CN105544217A - Resin non-ironing finishing agent and preparation method thereof - Google Patents
Resin non-ironing finishing agent and preparation method thereof Download PDFInfo
- Publication number
- CN105544217A CN105544217A CN201610111194.1A CN201610111194A CN105544217A CN 105544217 A CN105544217 A CN 105544217A CN 201610111194 A CN201610111194 A CN 201610111194A CN 105544217 A CN105544217 A CN 105544217A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- wash
- resinae
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a resin non-ironing finishing agent comprising components in parts by weight as follows: 15-25 parts of resorcinol-acetaldehyde pre-condensed resin, 10-18 parts of terpene resin, 8-16 parts of manila elemi gum, 5-10 parts of butyl acrylate, 10-15 parts of acrylic acid, 3-8 parts of sodium bicarbonate, 2-7 parts of styrene, 4-7 parts of diacetone acrylamide, 5-12 parts of glyoxal and 30-40 parts of deionized water. With the adoption of the finishing agent, crease resistance, shrinkage resistance and non-ironing performance of textile clothes can be obviously improved and harmful substances such as formaldehyde are effectively avoided.
Description
Technical field
The invention belongs to finishing agent field, be specifically related to a kind of resinae wash and wear finisher and preparation method thereof.
Background technology
Mainly there is wrinkle resistance difference to improve COTTON FABRIC in wash and wear finisher, crease easily, easily shrink, wash after need the defect that presses.Existing resinae wash and wear finisher is mainly N-methylol amide resinae crease proofing agent, and it has cheap, and the advantage of good finishing effect, is thus widely used in textile industry.But the fabric that it arranges can discharge the formaldehyde to human body and bad environmental in processing, storage and use procedure.Thus develop environmental friendliness, the resinae wash and wear finisher of good finishing effect seems particularly important.
Summary of the invention
For the above technical problem existed in prior art, the invention provides a kind of resinae wash and wear finisher and preparation method thereof, utilize this finishing agent process cotton thing, while not discharging formaldehyde, the wrinkle resistance of clothing, anti-shrinkage can be significantly improved, exempt to press performance.
Technical scheme: a kind of resinae wash and wear finisher, comprise the composition of following parts by weight: resorcinol-acetaldehyde precondensate resin 15-25 part, polyterpene resin 10-18 part, Manila elemi resin 8-16 part, butyl acrylate 5-10 part, acrylic acid 10-15 part, sodium bicarbonate 3-8 part, styrene 2-7 part, diacetone acrylamide 4-7 part, glyoxal 5-12 part, deionized water 30-40 part.
Preferably, described resorcinol-acetaldehyde precondensate resin 17-22 part, polyterpene resin 13-16 part, Manila elemi resin 10-14 part, butyl acrylate 7-9 part, acrylic acid 12-14 part, sodium bicarbonate 4-7 part, styrene 3-6 part, diacetone acrylamide 5-7 part, glyoxal 6-9 part, deionized water 35-40 part.
Preferably, described resorcinol-acetaldehyde precondensate resin 20 parts, polyterpene resin 14 parts, Manila elemi resin 13 parts, butyl acrylate 8 parts, 13 parts, acrylic acid, sodium bicarbonate 6 parts, styrene 5 parts, diacetone acrylamide 6 parts, glyoxal 8 parts, deionized water 38 parts.
A preparation method for resinae wash and wear finisher, comprises the steps:
S1: resorcinol-acetaldehyde precondensate resin 15-25 part, polyterpene resin 10-18 part, Manila elemi resin 8-16 part, styrene 2-7 part and glyoxal 5-12 part are added in reactor, raised temperature is to 70-80 DEG C, and reaction 30-50min, obtains mixed liquor A;
S2: butyl acrylate 5-10 part, acrylic acid 10-15 part and deionized water 30-40 part are stirred, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 4-7 part, raised temperature 60-80 DEG C, reaction 10-15min;
S4: drip sodium bicarbonate 3-8 part in step S3, be heated to 90-100 DEG C while stirring, following reaction 1-3h; Described resinae wash and wear finisher can be obtained after question response cooling.
Preferably, temperature described in step S1 is 75 DEG C, reaction 45min.
