US20020079487A1 - Diffusion barriers comprising a self-assembled monolayer - Google Patents
Diffusion barriers comprising a self-assembled monolayer Download PDFInfo
- Publication number
- US20020079487A1 US20020079487A1 US09/976,927 US97692701A US2002079487A1 US 20020079487 A1 US20020079487 A1 US 20020079487A1 US 97692701 A US97692701 A US 97692701A US 2002079487 A1 US2002079487 A1 US 2002079487A1
- Authority
- US
- United States
- Prior art keywords
- group
- diffusion barrier
- groups
- self
- hydrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention provides a method for forming a diffusion barrier layer, a diffusion barrier in an integrated circuit and an integrated circuit. The method for forming a diffusion barrier involves the following steps: 1) preparing a silicon substrate; 2) contacting the silicon substrate with a composition comprising self-assembled monolayer subunits and a solvent; and, 3) removing the solvent. The diffusion barrier layer includes a self-assembled monolayer. The integrated circuit includes a silicon substrate, a diffusion barrier layer and a metal deposited on the diffusion barrier layer. The diffusion barrier layer in the integrated circuit is covalently attached to the silicon substrate and includes a self-assembled monolayer.
Description
- This application is related to and claims priority to provisional Applications Nos. 60/240,109 entitled Diffusion Barriers Comprising A Self-Assembled Monolayer naming G. Ramanath, Ahila Krishnamoorthy, Kaushik Chanda and Shyam P. Murarka as inventors and filed Oct. 12, 2000 and 60/244,160 entitled Diffusion Barriers Comprising A Self-Assembled Monolayer naming G. Ramanath, Ahila Krishnamoorthy, Kaushik Chanda and Shyam P. Murarka as inventors and filed Oct. 27, 2000. These applications are incorporated herein for all purposes as if set forth herein in full.
- NOT APPLICABLE
- NOT APPLICABLE
- A. Field Of The Invention
- The present invention generally relates to integrated circuits. In particular, it relates to forming a diffusion barrier layer comprising a self-assembled monolayer in an integrated circuit.
- B. Description Of Related Art
- Copper is becoming the metal of choice for forming conductive patterns in integrated circuits. There are, however, unresolved issues with its use. For instance, copper diffuses rapidly in silicon and silicon dioxide. The diffusion, over time, results in junction linkage, which decreases device efficiency.
- To address the problem of copper diffusion, researchers have developed “diffusion barriers.” A diffusion barrier is part of the metallization scheme, comprising a layer of material formed between an overlying copper layer and an underlying silicon or silicon dioxide layer. The diffusion barrier serves to inhibit the diffusion of copper into the surrounding layer.
- The use of amorphous alloys as diffusion layers has been discussed. Amorphous binary silicides, such as molybdenum-, tantalum and tungsten silicide and amorphous ternary alloys (e.g., Ti—Si—N) have been reported as diffusion barriers. The formation of these layers uses sophisticated processes, such as sputtering and/or chemical vapor deposition, or their variants. This results in the inclusion of substantial contaminants and residual stresses. Perhaps more importantly, these films have poor continuity and uniformity in non-planar structures.
- Diffusion barriers made of TiN, TiSiN and TiN/TiSiN have also been reported. Many of the processes to form these layers involve treatments such as nitridation, oxidation, and post-deposition annealing.
- While a number of diffusion barriers have been discussed in the art, improved diffusion barriers are desirable, especially those that are very thin and continuous.
- The present invention provides a method for forming a diffusion barrier layer. The method involves the following steps: 1) preparing a silicon substrate; 2) contacting the prepared silicon substrate with a composition comprising self-assembled monolayer subunits and a solvent; and, 3) removing the solvent.
- The present invention also provides a diffusion barrier in an integrated circuit. The diffusion barrier includes a self-assembled monolayer.
- The present invention further provides an integrated circuit with a multilevel metallization scheme. The integrated circuit includes a silicon substrate, a diffusion barrier layer and a metal deposited on the diffusion barrier layer. The diffusion barrier layer is covalently attached to the silicon substrate and includes a self-assembled monolayer.
- FIG. 1 shows a cross-sectional view of an MOS test structure comprising a self-assembled monolayer diffusion barrier layer.
- FIG. 2 shows a bar graph representing bias temperature testing of five different test structures.
- FIG. 3 shows a cross-sectional view of a two-level integrated circuit comprising a self-assembled monolayer diffusion barrier layer.
- A. Introduction
- The present invention provides a diffusion barrier in an integrated circuit, a method for forming the diffusion barrier and an integrated circuit containing the diffusion barrier. The diffusion barrier includes a self-assembled monolayer. Formation of the monolayer is typically done on the surface of a silicon substrate by contacting the substrate with monolayer subunits. The silicon substrate is represented by the formula SiOAXB, wherein A and B are ≧0, and X is N, C, B, F, P or As. In particular, in addition to subscript A assuming particular values of 0, 1, and 2, fractional compositions are also envisioned and included. The value of subscript B is dependent upon the element X. The combination of silicon substrate and self-assembled monolayer serves as an integrated circuit element.
