CA2723172A1 - Wound dressing devices and methods - Google Patents

Abstract

The present invention provides an absorbent wound dressing assembly that can be used to stanch, seal, or stabilize a site of tissue injury, tissue trauma, or tissue access. The wound dressing assembly is flexible so that it can be adapted and used to fit in narrow and small wound sites. Generally the wound dressing assembly comprises a flexible carrier material that is impreg-nated with a non-mammalian material for control of severe bleeding. The preferred non-mammalian material is poly [(.beta.- (1-.fwdarw.4) -2-amino-2-deoxy-D-glucopyranose] more commonly referred to as chitosan.

Description

Wound Dressing Devices And Methods Related Applications The present application claims priority to U.S. provisional application, Serial No. 61/049,831, filed on 2 May 2008.
Background of the Invention The present invention is related to flexible wound dressings and more specifically to flexible wound dressings that have therapeutic qualities.
Controlling bleeding, fighting infection and improving wound healing are major medical issues.
Methods to control bleeding and repairing wounds have existed for many years. Traditional surgical hemostatic techniques have included applying pressure, cauterizing, and suturing. Over the past 20 years, a number of hemostatic agents and tissue sealants have been developed and are currently used in various surgical disciplines.
The hemostatic agents act to stop bleeding either mechanically or by augmenting the coagulation cascade, whereas tissue sealants are products that bind to and close defects in tissue. Currently there are five major classes of the hemostatic agents and tissue sealants for surgical use, including fibrin glue, bovine collagen and thrombin, cyanoacrylate, polyethylene glycol polymer, and albumin crosslinked with glutaraldehyde. These hemostatic agents are mainly composed of allogeneic or hetreallogeneic proteins.
Recently, chitosan based hemostatic dressings have been. shown to control aggressive hemorrhages from severe. external injuries. The chitosan dressing acts to control severe hemorrhagic bleeding by first sealing the wound site followed by promotion of local blood coagulation. An external form of this chitosan wound dressing was cleared by the Food and Drug Administration for external temporary control of severely bleeding wounds intended for emergency use.
However, in some applications, for example, a narrow entry wound, current chitosan and nonchitosan based wound dressing are not effective at providing hemostasis, fighting infection and/or promoting wound healing. Currently available dressings are often too stiff and too rigid to fit in a narrow space or they are too flexible and porous to efficiently promote hemostasis. Powder based hemostatic products also have limited effectiveness as they are difficult to apply to bleeding sites through narrow wound entries.
Summary of the Invention The present invention provides a wound dressing assembly that can be used to stanch, seal, or stabilize bleeding at a site of tissue injury, tissue trauma, or tissue access. The wound dressing assembly is flexible so that it can be adapted and used to fit in narrow and small wound sites, while still providing sufficient stiffness at small wound sites so that it can properly address the wound site, promote hemostasis, and also capable of properly fitting to the wound.
Generally the wound dressing assembly comprises a flexible carrier material that is impregnated with a non-mammalian material for control of severe bleeding. The preferred non-mammalian material is poly [(3-(1.4)-2-amino-2-deoxy-D-glucopyranose] more commonly referred to as chitosan. The combination of the chitosan on the carrier strip provides a unique structure, wherein the chitosan material forms films and layers extending between individual fibers interstices that comprise the carrier strip, with the films being dispersed in a varied arrangement throughout the dressing assembly.
An advanced supple wound dressing assembly for control of severe, life-threatening bleeding should preferably have the following properties:
i) easily and quickly applied in one step after removal from package;
ii) rapid and strong blood clotting;
iii) at least a minimal level of tissue adhesion;
iv) strong internal cohesive properties;
v) rapid and strong wound sealing;
vi) resistant to dissolution under strong blood flow;
vii) able to be. treated roughly without compromising efficacy;
viii) the dressing assembly must be flexible enough so that it can address narrow and oddly shaped wound sites, while having sufficient stiffness to allow for concentration of blood sells throughout the dressing assembly when being used.
Other features and advantages of the invention shall be apparent based upon the accompanying description, drawings, and claims.
Brief Description of the Drawings Figure 1A is a perspective view of a prior art wound-dressing assembly, where seepage from the wound is shown spreading outwardly from the wound dressing.
Figure 1B is a perspective view of another prior art dressing assembly, wherein the dressing is not sufficiently flexible to properly cover the wound.
Figure 2 is a perspective view of an absorbable wound dressing assembly in accordance with the present invention.
Figure 3 is a pictorial depiction of a dry wound dressing assembly according to the present invention, demonstrating a chitosan material being attached to a dressing matrix.
Figure 4 is a pictorial depiction of the wound dressing assembly shown in Figure 3, demonstrating the assembly absorbing fluids, thereby causing the chitosan materials in the assembly to allow the individual fluid cells.to coagulate on the chitosan material.
Figure 5 is a three-dimensional depiction of the wound dressing assembly of Figure 4, demonstrating the arrangement of the dressing matrix fibers and the attached chitosan material, with the individual cells coagulating on within the dressing assembly.
Figure 6 is a perspective view of the wound dressing assembly shown in Figure 2 being applied to a wound to stanch the bleeding of the wound.
Figure 7A shows the wound dressing assembly of Figure 2 and 6 being inserted into a narrow wound site to stanch the blood flow from the wound site and further promote hemostasis.
Figure 7B shows the wound dressing assembly of Figures 2 and 6 administered on a wound and minimizing seepage of the wound outside of the wound dressing assembly.
Figure 8 is a schematic representation of a chitosan solution being applied to the carrier strip for the wound dressing assembly by soaking the carrier strip in the chitosan solution.
Figure 9 is a schematic representation of a -chitosan solution being applied to the carrier strip by spraying the carrier strip with the chitosan solution.
Figure 10 is a schematic representation of a chitosan solution being applied to the carrier strip by 5 passing the carrier strip through a set of rollers.
Figure 11 is a schematic representation of a dry chitosan powder being added to the carrier strip for the wound dressing assembly, either with or without a liquid chitosan solution being applied to the carrier strip.
Figure 12 is a schematic representation of excess liquid and/or chitosan powder being removed from a wound dressing matrix after the chitosan material has been applied to the wound dressing matrix.
Figure 13 is an alternate schematic representation of excess liquid and/or chitosan powder being removed from the carrier strip after the chitosan material has been administered to the carrier strip.
