CN105236917A - Novel durable waterproofing agent - Google Patents

Novel durable waterproofing agent Download PDF

Info

Publication number
CN105236917A
CN105236917A CN201510598056.6A CN201510598056A CN105236917A CN 105236917 A CN105236917 A CN 105236917A CN 201510598056 A CN201510598056 A CN 201510598056A CN 105236917 A CN105236917 A CN 105236917A
Authority
CN
China
Prior art keywords
parts
water
concrete
resisting agent
novel durable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510598056.6A
Other languages
Chinese (zh)
Inventor
黄志强
王继发
刘泓铭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEXIN WATERPROOF AND DECORATION MATERIAL Co Ltd
Original Assignee
HEXIN WATERPROOF AND DECORATION MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEXIN WATERPROOF AND DECORATION MATERIAL Co Ltd filed Critical HEXIN WATERPROOF AND DECORATION MATERIAL Co Ltd
Priority to CN201510598056.6A priority Critical patent/CN105236917A/en
Publication of CN105236917A publication Critical patent/CN105236917A/en
Pending legal-status Critical Current

Abstract

The invention discloses a novel durable waterproofing agent. The waterproofing agent is prepared from, by weight, 450-500 parts of sodium silicate, 2-4 parts of potassium dichromate, 1-5 parts of copper sulfate, 2-9 parts of zinc stearate, 2-9 parts of calcium stearate, 30-35 parts of diatomite, 2-4 parts of aluminum powder, 1-3 parts of polyaluminum ferric chloride, 2-4 parts of talcum powder, 1-4 parts of triisopropanolamine, 1-7 parts of sodium citrate and 300-350 parts of water. The waterproofing agent disclosed in the invention has the advantages of large penetration depth and good durability, and can be used in waterproofing of roofs, basements and toilets.

