materials, such as polypropylene, polyethylene and ethylene-propylene copolymers may also be used to form the primary backing.
The foam cushion backing can be applied to the back side of the greige good, in particular, a precoated greige good, by lamination of the finished foam cushion backing 5 to the greige good with a separate adhesive. Such lamination techniques are conventional and well known to one of ordinary skill in the art.
Alternatively, in preparing the foam cushion backings of the present invention, the polymer composition may be applied in a molten state to the back of a carpet or carpet tile structure e.g., a precoated greige good, and the foam activated as discussed in more detail below.
1o Stabilizing materials, such as a fiberglass or FLW or nonwoven materials (each of which are known as "scrims" to one of ordinary skill in the art) can be present in the foam cushion backing. The incorporation of such scrims is also well known to one of ordinary skill in the art. For example, the scrim may be incorporated using an "in situ"
process. Using such a process, the scrim can be situated on the foam while it is still in 15 molten form. Nip pressure can be applied to the fiberglass/molten polymer combination to provide good contact between the fiberglass and polymer. Such contact can be enhanced when the blowing agent in the foam is activated. That is, when activated, the foamed polymer composition can penetrate the interstices of the fiberglass to provide suitable attachment of the fiberglass to the foam.
2o The greige good can be laminated to the scrim-foam cushion structure at the scrim side by the use of a suitable adhesive. Still further, the scrim may be incorporated adjacent to the underside of the greige good by setting it in an adhesive (i.e., precoat or secondary adhesive) on the back of thereof. Such a process is disclosed in, for example, U.S. Patent No. 4,522,857, the disclosure of which is incorporated herein in its entirety by this reference. The foam cushion backing can then be affixed to the greige good by way of lamination with a suitable adhesive material. Still further, the scrim can be applied as disclosed in U.S. Patent No. 4,798,644, the disclosure of which is incorporated herein in its entirety by this reference.
In addition to polymeric secondary backings as described in U.S. Patent 3o Application Serial No. 10/077,609, the disclosure of which is incorporated herein in its entirety by this reference, other secondary backings can be used for tufted pile carpets #245780 or carpet tiles. Such secondary backings may be woven or non-woven fabrics made of one or more natural or synthetic fibers or yarns. Such secondary backings can be leno weave, i.e., tape yarn in the warp direction and spun staple fiber in the fill direction.
When such cloth-type secondary backings are used, they will be applied on an outer surface of the foam backing. The attachment can be in accordance with the in situ process discussed previously. Alternatively, the secondary backing can be attached with an adhesive in accordance with methods known to one of ordinary skill in the art. Such secondary backings can be polyester ("PET") or mixtures of PET with other polymeric materials. As would be recognized by one of ordinary skill in the art, secondary 1o backings can be useful to improve the dimensional stability of carpet and carpet tile products.
Additionally, in some aspects, a cap coat can be applied to the outer surface of the foam cushion backing. The cap coat can be applied prior to activation of the blowing agent or after activation of the blowing agent as discussed fiuther herein.
The cap coat layer can be an extruded layer of, for example, a HBEP, SLEP, LDPE, VLDPE, MDPE or HDPE in which an adhesive material has been included. As discussed elsewhere, the adhesive material can be a functionalized polyethylene material. Still further, the cap coat may comprise the polymeric secondary backing materials as disclosed in U.S. Patent Application Number 10/077,609, the disclosure of 2o which is incorporated in its entirety by this reference. The cap coat can be applied at from about 5 to about 25 oz/ydz. Still further, the cap coat can be applied at from about 5, 10, 15, 20, 25 oz/yd~, where any value can form an upper or a lower endpoint, as appropriate.
The foam cushion backings of the present invention are suitable for use in 6 or 12 foot roll good carpets. If a carpet tile is desired, conventional methods of cutting roll goods into carpet tiles may be used. Methods for cutting carpet tiles from roll goods are well known to one of ordinary skill in the art and, as such, are not discussed in detail herein.
Referring now to Figure 1, a precoated greige good 10 is shown. The greige 3o good has tufted yarn 12, primary backing 14 and adhesive precoat 16. An adhesive 18 attaches a foam cushion backing 22 to the precoated greige good 10. In this drawing, a #245780 fiberglass scrim 20 is attached to the foam cushion backing 22 prior to bringing the precoated greige good 10 together with the foam cushion backing 22. A non-woven textile backing 26 is attached at the lower surface 24 of the foam cushion backing 22.
In Figure 2, a capcoat 28 is attached at the lower surface 24 of the foam cushion backing 22.
The foam cushion backings of the present invention can be made by an extrusion foaming process. The backings may be prepared by heating the polymer composition with any additives thereto to form a plasticized or melt polymer material, incorporating therein a blowing agent to form a foamable composition and extruding 1o the composition through a die to form the foam product. The foamable composition may be extruded directly onto the back of a greige good. Alternatively, the foamable composition may be applied to a suitable surface so as to form a separate foam cushion backing material which can then be laminated to the back of a greige good or, alternatively, a polymeric secondary backing attached to a greige good, using a suitable adhesive as discussed elsewhere herein. When extruded directly onto the back of a greige good or a secondary backing affixed to a greige good, the polymer composition may comprise one or more adhesive materials as discussed above.
Blowing agents useful in making the foam backings of the present invention include inorganic agents, organic blowing agents and chemical blowing agents.
Suitable inorganic blowing agents include carbon dioxide, nitrogen, argon, water, air, sulfur hexafluoride (SF6) and helium. Organic blowing agents include aliphatic hydrocarbons having 1-9 carbon atoms, aliphatic alcohols having 1-3 carbon atoms, and fully and partially halogenated aliphatic hydrocarbons having 1-4 carbon atoms.
Aliphatic hydrocarbons include methane, ethane, propane, n-butane, isobutane, n-pentane, isopentane, neopentane, and the like. Aliphatic alcohols include methanol, ethanol, n-propanol, and isopropanol. Fully and partially halogenated aliphatic hydrocarbons include fluorocarbons, chlorocarbons, and chlorofluorocarbons.
Examples of fluorocarbons include methyl fluoride, perfluoromethane, ethyl fluoride, l,l-difluoroethane (HFC-152a), fluoroethane (HFC-161), 1,1,1-trifluoroethane (HFC-143a), 1,1,1,2-tetrafluoroethane (HFC-134a), 1,1,2,2-tetrafluoroethane (HFC-134), 1,1,1,3,3-pentafluoropropane, pentafluoroethane (HFC-125), difluoromethane (HFC-#245780 32), perfluoroethane, 2,2-difluoropropane, 1,1,1-trifluoropropane, perfluoropropane, dichloropropane, difluoropropane, perfluorobutane, perfluorocyclobutane.
Partially halogenated chlorocarbons and chlorofluorocarbons for use in this invention include methyl chloride, methylene chloride, ethyl chloride, 1,1,1-trichloroethane, l,l-dichloro-1 fluoroethane (HCFC-141b), 1-chloro-1,1-difluoroethane (HCFC-142b), chlorodifluoromethane (HCFC-22), 1,1-dichloro-2,2,2-trifluoroethane (HCFC-123) and 1-chloro-1,2,2,2-tetrafluoroethane (HCFC-124). Fully halogenated chlorofluorocarbons include trichloromonofluoromethane (CFC-11), dichlorodifluoromethane (CFC-12), trichlorotrifluoroethane (CFC-113), dichlorotetrafluoroethane (CFC-114), 1o chloroheptafluoropropane, and dichlorohexafluoropropane. Chemical blowing agents include azodicarbonamide, azodiisobutyro-nitrile, barium azodicarboxylate, N,N'-dimethyl-N,N'-dinitrosoterephthalamide, and benzenesulfonhydrazide, 4,4-oxybenzene sulfonyl semicarbazide, and p-toluene sulfonyl semicarbazide, trihydrazino triazine and mixtures of citric acid and sodium bicarbonate such as the various products sold under the name HydrocerolTM (a product of Boehringer Ingelheim). Any of the foregoing blowing agents may be used singly or in combination with one or more other blowing agents. Preferred blowing agents include isobutane, carbon dioxide, HFC-152a, and mixtures of the foregoing.
The amount of blowing agent incorporated into the polymer composition is 2o from about 0.05 to about 5.0 % by weight of the composition, or from about 0.2 to about 3.0 % by weight of the polymer composition. Still further, the amount of blowing agent can be from 0.2, 0.5, 0.7, 1.0, 1.2, 1.5 1.7, 2.0, 2.2, 2.5, 2.7 or 3.0 % by weight of the polymer composition, where any value can form an upper or a lower endpoint as appropriate. Yet still further, about 0.5, 1, 2, 3 or 4 parts blowing agent can be added to 100 parts of the polymer composition.
Prior to mixing with the blowing agent, the foamable polymer composition can be heated to a temperature at or above its glass transition temperature or melting point.
The blowing agent can then be incorporated or mixed into the melted polymer composition by any means known in the art such as with an extruder, mixer, blender, or 3o the like. The blowing agent can be mixed with the melted polymer composition at an elevated pressure sufficient to prevent substantial expansion of the melted polymer #245780 compo sition and to advantageously disperse the blowing agent homogeneously therein.
Optionally, a nucleator can be blended in the melted polymer composition or dry blended with the polymer composition prior to plasticizing or melting. Prior to extruding the foamable composition, the composition may be cooled to an optimum temperature. The composition may be cooled to a lower temperature than the melt temperature to optimize physical characteristics of the foam backing. This temperature, often referred to as the "foaming temperature," is typically above each component's polymer glass transition temperature (Tg), or for those having sufficient crystallinity, near the peak crystalline melting temperature (Tm). "Near" means at, above, or below 1o and largely depends upon where stable foam exists. The temperature desirably falls within 30 °C above or below the Tm. For foams of the present invention, an optimum foaming temperature is in a range in which the foam does not collapse. The polymer composition may be cooled in the extruder or other mixing device or in separate coolers. The composition can then be extruded or conveyed through a die of desired shape to a zone of reduced or lower pressure to form the foam backing.
In an alternative aspect, the blowing agent may be dry blended with the polymer composition, i.e., the unmelted polymer composition.
In another aspect, the resulting foam baclcing is optionally formed in a coalesced strand form by extrusion of the polymer material through a mufti-orifice die.
The orifices can be arranged so that contact between adjacent streams of the molten extrudate occurs during the foaming process and the contacting surfaces adhere to one another with sufficient adhesion to result in a unitary foam backing. The streams of molten extrudate exiting the die can take the form of strands or profiles, which desirably foam, coalesce, and adhere to one another to form a unitary structure. The coalesced individual strands or profiles should remain adhered in a unitary structure to prevent strand delamination under stresses encountered in preparing, shaping and using the foam. Apparatuses and methods for producing foam backings in coalesced strand form are described in U.S. Patent. Nos. 3,573,152 and 4,24,720, the disclosures of which are incorporated by their entireties herein by this reference.
3o Alternatively, the resulting foam backing can be conveniently formed by an accumulating extrusion process and apparatus as seen in U.S. Patent. No.
