CN105542593A - Anti-static corrugated carton - Google Patents
Anti-static corrugated carton Download PDFInfo
- Publication number
- CN105542593A CN105542593A CN201610081337.9A CN201610081337A CN105542593A CN 105542593 A CN105542593 A CN 105542593A CN 201610081337 A CN201610081337 A CN 201610081337A CN 105542593 A CN105542593 A CN 105542593A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- static
- calcium carbonate
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-static corrugated carton which comprises a box body made from a corrugated board, wherein the surface of the corrugated board is coated with a layer of anti-static coating with thickness of 1-3mm; and the anti-static coating is prepared from the following raw materials in parts by weight: 100 parts of waterborne acrylic resin, 35-45 parts of epoxy resin, 20-30 parts of alkyd resin, 1-5 parts of carbon nanotube, 3-9 parts of carbon fiber, 10-15 parts of nano calcium carbonate, 1-2 parts of conductive carbon black, 2-8 parts of conductive graphite, 1-2 parts of antifoaming agent, 0.8-1.5 parts of thickening agent, 0.1-0.3 part of modifier, 0.2-0.5 part of dispersing agent, 1-3 parts of silane coupling agent and 50-80 parts of water. According to the invention, since the anti-static coating is added with the carbon nanotube and carbon fiber, the corrugated carton has high strength, the surface is delicate and smooth, the static effect is greatly reduced, thus the surface of the corrugated carton does not adsorb dust, the scratch caused by friction is reduced, and the printing speed and printing effect are improved; and moreover, due to the addition of nano calcium carbonate, the coating has good gloss, transparency and stability.
Description
Technical field
The invention belongs to carton production technical field, relate to a kind of Corrugated Box, specifically a kind of anti-static corrugated carton.
Background technology
Corrugated cardboard, also known as corrugated cardboard, is bonded by least one deck fluting board and one deck boxboard, has good elasticity and extensibility.Mainly for the manufacture of other wrapping material of the sandwich and delicate articles of carton, carton.The corrugation ripple of corrugated cardboard, as the arched door connected one by one, mutually in a row side by side, supports mutually, forms three-legged structure body, has good physical strength, plane, also can bear certain pressure, and springiness, good buffering function; It can make liner or the container of different shape size as required, easier than plastic. buffer material, quick; Temperature influence is little, and opacifying property is good, never degenerates by illumination, general also less by humidity effect, but should not use for a long time in the environment that humidity is larger, and this can affect its intensity.
The micro-electrostatic gas hidden in the corrugated cardboards can make the precise electronic product such as electronic component, unicircuit have an impact and cause product bad, and therefore, anti-electrostatic is very necessary.At the coating of corrugated cardboard surface carbon dust, laminated aluminium foil, in Case Board production process, add steel fiber or carbon fibre, all can manufacture the corrugated cardboard of anti-electrostatic.
Summary of the invention
The object of the present invention is to provide a kind of anti-static corrugated carton improving printing effect, Improving The Quality of Products.
Object of the present invention can be achieved through the following technical solutions:
A kind of anti-static corrugated carton, comprise the casing be made up of corrugated cardboard, be the Antistatic Paint of 1-3mm in surface-coated a layer thickness of corrugated cardboard, described Antistatic Paint is prepared from by the raw material of following weight part: water-borne acrylic resin 100 parts, epoxy resin 35-45 part, Synolac 20-30 part, carbon nanotube 1-5 part, carbon fiber 3-9 part, nano-calcium carbonate 10-15 part, graphitized carbon black 1-2 part, electrically conductive graphite 2-8 part, defoamer 1-2 part, thickening material 0.8-1.5 part, properties-correcting agent 0.1-0.3 part, dispersion agent 0.2-0.5 part, silane coupling agent 1-3 part, water 50-80 part,
The preparation method of described Antistatic Paint is:
Water-borne acrylic resin, epoxy resin, Synolac and water are mixed, at 50-60 DEG C of temperature, stir 60-80min, stirring velocity is 120-135r/min, obtains resin compound;
Graphitized carbon black, electrically conductive graphite mixing are placed on loft drier, and dry 1-3h under 90-95 DEG C of condition, obtains pre-treatment conductive filler material, for subsequent use;
Pre-treatment conductive filler material is joined in resin compound, then adds carbon nanotube, carbon fiber, nano-calcium carbonate, defoamer, thickening material, properties-correcting agent, dispersion agent, silane coupling agent successively, stir 50min, obtain Antistatic Paint.