Description

A kind of Novel durable water-resisting agent
Technical field
The present invention relates to a kind of Novel durable water-resisting agent, belong to concrete construction water-proof material technical field.
Background technology
Concrete structure refers to the structure of concrete for main making.It mainly comprises plain concrete structure, skeleton construction and prestressed concrete structure etc.Wherein, skeleton construction all be it is believed that all the time is concrete structure the firmest, durable.Although reinforcing bar and concrete are the materials that two kinds of physical and mechanical properties are not identical, between them, there is very strong cohesive force, them can be made effectively to combine cooperation.In addition, concrete can also form the protective layer of reinforcing bar, thus makes reinforcing bar not by corrosion, and then improves Steel Concrete performance.Therefore, the use of people to skeleton construction gives very high expectation, and have ignored its endurance issues at leisure.
Concrete durability refers to that the effect of various destructive factor resisted under active usage conditions by concrete, the long-term ability keeping intensity and complete appearance.But the index of general evaluation concrete durability has impermeability, splitting resistance, frost resistance, resisting carbonization, acid-fast alkali-proof, resistivity against fire, wear resistance, abrasion resistance, alkali-aggregate reaction etc.Although the mechanism of action of these indexs is different and very complicated, their common ground are: all relevant to the complexity that water or gas transmit to inside concrete, are namely relevant to concrete perviousness.Such as, concrete carbonization is mainly due to CO 2gas penetrate into inside concrete and with Ca (OH) wherein 2or caused by the reaction of the hydrolysis product of cement such as hydrated calcium silicate; Mainly because water, sour gas etc. penetrate into, inside concrete causes acid erosion; Steel bar corrosion is because carbonic acid gas, water, oxygen and chlorion etc. penetrate into the reinforcement cover that concrete formed, and destroys caused by passive film; Concrete freeze-thaw damage causes owing to infiltrating concrete water icing frost heave under the condition of low temperature.Therefore, the key that solves the problem forms protective layer at concrete surface, blocking concrete inner capillary tube hole, and anti-sealing or gas etc. penetrate into inside concrete, improve concrete durability, thus extend concrete work-ing life.
At present, domestic permeable waterproof agent is of a great variety, but can be divided into inorganic infiltration water-resisting agent and the large class of organic infiltration water-resisting agent two by its chemical composition.Inorganic infiltration water-resisting agent, generally referring to by water glass is main carriers, and the semi-transparent clear liquid that is composited of appropriate catalyzer, dispersion agent, auxiliary agent and water etc. in addition, there is higher permeability, direct spraying is in the concrete surface needing waterproof, inside can be infiltrated rapidly, and with hydrolysis product of cement Ca (OH) 2react, generate water insoluble and there is the silicate of some strength, thus blocking internal void, close capillary porosity duct, improve concrete impermeability.Organic infiltration water-resisting agent, generally refer to organosilicon or non-organic silicon macromolecular compound is the infiltration water-resisting agent that main carriers synthesizes, there is penetrating power to a certain degree, concrete surface layer can be infiltrated, make it that there is hydrophobic nature or filling pore, form closely knit capillary structure, there is good water tolerance simultaneously.But part inorganic infiltration water-resisting agent has higher viscosity, the effect of use is not very desirable; The organic infiltration water-resisting agent of part also has pungent odour, or toxicity, or has higher production cost, and these largely limit its practical application.But basic reason is these infiltration water-resisting agents only to be covered concrete surface and maybe can not infiltrate into enough degree of depth, and waterproofing layer thickness is not enough, easily by water or gas pickling, thus reduces endurance performance of concrete.
Chinese patent literature discloses the curing agent that a kind of name is called " a kind of concrete protective curing agent " (publication number: CN1699290A, publication date: on November 23rd, 2005).It is made up of alkalimetal silicate, organosilane permeate agent, stablizer, wetting dispersing agent, water, and to realize improving concrete surface compactness and hydrophobic nature, and make surface have defencive function as target.Although which employs inorganic silicate primary coat method and organic silicon face coating method, make it have waterproof to a certain degree and care action, but because its main component has more full-bodied silicate, in process of osmosis, silicate not only can have influence on the speed that other moietys penetrate into inside concrete, but also can with concrete generation premature reaction, thus result in depth of penetration and only have 2-5mm, waterproofing layer thickness is not enough, and then affects endurance performance of concrete.Therefore, develop a kind of new Novel durable water-resisting agent and will play very important effect to concrete construction.
Summary of the invention
Too high and cause the depth of penetration of water-resisting agent low for above-mentioned prior art mesosilicic acid salt viscosity, and occur too early fully to react with concrete and affect the technical problem of concrete durability, technical problem to be solved by this invention proposes a kind of depth of penetration greatly, and the Novel durable water-resisting agent that endurance quality is good.
The present invention for the taked technical scheme that solves the problem is:
A kind of Novel durable water-resisting agent, is made up of each component of following weight: water glass 450 ~ 500 parts, potassium bichromate 2 ~ 4 parts, 1 ~ 5 part, copper sulfate, Zinic stearas 2 ~ 9 parts, calcium stearate 2 ~ 9 parts, 30 ~ 35 parts, diatomite, aluminium powder 2 ~ 4 parts, aluminium iron polychloride 1 ~ 3 part, talcum powder 2 ~ 4 parts, tri-isopropanolamine 1 ~ 4 part, Trisodium Citrate 1 ~ 7 part, 300 ~ 350 parts, water.
Its weight is as follows:
Water glass 475 parts, potassium bichromate 3 parts, 3 parts, copper sulfate, Zinic stearas 6 parts, calcium stearate 6 parts, 33 parts, diatomite, aluminium powder 3 parts, aluminium iron polychloride 2 parts, talcum powder 3 parts, tri-isopropanolamine 3 parts, Trisodium Citrate 4 parts, 325 parts, water.
In order to effectively improve the depth of penetration of Novel durable water-resisting agent, water glass modulus of the present invention is 1.2 ~ 1.8.
Preferably, the modulus of described water glass is 1.5.
In order to effectively improve the water resistance of Novel durable water-resisting agent, aluminium powder order number of the present invention is 200 ~ 300.
In the present invention, the hydrated product of water glass and inside concrete reacts, and generates Silica hydrogel, and these Silica hydrogel fill original for inside concrete capillary channel and micro gap get up, thus improve the density of concrete within the scope of depth of penetration.In addition, these Silica hydrogel also have certain constraint ability, can fetter the water being free in inside concrete, thus the impact that minimizing water causes concrete, improve concrete durability, extend concrete life.By adding potassium bichromate and copper sulfate protects Silica hydrogel, making the stable colloidal solutions of its integrated larger particles, being filled in the middle of concrete pore, improving concrete impervious water resistance.