Figure 14 depicts the wet wound dressing assembly comprising the chitosan material and the carrier strip being heated within the oven to dry the wound dressing assembly.
Figure 15 shows the dried wound dressing assembly being stored within a pouch until the wound dressing assembly is to be used.
Figure 16 is a perspective, exploded view of an alternate wound dressing assembly in accordance with present invention, with the dressing assembly further comprising a layer of adhesive material.
Figure 17 provides scanning electron micrograph (SEM) images (5X resolution) of wound dressing assemblies according to the present invention, with the images demonstrating wound dressing assemblies having various densities.
Figure 18 shows an SEM image of a wound dressing assembly according to the present invention, wherein a cotton fiber material is coated with a therapeutic agent comprising 1% chitosan.
Figure 19 showing a magnified view of the SEM
image of Figure 18.
Figure 20 shows an SEM image of a wound dressing assembly according to the present invention, wherein a cotton fiber material is coated with a therapeutic agent comprising 2% chitosan and the wound dressing assembly has expanded with the absorption of a fluid.
Figure 21 provides a scanning electron micrograph (SEM) image of a dressing material developed according to the present invention prior to interacting with blood.
Figure 22 provides a scanning electron micrograph (SEM) image of-human blood interacting with a dressing material that does incorporates chitosan material, demonstrating marked blood cells accumulation and aggregation on the surface of assembled dressing.
Figure 23 is a graph showing the effect of drying temperatures on various wound dressing assemblies compared to the resultant contact angle for the various assemblies.
Figure 24 is a graph comparing the adhesion strength for wound dressing assemblies with various amounts of chitosan material.
Figure 25 is a graph comparing the adhesion strength of wound dressing assemblies with various amounts of lactic acid added to the dressing assemblies.
Figure 26 is a graph comparing various dressing assemblies and the flexibility of those dressing assemblies based on values for the Taber Stiffness Scale.
Figure 27 provides a table comparing qualities of various wound dressing assemblies developed according to the present invention, as well as comparing the wound dressing assemblies to prior art dressing assemblies.
Figure 27A provides another table comparing qualities various wound dressing assemblies developed according to the present invention, as well as comparing the wound dressing assemblies to prior art dressing assemblies.
Figures 28 - 39 are various scanning electron micrograph (SEM) images of various wound dressing assemblies comprising various carrier strips.
Figure 40 is a scanning electron micrograph (SEM) image of a prior art dressing assembly interacting with blood.
Figures 41-43 are various scanning electron micrograph (SEM) images of various wound dressing assemblies according to the present invention interacting with blood.
Description of the Preferred Embodiment Although the disclosure hereof is detailed and exact to enable those skilled in the art to practice the invention, the physical embodiments herein disclosed merely exemplify the invention which may be embodied in other specific structures. While the preferred embodiment has been described, the details may be changed without departing from the invention, which is defined by the claims.
The application is generally organized as follows:
A. Overview of the Wound Dressing Assembly and Its Uses B. Manufacture of the Wound Dressing Assembly C. Physical Description of the Wound Dressing Assembly I. Preparation of A Chitosan Solution II. Description of the Absorbable Carrier III. Physical Characteristics D. Results E. Other Uses of the Wound Dressing Assembly A. Overview of the Wound Dressing Assembly And Its Uses Figures 1A-7B provide a general overview of a wound dressing assembly 20 according to the present invention, with the assembly 20 compared to structures of the prior art to demonstrate the improved physical adaptability of the present invention. An arm 10 having a wound site 12 is depicted in the Figures with different assemblies addressing the wound site 12.
Figure 1A shows a prior art gauze style assembly 14 wrapped around the arm 10 to cover the wound 12. The assembly 14 is flexible (i.e., not stiff) so it is capable of being wrapped around the arm 10 so that the wound site 12 is tightly covered. Still, the assembly 14 is not capable of stanching the flow of blood from the wound site 12 as desired. The volume of blood that flows into the assembly 14 prior to coagulation exceeds the absorbance capacity of the assembly 14. Not being absorbed by the assembly 14, excess blood flows outward from the wound site and beyond the periphery of the assembly 14. Further, the assembly 14 is free of a hemostatic material that is desired to accelerate or otherwise promote hemostasis. For these reasons, the assembly 14 is not completely effective at treating the wound site 12.
Figure 1B shows another prior art pad style assembly 16 being applied to the wound site 12. As demonstrated, the assembly 16 includes a hemostatic material that accelerates or otherwise promotes hemostasis, and is thereby capable of stanching the flow of blood at the wound site. Still, the assembly 16 is stiff (i.,e., not flexible), and cannot be wrapped around the arm 10 to hold the assembly 16 in place. If the assembly 16 is to be held in place, outside pressure needs to be applied to the assembly 16. Furthermore, if the wound site 12 is small or narrow, the assembly 16 may be too rigid to properly address the wound site 12.
Figure 2 shows a supple wound dressing assembly 20 that embodies features of the present invention. The supple dressing assembly 20 comprises a flexible carrier structure 22 made from of a blood-absorbable material. The supple dressing assembly further includes a biocompatible, hemostatic material 24, preferably a chitosan material 24, deposited within the interstices of the carrier structure 22.
A close-up,representation of the arrangement of the supple wound dressing assembly 20 is demonstrated in Figures 3-5. Figure 3 represents the supple wound dressing assembly 20 in a dry state before being applied to a wound. The individual fibers of the carrier strip 22 provide a supporting' structure for the chitosan material 24, which forms various dispersed web-like structures between the individual fibers. When the carrier strip 22 is treated with the chitosan material 24, which will be described further, below, the chitosan material 24 will adhere to the individual fibers that make up the carrier strip 22, and, surprisingly, also will form thin layers or membranes of material interspersed between the various individual fibers 22.
In Figure 4, the dressing assembly 20 is shown absorbing a fluid, i.e. blood, with the membranes of chitosan material 24 formed between the individual fibers of the carrier strip 22 collecting the majority of the individual red blood cells.
While prior art and conventional wisdom would indicate that the chitosan material 24 would be coated onto the carrier strip 22 and would outwardly fill in the area around and between the individual carrier strip fibers in the carrier strip 22, the present invention provides an unexpected arrangement. That is, there are voids retained in the assembly 20, as shown in Figure 19, with the chitosan material 24 also forming webs of material between various fibers and not necessarily coating those fibers. This lack of "solidification" of the saturated assembly 20 has a further advantage over prior dressing assemblies. The webs increase the surface area of the carrier strip, while still maintaining permeability. Not only does the arrangement let further blood seep into the dressing assembly 20, it also allows blood cells to aggregate and accumulate on the web-like areas of chitosan material 24 located in the dressing 20.