Preferably, temperature described in step S3 is 70 DEG C, reaction 12min
Preferably, temperature described in step S4 is 95 DEG C, and reaction 2h, heating rate is 1 °/min.
Beneficial effect: the preparation method of a kind of resinae wash and wear finisher of the present invention, with materials such as resorcinol-acetaldehyde precondensate resin, polyterpene resin, Manila elemi resins for raw material, through stirring, adding the steps such as thermal response and prepare resinae wash and wear finisher, avoid the generation of formaldehyde harmful substance; This preparation technology is simple, process is shorter; Wrinkle resistance, the anti-shrinkage of clothing can be significantly improved after textile clothes utilizes finishing agent of the present invention, exempt to press performance.
Detailed description of the invention
Embodiment 1
S1: resorcinol-acetaldehyde precondensate resin 15 parts, polyterpene resin 10 parts, Manila elemi resin 8 parts, styrene 2 parts and glyoxal 5 parts are added in reactor, raised temperature to 70 DEG C, reaction 30min, obtains mixed liquor A;
S2: by butyl acrylate 5 parts, 10 parts, acrylic acid and deionized water 30 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 4 parts, raised temperature 60 DEG C, reaction 10min;
S4: drip sodium bicarbonate 3 parts in step S3, be heated to 90 DEG C while stirring, heating rate is 1 °/min; Following reaction 1h; Described resinae wash and wear finisher can be obtained after question response cooling.
Comparative example 1
S1: styrene 2 parts and glyoxal 5 parts are added in reactor, raised temperature to 70 DEG C, reaction 30min, obtains mixed liquor A;
S2: by butyl acrylate 5 parts, 10 parts, acrylic acid and deionized water 30 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 4 parts, raised temperature 60 DEG C, reaction 10min;
S4: drip sodium bicarbonate 3 parts in step S3, be heated to 90 DEG C while stirring, heating rate is 1 °/min; Following reaction 1h; Finishing agent can be obtained after question response cooling.
Embodiment 2
S1: resorcinol-acetaldehyde precondensate resin 25 parts, polyterpene resin 18 parts, Manila elemi resin 16 parts, styrene 7 parts and glyoxal 12 parts are added in reactor, raised temperature to 80 DEG C, reaction 50min, obtains mixed liquor A;
S2: by butyl acrylate 10 parts, 15 parts, acrylic acid and deionized water 40 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 7 parts, raised temperature 80 DEG C, reaction 15min;
S4: drip sodium bicarbonate 8 parts in step S3, be heated to 100 DEG C while stirring, heating rate is 1 °/min; Following reaction 3h; Described resinae wash and wear finisher can be obtained after question response cooling.
Comparative example 2
S1: styrene 7 parts and glyoxal 12 parts are added in reactor, raised temperature to 80 DEG C, reaction 50min, obtains mixed liquor A;
S2: by butyl acrylate 10 parts, 15 parts, acrylic acid and deionized water 40 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 7 parts, raised temperature 80 DEG C, reaction 15min;
S4: drip sodium bicarbonate 8 parts in step S3, be heated to 100 DEG C while stirring, heating rate is 1 °/min; Following reaction 3h; Finishing agent can be obtained after question response cooling.
Embodiment 3
S1: resorcinol-acetaldehyde precondensate resin 17 parts, polyterpene resin 13 parts, Manila elemi resin 10 parts, styrene 3 parts and glyoxal 6 parts are added in reactor, raised temperature to 70 DEG C, reaction 30min, obtains mixed liquor A;
S2: by butyl acrylate 7 parts, 12 parts, acrylic acid and deionized water 35 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 5 parts, raised temperature 60 DEG C, reaction 10min;
S4: drip sodium bicarbonate 4 parts in step S3, be heated to 90 DEG C while stirring, heating rate is 1 °/min; Following reaction 1h; Described resinae wash and wear finisher can be obtained after question response cooling.
