CA2735867C - Food wrap basesheet with regenerated cellulose microfiber - Google Patents

Abstract

A basesheet for food wrap products.
The base sheet can include a pulp-derived papermaking fiber and a fibrillated regenerated cellulose microfiber having a CSF value of less than about 175 mL.

Description

FOOD WRAP BASESHEET WITH REGENERATED CELLULOSE MICROFIBER
BACKGROUND OF THE INVENTION
Field of the Invention [0001] Embodiments of the present disclosure generally relate to paper-containing products and, in particular, to paper suitable for use as a base sheet. More particularly, embodiments of the present disclosure relate to base sheets adapted for use in the production of food wrap products.
Description of the Related Art

[0002] Paper for producing food-wrap products is well known in the art.
Generally speaking, such products are manufactured similarly to tissue type products, except that they are not creped from a Yankee dryer. Instead, they are pulled from the dryer under tension, or may be can-dried on a flat paper machine. Such products include so-called dry-waxing sheets, wet waxing sheets, and sheets adapted for making oil and grease resistant ("OGR") papers. The base sheet is impregnated or coated with a water-resistant agent such as wax, polyethylene or fluorocarbons to provide water and grease resistance.

[0003] While materials for improving water and oil resistance have been improved over the years, numerous desirable attributes in the food-wrap base sheet are currently addressed by additives. Wet strength, for instance, is usually provided by conventional wet strength resins, while opacity is provided by conventional opacifiers such as titanium dioxide and the like.
These additives are expensive and can aggravate processing difficulties when the paper is impregnated with a water-resistant agent and/or printed as is common, especially with wet-waxing papers. What is needed, therefore, is a food-wrap base sheet that reduces the required amount of additives, while maintaining the desired physical properties.
SUMMARY

[0004] Embodiments of the disclosure may provide an exemplary base sheet for food wrap products including a pulp-derived papermaking fiber and a fibrillated regenerated cellulose microfiber having a CSF value of less than about 175 mL. Embodiments of the disclosure may . .

also provide an exemplary method for making a food wrap paper product. The exemplary method includes forming a base sheet including a pulp-derived papermaking fiber and a regenerated cellulose microfiber, and treating the base sheet with a water or grease resistant agent.

[0005] Such products can include so-called dry-waxing sheet, wet waxing sheet and sheet, particularly adapted for making oil and grease resistant ("OGR") papers.
BRIEF DESCRIPTION OF THE DRAWINGS

[0006] So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

[0007] Figure 1 illustrates a histogram showing fiber size or "fineness" of exemplary fibrillated lyocell fibers, according to one or more embodiments described.

[0008] Figure 2 illustrates a plot of FQA measured fiber length for various exemplary fibrillated lyocell fiber samples, according to one or more embodiments described.

[0009] Figure 3 depicts a photomicrograph of 1.5 denier unrefined, regenerated cellulose fiber, in accordance with the disclosure.

[0010] Figure 4 is a photomicrograph of 14 mesh of refined, regenerated cellulose fiber, according to one or more embodiments described.

[0011] Figure 5 depicts a photomicrograph of 200 mesh refined, regenerated cellulose fiber, according to one or more embodiments described.

[0012] Figures 6-10 are photomicrographs at increasing magnification of fibrillated, regenerated cellulose microfiber passed through a 200 mesh screen of a Bauer-McNett classifier, according to one or more embodiments described.

SUBSTITUTE SHEET (RULE 26) . .

[0013] Figure 11 illustrates a graph of hand sheet bulk versus tensile (i.e., breaking length) of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0014] Figure 12 illustrates a plot of roughness versus tensile of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0015] Figure 13 illustrates a plot of opacity versus tensile of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0016] Figure 14 illustrates a plot of modulus versus tensile of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0017] Figure 15 illustrates a plot of hand sheet tear versus tensile of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0018] Figure 16 illustrates a plot of hand sheet bulk versus ZDT bonding of handsheets including regenerated cellulose microfiber, according to one or more embodiments described.

[0019] Figure 17 depicts a photomicrograph at 250 magnification of a softwood handsheet without fibrillated regenerated cellulose fiber, according to one or more embodiments described.

[0020] Figure 18 depicts a photomicrograph at 250 magnification of a softwood handsheet incorporating fibrillated regenerated cellulose microfiber, according to one or more embodiments described.

[0021] Figure 19 illustrates a schematic diagram of an extrusion or liquid porosimetry apparatus, according to one or more embodiments described.

[0022] Figure 20 illustrates a plot of pore volume in percent versus pore radius in microns for various sheets, according to one or more embodiments described.

[0023] Figure 21 illustrates a plot of pore volume, according to one or more embodiments described.

[0024] Figure 22 illustrates a plot of average pore radius in microns versus microfiber content for softwood Kraft sheets, according to one or more embodiments described.

[0025] Figure 23 illustrates a plot of pore volume versus pore radius for sheets with and without cellulose microfiber, according to one or more embodiments described.

SUBSTITUTE SHEET (RULE 26) . .

[0026] Figure 24 illustrates another plot of pore volume versus pore radius for sheets with and without cellulose microfiber, according to one or more embodiments described.

[0027] Figure 25 illustrates a plot of cumulative pore volume versus pore radius for wipers with and without cellulose microfiber, according to one or more embodiments described.

[0028] Figure 26 illustrates a plot of capillary pressure versus saturation for sheets with and without cellulose microfiber, according to one or more embodiments described.

[0029] Figure 27 illustrates a plot of average Bendtsen Roughness at 1 kg, mL/min versus percent by weight cellulose microfiber in the sheet, according to one or more embodiments described.
DETAILED DESCRIPTION

[0030] A detailed description will now be provided. Each of the appended claims defines a separate invention, which for infringement purposes is recognized as including equivalents to the various elements or limitations specified in the claims. Depending on the context, all references below to the "invention" may in some cases refer to certain specific embodiments only. In other cases it will be recognized that references to the "invention" will refer to subject matter recited in one or more, but not necessarily all, of the claims. Each of the inventions will now be described in greater detail below, including specific embodiments, versions and examples, but the inventions are not limited to these embodiments, versions or examples, which are included to enable a person having ordinary skill in the art to make and use the inventions, when the information in this disclosure is combined with available information and technology.

[0031] Terminology used herein is given its ordinary meaning consistent with the exemplary definitions set forth immediately below; mils refers to thousandths of an inch; mg refers to milligrams and m2 refers to square meters, percent means weight percent (dry basis), "ton"
means short ton (2,000 pounds), and so forth. Unless otherwise specified, the version of a test method applied is that in effect as of January 1, 2008, and test specimens are prepared under standard TAPPI conditions; that is, conditioned in an atmosphere of 23 C + 1.0 C (73.4 F
1.8 F) at 50% relative humidity for at least about 2 hours.

[0032] Unless otherwise specified, "basis weight," "BWT," "bwt," and so forth, are used interchangeably and refer to the weight of a 3,000 square foot (ft2) ream of product. Consistency SUBSTITUTE SHEET (RULE 26) refers to percent solids of a nascent web, for example, calculated on a bone dry basis. "Air dry"
means including residual moisture, by convention up to about 10 percent moisture for pulp and up to about 6% for paper. A nascent web having 50% water and 50% bone-dry pulp has a consistency of 50%.

[0033] The terms "cellulosic," "cellulosic sheet," and the like, are meant to include any product incorporating papermaking fiber having cellulose as a major constituent.
"Papermaking fibers"
include virgin pulps, recycle (secondary) cellulosic fibers, or fiber mixes including cellulosic fibers. Fibers suitable for making the webs can include: nonwood fibers, such as cotton fibers or cotton derivatives, abaca, kenaf, sabai grass, flax, esparto grass, straw, jute hemp, bagasse, milkweed floss fibers, and pineapple leaf fibers; and wood fibers such as those obtained from deciduous and coniferous trees, including softwood fibers, such as northern and southern softwood Kraft fibers; hardwood fibers, such as eucalyptus, maple, birch, aspen, or the like.

[0034] Papermaking fibers can be naturally occurring pulp-derived fibers, as opposed to reconstituted fibers such as lyocell or rayon that are liberated from their source material by any one of a number of pulping processes familiar to one experienced in the art including sulfate, sulfite, polysulfide, soda pulping, etc. The pulp can be chemically bleached if desired. Suitable bleaching agents or chemical include, but are not limited to, chlorine, chlorine dioxide, oxygen, alkaline peroxide, and the like.

[0035] Naturally occurring pulp-derived fibers are referred to herein simply as "pulp-derived"
papermaking fibers. "Furnishes" and like terminology refers to aqueous compositions including papermaking fibers, optionally wet strength resins, debonders, and the like, for making paper products. For purposes of calculating relative percentages of papermaking fibers, the fibrillated cellulose, e.g. lyocell, content is excluded as noted below.

[0036] Kraft softwood fiber is low yield fiber made by the well known Kraft (sulfate) pulping process from coniferous material and includes northern and southern softwood Kraft fiber, Douglas fir Kraft fiber and so forth. Kraft softwood fibers generally have a lignin content of less than about 5 percent by weight, a length weighted average fiber length of greater than about 2 mm, as well as an arithmetic average fiber length of greater than about 0.6 mm.

[0037] Kraft hardwood fiber is made by the Kraft process from hardwood sources, i.e., eucalyptus, and also generally has a lignin content of less than about 5 wt%.
Kraft hardwood SUBSTITUTE SHEET (RULE 26) Docket No. 20515-PCT
fibers are shorter than softwood fibers, typically having a length weighted average fiber length of less than about 1 mm and an arithmetic average length of less than about 0.5 mm or less than about 0.4 mm.

[0038] Recycle fiber may be added to the furnish in any amount. Any suitable recycle fiber may be used, including recycle fiber with relatively low levels of groundwood, for example, recycle fiber with less than about 15 wt% lignin content, or less than about 10 wt% lignin content may be used depending on the furnish mixture employed and the application.

[0039] Calipers and/or bulk reported herein may be referred to herein as 1, 8, or 16 sheet calipers, as specified. Hand sheet caliper and bulk is based on 5 sheets. The sheets are stacked and the caliper measurement taken about the central portion of the stack.
Preferably, the test samples are conditioned in an atmosphere of 23 C 1.0 C (73.4 F 1.8 F) at 50% relative humidity for at least about 2 hours and then measured with a Thwing-Albert Model 89-II-JR or Progage Electronic Thickness Tester with 2-in (50.8 mm) diameter anvils, 539 10 grams dead weight load, and 0.231 in/sec descent rate. For finished product testing, each sheet of product to be tested should have the same number of plies as the product when sold. For testing in general, eight sheets are selected and stacked together. For napkin testing, napkins are unfolded prior to stacking. For base sheet testing off of winders, each sheet to be tested must have the same number of plies as produced off the winder. For base sheet testing off of the paper machine reel, single plies must be used. Sheets are stacked together aligned in the MD. On custom embossed or printed product, try to avoid taking measurements in these areas if at all possible. Bulk may also be expressed in units of volume/weight by dividing caliper by basis weight (specific bulk).

[0040] A creping adhesive may be used to secure the base sheet web to the Yankee drying cylinder. The creping adhesive can be a hygroscopic, re-wettable, substantially non-crosslinking adhesive. Examples of creping adhesives can include poly(vinyl alcohol) of the general class described in U.S. Patent No. 4,528,316. Other examples of suitable adhesives are disclosed in U.S. Patent Application Serial No. 10/409,042. Suitable adhesives can be provided with modifiers and so forth; however, crosslinkers and/or modifiers may be used sparingly, or not at all, in the adhesive.

22955477.1 Docket No. 20515-PCT

[0041] "Freeness" or "Canadian Standard Freeness" (CSF) can be determined in accordance with TAPPI Standard T 227 M-94 (Canadian Standard Method). Any suitable method for preparing the regenerated cellulose microfiber for freeness testing may be employed, so long as the fiber is well-dispersed. For example, if the fiber is pulped at about 5% consistency for a few minutes or more, e.g., 5-20 minutes before testing, the fiber can be well dispersed for testing. Likewise, partially dried, fibrillated, regenerated cellulose microfiber can be treated for about 5 minutes in a British disintegrator at about 1.2% consistency to ensure proper dispersion of the fibers. All preparation and testing. can be done at room temperature and either distilled or deionized water can be used throughout.

