US20030102530A1 - Semiconductor wafer, method of manufacturing the same and semiconductor device - Google Patents
Semiconductor wafer, method of manufacturing the same and semiconductor device Download PDFInfo
- Publication number
- US20030102530A1 US20030102530A1 US10/336,808 US33680803A US2003102530A1 US 20030102530 A1 US20030102530 A1 US 20030102530A1 US 33680803 A US33680803 A US 33680803A US 2003102530 A1 US2003102530 A1 US 2003102530A1
- Authority
- US
- United States
- Prior art keywords
- wafer
- plane
- insulating film
- film
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The object of the present invention is to provide a semiconductor wafer in which a diffusion of Cu generated by a thermal treatment such as a Cu wiring formation step into silicon is prevented, and variations of transistor characteristics are lessened. The object of the present invention is to provide a method of manufacturing the same and a semiconductor device formed from the same.
In the present invention, a protection insulating film for preventing Cu from diffusing into the inside of the wafer is formed on a peripheral portion of a principal plane, a external side plane and a rear plane of the wafer. With this protection insulating film, the diffusion of Cu that is a wiring material into a chip formation region of the wafer is prevented, so that the variations of the transistor characteristic.
Description
- 1. Field of the Invention
- The present invention relates to a semiconductor wafer (hereinafter, referred to as a wafer) in which a semiconductor device is formed, a novel semiconductor device exhibiting less variation in a transistor characteristic, and a method for manufacturing the same.
- 2. Description of the Related Art
- A wafer formed of silicon or germanium, which is used for a semiconductor device, has heretofore been manufactured usually by slicing a cylindrical ingot that is grown by a single crystal growth method such as a high frequency induction-heating method or a pulling-up method. A plurality of processed semiconductor integrated circuits are formed on a principal plane of the wafer which has been formed from the ingot. Thereafter, the wafer is cut along scribe lines into chips in which an integrated circuit area is formed, and the chips are separated from each other.
- FIG. 1 is a section view showing a conventional semiconductor device formed in a semiconductor substrate. The semiconductor device is formed on a wafer, and the wafer is cut into chips in which an integrated circuit is formed. The chips are finally separated from each other. Accordingly, FIG. 1 is a section view of the chip, and especially illustrates a chip formed in a portion of the wafer, which is close to an external peripheral surface and a peripheral region where no integrated circuit is formed. A
semiconductor substrate 1 is, for example, a p-type silicon semiconductor. The left side of FIG. 1 is an external peripheral portion of the wafer and a peripheral portion thereof, and in these portions the surface of thesemiconductor substrate 1 is exposed for the reason described later. An inner portion of the external peripheral portion and the peripheral portion, that is, a central portion and a right side, show a chip region. In the chip region, anelement isolation region 2 formed of silicon dioxide (SiO2), which has a Shallow Trench Isolation (STI), is formed by a Local Oxidation of Silicon (LOCOS) method. N-type source/drain regions 3 are formed in an element region partitioned by theelement isolation region 2. A gate electrode 5 formed of polysilicon or the like is formed by a thermal oxide method on a portion of a gate insulating film formed of a silicon oxide film, the portion thereof being located between the source/drain regions 3. Thegate insulating film 4 is formed on the entire surface of thesemiconductor substrate 1, and, on thesemiconductor substrate 1, a silicon oxide film is formed so as to cover the gate electrode 5. - The silicon oxide film is subjected to an anisotropic etching such as an RIE (Reactive Ion Etching) and processed to a side wall insulating film6 left on the side wall of the gate electrode 5. Subsequently, on the
semiconductor substrate 1, aninterlayer insulating film 7 formed of such as BPSG (Boron-doped Phospho-Silicate Glass) is deposited, and flattened. A contact hole which communicates with one of the source/drain regions 3 is formed in theinterlayer insulating film 7, and aconnection wiring 8 formed of such as tungsten, for example (W) is filled in the contact hole. A metal film formed of copper (Cu) is deposited on the flattened surface of theinterlayer film 7, and patterned, thus forming acopper wiring 9 electrically connected to theconnection wiring 8. On thecopper wiring 9, a protection insulating film can be formed, or a plurality of copper wirings can be formed interposing the interlayer insulating film during the formation of the protection insulating film. - The above-described copper wiring technology used for semiconductor devices has been involved in a problem that diffusion of copper into a silicon wafer is seriously anxious for.
