US20040035448A1 - Selective treatment of microelectronic workpiece surfaces - Google Patents
Selective treatment of microelectronic workpiece surfaces Download PDFInfo
- Publication number
- US20040035448A1 US20040035448A1 US10/647,914 US64791403A US2004035448A1 US 20040035448 A1 US20040035448 A1 US 20040035448A1 US 64791403 A US64791403 A US 64791403A US 2004035448 A1 US2004035448 A1 US 2004035448A1
- Authority
- US
- United States
- Prior art keywords
- workpiece
- fluid
- chamber
- etchant
- peripheral edge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
This invention provides a process for treating a workpiece having a front side, a back side, and an outer perimeter. In accordance with the process, a processing fluid is selectively applied or excluded from an outer peripheral margin of at least one of the front or back sides or the workpiece. Exclusion and/or application of the processing fluid occurs by applying one or more processing fluids to the workpiece as the workpiece and corresponding reactor are spinning about an axis of rotation that is generally orthogonal to the center of the face of the workpiece being processed. The flow rate of the one or more processing fluids, fluid pressure, and/or spin rate are used to control the extent to which the processing fluid is selectively applied or excluded from the outer peripheral margin.
Description
- The present application is a: continuation-in-part of copending U.S. patent application Ser. No. 09/437,926 filed Nov. 10, 1999, which is a continuation of International Patent Application No. PCT/US99/05674 filed Mar. 15, 1999 designating the U.S., which claims the benefit of U.S. Provisional Patent Application No. 60/117,474 filed Jan. 27, 1999; and is also a continuation-in-part of copending U.S. patent application Ser. No. 09/437,711 filed Nov. 10, 1999, which is a continuation of International Patent Application No. PCT/US99/05676 filed Mar. 15, 1999 designating the U.S., which claims the benefit of U.S. Provisional Patent Application No. 60/116,750 filed Jan. 23, 1999, and which is also a continuation-in-part of U.S. patent application Ser. Nos. 09/041,649 filed Mar. 13, 1998 and 09/113,435 filed Jul. 10, 1998, which is a continuation-in-part of Ser. No. 09/041,901 filed Mar. 13, 1998.
- The present invention relates to the selective chemical processing of front side, back side and perimeter edge surfaces of microelectronic substrates.
- This invention pertains to treating a substrate such as a semiconductor wafer, e.g., a silicon wafer, so as to remove a thin film, such as a copper or other metal or oxide film, from selected regions on the wafer.
- The fabrication of a microelectronic circuit and/or component from a substrate typically involves a substantial number of processes. Many of these processes involve the deposition of a thin film on the surface of the workpiece followed by contact with a processing liquid, vapor, or gas. In a known process for treating a microelectronic workpiece, such as a silicon wafer, on which microelectronic devices have been fabricated and which has a front, device side, a back, non-device side, and an outer perimeter, thin-film layers are successively applied and etched to form, for example, a metallized interconnect structure. In a typical metallization process, both sides of a semiconductor wafer are coated with a protective film such as a silicon nitride or a silicon oxide. Thereafter, a barrier layer such as titanium nitride, tantalum or tantalum nitride is applied over a dielectric layer on the front side of the workpiece. Depending upon the particular process used to form the interconnect structures, the dielectric layer may include a pattern of recessed micro-structures that define the various interconnect paths. A thin metal film, such as a copper film is applied exterior to the barrier layer. In most instances, the thin film serves as an initial seed layer for subsequent electroplating of a further metal layer, such as a further copper layer. Due to manufacturing constraints, the thin film is not applied over an outer, peripheral margin of the front side.
- Known techniques, such as physical vapor deposition (sputtering) or chemical vapor deposition, are typically used to apply the barrier layer and the thin film. Both methods can deposit copper onto the wafer bevel (the peripheral edge of the wafer), and in many cases this deposit is non adherent and can flake off in subsequent processing steps such as annealing or CMP. After deposition of the barrier layer, additional layers may be deposited to the wafer front side edge. In instances in which a further metal layer is to be electroplated exterior to the thin film, one or more electrical contacts are connected to an outer margin of the thin film to provide plating power. Because subsequent layers are deposited with an edge exclusion, the previously deposited layers are left exposed. Many of these layers allow copper to be deposited on them, but the adhesion is very poor and flaking during post processing is observed. A typical copper example might be an exposed barrier layer such as Ti/TiN being exposed to copper plating solution. Following electrochemical deposition, the barrier layer would have a copper film of low quality which would flake off easily in CMP. Removal of flaking material before CMP processing is desirable as the flakes have the potential to cause scratches in the polished surface, resulting in yield losses.
- The surface area of the front side beyond the inner boundary of the outer margin of the thin film is not available for fabricating the microelectronic devices since the present manufacturing processes limit the extent to which device structures can be formed at the outer margin. It would be highly desirable and would result in increased yield if more of the surface area beyond the present limits of the outer margin of the thin film were available for fabricating interconnect structures.
- Covering the exposed barrier layer with a full coverage seed layer would eliminate copper metal from flaking off the barrier and also have the added benefit of increasing usable area on the wafer surface. Even in this case, copper deposited on the bevel during the seed layer and electrochemical deposition would need to be removed, as it too can flake off and/or cause cross contamination of metrology tools. A clear area inboard of the wafer bevel may also be necessary for reliable processing; many clamp rings are very sensitive to surface characteristics.
- In the known process discussed above, and in other processes, contamination by copper, other metals, or other contaminants can occur on the back side of the workpiece. Although copper and other metals tend to diffuse rapidly through silicon or silicon dioxide, the back side is generally not provided with barrier layers that are capable of preventing copper, other metals, or other contaminants from diffusing through the silicon wafer to the front side, at which such contamination can be very detrimental to device performance.
- Such contamination can result from overspraying or other processing artifacts or from cross-contamination via fabrication tools. Such contamination can occur on the outer perimeter of a silicon wafer as well as on its back side.
- If not removed, such contamination can lead to cross-contamination of other wafers, via fabrication tools. Such contamination can be very difficult to remove, particularly if the contaminant has formed a stable silicide. It would be highly desirable if such contamination could be easily removed in a controlled manner without detrimentally affecting the front side of the workpiece.
- The present invention provides processes for selectively treating surfaces of a workpiece having a first side, an opposing second side, and a peripheral edge defined between the perimeters of the first and second sides. In a first aspect of the present invention, a process is provided for applying a first fluid to the first side and peripheral edge of the workpiece, while excluding the first fluid from at least a majority of the second side of the workpiece. In a still further preferred embodiment, the first fluid is applied to the first side of the workpiece, the peripheral edge, and an outer perimeter portion of the second side of the workpiece. The first fluid preferably comprises an etchant to remove a metal film or oxide film from the exposed surface portions of the workpiece, to the exclusion of the remaining substantially non-exposed portion of the second side of the workpiece.
- In a still further aspect of the present invention, a workpiece having a first side, an opposing second side, and a peripheral edge defined between the outer perimeters of the first side and the second side is received within a fluid chamber of a reactor. The fluid chamber has a first chamber portion which receives the first surface of the workpiece, and a second chamber portion which receives the second surface of the workpiece. A first fluid is supplied to the first chamber portion, in which the first side is exposed to the first fluid to the exclusion of the second side of the workpiece, which is not exposed in totality or to a predetermined extent to the first fluid. In the preferred embodiment, the first fluid includes an acid, preferably an inorganic acid, and an oxidizer that act on the first side to remove a metal film or oxide film therefrom, while not substantially affecting the second side of the workpiece or a selected portion of a second side of the workpiece. In addition to or in lieu of supplying the first fluid, a second fluid may optionally be supplied to the second chamber portion of the reactor, so that the second side of the workpiece or a selected portion of the second side of the workpiece is exposed to the second fluid. The second fluid may be a different process fluid such as an inert gas or liquid, a diluent or rinsing agent or other fluid.
- The present invention thus provides a method and apparatus for selectively exposing a second side of a workpiece, such as a back side of a semiconductor wafer, to an etchant solution preferably including an etchant solvent, such as an acid, and optionally, an oxidizer, to remove a metal film, an oxide film or particulates from the back side of the wafer. The present invention also provides for exposure of the peripheral edge of the workpiece, such as the bevel edge of a semiconductor wafer, to the etchant solution to remove a metal film or oxide film from the bevel edge. Additionally, the processes and apparatus of the invention may be utilized to etch, remove, or reduce a metal film or an oxide film from a perimeter edge portion of the opposing second side of the workpiece, such as a narrow annular exclusion zone bordering the perimeter edge of the front (i.e., device) side of a semiconductor wafer. The selective exposures of surfaces of the workpiece are made without substantial exposure of the remainder of the second side of the workpiece, i.e., in the preferred embodiment, the device or front side of the semiconductor wafer. While the first fluid is supplied to the first side of the workpiece, the opposing second side of the workpiece may be exposed to no fluid, or may alternately be exposed to a purge fluid such as an inert gas or deonized water, or to another process fluid.
- The present invention also provides semiconductor wafers and other workpieces produced from these processes.
- The present invention also provides etchant solutions including an inorganic acid and ozone as an oxidizer, preferably hydrofluoric acid and ozone.
- In a still further aspect of the invention, a processing fluid is selectively applied or excluded from an outer peripheral margin of at least one of the front or back sides of the workpiece. Exclusion and/or application of the processing fluid occurs by applying one or more processing fluids to the workpiece as the workpiece and corresponding reactor are spinning about an axis of rotation that is generally parallel (or antiparallel) to the vector defining the face of the workpiece being processed. The flow rate of the one or more processing fluids, fluid pressure, and/or spin rate are used to control the extent to which the processing fluid is selectively applied or excluded from the outer peripheral margin.
- In a further aspect of the invention, a thin film is applied over the front side and over at least a portion of the outer perimeter. Usually, a barrier layer is applied over the front side and over at least a portion of the outer perimeter, whereupon a further thin film, such as a conductive seed layer, is applied over the barrier layer.
- In a preferred embodiment, after one or more further intervening steps, such as electroplating of a metal layer onto the conductive seed layer, an etchant capable of removing one or more of the thin film layers is caused to flow over an outer margin of the front side while the etchant is prevented from flowing over the front side except for the outer margin. Thus, the etchant only contacts the outer margin of the front side thereby selectively removing only the one or more thin film layers from the outer margin of the front side. If the etchant is also caused to flow over the back side and over the outer perimeter, as well as over the outer margin of the front side, the one or more thin film layers are removed from the outer perimeter and any contaminant that the etchant is capable of removing is stripped from the back side as well.
- Rather than an etchant, a cleaning chemical can be used in some applications to remove or dissolve the one or more thin film layers as described above.
- The foregoing aspects and many of the attendant advantages of this invention will become more readily appreciated as the same become better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:
- FIGS. 1A, 1B,1C, and 1D are fragmentary, cross-sectional views of a microelectronic workpiece, such as a silicon wafer, at various stages of a known sequence of processing steps in accordance with prior art.
- FIGS. 2A, 2B,2C, and 2D are fragmentary, cross-sectional views of a microelectronic workpiece, such as a silicon wafer, at various stages of a novel sequence of processing steps in accordance with this invention.
- FIG. 3 is a schematic representation of a system in which the processes of the present invention can be implemented.
- FIG. 4 is a cross-sectional view of a microelectronic workpiece housing and a rotor assembly constructed for use in accordance with one embodiment of the invention.
- FIG. 5 is an exploded view of a further embodiment of a microelectronic workpiece housing constructed in accordance with the teachings of the present invention
- FIG. 6 is a top plan view of the workpiece housing of FIG. 5 when the housing is in an assembled state.
- FIG. 7 is a cross-sectional view of the workpiece housing taken along line IV-IV of FIG. 6.
- FIG. 8 is a cross-sectional view of the workpiece housing taken along line V-V of FIG. 6.