[0042] The fibers can be solvent spun cellulose fibers, which can be produced by extruding a solution of cellulose into a coagulating bath. Lyocell fiber, for example, is distinct from cellulose fiber made by other known processes, which rely on the formation of a soluble chemical derivative of cellulose and its subsequent decomposition to regenerate the cellulose, for example, the viscose process. Lyocell is generally defined herein to mean fibers spun directly from a solution of cellulose in an amine-containing medium. In one or more embodiments, the amine-containing medium can be a tertiary amine N-oxide. Examples of solvent-spinning processes for the production of lyocell fibers are described in U.S. Patent Nos. 6,235,392;
6,042,769; and 5,725,821.

[0043] Dry tensile strengths (MD and CD), stretch, ratios thereof, modulus, break modulus, stress, and strain can be measured with a standard INSTRON test device or other suitable elongation tensile tester. "MD" means machine direction and "CD" means cross-machine direction. Opacity is measured according to TAPPI test procedure T425-0M-91, or equivalent.
The tensile tester may be configured in various ways, including using about I
inch, about 3 inch, or about 15 mm wide strips of a specimen conditioned in an atmosphere of 23 C
1 C (73.4 F
1 F) at about 50% relative humidity for about 2 hours. The tensile test can be run at a crosshead speed of about 2 in/min. Tensile strength can also be referred to herein simply as "tensile," and may be described in terms of breaking length (km), g/3" or g/in.

[0044] GM Break Modulus is expressed in grams/3 inches/ %strain, or grams/inch/ %strain unless other units are indicated. Percent strain is dimensionless. Tensile values generally refer 22955477.1 . = .

to break values unless otherwise indicated. Tensile strengths are reported in g/3" or g/inch at break. GM Break Modulus is calculated as [(MD tensile / MD Stretch at break) X
(CD tensile /
CD Stretch at break)]1/2. Break Modulus for handsheets may also be measured on a 15 mm specimen and expressed in kg/mm2, if so desired. Tensile ratios can simply be ratios of the values determined by way of the foregoing methods. Unless otherwise specified, a tensile property is a dry sheet property.

[0045] Total Energy Absorbed (TEA) is a measure of toughness and is reported CD TEA, MD
TEA, or GM TEA. TEA is calculated as the area under the stress-strain curve using a tensile tester as has been previously described above. The area is based on the strain value reached when the sheet is strained to rupture and the load placed on the sheet has dropped to 65 percent of the peak tensile load. Since the thickness of a paper sheet is generally unknown and varies during the test, it is common practice to ignore the cross-sectional area of the sheet and report the "stress" on the sheet as a load per unit length or typically in the units of grams per 3 inches of width. For the TEA calculation, the stress is converted to grams per millimeter and the area calculated by integration. The units of strain are millimeters per millimeter so that the final TEA
units become g-mm/mm2.

[0046] Wet tensile is measured using a one or three-inch wide strip of material that is folded into a loop, clamped in a special fixture termed a Finch Cup, then immersed in water. The Finch Cup, which is commercially available from the Thwing-Albert Instrument Company of Philadelphia, Pa., is mounted onto a tensile tester equipped with a 2.0 pound load cell with the flange of the Finch Cup clamped by the tester's lower jaw and the ends of tissue loop clamped into the upper jaw of the tensile tester. The sample is immersed in water that has been adjusted to a pH of about 7.0 about 0.1 and the tensile is tested after about a 5 second immersion time. Values are divided by two, as appropriate, to account for the loop.

[0047] Wet/dry tensile ratios are expressed in percent by multiplying the ratio by 100. For towel products, the wet/dry CD tensile ratio is of heightened relevancy. Throughout this specification and claims which follow "wet/dry ratio" or like terminology refers to the wet/dry CD tensile ratio unless clearly specified otherwise. For handsheets, MD and CD values are approximately equivalent.

SUBSTITUTE SHEET (RULE 26)

[0048] The pulp may be mixed with strength adjusting agents such as permanent wet strength agents (WSR), optionally dry strength agents, and the like, before the sheet is formed. Suitable permanent WSRs are known. Such WSRs can include urea-formaldehyde resins, melamine formaldehyde resins, glyoxylated polyacrylamide resins, polyamidamine-epihalohydrin resins, and the like. Such WSRs can be produced by reacting acrylamide with diallyl dimethyl ammonium chloride (DADMAC) to produce a cationic polyacrylamide copolymer which is ultimately reacted with glyoxal to produce a cationic cross-linking wet strength resin, glyoxylated polyacrylamide. Examples of these materials are generally described in U.S. Patent Nos. 3,556,932 and 3,556,933. Resins of this type are commercially available under the trade name PAREZO. Different mole ratios of acrylamide/DADMACI-glyoxal can be used to produce cross-linking resins, which are useful as wet strength agents. Furthermore, other dialdehydes can be substituted for glyoxal to produce thermosetting wet strength characteristics. Polyamidamine-epichlorohydrin peimanent wet strength resins, can also be used, an example of which is sold under the trade names KYMENEO 557LX and 557H by Hercules, Inc. of Delaware and AMRESO by Georgia-Pacific Resins, Inc. These resins and the process for making the resins are described in U.S. Patent Nos. 3,700,623 and 3,772,076. An extensive, non-limiting description of polymeric-epihalohydrin resins is given in Chapter 2: "Alkaline-Curing Polymeric Amine-Epichlorohydrin," by Espy in Wet Strength Resins and Their Application (L. Chan, Editor, 1994). A non-limiting list of wet strength resins is described by Westfelt in Cellulose Chemistry and Technology Volume 13, p. 813, 1979.

[0049] Suitable dry strength agents may include starch, guar gum, polyacrylamides, carboxymethyl cellulose (CMC) and the like. Of particular utility is carboxymethyl cellulose, an example of which is sold under the trade name HERCULES CMC, by Hercules, Inc.
of Delaware.

[0050] Regenerated cellulose fiber can be prepared from a cellulosic dope comprising cellulose dissolved in a solvent comprising tertiary amine N-oxides or ionic liquids.
The solvent composition for dissolving cellulose and preparing underivatized cellulose dopes can include tertiary amine oxides such as N-methylmorpholine-N-oxide (NMMO) and similar compounds enumerated in U.S. Patent No. 4,246,221. Cellulose dopes may also contain non-solvents for cellulose such as water, alkanols, or other solvents, as described in greater detail below.

SUBSTITUTE SHEET (RULE 26) =

[0051] Suitable cellulosic dopes are enumerated in Table 1, below; however, it will be appreciated that all numerical ranges shown are approximate.

[0052] Table 1 EXAMPLES OF TERTIARY AMINE N-OXIDE SOLVENTS
Tertiary Amine N-oxide % water % cellulose N-methylmorpholine up to 22 up to 38 N-oxide N,N-dimethyl-ethanol- up to 12.5 up to 31 amine N-oxide N,N- up to 21 up to 44 dimethylcyclohexylamine N-oxide N-methylhomopiperidine 5.5-20 1-22 N-oxide N,N,N-triethylamine 7-29 5-15 N-oxide 2(2-hydroxypropoxy)- 5-10 2-7.5 N-ethyl-N,N,-dimethyl-amide N-oxide N-methylpiperidine up to 17.5 5-17.5 N-oxide N,N- 5.5-17 1-20 dimethylbenzylamine N-oxide

[0053] Details with respect to preparation of cellulosic dopes including cellulose dissolved in suitable ionic liquids and cellulose regeneration therefrom can be found in U.S. Patent No.
6,824,599. Here again, suitable levels of non-solvents for cellulose may be included.

[0054] There is described in this disclosure a process for dissolving cellulose in an ionic liquid without derivatization and regenerating the cellulose in a range of structural forms. It is reported that the cellulose solubility and the solution properties can be controlled by the selection of ionic liquid constituents with small cations and halide or pseudohalide anions favoring solution.
Suitable ionic liquids for dissolving cellulose can include those with cyclic cations, such as:
imidazolium; pyridinum; pyridazinium; pyrimidinium; pyrazinium; pyrazolium;
oxazolium;
1,2,3-triazolium; 1,2,4-triazolium; thiazolium; piperidinium; pyrrolidinium;
quinolinium; and isoquinolinium.

SUBSTITUTE SHEET (RULE 26)

[0055] Exemplary processing techniques for ionic liquids/cellulose dopes, and the like, are also described in U.S. Patent Nos. 6,808,557 and 6,808,557 and U.S. Patent Applications having Serial Nos. 11/087,496; 11/406,620; 11/472,724; 11/472,729; 11/263,391; and 11/375,963.
Some ionic liquids and quasi-ionic liquids which may be suitable are disclosed by Konig et al., Chem. Commun. 2005, 1170-1172.

[0056] "Ionic liquid" generally refers to a molten composition including an ionic compound that is preferably a stable liquid at temperatures of less than about 100 C at ambient pressure. Such liquids can have low vapor pressure at 100 C; specifically, the vapor pressure may be less than 75 mBar, less than 50 mBar, less than 25 mBar, less than about 10 mBar, or less than about 1 mBar. Moreover, suitable liquids can have a vapor pressure that is so low that it is negligible and is not easily measurable. Exemplary commercially available ionic liquids are BASIONICIm ionic liquid products available from BASF and are listed in Table 2 below.

SUBSTITUTE SHEET (RULE 26)

[0057] Table 2 ¨ Exemplary Ionic Liquids IL BasionicTM Product name CAS Number Abbreviation Grade EMIM Cl ST 80 1-Ethyl-3-methylimidazolium 65039-09-0 chloride EMIM ST 35 1-Ethyl-3-methylimidazolium 145022-45-3 CH3S03 methanesulfonate BMIM Cl ST 70 1-Butyl-3-methylimidazolium 79917-90-1 chloride BMIM ST 78 1-Butyl-3-methylimidazolium 342789-81-5 CH3S03 methanesulfonate MTBS ST 62 Methyl-tri-n-butylammonium 13106-24-6 methylsulfate MMMPZ ST 33 1,2,4-Trimethylpyrazolium Me0S03 methylsulfate EMMIM ST 67 1-Ethy1-2,3-di-methylimidazolium 516474-08-01 Et0S03 ethylsulfate MMMIM ST 99 1,2,3-Trimethyl-imidazolium 65086-12-6 Me0S03 methylsulfate SUBSTITUTE SHEET (RULE 26) ACIDIC
IL BasionicTM Product name CAS Number Abbreviation Grade HMIM Cl AC 75 Methylimidazolium chloride 35487-17-3 HMIM HSO4 AC 39 Methylimidazolium hydrogensulfate 681281-87-8 EMIM HSO4 AC 25 1-Ethyl-3-methylimidazolium 412009-61-1 hydrogensulfate EMIM AlC14 AC 09 1-Ethyl-3- methylimidazolium 80432-05-9 tetrachloroaluminate BMIM AC 28 1-Butyl-3-methylimidazolium 262297-13-2 HSakt hydrogensulfate BMIM AlC14 AC 01 1-Butyl-3-methylimidazolium 80432-09-3 tetrachloroaluminate BASIC
IL BasionicTM Product name CAS Number Abbreviation Grade EMIM Acetat BC 01 1-Ethyl-3-methylimidazolium acetate 143314-17-4 BMIM Acetat BC 02 1-Butyl-3-methylimidazolium acetate 284049-75-8 SUBSTITUTE SHEET (RULE 26) LIQUID AT RT
IL BasionicTM Product name CAS Number Abbreviation Grade EMIM LQ 01 1-Ethyl-3- methylimidazolium 342573-75-5 Et0S03 cthylsulfate BMIM LQ 02 1-Buty1-3-methylimidazolium 401788-98-5 Me0S03 methylsulfate LOW VISCOSITY
IL BasionicTM Product name CAS Number Abbreviation Grade EMIM SCN VS 01 1-Ethy1-3-methylimidazolium 331717-63-6 thiocyanate BMIM SCN VS 02 1-Butyl-3-methylimidazolium 344790-87-0 thiocyanate FUNCTIONALIZED
IL BasionicTM Product name CAS Number Abbreviation Grade COL Acetate FS 85 Choline acetate 14586-35-7 COL FS 65 Choline salicylate 2016-36-6 Salicylate MTEOA FS 01 Tris-(2-hydroxyethyl)- 29463-06-7 Me0S03 methylammonium methylsulfate

[0058] Exemplary cellulose dopes including ionic liquids having dissolved therein about 5 wt%
underivatized cellulose are commercially available from Aldrich. These compositions utilize SUBSTITUTE SHEET (RULE 26) = Docket No. 20515-PCT
alkyl-methylimidazolium acetate as the solvent. It has been found that choline-based ionic liquids are not particularly suitable for dissolving cellulose.

