DE19628294A1

DE19628294A1 - Recyclable sticky plaster

Info

Publication number: DE19628294A1
Application number: DE19628294A
Authority: DE
Inventors: Uwe Dipl Chem Dr Skurnia; Gottfried Dipl Chem Dr Philipp; Andreas Dipl Chem In Marquardt; Manfred Gebauer
Original assignee: Zweckform Buero Produkte GmbH
Current assignee: Zweckform Buero Produkte GmbH
Priority date: 1996-07-12
Filing date: 1996-07-12
Publication date: 1998-01-15

Abstract

A pressure-sensitive adhesive plaster comprising a film with an adhesive coating on one side - uses a polyolefin-based film and a hot-melt adhesive applied by screen, gravure or flexo printing to form a 10-100 g/m<2> coating consisting of a pattern of discrete segments. Preferably a polypropylene or (preferably low density) polyethylene perforated film with a thickness of 50-120 mu is used. The pattern coating contains 100-10000 hot-melt segments per 625 mm<2> film.

Description

Diese Erfindung betrifft ein selbstklebendes Pflaster, das eine Folie und einen darauf aufgebrachten Klebstoff umfaßt.This invention relates to a self-adhesive plaster, the one Foil and an adhesive applied thereon.

Beim Aufbringen von medizinischen Pflastern auf die Haut tritt grundsätzlich das Problem auf, daß der Feuchtigkeitsaustausch der Haut mit der Umgebung unterbunden wird. Dies führt dazu, daß die Haut mazeriert, d. h. sich weißlich verfärbt und schrumpelt. Bislang hat man versucht, Pflastern eine gewisse Luftdurchlässigkeit zu vermitteln, indem man luftdurchlässige poröse Träger (z. B. ein Gewebe) vollflächig mit Klebstoffmasse beschichtete und bei der Beschichtung durch spezielle Techniken statistisch verteilte Risse und Poren erzeugte, durch die Luft hindurchtreten kann. Bei einer vollflächigen Beschichtung tritt jedoch häufig das Problem auf, daß beim Ablösen des Pflasters Klebemassenrückstände auf der Haut zurückbleiben.When applying medical plasters on the skin occurs basically the problem is that the moisture exchange the skin with the environment is prevented. This leads to, that the skin macerates, d. H. turns whitish and shrinks. So far, attempts have been made to pave a certain To convey air permeability by being air permeable Porous carrier (e.g. a fabric) with adhesive over the entire surface coated and in the coating by special techniques statistically distributed cracks and pores created by the air can step through. With a full-surface coating occurs however, the problem often arises when peeling off the patch Adhesive residues remain on the skin.

Weiterhin ist bekannt, die Luftdurchlässigkeit von Pflastern auf der Basis von Kunststoffolien dadurch zu erhöhen, daß man Löcher in die Folien stanzt.Furthermore, the air permeability of plasters is known on the basis of plastic films to increase that one Punches holes in the foils.

Als Folienmaterial für Pflaster wird kommerziell insbesondere PVC eingesetzt. PVC läßt sich jedoch wegen seines Chlorgehalts nicht problemlos recyclen oder verbrennen. Aus diesem Grund besteht Interesse an der Herstellung von Pflastern auf der Basis von Kunststoffolien, die beim Recyclen keine Probleme aufwerfen.The film material for plasters is used commercially in particular PVC used. PVC can, however, because of its chlorine content do not recycle or burn easily. For this reason there is interest in the production of plasters on the Base of plastic films, which are no problems when recycling pose.

Die Aufgabe der vorliegenden Erfindung ist, ein atmungsaktives, leicht wiederablösbares Pflaster mit einer umweltverträglichen Folie bereitzustellen, das wirtschaftlich herzustellen ist. The object of the present invention is to provide a breathable, easily removable plaster with an environmentally friendly To provide film that is economical to manufacture.

Diese Aufgabe wird durch ein selbstklebendes Pflaster gelöst, das eine Folie und einen auf einer Seite der Folie aufgebrachten Haftkleber umfaßt, dadurch gekennzeichnet, daß die Folie ein Material auf Polyolefin-Basis beinhaltet und daß der Haftkleber ein Schmelzhaftklebstoff ist, der auf der Folie ein durch Siebdruck, Tiefdruck oder Flexodruck erhältliches Raster diskreter Klebemassensegmente in einer Menge von 10-100 g/m² bildet.This task is solved by a self-adhesive plaster, one slide and one on one side of the slide applied pressure sensitive adhesive, characterized in that the film contains a polyolefin-based material and that the pressure sensitive adhesive is a hot melt pressure sensitive adhesive that is on the film one available by screen printing, gravure printing or flexographic printing Grid of discrete adhesive segments in a quantity of 10-100 g / m² forms.

Bevorzugtermaßen liegt der Schmelzklebstoff in einer Menge von 20-100 g/m², insbesondere 20-80 g/m² auf der Folie vor.The hot melt adhesive is preferably in an amount of 20-100 g / m², especially 20-80 g / m² on the film.

