CA2583268A1 - Self crosslinking waterborne coatings - Google Patents
Self crosslinking waterborne coatings Download PDFInfo
- Publication number
- CA2583268A1 CA2583268A1 CA002583268A CA2583268A CA2583268A1 CA 2583268 A1 CA2583268 A1 CA 2583268A1 CA 002583268 A CA002583268 A CA 002583268A CA 2583268 A CA2583268 A CA 2583268A CA 2583268 A1 CA2583268 A1 CA 2583268A1
- Authority
- CA
- Canada
- Prior art keywords
- coating
- monomer
- weight
- poly
- coating composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An aqueous coating composition comprising (i) a binder resin having latent crosslinking functionality, (ii) a crosslink for the resin, and (iii) polymeric extender particles is disclosed.
Claims (21)
1. An aqueous coating composition comprising:
(i) a binder resin having latent crosslinking functionality;
(ii) an effective crosslinking amount of a crosslinker for the binder resin;
(iii) polymeric extender particles.
(i) a binder resin having latent crosslinking functionality;
(ii) an effective crosslinking amount of a crosslinker for the binder resin;
(iii) polymeric extender particles.
2. The coating of claim 1 wherein the latent crosslinking functionality comprises carbonyl groups.
3. The coating of claim 2 wherein the crosslinking agent is selected from the group consisting of di and poly amines, di and poly hydrazides, and di and poly hydrazines and mixtures thereof.
4. The coating of claim 1 wherein the binder resin is a latex resin.
5. The coating of claim 4 wherein the latex resin is the polymerized reaction product of a mixture of monomers comprising:
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 60 to about 98.5% of at least one other copolymerizable monomer.
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 60 to about 98.5% of at least one other copolymerizable monomer.
6. The coating of claim 5 wherein the monomer having latent crosslinking functionality has pendent carbonyl groups as reactive crosslinking sites.
7. The coating of claim 2 wherein the crosslinker is selected from the group consisting of di and poly amines, di and poly hydrazides, and di and poly hydrazines.
8. The coating of claim 4 wherein the latex resin is the polymerized reaction product of a mixture of monomers comprising:
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 0.1 to about 10% of a wet adhesion promoting monomer; and (iv) about 50 to about 98.4% of at least one other copolymerizable monomer.
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 0.1 to about 10% of a wet adhesion promoting monomer; and (iv) about 50 to about 98.4% of at least one other copolymerizable monomer.
9. The coating of claim 8 wherein the monomer having latent crosslinking functionality has pendent carbonyl groups as reactive crosslinking sites.
10. The coating of claim 9 wherein the crosslinker is selected from the group consisting of di and poly amines, di and poly hydrazides, and di and poly hydrazines.
11. The coating of claim 4 wherein the latex resin is the polymerized reaction product of a mixture of monomers comprising:
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 0.1 to about 10% of a wet adhesion promoting monomer;
(iv) about 1 to about 55% by weight of styrene; and (v) zero to about 98.4% by weight of at least one other copolymerizable monomer.
(i) about 1 to about 25% by weight of a monomer having latent crosslinking functionality;
(ii) about 0.5 to about 15% by weight of an acid functional monomer;
(iii) about 0.1 to about 10% of a wet adhesion promoting monomer;
(iv) about 1 to about 55% by weight of styrene; and (v) zero to about 98.4% by weight of at least one other copolymerizable monomer.
12. The coating of claim 1 wherein the extender particles comprise polyvinyl chloride particles.
13. The coating of claim 12 wherein the polyvinyl chloride particles have an average particle size greater than 5 microns.
14. The coating of claim 13 wherein the polyvinyl chloride particles have an average particle size of 5 to about 150 microns.
15. The coating of claim 12 wherein the polyvinyl chloride extender particles are homopolymers of vinyl chloride.
16. The coating composition of claim 1 wherein the polymeric extender particles are present at about 5 to about 60 weight percent on a solids basis of the coating composition.
17. The coating composition of claim 16 wherein the polymeric extender particles are present at a level of about 25 to about 50 weight per cent on a solids basis of the coating composition.
18. The coating composition of claim 1 wherein the crosslinker is present at a level to provide at least 0.1 equivalent for each equivalent of latent crosslinking functionality.
19. The coating composition of claim 1 wherein the crosslinker is present at a level to provide about 0.2 to about 2.0 equivalents for each equivalent of latent crosslinking functionality.
20. The coating composition of claim 1 wherein the crosslinker is present at a level to provide about 0.4 to about 1.2 equivalents for each equivalent of latent crosslinking functionality.
21. A coating composition comprising:
(i) a binder resin obtained by polymerizing a monomer mixture comprising:
(a) about 1 to about 25% by weight of a monomer having carbonyl latent crosslinking functionality;
(b) about 0.5 to about 15% by weight of an acid functional monomer;
(c) about 0.1 to about 10% of a wet adhesion promoting monomer; and (d) about 50 to about 98.4% of at least one other copolymerizable monomer.
(ii) a crosslinker selected from the group consisting of di and poly amines, di and poly hydrazides, and di and poly hydrazines;
(iii) polyvinyl chloride extender particles.
(i) a binder resin obtained by polymerizing a monomer mixture comprising:
(a) about 1 to about 25% by weight of a monomer having carbonyl latent crosslinking functionality;
(b) about 0.5 to about 15% by weight of an acid functional monomer;
(c) about 0.1 to about 10% of a wet adhesion promoting monomer; and (d) about 50 to about 98.4% of at least one other copolymerizable monomer.
(ii) a crosslinker selected from the group consisting of di and poly amines, di and poly hydrazides, and di and poly hydrazines;
(iii) polyvinyl chloride extender particles.