[0059] After the cellulosic dope is prepared, it can be spun into fiber, fibrillated and incorporated into absorbent sheet as hereinafter described. A synthetic cellulose such as lyocell can be split into micro- and nano-fibers and added to conventional wood pulp. The fiber may be fibrillated, for example, in an unloaded disk refiner, or any other suitable technique including using a PFI
mil. Relatively short fiber can be used and the consistency kept low during fibrillation. The beneficial features of fibrillated fibers include: biodegradability, hydrogen bonding, dispersibility, repulpability, and smaller microfibers than obtainable with meltspun fibers, for example.

[0060] Fibrillated cellulose, e.g. lyocell or its equivalents can have advantages over splittable meltspun fibers. Synthetic microdenier fibers come in a variety of forms. For example, a 3 denier nylon/PET fiber in a "pie wedge" configuration can be split into 16 or 32 segments, typically in a hydroentangling process. Each segment of a 16-segment fiber can have a coarseness of about 2 mg/100 m, versus eucalyptus pulp at about 7 mg/100 m.
Unfortunately, a number of deficiencies have been identified with this approach for conventional wet laid applications. First, dispersibility can be less than optimal. Also, meltspun fibers often must be split before sheet formation, and an efficient method is lacking. Further, most available polymers for these fibers are not biodegradable. The coarseness is lower than wood pulp, but still high enough that they must be used in substantial amounts, and, therefore, can form a costly part of the furnish. Additionally, the lack of hydrogen bonding can require other methods of retaining the fibers in the sheet.

[0061] Fibrillated fibrils can be about 0.10 microns (um) to about 0.25 microns in diameter, translating to a coarseness of about 0.0013 mg/100 m to about 0.0079 mg/100 m.
Diameters can also range from a low of about 0.1 microns, 0.15 microns, or 0.20 to a high of about 0.25 microns, 0.3 microns, or 0.35 microns. In one or more embodiments, the fibrillated regenerated cellulose microfiber can have a coarseness value of from about 0.001 mg/100 m to about 0.6 mg/100 m. The fibrillated regenerated cellulose microfiber can also have a coarseness value of from about 0.01 mg/100 m to about 0.6 mg/100 m The fibrillated regenerated cellulose microfiber can also have a coarseness value that ranges from a low of about 0.001 mg/100 m, 22955477.1 Docket No. 20515-PCT
0.01 mg/100 m, or 0.10 mg/100 m to a high of about 0.2 mg/100 m, 0.4 mg/100 m, or about 0.6 mg/100 m

[0062] In one or more embodiments, the weight average of the diameter can be about 0.1 to about 2 microns, less than about 2 microns, less than about 1 micron, less than about 0.5 microns, or less than about 0.25 microns. In one or more embodiments, the weight average of the diameter can be 0.1 microns to about 1.5 microns; 0.2 microns to about 1.2; or about 0.3 microns to about 0.9 microns. In one or more embodiments, the weight average of the length can be less than about 500 microns, less than about 400 microns, less than about 300 microns, or less than about 200 micron's. In one or more embodiments, the weight average of the length can range from a low of about 50 microns, 75 microns, or 100 microns to a high of about 250 microns, 375 microns, or 500 microns. Assuming these fibrils are available as individual strands (i.e., separate from the parent fiber) the furnish fiber population can be increased at a low addition rate. Further, fibrils not separated from the parent fiber may also provide benefit.
Dispersibility, repulpability, hydrogen bonding, and biodegradability remain product attributes since the fibrils are cellulose.

[0063] Fibrils from lyocell fiber have important distinctions from wood pulp fibrils, including the length of the lyocell fibrils. Wood pulp fibrils can be mere microns long, and therefore, can act in the immediate area of a fiber-fiber bond. Wood pulp fibrillation from refining can lead to stronger, denser sheets. Lyocell fibrils, however, may be as long as the parent fibers. These fibrils can act as independent fibers and can thereby improve the bulk while maintaining or improving strength. Southern pine and mixed southern hardwood (MSHW) are two examples of fibers that are disadvantaged relative to premium pulps with respect to softness. The term "premium pulps" as it is used herein generally refers to northern softwoods and eucalyptus pulps commonly used in the tissue industry for producing the softest bath, facial, and towel grades.
Southern pine is coarser than northern softwood Kraft, and mixed southern hardwood is both coarser and higher in fines than market eucalyptus. The lower coarseness and lower fines content of premium market pulp leads to a higher fiber population, expressed as fibers per gram (N or Ni>0.2) in Table 3. Illustrative coarseness and length values, shown in Table 3, can be obtained with a commercially-available OpTestO Fiber Quality Analyzer.
Definitions are as follows:

22955477.1 ni Li Ln _ all fibers Eni Li C =105 all fibers L 1>0.2 xsamplevveight n,i>0.2 Z-4 ni ni Li 1>0.2 all fibers N = -[=1 millionfibers I gram CL

[0064] Northern bleached softwood Kraft (NBSK) and eucalyptus have more fibers per gram than southern pine and hardwood. Lower coarseness leads to higher fiber populations and smoother sheets.

[0065] Table 3 - Fiber Properties Sample Type C, mg/100m Fines, % Ln,mm N, MM/g Ln,r>0.2,mm N,02, MM/g Southern HW Pulp 10.1 21 0.28 35 0.91 11 Southern HW -Jow fines Pulp 10.1 7 0.54 18 0.94 11.
Aracruz Eucalyptus Pulp 6.9 5 0.50 29 0.72 20 -Southern SW .Pulp 18.7 9 0.60 9 1.57 3 Northern SW Pulp 14.2 3 1.24 6 1.74 4 Southern (30 SW/70 HW) Base sheet 11.0 18 0.31 29 0.93 30 Southern SW/70 Eucalyptus Base sheet 8.3 7 0.47 26 0.77 16

[0066] For comparison, the "parent" or "stock" fibers of lyocell can have a coarseness of about 16.6 mg,1100 m before fibrillation and a diameter of about 11 [tm to about 12 rim. The fibrils (i.e., fibers post-fibrillation) have a coarseness of from about 0.001 mg/100 m to about 0.2 mg/100 m. Thus, the fiber population can be increased at relatively low addition rates. Fiber length of the parent fiber can be selectable, and fiber length of the fibrils can depend on the starting length and the degree of cutting during the fibrillation process.

[0067] The dimensions of the fibers passing the 200 mesh screen are generally from about 0.2 pm in diameter by about 100 um long. Using these dimensions, the fiber population can be calculated as about 200 billion fibers per gram. For perspective, southern pine can be three million fibers per gram and eucalyptus can be 20 million fibers per gram (see Table 3). Different fiber shapes with lyocell can result in approximately 0.2 p.m diameter fibers that can be, for example, about 1,000 pm or more long. In one or more embodiments, the approximately 0.2 1.1m diameter fibers can have a length of less than about 500 pm, less than about 400 vm, less than about 300 p,m, or less than about 200 lun. As noted above, fibrillated fibers of regenerated SUBSTITUTE SHEET (RULE 26) cellulose can be made by producing stock fibers having a diameter of about 10 p.m to about 12 [tm by fibrillating the parent fibers. Alternatively, fibrillated lyocell microfibers, for example, commercially available from Engineered Fibers Technology having suitable properties can be used.

[0068] Figure 1 illustrates a series of Bauer-McNett classifier analyses of fibrillated lyocell samples showing various degrees of "fineness." Materials having more than about 40% fiber finer than 14 mesh can exhibit a low coarseness (i.e., a low freeness). As reference, exemplary, non-limiting mesh sizes appear in Table 4, below.

[0069] Table 4 ¨ Mesh Size Sieve Mesh # Inches Microns 14 0.0555 1400 28 0.028 700 60 0.0098 250 100 0.0059 150 200 0.0029 74

[0070] In one or more embodiments, the freeness CSF value can be below about 150 mL, about 100 mL, about 50 mL, or about 25 mL. In one or more embodiments, the freeness CSF value can range from a low of about 4 mL, about 10 mL, or about 25 mL to a high of about 85 mL, about 115 mL, or about 150 mL. In one or more embodiments, at least about 50 wt%, about 60 wt%, about 70 wt%, or about 80 wt% of the fibrillated cellulose can be finer than 14 mesh. In one or more embodiments, of from about 50 wt%, 55 wt% or 60 wt% to a high of about 65 wt%, 75 wt%, or 80 wt% of the fibrillated cellulosecan be finer than 14 mesh.
Details as to fractionation using the Bauer-McNett Classifier appear in Gooding et al., "Fractionation in a Bauer-McNett Classifier", Journal of Pulp and Paper Science; Vol. 27, No. 12, December 2001.

[0071] Figure 2 illustrates a plot showing fiber length as measured by an FQA
analyzer for various samples including samples 17-20 shown on Figure 1. From this data it is appreciated that much of the fine fiber is excluded by the FQA analyzed and length prior to fibrillation has an effect on fineness. For fibrillating cellulose, preferably lyocell, typical conditions can be low consistency (about 0.5% to about 1%), low intensity (as defined by conventional refining SUBSTITUTE SHEET (RULE 26) . , technology), and high energy (about 20 HPD/T). High energy is desirable when fibrillating the regenerated cellulose, since it can take a long time at low energy. Up to about 6% consistency or more can be used and high energy input, about 20 HPD/T or more, may be employed.

[0072] The fibrillated cellulose microfiber can be present in the base sheet in any suitable amount. In one or more embodiments, up to about 75 wt% regenerated cellulose microfiber can be used although one may, for example, employ up to 90 wt% or 95 wt%
regenerated cellulose microfiber in some cases. In one or more embodiments, the amount of regenerated cellulose microfiber can range from a low of about 1 wt%, 5 wt%, or 15 wt% to a high of about 75 wt%, 85 wt%, or 95 wt%. The amount of regenerated cellulose microfiber can have a suitable maximum, i.e., 1 + X(%) where X is any positive number up to about 50 or about 98. The following are some exemplary compositions, it being appreciated that all numbers presented are approximate:

[0073] Table 5 ¨ Exemplary Cellulose and Pulp-Derived Papermaking Fiber Content % Regenerated Cellulose Microfiber % Pulp-Derived Papermaking Fiber >1 up to 95 5 to less than 99 >5 up to 95 5 to less than 95 >1 up to 35 65 to less than 99 >1 up to 25 75 to less than 99

[0074] Furthermore, lyocell fibrils are distinct from wood pulp fibrils. A
wood pulp fiber is a complex structure of several layers (P, Si, S2, S3), as known in the art, each with cellulose strands arranged in spirals around the axis of the fiber. When subjected to mechanical refining, portions of the P and Si layers peel away in the form of fines and fibrils.
These fibrils are generally short, for example, less than about 20 microns. The fibrils can act in the immediate vicinity of the fiber at the intersections with other fibers. Thus, wood pulp fibrils can increase bond strength, sheet strength, sheet density, and sheet stiffness. The multilayered fiber wall structure with spiraled fibrils can make it difficult to split the wood fiber along its axis using commercial processes. By contrast, Lyocellfiber has a much simpler structure that allows the fiber to be split along its axis. The resulting fibrils can be about 0.1 microns to about 0.25 microns in diameter, as described above, and potentially as long as the original fiber. Fibril SUBSTITUTE SHEET (RULE 26) length is likely to be less than the "parent" fiber, and disintegration of many fibers can be incomplete. Nevertheless, a sufficient numbers of fibrils can act as individual fibers, thereby substantially raising the paper properties at a relatively low addition rate.