- FIG. 9 is a cross-sectional view of the workpiece housing taken along line VI-VI of FIG. 6.
- FIGS. 10A and 10B are cross-sectional views showing the workpiece housing in a closed state and connected to a rotary drive assembly.
- FIGS. 11A and 11B are cross-sectional views showing the workpiece housing in an open state and connected to a rotary drive assembly.
- FIGS. 12A, 12B, and12C illustrate three embodiments of edge configurations that facilitate mutually exclusive processing of the upper and lower wafer surfaces in the workpiece housing.
- FIG. 13 illustrates an embodiment of the workpiece housing employed in connection with a self-pumping re-circulation system.
- FIGS. 14 and 15 are schematic diagrams of exemplary processing tools that employ the present invention.
- FIG. 16 illustrates a batch wafer processing tool constructed in accordance with the principles of the present invention.
- FIG. 17 illustrates a further embodiment of a reactor including features that render it well-suited for integration with workpiece transfer automation equipment, wherein the reactor is in an open state for loading/unloading a workpiece that is to be processed.
- FIG. 18 illustrates the embodiment of the reactor of FIG. 17 wherein the reactor is in a closed processing state.
- FIG. 19 illustrates one embodiment of a biasing member that may be used in the reactor of FIG. 17.
- FIG. 20 illustrates a system in which the foregoing reactor is used to implement a rinsing/drying process.
- FIG. 21 is a cut-away, perspective view of the reactor, as seen from a different vantage.
- FIG. 22 is a cross-sectional view of the reactor, as taken through its central, vertical axis.
- FIG. 23 is an enlarged detail of certain elements of the reactor, as taken within a circle drawn in FIG. 3.
- FIGS. 24 and 25 are further enlarged details of a portion of what is illustrated in FIG. 23, as taken at different places around the reactor.
- FIG. 26 is an enlarged, perspective view of a rotor, as used in the reactor.
- FIG. 27 is an enlarged, perspective view of a lower chamber wall and four lifting levers, as used in the reactor.
- FIGS. 28 and 29 are further enlarged details of one lifting lever, as seen in two different positions.
- FIG. 30 provides an SEM photo of a perimeter edge portion of a wafer processed in accordance with the present invention.
- FIG. 31 provides etching results for various chemistries useful as processing fluids in the present invention.
- Although the process of the present invention has applicability to any process in which a processing fluid is selectively provided to or excluded from an outer margin of an electrochemically processed workpiece, the present invention is particularly well suited for removal of a film, or a portion of a film, that has been deposited on a substrate by electrolytic or electroless processing, specifically metal films and oxide films. Thus the invention is suitably used for removing or decreasing the thickness of metal films from select surfaces of a workpiece, including by way of nonlimiting example, films containing copper, copper alloys such as copper zinc, neon, zinc, chromium, tin, gold, silver, lead, cadmium, platinum, palladium, iridium, or rubidium. Such metal films are typically removed using solutions applied in accordance with the present invention, including an etchant such as an acid and preferably an oxidizing agent, as shall be described further subsequently. Oxide films can also be suitably removed in whole or in part in accordance with the present invention, including metal oxides, silicon oxides, and barrier and protective layers, such as by way of nonlimiting examples, silicon nitride, silicon oxide, polysilicon, tantalum nitride, and titanium nitride. The term “film” and “contaminant” are used interchangeably herein. However, the term “workpiece” is not limited to semiconductor wafers, but rather refers to substrates having generally parallel planar first and second surfaces and that are relatively thin, including semiconductor wafers, ceramic wafers, and other substrates upon which microelectronic circuits or components, data storage elements or layers, and/or micromechanical elements are formed.
- A preferred embodiment of the invention will be described in connection with a sequence of processing steps for depositing one or more metallization layers or metallized structures on a semiconductor workpiece, with it being understood that the invention is adaptable for use with other workpieces and films.
- A. Semiconductor Workpiece Processing
- The known sequence of processing steps in accordance with the prior art begins with a
semiconductor wafer 10, on which microelectronic devices (not shown) have been fabricated. As illustrated in FIG. 1A, thewafer 10 has a front,device side 12, a back,non-device side 14, and a beveled,outer perimeter 16. Via physical vapor deposition (sputtering) or chemical vapor deposition, abarrier layer 20 is applied over thefront side 12 and over anupper portion 18 of theouter perimeter 16. A thin-film seed layer, such as acopper film 30, is applied over thebarrier layer 20. Conventionally, theseed layer 30 is only deposited within the bounds of anouter margin 22 of thebarrier layer 20, as illustrated in FIG. 1B. At anouter edge 32 of thecopper film 30, one or moreelectrical contacts 40 to be used in providing electroplating power to the seed layer are placed in electrical contact with thecopper film 30, as illustrated in FIG. 1C. - After the one or more
electrical contacts 40 have been connected to the seed layer copper film 30 afurther copper layer 50 from which interconnect structures and/or metallized devices are fabricated is electroplated onto thewafer 110 as illustrated in FIG. 1C. The electrical contact(s) 40 are then removed to provide the resultant multi film structure, shown generally at 60 in FIG. 1D. Beyond aninner boundary 34 of theouter margin 32 of thecopper layer 50, anannular region 62 of thefront side 12 is not available for fabricating such interconnect structures or metallized devices. - One example of novel sequence of processing steps in accordance with the present invention begins with a
silicon wafer 70, which is similar to thesilicon wafer 10 before processing, on which microelectronic devices (not shown) have been fabricated, and which has a front,device side 72, a back,non-device side 74, and a beveled,outer perimeter 76, as illustrated in FIG. 2A. Via physical vapor deposition (sputtering) or chemical vapor deposition, abarrier layer 80 is applied over thefront side 72 and over anupper portion 78 of theouter perimeter 76 and a thin seed layer, such as acopper film 82 is applied over theentire barrier layer 80, without exclusion from a peripheralouter margin 86, so as to cover thebarrier layer 80 where applied over thefront side 72 and over theupper portion 78 of theouter perimeter 76, as illustrated in FIG. 1B. At anouter edge 84 of thecopper seed layer 82, one or moreelectrical contacts 87 to be used in electroplating are connected to provide electroplating power to thecopper film 82, as illustrated in FIG. 2C. As illustrated, theouter edge 84 at which contact may be made for the supply of electroplating power illustrated in FIG. 2C is substantially closer to the peripheral edge than the process as illustrated in FIG. 1C. - A
further copper film 88 from which metallized interconnects and/or microelectronic devices are fabricated is then applied using an electrochemical deposition process. As illustrated in FIG. 2C, thefurther copper film 88 is deposited within theouter margin 92 of thecopper film 82. Theelectrical contact 86 is then removed leaving the resultant multi-layer structure shown generally at 90 of FIG. 2D. Metallized devices (not shown) and/or interconnects are formed by known techniques, from theresultant structure 90. After thecopper layer 88 has been deposited, theseed layer 82,film 88, and/orbarrier layer 80 may be removed from theouter margin 84 and, if desiredperipheral edge 76 of theworkpiece 70. Removal of at leastlayer 82 from the outer margin assists in preventing film flaking and cross-contamination problems that may occur during subsequent workpiece processing. - In accordance with an embodiment the process, processing fluid is selectively applied to the outer peripheral margin of at least the front side of the workpiece. Exclusion and/or application of the processing fluid occurs by applying one or more processing fluids to the workpiece as the workpiece and corresponding reactor are spinning about an axis of rotation that is generally aligned on the central orthogonal axis of the face of the workpiece being processed. The flow rate of the one or more processing fluids, fluid pressure, and/or spin rate are used to control the extent to which the processing fluid is selectively applied to the outer peripheral margin.
- A reactor suitable for executing the foregoing removal process may generally be comprised of upper and lower members that define an upper chamber and a lower chamber with respect to the workpiece contained therein. A centrally disposed inlet is provided to each of the upper an lower chambers for supplying one or more processing fluids. Fluid outlets are disposed at peripheral portions of the chambers and are adapted to assist in the exclusion of one processing fluid from the outer margin of the workpiece while allowing intrusion of an etchant thereat. The upper and lower chambers are rotated conjointly so as to distribute a processing fluid in the upper chamber across an upper side of the workpiece through centripetal acceleration and so as to distribute a processing fluid in the lower chamber across a lower side of the workpiece through centripetal acceleration. Depending upon the processes being performed, however, the processing fluids in the upper and lower chambers may be the same fluid or different fluids.
- Also, rather than relying on the rotation of the workpiece, the processing fluid could also be selectively driven by pumps.
- Through control of the respective pressures of the processing fluids entering the respective chambers and of the rotational speed of the rotating chambers, it is possible to control the reactor so as to cause the processing fluid entering the inlet of the lower chamber to flow over the near side of the wafer, over the outer perimeter of the workpiece, and over an outer margin of the far side of the workpiece, and so as to prevent the same processing fluid from flowing over the far side except for the outer margin. The control of the fluid pressures may be achieved for example through the use of a pump for liquids, or a pressure regulator for a pressurized gas source.
- B. Process Overview
- The present invention provides processes for selectively removing a film, such as a metal film or oxide film, from selected surface portions of a semiconductor workpiece. The metal film or oxide film can be selectively removed from: a single side of the workpiece; the peripheral edge of the workpiece; the peripheral edge and back side of the workpiece; the peripheral edge and an exclusion zone defined by a narrow annular perimeter edge portion of the front side of the workpiece; or the back side, peripheral edge and exclusion zone. To remove such films, such as metal contaminants that are not desired on the peripheral edge and/or the back side, an etchant solution is utilized which first oxidizes the metal and then solubilizes the oxidized metal to remove it from the selected surface portion. Oxide films may likewise be removed from selected surfaces of the workpiece using an acidic etchant. While the back side and/or peripheral edge is being etched, the front or device side of the semiconductor wafer may be left unprocessed, or may be exposed to an inert material such as a purge gas (e.g., nitrogen or helium), to a rinse such as deionized water, or to another processing fluid such as a more highly diluted, etchant. The front side of the wafer (excluding the exclusion zone) is either left unprocessed, or is processed to a lesser degree without damage to the underlying devices, metal interconnects or semiconductor layers.
- The processes of the present invention are adapted for many types of processes, including the removal of metal films such as copper ion contamination that is deposited on the peripheral bevel edge or the back side of a wafer during previous processing steps. For example, copper ion contamination can be removed from the bevel edge and back side, and additionally bulk copper can be selectively removed by a reduction in thickness from all areas of the substrate including the front or device side, to a predetermined extent. While reference is made herein to treating a bevel edge, it should also be understood that the methods of the present invention are adaptable for treating non-beveled edges such as flatted edges of semiconductor wafers.
- In addition to copper removal, other examples of uses for the processes and apparatus of the present invention are, without limitation: the removal of cobalt contaminants from the back side and/or bevel edge of the wafer; the removal of contaminant particles from the back side of a semiconductor wafer prior to photolithography; the removal of residue remaining after dry plasma etching of the front side of the front side of a semiconductor wafer; the oxide etching of one or both sides and/or the peripheral edge of a semiconductor wafer; the etching of silicon nitride from one or both sides of the peripheral edge of a semiconductor wafer, and other processing techniques where it is desirable to selectively remove a metal or oxide film from surfaces. Other uses of the processes of the present invention include removal of noble metals (Pt, Pd, Ru, Ir), and removal of metallic oxides such as high K dielectorics (BST, SBT, Ta2O5) from the backside and peripheral edge.
- Before describing these processes in detail, suitable equipment for carrying out the processes of the present invention are first described.
