CN102443347A - Elastic metal shining coating and its preparation method - Google Patents
Elastic metal shining coating and its preparation method Download PDFInfo
- Publication number
- CN102443347A CN102443347A CN2011103353942A CN201110335394A CN102443347A CN 102443347 A CN102443347 A CN 102443347A CN 2011103353942 A CN2011103353942 A CN 2011103353942A CN 201110335394 A CN201110335394 A CN 201110335394A CN 102443347 A CN102443347 A CN 102443347A
- Authority
- CN
- China
- Prior art keywords
- component
- agent
- coating
- metallic luster
- elastic metallic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an elastic metal shining coating and its preparation method, and belongs to the field of building materials. The coating is composed of a component 1 and a component 2 at the weight ratio of 6-10:1. The component 1 contains the following raw materials of: by weight, xylene, hexone, butyl acetate, propylene glycol methyl ether acetate, a fluorocarbon resin, aluminum paste, a dispersant, a leveling agent, an antifoaming agent, a scratch-resistance auxiliary agent and a polyester polyol resin. The component 2 is a curing agent. The combination of a fluorine-containing polymer and the elastic polyester resin in the coating endows the paint film with good elasticity, resistance to chemicals, non-adhesiveness, low friction and the like. Therefore, the coating provided by the invention is an elastic and persistant coating with excellent comprehensive properties. The raw materials of the coating are easily available. The coating requires a simple production method and convenient manual operation, accords with application requirements, has an extensive application prospect, and can be used for resisting fine cracks on exterior walls of buildings.
Description
Technical field
The present invention relates to building material field, what relate in particular to that a kind of modern city external wall and external thermal insulation wall surface use has elastic metallic luster coating of elasticity flash effect and preparation method thereof.
Background technology
From early eighties, the fluorocarbon coating of ambient cure is succeeded in developing, and this coating easy to use has the unrivaled weathering resistance of general coating, chemical-resistant, preservative property, contamination property not, premium propertiess such as water tolerance high firmness and high gloss.But itself does not have elasticity fluorine carbon metal paint; The cracking resistance effect is bad; Conventional in recent years fluorine carbon metal paint causes the fluorine carbon metal paint paint film along with the cracking of heat insulation base layer and seriously ftractures on the insulation basal plane, influence whole facade image, even influences the quality of whole engineering; The performance of fluorine carbon metal paint is had a greatly reduced quality, and then influence the large scale application of fluorocarbon coating at the exterior wall product scope.
Summary of the invention
Embodiment of the present invention provides a kind of elastic metallic luster coating and preparation method thereof; Can solve existing fluorine carbon metal paint itself and not have elasticity; The problem that the cracking resistance effect is bad is that a kind of simple for production, excellent performance, cracking resistance are effective, the elastic metallic luster coating of long service life.
Following for addressing the above problem technical scheme provided by the invention:
Embodiment of the present invention provides a kind of elastic metallic luster coating, and this coating is by component one and component two by weight ratio 6～10: 1 forms;
Wherein, component one is made up of following each raw material by mass percentage: YLENE 18～22%, hexone 6～8%, N-BUTYL ACETATE 8～12%, 1-Methoxy-2-propyl acetate 4～6%, fluorocarbon resin 43～47%, aluminium-silver slurry 7～9%, dispersion agent 0.5～0.6%, flow agent 0.2～0.3%, skimmer 0.2～0.3%, scratch resistance auxiliary agent 0.9～1% and polyester polyol resin 4.0～4.1%;
Component two is a solidifying agent.
In the above-mentioned coating, it is the normal temperature solidified fluorocarbon resin of fluorochemical monomer and the copolymerization of alkyl ethane and ethylene ether that said fluorocarbon resin adopts with the trifluorochloroethylene.
In the above-mentioned coating, said dispersion agent adopts fatty acid dispersion agent or aliphatic amide type dispersion agent.
In the above-mentioned coating, said flow agent adopts polyacrylic ester or modified polyacrylate class flow agent.
In the above-mentioned coating, said skimmer adopts mineral oil defoaming agent or silicoorganic compound defoamer.