[0075] Considering the relative fiber coarsenesses of wood pulp furnishes, northern softwood (NBSK) has a coarseness of about 14 mg/100 m, and southern pine has a coarseness of about 20 mg/100 m. Mixed southern hardwood (MSHW) has a coarseness of 10 mg/100 m, and eucalyptus has a coarseness of about 6.5 mg/100 m. Lyocell fibrils with diameters between about 0.1 microns and 0.25 microns can have coarseness values between about 0.0013 mg/100 m and about 0.0079 mg/100 m, as described above. One way to express the difference between a premium furnish and southern furnish is fiber population, expressed as the number fibers per gram of furnish (N). N is inversely proportional to coarseness, so premium furnish has a larger fiber population than southern furnish. The fiber population of southern furnish can be increased to equal or exceed that of premium furnish by the addition of fibrillated lyocell.

[0076] Lyocell microfibers can have many attractive features including biodegradability, dispersibility, repulpability, low coarseness, and extremely low coarseness to length (C/L). The low C/L means that sheet strength can be obtained at a lower level of bonding, which makes the sheet more drapable (lower modulus as shown in Figure 14 and described below with reference thereto).

[0077] Integrated southern softwood and hardwood can have a lower cost than premium pulp, yet the ability of southern furnish to produce soft tissue can be less than desired for some applications. Mills producing premium products may be required to purchase premium fibers like northern softwood and eucalyptus for the highest softness grades, which can increase cost and negatively impact the mill fiber balance. Accordingly, refined lyocell fibers can be added to improve furnish quality.

[0078] At high levels of refining, the fibrils can be separated from the parent fiber and act as independent micro- or perhaps even nano-fibers. A high level of refining may produce a substantial impact at the lowest addition rate. More refining can produce a higher population of very low coarseness fibers, but may also reduce average fiber length. It is generally preferred to maximize production of low coarseness fibrils while minimizing the cutting of fibers. As discussed earlier, the 1.6 mm as measured by the FQA is not considered an accurate average SUBSTITUTE SHEET (RULE 26) value, but is included herein to show the directional decrease in length with refining. The fibrillated lyocell obtained for later examples began as 6 mm fibers with a coarseness of 16.7 mg/100 m before refining. The ideal fibrils are substantially less coarse than eucalyptus while maintaining adequate length. Refining can reduce the fibril length, but the fibrils can remain long enough to reinforce the fiber network.

[0079] A relatively modest amount of lyocell microfiber makes it possible to increase the fibers/gram of a furnish. Consider the calculations in Table 6, wherein fibrillated lyocell achieves fiber counts of greater than a billion fibers per gram. For comparison, eucalyptus fiber, which has a relatively large number of fibers, has only up to about 20 million fibers per gram.

[0080] Table 6 ¨ Fibrillated lyocell Fiber Count D, N, microns C mg/100 m Length, mm million/g 0.1 0.0013 0.1 795,775 0.25 0.0079 0.2 63,662 0.5 0.031 0.3 10,610 1 0.126 0.4 1,989 2 0.50 0.5 398 11.5 16.6 6 1

[0081] As can be appreciated from Table 6, in one or more embodiments, the fibrillated regenerated cellulose microfiber can have a fiber count greater than about 50 million fibers/gram, about 400 million fibers/gram, about 2 billion fibers/gram, about 10 billion fibers/gram, about 50 billion fibers/gram, or about 200 billion fibers/gram, or more. In one or more embodiments, the fibrillated regenerated cellulose microfiber can have a fiber count ranging from a low of about 50 million fibers/gram, 75 million fibers/gram, or 100 million fibers/gram to a high of about 500 million fibers/gram, 1 billion fibers/gram, 100 billion fibers/gram, or 200 billion fibers/gram. In one or more embodiments, the fibrillated regenerated cellulose microfiber can have a fiber count ranging from a low of about 500 million fibers/gram, 800 million fibers/gram, or 1 billion fibers/gram to a high of about 10 billion fibers/gram, 80 billion fibers/gram, or 100 billion fibers/gram.

[0082] Another property, pore volume distribution (PVD) can be measured using liquid porosimetry techniques. For example, within a porous solid matrix. Each pore can be sized SUBSTITUTE SHEET (RULE 26) according to its effective radius, and the contribution of each size to the total free volume is the principal objective of the analysis. The data reveals useful information about the structure of a porous network, including absorption and retention characteristics of a material.

[0083] Liquid porosimetry generally requires quantitative monitoring of the movement of liquid either into or out of a porous structure. The effective radius R of a pore is operationally defined by the Laplace equation:
R = 2ycos AP , where y is liquid surface tension, 0 is advancing or receding contact angle of the liquid, and AP is pressure difference across the liquid/air meniscus. For liquid to enter or drain from a pore, an external pressure must be applied that is just enough to overcome the Laplace AP. Cos 0 is negative when liquid must be forced in; cos 0 is positive when it must be forced out. If the external pressure on a matrix having a range of pore sizes is changed, either continuously or in steps, filling or emptying will start with the largest pore and proceed in turn down to the smallest size that corresponds to the maximum applied pressure difference. Porosimetry involves recording the increment of liquid that enters or leaves with each pressure change and can be carried out in the extrusion mode; that is, liquid is forced out of the porous network rather than into it. The receding contact angle is the appropriate term in the Laplace relationship, and any stable liquid that has a known cos Or > 0 can be used. If necessary, initial saturation with liquid can be accomplished by preevacuation of the dry material.

[0084] Figure 19 illustrates an exemplary basic arrangement used for extrusion porosimetry measurements. The presaturated specimen is placed on a microporous membrane which is itself supported by a rigid porous plate. The gas pressure within the chamber can be increased stepwise, thereby causing liquid to flow out of some of the pores, largest ones first. The amount of liquid removed can be monitored by the top-loading recording balance. In this way, each level of applied pressure, which determines the largest effective pore size that remains filled, can be related to an increment of liquid mass. The chamber can be pressurized by means of a computer-controlled, reversible, motor-driven piston/cylinder arrangement that can produce the required changes in pressure to cover a pore radius range from about 1 um to about 1000 um.
Further details concerning the apparatus employed can be found in Miller et al., "Liquid SUBSTITUTE SHEET (RULE 26) = WO 2010/033536 Porosimetry: New Methodology and Applications," J. of Colloid and Interface Sci., 162, 163-170 (1994) (Till/Princeton). It will be appreciated that an effective Laplace radius R, can be determined by any suitable technique, including by using an automated apparatus to record pressure and weight changes.

[0085] The addition of regenerated cellulose microfiber to a papermaking furnish of conventional papermaking fibers surprisingly provides increased smoothness to the surface of a sheet, which can be a highly desirable feature in a wiper, since this property promotes good surface to surface contact between the wiper and a substrate to be cleaned.

[0086] Another property that can be measured is Bendtsen Roughness, which is one method by which to characterize the surface of a sheet. Generally, Bendtsen Roughness is measured by clamping a test piece between a flat glass plate and a circular metal land and measuring the rate of airflow between the paper and land, wherein the air is supplied at a nominal pressure of 1.47 kPa. The measuring land has an internal diameter of about 31.5 mm + about 0.2 mm. and a width of about 150 pm + about 2p.m. The pressure exerted on the test piece by the land can be 1 kg pressure or 5 kg pressure.

[0087] The base sheet can have a MD tensile of greater than about 5 lbs/inch, such as greater than 10 lbs/inch, or greater than 20 lbs/inch, or greater than 30 lbs/inch, or greater than 50 lbs/inch, or greater than 100 lbs/inch. The base sheet can also have a MD
tensile ranging from a low of about 5 lbs/inch, 25 lbs/inch, or 50 lbs/inch to a high of about 75 lbs/inch, 100 lbs/inch, or 200 lbs/inch.

[0088] The base sheet can further have a 1-sheet caliper of from about 1 mil to about 3 mils.
Preferably, the base sheet can have a 1-sheet caliper of from about 1.2 mil to about 2.8 mils, about 1.2 mil to about 2.5 mils, about 1.5 mil to about 2.5 mils, or about 2.0 mil to about 3.0 mils. The base sheet can also have a 1-sheet caliper ranging from a low of about 1.0 mil, 1.4 mil, or 1.8 mil to a high of about 2.0 mil, 2.4 mil, or 3.0 mil.

[0089] Bendtsen Smoothness relative to a sheet without microfiber is calculated by dividing the Bendtsen Roughness of a sheet without microfiber by the Bendtsen Roughness of a like sheet with microfiber. Either like sides or both sides of the sheets may be used to calculate relative smoothness, depending upon the nature of the sheet. If both sides are used, it is referred to as an average value.

SUBSTITUTE SHEET (RULE 26) ,

[0090] An illustrative base sheet for food wrap products can have the characteristics indicated in Tables 7 through 10, below. Such products made with regenerated cellulose microfiber generally contain less opacifier and less wet strength resin and optionally have lower roughness values.

[0091] Table 7. 17 lb Dry Waxing Sheet PROPERTY TAPPI CATEGORY TEST SPEC
TEST C = CRITICAL UNITS
METHOD
M = MAJOR
R=
REFERENCE

CALIPER T-411 C MILS/1 1.65 SHEET
MOISTURE T-412 4.0 TEAR, MD T-414 M G 20 TEAR, CD T-414 M G 23 TENSILE, MD T-494 M LBS /1 IN 13.0 TENSILE, CD T-494 M LBS / 1 IN 6.0 WET TENSILE, MD T-494 C LBS / 1 IN 1.8 WET TENSILE, CD T-494 C LBS /1 IN 0.9 ROUGHNESS, WS

ROUGHNESS, FS*

UNIT
BRIGHTNESS, T-452 C 85 DIRECTIONAL

[0092] Table 8. 14 lb Wet Waxing Sheet PROPERTY TAPPI CATEGORY TEST SPE
TEST C= UNITS
METHOD CRITICAL
M = MAJOR
R=

SUBSTITUTE SHEET (RULE 26) . .
' . WO 2010/033536 REFERENCE

1.35 SHEET
MOISTURE T-412 M %
4.5 TEAR, MD T-414 C G
9.0 TEAR, CD T-414 C G
13.0 TENSILE, MD T-494 C LBS /1 IN 6.5 TENSILE, CD T-494 M LBS / 1 IN 5.0 WET TENSILE, MD T-494 M LBS / 1 IN 0.5 WET TENSILE, CD T-494 M LBS /1 IN 0.3 ROUGHNESS, WS

ROUGHNESS, FS*

UNIT
BRIGHTNESS, T-452 M % 85 DIRECTIONAL

[0093] Table 9. 22 lb Wet Waxing Sheet PROPERTY TAPPI CATEGORY TEST SPEC
TEST C = CRITICAL UNITS
METHOD
M = MAJOR
R=
REFERENCE

LBS/REAM 22.0 1.70 SHEET
MOISTURE T-412 C %
5.0 TEAR, MD T-414 C G
TEAR, CD T-414 C G
TENSILE, MD T-494 M LBS / 1 IN 12.0 TENSILE, CD T-494 M LBS / 1 IN 7.0 WET TENSILE, MD T-494 M LBS / 1 IN 1.9 WET TENSILE, CD T-494 M LBS / 1 IN 1.1 ROUGHNESS, WS

ROUGHNESS, FS*

SUBSTITUTE SHEET (RULE 26) UNIT

BRIGHTNESS, T-452 88 DIRECTIONAL

[0094] Table 10. 19 lb Grease Resistant Paper Sheet PROPERTY TAPPI CATEGORY TEST SPEC
TEST C = CRITICAL UNITS
METHOD
M = MAJOR
R = REFERENCE
BASIS WEIGHT T-410 C LBS,/REAM 19.0 CALIPER T-411 C MILS/1 1.90 SHEET
MOISTURE T-412 M 4.5 TEAR, MD T-414 M G 20 TEAR, CD T-414 M G 25 TENSILE, MD T-494 M LBS /1 IN 15 TENSILE, CD T-494 M LBS /1 IN 7 WET TENSILE, MD T-494 C LBS / 1 IN 2.8 WET TENSILE, CD T-494 C LBS / 1 IN 1.5 ROUGHNESS, WS

ROUGHNESS, FS*

WATER ABS

ML
BRIGHTNESS, T-452 M 82 DIRECTIONAL

[0095] As will be appreciated form Tables 7 through 10, a base sheet for food wrap products generally have basis weights of from about 5 lbs to about 25 lbs per 3000 ft2 and 1-sheet calipers of from about 1.25 mils to 2.5 mils. The base sheet can also have a basis weight of from about 5 lbs to about 25 lbs per 3,000 ft2. More preferably, the base sheet can have a basis weight of from SUBSTITUTE SHEET (RULE 26) = WO 2010/033536 about 10 lbs to about 20 lbs per 3,000 ft2. In one or more embodiments, the base sheet can have a basis weight ranging from a low of about 8 lbs, 14 lbs, or 17 lbs to a high of about 19 lbs, 22 lbs, or 25 lbs per 3,000 ft2.