The unique arrangement will be evidenced more distinctly with respect to magnified views of the dressings. (scanning electron micrograph (SEM) images) (Figures 18-22 and 28-43). For example, Figure 21 provides a supple dressing assembly 20 prior to interaction with blood, while Figure 22 shows the assembly of Figure 21 after interaction with blood cells.
The blood cells are shown accumulating on the various webs of chitosan material 24. These features will be discussed in further detail, below in Part C.
The dressing assembly 20 is characterized by a unique combination of suppleness or multi-dimensional flexibility, with a permeability and absorbance capacity to blood flow, that enhance the hemostatic capacity of the hemostatic material 24 to stanch blood flow at a wound site. As Figs. 6, 7A, and 7B show, the dressing assembly 20 can be flexed, bent, folded, twisted, and even rolled upon itself before and during use, without creasing, cracking, fracturing, otherwise compromising the integrity and mechanical and/or therapeutic characteristics of the hemostatic material 24 it carries.
As shown in Figure 6, the supply dressing assembly 20 can be applied to the wound site 12 of the arm 10 in the manner of a conventional gauze wound dressing. The supply dressing assembly 20 is capable of being wrapped around the arm 10 to securely and independently apply pressure to the wound site. Further, as depicted in Figure 7B, the flexible carrier structure 22 possesses the permeability and absorbance capacity to blood, so that blood exiting the wound site 12 stays localized within the confines of the assembly 20 and does not flow around and outside the periphery of the assembly 20. The blood is thereby brought into contact with the hemostatic material 24 that is carried within the interstices of the dressing assembly 20, to thereby stanch blood flow at the wound site 12.
The supple dressing assembly 20 provides a flexible structure 22 that can be adapted to a wide variety of wound shapes and areas, while the deposition of the hemostatic material 24 within the flexible structure 22 provides significant benefits in stanching and therapeutically treating a wound site 12.
Figure 7A provides a further example of the flexibility and adaptability of the present invention.
The dressing assembly 20 is shown not being wrapped around the arm 10 as depicted in Figure 7B, but being inserted directly into the wound site 12. This is advantageous for deep, narrow, wounds and for quickly providing therapeutic qualities to the wound site 12.
The unique dressing assembly 20 can be characterized by a suppleness or multi-dimensional flexibility in terms of a Gurley stiffness value (in units of milligrams) (length X width) of not greater than about 10,000 (using a Gurley Stiffness Tester Model 4171D
manufactured by Gurley Precision Instruments of Troy, New York, and Gurley ASTM D6125-97) It is believed that a dressing assembly 20 having a Gurley stiffness value (in units of milligrams) greater than about 10,000 does not possess the requisite suppleness or multi-dimensional flexibility to be flexed, bent, folded, twisted, and even rolled upon itself before and during use, and thereby comprising the integrity and/or mechanical and/or therapeutic characteristics of the hemostatic material 24 carried by assembly 20. However, the dressing assembly 20 should not have a Gurley stiffness value that is too low, as there will not be sufficient blood absorbance capacity within such an assembly. For example, a dressing assembly below a Gurley stiffness number below 200 is not preferable. The unique dressing assembly is characterized by. a suppleness or multi-dimensional flexibility in terms of a Gurley stiffness value (in units of milligrams) between about 200-10,000, preferably between about 200-8000 and most desirably, between or about 500-6000.
The supple assembly 20 can also be characterized by a permeability to blood flow expressed in terms of a mean blood flow (in units of ml/sec). Blood flow is measured using the following procedure. A test piece of the dressing assembly that is 1" wide by the necessary length to achieve 0.8g is inserted into a 10cc plastic syringe with a diameter of 1cm containing 3cc of citrated whole bovine blood. Manual pressure is applied to the sample for 2 minutes. The syringe is then attached to a tubing line with 60mmHg pressure of citrated whole bovine blood. The syringe is inverted and the rate at which blood flows through the dressing is recorded. It is believed that a dressing assembly 20 having a permeability that is less than about 0.1 ml/s, preferably not less than 0.15 ml/s, possesses too much resistance to blood flow that will lead to blood finding paths of lesser resistance outside the confines of the assembly, thereby shunting blood flow away the hemostatic material 24 carried within the interstices of the assembly 20. Similarly, a permeability that is too high will limit the effectiveness of a hemostatic material on a dressing assembly, as.it will not provide sufficient impedance for the blood as it passes through the assembly. The unique dressing assembly 20 is characterized by a permeability to blood flow (in units of ml/sec) between about 0.1 - 0.5 ml/s and most desirably, between about 0.15 - 0.35 ml/s.
The supple assembly 20 can also be characterized by an absorbance capacity for blood in terms of a mean absorbance (in units of g/g). Total blood absorbancy is measured according to the following procedure. A 2" x 2" test piece of the dressing assembly is pre-weighed (W1) and placed in citrated whole blood for 2 minutes. The sample is removed from the blood and the excess blood is allowed to drip off for 30 seconds.
The sample wetted with blood is weighed (W). The total blood absorbance capacity is calculated as (W1-W)/W.
Optimal absorbance capacity will be maintained in the present dressing assemblies 20 while possessing the qualities discussed above. It is believed that a dressing assembly 20 having an absorbance capacity that is less than about 5 g/g does not possess the requisite ability to absorb blood into the interstices of the assembly into contact with the hemostatic material 24.
Like the lack of requisite permeability, the lack of requisite absorbance capacity will lead to blood flow outside the confines of the assembly, thereby shunting blood flow away the hemostatic material 24 carried within the interstices of the assembly 20. The unique dressing assembly 20 is characterized by an absorbance capacity for blood (in units of g/g) of not less that about 5 g/g, and most desirably, between about 5-15 g/g.
The single drop absorption time, which is generally characterized as the time for a single sessile 20 l drop of blood to decrease in volume to a 5 Al drop of blood, for the dressing assembly 20 is in a preferred range, as well. The time, expressed in seconds, is preferably between 20-300 seconds, and,_`more preferably between 60-240 seconds.
