CN105586601A - Novel stainless steel decorative plate treatment technique - Google Patents
Novel stainless steel decorative plate treatment technique Download PDFInfo
- Publication number
- CN105586601A CN105586601A CN201510974281.5A CN201510974281A CN105586601A CN 105586601 A CN105586601 A CN 105586601A CN 201510974281 A CN201510974281 A CN 201510974281A CN 105586601 A CN105586601 A CN 105586601A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- decorative plate
- steel decorative
- decorated sheet
- corrosion resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of field of surface treatment of stainless metal, in particular to a novel stainless steel decorative plate treatment technique. The novel stainless steel decorative plate treatment technique comprises the steps that deoiling and washing are conducted, a stainless steel decorative plate is placed in a deoiling solution to be soaked for 5-10 min under the normal temperature condition, and then the stainless steel decorative plate is washed; the washed stainless steel decorative plate is placed in an acid solution to be soaked; wire drawing is conducted on the pickled stainless steel decorative plate with a scouring pad; the stainless steel decorative plate subjected to wire drawing is cleaned under the normal temperature condition; the cleaned stainless steel decorative plate is aired completely; the completely-aired stainless steel decorative plate is sprayed with paint evenly; and the stainless steel decorative plate sprayed with the paint is placed in an anti-explosion oven, high-temperature baking is conducted on the stainless steel decorative plate at a certain temperature, and heat preservation is conducted for a period of time. By the adoption of the novel stainless steel decorative plate treatment technique, the requirement of modern people for diversified colors can be met, and the overall quality and modern sense of kitchen electric appliances are improved.
Description
Technical field
The present invention relates to stainless steel metal field of surface treatment, be specifically related to a kind of processing work of new type stainless steel. corrosion resistance decorative panelSkill.
Background technology
Stainless steel decorated sheet had both had the distinctive gloss of metal and intensity, had again that color appears, constant color.Stainless steel decorated sheet has not only kept the stainless physics of primary colors, chemistry, mechanical performance, and has stronger than primary colors stainless steelDecay resistance. Therefore, since it comes out from 20 century 70s, just at building materials, chemical industry, automobile, electronics industry andThe fields such as industrial art are widely used.
Current stainless pretreatment comprises the following steps: degreasing → Chemical cleaning → whitening → washing → air-dry → bakingRoasting, wherein whitening technique adopts high concentration (about 40-60%) nitric acid more, and danger coefficient is high, large to human body and environmental hazard, and washesBase material after white mostly is canescence usually bad with delustring; Stainless steel usually can be destroyed because of its passivation layer after whiteningCorrosion resistance declines, and touches and be easy to leave a trace on the surface of base material with hand.
The Chinese patent " anti-skidding acid-proof anticorrosive corrosion resistant plate " of application notification number CN104742435A, relates to metallic plateTechnical field, especially a kind of anti-skidding acid-proof anticorrosive corrosion resistant plate, comprises corrosion resistant plate body, described corrosion resistant plate bodyOn be provided with a plurality of interlaced anti-skidding stripeds, described corrosion resistant plate body upper surface has pickling layer, outside pickling layerBe coated with fluorine carbon paint anticorrosive coat, described fluorine carbon paint anticorrosive coat surface is coated with PVC diaphragm, under described corrosion resistant plate bodySurface is provided with polishing layer. Anti-skidding acid-proof anticorrosive corrosion resistant plate of the present invention can play good acid-proof anticorrosive and anti-Sliding effect, and stainless steel pipe inner surface is carried out to polishing, better effects if during for industrial building.
Although above-mentioned patent discloses a kind of corrosion resistant plate, this corrosion resistant plate is argenteous single sensation always, noCan meet the pursuit of the diversification color of modern's pursuit, reduce the overall quality of kitchen electricity with modern sense.
Summary of the invention
The object of the invention is to address the above problem, a kind for the treatment of process of new type stainless steel. corrosion resistance decorative panel is provided, canAddress the above problem.
The present invention addresses the above problem adopted technical scheme:
A treatment process for new type stainless steel. corrosion resistance decorative panel, carries out successively according to following step:
Step 1: the washing of deoiling; Stainless steel decorated sheet is placed in de-oiling solution and is soaked under the condition of normal temperature,Soak time is 5-10min, then washes;
Step 2: pickling; Stainless steel decorated sheet after washing is placed in acid solution and is soaked;
Step 3: wire drawing; Stainless steel decorated sheet after pickling is carried out to wire drawing with scouring pad;
Step 4: clean; Stainless steel decorated sheet after wire drawing is cleaned under the condition of normal temperature;
Step 5: dry; Stainless steel decorated sheet after cleaning is dried, parch completely;
Step 6: spray paint: the stainless steel decorated sheet after parching is painted to the processing of spraying paint, spray paint evenly;
Step 7: baking; Stainless steel decorated sheet after spraying paint is placed in explosion-proof baking box, carries out at a certain temperature heightTemperature baking, and be incubated a period of time.
Preferably, the acid solution described in step 2 comprises sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt, described inThe consumption (mass fraction) of sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt:
Preferably, the consumption (mass fraction) of described sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt:
Preferably, the uniform temperature described in step 7 is 150-180 DEG C, and a period of time is 30-40min.
Preferably, the uniform temperature described in step 7 is 165 DEG C, and a period of time is 35min.