[0096] Absorbencies are much lower than for absorbent products and tensiles much higher, distinguishing these products from tissue and towel base sheet. For example, absorbent products generally have SAT values of greater than 2 g/g, while these products have lower SAT values and higher tensiles.

[0097] In one or more embodiments, properties of a base sheet can be achieved through the addition of regenerated cellulose microfiber, which provides wet strength, opacity and smoothness. Basis weights and calipers may be reduced from the values shown in Tables 7 through 10, while maintaining tensile and opacity requirements. Still further advantages stem from the reduced pore size of the base sheet with the microfiber. The small pores help to hold a water and/or grease resistant coating on the surface where it is most effective and allow lower coatweights to be used, as further discussed below in connection with water and grease resistant agents which are applied to the base sheet.

[0098] In one or more embodiments, the base sheet can include one or more water and/or grease resistant agents. Such agents can include one, or more polymers, waxes, and other sizes, which usually provide water and/or grease resistance. It will be appreciated that a combination of materials may be needed to achieve the desired level of both resistance to water and grease.
These materials can be printed onto the base sheet or extruded onto the base sheet as appropriate and are preferably film-forming.

[0099] Aqueous barrier ancUor grease resistance coatings can include one or more synthetic latexes with acrylic, styrenic, olefinic polymers, derivatives thereof, or mixtures thereof. Wax emulsions and the like can also be applied to the base sheet in coatweights of from about 0.3 lbs solids to about 3 lbs solids per 3,000 square foot ream; however, more barrier coatings may be used in the case of wax, as also noted below. Instead of a latex, the liquid coating may be a solution of polymer (e.g., aqueous polyvinyl alcohol), and may be applied in like amounts by like methods.

[00100] The coatings may be applied by press coating methods, i.e., gravure, coil coating, flexographic methods and so forth as opposed to extrusion methods which are used for SUBSTITUTE SHEET (RULE 26) thermoplastic resins and waxes usually at higher coatweights than aqueous coatings. The coating(s) can also be applied to the base sheet in water-borne form.

[00101] Suitable synthetic aqueous latexes can have the following physical properties. It being appreciated that all numbers presented are approximate:
VISCOSITY: 40 - 80 cps @ 70 F
SOLIDS: 36% +2%
pH: 9.0 ¨ 9.4 VOC: 0.11 lbs./gal.
APPEARANCE: Milky FDA COMPLIANCE: 176.170, 176.180 DILUENTS: IPA, H20 LBS/GAL.: 8.6 - 8.7 FLASH POINT: None

[00102] Suitable polymers can include, but are not limited to, polyacrylates, polymethacrylates, polyamides, polystyrene/butadienes, polyolefins such as polypropylene or polyethylene, polyesters, polylactides, polyalkanoates, and the like, such as those described in U.S. Patent No.
6,893,693. Suitable polymers listed in the '693 patent can include:
poly(benzyl acrylate), poly(butyl acrylate)(s), poly(2-cyanobutyl acrylate), poly(2-ethoxyethyl acrylate), poly(ethyl acrylate), poly(2-ethylhexyl acrylate), poly(fluoromethyl acrylate), poly(5,5,6,6,7,7,7-heptafluoro-3-oxaheptyl acrylate), poly(heptafluoro-2-propyl acrylate), poly(heptyl acrylate), poly(hexyl acrylate), poly(isobomyl acrylate), poly(isopropyl acrylate), poly(3-methoxybutyl acrylate), poly(methyl acrylate), poly(nonyl acrylate), poly(octyl acrylate), poly(propyl acrylate), poly(p-toly1 acrylate), poly(acrylic acid) and derivatives and salts thereof;
polyacrylamides such as poly(acrylamide), poly(N-butylacrylamide), poly(N,N-dibutylacrylamide), poly(N-do decylacrylamide), and poly(morpholylacrylamide);
polymethacrylic acids and poly(methacrylic acid esters) such as poly(benzyl methacrylate), poly(octyl methacrylate), poly(butyl methacrylate), poly(2-chloroethyl methacrylate), poly(2-cyanoethyl methacrylate), poly(dodecyl methacrylate), poly(2-ethylhexyl methacrylate), poly(ethyl methacrylate), poly(1,1,1-trifluoro-2-propyl methacrylate), poly(hexyl methacrylate), poly(2-hydroxyethyl SUBSTITUTE SHEET (RULE 26) methacrylate), poly(2-hydroxypropyl methacrylate), poly(isopropyl methacrylate), poly(methacrylic acid), poly(methyl methacrylate) in various forms such as, atactic, isotactic, syndiotactic, and heterotactic; and poly(propyl methacrylate);
polymethacrylamides such as poly(4-carboxyphenylnethacrylamide); other alpha- and beta-substituted poly(acrylics) and poly(methacrylics) such as poly(butyl chloracrylate), poly(ethyl ethoxycarbonylmethacrylate), poly(methyl fluoroacrylate), and poly(methyl phenylacrylate). The latex applied to the base sheet can be any FDA-approved material, for example, a coating such as Plate Kote 982 Kosher available from Michelman.

[00103] Other suitable polymers can include polyethylene terephthalate (PET), or biopolymers such as polylactide (PLA) or polyhydroxyalkanoate (PHA). PLA and PHA are particularly preferred when a biodegradable product is desired. The polymers relating to latex coatings may be extrusion coated as well; however, many acrylics and styrene/butadiene polymers are more amenable to latex application.

[00104] The term "wax," as used herein, refers to relatively low melting organic mixtures or compounds of relatively high molecular weight, solid at room temperature, and generally similar in composition to fats and oils, except that the waxes contain little or no glycerides. Some waxes can be hydrocarbons. Others can be esters of fatty acids and alcohols.
Suitable waxes can be thermoplastic, but since they are not high polymers, are not considered in the family of plastics.
Common properties include smooth texture, low toxicity, and freedom from objectionable odor and color. Waxes are typically combustible and have good dielectric properties. They are soluble in most organic solvents and insoluble in water. Typical classes of waxes are enumerated briefly below.

[00105] Natural waxes can include carnauba waxes, paraffin waxes, montan waxes, and microcrystalline waxes. Carnauba is a natural vegetable wax derived from fronds of Brazilian palm trees (Copemica cerifera). Carnauba is a relatively hard, brittle wax whose main attributes are lubricity, anti-blocking, and FDA compliance. Paraffins are low molecular weight waxes with melting points ranging from about 48 to about 74 C. They are relatively highly refined, have a low oil content, and are straight-chain hydrocarbons. Paraffins provide anti-blocking, slip, water resistance, and moisture vapor transmission resistance. Montan waxes are mineral waxes which, in crude form, are extracted from lignite formed decomposition of vegetable SUBSTITUTE SHEET (RULE 26) substances. Microcrystalline waxes come from the distillation of crude oil.
Microcrystalline waxes have a molecular weight of from about 500 to 675 grams/mole and melting points of about 73 to about 94 C. These waxes are highly branched and have small crystals.

[00106] Synthetic waxes can include Fischer-Tropsch waxes, polyethylene waxes, and wax dispersions of various macromers. Fischer-Tropsch waxes are produced almost exclusively in South Africa by coal gasification. They include methylene groups which can have either even or odd numbers of carbons. These waxes have molecular weights of between about 300 and about 1400 gms/mole, and are used in various applications. Polyethylene waxes are made from ethylene produced from natural gas or by cracking petroleum naphtha. Ethylene is then polymerized to provide waxes with various melting points, hardnesses, and densities.
Polyethylene wax molecular weights range from about 500 to about 3000 gms/mole. Oxidized polyethylenes are readily emulsifiable, whereas non-oxidized polyethylenes largely are not.
However, some non-oxidized polyethylenes have been successfully emulsified.
High density polyethylenes (HDPE) have a great deal of crystallinity and their molecules are tightly packed.

[00107] Wax dispersions are known and, for example, disclosed in U.S. Patent Nos. 6,033,736;
5,431,840; and 4,468,254. In general, a wax dispersion includes from about 90 to about 50 percent water, from about 10 to about 50 percent wax solids, and minor amounts of an emulsifier. "Aqueous wax dispersion," and like terminology, as it is used herein, generally refers to a stable mixture of wax, emulsifier, and water without a substantial solvent component. Wax may be applied to the base sheet in the form of a dispersion, but a melt application without water or other solvent may be required.

[00108] Wax coatings can be fortified with low density polyethylene (LDPE) for wet wax applications. These wax coatings may be applied generally by the same methods as aqueous coatings noted above, or may be extrusion coated onto the base sheet substrate. Wax coatweight typically ranges from 1 lb solids to 5 lbs solid per 3000 square foot ream for wet waxing and for dry waxing applications. Extrusion coating coatweights of wax or high polymer suitably range from about 2 lbs to about 10 lbs solid per 3000 square foot ream depending on the product.

[00109] In one or more embodiments, the aqueous barrier and/or grease resistance coatings can include a fluorochemical sizing agent or a chrome complex sizing agent, or both. An illustrative agent is QUILONO chrome complex surface treatment chemicals, commercially-available from SUBSTITUTE SHEET (RULE 26) Dupont Chemical. Such materials can be applied by the methods specified above, or similar methods, and in like amounts, whether in polymeric or lower molecular weight form.
Examples

[00110] The present disclosure can be more fully described according to the following non-limiting examples.
Hand Sheet Study #1

[00111] A hand sheet study was conducted with southem softwood and fibrillated lyocell fiber.
Figure 3 is a photomicrograph of stock lyocell fiber of 1.5 denier (e.g., 16.6 mg/100 m) by 4 mm in length, which was fibrillated until the freeness was less than about 50 CSF. Figure 4 shows a photomicrograph of 14 mesh refined regenerated cellulose, and Figure 5 shows a photomicrograph of 200 mesh refined regenerated cellulose fiber. It will be appreciated from Figures 4 and 5, that the fibrillated fiber has a much lower coarseness than the stock fiber.

[00112] Figures 6-10 show photomicrographs of fibrillated lyocell material at increasing magnification, wherein the fibrillated lyocell material has been passed through the 200 mesh screen of a Bauer-McNett classifier. This material can be referred to as "fines." In wood pulp, fines are mostly particulate rather than fibrous. The fibrous nature of this material may allow it to bridge across multiple fibers and therefore contribute to network strength.
This material can make up a substantial amount (for example, about 16 to about 29%) of the 40 csf fibrillated lyocell.

[00113] The dimensions of the fibers passing the 200 mesh screen can be between about 0.2 micron diameter by about 100 micron long, as described above. Using these dimensions, the fiber population can be calculated at about 200 billion fibers per gram, as described above. For perspective, southern pine can commonly be three million fibers per gram and eucalyptus can commonly be 20 million fibers per gram (as shown and described above in Table 1). Comparing the fine fraction with the 14 mesh pictures, the fibers may be the fibrils that are broken away from the original unrefined fibers. Different fiber shapes with lyocell can result in 0.2 micron diameter fibers that are perhaps 1000 microns or more long instead of 100, as described above.

