Número de publicaciónEP0000949 A1
Tipo de publicaciónSolicitud
Número de solicitudEP19780100752
Fecha de publicación7 Mar 1979
Fecha de presentación25 Ago 1978
Fecha de prioridad26 Ago 1977
También publicado comoCA1122353A, CA1122353A1, DE2862259D1, EP0000949B1, US4167045
Número de publicación1978100752, 78100752, 78100752.1, EP 0000949 A1, EP 0000949A1, EP-A1-0000949, EP0000949 A1, EP0000949A1, EP19780100752, EP78100752
InventoresPhilip Nicholas Sawyer
SolicitantePhilip Nicholas Sawyer
Exportar citaBiBTeX, EndNote, RefMan
Enlaces externos:  Espacenet, Registro europeo de patentes
Cardiac and vascular prostheses and methods of making the same
EP 0000949 A1
Resumen
Cardiac and vascular prostheses and methods of making the same. The prostheses are suitable for implantation in a bloody environment. The prosthesis includes a surface material adapted for exhibiting a regular and periodic surface charge characteristic in the bloody environment (See Fig. 1A: scanning electron micrographs of an albumin Dacron hybrid graft). A prothesis means supports the surface material and is adapted to perform a prosthetic function in the bloody environment. In cases where cross- linking is desired and the surface material cannot cross-link with the substrate material, an adaptive material is provided which cross-links both to the surface material and to the material of the prothesis.
Imágenes(13)
Previous page
Next page
Reclamaciones(20)
1. A prosthesis suitable for implantation in a bloody environment, particularly for cardiac and vascular implants, said prosthesis comprising a surface material adapted for exhibiting a regular and periodic surface charge characteristic in said environment, and prosthesis means supporting said surface material and adapted to perform a prosthetic function in said environment.
2. A prosthesis as claimed in claim 1, wherein said prosthesis means is of a material normally incapable of cross- linking to said surface material, comprising an adaptive material to cross-link to the material of said prosthesis means and to said surface material to provide architectural continuity therebetween while preserving said surface charge characteristic.
3. A prosthesis as claimed in claim 2, wherein said adaptive material is glutaraldehyde or a succinic acid compound.
4. A prosthesis as claimed in claim 2, wherein said surface charge is equivalent to approximately one electron per thousand square Angstroms in a regular three-dimensional pattern.
5. A prosthesis as claimed in any of claims 1 to 4, wherein said surface material is aluminum, a protein, agar or acrylamide.
6. A prosthesis as claimed in claim 5, wherein said pro- . tein is albumin, gelatin or collagen.
7. A prosthesis as claimed in claim 5, wherein said surface material is albumin combined with gelatin.
8. A prosthesis as claimed in any of claims 1 to 7, wherein said prosthesis means is of Dacron.
9. A prosthesis as claimed in claim 8, wherein said Dacron is of a woven structure.
10. A method of preparing a prosthesis for functioning in a bloody environment with minimal thrombogenicity said method comprising depositing on the surface of the prosthesis means a material adapted for exhibiting a regular and periodic suface charge in said environment.
11. A method as claimed in claim 10, wherein said surface material is normally incapable of cross-linking to said prosthesis means comprising cross-linking the said material to said prosthesis means with an adaptive material.
12. A method as claimed in claim 11, wherein said adaptive material is glutaraldehyde or a succinic acid compound.
13. A method as claimed in any of claims 10, 11 or 12, wherein said surface material is aluminum, a protein, agar or acrylamide.
14. A method as claimed in claim 13, wherein said protein is albumin, gelatin or collagen.
15. A method as claimed in claim 13, wherein the said surface material is albumin combined with gelatin.
16. A method as claimed in claim 13, wherein said surface material is a protein and is applied in about 3 % solution.
17. A method of adapting a synthetic material for use as a prosthetic material adapted to function in a bloody environment, said method comprising metallizing the material at the surface thereof.
18. A method as claimed in claims 13 or 17, comprising vapor depositing aluminum on said prosthesis means.
19. A method as claimed in claims 13 or 17, comprising spraying aluminum in an aerosol on said prosthesis means.
20. A method as claimed in any of claims 10 to 19, wherein the prosthesis means is of woven Dacron.
Descripción
    Field of Invention
  • [0001]
    This invention relates to cardiac and vascular prostheses and methods of making the same and materials therefor.