4,323,52 and #245780 LT.S. Patent. No. 5,817,705, the disclosures of which are incorporated herein in their entireties by this reference. This apparatus, commonly known as an "extruder-accumulator system" allows one to operate a process on an intermittent, rather than a continuous, basis. The apparatus includes a holding zone or accumulator where 5 foamable gel remains under conditions that preclude foaming. The holding zone is eduipped with an outlet die that opens into a zone of lower pressure, such as the atmosphere. The die has an orifice that may be open or closed, preferably by way of a gate that is external to the holding zone. Operation of the gate does not affect the foamable composition other than to allow it to flow through the die. Opening the gate 1o and substantially concurrently applying mechanical pressure on the gel by a mechanism (e.g., a mechanical ram) forces the foamable composition through the die into a zone of lower pressure. The mechanical pressure is sufficient to force the foamable composition through the die at a rate fast enough to preclude significant foaming within the die yet slow enough to minimize and preferably eliminate generation of 15 irregularities in foam cross-sectional area or shape. As such, other than operating intermittently, the process and its resulting products closely resemble those made in a continuous extrusion process.
In this process low density foam backings having large lateral cross-sectional areas can be prepared by: 1) forming under pressure a gel of the polymer or blend 2o material and a blowing agent at a temperature at which the viscosity of the gel is sufficient to retain the blowing agent when the gel is allowed to expand; 2) extruding the gel into a holding zone maintained at a temperature and pressure which does not allow the gel to foam, the holding zone having an outlet die defining an orifice opening into a zone of lower pressure at which the gel foams, and an openable gate closing the 25 die orifice; 3) periodically opening the gate; 4) substantially concurrently applying mechanical pressure by a movable ram on the gel to eject it from the holding zone through the die orifice into the zone of lower pressure, at a rate greater than that at which substantial foaming in the die orifice occurs and less than that at which substantial irregularities in cross-sectional area or shape occurs; and 5) permitting the 3o ej ected gel to expand unrestrained in at least one dimension to produce the foam backing.
#245780 Foams can be optionally perforated to enhance or accelerate gaseous permeation exchange wherein blowing agent exits from the foam and air enters into the foam. The resulting perforated foams have defined therein a multiplicity of channels that are preferably free of direction with respect to the longitudinal extension of the foam. The channels extend from one foam surface at least partially through the foam, and sometimes completely through the foam from one external surface to another external surface. The channels are advantageously present over substantially an entire exterior foam surface, preferably with uniform or substantially uniform spacing.
Suitable spacing intervals may be up to and including 2.5 cm, preferably up to and including 1.3 1o cm. The foams optionally employ a stability control agent of the type described above in combination with perforation to allow accelerated permeation or release of blowing agent while maintaining a dimensionally stable foam. U.S. Patent. No.
5,424,016, U.S.
Patent. No. 5,585,058, WO 92/19439 and WO 97/22455, the disclosures of which are incorporated in their entireties by this reference, for their descriptions of foam 15 manufacture. If desired, the foams of this invention may be post-treated by any known means to increase foam open cell content. Such post-treatment methods include, without limit, mechanically compressing the foam and expanding the foam by exposure to steam or hot air.
In one aspect of the present invention, an extrusion method as discussed above 2o is used. In such a method, all ingredients are mixed together in the extruder and the foam prepared directly when the polymer composition exits out of the extruder.
When the one-step process is utilized, it may be desirable to minimize the amount of filler in the polymer composition so as to enhance the mixing of the various ingredients in the polymer composition. In some aspects of the one step process, it may be desirable to 25 use a blowing agent which has previously been dispersed in a polymer composition to improve blendability of the materials. One example of a suitable material is Ficel~ SL
50 (Bayer ACS Pittsburgh, PA). This material is believed to be a 50%
azodicarbonamide in LDPE. In this process, the polymeric components axe mixed with the filler, if any, and the blowing agent and other materials and melted.
#245780 In a further aspect, the foam backings of the present invention may be made by a two-step process. In the two-step process, the blowing agent is ,after added to the fully mixed polymer composition.
The polymer compositions should be subjected to heat for a time sufficient to activate the blowing agent so as to provide a suitable foam. In one aspect, the composition can be heated for about 1 to about 10 minutes. Still further, the composition can be heated for about l, 2, 3, 4, 5, 6, 7, 8, 9 or 10 minutes, where any value can form an upper or a lower endpoint, as appropriate. Still further, the temperature at which the composition is heated can be from about 200 to about 500 °F.
1o As would be recognized by one of ordinary skills in the art, the temperature needs to be high enough to cause activation of the blowing agent but below the decomposition temperature of the polymer. The optimum temperature to accomplish these objectives may be readily determined by one of ordinary skill in the art without undue experimentation.
In one aspect, the foam backings of the present invention are substantially uncrosslinked. By "substantially uncrosslinked" it is meant that the foams comprise less than about 2 % crosslinking. Still further, the foam backings of the present invention are essentially non-cross-linked. The amount of crosslinking of the foam backings does not include any crosslinked portion of the resilient material, which may 2o itself have some crosslinking. In accordance with the present invention, it has been found that the use of the non-crosslinked foam backing materials of the present invention allows ready recycling of the carpet and carpet tiles herein. That is, as would be understood by one of ordinary skill in the art, foam cushion backings prepared from polyurethane materials are crosslinked (thermoset). As such, it is not possible to remelt the backings and re-use them in the same or similar manner as they were originally used. In contrast, the substantially uncross-linked foam backings of the present invention can be re-melted and used again as backings for carpet or carpet tile products or as high value ingredients in products where such properties are needed.
Significantly, when recycled, the polymeric components of the foam backings of the 3o present invention retain many, if not most, of the physical properties of the original polymeric component.
#245780 Additionally, it has surprisingly been found that foam cushion backings with significant durability and comfort underfoot can be obtained even though the foams are uncrosslinked. That is, it was previously believed that in order to obtain durability and comfort underfoot from an HBEP backing it was necessary to use crosslinked materials.
Carpet and carpet tile products having the foam backings of the present invention affixed thereto, with or without the addition of the resilient material as discussed in detail above, have been found to be exceptionally durable and comfortable.
In a further aspect of the present invention, the cushion backing of the present invention is not applied to resilient flooring materials as defined elsewhere herein. Still 1o further, resilient flooring is not within the scope of this invention in that the thickness of the cushion backing herein is unsuited for use in such products. Further, such flooring is not designed for comfort underfoot and will generally not reduce fatigue in a person walking on the surface. As such, the backings disclosed in U.S. Patent No.
5,910,358, the disclosure of which is incorporated herein in its entirety by this reference, are not included within the scope of the present invention.
As mentioned above, when used as foam cushion backing for a carpet or carpet tile product, products have been found to be particularly durable and comfortable underfoot when compared to carpet and carpet tiles having prior art foamed carpet or carpet tiles backing, such as PVC or polyurethane. In particular, carpet or carpet tile 2o structures having the foam backings of the present invention exhibit excellent results in the roll stool test.
A further aspect of the present invention relates to a carpet or carpet tile that resists delamination. In particular, the carpet and carpet tile products of the present invention exhibit minimal delamination of the various layers. In these aspects, the carpet and carpet tiles exhibit a delamination strength of one or more of the layers of from about 2.5 to about 25 lbs/in, where the degree of delamination is measured according to ASTM D 3936. Still further, the amount of delamination is from about 2.5, 5, 7, 10, 12, 15, 17, 20, 22, or 25 lbs/in as measured in accordance with ASTM D
3936, where any value can form an upper or lower endpoint, as appropriate.
Still 3o further, the carpets and carpet tiles of the invention exhibit a minimum delamination of at least 2.5 lbs/in as measured by ASTM D936. As used herein, the delamination values #245780 relate to one or more of the layers, that is, the interface between the foam and the primary backing, the interface between the foam and the capcoat or the interface between the foam and the textile backing. As would be recognized by one of ordinary slcill in the art, the failure of adhesion at one or more of these interfaces in case, will be considered unacceptable. Thus, the delamination strength values referred to herein are applicable to each of these interfaces.
EXAMPLES
The following Examples are put forth so as to provide those of ordinary skill in 1o the axt with a complete disclosure and description of how the compounds claimed herein are made and evaluated, and axe intended to be purely exemplary of the invention and are not intended to limit the scope of what the inventors regard as their invention.
Efforts have been made to ensure accuracy with respect to numbers (e.g., amounts, temperature, etc.) but some errors and deviations should be accounted for.
Unless 15 indicated otherwise, parts are parts by weight, temperature is in °F
or is at room temperature, and pressure is at or near atmospheric.
#245780 Example 1: Cushion Backed Testing with Various Additives in Various Amounts All samples contained 1 % oil (Sunpar 150 Paraffmic Oil, Sun Chemicals, Philadelphia, PA) All samples had blowing agent post-add compounded unless otherwise specified.
(Note that % in post-added were in relation to amount of blowing agent in compound without blowing agent.) Compression resistance numbers are an average of 3 values.
Compression set and density are taken from single measurements.
1o Samples included fiberglass material foam and felt secondary backing as indicated.
Compression resistance measured according to the following:
A three by three inch sample of backing, i. e., scrim, foam and secondary backing (if 15 present) was compressed 25 % across its thickness for 1 minute and the force to recover the full thickness was measured in psi at ambient temperature (about 75 °F). Values are reported in psi.
Compression set was measured according to the following:
A three by three inch sample of backing was compressed 25 % across its thickness for 22 hours and allowed to recover for 24 hours. The % recovery after 24 hours equals the compression set at ambient temperature (about 75 °F). Values are reported in %.
Density was measured by calculating (sample weight/(sample thickness * sample area).
Values are reported in lbs/ft3.
Thickness Below/After: Thickness of material before and after activation of blowing agent.
Delamination strength was measured in lbs/ft as measured by ASTM D3936.