[00114] Figures 11-16 show the impact of fibrillated lyocell on hand sheet properties. Bulk, opacity, smoothness, modulus, and tear improve at a given tensile level.
Results are compared as SUBSTITUTE SHEET (RULE 26) a function of tensile since strength is always an important variable in paper products. Also, Kraft wood pulp tends to fall on similar curves for a given variable, so it is desirable to shift to a new curve to impact finished product properties. Fibrillated lyocell shifts the bulk/strength curve favorably. Some of the microfibers may nest in the voids between the much larger softwood fibers, but the overall result is the lyocell interspersed between softwood fibers with a net increase in bulk.

[00115] Figure 12 illustrates fibrillated lyocell increasing smoothness as measured by Bendtsen roughness. Bendtsen roughness is obtained by measuring the air flow between a weighted platten and a paper sample. Smoother sheets permit less air flow. The small fibers can fill in some of the surface voids that would otherwise be present on a 100% softwood sheet. The smoothness impact on an uncreped hand sheet should persist even after the creping process.

[00116] Figure 13 illustrates opacity, wherein the opacity of the material is improved by the lyocell. The large quantity of microfibers creates an increased surface area for light scattering, which can yield opacity in the 80s. It will be appreciated that low 80s for opacity can be equivalent to 100% eucalyptus sheets.

[00117] Figure 14 illustrates hand sheet modulus, which is lower at a given tensile with the lyocell. It will be appreciated that, with lower hand sheet modulus, "drapability" improves. The large number of fibers fills in the network better and allows more even distribution of stress.
One of the deficiencies of southern softwood is its tendency to obtain lower stretch in creped tissue than northern softwood. Lyocell can help address this deficiency.

[00118] Figure 15 illustrates that fibrillated lyocell improves hand sheet tear in southern softwood. Southern softwood is often noted for its tear strength relative to other Kraft pulps, so it is notable that the fibrillated lyocell increases tear in softwood hand sheets. Softwood fibers can provide network strength while hardwood fibers provide smoothness and opacity. The fibrillated lyocell can be sufficiently long to improve the network properties while its low coarseness provides the benefits of hardwood.

[00119] Table 11, below, summarizes some of the significant effects derived from Hand Sheet Test #1, and shows the benefits of fibrillated lyocell. These benefits are also shown in Figures 11-16, and include higher bulk, better smoothness, higher tear, better opacity, and lower modulus. The purpose for the different treatments was to measure the relative impacts on SUBSTITUTE SHEET (RULE 26) Docket No. 20515-PCT
strength. Southern softwood can be less efficient in developing network strength than northern softwood, so one item of interest is to see if lyocell can enhance southern softwood. The furnish with 20% lyocell and 80% Southern softwood is significantly better than 100%
Southern softwood. Bulk, opacity, and tear are higher at a given tensile while roughness and modulus are lower. These trends are directionally favorable for tissue properties. The hand sheets for Table 5 were prepared according to TAPPI Method T-205. Bulk caliper in centimeters cubed per gram is obtained by dividing caliper by basis weight. Bendtsen roughness is obtained by measuring the air flow between a weighted platten and a paper sample. "L" designates the labeled side of the hand sheet that is against the metal plate during drying while "U" refers to the unlabelled side.
ZDT refers to the out-of-plane tensile of the hand sheet.

[00120] Table 11. Effects on hand sheet properties SW Refining-Average Refining Fib.lyocell lyocell Test Value Effect Effect Interaction Caliper 5 Sheet (cm3/g) 1.76 -0.19 0.15 Bendtsen Rough L-lkg (mL/min) 466 -235 -101 28 (95%) Bendtsen Rough U-lkg (mL/min) 1482 137 (95%) ZDT Fiber Bond (psi) 49 36 -11 -13 Tear HS, g . 120 20 (95%) Opacity TAPPI 77 -4 13 Breaking Length, km 3.5 1.8 -0.6 (95%) Stretch Hand Sheet, % 2.4 0.9 -0.4 (95%) Tensile Energy Hand Sheet, kg-mm 6.7 5.3 -1.9 (95%) Tensile Modulus Hand Sheet, kg/mm2 98 28 -18

[00121] Table 12, below, compares the morphology of lyocell and softwood fibers as measured by the OpTest optical Fiber Quality Analyzer. The stock lyocell fibers (as shown in Figure 3 and described above with reference thereto) have a coarseness of 16.7 mg/100 m, similar to southern softwood coarseness (20 mg/100 m). After fibrillation, the FQA
measured coarseness drops to 11.9, similar to northern softwood. It is likely that resolution of the FQA instrument is unable to accurately measure the length, width, or coarseness of the very fine fibrils.

22955477.1 Docket No. 20515-PCT
Commonly, the smallest fine particle the FQA records is 41 microns, and the narrowest width the FQA records is 7 microns. Thus, it will be appreciated that the coarseness value of 11.9 mg/100 m is not representative of the fibrillated lyocell, and the average coarseness of the lyocell is less than 11.9 mg/100 m measured by the FQA.

[00122] Differences in fiber size are better appreciated by comparing Figures 17 and 18.
Figure 17 is a photomicrograph made with only southern softwood Kraft refined revolutions in a PFI mill, while Figure 18 is a photomicrograph of a hand sheet made with 80%
of the same southern softwood and 20% refined lyocell fiber. The low coarseness of the fibrillated lyocell relative to conventional wood pulp can be appreciated from a comparison of the photomicrographs.

[00123] Table 12. Morphology of fibrillated lyocell versus whole lyocell and softwood OpTest FQA Fib. lyocell lyocell, 1.5 denier Southern Softwood Ln, mm 0.38 2.87 0.68 Lw, mm 1.64 3.09 2.40 Lz, mm 2.58 3.18 3.26 Fines(n), % 67.4 2.9 64.0 Fines(w), % . 16.3 0.1 8.5 Curl Index (w) 0.36 0.03 0.19 Width, pm 16.5 20.1 29.9 Coarseness, mg/100 m 11.9 16.7 20.5 CSF, mL 22 746

[00124] The degree of fibrillation is measured by Canadian Standard Freeness (csf). Unrefined lyocell has a freeness of about 800 mL, and trial quantities were obtained at about 400, 200, and 40 mL. As shown, 4 mm lyocell was refined to a freeness of only 22 mL with an average fiber length (Lw) of 1.6 mm.
Hand Sheet Study #2

[00125] This hand sheet study demonstrates that the benefit of fibrillated lyocell is obtained predominantly from short, low coarseness fibrils rather than partially refined parent fibers unintentionally persisting after the refining process. Six mm by 1.5 denier lyocell was refined to 40 freeness and fractionated in a Bauer McNett classifier using screens with meshes of 14, 28, 48, 100, and 200. Fiber length is a primary factor in determining the passage of fibers through 22955477.1 =

=

each screen. The 14 and 28 mesh fractions were combined to form one fraction hereafter referred to as "Longs". The 48, 100, 200 mesh fractions and the portion passing through the 200 mesh were combined to form a second fraction hereafter referred to as "Shorts". Southern softwood was prepared by refining it 1000 revolutions in a PFI mill. Hand sheets were prepared at 15 lb/ream basis weight, pressed at 15 psi for five minutes, and dried on a steam-heated drum.
Table 13 compares hand sheets made with different combinations of softwood and fibrillated lyocell. Softwood alone (Sample 1) has low opacity, low stretch, and low tensile. Twenty percent longs (Sample 2) improves opacity and stretch modestly, but not tensile. Twenty percent Shorts (Sample 3) greatly increases opacity, stretch, and tensile, more so than the whole lyocell (Sample 4). Sample 5 used recombined Longs and Shorts to approximate the original fibrillated lyocell. It can be appreciated from this example that the shorts are the dominant contributor to the present invention. Microfiber decreases the average pore size and increases smoothness of cellulosic sheet including foodwrap base sheet. Such are highly desirable attributes, especially for coated and printed end-products as is seen in the-following porosity and roughness data.

[00126] Table 13. 15 lb/ream hand sheets with different components of fibrillated lyocell Opacity TAPP! Stretch Breaking Basis liandsht Length Bulk Weight Opacity Sample Description Units km cm3/g lb/ream 1 100% southern softwood 46 0.7 0.75 2.92 14.3 2 80% southern softwood/20% fib. lyocell Longs 52 0.9 0.73 3.09 15.4 3 80% southern softwood/20% fib. lyocell Shorts 65 1.4 0.98 2.98 15.0 4 80% southern softwood/20% fib. lyocell Whole 61 1.3 0.95 2.81 15.7 80% southern softwood/10% fib. lyocell Longs/
10% fib.lyocell Shorts 59 1.3 0.92 2.97 14.9 Longs = 14 mesh *28 mesh fractions Shorts = 48 mesh + 100 mesh + 200 mesh + material passing through 200 mesh

[00127] The apparatus shown in Figure 19, and described above with reference thereto, can be used for measurement by extrusion porosimetry in an uncompressed mode. Using water with 0.1% TX-100 wetting agent, having a surface tension of 30 dyne/cm, as the absorbed/extruded liquid, the PVD of a variety of samples were measured by extrusion porosimetry in an uncompressed mode. Alternatively, the test can be conducted in an intrusion mode if so desired.

SUBSTITUTE SHEET (RULE 26)

[00128] Sample A was a CWP base sheet prepared from 100% northern bleached softwood Kraft (NBSK) fiber. Sample B was a like CWP sheet made with 25% regenerated cellulose microfiber and sample C was also a like CWP sheet made with 50% regenerated cellulose microfiber and 50% NBSK fiber. Details and results appear in Table 13 below, and in Figures 20- 22 for these samples. The pore radius intervals are indicated in Cols. 1 and 4 only for brevity.

SUBSTITUTE SHEET (RULE 26) Docket No, 111.713-1 1

[00129] Table 14- CWP Porosity Distribution Pore Capillary Cumul. Cumul. Pore Pore Cumul.
Cumul. Pore Volume Cumul. Cumul, Pore Capillar:
adius, Pressure, Pore Pore Radius, Volume Pore Pore Sample Pore Pore Volume Pressure ricron mmH20 Volume Volume micron Sample Volume Volume B, Volume Volume Sample mmH2C
Sample Sample A, Sample Sample mm3/(um*g) Sample Sample C, mm3/
A, A,% mm.3/ B, B,% C, C,% (um*g) mm3/mg (um*g) mm3/mg mnrlmg 500 12 7.84 100 400 5,518 5,843 100 3.943 5.5 100 2.806 12.3 300 20 6.74 85.93 250 10.177 5.054 86.5 8.25 4.938 89.79 3.979 20.4 200 31 5.72 72.95 187.5 13.902 4.229 72.38 9.482 4.54 82.56 4.336 30.6 175 35 5.38 68.52 162.5 12.933 3.992 68.33 8.642 4.432 80.59 4.425 35 150 41 5.05 64.4 137.5 13.693 3.776 64.63 7.569 4.321 78.58 4.9 40.8 125 49 4.71 60,04 117,5 15.391 3.587 61,39 9.022 4.199 76.35 4.306 49 110 56 4.48 57.09 105 14.619 3.452 59.07 7.595 4.134 75.18 3.86 55.7 100 61 4.33 55.23 95 13.044 3.376 57,78 7.297 4.096 74.47 4.009 61,3 90 68 4.20 53,57 85 15.985 3.303 56.53 6.649 4.056 73.74 2.821 68.1 80 77 4.04 51.53 75 18.781 3.236 55.39 4,818 4.027 73.23 2.45 76.6 70 88 3.85 49.13 65 18.93 3.188 54.56 4.811 4.003 72.79 3.192 87.5 60 102 3.66 46.72 55 30.441 3.14 53,74 0.806 3.971 72.21 0.445 102,1 50 123 3.36 42.84 47.5 40.749 3.132 53,6 11.021 3.967 72.12 13.512 122,5 45 136 3.16 40,24 42.5 48.963 3.077 52.66 15.027 3.899 70.9 21.678 136.1 40 153 2.91 37.12 37.5 65.448 3.002 51,37 17,22 3.791 68.93 34.744 153,1 35 175 2.58 32.95 32.5 83.255 2.916 49.9 25.44 3.617 65.77 53.155 175 30 204 2.17 27.64 27.5 109.13 2.788 47,72 36.333 3.351 60.93 89.829 204,2 25 245 1.62 20.68 22.5 94.639 2.607 44.61 69.934 2.902 52,77 119.079 245 20 306 1.15 14.65 18.75 82.496 2.257 38.63 104.972 2.307 41.94 104.529 306.3 17.5 350 0.94 12.02 16.25 71.992 1.995 34,14 119.225 2.045 37.19 93.838 350 15 408 0.76 9.73 13,75 55.568 1.697 29,04 125.643 1.811 32,92 92.65 408,3 12.5 490 0.62 7.95 11,25 58.716 1.382 23,66 120,581 1.579 28.71 100.371 490 613 0.48 6.08 9.5 58.184 1.081 18.5 102,703 1.328 24.15 84.632 612.5 SUBSTITUTE SHEET (RULE 26) , WO 2010/033536 Pore Capillary Cumul. Cumul. Pore Pore Cumul. Cumul. Pore Volume Cumul. Cumul. Pore Capillary Radius, Pressure, Pore Pore Radius, Volume Pore Pore Sample Pore Pore Volume Pressure, micron mmH20 Volume Volume micron Sample Volume Volume B, Volume Volume Sample nunHiO
Sample Sample A, Sample Sample mm3/(weg) Sample Sample C, mm3/
A, A, % mm3/ B, B, % C, C, %
(uteg) mm3/mg (um*g) mm3/mg nufling 9 681 0.42 5.34 8.5 71.164 0.978 16.74 119.483 1.244 22.61 104.677 680.6 8 766 0.35 4.43 7.5 65.897 0.859 14.7 92.374 1.139 20.71 94.284 765.6 7 875 0.28 3.59 6.5 78.364 0.766 13.12 116.297 1.045 18.99 103.935 875 6 1021 0.20 2.6 5.5 93.96 0.65 11,13 157,999 0.941 17,1 83.148 1020.8 1225 0.11 , 1.4 4.5 21.624 0.492 8.42 91.458 0.857 15.59 97.996 1225 4 1531 0.09 1.12 3.5 23.385 0.401 6.86 120.222 0.759 13.81 198.218 1531.3 3 2042 0.07 0.82 2.5 64.584 0.28 4.8 176.691 0.561 10.21 311.062 2041.7 2 3063 0.00 0- - 1.5 12.446 0.104 1.78 103,775 0.25 4.55 250.185 3062.5 1 6125 0,01 0.16 0 0 0 AVG AVG AVG
73.6 35.3 23.7 Wicking ratio (Sample 2.1 (Sample AlSample 0 3.1 AlSample B) SUBSTITUTE SHEET (RULE 26)