  • Background of the Invention
  • [0002]
    The major emphasis in early research on implants was performed within the field of orthopedics. (Bechtol, C. D., Ferguson, Jr., A. B., and Laing, P. G. Metals and Engineering in Bone and Joint Surgery. Williams and Wilkins Co., Balt. Chapter 1, 1-18 (1959); Scales, J. T. Arthroplasty of the Hip Using Foreign Materials: A History, Paper 13, A Symposium, Institute of Mechanical Engineers, Vol. 181 Part 3J. 63-84, (1967); Weisman. S. Metals for Implantation in the Human Body. Ann. N.Y. Acad. Sci. 146, 80-95, (1968)). The most significant addition to implant surgery in the last twenty years has been the development of prostheses for vascular and cardiac reconstruction (Wesolowski, S.A., Martinez, A., and McMahone, J. D. The Use of Artificial Materials in Surgery, "Current Problems in Surgery." Year Book Medical Publishers, Inc., Chicago (1966). A major problem involved in the use of prosthetic alloplastic materials has been severe occlusive thrombogenicity (Hufnagel, C. A. The Use of Rigid and Flexible Plastic Prostheses for Arterial Replacement, Surgery, 37:165, (1955) ). The search for acceptable materials and designs for vascular prostheses was of great importance because of a number of problems which were encountered with the use of polymeric and metal prostheses, autologous, homologous and heterologous bypass grafts in man. (Johnson, W. D. Auer, J. E. and Tector, A. T., Late Changes in Coronary Vein Grafts, Am. Jour. of Cardiol. 26: 640, (1970) and Artegraft Conference, Johnson and Johnson, Toronto, Ontario, Canada, June 23, (1973)).
  • [0003]
    Following the development of open heart surgery, an enormous effort was made in the field of prosthetic heart valves. The first successful development in this area was made by Goodman, Berg and Stuckey (Wesolowski, C. A. eL al. The Use of Artificial Materials in Surgery, "Current Problems in Surgery" Year Book Medical Publishers, Inc., Chicago (1966). They produced the first completely thromboresistant prosthetic heart valve. This valve was later improved by Dr. Albert Star and Edwards Laboratories (Edwards, W. S. and Smith, L. Aortial Valve Replacement with a Sub Coronary Ball Valve. Sur. Forum 9:309 (1958); Starr, A. Mitral Valve Replacement with a Ball Valve Prosthesis. British Heart Journal, 33 Supp. 47 (1971). A number of valves were further developed by several corporations. These included the Bjork-Shiley valve which is the most successful of the prosthetic heart valves available today. More recently, glutaraldehyde tanned porcine collagen prosthetic heart valves developed by the Hancock Laboratory (Sauvage, L. R. Wesolowski, A. S., Sawyer, P. N. et al. Prosthetic Valve Replacement Ann. of the N. Y. Academy of Sci. 146:289 (1968)) have proven useful. They are resistant to intravascular thrombosis and have maintained their tensile strength following several years of implantation in man. Thus, a host of glutaraldehyde tanned collagen valvular prostheses have proven useful in man with respect to long term function and resistance to thrombosis.
  • [0004]
    Early attempts to replace blood vessels in man involved the use of rigid tubes of gold, silver, aluminum, magnesium, as well as the later development of polyethylene and polymethyl acrylic tubes (Szilagayi, D. E. Long Term Evaluation of Plastic Arterial Substitutes: An Experimental Study, Surg. 55:165 (1964); Woodward, S. C. Biological End Points for Compatibility, Plastics in Surgical Implants ASTM-STP 386, A Symposium on Surg. Implants, Indianapolis, Indiana (1964); Sawyer, P. N.,Wu, K. T., Wesolowski, A. S., Brattain, W. H. and Boddy, P. J. Long Term Patency of Solid Wall Vascular Prostheses, Arch. Surg. 91:735, (1965). In the majority of cases, these prostheses did not function satisfactorily. A major breakthrough came in 1952 when Voorhees and Blakemore described their experiments with a cloth prosthesis of Vinyon. (Voorhees, A. B., Jr., Jaretski, 111, A. and Blakemore, A. H. Use of tubes constructed from Vinyon-"N" Cloth in bridging Arterial Defects. Ann. Surg. 135; 332 (1952)). This material was easy to handle, preclottable and resistant to thrombosis following implantation, although tensile strength, in situ, was lost with the passage of time. Preclotting the graft with the patient's blood produced a compound prosthesis, whereby, the lumen was covered by a fibrous neo-intima and the adventitia was enclosed by a fibrous capsule, which resulted in a well tolerated graft. Presently, the Dacron graft is considered to be the most successful cloth type graft. (Sawyer, P. N. et al. Vascular Graft Symposium, Current Status and Future Trends. NIH (1976)).
  • [0005]
    Early attempts at vessel substitution with materials of biological origin were carried out using arteries from cadavers (Wesolowski, S. A. and Sauvage, L. R. Hetero- logus Aortic Hetergrafts with Special Reference to Recipient Site, Ethylene Oxide Freeze Dry Preparation and Specied of Origin, Ann. Surg. 145:187 (195 ). On the whole, these homografts functioned well for a period of time, but were soon replaced by fibrous tissue and calcium salts. This resulted in an inelastic structure, susceptible to thrombus, fracture, and aneurysm formation (Sauvage, L. R. and Wesolowski, A. S. Healing and Fate of Arterial Grafts, Surg. 38:1090 (1955)).