Als Folienmaterial kann jede Polyolefinfolie verwendet werden, die eine ausreichende Reißfestigkeit und gleichzeitig eine anwendungsgerechte Dehnfähigkeit aufweist. Diese Folien können z. B. die folgenden Additive enthalten:
Pigmente, organische Farbstoffe, Weichmacher, anorganische Füllstoffe.Any polyolefin film can be used as the film material, which has sufficient tear strength and at the same time has an elasticity suitable for the application. These foils can e.g. B. contain the following additives:
Pigments, organic dyes, plasticizers, inorganic fillers.

Es ist bevorzugt, daß die Folie aus Polyethylen oder Polypropylen, insbesondere low density polyethylene (LDPE) ist. Die Dicke der Folie beträgt bevorzugtermaßen 50-120 µm. Um den Feuchtigkeitsaustausch der Haut mit der Umgebung weiter zu verbessern, kann man eine mit Löchern versehene Folie verwenden (z. B. Perforon B der BP Chemical Plastec GmbH, eine mikroperforierte Folie, bei der die Löcher 8-12% der Gesamtfläche ausmachen). Der Durchmesser der Löcher beträgt üblicherweise 100-200 µm.It is preferred that the film be made of polyethylene or Polypropylene, especially low density polyethylene (LDPE). The thickness of the film is preferably 50-120 μm. To further the moisture exchange of the skin with the environment To improve, you can use a perforated film use (e.g. Perforon B from BP Chemical Plastec GmbH, a microperforated film with 8-12% holes Make up total area). The diameter of the holes is usually 100-200 µm.

Die Schmelzhaftklebersegmente des erfindungsgemäßen Pflasters können nach den bekannten Verfahren des Siebdrucks, Flexodrucks oder Tiefdrucks aufgebracht werden.The hot melt pressure sensitive adhesive segments of the patch according to the invention can according to the known methods of screen printing, flexographic printing or gravure.

Bei dem Siebdruckverfahren kann mit einem Flachsieb oder einem Rundsieb (Rotationssiebdruck) gearbeitet werden. Für den Flexodruck kommen Drei-Walzen-Verfahren zum Einsatz, wobei die Walzen beheizt werden. Möglich ist ebenso, anstelle von Abquetschwalzen Rakel zu verwenden. Bei dem Tiefdruckverfahren können Näpfchen-Rakelsysteme oder Näpfchen-Walzensysteme eingesetzt werden.In the screen printing process, a flat screen or a Round screen (rotary screen printing) can be worked. For the Flexo printing uses three-roll processes, whereby the Rollers are heated. It is also possible instead of Squeeze roller to use squeegee. With the gravure printing process can well-doctor blade systems or well-roller systems be used.

Die Auftragssysteme im Siebdruck, Flexodruck oder Tiefdruck können als geschlossene oder als offene Systeme vorliegen. In jedem Fall wird die Folie, die mit dem Schmelzhaftkleber beschichtet werden soll, zwischen einer Gegendruckwalze und dem Druckkörper, der den Leim aufbringt, durchgeführt. Die Punktfrequenz sowie die Größe der Schmelzhaftklebersegmente kann durch einen variablen separaten Druckkörper oder aber direkt durch das Sieb beim Siebdruck, die Näpfchen-Walze beim Tiefdruck oder die Rasterwalze beim Flexodruck gesteuert werden.The application systems in screen printing, flexo printing or gravure printing can exist as closed or open systems. In in any case, the film that comes with the hot melt pressure sensitive adhesive to be coated, between a counter-pressure roller and the Pressure body, which applies the glue, carried out. The Point frequency and the size of the hot melt pressure sensitive adhesive segments can by a variable separate pressure body or directly through the screen during screen printing, the well roller during Gravure printing or the anilox roller controlled in flexographic printing will.

Die Klebemassensegmente werden bevorzugtermaßen im Siebdruckverfahren erhalten und dabei entweder durch Direkt- oder Transferverfahren aufgebracht.The adhesive segments are preferably in Screen printing process and either by direct or transfer procedure applied.

Im Unterschied zum Direktverfahren erfolgt beim Transferverfahren der Auftrag des Schmelzhaftklebers indirekt unter Zuhilfenahme eines dehäsiv ausgerüsteten Zwischenträgers.In contrast to the direct process, the Transfer process the application of hot melt pressure sensitive adhesive indirectly with the help of an intermediate carrier that is equipped with adhesive.

Besonders bevorzugt erfolgt eine direkte Beschichtung im Rotationssiebdruck, bei dem eine rotierend nahtlose, trommelförmige, perforierte Rundschablone verwendet wird. Im Innenmantel drückt eine Beschichtungsvorrichtung die Schmelzhaftklebemasse durch die Perforation der Schablonenwand auf die Folie. Diese wird mit einer Geschwindigkeit, die der Umfanggeschwindigkeit der rotierenden Siebtrommel entspricht, mittels einer Gegendruckwalze gegen den Außenmantel der Siebtrommel geführt.Direct coating is particularly preferably carried out in the Rotary screen printing, in which a rotating seamless, drum-shaped, perforated round template is used. in the A coating device presses the inner jacket Hotmelt PSA through the perforation of the template wall on the slide. This is done at a speed that the Circumferential speed of the rotating drum corresponds to by means of a counter pressure roller against the outer jacket of the Screen drum led.

