US20030087463A1 - Method for producing high-brightness LED - Google Patents

Method for producing high-brightness LED Download PDF

Info

Publication number
US20030087463A1
US20030087463A1 US10/256,713 US25671302A US2003087463A1 US 20030087463 A1 US20030087463 A1 US 20030087463A1 US 25671302 A US25671302 A US 25671302A US 2003087463 A1 US2003087463 A1 US 2003087463A1
Authority
US
United States
Prior art keywords
layer
led
dielectric material
metal
type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/256,713
Inventor
Ray-Hua Horng
Tung-Hsing Wu
Shao-Hua Huang
Chih-Ru Chung
Juin-Jer Yang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
National Chung Hsing University
Original Assignee
National Chung Hsing University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by National Chung Hsing University filed Critical National Chung Hsing University
Assigned to NATIONAL CHUNG-HSING UNIVERSITY reassignment NATIONAL CHUNG-HSING UNIVERSITY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHUNG, CHIH-RU, HORNG, RAY-HUA, HUANG, SHAO-HUA, WU, TUNG-HSING, YANG, JUIN-JER
Publication of US20030087463A1 publication Critical patent/US20030087463A1/en
Abandoned legal-status Critical Current

Abstract

The present invention discloses a method for producing a high-brightness light emitting diode (LED), which primarily includes at least one step of bonding a reflective layer formed on an LED epitaxial layer to an adhesive layer formed on an Si substrate. An n-type ohmic contact electrode and a p-type ohmic contact electrode are deposed on the front side of the LED. In the present invention, the reflective layer, the adhesive layer and the ohmic contact electrodes preferably perform single function, so that the most appropriate materials can be applied. Therefore, the LED of the present invention can exhibit excellent brightness.