  • [0006]
    Following failure of the homografts, autografts from a patient's veins (saphenous) were used. Currently, the implantation statistics show that the saphenous vein is superior to synthetic implants (Sawyer, P. N. et al, Vascular Graft Symposium;Sauvage, L. R. and Wesolowski, A. S. Healing and Fate of Arterial Grafts, supra, and Vladamer, C. and Edwards, J. E. Pathological Changes in Aortocoronary Arterial Saphenous Vein Grafts. Circulation 44:719 (1971)). When the saphenous vein is not available, i.e., the question arises as to which implant should be used. Experience has shown that a vascular graft must: (i) have an appropriate porosity (10,000-20,000 ml of water/square cm/minute) Sawyer, P. N., Wu, K. T., Wesolowski, S. A. Brattain, W. and Boddy, P. J. An Aid in the Selection of Vascular Prosthesis Proc. Natl. Acad. Sci., U.S.A., 53:1965), (ii) be blood compatible, (iii) possess tensile strength and (iv) be easy to handle with respect to sewing characteristics (Sawyer, P. N. and Srinivasan, S. New Approaches in the Selections of Materials Compatible with Bluod. Artificial Heart Prog.Conf.Proc.Chapter 2,1969).
  • [0007]
    In an effort to overcome the problems of porosity, junctional thrombosis, and small diameter compliance exhibited by most implants in the periphery, I have conducted research on copolymeric collagen remnants from bovine carotid and brachial arteries. The collagen remains intact following enzymatic digestion (ficin) and is then glutaraldehyde tanned and negatively charged.
  • [0008]
    When implanted, these grafts reveal a striking tendency to remain thromboresistant and maintain their tensile strength as opposed to other commerically available collagen grafts that possess a limited degree of patency with early loss of tensile strength. My copolymeric grafts have remained patent in the femoral-popliteal, carotid and coronary positions (Vascular Graft Symposium, supra).
  • [0009]
    As to why these types of grafts perform so well, conclusive answers are not yet available. Scanning electron microscopic studies indicate that when the grafts fail, they become occluded by an atypical thrombus. It is therefore obvious that the success of this type of graft depends upon (i) the surface modification characteristics of the collagen (ii) blood interfacial reactions' occurring, (iii) structural aspects of the collagen surface.
  • SUMMARY OF THE INVENTION
  • [0010]
    I have heretofore developed a negatively charged, glutaraldehyde tanned collagen copolymeric vascular bypass graft This new graft appears to be superior to other commerically available bypass heterografts based upon life analysis tables. The processes used to chemically modify the collagen are uniquely versatile.
  • [0011]
    I am now working with second and third generation grafts and have produced Dacron* hybrid grafts of several types. The application of this graft is aimed at specific clinical problems where the saphenous vein or conventional heterografts would be considered unsatisfactory. The hybrid graft can also be applied to the total artificial heart and bypass pump chambers and Dacron skirt of heart valves providing a more satisfactory blood compatible surface.
  • [0012]
    Dacron vascular grafts have been altered, in accordance with the invention, by coating them and filling their interstitial spaces with a variety of agents, in a variety of ways, to produce grafts with superior anti- thrombogenic characteristics.
  • [0013]
    The techniques utilized include: (1) copolymerization of proteins to the Dacron with glutaraldehyde and subsequent negative charging, (2) aluminization of the grafts,
  • [0014]
    *Registered Trademark for a Polyester of terephthalic acid and ethylene glycol manufactured by DuPont de Nemours & Co., Inc., Wilmington, Delaware, U.S.A.
  • [0015]
    (3) the deposit of substances which may accept from a bloody environment materials which are compatible with the environment.
  • [0016]
    It is an object of the invention to provide an improved prosthesis material for making an improved prosthesis and method for making the same.
  • [0017]
    It is another object of the invention to provide for improved prosthesis characteristics in a blood environment.
  • [0018]
    To achieve the above and other objects of the invention there is provided a prosthesis suitable for implantation in a bloody environment, said prosthesis comprising a surface material adapted for exhibiting a regular and periodic surface charge characteristic in said bloody environment, and prostheses means supporting said surface material and adapted to perform a prosthetic function in this environment.
  • [0019]
    In accordance with one embodiment of the invention, the surface material may be aluminum. In accordance with another embodiment, the surface material may be albumin. In accordance with still other embodiments, the surface material may be agar or acrylamide.
  • [0020]
    In accordance with one aspect of the invention, the prosthetic means is of a material normally incapable of crosslinking to said surface material. In this case, there is provided an adaptive material to cross-link to the material of said prosthetic means and to said surface material to provide architectural continuity therebetween while preserving said surface charge characteristics.
  • [0021]
    In accordance with the invention and the preferred embodiment thereof, the surface charge is preferably equivalent to approximately one electron per thousand square Angstroms in a regular three-dimensional pattern.
  • [0022]
    According to the invention, there is provided a method for preparing a prosthesis for functioning in a bloody environment with minimal thrombogenicity. This method comprises depositing on the surface of the prostheses a material adapted for exhibiting a regular and periodic thrombosis resistant surface charge in the bloody environment. Thus, for example, a synthetic material may be adapted for use as a prosthetic material which is adapted to function in a bloody environment. This may be achieved, for example, by metallizing the material at the surface thereof.
  • [0023]
    According to one embodiment of the invention, the metallizing may take place by the vapor depositing of aluminum on the surface.
  • [0024]
    According to another embodiment, the aluminum may be sprayed in an aerosol on the surface.
  • [0025]
    The prosthesis may be, for example, of woven Dacron. Thereupon may be deposited a surface material in the form of albumin, combined with gelatin. The thusly coated prosthesis may, for example, thereafter be treated with glutaraldehyde. The material deposited on the prosthesis may be , for example, of the general category of proteins and may be applied preferably in, for example, about a 3 % solution.