Der Pumpendruck der Dosierpumpe fördert die Schmelzhaftklebemasse durch die Löcher des Siebes an die Oberfläche der Folie. Die Folie wird entsprechend der Geometrie der Siebmaschen mit dem Schmelzhaftkleber benetzt. Wenn das sich drehende Rundsieb von der Folie abhebt, wird durch die innere Kohäsion der in den Löchern des Siebes gespeicherte Vorrat des Schmelzhaftklebers abgezogen und der auf der Folie verbleibende Teil bildet aufgrund der Oberflächenspannung Segmente mit einer breiten Basisfläche und einem Scheitelpunkt oder einer im Verhältnis zur Basisfläche schmalen Scheitelfläche, die bei der Verklebung den Kontakt zur Haut bilden. Die Form der Basisfläche ist üblicherweise kreisförmig, kann aber z. B. geringe ellipsoide Abweichungen zeigen.The pump pressure of the dosing pump promotes the Hot melt pressure sensitive adhesive through the holes of the sieve to the Surface of the film. The foil is made according to the geometry the mesh screen is wetted with the hot melt pressure sensitive adhesive. If that the rotating rotary screen is lifted off the film internal cohesion the one stored in the holes of the sieve Pulled off the supply of hot melt pressure sensitive adhesive and that on the film remaining part forms due to the surface tension Segments with a wide base area and a vertex or narrow in relation to the base area Apex surface which, when glued, contacts the skin form. The shape of the base surface is usually circular, but can e.g. B. show small ellipsoidal deviations.

Die Größe des gebildeten Klebemassensegments wird primär durch den Lochdurchmesser der Siebperforationen und die Wandstärke der Siebschablone vorgegeben. Die Basisfläche des Segments erfährt nach der Auftragung nahezu keine Verbreiterung, so daß auch bei geringen Abständen zueinander diskrete Haftklebemassensegmente erhalten bleiben.The size of the adhesive segment formed is primarily determined by the hole diameter of the perforations and the wall thickness given the sieve template. The base area of the segment experiences almost no widening after application, so that discreet even at short distances from each other PSA segments are retained.

Die Schmelzhaftklebersegmente liegen auf der Polyolefinfolie bevorzugtermaßen mit einem Raster von 100 bis 10 000 Segmenten/625 mm² (10-100 mesh), insbesondere mit 400 bis 3600 Segmenten/625 mm² (20-60 mesh), vor.The hotmelt PSA segments lie on the polyolefin film preferably with a grid of 100 to 10,000 Segments / 625 mm² (10-100 mesh), in particular with 400 to 3600 Segments / 625 mm² (20-60 mesh).

Die Schmelzhaftklebersegmente des erfindungsgemäßen Pflasters haben bevorzugtermaßen einen Durchmesser an der Basisfläche von 70 bis 1000 µm bei einer Höhe von 30-300 µm, insbesondere einen Durchmesser von 100-700 µm bei einer Höhe von 50-200 µm.The hot melt pressure sensitive adhesive segments of the patch according to the invention preferably have a diameter at the base surface of 70 to 1000 microns at a height of 30-300 microns, especially one Diameter of 100-700 µm with a height of 50-200 µm.

Der Durchmesser und die Höhe der Schmelzklebersegmente können bei der Verwendung eines Siebes durch den Lochdurchmesser der Perforation bzw. die Wandstärke des verwendeten Siebes und den Beschichtungsdruck beeinflußt werden. Der Durchmesser, die Höhe und das Verhältnis Durchmesser/Höhe hängen ferner von den rheologischen Eigenschaften, wie z. B. von der Strukturviskosität, Thixotropie und der Fließfähigkeit des verwendeten Schmelzhaftklebers ab. The diameter and the height of the hot melt adhesive segments can when using a sieve through the hole diameter of the Perforation or the wall thickness of the screen used and the Coating pressure can be influenced. The diameter, the height and the diameter / height ratio also depend on the rheological properties, such as B. from the Structural viscosity, thixotropy and the flowability of the used hot melt pressure sensitive adhesive.

Bei der Verklebung auf der Haut läßt sich das erfindungsgemäße Pflaster rückstandsfrei wiederablösen, da bei den im Siebdruck, Tiefdruck oder Flexodruck erhältlichen Schmelzhaftklebersegmenten die schmale Kontaktfläche zur Haut sich quasi als Sollbruchstelle leicht von der Haut löst, während die breite Basisfläche fest auf der Folie haften bleibt. Dieser Effekt wird durch die innere Kohäsion der Schmelzhaftklebersegmente noch verstärkt. Insbesondere bei einem Durchmesser von 70-1000 µm und einer Höhe von 30-300 µm der Schmelzklebersegmente zeigt das erfindungsgemäße Pflaster eine rückstandsfreie Wiederablösbarkeit, wenn dieses auf anderen Oberflächen als Haut haften soll, z. B. beim Befestigen medizinischer Vorrichtungen aus Stahl oder Gummi. Rückstandsfrei wiederablösbar heißt, daß der Flächendeckungsgrad der nach dem Ablösen des Pflasters auf dem Substrat zurückbleibenden Haftklebemassenrückstände weniger als 0.1%/625mm² beträgt.When glued to the skin, the invention can be Remove the plaster without leaving any residue, since Gravure or flexographic printing available Hot melt adhesive segments the narrow contact surface to the skin easily separates from the skin as a predetermined breaking point, while the broad base surface adheres firmly to the film remains. This effect is due to the internal cohesion of the Hotmelt PSA segments reinforced. Especially at a diameter of 70-1000 µm and a height of 30-300 µm of the hot-melt adhesive segments shows the plaster according to the invention residue-free detachability when this is on should stick to surfaces other than skin, e.g. B. when attaching medical devices made of steel or rubber. Removable without residue means that the Area coverage of the after removing the patch on the Residual PSA residues less than Is 0.1% / 625mm².