Description

    BACKGROUND OF THE INVENTION
  • 1. Field of the Invention [0001]
  • The present invention relates to a method for producing a light emitting diode (LED) and, more particularly, to a method for producing a high-brightness light emitting diode by bonding a reflective layer formed on an LED epitaxial layer to an adhesive layer formed on an Si substrate. [0002]
  • 2. Description of Related Art [0003]
  • Currently, a trend of developing the light emitting diodes is to promote the brightness. In order to achieve this object, one or more reflective metal layers are combined therein. However, this metal layer has to also possess properties of adhesion and ohmic contact. [0004]
  • For example, R.O.C. Patent No. 369731 disclosed an LED in which the GaAs substrate is replaced with a Si substrate having a reflective metal layer thereon by wafer bonding technology. Unfortunately, such design cannot improve the lighting effect of short wavelengths. [0005]
  • Additionally, in U.S. Pat. No. 5,376,580, the GaAs substrate is a temporary substrate for epitaxying and then removed after being bonded to a transparent substrate. Though this method prevents absorption of the GaAs substrate, the processes have to be carried out at high temperature, which might damage the structure and thus decrease the lighting effect. Additionally, this transparent substrate is made by GaP, which can absorb the short-wavelength light. [0006]
  • R.O.C. Patent No. 415116 mentioned an [0007] LED 10 as shown in FIG. 1, in which two reflective adhesive metal layers 16, 12 are respectively attached on the bottom surface of the LED epitaxial layer 15 and the top surface of the substrate 11. By bonding the two reflective adhesive metal layers 16, 12, the light beams can be propagated from the front side of the LED 10 and the brightness can be promoted.
  • FIG. 2 shows another [0008] conventional LED 20, in which a metal adhesive layer 22 is formed on a top surface of the SiO2 substrate 21, and an LED epitaxial layer 25 is bonded to the top surface of the metal adhesive layer 22. Brightness of the LED 20 can be improved due to ohmic contact between the substrate 21 and the metal adhesive layer 22.
  • For the above LED structures, all of the reflective layers have combining functions of adhesion and ohmic contact, therefore only metal material is suitable. A disadvantage of such material is that atomic diffusion occurs at the interface of the metal layer and the LED epitaxial layer. When a light source more than 600 nm is applied, the lighting effect will be reduced since total reflection in the metal layer is not available. FIG. 3 shows the reflectivity varied with wavelengths, in which the reflectivity is 0.9 at 600 nm. Further, the reflectivity rapidly reduces at wavelength less than 600 nm, for example, 590 nm or 570 nm of yellow-green light. Consequently, the reflective layer can hardly perform expected effect. Both the reflective metal layers as shown in FIGS. 1 and 2 exist such problem. [0009]
  • Therefore, it is desirable to provide a method for producing an improved LED structure to promote the brightness, particularly at short wavelength. [0010]
  • SUMMARY OF THE INVENTION
  • An object of the present invention is to provide a method for producing a high-brightness light emitting diode, which can exhibit superior lighting effect at long wavelength. [0011]
  • Another object of the present invention is to provide a method for producing a high-brightness light emitting diode, which can exhibit much better lighting effect than the conventional at short wavelength. [0012]
  • In order to achieve the above object, the method primarily includes steps of: A) forming a reflective layer on an LED epitaxial layer and a first adhesive layer on an Si substrate, wherein the LED epitaxial layer is grown on a temporary substrate and has a pn junction structure to define a first-type layer adjacent to the temporary substrate and a second-type layer; B) bonding the reflective layer to the first adhesive layer by thermal pressing and then removing the temporary substrate; C) forming a first-type ohmic contact electrode on partial top surface of the LED eptaxitial layer by physical vapor deposition; D) etching at least partial remained LED epitaxial layer from top surface thereof and stopping at the second-type layer to form a metal contact layer; and E) forming a second-type ohmic contact electrode on the metal contact layer by physical vapor deposition. [0013]
  • The LED eptaxitial layer aforementioned can further include a p-type confining layer and a n-type confining layer. The first ohmic contact electrode can further include a transparent electrode thereon to enhance electric conduction. The reflective layer preferably includes at least two materials, for example, a metal and an insulator, a high-dielectric material and a low-dielectric material, etc, wherein the insulator and the low-dielectric material are preferably adjacent to the LED epitaxial layer. [0014]
  • The metal can be Al, Ag, Au, Pt, Pd, etc. The insulator can be Al[0015] 2O3, MgF2, SiO2, TiO2, Si3N4, etc. The high-dielectric material preferably has a refractive index larger than 2.1, and the low-dielectric material has a refractive index less than 1.56. The high-dielectric material can be TiO2, CeO2, Si, etc. The low-dielectric material can be Al2O3, MgF2, SiO2, Si3N4, etc.
  • The etching process of step D) is preferably chemical wet etching or dry etching. The physical vapor deposition of steps C) and E) can be e-gun evaporation deposition, thermal evaporation deposition, or sputter deposition. [0016]
  • The reflective layer can further include a second adhesive layer therebelow to reinforce attachment with the first adhesive layer. The first or second adhesive layer is preferably made from metal, for example, Au, Au/Be alloy, Au/Zn alloy, Pt, Pd, Cu, Ni, In and Al. The first adhesive layer can be also a polymer nonconductor. [0017]
