CN103773180A - Wear-resistant heat-resistant scratch-resistant mouse shell coating - Google Patents
Wear-resistant heat-resistant scratch-resistant mouse shell coating Download PDFInfo
- Publication number
- CN103773180A CN103773180A CN201410024662.2A CN201410024662A CN103773180A CN 103773180 A CN103773180 A CN 103773180A CN 201410024662 A CN201410024662 A CN 201410024662A CN 103773180 A CN103773180 A CN 103773180A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- wear
- scratch
- scratch resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a wear-resistant heat-resistant scratch-resistant mouse shell coating which is prepared from the following raw materials in parts by mass: 90-100 parts of epoxy resin, 12-15 parts of polyester resin, 5-8 parts of polytetrafluoroethylene powder, 8-10 parts of acetyl tributyl citrate, 1-4 parts of glass fiber, 28-30 parts of titanium dioxide, 2-5 parts of simethicone, 10-13 parts of ammonium dihydrogen phosphate and 150-170 parts of ethylene glycol. The wear-resistant heat-resistant scratch-resistant mouse shell coating is reasonable in formula; according to co-action of the components, the finished product has high wear and scratch resistance, the wear resistance is 0.5mg/1000 passes, the heat resistance is high, the finished product is coated on the surface of a mouse shell, the thickness of the dry film is 10mu m, the duration is 2 hours at the temperature of 500 DEG C, and the shell is not changed.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of antiwear heat resisting scratch resistance mouse case coating.
Background technology
Along with the development of information technology, computer becomes the requisite office accommodations in office space, and mouse has played vital effect in the use procedure of computer.Existing general mouse case mostly is plastic material; its surface-coated has one deck supercoat; if but in hot environment as in the time that be placed in heat-insulating mouse mat in by mouse winter; mouse case yielding and cause mouse damage; and existing mouse case coating abrasion performance is poor, use for some time rear surface coating to there will be cut even to drop.
In sum, how to overcome the deficiencies in the prior art and become existing field problem demanding prompt solution.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art and propose a kind of antiwear heat resisting scratch resistance mouse case coating, the present invention has good thermotolerance and wear-resistant scratch-resistant.
Technical scheme of the present invention is as follows:
Antiwear heat resisting scratch resistance mouse case coating, comprises the following raw material according to mass fraction meter: epoxy resin 90-100 part, vibrin 12-15 part, tetrafluoroethylene powder 5-8 part, tributyl acetylcitrate 8-10 part, glass fibre 1-4 part, titanium dioxide 28-30 part, dimethyl silicone oil 2-5 part, primary ammonium phosphate 10-13 part, ethylene glycol 150-170 part.
Described antiwear heat resisting scratch resistance mouse case coating, comprises the following raw material according to mass fraction meter: 98 parts of epoxy resin, 13 parts, vibrin, 7 parts of tetrafluoroethylene powders, 9 parts of tributyl acetylcitrates, 2 parts, glass fibre, 29 parts of titanium dioxides, 4 parts of dimethyl silicone oils, 12 parts of primary ammonium phosphates, 160 parts of ethylene glycol.
Described antiwear heat resisting scratch resistance mouse case coating, the particle diameter≤5 μ m of wherein said tetrafluoroethylene powder.
Preparation method of the present invention: according to quality proportioning, each raw material is stirred in high mixer under 200r/min to 40min and obtain finished product of the present invention.
beneficial effect:the present invention fills a prescription rationally, makes finished product of the present invention have good wear-resistant scratch-resistant under the acting in conjunction of each component, and wear-resisting amount is 0.5mg/1000 time, thermotolerance is good, and finished product of the present invention is coated on to mouse case surface, build 10 μ m, at 500 ℃, continue 2h, shell is unchanged.
Embodiment
Ptfe micropowder of the present invention is purchased from the sky, Shenyang City auspicious micropowder material factory, particle diameter≤5 μ m; Described vibrin is purchased from Bao Tian type material Science and Technology Ltd. of Zhangjagang City.
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Antiwear heat resisting scratch resistance mouse case coating, comprises the following raw material according to mass fraction meter: 90 parts of epoxy resin, 12 parts, vibrin, 5 parts of tetrafluoroethylene powders, 8 parts of tributyl acetylcitrates, 1 part, glass fibre, 28 parts of titanium dioxides, 2 parts of dimethyl silicone oils, 10 parts of primary ammonium phosphates, 150 parts of ethylene glycol.
According to quality proportioning, each raw material is stirred to 40min in high mixer under 200r/min and get product.This finished product is carried out to Performance Detection, and detected result is in table 1.
Embodiment 2
Antiwear heat resisting scratch resistance mouse case coating, comprises the following raw material according to mass fraction meter: 100 parts of epoxy resin, 15 parts, vibrin, 8 parts of tetrafluoroethylene powders, 10 parts of tributyl acetylcitrates, 4 parts, glass fibre, 30 parts of titanium dioxides, 5 parts of dimethyl silicone oils, 13 parts of primary ammonium phosphates, 170 parts of ethylene glycol.
The present embodiment preparation method, with embodiment 1, carries out Performance Detection by this finished product, and detected result is in table 1.
Embodiment 3
Antiwear heat resisting scratch resistance mouse case coating, comprises the following raw material according to mass fraction meter: 98 parts of epoxy resin, 13 parts, vibrin, 7 parts of tetrafluoroethylene powders, 9 parts of tributyl acetylcitrates, 2 parts, glass fibre, 29 parts of titanium dioxides, 4 parts of dimethyl silicone oils, 12 parts of primary ammonium phosphates, 160 parts of ethylene glycol.
The present embodiment preparation method, with embodiment 1, carries out Performance Detection by this finished product, and detected result is in table 1.
Embodiment 1-3 gained finished product is coated on to mouse case, and build 10 μ m, carry out scratch-resistant wear resisting property test to coating, the results are shown in Table 1:
Table 1 performance test data
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Wear-resisting amount, mg/1000 time | 0.6 | 0.5 | 0.5 |
| Heat-resisting, 500 ℃ of lasting 2h | Unchanged | Unchanged | Unchanged |
As seen from the above table, the present composition has good wear resistance and thermotolerance.
Above-described embodiment is only the explanation to product of the present invention; not the present invention is made to any pro forma restriction; within not departing from technical scheme scope of the present invention, any equivalent that utilizes the technology contents of above-mentioned announcement to make simple transformation, all belongs to protection scope of the present invention.
Claims (3)
1. antiwear heat resisting scratch resistance mouse case coating, it is characterized in that, comprise the following raw material according to mass fraction meter: epoxy resin 90-100 part, vibrin 12-15 part, tetrafluoroethylene powder 5-8 part, tributyl acetylcitrate 8-10 part, glass fibre 1-4 part, titanium dioxide 28-30 part, dimethyl silicone oil 2-5 part, primary ammonium phosphate 10-13 part, ethylene glycol 150-170 part.
2. antiwear heat resisting scratch resistance mouse case coating according to claim 1, it is characterized in that, comprise the following raw material according to mass fraction meter: 98 parts of epoxy resin, 13 parts, vibrin, 7 parts of tetrafluoroethylene powders, 9 parts of tributyl acetylcitrates, 2 parts, glass fibre, 29 parts of titanium dioxides, 4 parts of dimethyl silicone oils, 12 parts of primary ammonium phosphates, 160 parts of ethylene glycol.
3. antiwear heat resisting scratch resistance mouse case coating according to claim 1 and 2, is characterized in that, the particle diameter≤5 μ m of described tetrafluoroethylene powder.