[00130] It is seen in Table 14, above, and Figures 20-22, that the three samples respectively had average or median pore sizes of 74, 35 and 24 microns. Using the Laplace equation discussed above, the relative driving forces (Delta P) for 25% and 50%
microfiber were 2 to 3 times greater than the control: (74/35 = 2), (74/24 = 3). The Bendtsen smoothness data (discussed below) imply more intimate contact with the surface while the higher driving force from the smaller pores indicate greater ability to pick up small droplets remaining on the surface.
An advantage that cellulose has over other polymeric surfaces such as nylon, polyester and polyolefins is the higher surface energy of cellulose which attracts and wicks liquid residue away from lower energy surfaces such as glass, metals and so forth.

[00131] For purposes of convenience, the relative wicking ratio of a microfiber containing sheet is generally defined to be the ratio of the average pore effective sizes of a like sheet without microfiber to a sheet containing microfiber. Thus, the Sample B and C sheets had relative wicking ratios of approximately 2 and 3 as compared with the control Sample A.
While the wicking ratio readily differentiates single ply CWP sheet made with cmf from a single ply sheet made with NBSK alone, more universal indicators of differences achieved with cmf fiber are high differential pore volumes at small pore radius (less than about 10-15 microns) as well as high capillary pressures at low saturation as is seen with two-ply wipers and handsheets

[00132] A series of two ply CWP sheets were prepared and tested for porosity, following the described procedures. Sample D was a control, prepared with NBSK fiber and without cmf, Sample E was a two ply sheet with 75% by weight NBSK fiber and 25% by weight cmf, and Sample F was a two ply sheet with 50% by weight NBSK fiber and 50% by weight cmf. Results appear in Table 15 and are presented graphically in Figure 23.

22955477.1 ' = WO 2010/033536

[00133] Table 15 - Two-Ply Sheet Porosity Data CumulCumulative Cumul. Cumul, Cumul. Cunrul.
, Pore , Pore Volume , Pore Volume Pore Capillary (Cumul.) Pore Pore PoreVolumeyokime Pure sample Pore Pore satrie Radius, Pressure, Pore Volume Volume Radius, Sample D, Sample Volume E Volume Volume micron nunH20 Sample D, Sample micron min3/(um*g) Sample ' Sample F, Sample F' 3 E, mmlueg) 3 mm )(meg) nun 1mg D, %
nu3/mg E, % mm /mg F, %
500 12 11.700 100.0 400.0 12.424 11.238 100.0 14.284 13.103 100.0 12.982 300 20 9.216 78.8 250.0 8.925 8.381 74.6 9.509 10.507 80.2 14.169 200 31 8.323 71.1 187.5 11.348 7.430 66.1 12.618 9.090 69.4 23.661 175 35 8.039 68.7 1625 14.277 7.115 63.3 12.712 8.498 64.9 27.530 150 41 7.683 65.7 137.5 15.882 6.797 60.5 14.177 7.810 59.6 23.595 125 49 7.285 62.3 117.5 20.162 6.443 57.3 18,255 7.220 55.1 47,483 110 56 6.983 59.7 105.0 22.837 6,169 54.9 18.097 6.508 49.7 34.959 100 61 6.755 57.7 95.0 26.375 5.988 53.3 24.786 6.158 47,0 35,689 90 68 6.491 55.5 85.0 36.970 5.740 51.1 29.910 5.801 44,3 41.290 80 77 6.121 52.3 75.0 57.163 5.441 48.4 33.283 5.389 41.1 50.305 70 88 5.550 47.4 65.0 88.817 5.108 45.5 45.327 4.885 37.3 70.417 60 102 4.661 39.8 55.0 87.965 4.655 41.4 55.496 4.181 31.9 64.844 50 123 3.782 32,3 475 93.089 4.100 36.5 69.973 3.533 27,0 57.847 45 136 3.316 28.3 42.5 90.684 3.750 33.4 73.408 3.244 24.8 70.549 40 153 2.863 24.5 375 71.681 3.383 30.1 60.294 2.891 22.1 61.640 35 175 2.504 21.4 32.5 69.949 3.081 27.4 64.984 2.583 19,7 60.308 30 204 2.155 18.4 275 76.827 2,756 24.5 90.473 2.281 17.4 62.847 25 245 1.771 15.1 22.5 85.277 2.304 20.5 119.637 1.967 15.0 57.132 20 306 1.344 11.5 18.8 83.511 1.706 15,2 110,051 1.681 12.8 56.795 17.5 350 1.135 9.7 16.3 83.947 1.431 12.7 89.091 1.539 11.8 62.253 15 408 0.926 7.9 13.8 73.671 1.208 10.8 63.423 1.384 10.6 62.246 12.5 490 0.741 6.3 11.3 72.491 1.049 9.3 59.424 1.228 9,4 65.881 613 0.560 4.8 9.5 74.455 0.901 8.0 63.786 1.063 8.1 61.996 9 681 0.486 4.2 8.5 68.267 0,837 7.5 66.147 1.001 7.6 69.368 SUB STITUTE SHEET (RULE 26) . WO 2010/033536 PC17US2009/057078 CiinmlCumulative Cuinul. Cumul. Coal. Cumul.
Pore Pore Volume Pore Volume Pore Capillary (Cumul.) Pore Pore Pore Volume VolumePore Sam Pore Pore Pore Sample Radius, Pressure, Pore Volume Volume Radius, Sample D, Volume Volume Volume micron mmH20 Sample D, Sample micron imm3/(ueg) ample F Sample ' F Sampla, Sample ' 3 E, mm,(lieg) MM. 1(ueg) nun'inig D, %
, nn3/mg E, mtn3 img F, %
8 766 0.417 3.6 75 66.399 0.771 6.9 73.443 0.932 7.1 70.425 7 875 0.351 3M 6.5 64.570 0.698 6,2 82.791 0.861 6.6 79.545 6 1021 0.286 2.5 5.5 66.017 0,615 5.5 104.259 0.782 6.0 100.239 1225 0.220 1.9 4.5 70.058 0.510 4.5 119.491 0.682 5.2 122.674 4 1531 0.150 1.3 3,5 74.083 0.391 3,5 142.779 0.559 4,3 170.707 3 2042 0.076 0.7 25 63.471 0.248 2.2 150.017 0.388 3.0 220.828 2 3063 0.013 0,1 15 12.850 0.098 0.9 98.197 0.167 1.3 167.499 1 - 6125 0.000 OM 0,000 0.0 0.000 0.0 SUBSTITUTE SHEET (RULE 26)

[00134] It is seen in Table 15 and Figure 23 that the two ply sheet structure somewhat masks the pore structure of individual sheets. Thus, for purposes of calculating wicking ratio, single plies should be used.

[00135] The porosity data for the cmf containing two ply sheet is nevertheless unique in that a relatively large fraction of the pore volume is at smaller radii pores, below about 15 microns.
Similar behavior is seen in handsheets, discussed below.

[00136] Following the procedures noted above, handsheets were prepared and tested for porosity. Sample G was a NBSK handsheet without cmf, Sample J was 100% cmf fiber handsheet and sample K was a handsheet with 50% cmf fiber and 50% NBSK.
Results appear in Table 16 and Figures 24 and 25.

SUBSTITUTE SHEET (RULE 26) , . WO 2010/033536

[00137] Table 16- flandsheet Porosity Cumul.
Clunulative Pore Cumul. Pore Curnul.
(Cumul.) Volume Pore Volume Pore Capillary Pore Pore Pore Volume Pore .. Pore .. Volume Pore Pore Sample Sample Radius, Pressure, Volume Radius, Sample G, Volume Volume Sample Volume Volume K, mntH
micron 20 Sample micron inth(ueg) Sample J, Sample j' K
Sample Sample G, rnm3/(um min-1(eg) mm3ling G' % inm3Img 1, % mirim K, A, t bi g 500 12.3 4.806 100,0 400.0 1.244 9.063 100.0 3963 5.769 100.0 1.644 300 20.4 4.557 94.8 250,0 2.149 , 8.271 91.3 7,112 5.440 94.3 3.365 200 30.6 4,342 90.4 187.5 2.990 7.560 83.4 9927 5.104 88.5 5.247 175 35 4.267 88.8 162.5 3.329 7.311 , 80.7 10.745 4.972 862 5.543 150 40.8 4.184 87.1 137.5 3.989 7.043 77.7 13.152 4.834 83.8 6.786 125 49 4,084 85,0 117.5 4.788 6.714 74,1 15,403 4,664 80,9 8.428 110 55.7 4.013 83.5 105.0 5.734 6.483 71.5 16.171 4.538 78.7 8.872 100 61.3 3.955 82.3 95.0 6.002 6.321 69.8 17.132 4.449 77.1 9.914 90 68.1 3.895 81.1 85.0 8.209 6.150 67.9 17.962 4.350 75.4 11.115 80 76.6 3.813 79.4 75.0 7.867 5.970 65.9 23.652 4.239 73.5 15.513 70 87.5 3.734 77.7 65.0 8.950 5.734 63.3 25.565 4.083 70.8 13.651 60 102.1 3,645 75.9 55.0 13.467 5.478 60.4 20.766 3.947 68.4 10.879 50 122.5 3.510 73.0 47,5 12.794 5.270 58.2 25.071 3.838 66.5 11,531 45 136.1 3.446 71,7 42.5 16.493 5.145 56.8 29,581 3.780 65.5 21,451 40 153.1 3.364 70.0 37.5 19.455 4.997 55.1 37.527 3.673 63,7 22.625 35 175 3.267 68.0 32.5 28.923 4.810 53.1 41.024 3.560 61.7 24.854 30 204.2 3.122 65.0 27.5 42,805 4.604 50.8 46.465 3.436 59.6 32.211 25 245 2.908 60.5 22.5 88,475 4.372 48.2 54.653 3.275 56.8 35.890 20 306.3 2.465 51.3 18.8 164.807 4.099 45.2 61.167 3.095 53.7 47.293 17.5 350 2,053 42.7 16,3 220.019 3.946 43.5 73.384 2.977 51.6 48.704 15 408.3 1.503 31.3 13.8 186.247 3.762 41.5 61.228 2.855 49.5 62.101 12.5 490 1.038 21.6 11.3 126.594 3.559 39.3 95.602 2.700 46.8 78,623 612.5 0.721 15.0 9.5 108.191 3.320 36.6 104.879 2.504 43.4 91,098 SUBSTITUTE SHEET (RULE 26) . . WO 2010/033536 Docket No. 20515-PCT
Cumul.
Cumulative Pore Cumul. Cumul. Cumul. Pore Curnul.
Volume Pore Volume Pore Capillary (Cuifiul.) Pore Pore Pore Volume Pore Pore Volume Pore Pore Sample Radius, Pressure, Volume Radius, Sample G, Volume Volume Sample Volume Sample Volume micron mm1120 Sample micron mm3,1(um*g) Sample 1, Sample ' 3 K, Sample k' 3 Sample G, 3 MAN 3 mmlum*g) mm Img J, % mm K, %
mm3lmg G, % gorl g 9 680.6 0,613 12.8 8.5 94,149 3.215 35.5 118.249 2.412 41.8 109.536 8 765.6 0,519 10.8 7.5 84.641 3.097 34.2 132.854 2.303 39.9 136.247 7 875 0.434 9.0 6.5 78.563 2.964 32.7 155.441 2,167 37.6 291.539 6 1020.8 0.356 7.4 5.5 79.416 2.809 31.0 242.823 1.875 32.5 250.346 1225 0.276 5.8 4.5 73.712 2.566 28.3 529.000 1.625 28.2 397.926 4 1531.3 0.203 4.2 3.5 78.563 2.037 22.5 562.411 1.227 21.3 459.953 3 2041.7 0.124 2.6 2.5 86.401 1.475 16.3 - 777.243 0.767 13.3 411.856 2 . 3062.5 . 0.038 0.8 1.5 37.683 0.697 7.7 697.454 0.355 6.2 355.034 1 6125 0.000 0.0 0.000 0.0 0.000 0.0 SUBSTITUTE SHEET (RULE 26)