As preferred further, Antistatic Paint of the present invention is prepared from by the raw material of following weight part: water-borne acrylic resin 100 parts, epoxy resin 40 parts, Synolac 25 parts, carbon nanotube 3 parts, 6 parts, carbon fiber, nano-calcium carbonate 12 parts, graphitized carbon black 1.5 parts, electrically conductive graphite 6 parts, defoamer 1.5 parts, thickening material 1 part, properties-correcting agent 0.2 part, dispersion agent 0.4 part, silane coupling agent 2 parts, 70 parts, water.
As preferred further, nano-calcium carbonate particle diameter of the present invention is 5-18nm.
As preferred further, thickening material of the present invention is polyacrylamide.
Beneficial effect of the present invention: Antistatic Paint of the present invention adds carbon nanotube and carbon fiber, makes Corrugated Box intensity high, and surface is moist, greatly reduce electrostatic interaction, make Corrugated Box surface no longer attract dust, reduce because of the scratch caused that rubs, improve print speed and printing effect; Add nano-calcium carbonate, make coating have good glossiness, transparency, stability.
Embodiment
Embodiment 1
A kind of anti-static corrugated carton, comprise the casing be made up of corrugated cardboard, be the Antistatic Paint of 3mm in surface-coated a layer thickness of corrugated cardboard, Antistatic Paint is prepared from by the raw material of following weight part: water-borne acrylic resin 100 parts, epoxy resin 35 parts, Synolac 20 parts, carbon nanotube 2 parts, 3 parts, carbon fiber, nano-calcium carbonate 10 parts, graphitized carbon black 1 part, electrically conductive graphite 4 parts, defoamer 1.2 parts, polyacrylamide 0.8 part, properties-correcting agent 0.1 part, dispersion agent 0.2 part, silane coupling agent 1 part, 60 parts, water.
Preparation method is: water-borne acrylic resin, epoxy resin, Synolac and water are mixed, at 50 DEG C of temperature, stir 80min, stirring velocity is 120r/min, obtains resin compound;
Graphitized carbon black, electrically conductive graphite mixing are placed on loft drier, and dry 3h under 90 DEG C of conditions, obtains pre-treatment conductive filler material, for subsequent use;
Pre-treatment conductive filler material is joined in resin compound, then adds carbon nanotube, carbon fiber, nano-calcium carbonate, defoamer, polyacrylamide, properties-correcting agent, dispersion agent, silane coupling agent successively, stir 50min, obtain anti-electrostatic filler.
Embodiment 2
A kind of anti-static corrugated carton, comprise the casing be made up of corrugated cardboard, be the Antistatic Paint of 2mm in surface-coated a layer thickness of corrugated cardboard, Antistatic Paint is prepared from by the raw material of following weight part: water-borne acrylic resin 100 parts, epoxy resin 45 parts, Synolac 30 parts, carbon nanotube 5 parts, 9 parts, carbon fiber, nano-calcium carbonate 15 parts, graphitized carbon black 2 parts, electrically conductive graphite 8 parts, defoamer 2 parts, polyacrylamide 1.5 parts, properties-correcting agent 0.3 part, dispersion agent 0.5 part, silane coupling agent 3 parts, 80 parts, water.
Preparation method: water-borne acrylic resin, epoxy resin, Synolac and water are mixed, stir 60min at 60 DEG C of temperature, stirring velocity is 135r/min, obtains resin compound;
Graphitized carbon black, electrically conductive graphite mixing are placed on loft drier, and dry 1h under 95 DEG C of conditions, obtains pre-treatment conductive filler material, for subsequent use;
Pre-treatment conductive filler material is joined in resin compound, then adds carbon nanotube, carbon fiber, nano-calcium carbonate, defoamer, polyacrylamide, properties-correcting agent, dispersion agent, silane coupling agent successively, stir 50min, obtain anti-electrostatic filler.