- In the conventional copper wiring technology, copper is principally covered with a barrier film such as Ta, TiN and SiN. However, copper may attach to a wafer edge and a rear surface of the wafer during formation of the barrier film, or the copper may attach to them from a manufacturing apparatus and a wafer carrier. Since resist is usually removed from the wafer edge by about 1 to 3 mm before the time of patterning the wafer, the surface of the semiconductor substrate corresponding to the portion where the resist is removed is exposed after an etching treatment.
- A SiN film is formed on a region where transistors are formed, so that the diffusion of the copper into that region can be prevented. However, the silicon substrate formed of silicon is exposed in its rear surface and its wafer edge portion, and in such situation, when the wafer is subjected to the copper processing step, the copper diffuses into a chip from the external periphery of the wafer, so characteristics of the transistors formed in the chip may vary.
- To be more specific, with regard to the conventional semiconductor substrate, for example, a silicon wafer is formed of only silicon. In order to prevent the attachment of resist to the carrier, the resist of the periphery portion of the wafer is removed in manufacturing steps of the semiconductor device using such wafer, especially in a lithography step as described above. Accordingly, since the wafer edge portion is always exposed to etching atmosphere, so that the silicon substrate comes to be exposed. As a result, the contamination of the semiconductor substrate due to the attachment of the copper to the silicon portion in forming the copper wiring occurs as described above. Furthermore, there has been a problem that when a high concentration semiconductor substrate having a p-type epitaxial silicon semiconductor layer formed therein (p-epi on p+ substrate) is employed, impurities diffuse to the outside of the semiconductor substrate during a thermal step.
- The present invention was made in view of the foregoing circumstances, and the object of the present invention is to provide a wafer which prevents a diffusion of copper to silicon due to a thermal treatment such as a copper wiring formation step and lessens the variations in transistor characteristics, a method for manufacturing the same, and a semiconductor device formed of the same.
- The present invention is featured by forming a protection insulating film in a peripheral area (peripheral portion) of a principal plane of the wafer, an external side plane and a rear plane, which prevents a diffusion of copper to the inside of the wafer, specifically a protection insulating film formed of a material having a small Cu diffusion coefficient. The protection insulating film prevents the copper that is a wiring material from diffusing into a chip formation region of the wafer, and controls the changes of transistor characteristics caused by the Cu diffusion.
- The wafer of the present invention is first characterized in that the wafer has a semiconductor wafer having a first plane where an integrated circuit is formed, a second plane and a peripheral area, and a protection film formed in the second plane and the peripheral area. The wafer of the present invention is secondly characterized in that the wafer has a semiconductor wafer having a first plane where an integrated circuit is formed, a second plane and a peripheral area, and a protection film formed of silicon nitride, which is formed in the second plane and the peripheral area.
- A first aspect of a method for manufacturing the wafer of the present invention is that the method comprises the step of: forming a protection film on a first plane having an integrated circuit formed therein, a second plane and a peripheral area of a semiconductor wafer; and removing the protection film in a region forming the integrated circuit on the first plane. A MOS transistor which has a gate electrode having a side wall insulating film on its side wall is included in the integrated circuit. The foregoing protection insulating film may be formed in the step for forming this side wall insulating film.
- Furthermore, a second aspect of the method for manufacturing the wafer of the present invention is that the method comprises the steps of: growing a cylindrical semiconductor single crystal ingot; forming a protection insulating film in a surface of the single crystal ingot, the protection insulating film preventing a diffusion of copper into the interior of the single crystal ingot; and slicing the single crystal ingot, thereby forming a plurality of semiconductor wafers, each having an external side plane, in which the protection insulating film is formed. The second aspect of the method for manufacturing the wafer of the present invention may comprises a step for forming a protection insulating film which extends to the external side plane and prevents the diffusion of the copper to the interior of the semiconductor wafer.
- A semiconductor device of the present invention comprises a semiconductor chip having a first plane where an integrated circuit is formed and a second plane, the integrated circuit formed in the first plane; and a protection insulating film formed on the entire surface of the second plane.