- C. Apparatus
- A
system 92 useful for carrying out the processes of the present invention is illustrated in FIG. 3. FIG. 3 includes one ormore preprocessing stations 94, in which a substrate that is to be electrochemically processed is prepared. In the case of a semiconductor wafer, theprocessing station 94 may be a chemical vapor deposition or physical vapor deposition station, such as for applying a barrier layer to a workpiece. The thusly prepared workpiece is then moved to one or morefurther processing stations 96, where, for example, a thin metal film such as a seed layer may be deposited on the substrate. Additional process steps may be incorporated as required to complete preparation of the workpiece for electrochemical treatment, such as the application of a metal film. The workpiece then is passed, either manually or under automated control, to areactor 98, in which the metal film is to be deposited. In the case of a semiconductor wafer this may be an electroplatingreactor 98, in which metal is deposited over the seed layer to the front or device side of the wafer, with potential contamination of the bevel edge and back side of the wafer. - The semiconductor wafer is then moved to an
etching reactor 100, in which the surfaces of the workpiece are to be selectively treated to remove metal film or oxide film. In the preferred embodiment, thereactor 100 provides for selective etching of the back side, bevel edge and/or perimeter exclusion zone of a semiconductor wafer. The workpiece is received within a chamber defined within thereactor 100, with a first side of the workpiece being exposed to alower chamber portion 102 and a second side of the workpiece being exposed to anupper chamber portion 104. The terms “upper” and “lower” are used herein for convenience, and other orientation are also encompassed by the invention. - The perimeter edge of the workpiece may be sealed, or may be in communication with fluid outlets at a
perimeter edge portion 106 of the reactor. The side of the workpiece exposed to thelower chamber 102 may then be selectively supplied with one or more fluids fromfluid supplies 108, such as deionized water for rinsing, chemical solution for etching or other processing, or an inert fluid such as nitrogen. In addition to or in lieu of fluids being supplied from thesupplies 108 to thelower chamber 102, one or more fluids may be selectively supplied from one or morefluid supplies 110 to theupper chamber 104. Again, fluid supplies 110 may supply a chemical processing fluid, deionized water, or purge gas such as nitrogen. Supply of the various fluids is controlled by aprogrammable controller 112 that operates valves or pumps supplying the various fluids. In accordance with the present invention, fluid may be supplied only to one side of the workpiece, such as a chemical solution provided to etch the back side and/or peripheral edge, with no fluid being supplied to the opposing second side of the workpiece. In the preferred embodiment, however, while the first side is being supplied with a chemical solution, the second side is being supplied with an inert gas or deionized water rinse, or an alternate processing solution. After etching, the etched side of preferably both sides of the wafer are supplied with deionized water rinse, spun to remove fluids, and dried with heated nitrogen. - Various configurations of reactors may be utilized for carrying out the selective treatment of the present invention. By way of example, the processes provided by this invention can be advantageously practiced in one of a variety of reactors illustrated and described in U.S. patent application Ser. Nos. 09/437,711 filed Nov. 10, 1999 and 09/437,926 filed Nov. 10, 1999, the disclosures of which are hereby incorporated herein by reference.
- FIG. 4 is a cross-sectional view of one suitable embodiment of a reactor, shown generally at114, constructed in accordance with the teachings of the present invention. The embodiment of the
reactor 114 of FIG. 4 is generally comprised of arotor portion 115 and a microelectronic workpiece housing 116. Therotor portion 115 includes a plurality ofsupport members 118 that extend downwardly from therotor portion 115 to engage the workpiece housing 116. Each of thesupport members 118 includes agroove 120 that is dimensioned to engage aradially extending flange 122 that extends about a peripheral region of the workpiece housing 116.Rotor portion 115 further includes arotor motor assembly 124 that is disposed to rotate ahub portion 126, including thesupport members 118, about acentral axis 128. Workpiece housing 116 is thus secured for co-rotation with hub portion 130 whensupport members 118 are engaged withflange 122. Other constructions of therotor portion 115 and the engagement mechanism used for securement with the workpiece housing 116 may also be used. - The workpiece housing116 of the embodiment of FIG. 4 defines a substantially closed
processing chamber 132. Preferably, the substantially closedprocessing chamber 132 is formed in the general shape of themicroelectronic workpiece 134 and closely conforms with the surfaces of the workpiece. The specific construction of FIG. 1 includes an upper chamber member 136 having aninterior chamber face 138. The upper chamber member 136 includes a centrally disposed fluid inlet opening 140 in theinterior chamber face 138. The specific construction also includes alower chamber member 142 having aninterior chamber face 144. Thelower chamber member 142 has a centrally disposed fluid inlet opening 148 in theinterior chamber face 144. The upper chamber member 136 and thelower chamber member 146 engage one another to define theprocessing chamber 132. The upper chamber member 136 includessidewalls 150 that project downward from theinterior chamber face 138. One ormore outlets 152 are disposed at the peripheral regions of theprocessing chamber 132 through thesidewalls 150 to allow fluid within thechamber 132 to exit therefrom through centripetal acceleration that is generated when the housing 116 is rotated aboutaxis 128. - In the illustrated embodiment, the
microelectronic workpiece 134 is a generally circular wafer having upper and lower planar surfaces. As such, theprocessing chamber 132 is generally circular in plan view and the interior chamber faces 138 and 144 are generally planar and parallel to the upper and lower planar surfaces of theworkpiece 134. The spacing between the interior chamber faces 138 and 144 and the upper and lower planar surfaces of theworkpiece 134 is generally quite small. Such spacing is preferably minimized to provide substantial control of the physical properties of a processing fluid flowing through the interstitial regions. - The
wafer 134 is spaced from theinterior chamber face 144 by a plurality of spacingmembers 154 extending from theinterior chamber face 144. Preferably, a further set of spacingmembers 146 extend from theinterior chamber face 138 and are aligned with the spacingmembers 152 to grip thewafer 134 therebetween. -
Fluid inlet openings chamber 132 for processing the wafer surfaces. In the illustrated embodiment, processing fluids are delivered from above thewafer 134 toinlet 140 through afluid supply tube 156 having afluid outlet nozzle 158 disposedproximate inlet 140.Fluid supply tube 156 extends centrally through therotor portion 115 and is preferably concentric with the axis ofrotation 128. Similarly, processing fluids are delivered from below thewafer 134 toinlet 148 through afluid supply tube 160.Fluid supply tube 160 terminates at anozzle 162 disposedproximate inlet 148. Althoughnozzles tubes nozzles tubes lower chamber members 136 and 146 in the regions of theinlets - During processing, one or more processing fluids are individually or concurrently supplied through
fluid supply tubes inlets workpiece 134 in thechamber 132. Preferably, the housing 116 is rotated aboutaxis 128 by therotor portion 115 during processing to generate a continuous flow of any fluid within thechamber 132 across the surfaces of theworkpiece 134 through the action of centripetal acceleration. Processing fluid entering theinlet openings workpiece 134 to the exterior perimeter of theworkpiece 134. At the exterior perimeter of theworkpiece 134, any spent processing fluid is directed to exit thechamber 132 through outlets 166 as a result of the centripetal acceleration. Spent processing fluids may be accumulated in a cup reservoir disposed below and/or about the workpiece housing 116. As will be set forth below in an alternative embodiment, the peripheral regions of the workpiece housing 116 may be constructed to effectively separate the processing fluids provided throughinlet 140 from the processing fluids supplied throughinlet 148 so that opposite surfaces ofwafer 134 are processed using different processing fluids. In such an arrangement, the processing fluids may be separately accumulated at the peripheral regions of the housing 116 for disposal or re-circulation. - In the embodiment of FIG. 4, the workpiece housing116 may constitute a single wafer pod that may be used to transport the
workpiece 134 between various processing stations and/or tools. If transport of the housing 116 between the processing stations and/or tools takes place in a clean room environment, the various openings of the housing 116 need not be sealed. However, if such transport is to take place in an environment in which wafer contaminants are present, sealing of the various housing openings should be effected. For example,inlets fluid supply tubes chamber 132. Such tracor/slitted diaphragm constructions are used in the medical industry in intravenous supply devices. Selection of the polymer material used for the diaphragms should take into consideration the particular processing fluids that will be introduced therethrough. Similar sealing of the outlets 166 may be undertaken in which the tracor structures are inserted into the diaphragms once the housing 116 is in a clean room environment. - Alternatively, the outlets166 themselves may be constructed to allow fluids from the processing chamber to exit therethrough while inhibiting the ability of fluids to proceed from the exterior of housing 116 into
chamber 132. This effect may be achieved, for example, by constructing theopenings 152 as nozzles in which the fluid flow opening has a larger diameter at the interior ofchamber 132 than the diameter of the opening at the exterior of the housing 116. In a further construction, a rotational valve member may be used in conjunction with the plurality of outlets 166. The valve member, such as a ring with openings corresponding to the position of outlets 166, would be disposed proximate the opening 166 and would be rotated to seal with the outlets 166 during transport. The valve member would be rotated to a position in which outlets 166 are open during processing. Inert gas, such as nitrogen, can be injected into thechamber 132 throughsupply tubes inlets - FIG. 5 is a perspective view of a further reactor construction wherein the reactor is disposed at a fixed processing station and can open and close to facilitate insertion and extraction of the workpiece. The reactor, shown generally at200, is comprised of separable upper and lower chamber members, 205 and 210, respectively. As in the prior embodiment, the
upper chamber member 205 includes a generallyplanar chamber face 215 having a centrally disposedinlet 220. Although not shown in the view of FIG. 5, thelower chamber member 210 likewise has a generally planarinterior chamber face 225 having acentral inlet 230 disposed therethrough. Theupper chamber member 205 includes a downwardly extendingsidewall 235 that, for example, may be formed from a sealing polymer material or may be formed integrally with other portions ofmember 205. - The upper and lower chamber members,205 and 210, are separable from one another to accept a workpiece therebetween. With a workpiece disposed between them, the upper and lower chamber members, 205 and 210, move toward one another to form a chamber in which the workpiece is supported in a position in which it is spaced from the planar interior chamber faces 215 and 225. In the embodiment of the reactor disclosed in FIGS. 5-11B, the workpiece, such as a semiconductor wafer, is clamped in place between a plurality of
support members 240 andcorresponding spacing members 255 when the upper and lower chamber members are joined to form the chamber (see FIG. 10B). Axial movement of the upper and lower chamber members toward and away from each other is facilitated by a plurality offasteners 307, the construction of which will be described in further detail below. Preferably, the plurality offasteners 307 bias the upper and lower chambers to a closed position such as illustrated at FIG. 10A. - In the disclosed embodiment, the plurality of