Die Haftkraft des erfindungsgemäßen Pflasters auf der Haut läßt sich über das Klebeverhalten auf einem Glasuntergrund abschätzen, da das Klebeverhalten auf Glas dem auf der menschlichen Haut sehr ähnlich ist. Vorteilhafterweise beträgt die Haftkraft des erfindungsgemäßen Pflasters 1,0 bis 10 N/25 mm (auf Glas) (gemessen nach der Finat-Testmethode FTM1 bei einem Abzugswinkel von 180°).The adhesive force of the patch according to the invention on the skin about the adhesive behavior on a glass surface estimate, since the adhesive behavior on glass corresponds to that on the is very similar to human skin. Is advantageously the adhesive force of the patch according to the invention 1.0 to 10 N / 25 mm (on glass) (measured according to the Finat test method FTM1 at a trigger angle of 180 °).

Überraschenderweise wurde gefunden, daß durch Wahl geeigneter Bedingungen Polyolefinfolien direkt mit dem Schmelzhaftkleber beschichtet werden können, obwohl der Erweichungspunkt von Polyolefinfolien wesentlich niedriger liegt als die Temperatur, bei der die Folie mit dem Schmelzkleber beschichtet wird. Beispielsweise beträgt der Erweichungspunkt handelsüblicher LDPE-Folien 60-90°C, während der Schmelzhaftkleber auf Temperaturen bis zu 200°C (bevorzugtermaßen 80-130°C) erhitzt wird und die Polyolefinfolie sich mit der heißen Siebdruckschablone (50-150°C, bevorzugtermaßen 80-130°C) in Kontakt befindet. Dieser vorteilhafte Befund läßt sich damit erklären, daß bei kurzen Kontaktzeiten (üblicherweise < 1/10 sec) mit der Siebdruckschablone die Polyolefinfolie eine nur geringfügige Erwärmung erfährt.Surprisingly, it was found that by choosing more suitable Conditions Polyolefin films directly with the hot melt pressure sensitive adhesive can be coated, although the softening point of Polyolefin films is significantly lower than the temperature, in which the film is coated with the hot melt adhesive. For example, the softening point is more commercially available LDPE films 60-90 ° C while the hot melt pressure sensitive adhesive is on Temperatures up to 200 ° C (preferably 80-130 ° C) heated and the polyolefin film is hot with the Screen printing stencil (50-150 ° C, preferably 80-130 ° C) in Contact. This advantageous finding can be done with it explain that with short contact times (usually <1/10 sec) with the screen printing stencil the polyolefin one only undergoes slight warming.

Die Auftragung des Schmelzhaftklebers kann somit direkt auf die unbehandelte Folie erfolgen, falls die Folie einen ausreichend hohen Erweichungspunkt aufweist und der Schmelzhaftkleber bei relativ niedriger Temperatur aufgebracht wird.The hot melt pressure sensitive adhesive can thus be applied directly to the untreated film if the film is sufficient has a high softening point and the hotmelt PSA relatively low temperature is applied.

Bei Folien mit niedrigem Erweichungspunkt kann es jedoch beim Kontakt der Walzen bzw. der heißen Siebschablone mit der glatten Folienoberfläche zum Schmelzen der Folie kommen. Um die Wärmeübertragung der Walzen auf die Folie zu minimieren, ist es daher von Vorteil, die zu beschichtende Seite der Folie vor dem Auftragen des Schmelzhaftklebstoffs aufzurauhen. Günstige Ergebnisse werden bei Rauhigkeiten von 5-50 µm, insbesondere 10-30 µm erzielt. Die Rauhigkeit wird üblicherweise durch das Ausmessen mikroskopischer Aufnahmen der Oberfläche oder durch Perthometermessungen, d. h. durch mechanisches Abtasten der Oberfläche mit einer Nadel unter Aufzeichnung der Nadelbewegungen bestimmt.However, for films with a low softening point, Contact of the rollers or the hot screen template with the smooth film surface come to melt the film. To minimize the heat transfer from the rollers to the film, it is therefore advantageous to use the side of the film to be coated roughen before applying the hot melt pressure sensitive adhesive. Favorable results are obtained with roughnesses of 5-50 µm, achieved in particular 10-30 microns. The roughness will usually by measuring microscopic images of the Surface or by perthometer measurements, d. H. by mechanical scanning of the surface with a needle underneath Record of needle movements determined.

Man kann die Folie aufrauhen, indem man sie prägt, oder indem man feststoffpartikelhaltige Lacke aufträgt. Die Lacke, die als Bindemittel für die Festoffpartikel wirken, werden aus Polyacrylaten, Polyvinylacetaten, Polystyrol-Butadien- Copolymeren und dgl. ausgewählt.You can roughen the film by embossing it or by varnishes containing solid particles are applied. The paints that as Binders for the solid particles act out Polyacrylates, polyvinyl acetates, polystyrene butadiene Copolymers and the like.