- Other objects, features, and advantages of the present invention will become apparent from the following detailed description. It should be understood, however, that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
- A more complete appreciation of the present invention and many of its attendant advantages will be readily obtained by reference to the following detailed description considered in connection with the accompanying drawings, in which:
- FIG. 1 is a section view showing a manufacturing step of a conventional semiconductor device;
- FIG. 2 is a plan view showing a principle plane of a wafer of a first embodiment;
- FIGS.3(a) and 3(b) are section views showing manufacturing steps for manufacturing the wafer of the first embodiment;
- FIGS.4(a) and 4(b) are section views showing manufacturing steps for manufacturing the wafer of the first embodiment;
- FIG. 5 is a section view showing a manufacturing steps for manufacturing the wafer of the first embodiment;
- FIG. 6 is a plan view showing a principal plane of the wafer of the first embodiment;
- FIGS.7(a) and 7(b) are section views showing manufacturing steps for manufacturing a wafer of a second embodiment;
- FIG. 8 is a section view showing a manufacturing step of the wafer of the second embodiment;
- FIG. 9 is a section view showing a manufacturing step of a wafer of a third embodiment;
- FIGS.10(a) and 10(b) are section views showing manufacturing steps for manufacturing the wafer of the third embodiment;
- FIGS.11(a) and 11(b) are section views showing manufacturing steps for manufacturing a wafer of a fourth embodiment;
- FIGS.12(a) and 12(b) are section views showing manufacturing steps for manufacturing the wafer of the fourth embodiment;
- FIG. 13 is a section view showing a manufacturing step for manufacturing the wafer of the fourth embodiment;
- FIG. 14 is a plan view showing a principal plane of the wafer of the fourth embodiment;
- FIG. 15 is a plan view showing a principal plane of a wafer of a fifth embodiment;
- FIG. 16 is a plan view of a semiconductor substrate of the fifth embodiment;
- FIGS.17(a) and 17(b) are perspective views of an ingot of the fifth embodiment;
- FIGS.18(a) and 18(b) are perspective views of the ingot of the fifth embodiment and a plan view of a wafer of the fifth embodiment;
- FIGS.19(a) and 19(b) are section views showing manufacturing steps for manufacturing a semiconductor device of a sixth embodiment;
- FIGS.20(a) and 20(b) are section views showing manufacturing steps for manufacturing the semiconductor device of the sixth embodiment; and
- FIG. 21 is a section view showing the semiconductor device of the sixth embodiment.
- Embodiments of the present invention will be described with reference to the accompanying drawings in detail. A first embodiment will be described with reference to FIGS.2 to 6.
- FIG. 2 is a plan view of a principal plane of a wafer, FIGS.3(a) to 5 are section views of the wafer, and FIG. 6 is a plan view of the principal plane of the wafer after formation of a chip in its chip formation region. A
wafer 100 is formed of, for example, a p-type silicon semiconductor substrate which is obtained by slicing an semiconductor ingot and processing to a predetermined shape. A trench is formed in its principal plane, and an insulating film such as a silicon oxide film (SiO2) is filled in the trench. Thus, an element isolation region such as an STI structure is formed. Achip formation region 101 is formed on the principal plane of thewafer 100 when the STI structure is formed. After the element isolation region is formed, a silicon oxide (SiO2)film 102 is formed on the entire surface of thewafer 100 by a thermal oxidation and the like. Next, a silicon nitride (SiN)film 103 is deposited on thesilicon oxide film 102 by a LPCVD (Low Pressure Chemical Vapor Deposition) method. Subsequently, apolysilicon film 104 is deposited on thesilicon nitride film 103 by the LPCVD method. Furthermore, asilicon nitride film 105 is deposited on thepolysilicon film 104 by the LPCVD method (FIG. 3(a)). - Next,
photoresist 106 is applied onto thesilicon nitride film 105 formed on the principal plane of thewafer 100, and thephotoresist 106 on the peripheral portion of thewafer 100 is removed by patterning thephotoresist 106. Then, the portions of thesilicon nitride film 105 on the peripheral portion of the principal plane, the external side plane and the rear plane of thewafer 100 are removed by an isotropic etching such method as an RIE using the patternedphotoresist 106 as a mask. Specifically, thesilicon nitride film 105 and thephotoresist 106 formed on thesilicon nitride film 105 cover the region other than the peripheral portion of the principal plane where the chip is to be formed (FIG. 3(b)). - Next, the
photoresist 106 is removed, and then thepolysilicon film 104 on the peripheral portion of the principal plane of thewafer 100, the external side plane of thewafer 100 and the rear plane of thewafer 100 is oxidized by a thermal treatment step, and asilicon oxide film 107 is formed (FIG. 4(a)). Subsequently, thesilicon nitride film 105 is removed, and thereafter thepolysilicon film 104 which has been covered with thesilicon nitride film 105 is removed by, for example, a dry etching method, so as to expose thesilicon nitride film 103 partially (FIG. 4(b)). Next, the exposedsilicon nitride film 103 is removed by hot phosphoric acid using thesilicon oxide film 107 on the peripheral portion of the principal plane of thewafer 100, the external side plane of thewafer 100, and the rear plane of thewafer 100 as a mask (FIG. 5). - Thus, the main central area of the principal plane of the