Preferably, the paint described in step 6 comprises raw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, firstBase methyl acrylate, poly-phthalimide, described raw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylateThe consumption (mass fraction) of ester, poly-phthalimide:
Preferably, described raw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-phthaleinThe consumption (mass fraction) of imines:
The invention has the beneficial effects as follows:
1, the stainless steel decorated sheet that the present invention produces, improving that it is wear-resisting, in acid-proof alkaline, adopts homemade oilPaint makes it have oil resistant, water-fast, salt spray resistance, acidproof, alkaline-resisting, shock-resistant, rub resistance, fireproof feature. Can meet modernThe pursuit of the diversification color of pursuing, has improved the overall quality of kitchen electricity with modern sense.
Detailed description of the invention
Below by detailed description of the invention, the present invention is described in further detail:
Embodiment mono-
The treatment process of a kind of new type stainless steel. corrosion resistance decorative panel of the present invention, carries out successively according to following step:
Step 1: the washing of deoiling; Stainless steel decorated sheet is placed in de-oiling solution and is soaked under the condition of normal temperature,Soak time is 5-10min, then washes;
Step 2: pickling; Stainless steel decorated sheet after washing is placed in acid solution and is soaked; Described acid solutionComprise sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt, described sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone saltConsumption (mass fraction):
Step 3: wire drawing; Stainless steel decorated sheet after pickling is carried out to wire drawing with scouring pad;
Step 4: clean; Stainless steel decorated sheet after wire drawing is cleaned under the condition of normal temperature;
Step 5: dry; Stainless steel decorated sheet after cleaning is dried, parch completely;
Step 6: spray paint: the stainless steel decorated sheet after parching is painted to the processing of spraying paint, spray paint evenly; DescribedPaint comprises raw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-phthalimide, described paintThe consumption (mass fraction) of raw material, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-phthalimide:
Step 7: baking; Stainless steel decorated sheet after spraying paint is placed in explosion-proof baking box, at 150 DEG C, carries out high temperatureBaking, and temperature retention time is 30min.
Embodiment bis-
Compared with embodiment mono-, the consumption of the sulfuric acid described in step 2, hydrochloric acid, selenium dioxide, copper sulphate and winestone saltAmount (mass fraction):
Raw materials for varnish described in step 6, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-The consumption (mass fraction) of phthalimide:
Temperature described in step 7 is 165 DEG C, and temperature retention time is 35min. Other technological process is identical with embodiment mono-.
Embodiment tri-
Compared with embodiment mono-, the consumption of the sulfuric acid described in step 2, hydrochloric acid, selenium dioxide, copper sulphate and winestone saltAmount (mass fraction):
Raw materials for varnish described in step 6, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-The consumption (mass fraction) of phthalimide:
Temperature described in step 7 is 180 DEG C, and temperature retention time is 40min. Other technological process is identical with embodiment mono-.Other technological process is identical with embodiment mono-.
It should be noted last that: above embodiment is the unrestricted technical scheme of the present invention in order to explanation only, although ginsengAccording to above-described embodiment, the present invention is had been described in detail, will be understood by those skilled in the art that: still can be to thisInvention is modified or is equal to replacement, and does not depart from any modification or partial replacement of the spirit and scope of the present invention, and it is equalShould be encompassed in the middle of claim scope of the present invention.
Claims (7)
1. a treatment process for new type stainless steel. corrosion resistance decorative panel, is characterized in that: carry out successively according to following step:
Step 1: the washing of deoiling; Stainless steel decorated sheet is placed in de-oiling solution and is soaked under the condition of normal temperature, soakTime is 5-10min, then washes;
Step 2: pickling; Stainless steel decorated sheet after washing is placed in acid solution and is soaked;
Step 3: wire drawing; Stainless steel decorated sheet after pickling is carried out to wire drawing with scouring pad;
Step 4: clean; Stainless steel decorated sheet after wire drawing is cleaned under the condition of normal temperature;
Step 5: dry; Stainless steel decorated sheet after cleaning is dried, parch completely;
Step 6: spray paint: the stainless steel decorated sheet after parching is painted to the processing of spraying paint, spray paint evenly;
Step 7: baking; Stainless steel decorated sheet after spraying paint is placed in explosion-proof baking box, carries out at a certain temperature high temperature bakingRoasting, and be incubated a period of time.
2. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 1, is characterized in that: institute in step 2The acid solution of stating comprises sulfuric acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt, described sulfuric acid, hydrochloric acid, selenium dioxide, sulfuric acidThe consumption (mass fraction) of copper and winestone salt:
3. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 2, is characterized in that: described sulphurThe consumption (mass fraction) of acid, hydrochloric acid, selenium dioxide, copper sulphate and winestone salt:
4. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 3, is characterized in that: institute in step 7The uniform temperature of stating is 150-180 DEG C, and a period of time is 30-40min.
5. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 4, is characterized in that: institute in step 7The uniform temperature of stating is 165 DEG C, and a period of time is 35min.
6. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 1, is characterized in that: institute in step 6The paint of stating comprises raw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-phthalimide, described inRaw materials for varnish, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, the consumption (mass parts of poly-phthalimideNumber):
7. the treatment process of a kind of new type stainless steel. corrosion resistance decorative panel according to claim 6, is characterized in that: described paint is formerThe consumption (mass fraction) of material, polypropylene glycol acrylate, basic lead chromate silicate, methyl methacrylate, poly-phthalimide: