US20010045614A1 - Wafer trench article and process - Google Patents
Wafer trench article and process Download PDFInfo
- Publication number
- US20010045614A1 US20010045614A1 US09/283,530 US28353099A US2001045614A1 US 20010045614 A1 US20010045614 A1 US 20010045614A1 US 28353099 A US28353099 A US 28353099A US 2001045614 A1 US2001045614 A1 US 2001045614A1
- Authority
- US
- United States
- Prior art keywords
- trenches
- layer
- trench
- device substrate
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- This application is a divisional application of U S. patent application Ser. No. 08/637,937, filed Apr. 23, 1996 (Atty. Docket No. 875523.97R064/SE-1211TD).
- This invention relates generally to semiconductor wafer processing and, in particular, to processes that form trenches in wafers while reducing device stress and defects.
- Isolation trenches are common features in integrated circuits Trenches surround devices and isolate one device from another. Bonded wafers, especially bonded wafers made in accordance with U.S. Pat. No. 5,387,555 assigned to the same assignee as this invention, provide a bond oxide layer between a device substrate and a handle substrate. Trenches extend from the surface of the device substrate down to the bond oxide. The trench side walls and floors are then covered with one or more insulating materials. The trenches are filled with a conformal material, typically polysilicon. However, excess insulating material accumulates at the top corners of the trenches and interferes with the filling process. As a result, trenches have voids that extend to the tops of the trenches.
- It is common to oxidize exposed surfaces of the device substrate or exposed surfaces of a polysilicon layer in order to convert the device silicon or the polysilicon into silicon dioxide and thereby form a region of isolating material. During a thermal oxidation process, each atom of silicon is joined by two atoms of oxygen. The corner regions at the top of a trench lined with thermal oxide come under stress. Those corner regions increase in volume and the increased volume creates stress in adjacent device area The stress can result in device defects.
- Accordingly, there is an unmet need for an improved process that provides isolation trenches in an integrated circuit without generating stress and device defects In particular, there is an unmet need for an improved process that reduces device stress and device defects.
- The invention includes a new integrated circuit and a new method of manufacturing the integrated circuit. The integrated circuit has two or more device regions in a device substrate of semiconductor material, typically monocrystalline silicon. The device substrate may be either a single wafer of silicon or the device substrate of a bonded wafer. A bonded wafer may include a handle substrate of suitable material, also typically silicon. The handle substrate is bonded to the device substrate using an oxide bonding process that provides an oxide bonding layer of silicon dioxide on the bottom of the device substrate. The device substrate is separated into device regions by isolation trenches. Each isolation trench has a floor and sidewalls spaced from each other. The trench sidewalls extend into the device substrate. The sidewalls in a bonded wafer extend to the bonding oxide layer.
- The isolation trenches are formed by masking the device substrate and removing device silicon from unmasked regions to form trenches. Each trench has a floor and sidewalls spaced from each other. A nominally conformal layer of insulating material, typically silicon dioxide, is formed on the sidewalls and the floor. The insulating material tends to increase in thickness at the upper corner openings of the trench to produce dogbone structure. The dogbone structures are removed by a plasma anisotropic etch. A semiconductor material (polysilicon) is deposited on the device substrate to fill the trenches. With the dogbone structure removed, any voids that form in the filling material are small and are spaced from the top of the trench. The filling material is planarized to the surface of the device substrate. Then the device substrate is covered with a pad oxide layer and a silicon nitride layer. The pad oxide layer may be deposited or thermally grown. The oxide and silicon nitride layers are selectively removed from regions between trenches and remain over the trenches during further thermal oxidations. The oxide and silicon nitride layers prevent the growth of thermal oxides in the trench filling voids and at the tops of the trenches adjacent to the sidewalls. After thermal oxidations are substantially completed (e.g. no further oxidations greater than 500 Å) the nitride mask over the trenches may be removed.
- FIGS.1A-5A show sequential steps in a prior art trench process;
- FIGS.1B-5B show a corresponding series or sequential steps in the inventive trench process.