Als Feststoffpartikel eignen sich natürliche und synthetische anorganische Minerale mit einem mittleren Korngrößendurchmesser von 5-30 µm bzw. Feststoffkugeln aus Kunststoff (z. B. im Handel erhältliche sog. Abstandshalter aus Melamin- Formaldehydkondensaten, die bis 250°C temperaturbeständig sind; Durchmesser: 15 µm; Hersteller: Fa. Follmann (Minden).Natural and synthetic particles are suitable as solid particles inorganic minerals with an average grain size diameter of 5-30 µm or solid spheres made of plastic (e.g. commercially available so-called spacers made of melamine Formaldehyde condensates that are temperature resistant up to 250 ° C; Diameter: 15 µm; Manufacturer: Fa. Follmann (Minden).

Erfindungsgemäß ist es bevorzugt, Folien auf der Basis von Polyethylen oder Polypropylen einzusetzen, da diese Folien ähnlich günstige mechanische Eigenschaften aufweisen wie PVC- Folien, und eine Seite dieser Folien rauh einzustellen. Diese Vorgehensweise ermöglicht es auch, Schmelzhaftkleber mit höheren Erweichungs- und Schmelzpunkten einzusetzen, ohne Gefahr zu laufen, daß bei der Auftragung auf die Folie diese zu schmelzen beginnt.According to the invention, it is preferred to use films based on Use polyethylene or polypropylene as these films have similarly favorable mechanical properties as PVC Foils, and to set one side of these foils rough. This Procedure also allows using hot melt pressure sensitive adhesive use higher softening and melting points without There is a risk that this will apply when the film is applied begins to melt.

Insbesondere ist es bevorzugt, daß vor dem Beschichten mit dem Schmelzhaftkleber die zu beschichtende Seite der Folien Corona behandelt wird. Dies kann entweder vor und/oder nach dem Aufrauhen erfolgen.In particular, it is preferred that before coating with the Hot melt pressure sensitive adhesive the side of the Corona film to be coated is treated. This can either be before and / or after Roughening take place.

Das Pflaster kann erfindungsgemäß mit einer Geschwindigkeit von bis zu 100 m/min mit dem Schmelzhaftkleber beschichtet werden, wodurch die angestrebte Wirtschaftlichkeit gegeben ist.The patch can according to the invention at a speed of coated with the hot melt pressure sensitive adhesive up to 100 m / min, which gives the desired economy.

Der Schmelzhaftkleber wird ohne Trägersystem aufgebracht, d. h. nicht in Form einer Dispersion, einer Emulsion, eines Organisols oder Plastisols.The hot melt pressure sensitive adhesive is applied without a carrier system, i. H. not in the form of a dispersion, an emulsion, one Organisols or plastisol.

Die erfindungsgemäß verwendbaren Schmelzhaftkleber umfassen neben thermoplastischen Rückgratpolymeren gegebenenfalls die folgenden Bestandteile: Klebharze, Weichmacher, Viskositäts erniedrigende Mittel, Stabilisatoren und Füllstoffe. Im Hinblick auf die Hautverträglichkeit verzichtet man bevorzugtermaßen auf den Einsatz von Weichmachern, viskositätserniedrigenden Mitteln und Stabilisatoren, d. h. der eingesetzte Haftschmelzkleber enthält im wesentlichen nur thermoplastische Rückgratpolymere, Klebharze und gegebenenfalls Füllstoff.The hotmelt PSAs which can be used according to the invention comprise in addition to thermoplastic backbone polymers, optionally following components: adhesive resins, plasticizers, viscosity degrading agents, stabilizers and fillers. in the With regard to skin tolerance, one does not preferably on the use of plasticizers, viscosity reducing agents and stabilizers, d. H. of the Adhesive melt adhesive used essentially only contains thermoplastic backbone polymers, adhesive resins and optionally Filler.

Geeignete thermoplastische Rückgratpolymere sind z. B. synthetischer Kautschuk wie SBS (Styrol/Butadien/Styrol), SIS (Styrol/Isopren/Styrol), SEBS (Styrol/Ethylen/Butadien/Styrol), SEPS (Styrol/Ethylen/Propylen/Styrol) und S-B, S-I, S-EP; Polyacrylate wie z. B. Polybutylacrylsäureester, Poly(2- ethylhexylacrylsäureester); Polymethacrylsäureester und deren Copolymere mit z. B. Acrylsäure, Methacrylsäure, Vinylacetat, Maleinsäureanhydrid, Diacetonacrylamid oder Acrylnitril; Polyvinylderivate wie Ethylen-Vinylacetat-Copolymer, (1-Vinyl- 2-Pyrrolidon) Vinylacetat-Copolymer, Vinylavetat-Vinyllaurat Copolymer; Polyester; Copolyester wie z. B. Polyesteracrylate; Copolyetherester; oder eine Mischung daraus. Diese Rückgratpolymere können als Copolymerisate oder als Gemische untereinander vollständig vernetzt sein oder in einer mit UV- oder Elektronenstrahlung nachvernetzbaren Form eingesetzt werden.Suitable thermoplastic backbone polymers are e.g. B. synthetic rubber such as SBS (styrene / butadiene / styrene), SIS (Styrene / isoprene / styrene), SEBS (styrene / ethylene / butadiene / styrene), SEPS (styrene / ethylene / propylene / styrene) and S-B, S-I, S-EP; Polyacrylates such as B. polybutyl acrylic acid ester, poly (2- ethylhexylacrylic acid ester); Polymethacrylic acid esters and their Copolymers with e.g. B. acrylic acid, methacrylic acid, vinyl acetate, Maleic anhydride, diacetone acrylamide or acrylonitrile; Polyvinyl derivatives such as ethylene-vinyl acetate copolymer, (1-vinyl 2-pyrrolidone) vinyl acetate copolymer, vinyl acetate-vinyl laurate Copolymer; Polyester; Copolyesters such as B. polyester acrylates; Copolyetherester; or a mixture of them. This Backbone polymers can be used as copolymers or as mixtures completely networked with each other or in a UV or electron beam post-crosslinkable form will.

