CN102909803B - Kettle pattern manufacturing method - Google Patents
Kettle pattern manufacturing method Download PDFInfo
- Publication number
- CN102909803B CN102909803B CN201210461572.0A CN201210461572A CN102909803B CN 102909803 B CN102909803 B CN 102909803B CN 201210461572 A CN201210461572 A CN 201210461572A CN 102909803 B CN102909803 B CN 102909803B
- Authority
- CN
- China
- Prior art keywords
- kettle
- mould
- mold
- cavity plate
- cavity board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kettle pattern manufacturing method, which comprises the following steps of: S01, designing a mold according to the appearance of a kettle; S02, forming a mold cavity plate and performing surface electronic initial polishing; S03, cleaning the mold cavity plate in the step S02; S04, coating the pre-manufactured silk screen patterns on the mold cavity plate by using DPS-400 type etching printing ink, immediately removing the silk screen after the ink is coated, and forming a film layer on the mold cavity plate through the DPS-400 type etching printing ink; S05, drying the mold in the step S04; S06, putting the mold dried in the step S05 into the prepared ferric trichloride solution, and etching; S07, washing the mold etched in the step S06 by using kerosene, and demolding; S08, performing surface electronic finishing polish on the mold cavity plate etched in the step S07; S09, performing an injection-compression molding process by using an injection molding machine; and S10, obtaining the kettle with patterns. The method is simple in process and convenient to manufacture, and the manufactured kettle has clear patterns.
Description
Technical field
The present invention relates to kettle technical field, particularly relate to a kind of Kettle pattern manufacture method.
Background technology
Kettle is the central requisite daily necessities of family and life.At present, the large Multiple Shape of existing kettle is single, and existing technique can not realize one-shot forming and some lines or pattern are directly identified to kettle case surface, so invent a kind of simple and effective process to become a kind of necessary.
Summary of the invention
(1) technical problem that will solve
The problem to be solved in the present invention is to provide a kind of Kettle pattern manufacture method, can not realize to overcome existing technique in prior art the defect that some lines or pattern to be directly identified to kettle case surface by one-shot forming.
(2) technical scheme
For solving the problems of the technologies described above, the invention provides a kind of Kettle pattern manufacture method,
Include following steps:
S01, carrys out designing mould according to kettle profile;
S02, cavity board carries out surface electronic just polishing after machine-shaping;
S03, cleans the described cavity board of S02;
S04, be coated on described cavity board with DPS-400 type etching ink by ready made silk-screen patterns, after described ink is painted with, silk screen is taken away immediately, and DPS-400 type etching ink forms a skim on described cavity board;
S05, dries the described mould of S04;
S06, puts into the described mould after oven dry in S05 among the liquor ferri trichloridi configured, etches;
S07, rinses well the mould kerosene etched in S06, and demoulding;
S08, carries out surface electronic finishing polish by the cavity board etched in S07;
S09, carries out shaping process of pressure injection with injection machine;
S10, obtains being with dapple kettle body.
Further, the sodium hydroxide solution containing 20% in described S03, during cleaning die die cavity, is adopted to clean, or the aqueous solution soaking of 50 ~ 60 DEG C about ten minutes.
Further, dry with infrared lamp direct irradiation in described S05.
Further, the described mould after oven dry in S05 is put among the liquor ferri trichloridi configured and soak 5 ~ 6 hours.
(3) beneficial effect
A kind of Kettle pattern manufacture method of the present invention, technique is simple, and easily manufactured, the Kettle pattern made is clear.
Accompanying drawing explanation
Fig. 1 is the flow chart of a kind of Kettle pattern manufacture method of the present invention.
Detailed description of the invention
Below in conjunction with drawings and Examples, the specific embodiment of the present invention is described in further detail.Following examples for illustration of the present invention, but are not used for limiting the scope of the invention.
As shown in Figure 1, a kind of Kettle pattern manufacture method of the present invention,
Include following steps:
S01, carrys out designing mould according to kettle profile;
S02, cavity board carries out surface electronic just polishing after machine-shaping;
S03, cleans the above-mentioned cavity board of S02;
S04, be coated on described cavity board with DPS-400 type etching ink by ready made silk-screen patterns, after described ink is painted with, silk screen is taken away immediately, and DPS-400 type etching ink forms a skim on described cavity board;
S05, dries the above-mentioned mould of S04;
S06, puts into the described mould after oven dry in S05 among the liquor ferri trichloridi configured, etches;
S07, rinses well the mould kerosene etched in S06, and demoulding;
S08, carries out surface electronic finishing polish by the cavity board etched in S07;
S09, carries out shaping process of pressure injection with injection machine;
S10, obtains being with dapple kettle body.
Ferric trichloride is molten to react with mould, and the skim do not formed with DPS-400 type etching ink reacts.
The sodium hydroxide solution containing 20% is adopted to clean in above-mentioned S03 during cleaning die die cavity, or the aqueous solution soaking of 50 ~ 60 DEG C about ten minutes.The present embodiment selects the sodium hydroxide solution of 20% to clean.
Dry with infrared lamp direct irradiation in above-mentioned S05.The object of drying, makes film not loosen easily, firmly fixes.
Above-mentioned mould after oven dry in S05 is put among the liquor ferri trichloridi configured and soak 5 ~ 6 hours, depending on the degree of depth of concrete etching.
A kind of Kettle pattern manufacture method of the present invention, technique is simple, and easily manufactured, the Kettle pattern made is clear.
In sum, above-mentioned embodiment is not restricted embodiment of the present invention, and the modification that all those skilled in the art carry out on the basis of flesh and blood of the present invention or equivalent deformation, all at technology category of the present invention.
Claims (3)
1. a Kettle pattern manufacture method, is characterized in that,
Include following steps:
S01, carrys out designing mould according to kettle profile;
S02, cavity board carries out surface electronic just polishing after machine-shaping;
S03, cleans the described cavity board of S02, adopts the sodium hydroxide solution containing 20% to clean in described S03 during cleaning die die cavity;
S04, be coated on described cavity board with DPS-400 type etching ink by ready made silk-screen patterns, after described ink is painted with, silk screen is taken away immediately, and DPS-400 type etching ink forms a skim on described cavity board;
S05, dries the described mould of S04, dries in described S05 with infrared lamp direct irradiation;
S06, puts into the described mould after oven dry in S05 among the liquor ferri trichloridi configured, etches;
S07, rinses well the mould kerosene etched in S06, and demoulding;
S08, carries out surface electronic finishing polish by the cavity board etched in S07;
S09, carries out shaping process of pressure injection with injection machine;
S10, obtains being with dapple kettle body.
2. Kettle pattern manufacture method according to claim 1, is characterized in that: the aqueous solution soaking of 50 ~ 60 DEG C can also be adopted in described S03 during cleaning die die cavity to clean for about ten minutes.
3. Kettle pattern manufacture method according to claim 1 and 2, is characterized in that: the described mould after oven dry in S05 is put among the liquor ferri trichloridi configured and soak 5 ~ 6 hours.