  • Other objects, advantages, and novel features of the invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings. [0018]
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 shows the cross section view of a conventional LED. [0019]
  • FIG. 2 shows the cross section view of another conventional LED. [0020]
  • FIG. 3 shows the reflectivity varied with wavelengths. [0021]
  • FIG. 4 shows the flow diagram for producing the LED in accordance with the present invention. [0022]
  • FIG. 5 shows the cross section view in the step of combining the LED epitaxial layer and the Si substrate of the present invention. [0023]
  • FIG. 6 shows the cross section view in the step of depositing the first-type ohmic contact electrode on the LED epitaxial layer of the present invention. [0024]
  • FIG. 7 shows the cross section view in the step of etching the LED epitaxial layer to form the metal contact layer and the second-type ohmic contact electrode of the present invention. [0025]
  • FIG. 8 shows the cross section view of the second embodiment in accordance with the present invention. [0026]
  • FIG. 9 shows the cross section view of the third embodiment in accordance with the present invention.[0027]
  • DETAILED DESCRIPYION OF THE PREFERRED EMBODIMENTS
  • Referring to FIG. 4, the flow diagram for producing the high-[0028] brightness LED 50 of the present invention is shown. In step A, also with refer to FIG. 5, an Si substrate 51 having a first adhesive layer 52 and a LED epitaxial layer 55 having a nonconductive reflective layer 56 or a mirror layer formed on a bottom surface thereof are provided. The LED epitaxial layer 55 is an active structure and fabricated by II-VI or III-V alloys, for example, direct-bandgap LEDs, AlGaInP. The LED epitaxial layer 55 previously grows on a temporary GaAs substrate 59 and has a pn junction structure, wherein the upper one is a p-type layer 55A and the lower one is an n-type layer 55B. In this embodiment, the p-type layer 55A is arranged to be adjacent to the reflective layer 56 and the n-type layer 55B to the temporary substrate 59. The reflective layer 56 is a composite material including two materials. In this embodiment, the reflective layer 56 includes a metal 561 and a insulator 562, wherein the metal 561 is not provided for omhic contact, and the insulator 562 is adjacent to the LED epitaxial layer 55. The composite reflective layer 56 is not restricted, and can be Al/Al2O3, Al/SiO2, Al/MgF2, Pt/Al2O3, Pt/SiO2, Pt/MgF2, Ag/Al2O3, Ag/SiO2, Ag/MgF2, etc.
  • In step B, the [0029] LED eptaxitial layer 55 and the reflective layer 56 are bonded to the Si substrate 51 by thermal pressing, wherein the metal 561 is attached and adjacent to the first adhesive layer 52, as shown in FIG. 5. The temporary substrate 59 is then removed.
  • In step C, an n-type [0030] ohmic contact electrode 60 having the same type as the n-type layer 55B of the LED eptaxitial layer 55 is formed on the left top surface thereof by physical vapor deposition. FIG. 6 shows the cross section view of the structure developed in this step.
  • In step D, the right top surface of the [0031] LED epitaxial layer 55 is etched and stopped beneath the pn junction to form a metal contact layer 58 and expose the p-type layer 55A. In step E, a p-type ohmic contact electrode 65 having the same type as the p-type layer 55A of the exposed LED eptaxitial layer 55 is formed by physical vapor deposition. FIG. 7 shows the cross section view of the structure developed in these two steps. By supplying appropriate voltage to the ohmic contact electrodes 60, 65, the LED epitaxial layer 55 can be excited and emit light, wherein the backward light can be reflected by the reflective layer 56. Therefore, the light beams are all propagated frontward and the short-wavelength light would not be absorbed by the Si substrate 51, the brightness is hence promoted.
  • The LED eptaxitial layer in the present invention is not limited to the above form, and can alternatively has the p-type layer on the lower layer and the n-type layer on the upper layer, or further includes confining layers having the same types as adjacent layers on their surfaces respectively. [0032]
  • FIG. 8 shows the cross section view of the second embodiment in accordance with the present invention. In this embodiment, a [0033] transparent electrode 70 is applied on the n-type ohmic contact electrode 60 and the exposed n-type layer 55B of the LED epitaxial layer 55 to advance electric conduction. Additionally, a second adhesive layer 57 is applied below the reflective layer 56 to reinforce the attachment of the structures.
  • FIG. 9 shows the cross section view of the third embodiment in accordance with the present invention, in which the [0034] reflective layer 56 is composed of a high-dielectric material 563 and a low-dielectric material 564. The high-dielectric material 563 has a refractive index larger than 2.1, and the low-dielectric material 564 has a refractive index less than 1.56, for example, (TiO2/SiO2)n, (Si/SiO2)n, (Si/Si3N4)n, wherein n is number of pairs. By means of properly arranging the layers of different refractive indices and thicknesses, high reflection of desired wavelengthes can be achieved.
  • In the present invention, the [0035] reflective layer 56, the first and second adhesive layers 52, 57 and the ohmic contact electrodes 60, 65 preferably perform single function, so that the most appropriate materials can be applied. For example, the first adhesive layer 52 and/or the second adhesive layer 57 can be a polymer nonconductor. Furthermore, reflectivity of the LED according to the present invention can be promoted above 98% at wavelength larger than 600 nm and above 90% at wavelength less than 600 nm.
  • Although the present invention has been explained in relation to its preferred embodiments, it is to be understood that many other possible modifications and variations can be made without departing from the spirit and scope of the invention as hereinafter claimed. [0036]