The supple assembly 20 is characterized by the unique properties discussed above. The described assembly provides unique permeability, absorbance, and stiffness qualities, thereby providing an assembly that has effective and advantageous qualities of both stiffer and flexible prior art assemblies. The qualities of the 15 dressing fall within a range not previously realized with hemostatic dressings, wherein the dressing has the adaptability characteristics of prior art gauze-style dressings, while providing hemostasis similar to pad-type products'.
B. Manufacture of the Wound Dressing Assembly A desirable methodology for making the wound dressing assembly 20 will now be described. It should be realized, of course, that other methodologies can be used. Generally speaking, the methodology consists of providing a solution of chitosan material 24, applying the solution to a carrier strip 22, removing excess solution from the carrier strip 22, and drying the carrier strip 22 to form the supple dressing assembly 20.
Figures 8-10 depict various methods that can be employed to apply the chitosan -solution to the carrier strip 22. Generally speaking, the carrier strip 22 must be sufficiently wetted, either by directly placing the carrier strip 22 into the chitosan solution, or first submerging the carrier strip 22 into an aqueous solution, and then applying a chitosan material to the carrier strip. Wetting or soaking times are between 0-72 hours, with a typical soaking time being between 0-16 hours, with a more preferable soaking being between about 0-4 hours.
Figure 8 provides a container 30 containing the chitosan solution 24. The carrier strip 22 will be submerged within the container 30, thereby absorbing the chitosan solution 24 onto the carrier strip 22.
Figure 9 demonstrates the chitosan solution 24 being applied to the carrier strip 22 by way of a spraying device 40. An example of such a spraying device could be an electrospraying device.
Figure 10 shows the carrier strip 22 being fed through a rolling member 50 to mechanically integrate the chitosan material into the carrier strip 22. The rolling member will be in contact with the container 30 containing the chitosan solution 24, thereby transferring the chitosan solution onto the carrier strip 22 as the carrier strip 22 passes through the rolling member 50.
It should be understood that any process involving the addition of the chitosan solution 24 to the carrier strip 22 must be of a sufficient time so that the carrier strip 22 will thoroughly absorb the chitosan solution. In certain embodiments of the present invention, the chitosan solution 24is effectively immediately absorbed into the carrier strip 22. It also should be noted that dry chitosan material could be applied directly to the carrier strip 22 after the carrier strip 22 has been wetted, i.e. after the carrier strip 22 absorbs the chitosan solution 24. As shown in Figure 9, dry chitosan flake 26 can be coated on the wetted carrier strip 22. Once the chitosan solution 24 and/or chitosan 26 have been applied to the carrier strip 22, the excess solution 24 (and dry chitosan flake 26) will be removed from the carrier strip 22. Figures 12 and 13 demonstrate possible methods for removing excess chitosan solution 24 and/or chitosan flake 26 from the carrier strip 22. In Figure 12, the carrier strip 22 is run past a squeegee 60, to remove excess material from the strip 22. The squeegee method adds an additional mechanical softening process, increases the surface area, and lengthens the fibers of the carrier strip that will improve the stiffness, permeability, and blood interaction characteristics of the dressing assembly.
In Figure 13, the carrier strip 22 is run past a rolling member 70, thereby removing excess material from the carrier strip. Other devices, such as scrapers or trowels, may be used to remove excess material.
Further, excess chitosan flake 26 may be removed from the strip by shaking the carrier strip 22 or blowing compressed air over the carrier strip 22. Preferably, a range of about 1-100 grams of chitosan solution is used per every gram of carrier strip 22 (dry weight), with a preferred range being from about 1-10 grams being used, and a more preferred range being from about 5-6 grams being used per one gram of dry carrier strip 22 material.
Referring further to the methods described in Figures 12 and 13, the various methods for removing excess solution can potentially alter the final characteristics of the supple dressing assembly 20.
Figures 27 and 27A provides characteristics of various supple dressing assemblies 20. Particularly, the assemblies referred to in Figure 27 as 100808, 120808 were prepared according to the method described with respect Figure 12, and the dressing assembly referred to as 08-XL-045 was prepared according to the method described with respect to Figure 13. For Figure 27A, the methods are noted, with the "squeegee" removal technique referring to the method of Figure 12 and the "rolling member" technique referring to the method of Figure 13.
Each of the carrier strips 22 for the three assemblies 20 had the same composition, and the same amount of chitosan material 24 was applied to the carrier strips 22. The results indicate that 100808, 120808, i.e. the assemblies 20 prepared according to the squeegee method, have a lower Gurley stiffness value than the assemblies 20 made without using the squeegee method.
After removal of the excess solution 24 and/or chitosan flake 26, the carrier strip 22 will be placed within an oven 80 to heat and dry the carrier strip 22 to form the wound dressing assembly 20, as shown in Figure 14. The oven 80 could be of various types of ovens or heaters, such as a conveyor oven, multideck oven, a microwave vacuum dryer, infrared dryer, or infrared heater. Depending on the type of oven used, and possibly the addition of an adhesive material 23 to the carrier strip 22, the drying time is preferably between about 1-24 hours, more preferably between about 12-24 hours, with overnight drying generally being standard procedure.
Similarly, the drying temperature normally can be between 22 -100 C, more preferably between 40 -90 C and more preferably between 50 -70 C.
After drying is complete, the wound dressing assembly 20 can be subsequently packaged in a pouch 28 as shown in Figure 15, which is desirably purged with an inert gas such as either argon or nitrogen gas, evacuated and heat sealed. The pouch 28 acts to maintain interior contents sterility over an extend time (at least 24 months) and also provides a very high barrier to moisture and atmospheric gas infiltration over the same period.
After pouching, the processed supple wound dressing assembly 20 is desirably subjected to a sterilization step. The wound dressing pad assembly 20 can be sterilized by a number of methods. For example, a preferred method is by irradiation, such as by gamma irradiation, which can further enhance the blood dissolution resistance, the tensile properties and the adhesion properties of the wound dressing. The irradiation can be conducted at a level of at least about 5 kGy, more preferably a least about 10 kGy, and most preferably at least about 25 kGy.
In an alternative step, an adhesive material 23 may be used to bind the carrier strip 22 with the chitosan material 24, which is shown in Figure 16.
Preferably, the adhesive material 23 would be added to the carrier strip 23 prior to addition of the chitosan material 24. Examples of adhesive materials could be lactic acid or polyacrylic acid (PAA). Typically, one is looking for ability to uniformly and robustly apply a final coat layer as efficiently as possible, as to enhance mating of base and top layer, i.e. the carrier strip 22 and the biocompatible material 24.