In the above-mentioned coating, said scratch resistance auxiliary agent adopts micronization polyolefine blended wax class scratch resistance auxiliary agent.
In the above-mentioned coating, the solidifying agent of said component two adopts aliphatic polymeric isocyanate.
Embodiment of the present invention also provides a kind of preparation method of elastic metallic luster coating, and this method comprises:
Preparation component one:
Get each raw material of the component one of preparation elastic metallic luster coating by above-mentioned prescription;
With hexone, N-BUTYL ACETATE, fluorocarbon resin, dispersion agent in component one raw material and account for the YLENE of YLENE gross weight 10%, the fluorocarbon resin that accounts for fluorocarbon resin gross weight 30% add to disperse in the cylinder, dispersion is 5 minutes under the rotating speed of 300～400rpm; And then adding flow agent, scratch resistance auxiliary agent and aluminium-silver slurry; Under the rotating speed of 800～1000rpm, disperseed 20 minutes; Rotating speed is adjusted to 300～400rpm; Under whipped state, add skimmer, polyester polyol resin, remaining YLENE and remaining fluorocarbon resin, treat the bubble completely dissolve after, the product that obtains is component one;
By the above-mentioned solidifying agent of getting as component two, with the above-mentioned component that make mix component two at 6～10: 1 by weight ratio, promptly obtains the elastic metallic luster coating.
Can find out by the above-mentioned technical scheme that provides; Pass through in the coating composition one of embodiment of the present invention to add fluorocarbon resin (elastic resin) as filmogen; And cooperate with solidifying agent as component two, make and the existing fine elasticity of this fluorocarbon resin can stretch and restore repeatedly; The effectively lasting crackle that covers can ensure effective weathering resistance again.And, also make this coating have good metallic travel owing to add aluminium-silver slurry in the component one.
Embodiment
Below in conjunction with specific embodiment the technical scheme among the present invention is carried out clear, intactly description, obviously, described embodiment only is the present invention's part embodiment, rather than whole embodiment.Based on embodiments of the invention, those of ordinary skills belong to protection scope of the present invention not making the every other embodiment that is obtained under the creative work prerequisite.
Do to describe in detail further in the face of the embodiment of the invention down.
Embodiment of the present invention provides a kind of elastic metallic luster coating, and this coating is by component one and component two by weight ratio 6～10: 1 forms;
Wherein, component one is made up of following each raw material by mass percentage: YLENE 18～22%, hexone 6～8%, N-BUTYL ACETATE 8～12%, 1-Methoxy-2-propyl acetate 4～6%, fluorocarbon resin 43～47%, aluminium-silver slurry 7～9%, dispersion agent 0.5～0.6%, flow agent 0.2～0.3%, skimmer 0.2～0.3%, scratch resistance auxiliary agent 0.9～1% and polyester polyol resin 4.0～4.1%;
Component two is a solidifying agent.
It is the normal temperature solidified fluorocarbon resin of fluorochemical monomer and the copolymerization of alkyl ethane and ethylene ether that fluorocarbon resin in the above-mentioned coating adopts with the trifluorochloroethylene.This fluorocarbon resin is as filmogen, makes the elastic metallic luster coating of processing not only can be used on the surfaces such as concrete substrate, ceramic tile, can be used in equally on metal such as copper, aluminium, stainless steel, iron and steel and the glass surface.
Dispersion agent in the above-mentioned coating adopts fatty acid dispersion agent or aliphatic amide type dispersion agent.Dispersion agent is a kind of surfactant, can disperse and stabilising system in various materials.
Flow agent in the above-mentioned coating adopts polyacrylic ester or modified polyacrylate class flow agent.Flow agent is to help filmogen reasonable levelling surface effect in the process of drying and forming-film, to occur.
Skimmer in the above-mentioned coating adopts mineral oil defoaming agent or silicoorganic compound defoamer.Skimmer is to eliminate in the production process and the bubble that is generated in the construction process.Make coating have the apparent effect of good stability in storage, application property and paint film.