- B. Composition Of Barrier Layer
- The diffusion barrier layer includes a self-assembled monolayer. As the term is applied to the present invention, a “self-assembled monolayer” is a single layer of molecules that forms on a substrate surface when monolayer subunits are contacted with the surface under appropriate reaction conditions. The subunits are attached to the substrate at a first end; the second end of the molecule projects upward from the substrate surface. As surface sites on the surface are reacted with monolayer subunits, the single molecular layer is formed.
- The subunits of the self-assembled monolayer are preferably attached to the substrate through a covalent bond. Typically, the substrate has reactive moieties extending from its surface (e.g., O, OH, NH2, SH). The reactive moieties provide a point of covalent attachment to the subunit. For instance, SiO2 is a typical substrate for monolayer formation. The hydroxylated SiO2 surface provides OH groups that can covalently bind to substrates containing certain types of functional groups.
-
- Y is typically an O-alkyl group (e.g., OCH3 or OC2H5) but can also be other displaceable groups such as Cl. R2 is an alkyl group, heteroalkyl group, aryl group or heteroaryl group.
- “Alkyl group” refers to a straight-chain, branched or cyclic group containing a carbon backbone and hydrogen. Examples of straight-chain alkyl groups include methyl, ethyl, propyl, butyl, pentyl and hexyl. Examples of branched alkyl groups include i-propyl, sec-butyl and t-butyl. Examples of cyclic alkyl groups include cyclobutyl, cyclopentyl and cyclohexyl.
- Alkyl groups are substituted or unsubstituted. In a substituted alkyl group, a hydrogen on the carbon backbone is replaced by a different type of atom (e.g., oxygen, nitrogen, sulfur, halogen). For instance, 2-hydroxyethyl is an ethyl group where one of the hydrogens is replaced by an OH group; 2-chloropropyl is a propyl group where one of the hydrogens is replaced by a Cl group.
- “Heteroalkyl group” refers to a straight-chain, branched or cyclic group containing a carbon-heteroatom backbone and hydrogen. Heteroatoms include, without limitation, oxygen, nitrogen and sulfur. Methyl ethylether (i.e., CH2OCH2CH3) is an example of a straight-chain heteroalkyl group. As with alkyl groups, heteroalkyl groups are substituted or unsubstituted.
- “Aryl group” refers to a carbocyclic aromatic group containing six carbon atoms (e.g., phenyl) or a carbocyclic aromatic group containing ten carbon atoms (e.g., naphthyl). An aryl group is substituted or unsubstituted. A substituted aryl group is one where at least one hydrogen atom of an aryl group has been replaced with a different type of atom (e.g., oxygen, nitrogen, sulfur, halogen). Examples of substituted aryl groups include the following: 2-chlorophenyl; 3-methylphenyl; and, 4 methoxyphenyl.
- “Heteroaryl group” refers to an aromatic group containing both carbon atoms and heteroatoms. Examples of heteroaryl groups include pyridyl, furyl, pyrrolyl and imidazolyl. As with aryl groups, heteroaryl groups are substituted or unsubstituted. 2-Chloropyridyl is an example of a substituted heteroaryl group.
-
- wherein R1 is a straight-chain alkyl group and n is an integer≧1. Preferably n is an integer ranging from 1 to 5. Preferably, R1 is methyl and n is 2.
-
- wherein R1 is a straight-chain alkyl group, n is an integer≧1 and R3, R4 and R5 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, Br, Cl, F, I, NH2, NHR6NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN. R6 and R7 are alkyl groups or aryl groups. Preferably, n is an integer ranging from 1 to 5. Preferably, R1 is methyl, R3, R4 and R5 are hydrogen and n is 2.
-
- wherein R1 is a straight-chain alkyl group, n is an integer≧1 and R3 and R4 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, Br, Cl, F, I, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN. R6 and R7 are alkyl groups or aryl groups. Preferably n is an integer ranging from 1 to 5. Preferably, R1 is methyl, R3, R4 and R5 are hydrogen and n is 2.
-
-
- wherein R1 is a straight-chain alkyl group, and R3, R4 and R5 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, Br, Cl, F, I, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN. R6 and R7 are alkyl groups or aryl groups.
- C. Process For Forming Barrier Layer
- To form the self-assembled monolayer on the surface of a substrate, a substrate is first prepared. The substrate is typically cleaned, washed and dried. Contact of the prepared substrate with monolayer subunits in a suitable solvent and under appropriate reaction conditions attaches the subunits to the surface. Removal of the solvent provides the desired layer on the substrate.
- In one embodiment, the substrate is a silicon wafer that has been oxidized to form an SiO2 surface layer. The layer is typically cleaned using an organic solvent (e.g., xylene) or a series of organic solvents followed by a water wash. The wet wafer is dried, for example, by blow-drying it with N2. Immersion of the dry wafer in an organic solvent (e.g., toluene) containing self-assembled monolayer subunits followed by heating the solution attaches subunits to the SiO2 surface. The reacted substrate is washed with an organic solvent (e.g., toluene) and dried (e.g., blown dry with N2).