wafer 100 where the chip is formed is covered with thesilicon oxide film 102, and the peripheral portion of the principal plane, the external side plane, and the rear plane are covered with a stacked body composed of thesilicon nitride film 103 and thesilicon oxide film 107. Thesilicon oxide film 102 is used as a gate insulating film formed on thewafer 100. - The
wafer 100 is subjected to treatments (a thin film formation treatment, an oxidation treatment, a doping treatment, an annealing treatment, a resist treatment, an exposure treatment, an etching treatment and the like) after the element isolation region formation step and the gate insulating film formation step, thus forming an integrated circuit in each of thechip formation region 101, and thechip formation region 101 is processed to thechip 108. Thereafter, thewafer 100 is cut along the scribe line formed in its principal plane, and thechip 108 is separated from each other (FIG. 6). Since the chips A, B and C partially covered with theprotection insulating film 107 shown in FIG. 5 sometimes exhibit unstable characteristics, these chips are not used as the product. - Since the wafer used in this embodiment is covered with the silicon nitride film covered with the silicon oxide film in its peripheral portion of the principal plane, its external side plane and its rear plane, it is possible to prevent the silicon substrate from being exposed in its peripheral portion of the principal plane during the Cu wiring formation step among the foregoing treatment steps. As a result, diffusion of copper that is a wiring material into the chip formation region of the wafer can be prevented, and variations of transistor characteristics due to the copper diffusion can be controlled. Specifically, the silicon nitride film and the silicon oxide film are used as a protection insulating film for preventing the copper diffusion.
- Next, a second embodiment will be described with reference to FIGS. 7 and 8.
- FIGS. 7 and 8 are section, a views of a wafer. The
wafer 200 is formed of, for example, a p-type silicon semiconductor substrate obtained by slicing an ingot and processing to a predetermined shape. Thewafer 200 forms a trench in its principal plane, and an insulating film such as a silicon oxide (SiO2) film is filled in the trench, thus forming an element isolation region of an STI structure. When the element isolation region is formed, a chip formation region (not shown) is formed in the principal plane of thewafer 200. After the formation of the element isolation region, a silicon oxide (SiO2)film 201 is deposited by, for example, an LPCVD method on the entire surface of the silicon wafer 200 (FIG. 7(a)). - Subsequently,
photoresist 202 is applied onto thesilicon oxide film 201 on the principal plane of thewafer 200, and the photoresist is patterned, thus removing the portion of thephotoresist 202 on the peripheral portion of the principal plane of thewafer 200. Then, thesilicon oxide film 201 on the peripheral portion of the principal plane, the external side plane and the rear plane of thewafer 200 is removed by an isotropic etching such as an RIE. Thus, the region other than the peripheral portion of the principal plane, where chips are to be formed, is covered with thesilicon oxide film 201, and thephotoresist 202 is left on the film 201 (FIG. 7(b)). - Next, after removing the
photoresist 202, asilicon nitride film 203 is deposited on thesilicon oxide film 201 by, for example, a LPCVD method. Thereafter, the surface of thesilicon nitride film 203 is subjected to a flattening treatment by a CMP (Chemical Mechanical Polishing) technique using thesilicon oxide film 201 as a stopper until thesilicon oxide film 201 is exposed (FIG. 8). As a result of the flattening treatment, the situation where thesilicon nitride film 203 is formed on the peripheral portion of thewafer 200 and the rear plane thereof is created. Thesilicon oxide film 201 is afterward removed by etching. - Thus, the peripheral portion of the principal plane, the external side plane and the rear plane of the
wafer 200 are covered with thesilicon nitride film 203. Thewafer 200 is subjected to treatments (a thin film formation treatment, an oxidation treatment, a doping treatment, an annealing treatment, a resist treatment, an exposure treatment, an etching treatment and the like) after the element isolation region formation step, thus forming an integrated circuit in each of the chip formation region, and the chip formation regions are processed to thechip 108. Thereafter, the wafer is cut along the scribe line formed in its principal plane, and the chips are separated from each other. - Since the wafer used in this embodiment is covered with the silicon nitride film covered with the silicon oxide film in its peripheral portion of the principal plane, its external side plane and its rear plane, it is possible to prevent the silicon substrate from being exposed in its peripheral portion of the principal plane during the Cu wiring formation step among the foregoing treatment steps. Specifically, the silicon nitride film is used as a protection insulating film for preventing the copper diffusion. By the presence of this protection insulating film, diffusion of copper that is a wiring material into the chip formation region of the wafer can be prevented, and variations of transistor characteristics due to the copper diffusion can be controlled.