Product Sources KC 8852 Dow Chemical (Midland, Ml) EG 8200 Dow Chemical EG8185 Dow Chemical XLT 60769.07L Dow Chemical Buna Products Bayer AG (Pittsburgh, PA) Class C1F Flyash Boral Materials Technologies (San Antonio, TX) ADC/S-C2 L-251 Bayer AG

ADC/M-C1 L-241 BayerAG

4o Ficel Bayer AG

1085 NT Elastomer Dow Chemical 9042 NT Elastomer Dow Chemical 1088 NT Elastomer Dow Chemical Freuenberg 100 PET Freudenberg Non-wovens Group (Weinham, DE) Ellc Thermally Stable FillerElk Performance Non-wovens (Ennis, Media TX) W.G Steve PET Blend W.E. Steven Co. (Dalton, GA) #zas~so Example 1 Twin 270-1398D'Itvin 269-1398CTwin 268.2- l~vin 268.1-1398A

HBEP type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 50 50 50 50 FunctionalizedXU60769.07L XU60769.07L ~iJ60769.07LXiJ60769.07L

Polyethylene (FP) T a FP Amount 4 4 4 4 (%) Elastomeric Buna EPT Buna EPT 2070Buna EPT Buna EPT 2070 Material Elastomeric 20 20 20 20 Material Amount J) Filler Type Class C FlyashCaC03 Class F FlyashClass C Flyash Filler Amount25 25 25 25 (%) Blowing AgentADC/S-C2 ADC/S-C2 L-251ADC/S-C2 ADC/S-C2 L-251 T a Blowing Agent1 1 1 1 Amount Blowing 450F/ 7 mires450F/ 7 wins 450F/ 7 mires450F/ 7 mina Conditions Compression 11.88 12.9 13.77 11.42 Resistance Density 18.7 18.7 20.3 20.0 Compression 6.6 6.2 5.5 6.2 Set Cushion RatingGood Good Good Good Thickness 0.083/0.2 0.085/0.191 0.086/0.193 0.084/0.181 Before/After oz/yd2 31.8 31.5 31.8 31.6 Foam Rating Good lookingGood looking Medium cell Good looking cell cell cell structure/ structure/ structure/ structure/small medium small uniform and uniform uniform uniform Secondary Fruedenberg Fruedenberg Fruedenberg Fruedenberg Used 100 100 100 100 PET 2.9 oz/ PET 2.9 oz/ PET 2.9 oz/ PET 2.9 oz/
d2 dz d2 d2 Secondary 18,03 19.73 Delamination #245780 Twin 246-1314ATwin 245-1313BTwin 242- Twin 241-1308B