Zinic stearas, calcium stearate have good water resistance and oilness.Because they not only can make the capillary wall in concrete forms water-repellent layer, insoluble substance can also be generated with the compound in concrete, cut off infiltration water route, thus improve concrete water resistance.In addition, their lubrication, can reduce the viscosity of water glass, thus improves the mobility of water-resisting agent moiety, and then improves seepage velocity and the speed of reaction of water-resisting agent.Moreover when concrete runs into acid erosion, Zinic stearas, calcium stearate can act on acid, generate stearic acid.And stearic acid is a kind of good tensio-active agent, the reaction each other of concrete mineral compound can be intensified, thus improve concrete durability.In addition, Zinic stearas also has delayed coagulation to concrete, slow down water glass congealing reaction speed, improves depth of penetration, and then decreases the cracking that the temperature difference brings.But calcium stearate is concrete provides calcium ion, increase calcium ion concn in concrete, thus promote the reaction that in concrete, relevant calcium ion participates in, raising concrete durability.
Diatomaceous main chemical compositions is silicon-dioxide.Silicon-dioxide have high temperature resistant, acidproof, thermal expansivity is low, corrosion resistant characteristic, this is Concrete Structure weather resistance widely.In addition, because the siloxane bond constructional feature of silicon-dioxide makes it have very strong surface tension, a large amount of water moleculess can be adsorbed, improve concrete water-proof performance.Moreover, diatomite or a kind of porous material, there is the features such as porosity is large, absorptivity strong, stable chemical nature, excellent surface adsorption water molecules and ionic nature can be provided for concrete, simultaneously diatomite can also by the material storage of absorption therein, and when concrete lacks water by the substance release that adsorbs out.Because diatomite has this feature, therefore diatomite can increase concrete self water-preserving curing function, reduces the cracking that concrete causes because of lack of water; The material of release can also be utilized to regulate the concentration of water glass simultaneously, reduce its viscosity, improve the mobility of mixture, thus increase the concrete impervious degree of depth, and then improve endurance performance of concrete.
Aluminium powder can be filled in concrete pore on the one hand, improves concrete density, thus improves concrete water-proof performance; On the other hand, aluminium powder can permeate inside concrete together along with water-resisting agent, and be deposited on the lower floor of Silica hydrogel waterproof layer or be suspended in centre, play physical property iris action, the matter that can intercept moisture and have a corrosive goods, through waterproof layer, strengthens water tolerance and the anti-corrosion capability of waterproof layer further.
When aluminium iron polychloride runs into water in concrete, can have an effect with water, generate closely knit alumen ustum, be filled in the concrete voids within the scope of depth of penetration, block water and gas pickling, thus improve concrete durability.
Talcum powder is a kind of good lubricant, serves and accelerates the effect of water-resisting agent each moiety velocity of flow, and then increase depth of penetration scope, improve concrete durability in concrete.
Tri-isopropanolamine plays the effect of catalyzer, can promote that the aquation of the wustite of more difficult aquation and dispersiveness reach the extent of hydration improving cement minerals, thus improve concrete strength.
Trisodium Citrate plays the effect of dispersion agent in water-resisting agent, can accelerate the uniform acceleration of mixture, thus makes mixture and concrete react more abundant, improves concrete performance.In addition, Trisodium Citrate is a kind of weak acid strong alkali salt, has good pH value regulating power, and concrete can be made to meet Service Environment requirement complicated and changeable, improves concrete durability.
Described water-resisting agent is before construction, and reply needs the concrete base layer surface of waterproof to carry out deashing, repairing, levelling, keep basic unit moistening, without open fire.During construction, can adopt spraying, to brush or the mode of roller coat is directly applied to and needs on the basal plane of waterproof, overcoating brush of laying equal stress on is to certain thickness, and maintenance 3 days or more.
The invention has the beneficial effects as follows:
The present invention mainly make use of Zinic stearas, calcium stearate, talcous lubrication, improves the viscosity of water glass, thus improves water-resisting agent depth of penetration, improves endurance performance of concrete.Also utilize Silica hydrogel waterproof layer that water glass formed and the water-repellent layer that Zinic stearas, calcium stearate are formed simultaneously, improve concrete water-proof performance widely.Moreover the present invention also applies the pH value regulating power of diatomaceous porosity characteristic, the iris action of aluminium powder, aluminium iron polychloride and water effect, Trisodium Citrate, improves endurance performance of concrete.Water-resisting agent depth of penetration disclosed in this invention is large, and endurance quality is good, can be applicable to the waterproof of roofing, vault and toilet etc.
Embodiment
Embodiment 1
Present embodiment discloses a kind of Novel durable water-resisting agent, be made up of each component of following weight: water glass 475 parts, potassium bichromate 3 parts, 3 parts, copper sulfate, Zinic stearas 6 parts, calcium stearate 6 parts, 33 parts, diatomite, aluminium powder 3 parts, aluminium iron polychloride 2 parts, talcum powder 3 parts, tri-isopropanolamine 3 parts, Trisodium Citrate 4 parts, 325 parts, water.
Embodiment 2
Present embodiment discloses a kind of Novel durable water-resisting agent, be made up of each component of following weight: water glass 450 parts, potassium bichromate 2 parts, 1 part, copper sulfate, Zinic stearas 2 parts, calcium stearate 2 parts, 35 parts, diatomite, aluminium powder 4 parts, aluminium iron polychloride 3 parts, talcum powder 4 parts, tri-isopropanolamine 4 parts, Trisodium Citrate 1 part, 350 parts, water.
Embodiment 3
Present embodiment discloses a kind of Novel durable water-resisting agent, be made up of each component of following weight: water glass 500 parts, potassium bichromate 4 parts, 5 parts, copper sulfate, Zinic stearas 9 parts, calcium stearate 9 parts, 30 parts, diatomite, aluminium powder 2 parts, aluminium iron polychloride 1 part, talcum powder 2 parts, tri-isopropanolamine 1 part, Trisodium Citrate 7 parts, 300 parts, water.
Embodiment 4
Present embodiment discloses a kind of Novel durable water-resisting agent, be made up of each component of following weight: water glass 460 parts, potassium bichromate 3 parts, 2 parts, copper sulfate, Zinic stearas 5 parts, calcium stearate 5 parts, 34 parts, diatomite, aluminium powder 3 parts, aluminium iron polychloride 3 parts, talcum powder 4 parts, tri-isopropanolamine 2 parts, Trisodium Citrate 3 parts, 340 parts, water.
Embodiment 5
Present embodiment discloses a kind of Novel durable water-resisting agent, be made up of each component of following weight: water glass 490 parts, potassium bichromate 4 parts, 4 parts, copper sulfate, Zinic stearas 7 parts, calcium stearate 7 parts, 31 parts, diatomite, aluminium powder 4 parts, aluminium iron polychloride 2 parts, talcum powder 3 parts, tri-isopropanolamine 3 parts, Trisodium Citrate 5 parts, 310 parts, water.
The water resistance of applicant to Novel durable water-resisting agent is tested, and result is as shown in table 1.
The performance test results of table 1 Novel durable water-resisting agent
Certainly, just the preferred embodiments of the disclosure is described in detail above, not limits practical range of the present invention with this, and all equivalence changes done according to principle of the present invention, structure and structure, all should be covered by protection scope of the present invention.

