CN103058604B - Paint - Google Patents
Paint Download PDFInfo
- Publication number
- CN103058604B CN103058604B CN201210565433.2A CN201210565433A CN103058604B CN 103058604 B CN103058604 B CN 103058604B CN 201210565433 A CN201210565433 A CN 201210565433A CN 103058604 B CN103058604 B CN 103058604B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- calcium chloride
- paint
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses paint. The paint comprises the following components according to every one hundred parts by weight: 25-30 parts of white cement, 20-25 parts of titanium dioxide, 18-22 parts of activated chalk, 15 parts of white quartz powder, 2.5-3.5 parts of particulate silicic acid, 1-1.5 parts of calcium chloride, 0.5-1 part of cuprous chloride, 1.5-2.5 parts of diatom powder, 1.5-2.5 parts of bentonite, and 3-4 parts of polyacrylamide. The calcium chloride is food grade calcium chloride. The white cement is in a 325 type. The titanium dioxide is in a rutile type. The paint is safe, environment-friendly, dampproof, anti-condensation, anti-ice, mildew proof, capable of purifying indoor air and adsorbing peculiar smell, low in cost, free of peculiar smell, nonflammable, and capable of being applied to fitment-coating of the inner surfaces of buildings of various industries and houses, wherein the market-set price of solid objects of the paint is 20 yuan/kg, the situations that due to moisture condensation on the surfaces of the buildings, water dripping, water flowing, mould breed and spread, even crack which results in collapse and falling off of a surface layer are caused are avoided, and normal production and living health and safety of people are guaranteed.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of coating.
Background technology
Some enterprises are as paper mill, food factory etc., its production environment, because atmospheric moisture causes greatly factory building in winter warehouse ceiling, the serious dewfall of metope, causes and drips, drops down water, and big area mould grows and stretches, quality product is exerted an influence, if after top board, wall infiltration, in severe cold certain period in winter, also can freeze, expand, cause coating and matrix to burst apart, cause top layer slump, cause body of wall local area to burst apart, building safety and corporate image are worked the mischief.Existing solution is: adopt the traditional products such as porcelain-imitated coating, 108 coating, Nippon, latex coating, form after coating, it has hydrophobicity, after metope makes moist, aqueous vapor is difficult to discharge, under temperature variation effect, a series of breakoff phenomenons such as can causing coating bubbling, burst apart, anti-salty, coating is stuck up volume, come off occur, on market, occurred that some novel product price comparisons are expensive as the new happy 100 yuan/kg of antifogging coating of Changsha, also there is low-cost novel product, if Tianchi its price of board antifogging coating in Shenzhen is 38 yuan/kg, belong to organic product, itself there is inflammable danger, at paper industry, food-processing industry is definitely out of use, and can produce niff during construction operation, nauseating, produce environmental pollution, moreover, the rate of drying of coating is excessively slow, be generally about seven days, this also can have influence on engineer operation progress greatly, be difficult to be accepted by users.
Summary of the invention
The object of the invention is to propose a kind of buildings internal surface that is applied to, with low cost, protection against the tide, antisweat, mildew-resistant, anti-freeze, the absorption peculiar smell that purifies the air of a room, the coating of safety and environmental protection.
Object of the present invention is achieved through the following technical solutions: a kind of coating, contains following component: 25～30 parts of white cements, 20～25 parts of titanium dioxides, 18～22 parts of activated Calcium carbonates, 15 parts, white quartz powder, 2.5～3.5 parts of particulate silicic acid, 1～1.5 part, calcium chloride, 0.5～1 part of cuprous chloride, 1.5～2.5 parts, diatom powder, 1.5～2.5 parts of wilkinites, 3～4 parts of polyacrylamides in every 100 weight part coating.
Described calcium chloride is food-grade calcium chloride.
Described white cement is 325#.
Described titanium dioxide is rutile-type.
The invention has the beneficial effects as follows: owing to containing a certain proportion of several strong hygroscopic material composition calcium chloride, diatom powder, wilkinite, activated Calcium carbonate in product, coating has excellent moistureproof antisweat performance, it is one of main characteristic of product, test and show when coat-thickness reaches 3mm, every square metre of water-retaining capacity can reach 1.5 kg.