HBEP type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 50 41 49 50 (%) FunctionalizedXU60769.07L XCT60769.07L XU60769.07LXU60769.07L

Polyethylene T a FP Amount 4 4 4 4 (%) Elastomeric Buna EPT 2070Buna EPT 2070Buna EPT Buna EPT
Material 2070 2070 Elastomeric 20 20 20 20 Material Amount Filler Type Class C FlyashClass C FlyashClass C Class C Flyash Flyash Filler Amount25 25 25 25 (%) Blowing AgentADC/S-C2 L-251ADC/S-C2 L-251Ficel SL-50ADC/S-C2 Type L-251 Blowing Agenti - i 11 l i -Amount Blowing Conditions450F/ 7 mires450F/ 7 mires450F/ 7 450F/ 7 mires mires Compression 10.1 9.05 20.33 13.86 Resistance Density n/d 12.44 22.7 23.4 Compression n/d n/d n/d n/d Set Cushion Ratingn/d Good Fair to Good Good CR increased vs. Post Addition Blowin a ent Thickness n/d/0.213 n/d/0.219 0.095/0.1940.091/0.15 Before/After oz/yd2 33.0 27.4 35.7 34.6 Foam Rating n/d Good looking Very good Very good cell cell cell structure/ structure stnxcture/small small Secondary Fruedenberg Fruedenberg FruedenbergFruedenberg Used 100 100 100 PET 2.9 oz/yd2PET 2.9 oz/ydz100 PET PET 2.9 oz/yd2 2.9 oz/ dz Secondary n/d n/d n/d n/d Delamination t Blowing agent compounded in base mixture.

Twin 240-1308ATwin 240-1299Twin 234-1287Twin 233.2-HBEP type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 50 50 44 50 (%) FunctionalizedXLT60769.07L XIJ60769.07L XCT60769.07L

Polyethylene T a FP Amount (%) 4 4 4 Elastomeric Buna EPT 2070Buna EPT 2070Polyone Polyone EG-9190 Material EG-9190 NaturalNatural 0000 Elastomeric 20 20 30 20 Material Amount %) Filler Type Class C FlyashClass C FlyashClass C Class C Flyash Flyash Filler Amount 25 25 , 25 25 (%) Blowing Agent ADC/S-C2 L-251A.DC/S-C2 ADC/S-C2 ADC/S-C2 Type L-251 L- L-251 Blowing Agent 1 1 1 1 Amount Blowing Conditions450F/ 7 mires450F/ 7 rains450F/ 7 450F/ 7 mires rains Compression 10.89 12.85 18.63 15.54 Resistance Density 18.75 17.45 19.07 18.37 Compression n/d n/d 10.3 11.4 Set Cushion RatingVery good Very good Fair Fair Thickness 0.081/0.193 0.090/0.202 0.093/0.2530.073/0.238 Before/After oz/yd2 29.3 3 3.7 40.5 27.9 Foam Rating Good looking Good looking Large cell Large cell cell cell structure/ structure! structure structure small small uniform uniform Secondary UsedFruedenberg Fruedenberg ,FruedenbergFruedenberg PET 2.9 oz/ydzPET 2.9 oz/ydZ100 PET PET 2.9 oz/ydZ
2.9 oz/ d2 Secondary n/d n/d n/d n/d Delamination Twin 231-1279Twin 228-1276A Twin Twin 226-1274B

HBEP type KC 8852 EG 8200 EG EG 8200 HBEP Amount50 50 50 50 FunctionalizedXLJ60769.07LXU60769.07L XLT60769.07L XLJ60769.07L

Polyethylene T a FP Amount 4 4 ~ 4 4 ElastomericBuna EPT Union Union Union Carbide Carbide Carbide NT

Material 2070 elastomer 9042 1088 NT
NT

elastomer elastomer Elastomeric20 20 20 20 Material Amount %) Filler Class C Class Class Class C Flyash Type Flyash C Flyash C
Flyash Filler 25 25 25 25 Amount (%) Blowing Bayer FicelADC/S-C2 ADC/S-C2 ADC/S-C2 Agent L-251 L-251 L-251 T a SL-50 Blowing 0.5 1 1.5 1 1.5 1.5 Agent Amount Blowing 450F/ 7 450F/ 450F/ 450F/ 7 mires mires 7 mires 7 mires Conditions Compressionn/d 14.07 n/d n/d n/d 9.96 .

Resistance Density n/d 19.59 n/d n/d n/d 15.26 Compressionn/d 10.3 n/d. n/d n/d 8.3 Set Cushion n/d Good n/d n/d n/d Good Rating Thickness 0.097/n/d 0.082/0.222n/d n/d n/d/ 0.075/0.221 /
n/d B efore/After n/d oz/yd2 n/d 35.9 n/d n/d n/d 25.8 Foam Ratingn/d Good n/d n/d n/d Very large cell looking structure cell structure/

small uniform Secondary FruedenbergFruedenbergFruedenbergFruedenFruedeFruedenberg Used 100 PET 100 PET 100 PET berg nberg PET 2.9 oz/ydz 2.9 oz/yd2 2.9 oz/yd22.9 oz/yd2100 100 PET PET
2.9 oz/yd22.9 oz/
dZ

Secondary 28.17 22.33 n/d n/d n/d n/d Delamination Twin 226- Twin 225-1273-Twin 225-1273-Twin 224-1273-lA

HBEP type EG 8200 EG 8200 EG 8200 EG 8200 HBEP Amount50 50 50 54 FunctionalizedXLT60769.07LXU60769.07L XLT60769.07L

Polyethylene T a FP Amount 4 4 4 (%) ElastomericUnion CarbideBuna EPT Buna EPT Buna EPT

Material 1088 NT

elastomer Elastomeric20 20 20 20 Material Amount Filler TypeClass C Class C FlyashClass C Class C
Flyash Flyash Flyash Filler Amount25 25 25 25 Blowing ADC/S-C2 ADC/S-C2 ADC/S-C2 ADC/S-C2 Agent L- L- L- L-251 T a 251 251 251 Blowing 1 1.5 l 1 1.5 Agent Amount (%

Blowing 450F/ 7 450F/ 7 mires450F/ 7 450F/ 7 mires miss mires Conditions Compression25.77 9.49 18.35 20.43 n/d Resistance Density 23.73 15.82 22.60 24.51 n/d Compression13.3 8.6 10.1 9.3 n/d Set Cushion n/d Very good Fair Fair n/d Rating Thickness 0.085/0.1830.091/0.234 0.094/0.2050.096/0.173n/d BeforelAfter oz/yd2 31.8 33.6 40.1 38.7 n/d Foam RatingLarge cellLarger cell Large cell Good lookingn/d structure siructure/somestructure cell voiding structure/small and uniform Secondary FruedenbergFruedenberg FruedenbergFruedenbergFruedenberg Used 100 100 100 PET PET 2,9 oz/ydzPET 2.9 100 PET 100 PET
2.9 oz/yd2 2.9 oz/ dz oz/ dz 2.9 oz/
d2 Secondary 16.97 n/d 22.5 22.63 n/d Delamination Twin 223-1272ATwin 222-1 Twin 222-2 Twin 221-HBEP type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 54 50 50 50 (%) Functionalized XLT60769.07L XIJ60769.07L XIJ60769.07L

Polyethylene T a FP Amount 4 4 4 (%) Elastomeric Buna EPT 2070Buna EPT 2070Buna EPT 2070Buna EPT
Material Elastomeric 20 20 20 20 Material Amount (%) Filler Type Class C FlyashClass C FlyaslzClass C FlyashClass C