- FIG. 6 shows an alternate embodiment of the invention where the protective nitride is deposited over the passivation oxide.
- FIG. 7 is an enlarged, partial view of the structure shown inside dashed line7-7′ of FIG. 4A.
- One problem of prior art trench processes is the formation of dogbone structures at trench openings. With reference to FIG. 1A, there is generally shown a bonded
wafer substrate 10 comprising ahandle substrate 12 that is oxide bonded to adevice substrate 16 byoxide bonding layer 14. Thedevice wafer 16 is suitably masked and etched in order to formtrenches 30 anddevice regions 18. A deposited oxide process covers the exposed surfaces of the device substrate, including the side walls and the floors of thetrenches 30, to createoxide layer 20. The deposition process also createsdogbone structures 32 at the upper corner openings of thetrenches 30. Thedogbone structures 32 are regions of increased oxide thickness that extend toward the opening of thetrench 30. Thedogbone structures 32 reduce the trench openings. The reduced openings make it difficult to deposit a conformal layer of trench fill material in the trenches. As a result, trenches with dogbone structures often have voids that extend to the tops of the trenches. - The invention solves the dogbone problem by removing the dogbone structures prior to filling the trenches. In FIG. 1B, the
dogbone structures 32 on bondedwafer substrate 100 are removed by anisotropically etching theoxide layer 20. The anisotropic etch is typically a plasma assisted etch which is designed to remove oxide material at the maximum sputtering angle of around 45° to the surface of the wafer. In order to remove thedogbone structures 32, the bondedwafer substrate 100 is subjected to the anisotropic etch for approximately seven minutes. A typical etching apparatus is a AME8110 machine made by Applied Materials. The etching process creates facets on the upper corners. Thefacets 24 slope away from the openings and thus widen the openings. - FIG. 2A illustrates another typical problem of prior art bonded wafer trench processes. A conformal layer of
polysilicon 34 is deposited by chemical vapor deposition over thedevice substrate 16 in order to fill thetrenches 30. However, the conformal layer ofpolysilicon layer 34 does not completely fill thetrenches 30. Instead, voids 36 are left in the trenches. The voids are due, in part, to the presence of thedogbone structures 32 and the trench shape that reduce the trench openings. FIG. 2A shows trenches with sidewalls perpendicular to the trench floor. However, the trench walls may taper toward or away from each other. The voids can exist in thermal oxide passivated trenches, deposited oxide passivated trenches or combination thermal and deposited oxide passivated trenches. The void may extend laterally along all or substantially all the length of the trench. So, the void is a near-continuous, subsurface channel in the trench. Vertical portions ofvoids 36 often extend to the tops of the trenches where they oxidize later in the process. As a result, the silicon adjacent the vertical portions and the subsurface lateral portions is oxidized. - Turning to FIG. 2B of the invention, there is shown how the faceting of the trench openings removes the
dogbone 32 and improves the trench profile to enhance the filling of thetrenches 30. So, without interfering dogbone structures and having a more tapered trench opening, thepolysilicon 34 more fully fills thetrenches 30. Althoughvoids 37 may still be present in thetrenches 30, the voids are smaller and are spaced from the tops of the trenches. - The prior art process planarizes the surface of the
device wafer 16 in order to removeexcess polysilicon 34. As shown in FIG. 3A, after thepolysilicon layer 34 is planarized thevoids 36 are open at the surface of thedevice wafer 16. The corners of the trenches may become sources of increased stress and defects. As shown in FIGS. 4A and 7, a typical step following planarization is growth of apad oxide 40 on thedevice substrate 16. The pad oxide is grown by thermal oxidation of the silicon indevice substrate 16 and thepolysilicon 34 in thetrenches 30. As expected, the surface of the voids and the corners of the trenches are similarly oxidized. The growth ofoxides oxide 42 on thepolysilicon 34 invoid regions 36 increase stress and tends to induce defects indevice regions 18 ofdevice substrate 16. - The thermal