  • [0026]
    According to the further feature of the invention, a thusly coated prosthesis may be further treated with a succinic acid compound.
  • [0027]
    According to still further aspects of the invention, the material may be applied by immersing the prosthesis in a slurry of agar. As an alternative, the prosthesis may be immersed in a solution of acrylamide.
  • [0028]
    The above and further objects and features of the invention will be found in the detailed description thereof as follows hereinafter.
  • BRIEF DESCRIPTION OF DRAWING IN THE DRAWING:
  • [0029]
    • Figure l(A) is a scanning electron microphotograph group of a polarized protein;
    • Figure l(B) is a collection of scanning electron micrographs of a protein-gelatin Dacron hybrid graft;
    • Figure 2(A) shows scanning electron micrographs of a gelatin-Dacron hybrid graft;
    • Figure 2 (B) is a group of scanning electron micrographs of a gelatin-Dacron hybrid graft;
    • Figure 3(A) shows the structure of an agar coated graft;
    • Figure 3(B) shows the implantation results of a protein-gelatin Dacron hybrid graft;
    • Figure 4 is a group of scanning electron micrographs of an aluminum coated Dacron hybrid graft;
    • Figure 5 shows scanning electron micrographs of an agar coated Dacron hybrid graft;
    • Figure 6(A) shows an aluminum coated Dacron prosthesis exposed to blood for one second; and
    • Figure 6(B) shows further magnification of the prosthesis illustrated in Fig. 6(A).
  • DETAILED DESCRIPTION
  • [0030]
    As has been stated hereinabove, the invention relates to the provision of a prosthesis having the capability of fuctioning in a bloody environment. The prosthesis may be of varying types but it can be for example, a vascular prosthesis consisting of a tube adapted to function as a connection for bypass or a valve functioning to operate in the cardiac environment.
  • [0031]
    The invention is based in general on having the prosthesis exhibit a regular and periodic negative surface charge characteristic in the preferred case approximating one electron per thousand square Angstroms of surface in a regular threedimensional pattern. Under certain circumstances, the regular and periodic surface charge may be positive.
  • [0032]
    A surface material will generally be employed to exhibit the above-noted characteristic. For this reason, the present invention is concerned with hybrid prostheses which are prostheses consisting of a basic material forming a prosthesis so that it is capable of performing the desired function and a surface material which exhibits the aforenoted charge.
  • [0033]
    In case the basic material is incapable of crosslinking with the surface material, an adaptive material may be provided to offer architectural continuity and cross-link the surface material and the supporting material by being adapted to cross-link itself respectively to each of these materials.
  • [0034]
    The invention offers, for example, copolymerization for a form of protein deposition, metallizing, agar application in the form of a uniform coating and the application of, for example, acrylamide. The invention offers further selective processing of certain of the above materials by treatment with succinic acid or the like or, for example, by treatment with glutaraldehyde.
  • [0035]
    The following are details of materials and methods which may be employed in accordance with the above: Copolymerization (a method of protein deposition) Fraction V Albumin (purified bovine or other mammalia albumin) purchased from Sigma Corporation, St. Louis, Mo.,USA was dissolved (1, 3, 5 and 10 grams in 100 ml. of water) to produce several solutions of 1 % - 10 % with distilled and deionized water Gelatin (cutaneous), purchased from Baker Corporation*, was dissolved at room temperature in water, producing solutions ranging in concentration (1, 3, 5 and 10 grams in 100 ml of water) from 1 % - 10%.
  • [0036]
    A Microknit® knitted or woven vascular prosthesis (Go- laski Labs. Inc. of Philadelphia, Penna.USA) possessing 18 ridge to the inch (50 interstices per inch) was cut into 10 cm. segmen (collapsed length) and cleaned in distilled and deionized water. It is then immersed in 10-20 % (preferably 20%) qlutaraldehyde (purchased from Electron Microscope Science Corporation of Fort Washington Penna., USA) with distilled and deionized water (40 ml of 50 % glutaraldehyde in 60 ml of water) and was allowed to stand for three hours.
  • [0037]
    The graft materials were then immersed in the appropriate protein (albumin, gelatin, collagen or the like) solution until thin (1 to 2,000 microns) coats of polymerized protein surrounded the Dacron tube. They were then suspended in air at room temperature and rinsed with water at room temperature for a minimum of 2 minutes. Care was taken to rinse the lumen of the grafts with water. The graft-protein "hybrid" prostheses were then reintroduced into fresh (20%) glutaraldehyde (40 ml of 50 % glutaraldehyde in 60 ml of water) for 5-15 minutes. The process was repeated several times (three to ten times) until thin (1 to 2000 microns), uniformly coated grafts with their interstitial spaces filled were produced.
  • [0038]
    * J. T. Baker Chemical Co., Phillipsburgh, New Jersey,USA.