In product proportioning, contain appropriate frostproofer calcium chloride, after coating water suction, can effectively resist-30 ℃ of low temperature, make water suction in coating not produce the destruction that the crystallization of freezing causes expansion stress.
In coating, contained hygroscopic material calcium chloride is in when water suction, the thermopositive reaction that can produce, and its instantaneous temperature can reach 50 ℃ of left and right, and discharges that can evaporate the water during heat absorption just fundamentally stoped the icing possibility of aqueous vapor dewfall.
In product, be added with a certain amount of sanitas calcium chloride and disinfectant cuprous chloride, effectively mould fungus inhibition grows and stretches.
In product ingredient particles silicic acid, contain abundant hydroxyl OH-and abundant negative oxygen ion 0-is contained on diatom powder surface, coating has the various gas with foreign flavor molecules of absorption, and carries out with it the effect of ion-exchange chemical reaction, mainly generates CO
2and H
2the performance that O discharges, has outstanding environment-friendly function.
Existence due to contained above-mentioned activeconstituents in coating, in coating dry solidification process due to the repulsive interaction between same sex ion, coatingsurface can form very small, the densely covered uniform capillary micropore that naked eyes cannot be seen, these micropores form the passage of water, gas discrepancy, coating is possessed when extraneous atmospheric moisture is large, suck water, gas, and when in coating, water content is greater than ambient air humidity, unnecessary moisture in coating can be discharged to atmospheric environment automatically, makes coating possess this permanent automatic balance function.
Because its refractive index of white pigment titanium dioxide in coating is 2.7, ultraviolet ray is had to stronger reflection potential, so the ultra-violet radiation resisting performance of coating strengthens greatly, use useful life greatly to extend.
Safety and environmental protection of the present invention, protection against the tide, antisweat, anti-freeze, mildew-resistant, absorption peculiar smell purifies the air of a room, the market price of its solid phase prod with low cost is 20 yuan/kg, without any peculiar smell, non-combustible, the buildings internal surface dress that can be applicable to all trades and professions and household is coated with, and prevents building surface dewfall, causes and drips, drops down water, and big area mould grows and stretches, even burst apart, cause top layer slump, ensured the healthy and safe of the normal of production and people's life.
Embodiment
Embodiment 1:
A coating, the raw material of employing following weight parts: 30 parts of white cements, 24 parts of titanium dioxides, 20 parts of activated Calcium carbonates, 15 parts, white quartz powder, 3 parts of particulate silicic acid, 1 part, calcium chloride, 0.5 part of cuprous chloride, 1.5 parts, diatom powder, 2 parts of wilkinites, 3 parts of polyacrylamides.
Described calcium chloride is food-grade calcium chloride.
Described white cement is 325#.
Described titanium dioxide is rutile-type.
The invention has the beneficial effects as follows: owing to containing a certain proportion of several strong hygroscopic material composition calcium chloride, diatom powder, wilkinite, activated Calcium carbonate in product, coating has excellent moistureproof antisweat performance, is one of main characteristic of product.Test and show when coat-thickness reaches 3mm, every square metre of water-retaining capacity can reach 1.5 kg.
In product proportioning, contain appropriate frostproofer calcium chloride, after coating water suction, can effectively resist-30 ℃ of low temperature, make water suction in coating not produce the destruction that the crystallization of freezing causes expansion stress.
In coating, contained hygroscopic material calcium chloride is in when water suction, the thermopositive reaction that can produce, and its instantaneous temperature can reach 50 ℃ of left and right, and discharges that can evaporate the water during heat absorption just fundamentally stoped the icing possibility of aqueous vapor dewfall.
In product, be added with a certain amount of disinfectant cuprous chloride, effectively mould fungus inhibition grows and stretches.
In product ingredient particles silicic acid, contain abundant hydroxyl OH-and abundant negative oxygen ion 0-is contained on diatom powder surface, coating has the various gas with foreign flavor molecules of absorption, and carries out with it the effect of ion-exchange chemical reaction, mainly generates CO
2and H
2the performance that O discharges, has outstanding environment-friendly function.