Claims (5)

1. a Novel durable water-resisting agent, is characterized in that: be made up of each component of following weight: water glass 450 ~ 500 parts, potassium bichromate 2 ~ 4 parts, 1 ~ 5 part, copper sulfate, Zinic stearas 2 ~ 9 parts, calcium stearate 2 ~ 9 parts, 30 ~ 35 parts, diatomite, aluminium powder 2 ~ 4 parts, aluminium iron polychloride 1 ~ 3 part, talcum powder 2 ~ 4 parts, tri-isopropanolamine 1 ~ 4 part, Trisodium Citrate 1 ~ 7 part, 300 ~ 350 parts, water.
2. Novel durable water-resisting agent according to claim 1, is characterized in that: its weight is as follows: water glass 475 parts, potassium bichromate 3 parts, 3 parts, copper sulfate, Zinic stearas 6 parts, calcium stearate 6 parts, 33 parts, diatomite, aluminium powder 3 parts, aluminium iron polychloride 2 parts, talcum powder 3 parts, tri-isopropanolamine 3 parts, Trisodium Citrate 4 parts, 325 parts, water.
3. Novel durable water-resisting agent according to claim 1, is characterized in that: described water glass modulus is 1.2 ~ 1.8.
4. Novel durable water-resisting agent according to claim 3, is characterized in that: described water glass modulus is 1.5.
5. Novel durable water-resisting agent according to claim 1, is characterized in that: described aluminium powder order number is 200 ~ 300.
CN201510598056.6A 2015-09-16 2015-09-16 Novel durable waterproofing agent Pending CN105236917A (en)