  • Dacron Backbone Structure
  • [0039]
    Several types of grafts and varying concentrations of proteins were utilized to determine optimal reaction condition. They included 3 and 6 mm. I.D. (2-20 mm is the range), 18 and 32 ridges/inch (10-32 ridges would be the range), and 1, 3, 5 and 10 % protein solutions. It was found that the grafts possessing 18 ridges/inch (half crimp) were the optimal type of graft to modify, as they possessed the best surface configuration to provide for an even deposition of protein. The grafts having 32 ridges/inch (full crimp) had to be stretched on a glass rod of the same I.D. as the grafts in order to coat them properly. This prevented intra lumen coating and produced cracking when the rod was removed and the grafts regained their original shape. It was further found that a 3 % solution of protein provided the most effective coating both in optimizing time to coat and in thickness. One percent took a much longer time period to coat (greater than 1 hour). A 10 % coating was achieved within 30 seconds but was very thick and did not permit obtaining the amount of flexibility required. In the aforegoing, the range of depth of the crimps is about 1 to 2 mm and the wall thickness of the grafts is about 1/2 to 1 mm. Using the techniques described above (i.e., 3 % protein solutions and half crimped grafts) it was possible to coat both 3 mm and 6 mm I.D. grafts without difficulty.
  • Chemical Modification
  • [0040]
    The protein copolymerized hybrid grafts were further modified to enhance their net negative surface charge.
  • [0041]
    The end terminal amino acid residues were covalently coupled to succinic acid under acetylation reaction conditions (see Pat. No. 3,927,422). The grafts were rinsed thoroughly with distilled deionized water, and placed into a 10 % (8-10 % range) sodium bicarbonate buffer at a pH 8.5 (8.2-8.7 range) (8-10 grains in 100 ml of water). The grafts were allowed to equilibrate with the buffer (5-30 minutes at 17-27°C) then ground solid succinic anhydride was added in 5 mg portions (range 2-5 grams) to the buffer such that the final succinate solution concentration would be 1 M, (range: 1 to 5 molar) (2 to 8 micromoles of succinate per gram of protein). The reaction was sufficiently vigorous to perfuse the lumen of the grafts. Several aliquots (range: 3 to 5) of the solid anhydride were added directly into the lumens of the grafts which were then placed into the buffer. At the conclusion of the reaction (i.e., cessation of effervescence), the grafts were retested on a Zarb hydrostatic testing apparatus to ascertain structural integrity of copolymerization. The grafts were recoated if necessary and then stored and sterilized in 10 % (range 3 - 10 %) glutaraldehyde.
  • Acrylamide Hybridization
  • [0042]
    Acrylamide was prepared in accordance with the method of Davis et al. A solution which would yield 7 % (range: 5 to 8 %) gel was utilized. The graft was immersed into solution and was allowed to polymerize. The graft was removed, washed with distilled deionized water and stored in 40 % ETOH and water.
  • [0043]
    More particularly, a 20 ml solution of 28,0 g of acrylamide (Bio-Rad Labs of Richmond, Ca.) and .735 g of bis-acrylamide (Bio-Rad Labs of Richmond, Ca.) were added to a 20 ml solution containing 1 N. HC1, 48.0ml/100 ml., 36.3 g/100 ml of TRIS (Bio-Rad Inc. of ) and 0.723 ml of TEMED/100 ml.
  • [0044]
    A segment ot graft material was added to the acrylamide solution and allowed to equilibrate for one hour (1/2-1 hours at room temperature). At that time, a 40 ml solution of ammonium persulfate, 1 mg/ml, (Bio-Rad Labs of Richmond, Ca.) was added to the acrylamide-bis-acrylamide solution in order to polymerize the solution. The solution was allowed to gel at room temperature for 1/2 hour (range: 10-40 minutes). During this time interval, the graft was removed and reintroduced into the gelling medium 10 (range: 10 to 20) times. The graft was removed after the solution began to gel but before a solidified gel could form. The graft was then placed into a new test tube, and the acrylamide which had coated the Dacron fibers was allowed to gel. After the acrylamide polymerized, the graft was perfused with water at room temperature for 1 hour (range: 1/2 to 1 hour).
  • Agar Hybridization
  • [0045]
    A 3 % agar-water mixture (Difco Labs, Detroit,Mich. USA) was made and heated to 100°C until a uniform (aggregate free) slurry was evident. The graft material, washed three to ten times in distilled and deionized water, was immersed in the agar slurry until it was uniformly coated (100-2,000 microns). It was then kept at 4°C (range: 4-10°C) until the agar congealed. The graft was removed, washed and stored in 40 % ethanol-H20 until used.
  • Method of In Vitro Testing
  • [0046]
    All hybrid grafts underwent hydrostatic testing using a Zarb hydraulic pressure tester. The criterion used was the ability to withstand 30 mm (range 20-50) of Hg pressure without showing evidence of air leaks through the graft pores.
  • [0047]
    If a graft failed because of leaks during the test procedure, it was recoated by the process described above until there was no evidence of leakage. The hybrid grafts were stored in 10 % glutaraldehyde until used.
  • Aluminization
  • [0048]
    Two techniques of coating a Dacron prosthesis with aluminum were utilized. They were: (1) vapor deposition and (2) hot plasma spray technique.