The following two examples demonstrate general preparation methods for a wound dressing assembly according to the present invention. More detailed examples are described with respect to the table shown in Figure 27 and will be discussed in further detail, below, in Section C.

Example 1 A cotton gauze (i.e. carrier strip 22) was soaked in 1% chitosan and 2% acetic acid solution (chitosan material 24) for 12 hours. The gauze was stirred dry in an oven at 50 C for 24 hours. The dry gauze (i.e. the wound dressing assembly 20) was then rolled and packaged in a heat-sealable pouch. The package was sterilized using gamma irradiation. The wound dressing assembly 20 had a moisture content of 1.58 0.440, with the residual volatile acid content ranging from between 1 to 3.5%.

Example 2 A cotton-made gauze (i.e. carrier strip 22) was soaked in 1% chitosan and 2% acetic acid solution (chitosan material 24) for 12 hours. A chitosan powder (26) pretreated with acetic was coated on the gauze. The chitosan powder had a particle size of between 200 to 400 mesh and emitted zero or near zero volatile organic compounds. The excess powder was removed from the gauze, and the gauze was dried in an oven at 50 C for approximately 24 hours. The dry gauze (i.e. the wound dressing assembly 20) was then rolled and packaged in a heat-sealable pouch. The package was sterilized using gamma irradiation.
The resultant wound dressing assembly 20 is capable of stanching the flow of blood and other bodily fluids at a wound site, as shown and described above with respect to Figures 2-.7B. The improved absorbency and efficacy of the wound dressing is further described and discussed in the following section that described the physical properties of the dressing assembly.

C. Physical Properties of the Wound Dressing Assembly I. Biocompatible Material The biocompatible material 24 of the wound dressing assembly 20 comprises a non-mammalian material, which is most preferably poly [13-(1-.4)-2-amino-2-deoxy-D-glucopyranose, which is more commonly referred to as chitosan. The chitosan selected for the matrix preferably has a weight average molecular weight of at least about 100 kDa, and more preferably, of at least about 150 kDa.
Most preferably, the chitosan has a weight average molecular weight of at least about 300 kDa.
The chitosan used to prepare the chitosan solution preferably has a fractional degree of deacetylation greater than 0.75 but less than 0.97. Most preferably the chitosan has a fractional degree of deacetylation greater than 0.85 but less than 0.95.
Preferably the chitosan selected for processing into the matrix has a viscosity at 25 C in a 2%(w/w) solution of 2%(w/w) acetic acid (AA) with spindle LVI at 30 rpm, which is about 100 centipoise to about 2000 centipoise.
More preferably, the chitosan has viscosity at 25 C in a 2%(w/w) solution of 2%(w/w) acetic acid (AA) with spindle LVI at 30 rpm, which is about 100 centipoise to about 1000 centipoise. Most preferably, the chitosan has viscosity at 25 C in a 2%(w/w) solution of 2%(w/w) acetic acid (AA) with spindle LV1 at 30 rpm, which is about 100 centipoise to about 500 centipoise.
The chitosan solution is preferably prepared at 25 C by addition of water to solid chitosan flake or powder and the solid dispersed in the liquid by agitation, stirring or shaking. On dispersion of the chitosan in the liquid, the acid component is added and mixed through the dispersion to cause dissolution of the chitosan solid. The rate of dissolution will depend on the temperature of the solution, the molecular weight of the chitosan and the level of agitation. Preferably the dissolution step is performed within a closed tank reactor with agitating blades or a closed rotating vessel. This ensures homogeneous dissolution of the chitosan and no opportunity for high viscosity residue to be trapped on the side of the vessel. Preferably the chitosan solution percentage (w/w) is greater than 0.5%
chitosan and less than 4.0% chitosan. More preferably the chitosan solution percentage (w/w) is greater than 1%
chitosan and less than 2.3% chitosan. Most preferably the chitosan solution percentage is greater than 1.0%
chitosan and less than 2.01 chitosan. Preferably the acid used is acetic acid. Preferably the acetic acid is added to the solution to provide an acetic acid solution percentage (w/w) at more than 0.81 and less than 4.0%.
More preferably the acetic acid is added to the solution .to provide an acetic acid solution percentage (w/w) at more than 1.5% (w/w) and less than 2.5%.
An adhesive material may be added to the chitosan material, as well. The dressing assembly may be capable of forming an adhesive material in combination with blood flowing from said wound at a wound dressing-blood interface. Preferably, the adhesive material, when hydrated by interaction with the blood interface, preferably has a pH of not less than about 5.5 when the wound is sealed. More preferably, the adhesive material preferably has a pH of not more than about 6.5 when the wound is sealed. Most preferably, the adhesive material preferably has a pH of not more than about 7.5 when the wound is sealed. Preferably, the adhesive material comprises an acid selected from the group consisting of acetic acid, formic acid, lactic acid, ascorbic acid, hydrochloric acid, and citric acid.
The wound dressing of the present invention has at least a minimal degree of adhesion to the wound site. Prior art carrier strips generally display no degree of adhesion. Preferably, the degree of adhesion is between 1 and 40kPa, and more preferably between about 10-40 kPa.
II. Description of the Absorbable Carrier strip The absorbable carrier strip 22 used in the present invention generally comprises a flexible material, such as a low-modular mesh, film, or weave, either of a synthetic or naturally occurring polymer. The strip 22 preferably is defined by interconnected strands, filaments, or strips of material. The strands, filaments, or strips can be interconnected in any one or a combination of manners including, but not limited to, being woven into a gauze, intertwined, integrally-formed, and the like. Preferably, the interconnection is such that the mesh can flex while substantially maintaining the dimensions of the openings defined thereby.
The material from which the absorbable carrier strip is fabricated may be a polymer (e.g., nylon, polyethylene, polypropylene, polyester, or the like), metal, fiberglass, or an organic substance (e.g., cotton, wool, silk, or the like). Commercial versions of acceptable blood absorbent strips are available as gauzes and bandages, such as Johnson & Johnson Nu Gauze All Purpose Dressings, Kling Rolls, and First Aid Gauze Pads, Kendall Kerlix and Kerlix Lite Gauze, and gauzes sold by such companies as Walgreens, Safeway and Rite Way, to name a few. Preferably, the carrier strip 22 may comprise a creped or butterfly material, with or without apertures.
The wound dressing has an available blood contacting surface area per base surface of said wound dressing of preferably at least about 100 cm2 per cmz, more preferably at least about 200 cm2 per gram per cm2, and most preferably at least about 300 cm2 per gram per cm2. The available mass of chitosan biomaterial per wound surface area is preferably at least about 0.02g/cm2, more preferably at least about 0.04g/cm2, and most preferably at least about 0.06g/cm2 Furthermore, the wound dressing has a mean rate of dissolution per base surface area of said wound dressing when adhered to said wound site, at a temperature of about 37 C, of preferably not more than about 0.008 grams per minute per cm2, more preferably not more than about 0.005 grams per minute per cm2, and most preferably not more than about 0.002 grams per minute per cm2 .
The wound dressing assembly 20 provides an improved flexible dressing that can be adapted for use on or at wound sites of varying sizes and degrees. The dressing assembly 20 is easily wrapped around an injured body part and also provides the necessary absorbency required for preventing blood and other bodily fluids from flowing outwardly from the wound site. This is accomplished while delivering a therapeutic agent to a wound site by way of the wound dressing assembly 20. The following discussion of the interaction of the carrier strip 22 and the chitosan material 24 will further demonstrate the advantages of the present dressing assembly.
Figure 17 depicts various wound dressing assemblies 20 having various degrees of density for the carrier strip 22. The carrier strip is shown underneath the view of a scanning electron micrograph (SEM), wherein the image is magnified five times from normal. Any of the shown densities provide capable carrier strips 22.
However, it has been determined that the density of the material should not be too low, which would not provide the necessary absorbency required, nor should the material be too dense, which would prevent absorbency altogether and may be too stiff of a material, as well.
Preferable densities are dependent on the type of material that comprises the carrier strips 22, as well.
For example, carrier strips made out of cotton gauze tend to show the greatest hemostatic efficiency when the density of the gauze is a medium density, while a nonwoven rayon/polyester blend material that formed the carrier strip would be preferably a high density to best promote hemostatic efficiency. Preferably the density range is between 20 and 200 g/m2, and more preferably between 50 and 75 g/m2.
An example of a suitable material is a combination of rayon and polyester in approximately 1:4 -3:4 ratio with an average density of 62.2 2.2 g/m2.
mesh density with a special non-woven textile technique.
The material was tested, and the results are listed below in Table 1.

