CN1905116A - Method for mfg. piezo-optical x-ray screen - Google Patents
Method for mfg. piezo-optical x-ray screen Download PDFInfo
- Publication number
- CN1905116A CN1905116A CN 200610105008 CN200610105008A CN1905116A CN 1905116 A CN1905116 A CN 1905116A CN 200610105008 CN200610105008 CN 200610105008 CN 200610105008 A CN200610105008 A CN 200610105008A CN 1905116 A CN1905116 A CN 1905116A
- Authority
- CN
- China
- Prior art keywords
- end liner
- phosphor screen
- screen end
- plane
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses press polish type X light fluorescent screen manufacturing method. It includes the following steps: mixing fluorescent powder that using sulfide or sulfur-oxidizing gadolinium terbium with 3-10um granularity as fluorescent powder, potassium bromide or potassium silicate as adhesive, adding 5-10permile latter in the former and stirring; processing fluorescent screen end liner; decontaminating; layering or spraying the mixed fluorescent powder into the end liner with 0.4-0.8mm; making compacting tool set; stamping at 40-60 degree centigrade 10-150kg/cm2 for 3-4h. The invention can improve X light image quality in vacuum.
Description
Technical field
The present invention relates to make the fluoroscopic method of X-ray, the x-ray image that is mainly used in the electrovacuum container shows.
Background technology
The phosphor screen manufacture method of using is in a vacuum all used the whole bag of tricks processing such as the precipitation method, spraying process, centrifugal process now.The large tracts of land phosphor screen all has the phosphor powder layer air spots, and the uniformity of image display brightness is had certain influence, and when the image display requirement was higher, influence is obviously aggravation also.
Summary of the invention
The purpose of this invention is to provide the fluoroscopic manufacture method of a kind of piezo-optical x-ray, to solve phosphor powder layer surface roughness and the unevenness problem of higher that existing large tracts of land phosphor screen exists.
It comprises the following steps the present invention,
A), mixed fluorescent powder, with granularity be the sulfide of 3~10 μ m or gadolinium oxysulfide terbium as fluorescent material, as adhesive, add 5~10 ‰ adhesive with KBr or potassium silicate in fluorescent material, the back that stirs is standby;
B), processing phosphor screen end liner, phosphor screen end liner 4 materials adopt metal or nonmetallic substance, can can process the phosphor screen end liner of the size geometry that varies in size according to the actual needs, make phosphor screen end liner two plane parallel degree error<0.01mm up and down, bottom substrate plane surface roughness is 0.8-1.6, unevenness≤0.03mm;
C), decontamination handles, and adhesive is coated on the phosphor screen end liner that the surface cleaned up uniformly, carries out the decontamination processing with the surface that absolute ethyl alcohol and oxidant contact with phosphor powder layer the phosphor screen end liner; To guarantee the reliable firmly contact of following fluoresent coating;
D), with the tiling or spraying process the mixed fluorescent powder in a step is put into the phosphor screen end liner, fluorescent material thickness is 0.4-0.8mm; So that can guarantee that when press forming the thickness of phosphor powder layer is 0.1-0.4mm;
E), make compacting tool set, plane compacting drift is corresponding with phosphor screen end liner size, plane compacting punch head surface roughness is 0.4-0.8, unevenness≤0.03mm, two plane parallel degree error<0.01mm about the plane compacting drift;
F), punching press, the phosphor screen end liner is heated to 40~60 ℃, press plane compacting drift, put into slowly pressurization on the hydraulic press table top, pressure is 10~150kg/cm
2, keep-uped pressure 3-4 hour, progressively reduce pressure then to normal pressure.To reduce the internal stress that metal material and fluorescent material work in-process produce, prevent the fluorescence coating fracture; Pressure is relevant with the area of phosphor screen end liner, and the area of phosphor screen end liner is little, and pressure is just little.
The present invention makes simply, process stabilizing, and control is convenient, can improve X light image quality under vacuum.This method has no effect to environment.
Description of drawings
Fig. 1 is a punching press schematic diagram of the present invention.
Embodiment
The following examples can make those skilled in the art understand the present invention better, but do not limit the present invention in any way.
Embodiment 1:
A), choose the green emitting phosphor that granularity is 3~10 μ m (gadolinium oxysulfide terbium) 10g, add 5 ‰ KBr or potassium silicate adhesive in fluorescent material, the back that stirs is standby;
B), the processing diameter is the phosphor screen end liner 4 of 50mm, makes phosphor screen end liner two plane parallel degree error<0.01mm about in the of 4, bottom substrate plane surface roughness is 0.8, unevenness≤0.03mm;
C), decontamination handles, and adhesive is coated on the phosphor screen end liner 4 that the surface cleaned up uniformly, carries out the decontamination processing with the surface that absolute ethyl alcohol and oxidant contact with phosphor powder layer 3 phosphor screen end liner 4; To guarantee the reliable firmly contact of following fluoresent coating;
D), with the tiling or spraying process the mixed fluorescent powder in a step is put into phosphor screen end liner 4, fluorescent material thickness is 0.4mm; So that can guarantee that when press forming the thickness of phosphor powder layer 3 is 0.1-0.4mm;
E), make compacting tool set, plane compacting drift 2 is corresponding with phosphor screen end liner 4 sizes, plane compacting drift 2 surface roughnesses are 0.4-0.8, unevenness≤0.03mm, drift two plane parallel degree error<0.01mm about in the of 2 are suppressed on the plane;
F), punching press, phosphor screen end liner 4 is heated to 40 ℃, press plane compacting drift 2, plane compacting drift 2 is provided with hydraulic press piston 1, and phosphor screen end liner 4 is put into slowly pressurization on the hydraulic press table top 5, pressure is 40kg/cm
2, keep-uped pressure 3-4 hour, progressively reduce pressure then to normal pressure.To reduce the internal stress that metal material and fluorescent material work in-process produce, prevent the fluorescence coating fracture; Pressure is relevant with the area of phosphor screen end liner, and the area of phosphor screen end liner is little, and pressure is just little.