  • Vapor Deposition
  • [0049]
    Vapor deposition was accomplished in vacuum at 10-5 Torr. The aluminium vapor was forced through a small opening ( .25 to 20 mm) in a heat shield and deposited on a Dagron graft in a thin, uniform coat of 1/2 to 10 microns.
  • [0050]
    This technique proved to be the best technique for coating Dacron tubular material with aluminum as it provides a vapor which coats the graft completely with localized over concentration.
  • Hot Plasma Spray
  • [0051]
    Aluminium powder is heated to its melting points and is then sprayed by a pressurized aerosol-like container. This is repeated until a thin coating (1/2 to 10 microns) of aluminum is observed on the Dacron.
  • Implantation Studies
  • [0052]
    Implantation studies were divided into chronic and short term evaluation of hybrid graft materials.
  • [0053]
    Three and four mm hybrid grafts were sutured (implanted) into the carotid and femoral arteries of dogs for periods ranging from 1 second to 2 months. (1 second, 2 hours, 1 week, 1 month, 2 months).
  • [0054]
    Six mm hybrid grafts were implanted into the abdominal aorta of dogs for time periods ranging from 1 month to 1 year (1 month, 6 months, 9 months, 1 year).
  • [0055]
    The hybrid grafts were removed from their sterile solutions and placed into a sterilized 500 ml beaker and sequential washed with 250 ml of sterile saline 20 x. The grafts were then placed into a sterile stainless steel bin containing 1.5 liters of sterile saline, until placed in a sterile field and implanted.
  • [0056]
    Prior to implantation, the end pieces were cut to provide an even surface for anastomosis and samples for controls, culturing and SEM studies to determine efficiency of coating and fuction.
  • [0057]
    End-to-end anastomosis was carried out using a running Carrell suture with 4-0 cardiovascular Dacron or other material. Precise anastomosis was carried out in all cases.
  • [0058]
    Percent patency has been determined using a semiquantative scale. This has been determined by taking the cross sectional view of a graft and dividing it into equal
  • [0059]
    concentric circles of 1/4 D from the wall of the vessel. Thus, it is now possible to quantify the amount of thrombus formed by measuring the depth of the thrombus then relating it to the total cross sectional area. The numbers generated by this technique are expressed in terms of percentage of'the entire vessel.
  • Post Implantation Studies
  • [0060]
    The graft-hybrid materials were analyzed using (1) scanning electron microscopy (SEM), (2) light microscopy and (3) histological staining. Patency was determined using the aforementioned semi-quantitative technique.
  • Scanning Electron Microscopy (SEM)
  • [0061]
    SEM's were performed on the grafts before implantation and after removal using a Phillip's scanning electron microscope at 200x, 10Kx and 20Kx magnifications. With these magnifications, it is possible to resolve and differentiate platelets, erythrocytes, and leukocytes, and white blood cells and to visualize protein (including fibrin) deposition.
  • [0062]
    The SEM's were used to detect (1) efficiency of hybridization (to determine structural flaws in the coatings) and (2) to determine visible evidence of the type of blood prostheses interfacial reactions.
  • Histological and Light Microscopic Evaluations
  • [0063]
    Graft sections were evaluated by the use of several standard histological stains including Hemotoxylan and Eosin (H&E) Van Geisen (Elastic VG stain), PTAH and Trichrome. Each stain specifically detects the type of material adhering to the graft or removal from the animal by the colors which are produced when the staining solution is in contact with the biologic material. H&E is used to visualize cellular entities and to demonstrate if an inflamatory response has occurred and if polynucleated cells or lymphocytes are present. EVG stain is used to illustrate fibroblastic invasion and to dye the collagen present. For instance, Trichrome stains collagen blue. PTAH stain is used to demonstrate the presence of fibrin.
  • Results
  • [0064]
    The following table illustrates the patency levels of the various hybrid grafts.
  • % Patency of Hybrid Grafts
  • [0065]
  • [0066]
    Table 1: Relates the type of hybridization, time of implantation and percent patency. Column 1 is the type of "coating" and subsequent negative charging. The next 4 colums are the time parameters at which they were analyzed. The numbers represent the % of patency. A check indicates that the graft is still functioning in-vivo. A - indicates that that parameter was not measured. The last column is the type of Dacron support used with that particular modification.
  • [0067]
    The following figures are SEM studies of the following hybrid grafts before and after implantation, negative charged and unmodified, of (i) Albumin (A) coated grafts, (ii) Gelatin (G) coated grafts, (iii) a 50/50 mixture of albumin and gelatin a concentration of 3 % each (AG), (iv) acrylamide coated graft (ACD), (v) agar-agar coated grafts (AGR), and CVD aluminum coated grafts (Al). Fig. l(a) shows scanning electron micrographs of a polymerized protein, namely, of an albumin Dacron hybrid graft. This series of photographs demonstrates the homo- genicity of a protein on Dacron surface.
  • [0068]
    Fig. l(B) shows scanning electron micrographs of a protein-gelatin Dacron hybrid graft. The photographs show a homogeneous surface prior to and after exposure of the surface to blood for 1 second.
  • [0069]
    Fig. 2(A) shows scanning electron micrographs of a gelatin-Dacron hybrid graft. These photographs reveal minor cracking of the polymerized surface at high (lOKx) magnification.