Table 1 -Characteristics of Carrier Strip Comprising Rayon and Polyester Materials Characteristics Results (Avg.) Generic Fiber content 64% Polyester and 360 rayon Weight (g/m2) 62.23 2.24 Thickness (mm) 0.962 0.046 Stiffness ( joules/m) 1128.6 150.4 Air permeability (m3/m2/min) 155.3 5.8 Machine direction (MD):
Tensile strength .66.4 3.8 ( joules/m) Cross direction (CD): 33.0 4.7 Elongation (%) MD: 144 12 CD: 219 4 Tearing strength (N) CD: 6.43 0.78 Bursting Strength (kPa) 138.3 9.8 Pilling resistance (visual 1 rating) Liquid absorbency time 4.9 0.3 (sec) Liquid wicking rate N/A
Demand absorbance capacity 3.54 0.75 (g/g) Maximum absorption rate 0.034 0.015 (g/g/sec) III. PHYSICAL PROPERTIES OF THE SUPPLE
DRESSING ASSEMBLY
Figures 27 and 27A provides a further comparison between supple wound dressing assemblies 20 of the present invention, along with a comparison to other prior art dressing assemblies. Figure 27A demonstrates various wound dressing assemblies 20 encompassing preferred commercial embodiments. Reference to the Prototypes RD049034-(1-4) provide dressing assemblies 20 that have been produced with the carrier strip 22 material comprising about 40% polyester and about 60%
rayon (i.e., 40/60 material). The strips 22 were general soaked in the chitosan solution 24 in a minimal time, 0-2 hours, with the assemblies being fed through the rolling members 50 (Figure 13) and dried overnight. The resultant assemblies 20 are shown to be relatively pliable with a Gurley Stiffness value below about 1100, while still retaining the absorption and permeability qualities described and discussed above.
Along with the carrier strip 22, the chitosan material 24 also defines an absorbable material. The combination of the absorbable carrier strip 22 and the absorbable chitosan material 24 provides the improved overall properties of the wound dressing assembly.
Generally speaking, the chitosan material 24 will bind to the individual fibers that make up the carrier strip 22, thereby forming webs and films between the various individual fibers of the carrier strip 22. The dressing assembly 20 further has open areas for blood to seep into the assembly, as well as areas for blood cells to coagulate. That is, the arrangement has open voids that allow fluids to move upwardly into the wound dressing assembly 20, as opposed to moving outwardly around a bandage or gauze, as shown in the prior art in Figure lA.
Not only does this assist in absorbing blood and fluid, but also prevents the blood cells or cellular components from being disassociated from the plasma in the blood.
Figures 18 and 19 provide scanning electron micrograph (SEM) images of wound dressing assemblies 20 according to the present invention. The assemblies 20 are shown in a dry state, i.e. prior to being used. As is shown, the chitosan material 24 is bound onto and between the individual fibers of the carrier strip 22.
The dressing assembly 20 still has large open areas located throughout the dressing assembly 20, which allows fluid to seep into the dressing assembly 20.
Figure 20 provides a scanning electron micrograph (SEM) image of the wound dressing assembly 20 after a fluid has been absorbed into the assembly 20.
The carrier strip 22 and the chitosan material 24 both have expanded with the fluid they have absorbed.
However, there are still void areas within the dressing assembly 20, which allows fluid to move upwardly into the dressing assembly.
The assembly 20 of the present invention (Figure 21) demonstrates marked blood cells accumulation and aggregation on the surface of the assembly 20 compared to the prior art dressings, which is shown in Figure 40. In comparison, the cell count on the surface of the dressing assembly 20 is significantly higher 32,086 21390/mm2 than the cell count 4,456 2,674 /mm2 of dressing of Figure 40 that contains no chitosan material.
It has been further determined that total blood absorbance capacity (TBAC) of dressing assemblies 20 of the present invention is in a range of 0.5 to 12 g/g (gram blood absorbed/gram gauze), preferable in a range of 2-8 g/g, with the range of material prior to the addition of a chitosan material being in a range of 8 to 16 g/g, preferable in a range of 10-14 g/g.
While the general arrangement of the dressing assembly has been demonstrated, other variables may have an effect on the overall efficacy of the material by providing different adhesion or stiffness properties, or by altering the contact angle of the gauze.