[00138] Here again, it is seen that the sheets containing cmf had significantly more relative pore volume at small pore radii. The cmf containing two ply sheet had twice as much relative pore volume below 10-15 microns than the NBSK sheet; while the cmf and cmf containing handsheets had 3-4 times the relative pore volume below about 10-15 microns than the handsheet without cmf.

[00139] Figure 26 is a plot of capillary pressure versus saturation (cumulative pore volume) for CWP sheets with and without cmf. Here it is seen that sheets with cellulose microfiber exhibit up to 5 times the capillary pressure at low saturation due to the large fraction of small pores.

[00140] A Bendtsen smoothness and porosity tester (9 code SE 114), equipped with air compressor, 1 kg test head, 4 kg weight and clean glass plate was obtained from L&W USA, Inc., 10 Madison Road, Fairfield, New Jersey 07004 and used in the tests which are described below. Tests were conducted in accordance with ISO Test Method 8791-2 (1990).

[00141] A series of handsheets were prepared with varying amounts of cmf and the conventional papermaking fibers listed in Table 16. The handsheets were prepared wherein one surface was plated and the other surface was exposed during the air drying process. Both sides were tested for Bendtsen Roughness at lkg pressure and 5 kg pressure. Table 17 presents the average values of Bendtsen Roughness at lkg pressure and at 5 kg pressure, as well as the relative average Bendtsen Smoothness as compared with cellulosic sheets made without regenerated cellulose microfiber.

[00142] Table 17 - Bendtsen Roughness and Relative Bendtsen Smoothness Description % cmf Bendtsen Bendtsen Relative Relative Roughness Roughness Bendtsen Bendtsen Ave-lkg Ave-5kg Smoothness Smoothness mL/min mL/min (Avg) lkg (Avg) 5kg 0% cmf / 100 % NSK 0 762 372 1.00 1.00 20% cmf / 80 % NSK 20 382 174 2.00 2.14 50% cmf / 50 NSK 50 363 141 2.10 2.63 100% cmf / 0 NSK 100 277 104 0% cmf! 100 % SWK 0 1,348 692 1.00 1.00 20% cmf / 80 % SWK 20 590 263 2.29 2.63 50% cmf / 50 SWK 50 471 191 2.86 3.62 100% cmf / 0 % SWK 100 277 104 0% cmf/ 100 % Euc 0 667 316 1.00 1.00 20% cmf / 80 % Euc 20 378 171 1.76 1.85 SUBSTITUTE SHEET (RULE 26) 50% cmf / 50 % Euc 50 314 128 2.13 2.46 100% cmf / 0 Euc 100 277 104 0% cmf / 100 % SW BCTMP 0 2,630 1,507 1.00 1.00 20% cmf / 80 % SW BCTMP 20 947 424 2.78 3.55 50% cmf /50 % SW BCTMP 50 704 262 3.74 5.76 100% cmf / 0 % SW BCTMP 100 277 104

[00143] Figure 27 graphically represents the measured Bendtsen Roughness at 1 kg pressure. It can be appreciated from Table 17 and Figure 27 that Bendtsen Roughness decreases in a synergistic fashion (i.e. exponentially), especially at additions of fiber up to 50% or so. The relative smoothness of the sheets relative to a sheet without papermaking fiber ranged from about 1.7 at lkg up to about 6 in these tests.

[00144] Other embodiments can include:
[01]. A base sheet for food wrap products comprising:
a pulp-derived papermaking fiber and a fibrillated regenerated cellulose microfiber having a CSF value of less than about 175 mL.
[02]. The base sheet according to paragraph 01, wherein the base sheet has a 1-sheet caliper of from about 1 mil to about 3 mils, a basis weight of from about 5 lbs to about 25 lbs per 3,000 ft2, and an MD tensile of greater than about 5 lbs/inch.
[03]. The base sheet according to paragraphs 01 or 02, wherein the fibrillated regenerated cellulose microfiber has a CSF value of less than about 100 mL.
[04]. The base sheet according to any paragraph 01 to 03, wherein the fibrillated regenerated cellulose microfiber has a CSF value of less than about 25 mL.
[05]. The base sheet according to any paragraph 01 to 04, wherein the fibrillated regenerated cellulose microfiber has a number average diameter of from about 0.1 microns to about 2 microns.
=

22955477.1 Docket No. 20515-PCT
[06]. The base sheet according to any paragraph 01 to 05, wherein the fibrillated regenerated cellulose rnicrofiber has a coarseness value of from about 0.001 mg/100 m to about 0.6 mg/100 m.
[07]. The base sheet according to any paragraph 01 to 06, wherein the fibrillated regenerated cellulose microfiber has a weight average diameter of less than about 2 microns, a weight average length of less than about 500 microns, and a fiber count of greater than about 400 million fibers/gram. .
[08]. The base sheet according to any paragraph 01 to 07, wherein the fibrillated regenerated cellulose microfiber has a fiber count greater than about 200 billion fibers/gram.
[09]. The base sheet according to any paragraph 1 to 8, wherein at least about 50 wt%
of the fibrillated regenerated cellulose microfiber is finer than 14 mesh.
[10]. The base sheet according to any paragraph 01 to 09, wherein at least about 75%
by weight of the fibrillated regenerated cellulose microfiber is finer than 14 mesh.
[11]. A method for making a food wrap paper product comprising:
forming a base sheet comprising pulp-derived papermaking fiber and regenerated cellulose microfiber; and treating the base sheet with a water or grease resistant agent.
[12]. The method according to paragraph 11, wherein the water or grease resistant agent comprises a polyacrylate or polymethacrylate.
[13]. The method according to paragraphs 11 or 12, wherein the water or grease resistant agent comprises a polyamide or a styrene/butadiene polymer.
[14]. The method according to any paragraph 11 to 13, wherein the water or grease resistant agent comprises a polyolefin polymer or a polyester polymer.

22955477.1 = Docket No. 20515-PCT
[15]. The method according to any paragraph 11 to 14, wherein the water or grease resistant agent comprises a polylactide polymer or a polylalkanoate polymer.
[16]. The method according to any paragraph 11 to 15, wherein the water or grease resistant agent comprises a wax.
[17]. The method according to any paragraph 11 to 16, wherein the water or grease resistant agent comprises a fluorochemical sizing agent or a chrome complex sizing agent.
[18]. The method according to any paragraph 11 to 17, wherein the water resistant agent, the grease resistant agent, or both are applied to the base sheet in water-borne form.
[19]. The method according to any paragraph 11 to 18, wherein the water resistant agent, the grease resistant agent, or both are applied to the base sheet as a latex.
[20]. The method according to any paragraph 11 to 19, wherein the water resistant agent, the grease resistant agent, or both are applied to the base sheet in melt form.

[00145] Certain embodiments and features have been described using a set of numerical upper limits and a set of numerical lower limits. It should be appreciated that ranges from any lower limit to any upper limit are contemplated unless otherwise indicated. Certain lower limits, upper limits and ranges appear in one or more claims below. All numerical values are "about" or "approximately" the indicated value, and take into account experimental error and variations that would be expected by a person having ordinary skill in the art.

[00146] Various terms have been defined above. To the extent a term used in a claim is not defined above, it should be given the broadest definition persons in the pertinent art have given that term as reflected in at least one printed publication or issued patent.

22955477.1

[00147] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
_ SUBSTITUTE SHEET (RULE 26)

Claims (15)

Claims:
What is claimed is:

1. A base sheet for food wrap products, comprising:
a pulp-derived papermaking fiber; and a fibrillated regenerated cellulose microfiber having a CSF value of less than about 175 mL, wherein the base sheet has a SAT value of less than 2 g/g, a 1-sheet caliper of from about 1 mil to about 3 mils, a basis weight of from about 5 lbs to about 25 lbs per 3,000 ft2, and an MD
tensile of greater than about 5 lbs/inch.

2. The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a CSF value of less than about 100 mL.

3. The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a CSF value of less than about 25 mL.

4. The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a number average diameter of from about 0.1 microns to about 2 microns.

5. The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a coarseness value of from about 0.001 mg/100 m to about 0.6 mg/100 m.

6. The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a weight average diameter of less than about 2 microns, a weight average length of less than about 500 microns, and a fiber count of greater than about 400 million fibers/gram.

7 . The base sheet of claim 1, wherein the fibrillated regenerated cellulose microfiber has a fiber count greater than about 200 billion fibers/gram.

8. The base sheet of claim 1, wherein at least about 50 wt% of the fibrillated regenerated cellulose microfiber is finer than 14 mesh.

9. The base sheet of claim 1, wherein at least about 75% by weight of the fibrillated regenerated cellulose microfiber is finer than 14 mesh.

10. The base sheet of claim 1, wherein the base sheet comprises from about 15 wt% to about 95 wt% of the fibrillated regenerated cellulose microfiber.

11. The base sheet of claim 1, wherein the base sheet has a pore size of less than about 15 microns.

12. The base sheet of claim 1, wherein the base sheet has about 50% of its cumulative pore volume in pore sizes of about 15 microns or less.

13. A base sheet for food wrap products, comprising:
a pulp-derived papermaking fiber;
a fibrillated regenerated cellulose microfiber having a CSF value of less than about 175 mL, a weight average length of less than about 400 microns, and a weight average diameter of less than about 2 microns; and a water or grease resistant agent, or both applied to the base sheet in water borne form, melt form, or as a latex, wherein the base sheet has a SAT value of less than 2 g/g, a MD tensile strength of greater than about 10 lbs/inch, and a pore size of less than about 15 microns.

14. The base sheet of claim 13, wherein the fibrillated regenerated cellulose microfiber has a CSF value of less than about 25 mL.

15. The base sheet of claim 13, wherein the base sheet has a 1-sheet caliper of about 1 mil to about 3 mils and a basis weight of about 5 lbs to about 25 lbs per 3,000 ft2.