DE160267T1 - Poroese keramische cordientkoerper, ihre herstellung und ihre verwendung. - Google Patents
Poroese keramische cordientkoerper, ihre herstellung und ihre verwendung.Info
- Publication number
- DE160267T1 DE160267T1 DE198585104934T DE85104934T DE160267T1 DE 160267 T1 DE160267 T1 DE 160267T1 DE 198585104934 T DE198585104934 T DE 198585104934T DE 85104934 T DE85104934 T DE 85104934T DE 160267 T1 DE160267 T1 DE 160267T1
- Authority
- DE
- Germany
- Prior art keywords
- organic solvent
- percent
- organic
- glass powder
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/14—Silica and magnesia
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
- B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
- B01J20/16—Alumino-silicates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/281—Sorbents specially adapted for preparative, analytical or investigative chromatography
- B01J20/282—Porous sorbents
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B33/00—Silicon; Compounds thereof
- C01B33/20—Silicates
- C01B33/26—Aluminium-containing silicates, i.e. silico-aluminates
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/10—Forming beads
- C03B19/107—Forming hollow beads
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/10—Forming beads
- C03B19/108—Forming porous, sintered or foamed beads
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C10/00—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition
- C03C10/0036—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and a divalent metal oxide as main constituents
- C03C10/0045—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and a divalent metal oxide as main constituents containing SiO2, Al2O3 and MgO as main constituents
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C11/00—Multi-cellular glass ; Porous or hollow glass or glass particles
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C11/00—Multi-cellular glass ; Porous or hollow glass or glass particles
- C03C11/002—Hollow glass particles
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
- C04B35/18—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay rich in aluminium oxide
- C04B35/195—Alkaline earth aluminosilicates, e.g. cordierite or anorthite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
- C04B38/009—Porous or hollow ceramic granular materials, e.g. microballoons
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
- C04B38/08—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof by adding porous substances
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N30/00—Investigating or analysing materials by separation into components using adsorption, absorption or similar phenomena or using ion-exchange, e.g. chromatography or field flow fractionation
- G01N30/02—Column chromatography
- G01N30/50—Conditioning of the sorbent material or stationary liquid
- G01N30/52—Physical parameters
- G01N2030/524—Physical parameters structural properties
- G01N2030/528—Monolithic sorbent material
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Ceramic Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Structural Engineering (AREA)
- Life Sciences & Earth Sciences (AREA)
- Analytical Chemistry (AREA)
- Geochemistry & Mineralogy (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Crystallography & Structural Chemistry (AREA)
- Dispersion Chemistry (AREA)
- Glass Compositions (AREA)
- Compositions Of Oxide Ceramics (AREA)
Claims (15)
1. Poröse Cordierit-Keramikmassen die mit im wesentlichen
der chemischen Zusammensetzung von Cordierit und mit einer neuen charakteristischen, offenen
Struktur mit untereinander verbundenen Zellen, die durch thermische Zersetzung einer versprühten Ausgangslösung
in Gegenwart eines oxidierenden Gases zu hohlkugeligem, mikrosphärischem Cordieritglaspulver, Verarbeiten
des Glaspulvers zu Formkörpern, gegebenenfalls nach Hitzebehandlung, und nachfolgendes Brennen der
Formkörper erhalten werden, wobei die Ausgangslösung in einem organischen oder wäßrig-organischen Lösemittel
ein Alkylsilikat und im organischen Lösemittel lösliche Aluminium- und Magnesiumsalze in einem Verhältnis
von 44 bis 65 Gewichtsprozent SiO2, 25 bis 43 Gewichtsprozent
Al3O3 und 10 bis 16 Gewichtsprozent MgO enthält.
2. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei das organische Lösemittel ein niederes Alkanol mit
1 bis 5 Kohlenstoffatomen, ein niederer zweiwertiger oder dreiwertiger Alkohol, ein niederer Alkoxyalkanol
oder ein niederes Dialkylketon ist.
3. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei
das Alkylsilikat ein Tetraalkylsilikat mit jeweils 1 bis 5 Kohlenstoffatomen in den Alkylresten ist.
4. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei das organische oder wäßrig-organische Lösemittel eine
oder mehrere Na3O, K3O, TiO- oder ZrO2 liefernde Me-
tallverbindungen enthält, die im organischen oder wäßrig-organischen
Lösemittel in einer Menge von bis zu 5 Gewichtsprozent löslich sind.
5. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei das Brennen der Formkörper bei einer Temperatur oberhalb
der Kristallisationstemperatur und unterhalb des Schmelzpunkts von Cordierit erfolgt.
6. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei die thermische Zersetzung durch Versprühen der Ausgangslösung
zusammen mit einem oxidierenden Gas aus einer Düse in eine erhitzte Reaktionszone oder in die Flamme
eines Brenners erfolgt. .
15
15
7. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei die Verarbeitung des Glaspulvers zu Formkörpern durch
Pressen, Formen, Extrudieren, Kalandern, Härten in Flüssigkeit, Flüssigtrocknen, Sprühtrocknen oder Gefriertrocknen
erfolgt.
8. Poröse Cordierit-Keramikmassen nach Anspruch 1, wobei die Hitzebehandlung bei Temperaturen unter 9500C durchgeführt
wird.
9. Mikrosphärisches, hohlkugeliges Cordieritglaspulver mit völlig porenfreier oder mit wenigen oder vielen
offenen Poren versehener Außenhaut, das durch thermische Sprühzersetzung einer Ausgangslösung in Gegenwart
eines oxidierenden Gases gebildet worden ist, wobei die Ausgangslösung in einem organischen oder wäßrig-organischen
Lösemittel ein Alkylsilikat und im organischen Lösemittel lösliche Aluminium- und Magnesiumsalze
in einem Verhältnis von 44 bis 65 Gewichtsprozent si02' 25 bis 43 Gewichtsprozent Al3O3 und 10 bis
16 Gewichtsprozent MgO enthält.
10. Glaspulver nach Anspruch 9, wobei das organische Lösemittel
ein niederes Alkanol mit 1 bis 5 Kohlenstoffatomen, ein niederer zweiwertiger oder dreiwertiger
Alkohol, ein niederer Alkoxyalkanol oder ein niederes Dialkylketon ist.
11. Glaspulver nach Anspruch 9, wobei das Alkylsilikat ein Tetraalkylsilikat mit jeweils 1 bis 5 Kohlenstoffatomen
in den Alkylresten ist.
12. Glaspulver nach Anspruch 9, wobei das organische oder
wäßrig-organische Lösemittel eine oder mehrere Na2O,
K-O, TiO2 oder ZrO2 liefernde Metallverbindungen enthält,
die in dem organischen oder wäßrig-organischen Lösemittel zu bis 5 Gewichtsprozent löslich sind.
13. Glaspulver nach Anspruch 9, wobei die thermische Zersetzung
durch Versprühen der Ausgangslösung zusammen mit einem oxidierenden Gas aus einer Düse in eine erhitzte
Reaktionszone oder in die Flamme eines Brenners [ erfolgt. L
14. Glaspulver nach Anspruch 9, wobei die Hitzebehandlung
bei Temperaturen unter 9500C durchgeführt wird.
15. Verwendung der porösen Cordierit-Keramikmassen nach
einem der Ansprüche 1 bis 8 als Träger für die Gaschromatographie.
16· Verwendung der porösen Cordierit-Keramikmassen nach
einem der Ansprüche 1 bis 8 als Träger für katalytische oder biochemische Reaktionen.