- Next, a third embodiment of the present invention will be described with reference to FIGS. 9 and 10(a) and 10(b). FIGS. 9,10(a) and 10(b) are section, a views for explaining manufacturing steps to form a protection insulating film on a wafer.
- The
wafer 300 is formed of, for example, a p-type silicon semiconductor substrate obtained by slicing an ingot and processing to a predetermined shape. This embodiment has a feature in that in order to form the protection insulating film, a dummy wafer is employed. Thesilicon wafer 300 and thedummy wafer 301 having a diameter slightly smaller than that of thewafer 300 are stacked. The peripheral portion of thesilicon wafer 300 projects from the dummy wafer after stacking thewafer 300 and thedummy wafer 301 upon another (FIG. 9). In a situation where the plurality of silicon wafers and dummy wafers are placed upon another, a silicon nitride (SiN) film is deposited by a LPCVD method around the lamination body composed of the plurality of silicon wafers and dummy wafers (FIG. 10(a)). Thereafter, when the silicon wafers are separated from the lamination body, the silicon wafer having a wafer edge portion in which the silicon nitride film is deposited is prepared (FIG. 10(b)). However, the central portion of the rear plane is not covered with the silicon nitride film as shown in FIG. 10(b). Accordingly, before the Cu wiring step is performed, the silicon nitride film is left as a protection insulating film for preventing the diffusion of copper to the interior of the wafer in the wafer processing step when the side wall insulating film of the gate electrode is formed by the silicon nitride film. Thus, it is possible to cover a specified portion with the protection insulating film completely. In other words, in such case, the protection insulating film is formed in the two steps, that is, in the pretreatment prior to the wafer processing step and in the wafer processing step. - As described above, the peripheral portion of the principal plane, the side plane and the rear plane of the
wafer 300 are covered with thesilicon nitride film 302. Thewafer 300 is subjected to treatments (a thin film formation treatment, an oxidation treatment, a doping treatment, an annealing treatment, a resist treatment, an exposure treatment and an etching treatment) after the element isolation region formation step, and an integrated circuit is formed in each chip formation region. The chip formation region is processed to a chip. Thereafter, the wafer is cut along the scribe line formed in the principal plane of thewafer 300, and the chip is separated from each other. - Since the wafer used in this embodiment is covered with the silicon nitride film covered with the silicon oxide film in its peripheral portion of the principal plane, its external side plane and its rear plane, it is possible to prevent the silicon substrate from being exposed in its peripheral portion of the principal plane during the Cu wiring formation step among the foregoing treatment steps. Specifically, the silicon nitride film is used as a protection insulating film for preventing the copper diffusion. By the presence of this protection insulating film, diffusion of copper that is a wiring material into the chip formation region of the wafer can be prevented, and variations of transistor characteristics due to the copper diffusion can be controlled. Moreover, since the step in the wafer processing steps is used, the step is simplified.
- A material of the dummy wafer is not limited to silicon, any material may be satisfactorily used for the dummy wafer as long as the dummy wafer is used for a spacer.
- Next, a fourth embodiment will be described with reference to FIGS.11(a) to 14.
- This embodiment has a feature in that two wafers are adhered to each other, thus forming a single wafer. FIGS.11(a), 11(b) and FIGS. 12(a), 12(b) are sectional views for explaining steps to form a protection insulating film on a wafer, and FIG. 13 is a plan view of the wafer. The
wafers silicon nitride film 401 is deposited on the entire surface of thewafer 400 a by a LPCVD method. Subsequently, the surface of thesilicon nitride film 401 is oxidized by a thermal treatment, and asilicon oxide film 402 is formed (FIG. 11(a)). - Next, the
other silicon wafer 400 b is integrated with thewafer 400 a by adhering thewafer 400 b to thesilicon oxide film 402 formed on the silicon nitride film 401 (FIG. 11(b)). Subsequently, photoresist (not shown) patterned is applied onto thewafer 400 b, and thereafter thewafer 400 b is etched by a RIE using the photoresist as a mask. Thus, atrench 403 reaching to thesilicon nitride film 401 is formed on the peripheral portion of the principal plane of thewafer 400 b (FIG. 12(a)). Asilicon nitride film 404 is deposited by a CVD method (FIG. 12(b)). Thereafter, the surface of thesilicon nitride film 404 is flattened by a CMP until the principal plane of thewafer 400 b is exposed (FIG. 13). - It is possible to produce a situation where a part of the peripheral portion of the principal plane, the external side plane and the rear plane of the
wafer 400 b are covered with the silicon nitride film. Although the part of the peripheral portion of the principal plane is exposed as shown in FIG. 14, the copper never enters from the peripheral portion of thewafer 400 b into the central portion thereof. - As described above, the peripheral portion of the principal plane, the external side plane and the rear plane of the wafer are covered with the silicon nitride film. The wafer is subjected to treatments (a thin film formation treatment, an oxidation treatment, a doping treatment, an annealing treatment, a resist treatment, an exposure treatment and an etching treatment) after the element isolation region formation step, and an integrated circuit is formed in each chip formation region. The chip formation region is processed to a chip. Thereafter, the wafer is cut along the scribe line formed in the principal plane of the wafer, and the chip is separated from each other.