Im Hinblick auf die Hautverträglichkeit wählt man für den Schmelzhaftkleber vorteilhafterweise einen synthetischen Kautschuk (SIS, SBS, SEBS, SEPS, S-B, S-I, S-EP, wobei SIS und SBS besonders bevorzugt sind), Polyacrylate oder Copolyester.With regard to skin tolerance, you choose for the Hot melt pressure sensitive adhesive advantageously a synthetic Rubber (SIS, SBS, SEBS, SEPS, S-B, S-I, S-EP, where SIS and SBS are particularly preferred), polyacrylates or copolyesters.

Geeignete Klebharze sind z. B. aliphatische, alicyclische und aromatische Kohlenwasserstoffe; Polyterpene; Kolophoniumester wie Kolophonium-Glycerin-Ester, hydrierter Kolophonium- Pentaerythrit-Ester, polymerisierte Kolophonium-Glycerin-Ester, polymerisierte Kolophonium-Diethylenglykol-Ester; polymerisiertes Kolophonium.Suitable adhesive resins are e.g. B. aliphatic, alicyclic and aromatic hydrocarbons; Polyterpenes; Rosin ester such as rosin glycerin esters, hydrogenated rosin Pentaerythritol esters, polymerized rosin glycerin esters, polymerized rosin-diethylene glycol esters; polymerized rosin.

Geeignete Füllstoffe sind z. B. mineralische Stoffe wie Kaolin oder Talk.Suitable fillers are e.g. B. mineral substances such as kaolin or talk.

Bevorzugte Schmelzhaftklebstoffe sind solche, deren thermoplastische Rückgratpolymere strahlenvernetzbar sind, z. B. durch UV- oder Elektronenstrahlung. Geeignete thermoplastische Rückgratpolymere sind z. B. Polyacrylate; Polyesteracrylate; synthetische Kautschuke. Der strahlenvernetzbare Schmelzhaftklebstoff wird auf das Substrat des Flächengebildes aufgebracht und dann erst strahlenvernetzt. Gegenüber nicht nachvernetzbaren Schmelzhaftklebstoffen zeichnen sich die strahlenvernetzbaren Schmelzhaftklebstoffe durch eine merklich höhere Temperaturbeständigkeit aus. Vorzugsweise weist der Schmelzhaftkleber eine Verarbeitungstemperatur im Bereich von 50 bis 140°C auf und nach der Vernetzung einen Erweichungsbereich oberhalb von 150°C.Preferred hotmelt PSAs are those whose thermoplastic backbone polymers are radiation crosslinkable, e.g. B. by UV or electron radiation. Suitable thermoplastic Backbone polymers are e.g. B. polyacrylates; Polyester acrylates; synthetic rubbers. The radiation cross-linkable Hot melt pressure sensitive adhesive is applied to the substrate of the fabric applied and only then crosslinked by radiation. Not opposite post-crosslinkable hotmelt adhesives stand out radiation-crosslinkable hotmelt adhesives through a noticeable higher temperature resistance. Preferably, the Hot melt pressure sensitive adhesive has a processing temperature in the range of 50 to 140 ° C on and after crosslinking one Softening range above 150 ° C.

Unter den nicht nachvernetzbaren Schmelzhaftklebern sind solche bevorzugt, die im Temperaturbereich von 100-160°C eine Viskosität von etwa 1000 bis 80 000 mPa·s aufweisen.Such are among the non-post-crosslinkable hotmelt adhesives preferred, which in the temperature range of 100-160 ° C. Have viscosity of about 1000 to 80,000 mPa · s.

Besonders bevorzugt sind Ausführungsformen des erfindungsgemäßen Pflasters, bei denen die mit Schmelzhaftklebstoff beschichtete Seite der Polyolefinfolie zusätzlich mit einer Wundabdeckung versehen ist. Bei der Wundabdeckung handelt es sich üblicherweise um ein luft- und feuchtigkeitsdurchlässiges Wundkissen, das das Eindringen von Bakterien in die Wunde unterbindet und somit Infektionen verhindert.Embodiments of the plasters according to the invention, in which the Hot melt pressure sensitive adhesive coated side of the polyolefin film is also provided with a wound cover. In the Wound coverage is usually an air and moisture-permeable wound pad that prevents the penetration of Bacteria in the wound prevents infections prevented.