Existence due to contained above-mentioned activeconstituents in coating, in coating dry solidification process due to the repulsive interaction between same sex ion, coatingsurface can form very small, the densely covered uniform capillary micropore that naked eyes cannot be seen, these micropores form the passage of water, gas discrepancy, coating is possessed when extraneous atmospheric moisture is large, suck water, gas, and when in coating, water content is greater than ambient air humidity, unnecessary moisture in coating can be discharged to atmospheric environment automatically, makes coating possess this permanent automatic balance function.
Because its refractive index of white pigment titanium dioxide in coating is 2.7, ultraviolet ray is had to stronger reflection potential, so the ultra-violet radiation resisting performance of coating strengthens greatly, use useful life greatly to extend.
Safety and environmental protection of the present invention, protection against the tide, antisweat, anti-freeze, mildew-resistant, absorption peculiar smell purifies the air of a room, the market price of its solid phase prod with low cost is 20 yuan/kg, without any peculiar smell, non-combustible, the buildings internal surface dress that can be applicable to all trades and professions and household is coated with, and prevents building surface dewfall, causes and drips, drops down water, and big area mould grows and stretches, even burst apart, cause top layer slump, ensured the healthy and safe of the normal of production and people's life.
Embodiment 2:
A coating, contains following component: 25 parts of white cements, 25 parts of titanium dioxides, 22 parts of activated Calcium carbonates, 15 parts, white quartz powder, 3.5 parts of particulate silicic acid, 1 part, calcium chloride, 0.5 part of cuprous chloride, 2.5 parts, diatom powder, 2.5 parts of wilkinites, 3 parts of polyacrylamides in every 100 weight part coating.
Described calcium chloride is food-grade calcium chloride.
Described white cement is 325#.
Described titanium dioxide is rutile-type.
The invention has the beneficial effects as follows: owing to containing a certain proportion of several strong hygroscopic material composition calcium chloride, diatom powder, wilkinite, activated Calcium carbonate in product, coating has excellent moistureproof antisweat performance, is one of main characteristic of product.Test and show when coat-thickness reaches 3mm, every square metre of water-retaining capacity can reach 1.5 kg.
In product proportioning, contain appropriate frostproofer calcium chloride, after coating water suction, can effectively resist-30 ℃ of low temperature, make water suction in coating not produce the destruction that the crystallization of freezing causes expansion stress.
In coating, contained hygroscopic material calcium chloride is in when water suction, the thermopositive reaction that can produce, and its instantaneous temperature can reach 50 ℃ of left and right, and discharges that can evaporate the water during heat absorption just fundamentally stoped the icing possibility of aqueous vapor dewfall.
In product, be added with a certain amount of sanitas calcium chloride and disinfectant cuprous chloride, effectively mould fungus inhibition grows and stretches.
In product ingredient particles silicic acid, contain abundant hydroxyl OH-and abundant negative oxygen ion 0-is contained on diatom powder surface, coating has the various gas with foreign flavor molecules of absorption, and carries out with it the effect of ion-exchange chemical reaction, mainly generates CO
2and H
2the performance that O discharges, has outstanding environment-friendly function.
Existence due to contained above-mentioned activeconstituents in coating, in coating dry solidification process due to the repulsive interaction between same sex ion, coatingsurface can form very small, the densely covered uniform capillary micropore that naked eyes cannot be seen, these micropores form the passage of water, gas discrepancy, coating is possessed when extraneous atmospheric moisture is large, suck water, gas, and when in coating, water content is greater than ambient air humidity, unnecessary moisture in coating can be discharged to atmospheric environment automatically, makes coating possess this permanent automatic balance function.
Because its refractive index of white pigment titanium dioxide in coating is 2.7, ultraviolet ray is had to stronger reflection potential, so the ultra-violet radiation resisting performance of coating strengthens greatly, use useful life greatly to extend.
Safety and environmental protection of the present invention, protection against the tide, antisweat, anti-freeze, mildew-resistant, absorption peculiar smell purifies the air of a room, the market price of its solid phase prod with low cost is 20 yuan/kg, without any peculiar smell, non-combustible, the buildings internal surface dress that can be applicable to all trades and professions and household is coated with, and prevents building surface dewfall, causes and drips, drops down water, and big area mould grows and stretches, even burst apart, cause top layer slump, ensured the healthy and safe of the normal of production and people's life.