Scratch resistance auxiliary agent in the above-mentioned coating adopts the scratch resistance auxiliary agent to adopt micronization polyolefine blended wax class scratch resistance auxiliary agent.The scratch resistance auxiliary agent is a kind of surperficial auxiliary agent of tetrafluoroethylene, after the coating film forming, can rest on coating surface, and improves the scratch resistance performance of coating surface.
Aluminium-silver slurry in the above-mentioned coating is the aluminium powder slurry through the chemistry coating of Switzerland Eckart GmbH & Co. KG.Aluminium-silver slurry is the main pigment of this coating as the metallic paint that flash effect is arranged.
Solidifying agent in the above-mentioned coating adopts aliphatic polymeric isocyanate.
Polyester polyol resin in the above-mentioned coating plays the elastic effect of paint film of regulating in whole formula system.
The solidifying agent as component two in the above-mentioned coating is to react with the fluorocarbon resin in the component one, forms the tridimensional network paint film of crosslinking curing, the paint film of this two-pack ambient cure, and surface compact, good hardness can provide the surface of good effect.Can make the elastic metallic lacquer can either obtain elasticity preferably, can satisfy the requirement of exterior wall again, guarantee the workability of this elastic metallic luster coating paint film weatherability.
The preparation method of above-mentioned elastic metallic luster coating specifically may further comprise the steps:
Preparation component one:
Get each raw material of the component one of preparation elastic metallic luster coating by above-mentioned prescription;
With hexone, N-BUTYL ACETATE, fluorocarbon resin, dispersion agent in component one raw material and account for the YLENE of YLENE gross weight 10%, the fluorocarbon resin that accounts for fluorocarbon resin gross weight 30% add to disperse in the cylinder, dispersion is 5 minutes under the rotating speed of 300～400rpm; And then adding flow agent, scratch resistance auxiliary agent and aluminium-silver slurry; Under the rotating speed of 800～1000rpm, disperseed 20 minutes; Rotating speed is adjusted to 300～400rpm; Under whipped state, add skimmer, polyester polyol resin, remaining YLENE and remaining fluorocarbon resin, treat the bubble completely dissolve after, the product that obtains is component one;
Get the solidifying agent as component two by above-mentioned prescription, with the above-mentioned component that make mix component two at 6～10: 1 by weight ratio, promptly obtains the elastic metallic luster coating.
All kinds of SOLVENTS mainly plays dilution and is dissolved into membrane substance, reaches working viscosity, is easy to construction.
Construction technology is:
A. processing base level: before base treatment, concrete wall needs the maintenance of certain hour, and the curing time in general new cement wall surface winter is 28 days, and the curing time in summer is 14 days.Maintenance is arrived the pH value of basic unit less than 10, and water ratio carries out processing base level again after 10%.Should thoroughly remove loose, peeling, hollowing, atomizing basic unit, remove pollutents such as dust, greasy dirt.
Base materials such as ceramic tile, marble, metal must carry out necessary polishing to be handled, and thoroughly removes loose, peeling, hollowing, atomizing basic unit then, removes pollutents such as dust, greasy dirt.
B. elastic metallic luster coating: press component 1: component 2=8: 1 mixed is good, converts 20% special diluting agent again and dilutes.Directly evenly spray on the object plane, generally spray twice.In order to make protective material reach good perviousness, back one time and then last time directly spraying must pitch time.Spraying must put in place, and the spray of leakage and uneven phenomenon can not be arranged.With joining with usefulness, the same day, allotment will use up in 4 hours after preparing in the use.
Elastic metallic luster coating of the present invention belongs to the solvent-borne type product, and service tool cleans with special diluting agent and gets final product.
Through specific embodiment, the present invention is described further below.