wafer support members 240 extend about a peripheral region of theupper chamber member 205 at positions that are radially exterior of thesidewall 235. Thewafer support members 240 are preferably disposed for linear movement alongrespective axes 245 to allow thesupport members 240 to clamp the wafer against the spacingmembers 255 when the upper and lower chamber members are in a closed position (see FIG. 10A), and to allow thesupport members 240 to release the wafer from such clamping action when the upper and lower chamber members are separated (see FIG. 11A). Eachsupport member 240 includes asupport arm 250 that extends radially toward the center of theupper chamber member 205. An end portion of eacharm 250 overlies acorresponding spacing member 255 that extends from theinterior chamber face 215. Preferably, the spacingmembers 255 are each in the form of a cone having a vertex terminating proximate the end of thesupport arm 250.Notches 295 are disposed at peripheral portions of thelower chamber member 210 and engage roundedlower portions 300 of thewafer support members 240. When thelower chamber member 210 is urged upward to the closed position,notches 295 engageend portions 300 of thesupport members 240 and drive them upward to secure thewafer 55 between thearms 250 of thesupports 240 and thecorresponding spacing members 255. This closed state is illustrated in FIG. 8. In the closed position, thenotches 295 and corresponding notches 296 of the upper chamber member (see FIG. 5) provide a plurality of outlets at the peripheral regions of thereactor 200. Radial alignment of thearm 250 of eachsupport member 240 is maintained by a set pin 308 that extends through lateral grooves 309 disposed through an upper portion of each support member. - The construction of the
fasteners 307 that allow the upper and lower chamber members to be moved toward and away from one another is illustrated in FIGS. 5, 9 and 10B. As shown, thelower chamber member 210 includes a plurality ofhollow cylinders 270 that are fixed thereto and extend upward throughcorresponding apertures 275 at the peripheral region of theupper chamber member 205 to form lower portions of eachfastener 307.Rods 280 extend into the hollow of thecylinders 270 and are secured to form an upper portion of eachfastener 307. Together, therods 280 andcylinders 270 form thefasteners 307 that allow relative linear movement between the upper and lower chamber members, 205 and 210, alongaxis 283 between the open and closed position. Two flanges, 285 and 290, are disposed at an upper portion of eachrod 280.Flange 285 functions as a stop member that limits the extent of separation between the upper and lower chamber members, 205 and 210, in the open position.Flanges 290 provide a surface against which a biasing member, such as a spring (see FIG. 9) or the like, acts to bias the upper and lower chamber members, 205 and 210, to the closed position. - With reference to FIG. 9, the
spring 303 or the like, has a first end that is positioned within acircular groove 305 that extends about eachrespective fastener 307. A second end of each spring is disposed to engageflange 290 of therespective fastener 307 in a compressed state thereby causing the spring to generate a force that drives thefastener 307 and thelower chamber member 210 upward into engagement with theupper chamber member 205. - The
reactor 200 is designed to be rotated about a central axis during processing of the workpiece. To this end, a centrally disposedshaft 260 extends from an upper portion of theupper chamber member 205. As will be illustrated in further detail below in FIGS. 10A-11B, theshaft 260 is connected to engage a rotary drive motor for rotational drive of thereactor 200. Theshaft 260 is constructed to have a centrally disposed fluid passageway (see FIG. 7) through which a processing fluid may be provided toinlet 220. Alternatively, the central passageway may function as a conduit for a separate fluid inlet tube or the like. - As illustrated in FIGS. 6 and 7, a plurality of
optional overflow passageways 312 extend radially from a central portion of theupper chamber member 205.Shaft 260 terminates in a flaredend portion 315 havinginlet notches 320 that provide fluid communication between the upper portion ofprocessing chamber 310 and theoverflow passageways 312. The flaredend 315 of theshaft 260 is secured with theupper chamber member 205 with, for example, a mountingplate 325. Mountingplate 325, in turn, is secured to theupper chamber member 205 with a plurality of fasteners 330 (FIG. 8).Overflow passages 312 allow processing fluid to exit thechamber 310 when the flow of fluid to thechamber 310 exceeds the fluid flow from the peripheral outlets of the chamber. - FIGS. 10A and 10B are cross-sectional views showing the
reactor 200 in a closed state and connected to a rotary drive assembly, shown generally at 400, while FIGS. 11A and 11B are similar cross-sectional views showing thereactor 200 in an opened state. As shown,shaft 260 extends upward into therotary drive assembly 400.Shaft 260 is provided with the components necessary to cooperate with astator 405 to form a rotarydrive motor assembly 410. - As in the embodiment of FIG. 4, the upper and
lower chamber members processing chamber 310 that, in the preferred embodiment, substantially conforms to the shape of theworkpiece 55. Preferably, thewafer 55 is supported within thechamber 310 in a position in which its upper and lower faces are spaced from the interior chamber faces 215 and 225. As described above, such support is facilitated by thesupport members 240 and thespacing members 255 that clamp the peripheral edges of thewafer 55 therebetween when thereactor 200 is in the closed position of FIGS. 10A and 10B. - It is in the closed state of FIGS. 10A and 10B that processing of the
wafer 55 takes place. With the wafer secured within theprocessing chamber 310, processing fluid is provided throughpassageway 415 ofshaft 260 andinlet 220 into the interior ofchamber 310. Similarly, processing fluid is also provided to thechamber 310 through aprocessing supply tube 125 that directs fluid flow throughinlet 230. As thereactor 200 is rotated by the rotarydrive motor assembly 410, any processing fluid supplied throughinlets wafer 55 by forces generated through centripetal acceleration. Spent processing fluid exits theprocessing chamber 310 from the outlets at the peripheral regions of thereactor 200 formed bynotches 295 and 296. Such outlets exist since thesupport members 240 are not constructed to significantly obstruct the resulting fluid flow. Alternatively, or in addition, further outlets may be provided at the peripheral regions. - Once processing has been completed, the
reactor 200 is opened to allow access to the wafer, such as shown in FIGS. 11A and 11B. After processing, actuator 425 is used to drive anactuating ring 430 downward into engagement with upper portions of thefasteners 307.Fasteners 307 are driven against the bias ofspring 303 causing thelower chamber member 210 to descend and separate from theupper chamber member 205. As thelower chamber member 210 is lowered, thesupport members 240 follow it under the influence of gravity, or against the influence of a biasing member, while concurrently lowering the wafer. In the lower position, thereactor chamber 310 is opened thereby exposing the wafer for removal and/or allowing a new wafer to be inserted into thereactor 200. Such insertion and extraction can take place either manually, or by an automatic robot. - The foregoing arrangement makes the
reactor 200 particularly well-suited for automated workpiece loading and unloading by, for example, a robotic transfer mechanism or the like. As evident from a comparison of FIGS. 10A and 11A, the spacing between the upper surface of the workpiece and the interior chamber wall of theupper chamber member 205 varies depending on whether thereactor 200 is in an open or closed state. When in the open state, the upper surface of the workpiece is spaced from the interior chamber wall of theupper chamber member 205 by a distance, x1, that provides sufficient clearance for operation of, for example, a workpiece transfer arm of a robotic transfer mechanism. When in the closed processing state, the upper surface of the workpiece is spaced from the interior chamber wall of theupper chamber member 205 by a distance, x2, that is less than the distance, x1. The distance, x2, in the disclosed embodiment may be chosen to correspond to the spacing that is desired during workpiece processing operations. While the processing of upper and lower surfaces is disclosed, processing of only a single surface is also within the scope of the present invention. - FIG. 12A illustrates an edge configuration that facilitates separate processing of each side of the wafer. As illustrated, a dividing
member 500 extends from thesidewall 235 of theprocessing chamber 310 to a position immediately proximate theperipheral edge 505 of thewafer 55. The dividingmember 500 may take on a variety of shapes, the illustrated tapered shape being merely one configuration. The dividingmember 500 preferably extends about the entire circumference of thechamber 310. A first set of one ormore outlets 510 is disposed above the dividingmember 500 to receive spent processing fluid from the upper surface of the wafer. Similarly, a second set of one ormore outlets 515 is disposed below the dividingmember 500 to receive spent processing fluid from the lower surface of the wafer. When the wafer rotates during processing, the fluid throughsupply 415 is provided to the upper surface of thewafer 55 and spreads across the surface through the action of centripetal acceleration. Similarly, the fluid fromsupply tube 125 is provided to the lower surface of the wafer and spreads across the surface through the action of centripetal acceleration. Because the edge of the dividingmember 500 is so close to the peripheral edge of the wafer, processing fluid from the upper surface of the wafer does not proceed below the dividingmember 500, and processing fluid from the lower surface of the wafer does not proceed above the dividingmember 500. As such, this reactor construction makes it possible to concurrently process both the upper and lower surfaces of the wafer in a mutually exclusive manner using different processing fluids and steps. - FIG. 12A also illustrates one manner in which the processing fluids supplied to the upper and lower wafer surfaces may be collected in a mutually exclusive manner. As shown, a
fluid collector 520 is disposed about the exterior periphery of thereactor 200. Thefluid collector 520 includes afirst collection region 525 having asplatter stop 530 and afluid trench 535 that is structured to guide fluid flung from theoutlets 510 to afirst drain 540 where the spent fluid from the upper wafer surface may be directed to a collection reservoir for disposal or re-circulation. Thefluid collector 520 further includes asecond collection region 550 having a further splatter stop 555 and a further fluid trench 560 that is structured to guide fluid flung from theoutlets 515 to asecond drain 565 where the spent fluid from the lower wafer surface may be directed to a collection reservoir for disposal or re-circulation. - FIGS. 12B and 12C illustrate two alternate embodiments for peripheral edge and front side exclusion zone treatment using reactors and processes of the present invention. Referring to FIG. 12B, the peripheral edge of the
wafer 12 is engaged by anedge seal 566, while anozzle 567 positioned above the front side exclusion zone, radially outboard from the center of the wafer, applies etchant or other solution to the exclusion zone. Alternately, if treatment of the entire front side, or treatment of the back side, is desired, multiple nozzles can be used at different radial locations, or the nozzle can move inwards and outwards while applying the treatment solution. FIG. 12C illustrates a still further embodiment, in which rather than anozzle 567, aninlet 568 is provided for application of a fluid above the exclusion zone or at other locations through the reaction chamber wall onto the side of the wafer to be treated. - FIG. 13 illustrates an embodiment of the
reactor 200 having an alternate configuration for supplying processing fluid through thefluid inlet opening 230. As shown, theworkpiece housing 20 is disposed in a cup 570. The cup 570 includessidewalls 575 exterior to theoutlets 100 to collect fluid as it exits thechamber 310. Anangled bottom surface 580 directs the collected fluid to asump 585.Fluid supply line 587 is connected to provide an amount of fluid to thesump 585. Thesump 585 is also preferably provided with adrain valve 589. An inlet stem 592 defines achannel 595 that includes a first end having anopening 597 that opens to thesump 585 at one end thereof and a second end that opens to theinlet opening 230. - In operation of the embodiment shown in FIG. 13, processing fluid is provided through
supply line 587 to thesump 585 while thereactor 200 is spinning. Once thesump 585 is full, the fluid flow to the sump throughsupply line 587 is eliminated. Centripetal acceleration resulting from the spinning of thereactor 200 provides a pressure differential that drives the fluid throughopenings chamber 310 to contact at least the lower surface of the wafer, andexit outlets 100 where the fluid is re-circulated to thesump 585 for further use. - There are numerous advantages to the self-pumping re-circulation system illustrated in FIG. 13. The tight fluid loop minimizes lags in process parameter control thereby making it easier to control such physical parameters as fluid temperature, fluid flow, etc. Further, there is no heat loss to plumbing, tank walls, pumps, etc. Still further, the system does not use a separate pump, thereby eliminating pump failures which are common when pumping hot, aggressive chemistries.