pad oxide layer 40 may be the first step in a local oxidation of silicon (LOCOS) process such as described in U.S. Pat. No. 5,217,919, the entire disclosure of which is herein incorporated by reference. In a typical LOCOS process, isolation regions are created in the surface of thedevice islands 18. A nitride layer is deposited over the surface of the device island in regions where isolation is not required. The nitride layer seals the underlying silicon from the subsequent thermal oxidation. The nitride layer is typically deposited upon a relatively thin pad oxide layer. A thin pad oxide layer is used to reduce nitride stress effects in the silicon and because it is very difficult to selectively remove nitride with respect to silicon. However, there are many known etching materials that can selectively remove nitride with respect to silicon dioxide. A typical etchant is hot phosphoric acid (wet etch) or SF6 (reactive ion etch). So, in a typical device island, the device area is masked with a nitride layer and the surrounding exposed silicon is thermally oxidized to create a relatively thick LOCOS layer. The nitride layer is stripped and the device is formed within the boundaries of the LOCOS layer. - Turning to FIG. 4B, the problem of prior art thermal oxide stress in the isolation trenches is solved by using a chemical vapor deposition process in order to form a deposited
pad oxide layer 60. The depositedpad oxide layer 60 does not consume any of the silicon in thedevice substrate 16 or any of the polysilicon in thetrenches 30. Since the depositedpad oxide layer 60 does not consume any silicon, the process shown in FIG. 4B does not oxidized thecorners 44 at the top side walls of thetrenches 30 as shown in FIG. 4A. A layer ofsilicon nitride 50 is deposited over the CVDpad oxide layer 40. - Turning to FIG. 5A, there is shown the
prior art structure 10 during a further step where asubsequent oxide layer 45 is grown over thedevice substrate 16. The growth of thethermal oxide layer 45 further oxidizes the silicon and expands thecorner oxide regions 44′ at the top of the trenches and also expandsregions 42′ on the surface ofvoids 36. - As shown in FIG. 5B, the nitride layer is removed except over the
trenches 30. Thesilicon nitride cap 50 will prevent thermal oxidation of the silicon beneath the silicon nitride layer. Accordingly, thermal oxidations subsequent to definition of thesilicon nitride cap 50 may be carried out over the rest of the device substrate or over selected portions of device substrate. In either case no oxidation occurs in the trench regions capped by thenitride layer 50. Semiconductor devices, including mos, jfet, and bipolar devices, are then formed indevice substrate 16 to create integrated circuits in a manner well known to one skilled in the art. After all thermal oxidations are completed, thenitride cap structure 50 may be removed from over the trenches or it may be left in place depending on the constraints of the process. Thenitride cap 50 may be removed earlier in the process and still be effective so long as subsequent thermal oxidations are relatively small in thickness, i.e., less than about 500 Angstroms. - With reference to FIG. 6, there is shown a further embodiment of the invention. There, a
bond wafer substrate 110 has anitride layer 70 deposited over thepassivation oxide layer 20 that covers thedevice substrate 16 and the side walls and the floors of thetrenches 30. The step of depositingnitride layer 70 is performed subsequent to the step shown in FIG. 1B, i.e. after thepassivation oxide 20 is conformally deposited. Thenitride layer 70 thus seals thepassivation oxide 20. A conformal layer ofpolysilicon 34 is then deposited to fill the trenches and subsequently planarized as shown in the above steps of FIGS. 1B-5B. Although the embodiment shown in FIG. 6 may create voids in the center of the polysilicon in the trenches, nevertheless it will prevent undesirablethermal oxide corners 44. - Having thus described embodiments of the invention, those skilled in the art will appreciate that further changes, additions, and modifications may be made to the disclosed embodiments without departing from the spirit and the scope of the claims. In particular, those skilled in the art will appreciate that, while the preferred embodiment of the invention is described in connection with a bonded wafer structure, the invention may also be practiced in single substrate wafers. Also, while the process is described in connection with an isolation trench, it may be applied to any trench structure including but not limited to capacitor trenches for dynamic random access memories and trench gate structures in dmos, qvdmos, mct and igbt devices.
Claims (22)