In der Ausführungsform ohne Wundkissen eignet sich das erfindungsgemäße Pflaster hervorragend zum Befestigen von Verbandmaterialien, kann aber auch als Klebestreifen z. B. zum Fixieren von medizinischen Werkzeugen und Vorrichtungen auf der Haut eingesetzt werden.This is suitable in the embodiment without a wound pad plasters according to the invention excellent for attaching Dressing materials, but can also be used as adhesive strips e.g. B. to Fixing medical tools and devices on the Skin can be used.

Bevorzugte Anwendungsgebiete für die Ausführungsform mit Wundabdeckung sind herkömmliche Wundpflaster, aber auch Augenpflaster, Fingerpflaster und Injektionspflaster.Preferred areas of application for the embodiment with Wound coverings are conventional wound plasters, however Eye patches, finger patches and injection plasters.

Das erfindungsgemäße Pflaster eignet sich ferner für den Einsatz von transdermalen Pflastern, keratolytischen Pflastern, Rheumapflastern oder Testpflastern, bei denen anstelle der Wundabdeckung Arzneimittelträger oder testsubstanzhaltige Träger auf das Pflaster aufgebracht werden.The plaster according to the invention is also suitable for Use of transdermal plasters, keratolytic plasters, Rheumatic plasters or test plasters where instead of the Wound cover drug carrier or test substance-containing Carrier can be applied to the patch.

Zur besseren Handhabbarkeit des Pflasters wird die mit Schmelzhaftklebstoff beschichtete Seite des Pflaster üblicherweise mit einem Trennpapier oder einer Trennfolie, meist in Form zweier Streifen abgedeckt. Gegebenenfalls können diese mit einem haftvermindernden Mittel (z. B. Silikonen, Stearylverbindungen) beschichtet werden.For better manageability of the patch is the Hot melt adhesive coated side of the patch usually with a release paper or film, usually covered in the form of two strips. If necessary, you can these with an adhesion-reducing agent (e.g. silicones, Stearyl compounds) are coated.

Weiterhin ist von Vorteil, wenn im Abschluß an das Herstellungsverfahren das erhaltene Pflaster sterilisiert wird. Dies kann z. B. durch γ-Strahlen oder die Behandlung mit Ethylenoxidgas erreicht werden.It is also an advantage if at the end of the Manufacturing process, the patch is sterilized. This can e.g. B. by γ-rays or treatment with Ethylene oxide gas can be achieved.

Die Möglichkeit, Polyolefinfolien mit Schmelzhaftklebern im Direktverfahren zum erfindungsgemäßen Pflaster zu beschichten, und die erzielbaren hohen Produktionsgeschwindigkeiten gewährleisten eine ausgezeichnete Wirtschaftlichkeit. Da der Schmelzhaftkleber nicht in einem Trägersystem vorliegt, d. h. nicht dispergiert oder emulgiert ist, kann man auf den unweltbelastenden und energieverbrauchenden Einsatz von Lösungsmitteln verzichten. Ferner ist es im Hinblick auf die Wirtschaftlichkeit des Pflasters von Vorteil, daß beim Verfahren zu seiner Herstellung keine energieverbrauchenden Trocknungsschritte, wie beim Einsatz organischer oder wässeriger Dispersionen/Emulsionen, notwendig sind. Ferner hat die Auftragung von Dispersionen/Emulsionen den Nachteil, daß das Substrat durch Dispersions/Emulsionsmittel oder durch die Trocknungsschritte ungünstig beeinflußt werden kann.The possibility of polyolefin films with hot melt pressure sensitive adhesives in the To coat direct processes for the plaster according to the invention, and the achievable high production speeds ensure excellent economy. Since the Hot melt pressure sensitive adhesive is not present in a carrier system, i. H. is not dispersed or emulsified, you can on the environmentally harmful and energy consuming use of Avoid solvents. It is also in terms of Profitability of the patch is advantageous in that Process for its production no energy consuming Drying steps, such as when using organic or aqueous dispersions / emulsions are necessary. It also has the application of dispersions / emulsions has the disadvantage that the substrate by dispersion / emulsion means or by the Drying steps can be adversely affected.

Die im Siebdruck, Tiefdruck oder Flexodruck erhältlichen Segmente des erfindungsgemäßen Pflasters bilden auf der Pflasteroberfläche Kanäle, über die ein Feuchtigkeitsaustausch zwischen der Haut und der Umgebung stattfinden kann. Das Pflaster ist daher atmungsaktiv und trägt sich sehr angenehm auf der Haut. Dieser Effekt kann durch Löcher in der Folie noch verstärkt werden. Die diskreten Segmente des erfindungsgemäßen Pflasters gewährleisten überdies auch nach längerem Tragen das leichte Wiederablösen des Pflasters von der Haut, ohne daß Klebemasse zurückbleibt.Those available in screen printing, gravure printing or flexo printing Segments of the patch according to the invention form on the Pavement surface channels through which moisture exchange between the skin and the environment. The The plaster is therefore breathable and very comfortable to wear on the skin. This effect can still be caused by holes in the film be reinforced. The discrete segments of the invention Patches also ensure that even after prolonged wear easy removal of the patch from the skin without Adhesive remains.

Die erfindungsgemäß verwendeten Polyolefinfolien lassen sich problemlos und umweltschonend recyclen.The polyolefin films used according to the invention can be Recycle easily and environmentally friendly.