Embodiment 3:
A coating, contains following component: 29 parts of white cements, 23 parts of titanium dioxides, 21 parts of activated Calcium carbonates, 15 parts, white quartz powder, 2.75 parts of particulate silicic acid, 1.25 parts, calcium chloride, 0.75 part of cuprous chloride, 2 parts, diatom powder, 1.75 parts of wilkinites, 3.5 parts of polyacrylamides in every 100 weight part coating.
Described calcium chloride is food-grade calcium chloride.
Described white cement is 325#.
Described titanium dioxide is rutile-type.
The invention has the beneficial effects as follows: owing to containing a certain proportion of several strong hygroscopic material composition calcium chloride, diatom powder, wilkinite, activated Calcium carbonate in product, coating has excellent moistureproof antisweat performance, is one of main characteristic of product.Test and show when coat-thickness reaches 3mm, every square metre of water-retaining capacity can reach 1.5 kg.
In product proportioning, contain appropriate frostproofer calcium chloride, after coating water suction, can effectively resist-30 ℃ of low temperature, make water suction in coating not produce the destruction that the crystallization of freezing causes expansion stress.
In coating, contained hygroscopic material calcium chloride is in when water suction, the thermopositive reaction that can produce, and its instantaneous temperature can reach 50 ℃ of left and right, and discharges that can evaporate the water during heat absorption just fundamentally stoped the icing possibility of aqueous vapor dewfall.
In product, be added with a certain amount of sanitas calcium chloride and disinfectant cuprous chloride, effectively mould fungus inhibition grows and stretches.
In product ingredient particles silicic acid, contain abundant hydroxyl OH-and abundant negative oxygen ion 0-is contained on diatom powder surface, coating has the various gas with foreign flavor molecules of absorption, and carries out with it the effect of ion-exchange chemical reaction, mainly generates CO
2and H
2the performance that O discharges, has outstanding environment-friendly function.
Existence due to contained above-mentioned activeconstituents in coating, in coating dry solidification process due to the repulsive interaction between same sex ion, coatingsurface can form very small, the densely covered uniform capillary micropore that naked eyes cannot be seen, these micropores form the passage of water, gas discrepancy, coating is possessed when extraneous atmospheric moisture is large, suck water, gas, and when in coating, water content is greater than ambient air humidity, unnecessary moisture in coating can be discharged to atmospheric environment automatically, makes coating possess this permanent automatic balance function.
Because its refractive index of white pigment titanium dioxide in coating is 2.7, ultraviolet ray is had to stronger reflection potential, so the ultra-violet radiation resisting performance of coating strengthens greatly, use useful life greatly to extend.Safety and environmental protection of the present invention, protection against the tide, antisweat, anti-freeze, mildew-resistant, absorption peculiar smell purifies the air of a room, the market price of its solid phase prod with low cost is 20 yuan/kg, without any peculiar smell, non-combustible, the buildings internal surface dress that can be applicable to all trades and professions and household is coated with, and prevents building surface dewfall, causes and drips, drops down water, and big area mould grows and stretches, even burst apart, cause top layer slump, ensured the healthy and safe of the normal of production and people's life.
Claims (1)
1. a coating, is characterized in that: in every 100 weight part coating, contain following component: 25～30 parts of white cements, 20～25 parts of titanium dioxides, 18～22 parts of activated Calcium carbonates, 15 parts, white quartz powder, 2.5～3.5 parts of particulate silicic acid, 1～1.5 part, calcium chloride, 0.5～1 part of cuprous chloride, 1.5～2.5 parts, diatom powder, 1.5～2.5 parts of wilkinites, 3～4 parts of polyacrylamides.
2. a kind of coating as claimed in claim 1, is characterized in that: described calcium chloride is food-grade calcium chloride.
3. a kind of coating as claimed in claim 1, is characterized in that: described white cement is 325# white cement.
4. a kind of coating as claimed in claim 1, is characterized in that: described titanium dioxide is Rutile type Titanium Dioxide.