Embodiment 1
Present embodiment provides a kind of elastic metallic luster coating; This coating is made up of component one and component two; Wherein, Component one is made up of YLENE, MIBK, N-BUTYL ACETATE, PMA, fluorocarbon resin JF-2X, polyester polyol resin, dispersion agent 163, flow agent 361, skimmer 2020, scratch resistance auxiliary agent 996 and solidifying agent N-75, and component one each raw material is by mass percentage:
| Component one | Quality (kg) |
| YLENE | 20.0 |
| MIBK | 7.0 |
| N-BUTYL ACETATE | 10.0 |
| PMA | 4.0 |
| Fluorocarbon resin JF-2X | 45.0 |
| Aluminium-silver slurry 214 | 8.0 |
| Dispersion agent 163 | 0.5 |
| Flow agent 361 | 0.2 |
| Skimmer 2020 | 0.3 |
| Scratch resistance auxiliary agent 996 | 1.0 |
| Polyester polyol resin | 4.0 |
| Component two | Quality (kg) |
| Solidifying agent 22A-75 | 12.5 |
The making method of present embodiment elastic metallic luster coating is: YLENE, MIBK, N-BUTYL ACETATE, PMA, the fluorocarbon resin JF-2X that accounts for fluorocarbon resin JF-2X gross weight 30%, the dispersion agent 163 that will account for YLENE gross weight 10% earlier add and disperse under the rotating speed of 300～400rpm, to disperse 5 minutes in the cylinder; And then adding flow agent 361, scratch resistance auxiliary agent 996 and aluminium-silver slurry 214; After 800～1000rpm middling speed is disperseed 20 minutes; Reduce to 300～400rpm to speed, add skimmer 066, polyester polyol resin and remaining YLENE, remaining fluorocarbon resin JF-2X under the state of stirring again, treat the bubble completely dissolve after; Promptly obtain component one, can be further with component one check and packing warehouse-in.
During use, component one with component two is by weight ratio in this elastic metallic luster coating: component one: component two=8: 1 mixes use, promptly obtains this elastic metallic luster coating.
The elastic metallic luster coating of present embodiment and paint film property such as following table:
Embodiment 2
Present embodiment provides a kind of elastic metallic luster coating; This coating is made up of component one and component two; Wherein, Component one is made up of YLENE, MIBK, N-BUTYL ACETATE, PMA, fluorocarbon resin JF-2X, polyester polyol resin, dispersion agent 163, flow agent 361, skimmer 2020, scratch resistance auxiliary agent 996 and solidifying agent N-75, and component one each raw material is by mass percentage:
| Component one | Quality (kg) |
| YLENE | 18.0 |
| MIBK | 6.0 |
| N-BUTYL ACETATE | 12.0 |
| PMA | 4.0 |
| Fluorocarbon resin JF-2X | 47.0 |
| Aluminium-silver slurry 214 | 7.0 |
| Dispersion agent 163 | 0.5 |
| Flow agent 361 | 0.2 |
| Skimmer 2020 | 0.2 |
| Scratch resistance auxiliary agent 996 | 1.0 |
| Polyester polyol resin | 4.1 |
| Component two | Quality (kg) |
| Solidifying agent 22A-75 | 12.5 |
The making method and the embodiment 1 of present embodiment elastic metallic luster coating are basic identical, can no longer repeat at this referring to embodiment 1.
Embodiment 3
Present embodiment provides a kind of elastic metallic luster coating; This coating is made up of component one and component two; Wherein, Component one is made up of YLENE, MIBK, N-BUTYL ACETATE, PMA, fluorocarbon resin JF-2X, polyester polyol resin, dispersion agent 163, flow agent 361, skimmer 2020, scratch resistance auxiliary agent 996 and solidifying agent N-75, and component one each raw material is by mass percentage:
| Component one | Quality (kg) |
| YLENE | 22.0 |
| MIBK | 6.0 |
| N-BUTYL ACETATE | 10.0 |
| PMA | 4.0 |
| Fluorocarbon resin JF-2X | 43.0 |
| Aluminium-silver slurry 214 | 9.0 |
| Dispersion agent 163 | 0.5 |
| Flow agent 361 | 0.3 |
| Skimmer 2020 | 0.2 |
| Scratch resistance auxiliary agent 996 | 1.0 |
| Polyester polyol resin | 4.0 |
| Component two | Quality (kg) |
| Solidifying agent 22A-75 | 12.5 |
The making method and the embodiment 1 of present embodiment elastic metallic luster coating are basic identical, can no longer repeat at this referring to embodiment 1.
