CN103074728A - Preparation method of knitted collar-sleeve material - Google Patents

Abstract

A preparation method of knitted collar-sleeve material comprises the following steps of step 1, adopting a flat knitting machine to weave the following materials by weight percent into fabric: 5 percent of 70D spandex, 80 percent of 100D Dacron and 15 percent of 75D Dacron; step 2, placing the woven fabric into a post-treatment pond to be soaked for 5min under the temperature of 45 DEG C, wherein the post-treatment pond comprises the following assistants: smoothing agent accounting for 2.5 to 3.5 percent of total weight of water in the post-treatment pond and loosening agent accounting for 1.5 to 2.5 percent of the total weight of the water in the post-treatment pond; the smoothing agent comprises the following ingredients in parts by weight: 25 parts of segmental silicon oil, 10 parts of polyether and 20 parts of nonionic surface active agent; the loosening agent comprises the following ingredients in parts by weight: 10 parts of emulsifier, 40 parts of polyurethane and 5 parts of permeable paste; and step 3, utilizing vapor to softly iron the well-soaked fabric, and completing the treatment step. The knitted collar-sleeve material prepared by the method is excellent in wash-and-wear effect, crease-resistant effect and warp-resistant effect.

Description

A kind of knitting leader's material preparation method

Technical field

The present invention relates to the knitting leader's material preparation method for the manufacture of neckline, cuff.

Background technology

In the prior art, producing non-ironing, crease-resistant, the anti-leader's product that sticks up mainly relies on and crease-resistant, anti-ly sticks up finishing auxiliaries and realize, and these auxiliary agents are only applicable to the cloth of single material, can not make the product of composite reach non-ironing, crease-resistant, anti-effect of sticking up, how to make leader's product of composite reach non-ironing, crease-resistant, anti-effect of sticking up is the target that the dealer pursues always.

Summary of the invention

Leader's product that main purpose of the present invention is to overcome composite in the prior art can't reach non-ironing, crease-resistant, anti-shortcoming of sticking up effect, and a kind of non-ironing, crease-resistant, anti-knitting leader's material preparation method of sticking up effect that has is provided.

In order to reach goal of the invention of the present invention, the applicant organizes the Corporation R ﹠ D personnel, and invite the scholar of colleges and universities to carry out a large amount of theory analysises and test, discovery will make leader's product of composite reach non-ironing, crease-resistant, the anti-effect of sticking up, not only relevant with auxiliary component, also relevant with compound raw material and the postfinishing process of leader's product, for this reason, raw material composition, auxiliary agent are formed the applicant and postfinishing process is studied simultaneously, test through a large amount of finally obtains following technical scheme:

A kind of knitting leader's material preparation method comprises the steps:

Step 1 adopts straight-bar machines to be woven into cloth the material of following percentage by weight: 70D spandex 5%, 100D terylene 80% and 75D terylene 15%;

Step 2, the cloth that is woven into is put into rear arrangement pond to be soaked, temperature 45 C, the time is 5min, contains following auxiliary agent in the arrangement pond after this: the leavening agent that accounts for the smooth agent of water gross weight 2.5-3.5% in the rear arrangement pond and account for water gross weight 1.5-2.5% in the rear arrangement pond; The composition that contains following parts by weight in this smooth agent: 20 parts of 25 parts of section property silicone oil, 10 parts of polyethers and non-ionic surface active agents; The composition that contains following parts by weight in this leavening agent: 5 parts of 10 parts of emulsifying agents, 40 parts of polyurethane and infiltration emulsifiable pastes; Push after the immersion, dry;

Step 3, the cloth that immersion is finished are carried out setting machine and are carried out soft boiling hot, the extrusion process of water vapour, and soft boiling hot temperature 140-150 ℃, extruding air pressure 5.8-6.2 pound is finished arranging process.

Compared with prior art, the knitting leader's material that adopts said method to prepare, confirm through test, has good non-ironing, crease-resistant, the anti-effect of sticking up, realize non-ironing, crease-resistant, the anti-target of sticking up effect of the long-term leader's product that makes composite of pursuing of dealer, had immeasurable economic and social benefit.

The specific embodiment

A kind of knitting leader's material preparation method comprises the steps:

Step 1 adopts straight-bar machines to be woven into cloth the material of following percentage by weight: 70D spandex 5%, 100D terylene 80% and 75D terylene 15%;

Step 2 is put into rear arrangement pond with the cloth that is woven into and is soaked, temperature 45 C, and the time is 5min, contains following auxiliary agent in the arrangement pond after this: the leavening agent that accounts for the smooth agent of water gross weight 3.0% in the rear arrangement pond and account for water gross weight 2.0% in the rear arrangement pond; The composition that contains following parts by weight in this smooth agent: 20 parts of 25 parts of section property silicone oil, 10 parts of polyethers and non-ionic surface active agents; The composition that contains following parts by weight in this leavening agent: 5 parts of 10 parts of emulsifying agents, 40 parts of polyurethane and infiltration emulsifiable pastes; Push after the immersion, dry;

Step 3, the cloth that immersion is finished are carried out setting machine and are carried out soft boiling hot, the extrusion process of water vapour, 145 ℃ of soft boiling hot temperature, and 6 pounds of extruding air pressure are finished arranging process.

The knitting leader's material that makes is delivered to national textile garment product quality supervision and inspection centers (Fujian), detects data such as following table:

Above-mentioned only is the specific embodiment of the present invention, but design concept of the present invention is not limited to this, allly utilizes this design that the present invention is carried out the change of unsubstantiality, all should belong to the behavior of invading protection domain of the present invention.

Claims (1)

1. knitting leader's material preparation method is characterized in that: comprise the steps:

Step 1 adopts straight-bar machines to be woven into cloth the material of following percentage by weight: 70D spandex 5%, 100D terylene 80% and 75D terylene 15%;

Step 2, the cloth that is woven into is put into rear arrangement pond to be soaked, temperature 45 C, the time is 5min, contains following auxiliary agent in the arrangement pond after this: the leavening agent that accounts for the smooth agent of water gross weight 2.5-3.5% in the rear arrangement pond and account for water gross weight 1.5-2.5% in the rear arrangement pond; The composition that contains following parts by weight in this smooth agent: 20 parts of 25 parts of section property silicone oil, 10 parts of polyethers and non-ionic surface active agents; The composition that contains following parts by weight in this leavening agent: 5 parts of 10 parts of emulsifying agents, 40 parts of polyurethane and infiltration emulsifiable pastes; Push after the immersion, dry;

Step 3, the cloth that immersion is finished are carried out setting machine and are carried out soft boiling hot, the extrusion process of water vapour, and soft boiling hot temperature 140-150 ℃, extruding air pressure 5.8-6.2 pound is finished arranging process.