Finished product of the present invention can guarantee the phosphor screen surface roughness at 0.4-0.8, and unevenness can be controlled in≤0.03mm.The physical dimension error is≤0.02mm.Phosphor powder layer discharges and recharges freely, faithfully the X light image details.
Embodiment 2:
A), choose the green emitting phosphor that granularity is 3~10 μ m (gadolinium oxysulfide terbium) 20g, add 5 ‰ KBr or potassium silicate adhesive in fluorescent material, the back that stirs is standby;
B), the processing diameter is the phosphor screen end liner 4 of 50mm, makes phosphor screen end liner two plane parallel degree error<0.01mm about in the of 4, bottom substrate plane surface roughness is 0.8, unevenness≤0.03mm;
C), decontamination handles, and adhesive is coated on the phosphor screen end liner 4 that the surface cleaned up uniformly, carries out the decontamination processing with the surface that absolute ethyl alcohol and oxidant contact with phosphor powder layer 3 phosphor screen end liner 4;
D), with the tiling or spraying process the mixed fluorescent powder in a step is put into phosphor screen end liner 4, fluorescent material thickness is 0.4mm;
E), make compacting tool set, plane compacting drift 2 is corresponding with phosphor screen end liner 4 sizes, plane compacting drift 2 surface roughnesses are 0.4-0.8, unevenness≤0.03mm, drift two plane parallel degree error<0.01mm about in the of 2 are suppressed on the plane;
F), punching press, phosphor screen end liner 4 is heated to 50 ℃, press plane compacting drift 2, plane compacting drift 2 is provided with hydraulic press piston 1, and phosphor screen end liner 4 is put into slowly pressurization on the hydraulic press table top 5, pressure is 90kg/cm
2, keep-uped pressure 3-4 hour, progressively reduce pressure then to normal pressure.
Embodiment 3:
A), choose the sulfide 25g that granularity is 3~10 μ m, add 10 ‰ KBr or potassium silicate adhesive in fluorescent material, the back that stirs is standby;
B), the processing diameter is the phosphor screen end liner 4 of 50mm, makes phosphor screen end liner two plane parallel degree error<0.01mm about in the of 4, bottom substrate plane surface roughness is 1.6, unevenness≤0.03mm;
C), decontamination handles, and adhesive is coated on the phosphor screen end liner 4 that the surface cleaned up uniformly, carries out the decontamination processing with the surface that absolute ethyl alcohol and oxidant contact with phosphor powder layer 3 phosphor screen end liner 4;
D), with the tiling or spraying process the mixed fluorescent powder in a step is put into phosphor screen end liner 4, fluorescent material thickness is 0.8mm;
E), make compacting tool set, plane compacting drift 2 is corresponding with phosphor screen end liner 4 sizes, plane compacting drift 2 surface roughnesses are 0.4-0.8, unevenness≤0.03mm, drift two plane parallel degree error<0.01mm about in the of 2 are suppressed on the plane;
F), punching press, phosphor screen end liner 4 is heated to 60 ℃, press plane compacting drift 2, plane compacting drift 2 is provided with hydraulic press piston 1, and phosphor screen end liner 4 is put into slowly pressurization on the hydraulic press table top 5, pressure is 140kg/cm
2, keep-uped pressure 3-4 hour, progressively reduce pressure then to normal pressure.
Claims (1)
1, the fluoroscopic manufacture method of a kind of piezo-optical x-ray is characterized in that: it comprises the following steps,
A), mixed fluorescent powder, with granularity be the sulfide of 3~10 μ m or gadolinium oxysulfide terbium as fluorescent material, as adhesive, add 5~10 ‰ adhesive with KBr or potassium silicate in fluorescent material, the back that stirs is standby;
B), processing phosphor screen end liner, make phosphor screen end liner two plane parallel degree error<0.01mm up and down, bottom substrate plane surface roughness is 0.8-1.6, unevenness≤0.03mm;
C), decontamination handles, and adhesive is coated on the phosphor screen end liner that the surface cleaned up uniformly, carries out the decontamination processing with the surface that absolute ethyl alcohol and oxidant contact with phosphor powder layer the phosphor screen end liner;
D), with the tiling or spraying process the mixed fluorescent powder in a step is put into the phosphor screen end liner, fluorescent material thickness is 0.4-0.8mm;
E), make compacting tool set, plane compacting drift is corresponding with phosphor screen end liner size, plane compacting punch head surface roughness is 0.4-0.8, unevenness≤0.03mm, two plane parallel degree error<0.01mm about the plane compacting drift;
F), punching press, the phosphor screen end liner is heated to 40~60 ℃, press plane compacting drift, put into slowly pressurization on the hydraulic press table top, pressure is 10~150kg/cm
2, keep-uped pressure 3-4 hour, progressively reduce pressure then to normal pressure.