- FIGS. 14 and 15 illustrate two different types of processing tools, each of which may employ one or more processing stations including the reactor constructions described above. FIG. 14 is a schematic block diagram of a tool, shown generally at600, including a plurality of
processing stations 605 disposed about anarcuate path 606. Theprocessing stations 605 may all perform similar processing operations on the wafer, or may perform different but complementary processing operations. For example, one or more of theprocessing stations 605 may execute an electrodeposition process of a metal, such as copper, on the wafer, while one or more of the other processing stations perform complementary processes such as, for example, clean/dry processing, pre-wetting processes, photoresist processes, etc. - Wafers that are to be processed are supplied to the
tool 600 at an input/output station 607. The wafers may be supplied to thetool 600 in, for example, S.M.I.F. pods, each having a plurality of the wafers disposed therein. Alternatively, the wafers may be presented to thetool 600 in individual workpiece housings, such as at 20 of FIG. 4. - Each of the
processing stations 605 may be accessed by arobotic arm 610. Therobotic arm 610 transports the workpiece housings, or individual wafers, to and from the input/output station 607. Therobotic arm 610 also transports the wafers or housings between thevarious processing stations 605. - In the embodiment of FIG. 14, the
robotic arm 610 rotates aboutaxis 615 to perform the transport operations alongpath 606. In contrast, the tool shown generally at 620 of the FIG. 15 utilizes one or morerobotic arms 625 that travel along alinear path 630 to perform the required transport operations. As in the embodiment of FIG. 13, a plurality ofindividual processing stations 605 are used, butmore processing stations 605 may be provided in a single processing tool in this arrangement. - FIG. 16 illustrates one manner of employing a plurality of workpiece housings700, such as those described above, in a
batch processing apparatus 702. As shown, the workpiece housings 700 are stacked vertically with respect to one another and are attached for rotation by acommon rotor motor 704 about acommon rotation axis 706. Theapparatus 702 further includes a processfluid delivery system 708. Thedelivery system 708 includes astationary manifold 710 that accepts processing fluid from a fluid supply (not shown). Thestationary manifold 710 has an outlet end connected to the input of arotating manifold 712. Therotating manifold 712 is secured for co-rotation with the housings 700 and, therefore, is connected to thestationary manifold 710 at arotating joint 714. A plurality offluid supply lines 716 extend from therotating manifold 712 and terminate atrespective nozzle portions 718 proximate inlets of the housings 700.Nozzle portions 718 that are disposed between two housings 700 are constructed to provide fluid streams that are directed in both the upward and downward directions. In contrast, thelowermost supply line 716 includes anozzle portion 718 that directs a fluid stream only in the upward direction. The uppermost portion of therotating manifold 712 includes an outlet 720 that provides processing fluid to the fluid inlet of the uppermost housing 700. - The
batch processing apparatus 702 of FIG. 16 is constructed to concurrently supply the same fluid to both the upper and lower inlets of each housing 700. However, other configurations may also be employed. For example,nozzle portions 718 may include valve members that selectively open and close depending on whether the fluid is to be supplied through the upper and/or lower inlets of each housing 700. In such instances, it may be desirable to employ an edge configuration, such as the one shown in FIG. 12, in each of the housings 700 to provide isolation of the fluids supplied to the upper and lower surfaces of thewafers 55. Still further, theapparatus 702 may include concentric manifolds for supplying two different fluids concurrently to individual supply lines respectively associated with the upper and lower inlets of the housings 700. - An embodiment of the reactor that is particularly well-suited for integration in an automated processing tool is illustrated in FIG. 17. The reactor, shown generally at800, includes features that cooperate in a unique manner to allow a robotic arm or the like to insert and extract a workpiece to and from the
reactor 800 during loading and unloading operations while also maintaining relatively tight clearances between the workpiece and the interior chamber walls of the reactor during processing. - One of the principal differences between the reactor embodiments described above and the
reactor 800 of FIG. 17 lies in the nature of the workpiece support assembly. As shown,reactor 800 includes a workpiece support assembly, shown generally at 805, that is associated with thelower chamber member 210. In accordance with the illustrated embodiment, the workpiece support assembly 805 includes a plurality ofworkpiece support members 810 that extend through thelower chamber member 210. Theworkpiece support members 810 are supported at a lower end thereof by a biasingmember 815. At the end of theworkpiece support member 810 that is distal the biasingmember 815, theworkpiece support member 810 terminates at aworkpiece support surface 820 and a guide structure 825. The guide structure 825 extends from theworkpiece support surface 820 and terminates at afrustoconical section 830. The guide structure 825 assists in urging the peripheral edges of the workpiece into proper alignment with theworkpiece support surface 820 thereby ensuring proper registration of the workpiece during processing. The guide structure 825 may also serve as a spacer that defines the clearance between the interior chamber wall of theupper chamber member 205 and the upper surface of the workpiece. - The biasing
member 815 of the illustrated embodiment serves to bias theworkpiece support members 810 in an upward direction when the upper andlower chamber members reactor 800 is ready for loading or unloading the workpiece. The biasingmember 815 may take on various forms. For example, a single biasing structure may be used that is common to all of theworkpiece support members 810. Alternatively, as shown in the disclosed embodiment, individual biasing structures may be respectively associated with individual ones of theworkpiece support members 810. The individual biasing structures are in the form ofleaf springs 835 but, for example, may alternatively be in the form of coil spring actuators or the like. - As in the embodiment of the reactor described above, the upper and
lower chamber members reactor 800 are movable with respect to one another between the open condition of FIG. 17 to a closed processing condition as illustrated in FIG. 18. As thechamber members frustoconical sections 830 of theworkpiece support members 810 engage the interior chamber wall of theupper chamber member 205. Continued movement between thechamber members workpiece support members 810 against theleaf springs 835 until the workpiece is clamped between the support surfaces 820 of theworkpiece support members 810 andcorresponding projections 840 that extend from the interior chamber wall of theupper chamber member 205. While in this closed state, the reactor is ready to process the workpiece. - The
reactor 800 of FIG. 17 also includes structures which assists in ensuring proper registration between the upper and alower chamber members pins 845 that extend from one of the chamber members to engage corresponding apertures of the other of the chamber members. Here, the lead-inpins 845 extend from thelower chamber member 210 to engage corresponding apertures (not shown) in theupper chamber member 205. The lead-inpins 845 are in the form of upstanding members that each terminate in a respective frustoconical section that functions as a guide surface. - The foregoing arrangement makes the
reactor 800 particularly well-suited for automated workpiece loading and unloading by, for example, a robotic transfer mechanism or the like, particularly one in which the workpiece is directly inserted into the reactor without flipping of the workpiece. As evident from a comparison of FIGS. 17 and 18, the spacing between the lower surface of the workpiece and the interior chamber wall of thelower chamber member 210 varies depending on whether thereactor 800 is in an open or closed state. When in the open state, the lower surface of the workpiece is spaced from the interior chamber wall of thelower chamber member 210 by a distance, x1, that provides sufficient clearance for operation of, for example, a workpiece transfer arm of a robotic transfer mechanism. When in the closed processing state, the lower surface of the workpiece is spaced from the interior chamber wall of thelower chamber member 210 by a distance, x2, that is less than the distance, x1. The distance, x2, in the disclosed embodiment corresponds to the spacing that is desired during workpiece processing operations. - One embodiment of the biasing
member 815 is illustrated in FIG. 19. As shown, the biasingmember 815 is comprised of a plurality ofleaf springs 835 that extend radially from acentral hub portion 850 to positions in which they contact the underside of respectiveworkpiece support members 810. A further plurality ofradial members 855 extend from thehub 850 to positions in which they contact the underside of respective lead-inpins 845. Unlike theleaf springs 835, the further plurality ofradial members 855 are not necessarily designed to flex as the upper andlower chamber members workpiece support members 810 and lead-inpins 845 may be formed integral with theirrespective leaf springs 835 andradial members 855. - In the illustrated embodiment, the
central hub portion 850 includes acentral aperture 900 that accommodates asecurement 905 which connects the biasingmember 815 to the underside of thelower chamber member 210. With reference to FIGS. 17 and 18, thesecurement 905 can be formed to provide the processing fluid inlet through thelower chamber member 210. When thesecurement 905 is formed in this manner, thereactor 800 is provided with a quick and easy manner of providing different inlet configurations for different processes. - On occasion, it may be desirable to remove the
reactor 800 fromhead portion 860. For example, thereactor 800 may be removed for service or for replacement with a reactor that is designed for executing other processes, or processing other workpiece types. - To this end, the
reactor 800 and thehead portion 860 are engaged at aconnection hub assembly 865 which allows thereactor 800 to be easily connected to and disconnected from thehead portion 860. In embodiment illustrated in FIG. 18, theconnection hub assembly 865 is comprised of ahead connection hub 870 that is fixed to theprocessing head portion 860, and areactor connection hub 875 that is fixed to thereactor 800. Theconnection hubs set screw 885 extends through thehead connection hub 870 and may be rotated to engage a surface of or corresponding aperture in thereactor connection hub 875 to thereby prevents theconnection hubs - When removal of the
reactor 800 is desired, the reactor is rotated to align setscrew 885 with a correspondingchannel sleeve 890 that is fixed to thehead portion 860. Thechannel sleeve 890 is constructed to allow a user to extend a tool therethrough to engage theset screw 885. The set screw is then turned to raise it until it engages and secures with ascrew head block 895. Once secured in this manner, thehead connection hub 870 is rotationally locked with thehead portion 860 thereby allowing thereactor 800 and correspondingreactor connection hub 875 to be unscrewed from thehead connection hub 870 to remove the reactor. - In accordance with a still further feature of the
reactor 800, a stiffeningmember 910 formed, for example, from aluminum is secured with theupper chamber member 205. By increasing the stiffness of the upper and/or lower chamber members, higher rotating speeds may be used and, further, the flatness of the interior chamber walls during processing may be increased. - Numerous substantial benefits flow from the use of the disclosed reactor configurations. Many of these benefits arise directly from the reduced fluid flow areas in the reactor chambers. Generally, there is a more efficient use of the processing fluids since very little of the fluids are wasted. Further, it is often easier to control the physical parameters of the fluid flow, such as temperature, mass flow, etc., using the reduced fluid flow areas of the reactor chambers. This gives rise to more consistent results and makes those results repeatable.
- The foregoing constructions also give rise to the ability to perform sequential processing of a single wafer using two or more processing fluids sequentially provided through a single inlet of the reaction chamber. Still further, the ability to concurrently or sequentially provide different fluids to the upper and lower surfaces of the wafer opens the opportunity to implement novel processing operations. For example, a processing fluid, such as HF liquid, may be supplied to a lower fluid inlet of the reaction chamber for processing the lower wafer surface while an inert fluid, such as nitrogen gas, may be provided to the upper fluid inlet. As such, the HF liquid is allowed to react with the lower surface of the wafer while the upper surface of the wafer is effectively isolated from HF reactions. Numerous other novel processes may also be implemented.
- The present inventors have recognized that demands for integrated circuit rinsing/drying processes may ultimately require more control and economic efficiency from the rinser/dryer. As such, a substantially new approach to rinsing and drying of the semiconductor wafer has been undertaken which provides greater control of the physical properties of the rinsing and drying fluids. Further, wafers may be rinsed and dried on an individual basis more quickly when compared to the drying of an individual wafer using any of the foregoing processes.
- FIG. 20 illustrates one manner of controlling the provision of rinsing/drying fluids that are supplied to the rinser/dryer of any of the foregoing embodiments. As illustrated, the fluid supply system, shown generally at1800, includes a
nitrogen gas supply 1805, anIPA supply 1810, anIPA vaporizer 1815, aDI water supply 1820,optional heating elements 1825,optional flowmeters 1830, optional flow regulators/temperature sensors 1835, andvalve mechanism 1840. All of the various components of thesystem 1800 may be under the control of acontroller unit 845 having the appropriate software programming. - In operation of the rinser/dryer, the
valve mechanism 1840 is connected to supply DI water fromsupply 1820 to both the upper and lower inlets of the rinser/dryer chamber. As the water is supplied to the chamber, the wafer is spun at for example, a rate of 200 RPM. This causes the water to flow across each surface of the wafer under the action of centripetal acceleration. Once a sufficient amount of water has been supplied to the chamber to rinse the wafer surfaces,valve mechanism 1840 is operated to provide a drying fluid, preferably comprised of nitrogen and IPA vapor, to both the upper and lower inlets of the rinser/dryer chamber.Valve mechanism 1840 is preferably operated so that the front of the drying fluid immediately follows the trailing end of the DI water. As the drying fluid enters the chamber, centripetal acceleration resulting from the spinning of the wafer drives the drying fluid across the wafer surface and follows a meniscus across the wafer surface formed by the DI water. The IPA vapor assists in providing a drying of the surface of the wafer at the edge of the meniscus. Drying of the wafer may be further enhanced by heating the DI water and/or the nitrogen/IPA vapor usingheating elements 1825. The particular temperature at which these fluids are supplied may be controlled by thecontroller 1845. Similarly,flow regulators 1835 andflowmeters 1830 may be used bycontroller 1845 to regulate the flow of the DI water and/or the nitrogen/IPA vapor to the rinser/dryer chamber. - With some modifications, the foregoing reactor designs may be adapted to execute several unique processes in which contact between the microelectronic workpiece and one or more processing fluids is controlled and confined to selected areas of the workpiece. One embodiment of such a reactor design is shown in FIGS.21-25.