Claims (20)

What is claimed is:
1. A method for producing a high-brightness light emitting diode, comprising steps of:
A) forming a reflective layer on an LED epitaxial layer and a first adhesive layer on an Si substrate, wherein said LED epitaxial layer is grown on a temporary substrate and has a pn junction structure to define a first-type layer adjacent to said temporary substrate and a second-type layer;
B) bonding said reflective layer to said first adhesive layer by thermal pressing and then removing said temporary substrate;
C) forming a first-type ohmic contact electrode on partial top surface of said LED eptaxitial layer by physical vapor deposition;
D) etching at least partial remained LED epitaxial layer from top surface thereof and stopping at said second-type layer to form a metal contact layer; and
E) forming a second-type ohmic contact electrode on said metal contact layer by physical vapor deposition.
2. The method as claimed in claim 1, wherein said LED eptaxitial layer further comprises a p-type confining layer and a n-type confining layer.
3. The method as claimed in claim 1, wherein said first ohmic contact electrode further comprises a transparent electrode thereon.
4. The method as claimed in claim 1, wherein said reflective layer comprises a metal and an insulator.
5. The method as claimed in claim 4, wherein said insulator is adjacent to said LED epitaxial layer.
6. The method as claimed in claim 4, wherein said metal is selected from the group consisting of Al, Ag, Au, Pt, Pd.
7. The method as claimed in claim 4, wherein said insulator is selected from the group consisting of Al2O3, MgF2, SiO2, TiO2 and Si3N4.
8. The method as claimed in claim 1, wherein said reflective layer comprises a high-dielectric material and a low-dielectric material.
9. The method as claimed in claim 8, wherein said low-dielectric material is adjacent to said LED epitaxial layer.
10. The method as claimed in claim 8, wherein said high-dielectric material has a refractive index larger than 2.1, and said low-dielectric material has a refractive index less than 1.56.
11. The method as claimed in claim 8, wherein said high-dielectric material is selected from the group consisting of TiO2, CeO2, and Si.
12. The method as claimed in claim 8, wherein said low-dielectric material is selected from the group consisting of Al2O3, MgF2, SiO2 and Si3N4.
13. The method as claimed in claim 1, wherein said etching of step D) is chemical wet etching or dry etching.
14. The method as claimed in claim 1, wherein said physical vapor deposition of steps C) and E) is e-gun evaporation deposition.
15. The method as claimed in claim 1, wherein said physical vapor deposition of steps C) and E) is thermal evaporation deposition.
16. The method as claimed in claim 1, wherein said physical vapor deposition of steps C) and E) is sputter deposition.
17. The method as claimed in claim 1, wherein said reflective layer further comprises a second adhesive layer therebelow to reinforce attachment with said first adhesive layer.
18. The method as claimed in claim 17, wherein said second adhesive layer is a metal.
19. The method as claimed in claim 1, wherein said first adhesive layer is a metal.
20. The method as claimed in claim 1, wherein said first adhesive layer is a polymer nonconductor.
US10/256,713 2001-11-07 2002-09-30 Method for producing high-brightness LED Abandoned US20030087463A1 (en)