Embodiment 4
S1: resorcinol-acetaldehyde precondensate resin 22 parts, polyterpene resin 16 parts, Manila elemi resin 14 parts, styrene 6 parts and glyoxal 9 parts are added in reactor, raised temperature to 80 DEG C, reaction 50min, obtains mixed liquor A;
S2: by butyl acrylate 9 parts, 14 parts, acrylic acid and deionized water 40 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 7 parts, raised temperature 80 DEG C, reaction 15min;
S4: drip sodium bicarbonate 7 parts in step S3, be heated to 100 DEG C while stirring, heating rate is 1 °/min; Following reaction 3h; Described resinae wash and wear finisher can be obtained after question response cooling.
Embodiment 5
S1: resorcinol-acetaldehyde precondensate resin 20 parts, polyterpene resin 14 parts, Manila elemi resin 13 parts, styrene 5 parts and glyoxal 8 parts are added in reactor, raised temperature to 75 DEG C, reaction 45min, obtains mixed liquor A;
S2: by butyl acrylate 8 parts, 13 parts, acrylic acid and deionized water 38 parts stirring, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 6 parts, raised temperature 70 DEG C, reaction 12min;
S4: drip sodium bicarbonate 6 parts in step S3, be heated to 95 DEG C while stirring, heating rate is 1 °/min; Following reaction 2h; Described resinae wash and wear finisher can be obtained after question response cooling.
By the finishing agent that each embodiment and comparative example obtain, be applied in textile clothes, test creasy recovery angle and the tearing brute force retention rate of treated textile clothes, result is as follows:
Claims (7)
1. a resinae wash and wear finisher, it is characterized in that, comprise the composition of following parts by weight: resorcinol-acetaldehyde precondensate resin 15-25 part, polyterpene resin 10-18 part, Manila elemi resin 8-16 part, butyl acrylate 5-10 part, acrylic acid 10-15 part, sodium bicarbonate 3-8 part, styrene 2-7 part, diacetone acrylamide 4-7 part, glyoxal 5-12 part, deionized water 30-40 part.
2. a kind of resinae wash and wear finisher according to claim 1, it is characterized in that, described resorcinol-acetaldehyde precondensate resin 17-22 part, polyterpene resin 13-16 part, Manila elemi resin 10-14 part, butyl acrylate 7-9 part, acrylic acid 12-14 part, sodium bicarbonate 4-7 part, styrene 3-6 part, diacetone acrylamide 5-7 part, glyoxal 6-9 part, deionized water 35-40 part.
3. a kind of resinae wash and wear finisher according to claim 2, it is characterized in that, described resorcinol-acetaldehyde precondensate resin 20 parts, polyterpene resin 14 parts, Manila elemi resin 13 parts, butyl acrylate 8 parts, 13 parts, acrylic acid, sodium bicarbonate 6 parts, styrene 5 parts, diacetone acrylamide 6 parts, glyoxal 8 parts, deionized water 38 parts.
4. a preparation method for resinae wash and wear finisher, is characterized in that, comprises the steps:
S1: resorcinol-acetaldehyde precondensate resin 15-25 part, polyterpene resin 10-18 part, Manila elemi resin 8-16 part, styrene 2-7 part and glyoxal 5-12 part are added in reactor, raised temperature is to 70-80 DEG C, and reaction 30-50min, obtains mixed liquor A;
S2: butyl acrylate 5-10 part, acrylic acid 10-15 part and deionized water 30-40 part are stirred, ultrasonic process, to dispersed shape, obtains mixed liquid B;
S3: mixed liquid B described in mixed liquor A described in step S1 and step S2 mixed, drips diacetone acrylamide 4-7 part, raised temperature 60-80 DEG C, reaction 10-15min;
S4: drip sodium bicarbonate 3-8 part in step S3, be heated to 90-100 DEG C while stirring, following reaction 1-3h; Described resinae wash and wear finisher can be obtained after question response cooling.
5. the preparation method of a kind of resinae wash and wear finisher according to claim 4, is characterized in that, temperature described in step S1 is 75 DEG C, reaction 45min.
6. the preparation method of a kind of resinae wash and wear finisher according to claim 4, is characterized in that, temperature described in step S3 is 70 DEG C, reaction 12min.
7. the preparation method of a kind of resinae wash and wear finisher according to claim 4, is characterized in that, temperature described in step S4 is 95 DEG C, and reaction 2h, heating rate is 1 °/min.