- With reference to FIGS.21-25, there is shown a
reactor 2100 for processing a microelectronic workpiece, such as asilicon wafer 10 having anupper side 12, alower side 14, and an outer,circular perimeter 16, in a micro-environment. For certain applications, theupper side 12 is the front side, which may be otherwise called the device side, and thelower side 14 is the back side, which may be otherwise called the non-device side. However, for other applications, thesilicon wafer 10 is inverted. - Generally, except as disclosed herein, the
reactor 2100 is similar to the reactors illustrated and described above. However, as illustrated in the drawings and described herein, thereactor 2100 is improved to be more versatile in executing selected microelectronic fabrication processes. - The
reactor 2100 has an upper chamber member that includes anupper chamber wall 2120 and a lower chamber member that includes alower chamber wall 2140. Thesewalls wafer 10 to be loaded into thereactor 100 for processing, by a loading and unloading mechanism (not shown) that, for example, may be in the form of a robot having an end effector. Thesewalls wafer 10 in a processing position, between thesewalls - The
reactor 2100, which defines a rotation axis A, has ahead 2200 containing arotor 2210, which mounts theupper chamber wall 2120, and mounting amotor 2220 for rotating therotor 2210 and the upper andlower chamber walls wafer 10 supported in the processing position. Themotor 2220 is arranged to drive asleeve 2222, which is supported radially in thehead 2200, by rolling-element bearings 2224. Thehead 2200 is arranged to be raised for opening thesewalls walls - The
upper chamber wall 2120 has aninlet 2122 for processing fluids, which may be liquid, vaporous, or gaseous, and thelower chamber wall 2140 has aninlet 2142 for such fluids, which for a given application may be similar fluids or different fluids. Thehead 2200 mounts anupper nozzle 2210, which extends axially through thesleeve 2222 so as not to interfere with the rotation of thesleeve 2222. Theupper nozzle 2210 directs streams of processing fluids downwardly through theinlet 2122 of theupper chamber wall 2120. - The
upper chamber wall 2120 includes an array ofsimilar outlets 2124, which are spaced similarly at uniform angular spacings around the vertical axis A. In the disclosed embodiment, thirty-sixsuch outlets 2124 are employed. Eachoutlet 2124 is spaced outwardly from the vertical axis A by a comparatively larger radial distance and is spaced inwardly from theouter perimeter 16 of awafer 10 supported in the processing position by a comparatively smaller radial distance, such as a distance of approximately 1.5 millimeters or other desired edge exclusion zone. - When the upper and
lower chamber walls upper processing chamber 2126 that is defined by theupper chamber wall 2120 and by a first generally planar surface of the supportedwafer 10, and alower processing chamber 2146 that is defined by thelower chamber wall 2140 and a second generally planar surface of the supported wafer opposite the first side. The upper andlower processing chambers annular region 2130 beyond theouter perimeter 16 of the supportedwafer 10 and are sealed by an annular, compressible seal (e.g. O-ring) 2132 bounding a lower portion 2134 of theannular region 2130. Theseal 2132 allows processing fluids entering thelower inlet 2142 to remain under sufficient pressure to flow toward the outlets 2134. - As compared to reactors of the type disclosed in the previously described embodiments, the
reactor 2100 is particularly suitable for executing a range of unique microfabrication processes. For example,reactor 2100 is particularly suited to execute a process that requires complete contact of a processing fluid at a first side of a workpiece and at only a peripheral margin portion of the second side thereof. Such processes may be realized because processing fluids entering theinlet 2142 of thelower chamber wall 2140 can act on thelower side 14 of a supportedwafer 10, on theouter periphery 16 of the supportedwafer 10, and on anouter margin 18 of theupper side 12 of the supportedwafer 10 before reaching theoutlets 2124, and because processing fluids entering theinlet 2122 of theupper chamber wall 2120 can act on theupper side 12 of the supportedwafer 10, except for theouter margin 18 of theupper side 12, before reaching theoutlets 2124. - As a significant example of one such process, the
reactor 2100 can be used with control of the respective pressures of processing fluids entering therespective inlets - In a more specific embodiment of such a process, the process may employed in a metallization process that is used to form a microelectronic component and/or interconnect structures on a semiconductor wafer or the like. To this end, a thin film, such as the seed layer, is applied over a barrier layer on the front side and over at least a portion of the outer perimeter. After one or more intervening steps, such as electroplating of a copper layer or the like thereover, an etchant capable of etching the electroplating material, thin film material, and/or the barrier layer material is caused to flow selectively over only an outer margin of the first side while being concurrently prevented from flowing over other radial interior portions of the first side. Thus, one or more of the layers are removed from the outer margin of the first side while the layers remain intact at the portions of the first side that are disposed interior of the outer margin. If the etchant is driven over the opposite side and over the outer perimeter, as well as over the outer margin of the first side, the one or more layers are also removed from the outer perimeter of the wafer and, further, any contaminant that the etchant is capable of removing is stripped from the back side.
- Based on the description of the foregoing process, it will be recognized that other layers and/or materials may be selectively etched, cleaned, deposited, protected, etc., based on selective contact of a processing fluid with the outer margin and/or opposing side of the workpiece. For example, oxide may be removed from the opposite side and outer margin of the first side of a workpiece through selective contact with an oxide etchant, such as hydrofluoric acid. Similarly, the oxide etchant may be controlled in the reactor so that it contacts all of the front side of the workpiece except for the outer margin thereby leaving the oxide at the outer margin intact. It will also be recognized that removal of the
outlets 2124 allows thereactor 2100 to be used for processes in which selective outer margin inclusion or exclusion is unnecessary or otherwise undesirable. - As illustrated in FIGS.26-29, additional structures may be incorporated with any of the foregoing reactors dependent on the particular process(es) the reactor is designed to implement and the automation, if any, that will be used along with it. In accordance with one such structural addition, the
lower chamber wall 140 has anupper surface 2144 shaped so as to define anannular sump 2146 around theinlet 2142. Thesump 2146 is used to collect liquid byproducts and/or residual processing fluids supplied through theinlet 2142. If a liquid, for example, strikes and drops fromwafer 10, it is conducted toward theoutlet 2124 under the influence of centripetal acceleration as thereactor 100 is rotated. - Another structural addition illustrated in connection with the
reactor 2100 relates to the lower nozzle design. As illustrated, thelower nozzle 2260, which is provided beneath theinlet 2142 of thelower chamber wall 2140, includes two or more ports 2262 (two shown) for directing two or more streams of processing fluids upwardly through theinlet 2142. Theports 2262 are oriented so as to cause the directed streams to converge approximately where the directed streams reach the lower surface of thewafer 10. Thereactor 2100 also includes apurging nozzle 2280, which is disposed at a side of thelower nozzle 2260, for directing a stream of purging gas, such as nitrogen, across thelower nozzle 2260. - Still further, the
reactor 2100 may have abase 2300, which mounts thelower nozzle 2260 and thepurging nozzle 2280 and which defines a coaxial,annular plenum 2320. Theplenum 2320 has plural (e.g. four) drains 2322 (one shown) each of which is equipped with a pneumatically actuated,poppet valve 2340 for opening and closing thedrain 2322. Thesedrains 2322 provide separate paths for conducting processing liquids of different types to appropriate systems (not shown) for storage, disposal, or recirculation. - An
annular skirt 2360 extends around and downwardly from theupper chamber wall 2120, above theplenum 2320, so as to be conjointly rotatable with theupper chamber wall 2140. Eachoutlet 2124 is oriented so as to direct processing fluids exitingsuch outlet 2124 through fluid passages 2364 against aninner surface 2362 of theannular skirt 2360. Theinner surface 2362 is flared outwardly and downwardly, as shown, so as to cause processing fluids reaching theinner surface 2362 to flow outwardly and downwardly toward theplenum 2320, under the influence of centripetal acceleration when the reactor is rotated. Thus, processing fluids tend to be swept through theplenum 2320, toward thedrains 2322. - The
rotor 2210 has a ribbedsurface 2215 facing and closely spaced from a smooth surface 2202 of therotor 2210, in an annular region 204 communicating with theplenum 2320. When therotor 2210 rotates, theribbed surface 2215 tends to cause air in the annular region 2204 to swirl, so as to help to sweep processing fluids through theplenum 2320, toward thedrains 2322. - The
upper chamber wall 2120 has spacers 2128 that project downwardly to prevent the lifting of a supportedwafer 10 from the processing position and from touching theupper chamber wall 2120. Thelower chamber wall 2140 has spacers 2148 that project upwardly for spacing a supportedwafer 10 above thelower chamber wall 140 by a given distance, and posts 2150 projecting upwardly beyond theouter perimeter 16 of a supportedwafer 10 for preventing the supportedwafer 10 from shifting off center from the vertical axis A. - The
lower chamber wall 2140 may mount alifting mechanism 2400 for lifting awafer 10 supported in the processing position to an elevated position. The lifting mechanism lifts thewafer 10 to the elevated position when thehead 2200 is raised above thebase 2300 so as to open the upper andlower chamber walls wafer 10 to the elevated position facilitates its being unloaded by a loading and unloading mechanism (not shown) such as a robotic arm having an end effector. - The
lifting mechanism 2400 includes an array of liftinglevers 2420. Each liftinglever 2420 is mounted pivotably to thelower chamber wall 2140 via apivot pin 2422 extending fromsuch lifting lever 2420 into asocket 2424 in thelower chamber wall 2140, so as to be pivotable between an operative position and an inoperative position. Each pivotinglever 2420 is arranged to be engaged by theupper chamber wall 2120 when the upper andlower chamber walls such pivoting lever 2420 is pivoted into the inoperative position. Each liftinglever 2420 is biased, as described below, so as to pivot into the operative position when not engaged by theupper chamber wall 2120. - Thus, each lifting lever420 is adapted to pivot from the operative position into the inoperative position as the upper and
lower chamber walls lower chamber walls lever 2420 mounts apin 2424, which extends beneath awafer 10 supported in the processing position and lifts the supported wafer to the elevated position, whensuch lifting lever 2420 is pivoted from the inoperative position into the operative position. - The lifting levers2420 may be biased by an elastic member 2440 (e.g. O-ring) surrounding the
lower chamber wall 2140 and engaging the lifting levers 2420, via ahook 2426 depending from each liftinglever 2420. On each liftinglever 2420, thepin 2422 defines an axis, relative to which thepin 2424 and thehook 2426 are opposed diametrically to the each other. The elastic member 2440 is maintained under comparatively higher tension when the upper andlower chamber walls lower chamber walls - The upper and
lower chamber walls latching mechanism 2500. In accordance with one embodiment, the latching mechanism, the latching mechanism includes a latching ring 2520 that is retained by thelower chamber wall 2140 and that is adapted to engage a complementary shaped recess 2540 disposed in theupper chamber wall 2120. The latching ring 2520 is made from a resilient spring material (e.g. polyvinylidine fluoride) with an array of inwardly stepped portions 2530. Thus stepped portions 2530 enable the latching ring 2520 to deform from an undeformed condition in which the latching ring 2520 has a first diameter into a deformed condition in which the latching ring 2520 has a comparatively smaller diameter. Such deformation occurs when the stepped portions 2530 are subject to radial inward directed forces. Upon removal of the forces, the latching ring 2520 returns to the undeformed. - The
latching mechanism 2500 further includes an array of latching cams 2540, each associated with a respective one of the stepped portions 2530. Each latching cam 2540 is adapted to apply radial forces to the respective stepped portions 2530. - The
latching mechanism 2500 further includes anactuating ring 2560, which is adapted to actuating the latchingcams 540 as theactuating ring 2560 is raised and lowered within a predetermined limited range of movement. In the illustrated embodiment, theactuating ring 2560 is adapted, when raised, to actuate the latching cams 2540, and, when lowered, to deactuate the latching cams. Thelatching mechanism 2500 further includes an array of pneumatic devices 2580 (e.g. three such devices) which are adapted to raise and lower theactuating ring 2560. When theactuating ring 2560 is raised, the upper andlower chamber walls head 2200 can be raised from thebase 2300 for opening the upper andlower chamber walls base 2300 for closing the upper andlower chamber walls - The
actuating ring 2560 mounts upwardly projecting pins 2562 (one shown) that project into respective ones ofmultiple apertures 2564 in an aligningring 2570 when theactuating ring 2560 is raised. The aligningring 2570 is mounted to rotate conjointly with thelower chamber wall 2140. Thepins 2562 are withdrawn from theapertures 2564 and clear the aligningring 2570 when theactuating ring 2560 is lowered. When projecting into therespective apertures 2564, thepins 2562 align awafer 10 that had been supported in the processing position so as to facilitate unloading thewafer 10 via a robotic system, as mentioned above. - D. Preferred Embodiments of the Processes and Solutions
- The reactor illustrated and described above may be employed to practice the processes provided by this invention for treating a semiconductor wafer having a front, device side, a back, non-device side, and an outer perimeter (i.e., the peripheral edge), so as to remove a bulk metal or oxide thin film, such as a copper film, or metal ion or oxide contamination from selected surfaces. The wafer is suitably placed into the reactor with its back side being the lower side (or in the opposing configuration for a differently configured reactor). An etchant capable of removing the copper is used as the processing fluid. The etchant is delivered by a pump to the lower chamber. An inert gas purge is preferably used as the processing fluid that is concurrently supplied and enters the upper chamber. The supply of an inert gas purge or an aqueous rinse, such as deionized water, is preferred to insure no vapor or etchant intrusion onto the majority of the first side (excluding the edge perimeter). However, the supply of fluid to the front side is not necessary, particularly for front sides coated with an exterior layer that is not vulnerable to etchant vapor, or from which a partial amount of film can be etched without a detrimental effect to the underlying layers. The etchant is caused to flow over the back side, over an outer perimeter of the silicon wafer, and over an outer margin (the exclusion zone) of the front side, but is prevented from flowing over the remainder of the front side except for the outer margin. After the etchant removes the thin film, any residual etchant is rinsed away, as with deionized water.