In sum; The elastic metallic luster coating fluoropolymer and the elastic polyester resin-bonded of the embodiment of the invention make paint film have good elasticity, chemical proofing, non-adhesive; Characteristics such as low frictional properties are the coating that a kind of elasticity has the excellent combination property of lasting retentivity.This coating raw material is easy to get; Working method is simple, and manual operation is convenient, meets request for utilization; Have broad application prospects; Can be used for resisting the fine cracks of modern architecture exterior wall, can use, can resist the erosion of acid rain, salt fog UV-light at external wall, facilities for transport and communication, maritime facilities, urban public utilities.The paint film cryodrying is functional, can construct in cold season.And owing to adopt fluorocarbon resin not only can be used on the surfaces such as concrete substrate, ceramic tile, can be used in equally on metal such as copper, aluminium, stainless steel, iron and steel and the glass surface as filmogen.
The above; Be merely the preferable embodiment of the present invention, but protection scope of the present invention is not limited thereto, any technician who is familiar with the present technique field is in the technical scope that the present invention discloses; The variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (8)
1. an elastic metallic luster coating is characterized in that, this coating is by component one and component two by weight ratio 6～10: 1 forms;
Wherein, component one is made up of following each raw material by mass percentage: YLENE 18～22%, hexone 6～8%, N-BUTYL ACETATE 8～12%, 1-Methoxy-2-propyl acetate 4～6%, fluorocarbon resin 43～47%, aluminium-silver slurry 7～9%, dispersion agent 0.5～0.6%, flow agent 0.2～0.3%, skimmer 0.2～0.3%, scratch resistance auxiliary agent 0.9～1% and polyester polyol resin 4.0～4.1%;
Component two is a solidifying agent.
2. elastic metallic luster coating according to claim 1 is characterized in that, it is the normal temperature solidified fluorocarbon resin of fluorochemical monomer and the copolymerization of alkyl ethane and ethylene ether that said fluorocarbon resin adopts with the trifluorochloroethylene.
3. elastic metallic luster coating according to claim 1 is characterized in that, said dispersion agent adopts fatty acid dispersion agent or aliphatic amide type dispersion agent.
4. elastic metallic luster coating according to claim 1 is characterized in that, said flow agent adopts polyacrylic ester or modified polyacrylate class flow agent.
5. elastic metallic luster coating according to claim 1 is characterized in that, said skimmer adopts mineral oil defoaming agent or silicoorganic compound defoamer.
6. elastic metallic luster coating according to claim 1 is characterized in that, said scratch resistance auxiliary agent adopts micronization polyolefine blended wax class scratch resistance auxiliary agent.
7. elastic metallic luster coating according to claim 1 is characterized in that, the solidifying agent of said component two adopts aliphatic polymeric isocyanate.
8. the preparation method of an elastic metallic luster coating is characterized in that, this method comprises:
Preparation component one:
Get each raw material of the component one of preparation elastic metallic luster coating by each described prescription of aforesaid right requirement 1-6;
With hexone, N-BUTYL ACETATE, fluorocarbon resin, dispersion agent in component one raw material and account for the YLENE of YLENE gross weight 10%, the fluorocarbon resin that accounts for fluorocarbon resin gross weight 30% add to disperse in the cylinder, dispersion is 5 minutes under the rotating speed of 300～400rpm; And then adding flow agent, scratch resistance auxiliary agent and aluminium-silver slurry; Under the rotating speed of 800～1000rpm, disperseed 20 minutes; Rotating speed is adjusted to 300～400rpm; Under whipped state, add skimmer, polyester polyol resin, remaining YLENE and remaining fluorocarbon resin, treat the bubble completely dissolve after, the product that obtains is component one;
By aforesaid right requirement 1 or 7 each get solidifying agent as component two, with the above-mentioned component that make mix component two at 6～10: 1 by weight ratio, promptly obtains the elastic metallic luster coating.