- Since the wafer used in this embodiment is covered with the silicon nitride film covered with the silicon oxide film in its peripheral portion of the principal plane, its external side plane and its rear plane, it is possible to prevent the silicon substrate from being exposed in its peripheral portion of the principal plane during the Cu wiring formation step among the foregoing treatment steps. Specifically, the silicon nitride film is used as a protection insulating film for preventing the copper diffusion. By the presence of this protection insulating film, the diffusion of copper that is a wiring material into the chip formation region of the wafer can be prevented, and variations of transistor characteristics due to the copper diffusion can be controlled. Moreover, since the step in the wafer processing steps is used, the step is simplified.
- Next, a fifth embodiment of the present invention will be described with reference to FIGS.15 to 18.
- FIG. 15 is a plan view of a wafer having a side plane covered with a protection insulating film for preventing diffusion of copper, and FIG. 16 is a partial section view showing a half of a principal plane of the wafer and a half of the left portion of the wafer. FIG. 17 is a perspective view of an ingot, and FIG. 18 is a perspective view of the ingot and a plan view of the wafer. In this embodiment, the peripheral portion of the
wafer 500 is covered with aprotection insulating film 501 for preventing the diffusion of copper. Specifically, the portion extending from the outermost of the wafer to the central portion of the wafer by several mm, for example, 1 mm, is composed of theprotection insulating film 501 formed of a silicon nitride film (FIG. 15). Accordingly, an end portion of theinterlayer insulating film 503 formed of a silicon oxide film which covers thegate electrode 502 is disposed inside the external periphery of thewafer 500, and the end portion of theinterlayer insulating film 503 is formed on theprotection insulating film 501. Thus, even though the Cu wiring is formed on theinterlayer insulating film 503, the Cu wiring does not contact with the silicon wafer directly, so that the diffusion of the copper into the wafer can be prevented (FIG. 16). Furthermore, also when a high concentration semiconductor substrate like a p-epitaxial on p+ substrate is employed, the exposed portion of the rear plane at the peripheral portion of the wafer is formed of a silicon nitride (SiN), so that diffusion of impurities toward the outside of the wafer due to thermal steps during the manufacturing of the semiconductor device can be prevented. - The
wafer 500 shown in FIG. 5 is manufactured in the following manner. The silicon ingot prepared, for example, by a well-known pulling-up method is processed to a predetermined diameter (FIG. 17(a)). In the conventional method, the ingot is sliced, thus cutting out the wafer. In this embodiment, the entire surface of theingot 510 is subjected to a nitriding treatment, whereby the entire surface of the ingot is converted to asilicon nitride film 501 serving as a protection insulating film. As another method, there is a method in which thesilicon nitride film 501 is deposited to a predetermined thickness on the surface of theingot 510 by a chemical vapor deposition (CVD) method (FIG. 17(b)). Theingot 510 covered with theprotection insulating film 501 formed in the above described manner is sliced to a predetermined thickness, and the surface of the sliced ingot is processed. Thus, a wafer shown in FIG. 15 is formed. - The protection insulating film for preventing the diffusion of copper, which is formed on the wafer, is not limited to the foregoing silicon nitride film, and, for example, a silicon oxide film may be satisfactory. Such silicon oxide film is formed in the following manner. An oxidation treatment by a thermal oxidation method is performed for the foregoing
ingot 510 that has not been undergone a surface treatment, thus chemically converting the surface of the ingot to asilicon oxide film 505 having a predetermined thickness (FIG. 18(a)). As another method, there is a method to deposit asilicon oxide film 505 having a predetermined thickness on the surface of theingot 510 by a chemical vapor deposition (CVD) method. Theingot 510 that has been subjected to the surface treatment is sliced and polished, thus obtaining asilicon wafer 500 having a peripheral portion formed of the silicon oxide film 505 (FIG. 18(b)). - In this embodiment, since the foregoing protection insulating film is formed on the peripheral portion of the principal plane of the wafer where the integrated circuit is formed, the peripheral portion of the principal plane of the wafer in which no photoresist is inherently formed is not exposed by etching when the Cu wiring is formed on the principal portion. Accordingly, the copper does not diffuse into the chip formation region of the wafer from this portion. Furthermore, since the rear plane of the wafer is exposed, it is expected that the copper may diffuse from the rear plane of the wafer. When such diffusion must be prevented, the protection insulating film such as a silicon oxide film or a silicon nitride film can be formed on the rear plane of the wafer after the preparation of the wafer. Among the wafer treatment steps, in a step for forming a side wall insulating film formed of a silicon nitride film, which is performed before the Cu wiring formation step, the foregoing silicon nitride film as the protection insulating film may be formed.