F1 ash Filler Amount25 25 25 25 (%) Blowing AgentADC/S-C2 L-251ADCIS-C2 L-251ADC/M-C1 L-241ADC/S-C2 Type L-Blowing Agent1.0 1.0 1.0 1.0 Amount Blowing Conditions450F/ 7 rains450F/ 7 rains450F/ 7 mires450F/ 7 mires Compression 14.26 n/d n/d 12.41 Resistance Density 19.29 n/d n/d 19.10 Compression 9.3 n/d n/d 12.3 Set Cushion RatingVery good n/d nld n/d Thickness 0.081/0.221 n/d n/d ~ 0.086/0.217 Before/After oz/yd2 33.6 n/d n/d 28.1 Foam Rating Good looking n/d n/d Good uniform cell structure/small cell and uniform structure/looks similar to urethane ad Secondary Fruedenberg Fruedenberg Fruedenberg Fruedenberg Used 100 lO0 100 PET 2.9 oz/ydzPET 2.9 oz/yd2PET 2.9 oz/ydz100 PET
2.9 oz/ dz Secondary 26.83 n/d n/d 25.37 Delamination Twin 221-1268BTwin 216.2-1261ATwin 216-1261BTwin 216.3-1260A

HBEP type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 50 50 50 50 FunctionalizedXU60769.07L XLT60769. XIJ60769.0 XU6076 Polyethylene 07L 7L 9.07L

T a FP Amount 4 4 4 4 (%) Elastomeric Buna EPT 2070Union Union Union Material Carbide Carbide Carbide Elastomeric 20 20 20 20 Material Amount Filler Type Class C FlyashClass C Class C Class C

F1 ash F1 ash F1 ash Filler Amount25 25 25 25 %) Blowing AgentADC/S-C2 L-251ADC/S- ADC/S-C2 ADC/S-Type C2 L-251 L-251 C2 L-Blowing Agent1.5 1.0 1.5 1 Amount % _ , Blowing 450F/ 7 mires450F/ 7 450F/ 7 450F/ 7 Conditions mires mires mires Compression 10.16 21.14 9.07 15.80 Resistance Density 15.55 19.15 15.03 18.73 Compression 12.5 11.1 11.1 12.6 Set Cushion Ratingn/d Fair Very good Fair Thickness 0.08210.252 0.073/0.1 0.070/0.191 0.078/0.

Before/After 73 163 oz/ydz 28.2 23.7 20.9 24.5 Foam Rating Somewhat thickSmall uniformSmall to mediumSmall to cell sized structure cell structure/medium some voiding sized cell structure Secondary Fruedenberg Fruedenbe Fruedenberg Frueden Used 100 PET 2.9 oz/yd2rg 100 100 PET 2.9 berg 100 PET 2.9 oz/yd2 PET 2.9 oz/ d2 oz/ d2 Secondary 7.95 26.73 n/d n/d Delamination ~vin 219-1264Bvin 219-1264B

HBEP type _ AT 1070 HBEP Amomit 50 50 (%) FunctionalizedXU60769.07L XU60769.07L
Polyethylene T a FP Amount 4 4 (%) Elastomeric Buna EPT Buna EPT 2070 Material 2070 Elastomeric 20 20 Material AmOUnt Filler Type Class C FlyashClass C Flyash Filler Amount25 25 (%) Blowing AgentADC/S-C2 ADC/S-C2 L-Type L-251 251 Blowing Agent1 1.5 Amount Blowing Conditions450F/ 7 mires450F/ 7 mires Compression 16.13 12.68 Resistance Density 19.97 17.94 Compression n/d n/d Set Cushion Ratingn/d n/d Thickness 0.093/0.180 0.075/0.165 Before/After oz/ydz 31.2 23 .3 Foam Rating Somewhat large cell structure Secondary Fruedenberg Fruedenberg 100 Used 100 PET 2.9 oz/ da PET 2.9 oz/
d2 Secondary 8.00 8.45 Delamination Twin 216.3-1260CTwin 216.1-1259ATwin 216.1-1259BTwin 214.2-HBEP type KC 8852 KC 8852 KC 8852 Dow EG

HBEPAmount 50 50 50 40 (%) FunctionalizedXU60769.07L XLT60769.07L XIT60769.07L XU60769.07L

Polyethylene T a FP Amount (%) 4 4 4 4 Elastomeric Union Carbide Union Carbide Union CarbideBayer Buna Material NT FDB-9042 FDB-9042 2070 P
EPDM

Elastomeric 20 20 20 30 Material Amount Filler Type Class C FlyashClass C FlyashClass C FlyashClass C

F1 ash FillerAmount 25 25 25 25 (%) Blowing Agent ADC/S-C2 L-251ADC/S-C2 L-251ADC/S-C2 L-251ADC/M-C1 Type L-Blowing Agent 1.5 1 1.5 1.0 Amount Blowing Conditions450F/ 7 mins 450F/ 7 mires 450F/ 7 mires450F/ 7 ' mires Compression 10.96 14.07 11.19 16.92 Resistance Density 17.54 18.97 15.84 n/d Compression 13.1 10.5 9.1 10.9 Set Cushion RatingGood Good Very good Good Thiclrness 0.068/0.148 0.075/0.182 0.063/0.178 0.074/0.183 Before/After oz/yd2 18.0 26.2 22.9 28.0 Foam Rating Small uniform Small uniform Small cell Medium cell cell sized structure structure structure/somecell voiding structure/unifo rm Secondary UsedFruedenberg Fruedenberg Fruedenberg Fruedenberg 2.9 oz/yd~ PET 2.9 oz/yd2PET 2.9 oz/ydz100 PET
2.9 oz/ d2 Secondary n/d n/d n/d n/d Delamination Twin 214.2-1255BTwin 214.2-1255CTwin 214.1-1254ATwin 214.1-HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG
(XLT (XLT (XLT 8185 59400 59400 59400 (XLJ59400 HBEP Amount 40 40 50 50 (%) FunctionalizedXLT60769.07L XU60769.07L XCT60769.07L XU60769.07L

Polyethylene T a FP Amount (%) 4 4 4 4 .

Elastomeric Bayer Buna Bayer Buna Bayer Buna Bayer Buna Material EPDM EPDM P EPDM 2070 P
EPDM

Elastomeric 30 30 20 20 Material Amount Filler Type Class C FlyashClass C FlyashClass C FlyashClass C

F1 ash Filler Amount 25 25 25 25 (%) Blowing Agent ADC/M-C1 L-241ADC/M-C1 L-241ADC/M-C1 L-241ADC/M-Cl Type L-Blowing Agent 1.5 1.5 1 1.5 Amount .

Blowing Conditions450F/ 7 rains 450F/ 7 mires 450F/ 7 rains450F/ 7 rains Compression 10.56 15.84 18.29 11.87 Resistance Density n/d n/d n/d n/d Compression 9.6 8.3 8.5 5.5 Set Cushion RatingVery good Very good Fair to Good Good Thickness 0.063/0.190 0.059/0.171 0.084/0.194 0.075/0.209 Before/After oz/yd2 24.7 21.4 30.3 27.8 Foam Rating Larger cell Larger cell Medium to Medium large cell structure/somestructure/somecell structure/structure/some voidin voidin uniform voidin Secondary UsedFruedenberg Fruedenberg Fruedenberg Fruedenberg 2.9 oz/ydz PET 2.9 oz/yd2PET 2.9 oz/yd~100 PET
2.9 oz/ d2 Secondary n/d n/d n/d n/d Delamination Twin 212.3-1250Twin 212.2-1249Twin 212.1-1248Twin 211B-1244 HBEP type Dow EG 8185 _ Dow EG 8185 Dow EG 8185 (XLT Dow EG 8185 (XLT (XLT
(XLT

59400) 59400 59400 59400 HBEP Amount 34 44 54 60 (%) Functionalized XU60769.07L

Polyethylene T a FP Amount 4 (%) Elastomeric Bayer Buna Bayer Buna B ayer Buna Bayer Buna Material P EPDM P EPDM P EPDM P EPDM

Elastomeric 40 30 20 25 Material Amount Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount25 25 25 10 (%) Blowing AgentADC/M-C1 L-241ADC/M-C1 L-241ADC/M-C1 L-241ADC/M-C1 L-241 Type Blowing Agent1 1 1 1.5 Amount Blowing Conditions450F/ 7 mires450F/ 7 mires450F/ 7 mires450F/ 7 minx .