Figure 23 is a graph comparing the contact angle of blood droplets on various wound dressing assemblies. The contact angle is the angle at which a specific- fluid interface meets a solid surface and subsequently spreads out over the solid surface. That is, the contact angle measures how quickly the fluid dissipates into the solid surface. The tested wound dressing assemblies comprised a carrier strip comprising a blend of rayon and polyester (RP) that was impregnated with a chitosan material according to the present invention. Reference to an Uncoated RP Gauze is for a dressing assembly that has not been treated or impregnated with chitosan, i.e. a prior art dressing assembly. The dressing assemblies were compared at various temperatures, 50 C for 24 hours, 70 C, and 90 C
For 4 hours. The contact angle was measured using an FTA200 contact angle instrument. A 20 L blood droplet was placed on the surface of the various wound dressing assemblies and the change of the contact angle of the blood/wound dressing assembly was measured over time.
The results indicate that the drying temperature of the wound dressing assemblies affects the assemblies by contact angles with different drying processes. Further, Figure 23 demonstrates that the contact angle shows that the dressing assemblies of the present invention are improvements over the prior art dressing assemblies (the uncoated RP gauze) by their ability to provide a more utile, efficacious, flow rate of blood into the wound dressing.
Figure 24 is graph comparing the adhesion properties of wound dressing assemblies of the present invention having various amounts of chitosan material applied to the dressing assemblies (2%, 3%, 4%) . The adhesion was performed using an Instron instrument with a lON load cell. Bovine blood (0.25 ml) was placed on a test piece of each of the dressing assemblies. A 0.4 inch PVC probe was then held in contact with the test pieces at 15kPa for seconds and then removed. The results indicate that each of the various amounts of chitosan used do have acceptable adhesion properties. As discussed, above, the dressing assemblies will have at least a minimal degree of adhesion, preferably between about 10-40 kPa.
Figure 25 is a further graph comparing wound dressing assemblies of the present invention. The dressing assemblies, which each comprised a 2% chitosan material, were subjected to various amounts of lactic acid (0%, 0.401, and 0.6%). The adhesion test was the same as what was carried out with respect to Figure 21.
The results indicated that addition of non-volatile acid does not significantly enhance the adhesion property of the dressing assemblies.
Figure 26 compares dressing assemblies of the present invention to prior dressing assemblies to determine the stiffness of the assemblies. The flexibility does not affect the efficacy of the assemblies themselves, but is more relevant when treating wounds as discussed, above. Stiffness can be expressed in terms of a ratio between the Tabor stiffness value (in units of milligrams) (as determined when dry by using a Taber Stiffness Tester Model 150E manufactured by Taber Industries of Buffalo, New York).
Comparisons were made between dressing assemblies that did not comprise any chitosan material (Uncoated) and dressing assemblies that contained chitosan materials (Coated), including different types of starting materials for the production of the chitosan (shrimp and squid) In addition, different materials were used for the carrier strip, as well (cotton and rayon polyester).

The wound dressing assemblies of the present invention were determined to have a degree of stiffness between about 30 and 2000 times of previously manufactured chitosan wound dressings, without a loss in the hemostatic properties of the assemblies. While both the dressing assemblies (cotton and rayon/polyester) containing a chitosan material had increased stiffness over the dressing assemblies that did not contain any chitosan material (i.e. Uncoated), the dressing assemblies that comprised a rayon/polyester carrier in combination with the chitosan material, as expected, showed higher stiffness compared to the Uncoated dressing assemblies.
D. Results Example 3 A wound dressing assembly as prepared according to Example 1, above was tested to determine its ability to control hemorrhaging. An auxillosubclavian injury was created in a porcine model. The injury was created with a 2-cm skin entry and was approximately 10-cm deep from the skin to the axillary artery. The axillary artery was trimmed to 3 cm length and dilated with vasodilator (10 lidocaine/paravine solution, having a 4:1 v/v ratio) A 4-mm diameter perforation injury was created in front of the axillary artery using a 4mm vascular punch, from Ethicon, in NJ. The wound dressing was applied through the 2-cm entry to fill and pack in the wound under manual pressure for 3 minutes. After pressure was released the hemorrhaging from the wound was controlled.
Figure 27 provides further comparison and results of dressing assemblies of the present invention compared to similar prior art dressing assemblies, i.e. control assemblies. Figures 28-43 provide various SEM images of the dressing assemblies, both prior to and after interacting with blood. Various qualities of the dressing assemblies were compared, such as stiffness, permeability, absorbance, and other qualities.
Referring to Figure 27, a carrier strip comprising a blend of 301 rayon and 70% polyester, sold by Johnson & Johnson, Inc. under the trademark Kling was tested, both without the addition of a chitosan material (J & J Kling Roll (uncoated)) and with chitosan material added according to the present invention (100808, 120808, - 08-XL-045). The uncoated carrier strip was used as a control. Each of the three dressing assemblies coated with chitosan exhibited improved qualities when compared to the control. For example, the three assemblies showed a significant increase in stiffness, an increase in the Single Drop Absorption Time (i.e., the contact angle), and an increase in the number of blood cells accumulated in the dressing assemblies.
The various characteristics in Figure 27 demonstrate the improvement of the present invention over the prior assemblies. For example, when comparing the stiffness of each of the dressings of the present invention (100808, 120808, 08-XL-045) to the prior art assembly (J & J Kling Roll (uncoated)) the stiffness (Gurley units, mg) is approximately 10 times stiffer in the width direction (60-70 compared to 5 for the prior art), respectively compared to the prior art and 5 times stiffer in the machining length directions compared to the prior art (20-40 compared to 5 for the prior art), respectively. The increased stiffness improves the ease of application.
Similarly, the contact angle, blood absorbance capacity, and permeability for the dressing assemblies demonstrates improved structures for the present invention compared to the prior dressing assemblies. The contact angle (measured as the time that a sessile 20 1 decreases in volume to 5 1 drop) is 5X to 20X longer for the present invention compared to the prior art, 25-130 seconds and <5 seconds, respectively.
Table 2, below, shows the blood absorbance capacity (grams of blood/grams dressing) for the present invention compared to the prior art invention, after a 2 minute interval. Each of the assemblies 20 of the present invention is lower than that of the prior art, but provides sufficient absorbance capacity values.
Table 2 Blood Absorbance Capacity After 2 Minutes SAMPLE # 120808 08-XL-045 100808 J&J Kling (Prior Art) AVG 6.4 10.4 2.9 14.0 STD DEV 3..9. 0.9 1.6 0.2 p<0.05 for all present art compared to prior art The permeability of blood (defined as the mean flow rate mL/sec of blood through the specimen) (see Fig.
27) is approximately four (4) times slower for the present invention compared to the prior art, 0.2 (avg.) and 0.8, respectively. The improved structural characteristics of the present invention compared to the prior art assemblies accelerate clot formation and hemostasis. Slow penetration allows cells to concentrate and then as they slowly permeate through the structure clot formation occurs.
The improved ability of the dressing assemblies of the present invention are further demonstrated by comparing scanning electron micrograph (SEM) images of the dressing assemblies. Images of the J
& J Kling Roll (uncoated) dressing assembly are shown in Figure 39 after the dressing assembly has interfaced with blood. Very few blood cells are shown coagulating within the dressing assembly.
Conversely, the three assemblies of the present invention (100808, 120808, 08-XL-045) are capable of significant blood cell coagulation within the dressing assemblies. The three assemblies are shown in Figures 29, 37, and 36, respectively, prior to interfacing with blood, and Figures 41, 42, and 43, respectively, after the assemblies.. have interfaced with blood. The webs of chitosan material 24 extending between the individual fibers of the carrier strip 22 provide membranes that will allow collection and coagulation of the blood cells within the dressing assemblies 20, demonstrating a visible improvement over the prior art dressing assemblies.
The SEM images provide other possible dressing assemblies and compositions that could be formed according to the present invention. Figure 28 shows and a dressing assembly as depicted and described with respect to Figure 16. That is, the dressing assembly includes an adhesive material, i.e. polyacrylic acid.
The carrier strip 22 comprises 30% rayon and 70%
polyester. The SEM image shows relatively robust areas of chitosan material 24 within the dressing assembly.
Figures 30, 31, and 33 contemplate dressing assemblies wherein the preparatory step of applying chitosan material has been repeated, or the carrier strip 22 has been "double coated" with chitosan material.
Alternative additives or material may be added to the dressing assembly of the present invention. For example, Figure 35 depicts a dressing assembly comprising chitosan material and a carrier strip that has been further treated with a plasma material.
Figure 39 depicts a dressing assembly having a carrier strip 22 comprised of 70% rayon and 30%
polyester.
E. Other Uses of the Wound Dressing Assembly The wound dressing assemblies of the present invention can also be incorporated for other uses. For example, the wound dressing assembly can be used to form an anti-microbial barrier; or to form an antiviral patch;
or to intervene in a bleeding disorder; or to release a therapeutic agent; or to treat a mucosal surface; or to dress a staph or MRSA infection site; or in various dental surgical procedures, or combinations thereof.
For example the wound dressing assembly may further comprise an active ingredient. The active ingredient may include, but is not limited to, calcium, thrombin, factor VIIa, factor XIII, thromboxane A2, prostaglandin-2a, epidermal growth factor, platelet derived growth factor, Von Willebrand factor, tumor necrosis factor (TNF), TNF-alpha, transforming growth factor (TGF), TGF-alpha, TGF-beta, insulin like growth factor, fibrobast growth factor, keratinocyte growth factor, nerve growth factor, penicillin, ampicillin, methicillin, amoxycillin, clavamox, clavulanic acid, amoxicillin, aztreonam, imipenem, streptomycin, Kanamycin, Tobramycin, gentamicin, vancomycin, clindamycin, erythromycin, polymyxin, hacitracin, amphotericin, nystatin. rifampicin, tetracycline, doxycycline, chloramphenicol, vasoconstrictors, e.g.
epinephrine and histamines, and combinations thereof.
The foregoing is considered as illustrative only of the principles of the invention. Furthermore, since numerous modifications and changes will readily occur to those skilled in the art, it is not desired to limit the invention to the exact construction and operation shown and described. while the preferred embodiment has been described, the details may be changed without departing from the invention, which is defined by the claims.

