CN103467811A - Light polyethylene pipe for building water supply - Google Patents
Light polyethylene pipe for building water supply Download PDFInfo
- Publication number
- CN103467811A CN103467811A CN2013103595885A CN201310359588A CN103467811A CN 103467811 A CN103467811 A CN 103467811A CN 2013103595885 A CN2013103595885 A CN 2013103595885A CN 201310359588 A CN201310359588 A CN 201310359588A CN 103467811 A CN103467811 A CN 103467811A
- Authority
- CN
- China
- Prior art keywords
- water supply
- minute
- building water
- cooled
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light polyethylene pipe for building water supply. The light polyethylene pipe is composed of the following raw materials in parts by weight: 100-103 of high density polyethylene, 4-5 of light calcium carbonate, 2-3 of diatomite, 1-2 of nano aluminous soil, 1-2 of alum powder, 0.1-0.2 of 3-(methacryloyloxy) propyl trimethoxysilane, 1-2 of ethylene bisstearamide, 1-2 of polybutyl acrylate, 0.2-0.3 of magnesium stearate, and 3-4 of a modifying assistant. The raw materials of the light polyethylene pipe are safe and non-toxic, the obtained product has relatively light weight, high surface resistance, strong corrosion resistance and strong aging resistance, and the added modifying assistant further improves the comprehensive quality of the product.
Description
Technical field
The present invention relates generally to a kind of PE water service pipe, belongs to the tubing field.
Background technology
The PE(polyethylene) material, due to characteristics such as its intensity are high, high temperature resistant, anticorrosive, nontoxic, is widely used in water service pipe and manufactures field.Because it can not get rusty, so, be the desirable tubing that substitutes common iron water service pipe; Polyethylene is the inertialess material, except a small amount of strong oxidizer, can corrode by the medicine of anti-the number of chemical, and is difficult for breed bacteria.Well-known steel pipe, cast iron pipe are not only by the reason that plastics tubing replaced because plastic pipe is low than its water delivery energy consumption, the life energy consumption is low, lightweight, flow resistance is little, simple installation is rapid, cost is low, the life-span is long, have heat insulation function etc., go back corrosion-resistant because of plastics tubing, be difficult for growing the performance such as microorganism and be better than steel pipe and cast iron pipe.
Expansion gradually along with urban construction, the PE water service pipe also will be used to rugged environment more, the chemical substance burn into persistence high pressure such as the high low temperature of persistence, soda acid etc., therefore further improve the performance of conventional P E water service pipe, improve product quality, for China's modernization construction, good promoter action is arranged.
Summary of the invention
The object of the invention just is to provide a kind of PE water service pipe.
The present invention is achieved by the following technical solutions:
A kind of building water supply lightweight polyethylene tube, it is comprised of the raw material of following weight parts:
High density polyethylene(HDPE) 100-103, light calcium carbonate 4-5, diatomite 2-3, nano aluminum alumina 1-2, alum powder 1-2,3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane 0.1-0.2, ethylene bis stearamide 1-2, butyl polyacrylate 1-2, Magnesium Stearate 0.2-0.3, modified additive 3-4;
Described modified additive is comprised of the raw material of following weight parts:
Middle low polyethylene 30-40, polyphthalamide 15-20, aluminium nitride 3-4, bentonite-thickened grease 1-2, silane resin acceptor kh-550 1-2, Flos Rosae Rugosae quintessence oil 1-2, calcium peroxide 0.1-0.2;
Polyphthalamide is heated to 120-130 ℃, adds aluminium nitride, insulated and stirred 10-15 minute, be cooled to normal temperature, obtains Preblend; Polyethylene is mixed with calcium peroxide, silane resin acceptor kh-550, mix with above-mentioned Preblend after 50-60 ℃ of lower constant temperature stirs 20-30 minute, is cooled to normal temperature, 400-500 rev/min of dispersed with stirring 3-5 minute, add each raw material of residue, and post-drying stirs, granulation, particle diameter is 2-4mm.
The preparation method of lightweight polyethylene tube for a kind of building water supply comprises the following steps:
Above-mentioned light calcium carbonate, diatomite, nano aluminum alumina, alum powder are mixed, at 100-120 ℃ of lower stirring reaction 10-20 minute, the reduction temperature is 50-60 ℃, add 3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane, 400-500 rev/min of dispersed with stirring 6-7 minute, be cooled to normal temperature, with each raw material of residue, mix, send into kneader, under 70-80 ℃, mediated, discharging is cooled to normal temperature, joins parallel co-rotating twin screw extruder and is extruded, in die for molding, obtain described building water supply lightweight polyethylene tube.