Compression 11.83 14.74 15.96 20.0 Resistance Density n/d n/d nld n/d Compression 11.1 8.6 7.5 8.7 Set Cushion RatingGood Good Good Somewhat good Thiclaiess 0.082/0.173 0.080/0.187 0.077/0.185 0.088/0.180 Before/After oz/ydz 27.6 29.0 28.5 28.6 Foam Rating Rougher mediumSmaller cell Smaller cell Larger cell sized cell structure structure/somestructure/uniform structure/some voiding voidin Secondary Fruedenberg Fruedenberg Fruedenberg Fruedenberg Used 100 100 100 100 PET 2.9 oz/ PET 2.9 oz/ PET 2.9 oz/ PET 2.9 oz/
dZ d' dz d~

Secondary 2.18 8.13 8.57 n/d Delamination Twin 211A-_1243Twin 206-1228ATwin 202 Twin 201-1204A

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG 8185 (XLT (XU (XU (XU

HBEP Amount 64 54 54 66 (%) Functionalized XIJ60769.07L
Polyethylene T a FP Amount 8 (%) Elastomeric Bayer Buna Bayer Buna Kraton D-4141 Material T 2070 T 2070 P EPDM P EPDM

Elastomeric 25 20 20 Material Amount (%

Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount10 25 25 25 (%) Blowing AgentADC/M-C1 L-241ADC/M-C1 L-241ADC/M-C1 L-241ADC/M-C1 L-241 Type Blowing Agent1 1 1 1 Amount Blowing Conditions450F/ 5 mires450F/ 5 mires450F/ 5 mires450F/ S mires .

Compression 24.7 15.50 n/d 19.4 Resistance Density n/d n/d n/d n/d Compression 11.5 8.0 n/d 10.1 Set Cushion RatingLow Good n/d Low Thiclrness 0.082/0.140 0.08310.159 n/d 0.064/0.168 Before/After oz/ydz 28.0 28.1 n/d 25.4 Foam Racing Large uniformSmall uniformDid not blow Medium cell cell cell in structure/some structure structure oven voidin Secondary PGI PET 2.0 PGI PET 2.0 PGI PET 2.0 PGI PET 2.0 Used oz/ydZ oz/yd' oz/ydz oz/yd2 Secondary n/d 7.g9 n/d 6.44 Delamination Twin 200-1203ATwin 182-1182FTwin 182-11826T_~vin 18_8_-1182B

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG 8185 (XU (XU (XU (XU

HBEP Amount 70 70 70 55 (%) Functionalized~iLJ60769.07LXU60769.07L XiJ60769_07L XU60769.07L
Polyethylene T a FP Amount 4 4 4 4 (%) Elastomeric Material Elastomeric Material Amount %) Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount25 10 10 40 (%) Blowing AgentADC/M-C1 L-241ADC/S-C2 L-251ADC/S-C2 L-251ADC/S-C2 L-251 Type Blowing Agent1 0.5 1 0.5 Amount %) Blowing Conditions450F/ 5 minx 450Fl 5 mires450FJ 5 _rn_ 450F/ 5 mires ins Compression 21.90 27.00 20.73 28.08 Resistance Density n/d n/d n/d n/d Compression 9.6 13.4 7.8 17.3 Set Cushion RatingModerate Low Low Low Thickness 0.069/0.173 0.077/0.130 0.071/0.168 0.072/0.113 Before/After oz/ydZ - - 32.6 - -35.7 36.5 35.9 Foam Rating Medium uniformMedium uniformMedium uniformMedium uniform cell structurecell structure/thincell structurecell structure backin Secondary PGI PET 2.0 PGI PET 2.0 PGI PET 2.0 PGI PET 2.0 Used oz/ydz oz/ydz oz/ydZ oz/yda Secondary n/d n/d n/d n/d Delamination Twin 188-1137BTwin 188-1181BTwin 183-1173BTwin 183-1173A

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG 8185 (XIJ (XIJ (XU XLT 59400) 59400) 59400 59400 HBEP Amount 55 55 55 55 (%) FunctionalizedXL160769.07L XLT60769.07LXU60769.07L XTJ60769.07L
Polyethylene T a FP Amount 4 4 4 4 (%) Elastomeric Material Elastomeric Material Amount %) Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount40 40 40 40 (%) Blowing AgentADC/S-C2 L-251ADC!F-C2 ADC/S-C2 L-251ADC/S-C2 Type L-249 L-251 Blowing Agent1 1 1.5 1.5 Amount (%

Blowing Conditions450Fl 5 mires 450F/ 5 mires450F/ 5 mires 450F/ 5 mires Compression 24.38 16.83 9.34 10.73 Resistance Density ~d ~d - ~d n/d Compression 9.5 n/d 5.7 8.0 Set Cushion RatingLow/Stiff n/d n/d n/d Thiclmess 0.075/0.188 0.069/0.164 0.07010.212 0.084/0.231 Before/After oz/ydz 38.3 31.4 35.4 35.4 Foam Rating Medium uniformMedium uniformMedium uniformMedium cell cell structure/somecell cell structure/somestructure/some voidin structure/uniformvoidin voidin Secondary None PGI PET 2.0 PGI PET 2.0 PGI PET 2.0 Used oz/yd2 oz/yd2 oz/ dz Secondary n/a n/d n/d n/d Delamination Twin 183-1172BTwin 183-1172ATwin 182-1160FTwin 183-1160C

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG 8185 (XU (XU (XU (XU

HBEP Amount 55 55 70 55 (%) FunctionalizedXIT60769.07L XIJ60769.07L XLT60769.07L XU60769.07L
Polyethylene T a FP Amount 4 4 4 4 (%) Elastomeric Material Elastomeric Material Amount %) Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount40 40 20 40 (%) Blowing AgentADC/S-C2 L-251ADC/S-C2 L-251ADC/S-C2 L-251ADC/M-C1 Type L-241 Blowing Agent1 1 2 2 Amount Blowing Conditions450F/ 5 mires450F/ 5 mires450F/ 5 mires 450F/ 5 mires .

Compression 14.87 20.98 12.51 10.2 Resistance Density n/d n/d n/d n/d Compression 10.0 11.7 4.9 9.4 Set Cushion Ratingn/d n/d n/d n/d Thickness 0.067/0.185 0.078/0.165 0.056/0.234 0.067/0.259 Before/After oz/ydz 32,2 32.2 32.4 -.. 38.1 Foam Rating Medium cell Medium cell Small uniform Larger cell structurelsomestructure/somecell structure/some voidin voidin structure voidin Secondary PGI PET 2.0 Freudenburg None None Used oz/yd2 100 %
PET 2.9 oz/
dz Secondary n/d n/d n/a n/a Delamination Twin 183-_1160ATwin 183-11626Twin 183-1162FTwin 182-1162B

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 Dow EG 8185 (XU (XIJ (XU (XU

HBEPAmount(%) 55 55 55 70 FunctionalizedXU60769.07L XU60769.07L XIJ60769.07L XU60769.07L
Polyethylene T a FP Amount (%) 4 4 4 4 Elastomeric Material Elastomeric Material Amount %

Filler Type Class C FlyashClass C FlyashClass C FlyashClass C Flyash Filler Amount 40 40 40 25 (%) Blowing Agent ADC/M-C1 L-241ADC/L-C2 L-257A.DC/L-C2 ADC/L-C2 L-257 Type L-257 Blowing Agent 1 2 1 2 Amount Blowing Conditions450F/ 5 mires450F/ 5 mires450F/ 5 mires450F/ 5 mires.