Embodiment 3
A kind of anti-static corrugated carton, comprise the casing be made up of corrugated cardboard, be the Antistatic Paint of 1.5mm in surface-coated a layer thickness of corrugated cardboard, the described raw material by following weight part is prepared from: water-borne acrylic resin 100 parts, epoxy resin 40 parts, Synolac 25 parts, carbon nanotube 3 parts, 6 parts, carbon fiber, nano-calcium carbonate 12 parts, graphitized carbon black 1.5 parts, electrically conductive graphite 6 parts, defoamer 1.5 parts, polyacrylamide 1 part, properties-correcting agent 0.2 part, dispersion agent 0.4 part, silane coupling agent 2 parts, 70 parts, water.
Preparation method: water-borne acrylic resin, epoxy resin, Synolac and water are mixed, stir 70min at 55 DEG C of temperature, stirring velocity is 125r/min, obtains resin compound;
Graphitized carbon black, electrically conductive graphite mixing are placed on loft drier, and dry 2h under 93 DEG C of conditions, obtains pre-treatment conductive filler material, for subsequent use;
Pre-treatment conductive filler material is joined in resin compound, then adds carbon nanotube, carbon fiber, nano-calcium carbonate, defoamer, polyacrylamide, properties-correcting agent, dispersion agent, silane coupling agent successively, stir 50min, obtain anti-electrostatic filler.
Above content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (4)
1. an anti-static corrugated carton, comprises the casing be made up of corrugated cardboard, it is characterized in that, be the Antistatic Paint of 1-3mm in surface-coated a layer thickness of corrugated cardboard, described Antistatic Paint is prepared from by the raw material of following weight part:
Water-borne acrylic resin 100 parts, epoxy resin 35-45 part, Synolac 20-30 part, carbon nanotube 1-5 part, carbon fiber 3-9 part, nano-calcium carbonate 10-15 part, graphitized carbon black 1-2 part, electrically conductive graphite 2-8 part, defoamer 1-2 part, thickening material 0.8-1.5 part, properties-correcting agent 0.1-0.3 part, dispersion agent 0.2-0.5 part, silane coupling agent 1-3 part, water 50-80 part;
The preparation method of described Antistatic Paint is:
Water-borne acrylic resin, epoxy resin, Synolac and water are mixed, at 50-60 DEG C of temperature, stir 60-80min, stirring velocity is 120-135r/min, obtains resin compound;
Graphitized carbon black, electrically conductive graphite mixing are placed on loft drier, and dry 1-3h under 90-95 DEG C of condition, obtains pre-treatment conductive filler material, for subsequent use;
Pre-treatment conductive filler material is joined in resin compound, then adds carbon nanotube, carbon fiber, nano-calcium carbonate, defoamer, thickening material, properties-correcting agent, dispersion agent, silane coupling agent successively, stir 50min, obtain Antistatic Paint.
2. anti-static corrugated carton according to claim 1, it is characterized in that, described Antistatic Paint is prepared from by the raw material of following weight part: water-borne acrylic resin 100 parts, epoxy resin 40 parts, Synolac 25 parts, carbon nanotube 3 parts, 6 parts, carbon fiber, nano-calcium carbonate 12 parts, graphitized carbon black 1.5 parts, electrically conductive graphite 6 parts, defoamer 1.5 parts, thickening material 1 part, properties-correcting agent 0.2 part, dispersion agent 0.4 part, silane coupling agent 2 parts, 70 parts, water.
3. anti-static corrugated carton according to claim 1 and 2, is characterized in that, described nano-calcium carbonate particle diameter is 5-18nm.
4. anti-static corrugated carton according to claim 1 and 2, is characterized in that, described thickening material is polyacrylamide.