Die vorliegende Erfindung wird durch das folgende Beispiel näher erläutert.The present invention is illustrated by the following example explained in more detail.

example

Einer durch Corona-Entladung vorbehandelten LDPE-Folie (Medifol der BP-chemicals, Plastec GmbH, D-83502 Wasserburg; Typ 44527: Flächengewicht 66 g/m², Dicke 87 µm) mit einem Erweichungspunkt von 90°C wurde durch Prägung eine Rauhigkeit von 25 µm verliehen. Diese Folie wurde in einer Rotationssiebdruckanlage unter Verwendung eines 40 mesh-Siebes mit einer Wandstärke von 0.2 mm und mit einem Lochdurchmesser von 0.3 mm mit einem Schmelzhaftkleber beschichtet. Als Schmelzhaftkleber verwendete man PS 9004 der Fa. Novamelt Research GmbH auf der Basis eines SIS (Styrol/Isopren/Styrol)-Blockcopolymers. Dieser Schmelzhaftkleber wies einen Schmelzpunkt von 108-110°C (gemessen nach ASTM 2398) und eine Viskosität von 55 000 mPa·s bei 150°C auf. Die Folie wurde mit einer Beschichtungsgeschwindigkeit von 30 m/min und bei einer Temperatur der Siebschablone von 108°C mit dem auf 155°C erwärmten Schmelzhaftkleber bei einem Beschichtungsdruck von 1 bar rasterförmig beschichtet (1600 Segmente/625 mm²). Die Haftklebstoffmenge auf der Pflasteroberfläche lag bei 31 g/m². Der Durchmesser der Basisfläche der Klebstoffsegmente betrug 0.450 mm und die Höhe der Segmente 0.112 mm. Das so hergestellte Pflaster wies eine Haftkraft von 3.5 N/25 mm auf Glas ( 2.8 N/25 mm auf Stahl, 8.1 N/25 mm auf Gummi, 1.2 N/25 mm auf der Rückseite der Folie) auf. Die Werte beziehen sich auf die Finatprüfmethode FTM1 bei einem Abzugswinkel von 180°.An LDPE film pretreated by corona discharge (Medifol BP-chemicals, Plastec GmbH, D-83502 Wasserburg; Type 44527: Weight 66 g / m², thickness 87 µm) with a softening point of 90 ° C was a roughness of 25 microns by stamping awarded. This film was in a rotary screen printing machine using a 40 mesh screen with a wall thickness of 0.2 mm and with a hole diameter of 0.3 mm with a Hot melt pressure sensitive adhesive coated. Used as hot melt pressure sensitive adhesive man PS 9004 from Novamelt Research GmbH on the basis of a SIS (styrene / isoprene / styrene) block copolymer. This Hot melt pressure sensitive adhesive had a melting point of 108-110 ° C (measured according to ASTM 2398) and a viscosity of 55,000 mPa · s at 150 ° C. The film was covered with a Coating speed of 30 m / min and at a Temperature of the screen template from 108 ° C to 155 ° C heated hotmelt PSA at a coating pressure of 1 bar coated in a grid pattern (1600 segments / 625 mm²). The The amount of pressure sensitive adhesive on the plaster surface was 31 g / m². The diameter of the base area of the adhesive segments was 0.450 mm and the height of the segments 0.112 mm. The so made Patches had an adhesive force of 3.5 N / 25 mm on glass (2.8 N / 25 mm on steel, 8.1 N / 25 mm on rubber, 1.2 N / 25 mm on the Back of the film). The values refer to the Finite test method FTM1 with a trigger angle of 180 °.

Claims

1. Self-adhesive plaster comprising a film and a pressure sensitive adhesive applied to one side of the film, characterized in that the film contains a polyolefin-based material and that the pressure sensitive adhesive is a hot melt pressure sensitive adhesive which is applied to the film by screen printing, gravure printing or flexographic printing available grid of discrete adhesive segments in an amount of 10-100 g / m².

2. Self-adhesive plaster according to claim 1, characterized characterized in that the film is a polyethylene or Is polypropylene film.

3. Self-adhesive plaster according to claim 2, characterized characterized in that the polyethylene film is an LDPE film is.

4. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the Film has a thickness of 50-120 microns.

5. Self-adhesive patch according to one or more of the preceding claims, characterized in that the Is provided with holes.

6. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the Grid 100-10,000 hot melt adhesive segments / 625 mm² foil includes.

7. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the Hot melt pressure sensitive adhesive in the form of segments with a diameter of the base area of 70-1000 µm and one Height of 30-300 microns is present.

8. Self-adhesive patch according to one or more of the preceding claims, characterized in that the Hot melt pressure sensitive adhesive a synthetic rubber Poly (meth) acrylate, a polyvinyl derivative, a polyester, a copolyester, a copolyetherester, or a mixture from it.

9. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the patch has an adhesive force of 1.0-10 N / 25 mm on glass, measured according to the finite test method FTM1 at an angle of 180 °.

10. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the side of the film coated with hot melt pressure sensitive adhesive is provided with a wound covering.

11. Self-adhesive plaster according to one or more of the preceding claims, characterized in that the side of the film coated with hot melt pressure sensitive adhesive Release paper or release film is covered.