Compression 17.22 7.68 17.4 9.35 Resistance Density ~d ~d ~a ~d Compression 25.7 6.8 14.6 6.2 Set Cushion Ratingn/d n/d n/d n/d Thickness 0.052/0.164 0,047/0.179 0.06110.132 0.051/0.178 B efore/After oz/yd2 26.2 27,5 28.0 25.0 Foam Rating Small to mediumLarger cell Small uniformLarger cell cell structure/somecell structure/some structure/somewhatvoiding structure voiding/looks uniform good Twin 182-1162ATwin 181-1158Bvin 181-1158A

HBEP type Dow EG 8185 Dow EG 8185 Dow EG 8185 (XU (XU (XU

HBEP Amount 70 69.8 69.8 (%) FunctionalizedXLT60769.07L XLJ60769.07L XLT60769.07L
Polyethylene T a FP Amount 4 4.2 4.2 (%) (%) Elastomeric Material Elastomeric Material Amount Filler Type Class C FlyashClass C FlyashClass C Flyash Filler Amount25 25 25 (%) Blowing AgentADC/L-C2 L-257ADC/M-C1 L-241ADC/M-C1 L-241 Type Blowing Agent1 2 1 Amount Blowing Conditions450F/ 5 rains450F/ 5 minx 450F/ 5 rains Compression 15.40 10.33 17.28 Resistance Density n/d n/d n/d Compression 9.9 21.9 21.4 Set Cushion Ratingn/d n/d n/d Thickness 0.044/0.100 0.049/0.166 0.048/0.121 Before/After oz/yd2 24,5 28.3 27.7 Foam Rating Medium uniformLarge cells/someUniform cell cell structurevoidin structure Example 2: Testing of Cushion-Backed Products Having Blowing Agent, Class C
Fly Ash and Resilient Material HBEP Type KC 8852 KC 8852 KC 8852 KC 8852 HBEP Amount 50 50 50 50 Functionalized PolyethyleneXU60769.07L XLT60769.07LXU60769.07L XIJ60769.07L
(FP) T a FP Amount 4 4 - 4 4 (%) Resilient Buna EPT 2070Buna EPT Buna EPT Buna EPT 2070 Material 2070 2070 Resilient Material Amount %) 20 20 20 20 Filler Type Class C FlyAshClass C Class C FlyAshClass C FlyAsh Fly Ash Filler Amount25 25 25 25 (%) Blowing AgentADC/S-C2 L-251ADC/S-C2 ADC/S-C2 ADC/S-C2 L-251 T a 251 Blowing Agent Amount % 1 1 1 1 Blowing ~ 450F/7 mires 450F/7 mires450F/7 mires450F/7 wins -Conditions ' Compression Resistance 16.13 16.13 16.13 16.13 Compression Resistance ASTM D 3676-O1 ASTM D 3575 ASTM D 3575 Method Section 13 Suffix D Suffix D

Used Density 311.4 kg/m n/d n/d n/d Density MethodASTM D 3676-O1 Used Section 12 Compression 11.32 n/d n/d n/d Set Compression ASTM D 3575-00 ASTM D 3575-00ASTM D 3575-00 Set Method Used Su~x B Suffix B Suffix B

Cushion RatingGood Good Good Good Thickness Before/After.077/.176 .047/.170 .065/.165 oz/yd2 31.6 31.6 31.6 31.6 Good looking Good lookingGood lookingGood looking cell cell cell structurelmediumcell structure/mediumstructure/medium uniform Foam Rating uniform struciure/mediumuniform uniform Elk thermallyFreudenburg W.G Steve PET
blend stable filter100% PET (black) 1.6 oz/ydz media 2.9 Seconda Used2.1 oz/ d2 ozl d2 None Secondary Delaminationn/d 17.63 nld 13.3 lb/in Example 2 (Continued) HBEP Type KC8852 KC8852 KC8852 HBEP Amount (%) 50 50 50 Functionalized Polyethylene XU60769.07L XU60769.07L XU60769.07L
T a FP Amount (%) 4 4 4 Elastomeric MaterialBuna EPT 2070 Buna EPT 2070 Buna EPT 2070 Elastomeric Material Amount 20 20 20 (%) Filler Type Class C Fly Class C Fly Ash Class C Fly Ash Ash Filler Amount 25 25 25 (%) Blowing Agent ADC/S-C2 L-251Ficel SL-50 Ficel SL-50 Type Blowing Agent 1 2 2 Amount (%

Blowing Conditions450 F/7 rains 450 F/7 rains 450 F/7 rains Compression Resistance 24.94 26.25 21.5 Compression Resistance MethodASTM D 3575 ASTM D 3575 ASTM D 3575 Used Suffix D Suffix D Suffix D

Density n/d n/d n/d Density Method Used Compression Set 14.36 14.22 17.3 Compression Set ASTM D 3575 ASTM D 3575 ASTM D 3575 Method Used Suffix B Suffix B Suffix B

Cushion Rating Fair Fair Fair Thickness n/d n/d n/d Before/After oz/yd 32.2 - 32.2 -- 32.2 Good looking Good looking Good looking Foam Ratin cell cell cell structure/mediumstructure/mediumstructure/medium uniform uniform uniform Freudenburg W.G Steve PET Freudenburg 100%
Secondary Used 100% blend PET 2.9 oz/yd2 PET 2.9 oz/ydz(black) 1.6 oz/yd2 Secondary 14.73 n/d n/d Delamination lb/in Material Sources as in Example 1.

Example 3 Blowing _Add-on ht oz/ Thickness beforeDensityCompression Wei d2 Agent Foam Cap Coat blowing (inches)lb/ft3 Resistance si 1 J L251 31.6 11.7 0.181 26.05 23.9 1.5 % L251 24.9 11.7 0.181 20.21 14.6 Samples included fiberglass, foam and capcoat.
Capcoat applied before activation of blowing agent. Foam and capcoat comprised of 24% Affinity 8185 4% Amplify GR204 11 % Piccotac 1115 1% Sunpar 150 60% Class C Fly Ash Blowing agent post-added to polymer composition to make foam. Foam blown at 7 mins at 450 °F
Density measurements include contribution of capcoat layer.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope of the invention. Other aspects of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only

Claims (52)

What is claimed is:

1) A foam cushion backing comprising:
a) a foamable polymer composition comprising:
i) one or more of a homogenously branched ethylene polymer (HBEP) or a substantially linear ethylene polymer (SLEP), wherein a foam cushion backing is prepared from the foamable polymer composition, wherein the foam cushion backing has a thickness of greater than 0.075 inches, and wherein the foam cushion backing is suitable for use in carpet or carpet tiles.

2) The foam cushion backing of claim 1, wherein the foam cushion backing is substantially uncrosslinked.

3) The foam cushion backing of claim 1, comprising the SLEP.

4) The foam cushion backing of claim 1 having a thickness of from about 0.100 to about 0.225 inches.

5) The foam cushion backing of claim 1, wherein the foamable polymer composition further comprises an adhesive material, and wherein the adhesive material comprises a functionalized polymer or copolymer.

6) The foam cushion backing of claim 5, wherein the foamable polymer composition comprises from about greater than 0 to about 10 % of the functionalized polymer or copolymer, as measured by total weight of the foamable polymer composition.

7) The foam cushion backing of claim 5, wherein the functionalized polymer or copolymer material comprises maleic anhydride grafted to an ethylene polymer.

8) The foam cushion backing of claim 1, wherein the foamable polymer composition further comprises a filler.

9) A carpet or carpet tile comprising a precoated greige good having a face side and a back side, wherein the precoated greige good has the foam cushion backing of claim 1 affixed to the back side thereof with an adhesive material.