Advantage of the present invention is:
Materials safety of the present invention is nontoxic, the relative light weight of the product obtained, and surperficial resistance is high, and erosion resistance, ageing resistance are strong, and the modified additive added has further improved the integrated quality of product.
Embodiment
Embodiment 1
A kind of building water supply lightweight polyethylene tube, it is comprised of the raw material of following weight parts:
High density polyethylene(HDPE) 5000S 103, light calcium carbonate 5, diatomite 2, nano aluminum alumina 2, alum powder 2,3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane 0.2, ethylene bis stearamide 1, butyl polyacrylate 1, Magnesium Stearate 0.3, modified additive 4;
Described modified additive is comprised of the raw material of following weight parts:
Middle low polyethylene 40, polyphthalamide 20, aluminium nitride 4, bentonite-thickened grease 2, silane resin acceptor kh-550 1, Flos Rosae Rugosae quintessence oil 1, calcium peroxide 0.2;
Polyphthalamide is heated to 130 ℃, adds aluminium nitride, insulated and stirred 15 minutes, be cooled to normal temperature, obtains Preblend; Polyethylene is mixed with calcium peroxide, silane resin acceptor kh-550, mix with above-mentioned Preblend after 60 ℃ of lower constant temperature stir 20 minutes, are cooled to normal temperature, 500 rev/mins of dispersed with stirring 3-5 minute, add each raw material of residue, and post-drying stirs, granulation, particle diameter is 4mm.
The preparation method of lightweight polyethylene tube for a kind of building water supply comprises the following steps:
Above-mentioned light calcium carbonate, diatomite, nano aluminum alumina, alum powder are mixed, 120 ℃ of lower stirring reactions 20 minutes, reducing temperature is 60 ℃, add 3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane, 500 rev/mins of dispersed with stirring 7 minutes, be cooled to normal temperature, with each raw material of residue, mix, send into kneader, under 80 ℃, mediated, discharging is cooled to normal temperature, joins parallel co-rotating twin screw extruder and is extruded, in die for molding, obtain described building water supply lightweight polyethylene tube.
Performance test:
Hydro-test (80 ℃, 5.5MPa): 168 hours, without brittle rupture;
Vertical relaxation shrinkage (110 ℃): 1.05%;
Elongation at break: 603%;
Body tensile yield strength: 25.8MPa;
Flexural strength: 34.9PMPa.
Claims (2)
1. a building water supply lightweight polyethylene tube is characterized in that what it was comprised of the raw material of following weight parts:
High density polyethylene(HDPE) 100-103, light calcium carbonate 4-5, diatomite 2-3, nano aluminum alumina 1-2, alum powder 1-2,3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane 0.1-0.2, ethylene bis stearamide 1-2, butyl polyacrylate 1-2, Magnesium Stearate 0.2-0.3, modified additive 3-4;
Described modified additive is comprised of the raw material of following weight parts:
Middle low polyethylene 30-40, polyphthalamide 15-20, aluminium nitride 3-4, bentonite-thickened grease 1-2, silane resin acceptor kh-550 1-2, Flos Rosae Rugosae quintessence oil 1-2, calcium peroxide 0.1-0.2;
Polyphthalamide is heated to 120-130 ℃, adds aluminium nitride, insulated and stirred 10-15 minute, be cooled to normal temperature, obtains Preblend; Polyethylene is mixed with calcium peroxide, silane resin acceptor kh-550, mix with above-mentioned Preblend after 50-60 ℃ of lower constant temperature stirs 20-30 minute, is cooled to normal temperature, 400-500 rev/min of dispersed with stirring 3-5 minute, add each raw material of residue, and post-drying stirs, granulation, particle diameter is 2-4mm.
2. the preparation method of lightweight polyethylene tube for a building water supply as claimed in claim 1 is characterized in that comprising the following steps:
Above-mentioned light calcium carbonate, diatomite, nano aluminum alumina, alum powder are mixed, at 100-120 ℃ of lower stirring reaction 10-20 minute, the reduction temperature is 50-60 ℃, add 3-(iso-butylene acyl-oxygen) propyl trimethoxy silicane, 400-500 rev/min of dispersed with stirring 6-7 minute, be cooled to normal temperature, with each raw material of residue, mix, send into kneader, under 70-80 ℃, mediated, discharging is cooled to normal temperature, joins parallel co-rotating twin screw extruder and is extruded, in die for molding, obtain described building water supply lightweight polyethylene tube.