  • [0070]
    Fig. 2(B) shows scanning electron micrographs of a gelatin-Dacron hybrid graft. Following polymerization of the hybrid, the surface was chemically treated (succinylating) to produce a net negative surface charge. These micrographs indicate that the negative surface at 1 second, 2 hours and 1 month is far less reactive than the unmodified hybrid surface. The unmodified surface has a dense amount of cellular protein deposition thereon, while the negatively charged surface attracts fewer cellular aggregates. The patency rate for the negatively charged grafts was approximately 90 % as opposed to 60 % for the unmodified surface at 2 hours.
  • [0071]
    Fig. 3(A) shows the smooth structure of an agar coated Microknit― Dacron graft and Fig. 3(B) shows implantation results of a protein-gelatin Dacron hybrid graft. The SEM photographs reveal that the protein-gelatin negatively charged hybrid is less reactive at 1 second, 2 hours and 1 month than the unmodified graft. Many erythrocytes entrapped in a protein matrix can be seen in the unmodified surface while the negatively charged surface possesses few red cells and no visible platelets. Patency rates for the negatively charged grafts was approximately 90 % as opposed to 70 % for the unmodified grafts at 2 hours.
  • [0072]
    Fig. 4 shows scanning electron micrographs of an aluminum coated Dacron hybrid graft. Following implantation, the graft was examined. Little protein deposition could be seen. A layer of cells which appear to be erythrocytes and monocytes bound to fibrinogin seem to be sparsely coating the surface. The metallic coating may be toxic to cellular elements, as the monocytes are atypical. The patency rate in all cases was 100 %.
  • [0073]
    Fig. 5 shows scanning electron micrographs of an agar coated-Dacron hybrid. Implantation results indicate a reactive surface with cellular and protein deposition. Patentcy rates were 80 % at 1 second and 40 % at 2 hours.
  • [0074]
    Fig. 6(A) shows an aluminum coated Dacron prosthesis exposed to blood for 1 second. The fibrils are virtually free of cellular elements with the exception of a very few erythrocytes and leukocytes with a few visible platelets attached as well. At 10K X magnification, the single large cell appears to be a toxic neutrophile. The remainder of the photograph displays proteinated aluminum substrate. At 2 hours, the cells are smaller and appear to be crenating.
  • [0075]
    Fig. 6(B) shows further magnifications at 1 K X and these reveal a few crenating cells with a very thin layer of protein attached to the aluminized Dacron fabric. These cells are completely gone by 1 month, the fabric being joined by what appears to be a thin amorphous layer of protein. This may be proteinated aluminum.
  • [0076]
    Histological evaluation was carried out in parallel to the SEM studies. In all cases, there was no evidence of (1) polynucleated cells or lymphocytes or, (ii) inflamatory response. All grafts had fibroblastic invasion. Type A presents the most explicit example. In all cases, protein coating was firmly attached to the Dacron. Coating of each strand of Dacron was also established.
  • [0077]
    The different histological responses to the various types of hybrid grafts are described in Table II.
  • [0078]
    There will now be obvious to those skilled in the art many modifications and variations of the methods and materials set forth hereinabove. These modifications and variations will not depart from the scope of the invention if defined by the following claims.
Citas de patentes
Patente citada Fecha de presentación Fecha de publicación Solicitante Título
CH593676A5 * Título no disponible
DE1494939A1 *11 Jun 19634 Jun 1969Buddecke Dr EckhartImplantationsmaterial und Verfahren zu seiner Herstellung
FR2029155A5 * Título no disponible
GB1008193A * Título no disponible
GB1064850A * Título no disponible
GB1097787A * Título no disponible
US3096560 *21 Nov 19589 Jul 1963William J LiebigProcess for synthetic vascular implants
US3276448 *14 Dic 19624 Oct 1966Ethicon IncCollagen coated fabric prosthesis
US3512183 *8 Jun 196719 May 1970Us Health Education & WelfareBioelectric polyurethane and use of same in internal prostheses
US3563925 *20 Dic 196716 Feb 1971Ceskoslovenska Akademie VedComposition containing interlocked foams of partly tanned collagen and cross-linked glycol methacrylate polymer
US3609768 *16 Jun 19695 Oct 1971Becton Dickinson CoAnticoagulant material having charged electrostatic surfaces suitable for use in prosthetic devices
US3744062 *8 Oct 197110 Jul 1973Parsonnet VHeart valve construction having a collagen cover encapsulation thereon
US3914802 *23 May 197428 Oct 1975Ebert MichaelNon-thrombogenic prosthetic material
US3927422 *12 Dic 197323 Dic 1975Sawyer Philip NicholasProsthesis and method for making same
US4038702 *21 Sep 19732 Ago 1977Philip Nicholas SawyerElectrochemical and chemical methods for production of non-thrombogenic metal heart valves