10) The carpet or carpet tile of claim 9, wherein the foam cushion backing is affixed to the back side of the precoated greige good with an adhesive material that is separately applied to either or both of the back side of the precoated greige good and foam cushion backing.

11) The carpet or carpet tile of claim 9, wherein the foam cushion backing is affixed to the back side of the precoated greige good with an adhesive material that is incorporated in the polymer composition.

12) The carpet or carpet tile of claim 9 having a compression set of from about 1 to about 20%, where the % refers to the % recovery of the backing after a 3"
× 3"
sample is compressed at 25% for 22 hours at ambient temperature.

13) The carpet or carpet tile of claim 9 having a compression set of from about 8 to about 20%, as measured by ASTM 3575 Suffix B.

14) The carpet or carpet tile of claim 9 having a compression resistance of from about 5 to about 25 psi, where the psi is measured by compressing a 3" × 3"
sample of backing is compressed across the thickness for 1 minute and the force to recover the thickness is measured, and where the temperature is at ambient.

15) The carpet or carpet tile of claim 9 having a compression resistance of from about 18 to about 32 psi, as measured by ASTM 3575 Suffix D.

16) The carpet or carpet tile of claim 9, wherein the foam cushion backing has an outer surface and wherein the outer surface has a woven or non-woven textile material affixed thereto.

17) The carpet or carpet tile of claim 9, wherein the foam cushion backing has an outer surface and wherein the outer surface has an ethylene polymer cap coat affixed thereto.

18) The carpet or carpet tile of claim 17, wherein the capcoat is present at from about 5 to about 25 oz/yd2.

19) The carpet or carpet tile of claim 9 having a delamination strength of greater than about 2.5 lbs/in as measured byASTM D3936.

20) The carpet or carpet tile of claim 9 having a scrim incorporated on a surface of the foam cushion backing adjacent to the adhesive material.

21) A foam cushion backing comprising:
a) a foamable polymer composition comprising.
i) one or more of a homogenously branched ethylene polymer (HBEP) or a substantially linear ethylene polymer (SLEP); and ii) one or more resilient materials, wherein the foam cushion backing has a thickness of greater than 0.075 inches, and wherein the foam cushion backing is suitable for use in carpet or carpet tiles.

22) The foam cushion backing of claim 21, wherein the resilient material comprises one or more of ethylene-propylene-dime monomer rubber (EPDM), ethylene-propylene monomer rubber (EPM), acrylonitrile-butadiene (NBR), styrene-butadiene (SBR), carboxylated NBR, carboxylated SBR, styrene block copolymer, thermoplastic elastomer and flexible very low density polyethylene resins.

23) The foam cushion backing of claim 22, wherein the resilient material is present in the polymer composition at from about 5 to about 40 % by weight of the foamable polymer composition.

24) The foam cushion backing of claim 21, wherein the foam cushion backing is substantially uncrosslinked.

25) The foam cushion backing of claim 21, comprising the SLEP.

26) The foam cushion backing of claim 21 having a thickness of from about 0.100 to about 0.225 inches.

27) The foam cushion backing of claim 21, wherein the foamable polymer composition further comprises an adhesive material, and wherein the adhesive material comprises a functionalized polymer or copolymer.

28) The foam cushion backing of claim 27, wherein the foamable polymer composition comprises from about greater than 0 to about 10 % of the functionalized polymer or copolymer, as measured by total weight of the foamable polymer composition.

29) The foam cushion backing of claim 27, wherein the functionalized polymer or copolymer material comprises maleic anhydride grafted to an ethylene polymer.

30) The foam cushion backing of claim 21, wherein the foamable polymer composition further comprises a filler.

31) A carpet or carpet tile comprising a precoated greige good having a face side and a back side, wherein the precoated greige good has the foam cushion backing of claim 21 affixed to the back side thereof with an adhesive material.

32) The carpet or carpet tile of claim 31, wherein the foam cushion backing is affixed to the back side of the carpet or carpet tile product with an adhesive material that is separately applied to either or both of the back side of the carpet or carpet tile structure and the foam cushion backing.

33) The carpet or carpet tile of claim 31, wherein the foam cushion backing is affixed to the back side of the precoated greige good with an adhesive material that is incorporated in the polymer composition.

34) The carpet or carpet tile of claim 31 having a compression set of from about 1 to about 20%, where the % refers to the % recovery of the backing after a 3"
× 3"
sample is compressed at 25% for 22 hours at ambient temperature.

35) The carpet or carpet tile of claim 31 having a compression set of from about 8 to about 20%, as measured by ASTM 3575 Suffix B.

36) The carpet or carpet tile of claim 31 having a compression resistance of from about to about 25 psi, where the psi is measured by compressing a 3" × 3"
sample of backing is compressed across the thickness for 1 minute and the force to recover the thickness is measured, and where the temperature is at ambient.

37) The carpet or carpet tile of claim 31 having a compression resistance of from about 18 to about 32 psi, as measured by ASTM 3575 Suffix D.

38) The carpet or carpet tile of claim 31, wherein the foam cushion backing has an outer surface, and wherein the outer surface has an ethylene polymer capcoat affixed thereto.

39) The carpet or carpet tile of claim 38, wherein the capcoat is present at from 5 to about 25 oz/yd2.

40) The carpet or carpet tile of claim 31 wherein the foam cushion backing has an outer surface, and wherein the outer surface has a woven or non-woven textile backing affixed thereto.

41) The carpet or carpet tile of claim 31 having delamination strength of greater than 2.5 lbs/in as measured by ASTM D3936.

42) The carpet or carpet tile of claim 31 having a scrim incorporated on a surface of the foam cushion backing adjacent to the adhesive material.

43) A method for making a foam cushion backing suitable for use in a carpet or carpet tile, wherein the method comprises:
a) providing a polymer composition comprising:
i) one or more of a homogenously branched ethylene polymer ("HBEP") or a substantially linear ethylene polymer ("SLEP"); and ii) a blowing agent;
b) applying the polymer composition to a surface suitable to provide a foam cushion backing after activation of the blowing agent; and c) activating the blowing agent, thereby providing a foam cushion backing suitable for use in a carpet or carpet tile, wherein the foam cushion backing has a thickness of greater than about 0.075 inches.

44) The method of claim 43, further comprising providing a precoated greige good, wherein the surface is the precoated greige good, and wherein the blowing agent is activated after application of the polymer composition to the greige good, thereby providing a carpet structure having a foam cushion backing adhered thereto.

45) The method of claim 44, wherein the carpet structure having the foam cushion backing adhered thereto has a delamination strength of greater than about 2.5 lbs/in as measured by ASTM D3936.

46) The method of claim 43, further comprising providing a precoated greige good, wherein the foam cushion backing is laminated to the precoated greige good with an adhesive material after activation of the blowing agent.

47) The method of claim 43, wherein the polymer composition comprises a filler.

48) The method of claim 43, wherein the polymer composition comprises a resilient material.

49) The method of claim 48, wherein the resilient material comprises one or more of:

ethylene-propylene-dime monomer rubber (EPDM), ethylene-propylene monomer rubber (EPM), acrylonitrile-butadiene (NBR), styrene-butadiene (SBR), carboxylated NBR, carboxylated SBR, styrene block copolymer, thermoplastic elastomer and flexible very low density polyethylene resins.

50) The foam cushion backing of claim 49, wherein the resilient material is present in the polymer composition at from about 5 to about 40 % by weight of the foamable polymer composition.

51) The method of claim 46, wherein the foam cushion backed carpet structure has a delamination strength of greater than about 2.5 lbs/in as measured by ASTM
D3936.

52) The method of claim 43, further comprising introducing a scrim onto the foamable polymer composition prior to activation of the blowing agent, thereby providing a foam cushion backing having a scrim attached to a side thereof.