- A sixth embodiment of the present invention will be described with reference to FIGS.19(a) and 19(b), FIGS. 20(a) and 20(b) and FIG. 21. In this embodiment, a protection insulating film for preventing a diffusion of copper is formed by utilizing the formation of the foregoing side wall insulating film of the gate electrode. A method of this embodiment will be described below.
- FIGS.19(a) and 19(b) and FIGS. 20(a) and 20(b) are sectional views showing manufacturing steps of a semiconductor device of this embodiment. The semiconductor device is formed on a wafer. The wafer is finally cut, and each chip in which the semiconductor device is formed is separated from others. Accordingly, FIGS. 19(a) and 19(b) and FIGS. 20(a) and 20(b) show sectional views of the chip communicated with the peripheral portion of the wafer. This peripheral portion of the wafer is removed when the chip is separated from each other. The
semiconductor device 601 is formed of, for example, a p-type silicon semiconductor. The peripheral portion of the wafer is located on the left side of the view. The inside of the peripheral portion of the wafer, that is, the central portion and right side of the drawing, are a chip region. Anelement isolation region 602 of a STI structure, which is formed of SiO2, is formed in the chip region by a LOCOS method. By an ion-implantation, a n-type extension region 603 and source/drain regions 3 are formed in the element region partitioned by theelement isolation region 602. Agate insulating film 604 formed of SiO2 is formed on the chip region of thesemiconductor substrate 601 by a thermal oxidation. Agate electrode 605 formed of polysilicon is formed on the gate insulating film 604 (FIG. 19(a)). - Next, a
silicon nitride film 606 is formed, by a LPCVD method or the like, on the entire surface of thesemiconductor substrate 601, that is, on the principal plane, the external side plane and the rear plane of the wafer (FIG. 19(b)). Next, the portion where the protection insulating film is to be formed is masked, and a sidewall insulating film 607 formed of a silicon nitride film is formed on the side surface of thegate electrode 605 by an isotropic etching such as an RIE. Theprotection insulating film 608 for preventing the diffusion of copper is formed on the peripheral portion, the external side plane and the rear plane of the wafer. Thereafter, impurities are implanted into source/drain formation regions using the sidewall insulating film 607 as a mask, and the n-type source/drain regions 609 is formed (FIG. 19(a)). - Next, an
interlayer insulating film 610 formed of, for example, BPSG is deposited on thesemiconductor substrate 601, and flattened. Furthermore, asilicon nitride film 611 having a smaller thickness than that of theinterlayer insulating film 610 is deposited on the flattened surface of theinterlayer insulating film 610. Acontact hole 612 reaching to any of the source/drain regions 609 is formed, and abarrier metal layer 613 formed of, for example, Ti or TiN/Ti is formed within thecontact hole 612 and on the surface of thesilicon nitride film 611. Furthermore, aCu film 614 is deposited on thebarrier metal layer 613. Then, aCu wiring 614 is formed by patterning the Cu film 614 (FIG. 19(b)). A protection insulating film may be further formed on theCu wiring 614, or a plurality of upper Cu wirings may be formed interposing an interlayer insulating film between theCu wiring 614 and the upper Cu wirings during formation of the protection insulating film. As shown in FIG. 20, the sidewall insulating film 608 formed of a silicon nitride film prevents the diffusion of copper into the inside of thewafer 601. Since a coefficient of diffusion of copper into the silicon nitride film is small, copper atoms and copper composition remain in the surface of theprotection insulating film 608, within theprotection insulating film 608 and at the interface between theprotection insulating film 608 and the wafer. For this reason, it is possible to prevent the diffusion of the copper atoms and the copper composition almost perfectly. - In this embodiment, since the foregoing protection insulating film is formed in the peripheral portion of the principal plane of the wafer, in which the integrated circuit is formed, the peripheral portion of the principal plane of the wafer in which no photoresist is inherently formed is not exposed by etching when the Cu wiring is formed on the principal portion. Accordingly, the copper does not diffuse into the chip formation region of the wafer from this portion. Among the wafer treatment steps, in a step for forming a side wall insulating film formed of a silicon nitride film, which is performed before the Cu wiring formation step, the foregoing silicon nitride film as the protection insulating film may be used.