US4082507 *10 May 19764 Abr 1978Sawyer Philip NicholasProsthesis and method for making the same
Otras citas
Referencia
1 *MEDICAL PROGRESS TECHNOLOGY, vol. 5, nr. 2 (1977) Springer Verlag, Berlin. S.D. BRUCK: "Biological Evaluation of Biomaterials for Cardiovascular Applications: Some Current Results", pages 51-56, (Invited paper presented at the Workshop on Biomaterials, 11th International Conference on Medical and Biological Engineering, Ottawa, Canada, Aug. 2-6, 1976)
Citada por
Patente citante Fecha de presentación Fecha de publicación Solicitante Título
EP0124659A1 *13 Abr 198314 Nov 1984Koken Co. Ltd.Medical material
EP0183365A2 *10 Oct 19854 Jun 1986Vascutek LimitedVascular graft
EP0183365B1 *10 Oct 198530 Dic 1992Vascutek LimitedVascular graft
EP0311305B1 *29 Sep 19889 Sep 1992Koken Company LimitedArtificial blood vessel
EP0542880A1 *23 Jul 199126 May 1993The Trustees of Columbia University in the City of New YorkTissue bonding and sealing composition and method of using the same
EP0542880A4 *23 Jul 199128 Jul 1993Lawrence Samuel BassTissue bonding and sealing composition and method of using the same
EP1267749B220 Mar 200126 Jul 2017Vactronix Scientific, Inc.Endoluminal implantable devices and method of making same
US4842575 *5 Ago 198827 Jun 1989Meadox Medicals, Inc.Method for forming impregnated synthetic vascular grafts
US5073171 *12 Ene 198917 Dic 1991Eaton John WBiocompatible materials comprising albumin-binding dyes
US5108424 *28 Ene 199128 Abr 1992Meadox Medicals, Inc.Collagen-impregnated dacron graft
US5197977 *30 Abr 199230 Mar 1993Meadox Medicals, Inc.Drug delivery collagen-impregnated synthetic vascular graft
US5716660 *31 May 199510 Feb 1998Meadox Medicals, Inc.Tubular polytetrafluoroethylene implantable prostheses
US5851230 *18 Oct 199622 Dic 1998Meadox Medicals, Inc.Vascular graft with a heparin-containing collagen sealant
US6162247 *21 Dic 199819 Dic 2000Meadox Medicals, Inc.Vascular graft impregnated with a heparin-containing collagen sealant
WO1996040302A1 *19 Abr 199619 Dic 1996W.L. Gore & Associates, Inc.Bioabsorbable space filling soft tissue prosthesis
Clasificaciones
Clasificación internacionalA61F2/00, A61M1/00, A61L27/14, A61L27/00, A61L33/00, A61F2/06, A61L27/34
Clasificación cooperativaA61F2/0077, A61L33/00, A61L27/34, A61L27/507, A61L27/14
Clasificación europeaA61L27/34, A61L33/00, A61F2/00L, A61L27/14
Eventos legales
FechaCódigoEventoDescripción
7 Mar 1979AKDesignated contracting states:
Designated state(s): BE CH DE FR GB LU NL SE
28 Nov 197917PRequest for examination filed
18 May 1983AKDesignated contracting states:
Designated state(s): BE CH DE FR GB LU NL SE
18 May 1983PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: NL
Effective date: 19830518
Ref country code: BE
Effective date: 19830518
7 Jul 1983REFCorresponds to:
Ref document number: 2862259
Country of ref document: DE
Date of ref document: 19830707
Format of ref document f/p: P
8 Jul 1983ETFr: translation filed
17 Oct 1983NLV1Nl: lapsed or annulled due to failure to fulfill the requirements of art. 29p and 29m of the patents act; no legal effect from
30 May 198426NNo opposition filed
4 Ene 1993PGFPPostgrant: annual fees paid to national office
Ref country code: DE
Payment date: 19930104
Year of fee payment: 15
5 Ene 1993PGFPPostgrant: annual fees paid to national office
Ref country code: CH
Payment date: 19930105
Year of fee payment: 15
8 Ene 1993PGFPPostgrant: annual fees paid to national office
Ref country code: SE
Payment date: 19930108
Year of fee payment: 15
Ref country code: GB
Payment date: 19930108
Year of fee payment: 15
21 Ene 1993PGFPPostgrant: annual fees paid to national office
Ref country code: FR
Payment date: 19930121
Year of fee payment: 15
25 Ago 1993PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: GB
Effective date: 19930825
26 Ago 1993PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: SE
Effective date: 19930826
31 Ago 1993PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: CH
Effective date: 19930831
27 Abr 1994GBPCGb: european patent ceased through non-payment of renewal fee
Effective date: 19930825
29 Abr 1994REGReference to a national code
Ref country code: CH
Ref legal event code: PL
29 Abr 1994PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: FR
Effective date: 19940429
3 May 1994PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: DE
Effective date: 19940503
24 Jun 1994REGReference to a national code
Ref country code: FR
Ref legal event code: ST
31 Ene 1995EUGSe: european patent has lapsed
Ref document number: 78100752.1
Effective date: 19940310
Format of ref document f/p: F
1 Abr 1996PGFPPostgrant: annual fees paid to national office
Ref country code: LU
Payment date: 19960401
Year of fee payment: 19
25 Ago 1997PG25Lapsed in a contracting state announced via postgrant inform. from nat. office to epo
Ref country code: LU
Free format text: LAPSE BECAUSE OF NON-PAYMENT OF DUE FEES
Effective date: 19970825