- The processing fluid can suitably be a mixture of an acid and an oxidizing agent.
- If the thin film is a metal film, such as a copper film, a preferred etchant is a mixture of hydrofluoric acid and hydrogen peroxide, as an oxidizing agent. Preferably the solution includes 0.4 to 0.6 volume % HF, most preferably 0.5% HF, and 5 to 15% H2O2, most preferably 10 volume % H2O2, with the balance being deionized water. An alternative reagent is approximately 10% to 25% sulfuric acid with 5% to 15% hydrogen peroxide. An HF/H2O2 solution is preferred for stripping metal from wafers treated with a silicon nitride protective layer, which HF/H2O2 and H2SO4/H2O2 solutions are useful in stripping metal contamination from thermal oxide (silicon oxide) protective layers. Other concentrations of sulfuric acid from approximately 5% to approximately 98%, along with approximately 0% to 20% of an oxidizing agent, can be instead used to remove a metal film, such as a copper film.
- The processing fluid can also be a mixture of sulfuric acid and ammonium persulfate. Other alternative enchants that can be instead used to remove a metal film, such as a copper film, include mixtures of hydrofluoric acid and a surfactant, mixtures of hydrofluoric and hydrochloric acids, mixtures of nitric and hydrofluoric acids, and EKC 5400, which is a proprietary chemical available commercially from EKC of Hayward, Calif. Mixtures of HF and HCL are suitably supplied as 0.4 to 0.6% HF and 5% to 15% HCL in deionized water. Mixtures of HNO3 and HF are suitably supplied as 0.4 to 0.6% HF and 5% to 15% HCL in deionized water.
- In place of hydrogen peroxide in the above etchant solutions, other oxidizers capable of etching metal films may be utilized. Dissolved ozone (O3) has been found suitable for use in the above solutions in place of hydrogen peroxide, and is preferred due to its limited duration of solubility in water, such that after treatment the ozone breaks down and leaves a less hazardous waste fluid. Thus for example a suitable etchant solution for removal of metal films, such as copper films, includes 0.4 to 0.6% HF, most preferably 0.5% HF, and 10 parts per million ozone to an ozone saturated solution, preferably 20 parts per million ozone, in deionized water. When utilizing ozone as an oxidizer, apparatus used in carrying into the invention suitably include a mixing chamber into which ozone is introduced to the solution, such as through sparging ozone gas through the solution. In addition to HF/Ozone solutions, ozone may also be included as the oxidizer, in place of H2O2, in the other solutions described above, such as the sulfuric acid solutions.
- The exact etchant solution to be utilized will be selected, based on the disclosure contained herein, for use with a particular film. Turning to a specific application of the processes of the present invention, treatment of the back side and bevel edge of a wafer for removal of copper contamination will be described in further detail. A preferred process sequence for a semiconductor wafer includes initially laying down a PVD or CVD barrier/adhesion layer onto the acidic wafer, followed by application of a seed layer of a metal onto the barrier layer to support subsequent deposition. The wafer is then subjected to electrochemical deposition to deposit the desired conductive film of copper over the front (device) side of the wafer, possibly excluding the outer perimeter of the substrate from the deposition, or potentially depositing copper to the edge and over the bevel of the wafer.
- The wafer is then placed into a reaction chamber to perform a controlled etch of the back side, bevel edge, end of the seed layer metal and/or electroplated metal on the front side within a controlled distance from the perimeter edge of the substrate, to define a distinct exclusion zone from which copper has been removed by the etchant. Alternately, etchant may be supplied to remove metal from only the back side and bevel edge of the wafer, or to just remove metal contaminant from the back side of the wafer. The various process configurations will be described in terms of a process for exposing the back side, bevel edge and controlled perimeter edge exclusion zone to etchant, but it should be understood that any of these variations are possible.
- After placement of the wafer in the etchant chamber, the chamber spins until it reaches a desired processing rotational speed, at which point any residual plating solution is rinsed from the front side of the wafer using deionized water. After rinsing, an inert gas stream is preferably (but not necessarily) supplied to the front (device) side of the wafer, while an etchant solution is delivered to the back side of the wafer. The etchant solution, such as use of the HF/H2O2 or H2SO4/H2O2 solutions disclosed above, is delivered at a concentration level and for a sufficient period of time to achieve the desired level of removal of copper ions from the back side and bevel, as well as the front side exclusion zone. After cleaning of the back side and etching of the bevel and front side exclusion zone in this fashion, the wafer is rinsed with deionized water on both sides, spun to remove liquid, and then dried with inert gas such as heated nitrogen. The following tables I and II illustrate suitable sets of process steps to achieve this back side cleaning and bevel etching:
TABLE I Suitable Cu Backside Clean and Bevel Etch Recipes Step Description Time DI N2 Chem. 1 Rinse 1 0:10-0:30 Front 2 Spin off 0:05 Front 3 Etch 0:20-0:40 Front Back (preferably 0:30) 4 Rinse 2 0:10-0:30 Front, Back 5 Purge 0:05 Front, Back Front, Back 6 Rinse 3 0:10-0:30 Front, Back 7 Dry 0:60 Front, Back -
TABLE II Suitable Cu Backside Clean and Bevel Etch Recipe Step Description Time Supply 1 Etch/process 0:20-0:60 Chemical to one or both sides; N2 alternate 2 Rinse 0:10-0:30 DI rinse to front and back 3 Dry 0:30-0:60 N2 Purge to front and back; dry - The above sequence times and sequence steps are provided by way of example only, and are not intended to limit the invention. Other sequence arrangements, such as single rather than multiple rinses, and rinsing or etching for different periods of time, are also within the scope of the present invention.
- Use of a diluted sulfuric acid and peroxide solution, including approximately 10 parts H2SO4 to thirty parts H2O2 in deionized water, for an etchant exposure of approximately 30 seconds, results in removal of copper films of less than approximately 1.5 microns and achieves a back side clean of less than or equal to 5-10 copper atoms/cm2. FIG. 30 provides a scanning electron microscope photo of the exclusion zone formed on the front side of a wafer treated in accordance with this process, yielding a clean etch exclusion zone (as well as clean bevel edge and back side (not shown)), and a distinct demarcation between the exclusion zone and the substantially unaffected copper film on the remainder of the front side.
- While the specific example above uses a dilute sulfuric acid and hydrogen peroxide solution, as noted above other solutions are suitably used. FIG. 31 provides results for use of various solutions on test wafers prepared by treating the polished side of bare silicon wafers with an acid copper solution. The acid copper solution was then rinsed from the wafer, and then the back side was cleaned and the edge bevel etched in accordance with the processes and apparatus of the present invention. Post cleaning analysis was done using a TXRF detector, with detection limits being roughly 7-9E10 atoms per centimeter square. FIG. 31 provides comparative post-processing copper residues for an untreated wafer (“control”), for the acid-copper treated wafer (“uncleaned ECD+SRD”), and various etchant solutions. Specimens showing a post cleaning copper contamination level of less than 1E11 atoms were judged to be suitable. Specifically, cleaning with a hydrogen fluoride/hydrogen peroxide solution was found to yield cleaning at a level equal to that of an uncontaminated control specimen, while cleaning with a dilute sulfuric acid etchant, sulfuric acid/hydrochloric acid solutions, and DSPM (dilute sulfuric acid/hydrogen peroxide) solutions were also found to yield suitable results. The exact solution utilized will be selected in accordance with compatibility for other films on the substrate and other process solutions.
- The above examples illustrate the use of the processes of the present invention for cleaning copper contamination from the back side of a semiconductor wafer, and for etching copper from the bevel edge and front side exclusion zones. However, other processes are also suitably carried out, and involve common steps of rinsing the wafer to clear it of any residual chemistry from prior processing steps if necessary, followed by etching the wafer with a suitable etchant solution, followed by post etch rinsing such as with deionized water, spinning to remove solution, and then dying such as with heated inert gas.
- One such further example entails the removal of trace amounts of cobalt from the back side of a wafer, and unreactive cobalt from the front side of the wafer, after cobalt processing. Specifically, after a wafer has been treated with cobalt to form contact points on the front device side, such as by sputtering cobalt (physical vapor deposition) onto the front side, the front side of the wafer includes both cobalt silicides where the cobalt has contacted bare silicon, and unreacted cobalt where the cobalt has contacted an oxide coating. Processes of the present invention may be utilized to remove this unreacted cobalt from the front side, as well as to remove any cobalt contaminant from the back side (and potentially the bevel edge). In this instance, both front and back side are preferably exposed to treatment solutions.
- The preferred cobalt etching process entails first rinsing the front and back sides of the wafer. A dilute sulfuric acid/hydrogen peroxide solution, as disclosed above, is then sprayed or otherwise applied onto both sides of the wafer, concurrently, to remove unreacted cobalt. A suitable dilution for the solution is one part sulfuric acid to 10-20 parts hydrogen peroxide. After exposing both sides to this dilute sulfuric acid solution for a suitable period of time to achieve a predetermined level of cobalt removal, both sides are exposed to a further deionized water rinse. Thereafter, the back side only of the wafer is exposed to a hydrofluoric acid solution (such as 200 parts deionized water to one part HF), to remove a portion of the protective cap of oxide layer present on the back side of the wafer, which typically has an amount of cobalt diffused thereinto. The entire oxide layer is not removed, but just a predetermined amount of the oxide layer as required to remove the cobalt contamination. The front side of the wafer is preferably supplied with an inert nitrogen gas concurrent to back side treatment with hydrofluoric acid. Both sides of the wafer are then rinsed and dried. Treatment requirements for the present invention will yield a removal of cobalt with less than 1E10 as measured with total x-ray fluorescent detection. While the supply of nitrogen to the front side has been described and is preferred in order to exclude hydrofluoric acid vapor from the front side, it is not strictly necessary. Similarly, wafers with films of Pt, Pd, BST, SBT, Ru, and IP can be processed using suitable etchants.