- D. Barrier Layer As Part Of Device
- The present invention provides an integrated circuit comprising a self-assembled monolayer diffusion barrier. FIG. 1 shows an MOS test structure containing a self-assembled monolayer barrier layer. The MOS test structure contains the following elements: a silicon layer (1); a silicon dioxide layer (2) on the top side of the silicon layer; an aluminum back contact (3) on the bottom side of the silicon layer; a diffusion barrier (4) comprising a self-assembled monolayer; and, copper dots (5) deposited on the diffusion barrier. FIG. 3 shows a cross-sectional view of a two-level integrated circuit comprising a self-assembled monolayer diffusion barrier layer. The illustrated integrated circuit contains the following elements: a copper layer (6); a self-assembled monolayer diffusion barrier layer (7) that surrounds the copper layer; and, a silicon substrate (8) that includes the copper and diffusion barrier layers.
-
- wherein R2 is an alkyl group, heteroalkyl group, aryl group or heteroaryl group.
- E. Metals Deposited On Diffusion Barrier
- The diffusion barrier of the present invention serves to inhibit the diffusion of a deposited metal on the surface of the self-assembled monolayer through to the substrate underneath the monolayer. The barrier inhibits the diffusion of a variety of metals.
- In a preferred embodiment, the barrier inhibits the diffusion of copper.
- 1. Preparation Of An MOS Test Structure.
- A (100) oriented, B-doped, 5″ diameter p-Si wafer was taken. It was RCA cleaned and oxidized in an ambient of dry O2 at 900° C. to grow an oxide of 100 nm thickness. The back oxide was completely removed using buffered HF and a 0.3-0.4 μm-thick aluminum layer was sputter deposited to form a back contact. The resulting wafer was vacuum annealed at 400° C. for 30 minutes.
-
- The wafer in the solution was heated from room temperature to 60° C. over 1 hour. The wafer was washed with toluene, blown dry with N2 and baked on a heating plate for about 4 minutes at 12° C.
- Copper dots of 1 mm diameter and 1.2 μm thickness were sputter deposited on the wafer monolayer, completing the preparation of the MOS test structure.
- 2. Bias Temperature Testing Of MOS Test Structures
- Test structures prepared according to Example 1 were subjected to electrical testing. A control structure (no diffusion barrier) and four different structures comprising self-assembled monolayer diffusion barriers (diffusion
barrier comprising subunits
Claims (23)
1. A method for forming a diffusion barrier layer comprising the steps of:
a) preparing a silicon substrate;
b) contacting the silicon substrate with a composition comprising self-assembled monolayer subunits and a solvent; and,
c) removing the solvent thereby forming the diffusion barrier.
4. The method according to claim 1 , wherein the silicon substrate preparation comprises the formation of a silicon oxide surface.
5. The method according to claim 1 , wherein the method further comprises the step of heating the silicon substrate and the composition during contact.
6. The method according to claim 2 , wherein R2 is an alkyl group of the following structure:
wherein R3, R4 and R5 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
7. The method according to claim 2 , wherein R2 is an alkyl group of the following structure:
wherein R3 and R4 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
8. The method according to claim 6 , wherein Y is OCH3.
9. The method according to claim 7 , wherein Y is OCH3.
10. The method according to claim 8 , wherein R3, R4 and R5 are hydrogen and n is 2.
12. A diffusion barrier layer in an integrated circuit, wherein the diffusion barrier comprises a self-assembled monolayer.
14. The diffusion barrier according to claim 13 , wherein R2 is an alkyl group of the following structure:
wherein R3, R4 and R5 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
15. The diffusion barrier according to claim 13 , wherein R2 is an alkyl group of the following structure:
wherein R3 and R4 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
16. The diffusion barrier according to claim 14 , wherein R3, R4 and R5 are hydrogen and n is 2.
18. An integrated circuit comprising a silicon substrate, a diffusion barrier layer and a metal deposited on the diffusion barrier layer, wherein the diffusion barrier is covalently attached to the silicon substrate, and wherein the diffusion barrier is a self-assembled monolayer.
20. The integrated circuit according to claim 19 , wherein R2 is an alkyl group of the following structure:
wherein R3, R4 and R5 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
21. The integrated circuit according to claim 19 , wherein R2 is an alkyl group of the following structure:
wherein R3 and R4 are independently selected from the group consisting of hydrogen, alkyl groups, heteroalkyl groups, halo groups, NH2, NHR6, NR6R7, OH, OR6, SH, SR6, CHO, COOH and CN, and wherein R6 and R7 are alkyl groups, and wherein n is an integer ranging from 1 to 5.
22. The integrated circuit according to claim 20 , wherein R3, R4 and R5 are hydrogen and n is 2.