Claims (21)

1. A wound dressing assembly comprising:
a flexible carrier strip comprised of a plurality of individual fibers; and a chitosan material, said chitosan material forming a plurality of webs between said individual fibers of said carrier strip, wherein the assembly has a degree of adhesion to a wound site of at least about 1 kPa.

2. The wound dressing assembly according to claim 1 wherein said chitbsan material comprises a chitosan solution containing between about 0.5%-4.0%
(w/w) chitosan.

3. The wound dressing assembly according to claim 2, wherein said chitosan solution contains between about 1.0%-2.3% (w/w) chitosan.

4. The wound dressing assembly according to claim 1 wherein said dressing assembly further comprises an adhesive material.

5. The wound dressing assembly according to claim 4 wherein the adhesive material is lactic acid.

6. The wound dressing assembly according to claim 1, wherein said flexible carrier strip comprises a rayon material and a polyester material

7. The wound dressing assembly according to claim 6 wherein said flexible carrier comprises between about 25-75% rayon material and between about 75%-25%
polyester material.

8. A wound dressing assembly comprising:
a flexible carrier strip; and a hemostatic material, located on said carrier strip;
wherein said dressing assembly has a stiffness between about 200 and 10,000 on a Gurley Stiffness test.

9. The wound dressing assembly according to claim 8 further having a stiffness of between about 500 and 8000 on a Gurley Stiffness Test.

10. The wound dressing assembly according to claim 9 further having a stiffness of between about 500 and 6000 on a Gurley Stiffness Test.

11. The wound dressing assembly according to claim 8, wherein the hemostatic material comprises a chitosan material.

12. A wound dressing assembly comprising:
a flexible carrier strip; and a heomstatic material, located on said carrier strip;
wherein said dressing assembly has a permeability between about 0.1 - 0.5 ml/s.

13. The wound dressing assembly according to claim 12, wherein the dressing assembly has a permeability between about 0.15 - 0.35 ml/s.

14. The wound dressing assembly according to claim 12, wherein said hemostatic material comprises a chitosan material.

15. A wound dressing assembly comprising:
a flexible carrier strip; and a hemostatic material, located on said carrier strip;
wherein said dressing assembly has a total blood absorbance capacity (TBAC) between about 0.5 - 12 g/g (grams blood absorbed/grams).

16. The wound dressing assembly according to claim 15, wherein the dressing assembly has a TBAC
between about 2 - 8 g/g.

17. A wound dressing assembly comprising:
a flexible carrier strip; and a hemostatic material, located on said carrier strip;
wherein said dressing assembly has a single drop absorption time between about 20-240 seconds.

18. The wound dressing assembly according to claim 15, wherein said hemostatic material is a chitosan material.

19. The wound dressing assembly according to claim 18, wherein said flexible carrier comprises between about 25-75% rayon material and between about 75%-25%
polyester material.

20. The wound dressing assembly according to claim 19, wherein the dressing assembly has a permeability between about 0.15 - 0.35 ml/s.

21. The wound dressing assembly according to claim 20, further having a stiffness of between about 500 and 5500 on a Gurley Stiffness Test.