- In the present invention, when a part of the wafer treatment steps is employed, the protection insulating film may be formed in a step other than the side wall insulating formation step. It is possible to use any step, for example, the step for forming the
silicon nitride film 611 as shown in FIG. 20(b), as long as it is a step before the Cu wiring formation step. - Since the silicon nitride film or the silicon oxide film as the protection insulating film for preventing the diffusion of the copper is formed on the peripheral portion, the external side plane and the rear plane of the wafer, it is possible to prevent the diffusion of the copper into the semiconductor substrate, so that the variation of the transistor characteristic, for example, a threshold, can be controlled. Furthermore, the protection insulating film can be formed by using a step among the wafer treatment steps for forming the integrated circuit in the chip region of the wafer, so that the manufacturing steps can be simplified.
- While there has been illustrated and described what are presently considered to be preferred embodiment of the present invention, it will be understood by those skilled in the art that various changes and modifications may be made, and equivalents may be substituted for devices thereof without departing from the true scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teaching of the present invention without departing from the central scope thereof. Therefore, it is intended that this invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention includes all embodiments falling within the scope of the appended claims.
Claims (16)
1. A semiconductor wafer comprising:
a semiconductor wafer having a first plane in which an integrated circuit is going to be formed, a second plane opposite the first plane and a peripheral region between the first and the second planes; and
a protection film formed on said second plane and said peripheral region.
2. The semiconductor wafer according to claim 1 , wherein said protection film is a silicon nitride film.
3. The semiconductor wafer according to claim 1 , wherein said protection film prevents a diffusion of copper into a semiconductor substrate.
4. A method of manufacturing a semiconductor wafer, comprising the steps of:
forming a protection film on substantially the entire outside surface of a semiconductor wafer; and
removing the protection film on a region of said first plane in which an integrated circuit will be formed.
5. The method according to claim 4 , wherein the protection film is a silicon nitride film.
6. The method according to claim 4 , wherein the protection film prevents a diffusion of copper into a semiconductor substrate.
7. The method according to claim 4 , wherein the protection film also forms gate insulation saidewalls of an integrated circuit.
8. A method for manufacturing a semiconductor wafer, comprising the steps of:
growing a cylindrical single crystal semiconductor ingot;
forming a protection insulating film on a surface of said single crystal semiconductor ingot, the protection insulating film preventing a diffusion of copper into said single crystal semiconductor ingot; and
slicing said single crystal semiconductor ingot into a plurality of semiconductor wafers, each semiconductor wafer having an external peripheral plane on which said protection insulating film is formed.
9. The method according to claim 8 , further comprising the step of:
forming a protection insulating film also on a peripheral portion of a principal plane and a rear plane of said semiconductor wafer, the protection insulating film preventing a diffusion of copper into said semiconductor wafer and extending to said external peripheral plane.
10. A semiconductor device comprising:
a semiconductor chip having a first plane in which an integrated circuit is going to be formed and a second plane opposite the first plane; and a protection insulating film formed on said second plane.
11. The semiconductor device according to claim 10 , wherein a copper ion or a copper composition is on a surface of said protection insulating film or within said protection insulating film.
12. The semiconductor device according to claim 10 , wherein a copper ion or a copper composition is contained in a surface between said protection insulating film and said semiconductor chip.
13. The semiconductor device according to claim 10 , wherein said protection insulating film prevents a diffusion of copper into a semiconductor substrate.
14. The semiconductor device according to claim 10 , wherein said protection insulating film is formed of silicon nitride.
15. The semiconductor device according to claim 10 , where the integrated circuit includes at least one element or layer formed of copper.
16. A method of manufacturing a semiconductor device, comprising the steps of:
forming a protection film on substantially the entire outside surface of a semiconductor wafer;
removing the protection film from a region of the semiconductor wafer, and
forming a integrated circuit in the region, the integrated circuit including a copper wiring.