- A further example of a process in accordance with the present invention is the cleaning of the back side of a semiconductor wafer prior to photo lithographic treatment. If particulate contamination is present on the back side of a semiconductor wafer, high spots, referred to as hotspots, can be formed on the front side of the wafer during further lithographic treatment due to the wafer sitting at an uneven degree of tilt. Prior to photo resist application, the wafer can be treated in accordance with the present invention to remove particulates and other contaminants from the backside. This process suitably is carried out by rinsing both sides of the wafer, followed by exposure of the back side only to a suitable etchant solution such as hydrofluoric acid/ozone, hydrofluoric acid/hydrogen peroxide, sulfuric acid/hydrogen peroxide or hydrochloric acid/hydrogen peroxide, as previously described above. Optionally, the front side of the wafer may be supplied with nitrogen gas at the same time as cleaning of the back side. The present invention insures that the front side is not contaminated with the cleaning solutions during the cleaning of the back side. A still further example of a process for use in the present invention is removal of dry etch residue material after patterning of a wafer. Specifically, when the front side of a wafer has been etched with a dry plasma etch, a residue consisting of materials being etched or removed from the substrate surface, gas etch residue or metallization and dielectric layer residue remains on the front side of a wafer. Conventionally, this residue is removed using a solvent to which the wafer must be exposed for a long period of time, often in an excess of 60 minutes, at elevated temperatures. In accordance with the present invention, wafers may be suitably treated at ambient temperatures, e.g., 23° C., for relatively short process times of approximately one minute in length or less, using commercially available dry etch residue removal solutions such as EKC 640 and Ashland NE 89, which are believed to be hydrofluoric acid or ammonium fluoride based solutions. EKC 640 is available from EKC Corporation, while Ashland NE 89 as available from the Ashland Corporation. The process entails rinsing and then exposing the front side of the wafer to the solvent, and then rinsing and drying both sides. Typically it is not necessary to treat the back side, which has not been contaminated during the dry etching process.
- It is noted that the above processes for cleaning the back side to remove particulate contamination prior to photo lithography, and the front side to remove dry etch residue, may be carried out concurrently in a reactor in accordance with the present invention.
- Other processes are also included with the scope of the present invention, such as etching oxides on one or both sides of the wafer, concurrently or separately.
- The present invention reduces the size of the annular exclusion zone on the front side of the wafer, which region is not available for fabricating interconnect structures and/or metallized components (see FIG. 2). All other dimensions being alike, the present invention, when used for bevel edge and front side exclusion zone cleaning, increases the surface area of a wafer available for fabricating interconnect structures and/or metallic components. It follows that this invention enables a greater yield of microelectronic devices from a silicon wafer of a given size. Advantageously, the process provided by this invention not only removes a thin film, such as a copper film, but also removes any contaminant, such as any copper or other metal, that the reagent is capable of solvating from the back side of the silicon wafer.
- The thin film removed by the process of the present invention could also be substantially comprised of silicon nitride, silicone oxide or polysilicon.
- The present invention has been illustrated with respect to a wafer. However, it will be recognized that the present invention has a wider range of applicability. By way of example, the present invention is applicable in the processing of disks and heads, flat panel displays, microelectronic masks, and other devices requiring effective and controlled wet processing. While the preferred embodiment of the invention has been illustrated and described, it will be appreciated that various changes can be made therein without departing from the spirit and scope of the invention.
Claims (66)
1. A process for treating an electrochemically processed workpiece, the workpiece having a first side, an opposing second side, and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion receiving the first side of the workpiece and a second chamber portion receiving the second side of the workpiece;
(b) supplying a first fluid to the first chamber portion to expose the first side to the first fluid while excluding at least a major portion of the second side from exposure to the first fluid; and
(c) supplying a second fluid to the second chamber portion to expose the second side to the second fluid, wherein at least one of the first and second fluids comprises an etchant for removal of a metal or oxide film from an exposed surface portion of the workpiece.
2. The process of claim 1 , wherein first and second fluids are supplied concurrently to the first and second sides of the workpiece.
3. The process of claim 1 , wherein the first and second fluids are supplied at differing time periods.
4. The process of claim 1 , further comprising exposing the peripheral edge of the workpiece to the first fluid.
5. The process of claim 4 , further comprising exposing a perimeter edge portion of the second side to the first fluid.
6. The process of claim 1 , wherein at least one of the first and second fluids comprises an inert purge gas.
7. The process of claim 1 , wherein at least one of the first and second fluids comprises an aqueous rinse.
8. The process of claim 1 , wherein the etchant comprises an acid, selected and supplied at a level sufficient to etch a metal film or oxide film to a predetermined extent, and an oxidizing agent.
9. The process of claim 8 , wherein the etchant comprises hydrofluoric acid and hydrogen peroxide.
10. The method of claim 9 , wherein the hydrofluoric acid is included at a level of 0.4 to 0.6 weight % and the hydrogen peroxide is included at a level of 5.0 to 15.0 weight %.
11. The process of claim 8 , wherein the etchant comprises hydrofluoric acid and ozone in an aqueous solution.
12. The process of claim 10 wherein the hydrofluoric acid is included at a level of 0.4 to 0.6 weight % and the ozone is present in solution at a level of 10 parts per million to an ozone saturated solution.
13. The process of claim 8 , wherein the etchant comprises sulfuric acid and hydrogen peroxide.
14. The process of claim 8 , wherein the etchant comprises hydrofluoric acid and hydrochloric acid.
15. The process of claim 8 wherein the etchant comprises nitric acid and hydrofluoric acid.
16. The process of claim 1 , further comprising excluding the first fluid from at least a major portion of the second side of the workpiece by removing the first fluid from a fluid outlet disposed in the reactor proximate the peripheral edge of the workpiece.
17. The process of claim 1 , further comprising excluding the first fluid from at least a major portion of the second side of the workpiece by creating a seal between the first side and the second side.
18. The process of claim 1 , wherein the second fluid is supplied concurrently with the first fluid and assists in excluding the first fluid from at least a major portion of the second side.
19. The process of claim 1 , wherein the first chamber portion and the second chamber portion are defined by separable first and second reactor members that cooperatively support the workpiece.
20. The process of claim 19 , wherein the first and second reactor members are spun together on a common axis during the supplying of the first and second fluids to the workpiece.
21. The process of claim 1 , further comprising spinning the reactor chamber and workpiece while supplying the first fluid to etch the surface portion of the workpiece.
22. The process of claim 1 , wherein the first and second chamber portions are defined by a unitary reactor housing.
23. The process of claim 1 , wherein a metal film is at least partially etched from the first side of the workpiece by the first fluid, the first fluid comprising an etchant.
24. The process of claim 1 , wherein the metal film comprises copper.
25. The workpiece produced by the process of claim 1 .
26. A process for treating an electrochemically processed workpiece, the workpiece having a first side, an opposing second side and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion receiving the first side and a second chamber portion receiving the second side; and
(b) supplying a first fluid to the first chamber portion to expose the first side and the peripheral edge to the first fluid while excluding at least a major portion of the second side from exposure to the first fluid, wherein the first fluid comprises an etchant for removal of a metal film or oxide film from an exposed surface portion of the workpiece.
27. The process of claim 26 , further comprising exposing a perimeter edge portion of the second side of the workpiece to the first fluid.
28. The process of claim 26 , wherein at least a portion of the first side and peripheral edge of the workpiece are contaminated with copper and the first fluid is an etchant capable of stripping the copper from the workpiece.
29. The process of claim 26 , wherein at least a portion of the first side and the perimeter edge are contaminated with cobalt and the first fluid is an etchant capable of etching the cobalt from the exposed surface of the workpiece.
30. The process of claim 26 , further comprising treating the first and second sides of the workpiece with a second fluid to remove unreacted cobalt followed by exposing the first side to the etchant.
31. The process of claim 26 wherein at least a portion of the back side and front edge are coated in an oxide film and the first fluid comprises an acidic etchant capable of removing the oxide film from the exposed surface of the workpiece.
32. The process of claim 26 , wherein the first chamber portion and the second chamber portion are defined by separable first and second reactor members that cooperatively support the workpiece.
33. The process of claim 32 , wherein the first and second reactor members are spun together on a common axis during the supplying of the first and second fluids to the workpiece.
34. The process of claim 26 , further comprising spinning the reactor chamber and workpiece while supplying the first fluid to etch the surface portion of the workpiece.
35. A process for treating a semiconductor workpiece having a front side on which a plurality of metallized devices are formed, an opposing back side and a peripheral edge defined between the front and back sides, the back side and/or peripheral edge, being contaminated with metal ions, comprising:
(a) placing the semiconductor workpiece in a reaction chamber;
(b) supplying a first fluid to the chamber to expose the back side to the first fluid while excluding at least a major portion of the front side from exposure to the first fluid, wherein the first fluid is supplied for a sufficient time period and comprises an etchant that removes at least a portion of the contaminant metal ions from the exposed surface of the workpiece; and
(c) supplying a second fluid to the chamber to expose the front side to the second fluid.
36. The process of claim 35 , wherein the first and second fluids are supplied concurrently to the back and front sides, respectively, of the workpiece.
37. The process of claim 35 , wherein the first and second fluids are supplied at different time periods.
38. The process of claim 35 , further comprising exposing the peripheral edge of the workpiece to the first fluid.
39. The process of claim 38 , further comprising exposing a perimeter edge portion of the second side to the first fluid.
40. The process of claim 35 , wherein the second fluid comprises a fluid that is different from the first fluid.
41. The process of claim 35 , wherein the second fluid comprises an inert purge gas or an aqueous rinse.
42. The semiconductor workpiece produced by the process of claim 35 .
43. The process of claim 35 , wherein the first chamber portion and the second chamber portion are defined by separable first and second reactor members that cooperatively support the workpiece.
44. The process of claim 43 , wherein the first and second reactor members are spun together on a common axis during the supplying of the first and second fluids to the workpiece.
45. The process of claim 35 , further comprising spinning the reactor chamber and workpiece while supplying the first fluid to etch the surface portion of the workpiece.
46. A process for treating a semiconductor workpiece having a front side on which a plurality of metallized devices are formed, an opposing back side and a peripheral edge defined between the front and back sides, the back side and/or peripheral edge being contaminated with metal ions, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion that receives the back side and including a first fluid inlet and a second chamber portion receiving the front side and including a second fluid inlet; and
(b) supplying a first fluid to the first chamber portion to expose the back side to the first fluid while excluding at least a major portion of the front side from exposure to the first fluid, wherein the first fluid is supplied for a sufficient time period and comprises an etchant that removes the contaminant metal ions from the exposed surface of the workpiece.
47. The process of claim 46 , wherein the first chamber portion and the second chamber portion are defined by separable first and second reactor members that cooperatively support the workpiece.
48. The process of claim 47 , wherein the first and second reactor members are spun together on a common axis during the supplying of the first and second fluids to the workpiece.
49. The process of claim 46 , further comprising spinning the reactor chamber and workpiece while supplying the first fluid to etch the surface portion of the workpiece.
50. A process for treating a semiconductor workpiece having a front side on which a plurality of metallized devices are formed, an opposing back side and a peripheral edge defined between the front and back sides, the back side and/or peripheral edge being contaminated with copper ions, comprising:
(a) placing the semiconductor workpiece in a reaction chamber that includes a first chamber portion that receives the back side of the workpiece and a second chamber portion that receives the front side of the workpiece;
(b) supplying a first fluid to the first chamber portion to expose the back side to the first fluid while excluding at least a major portion of the front side from exposure to the first fluid, wherein the first fluid is supplied for a sufficient time period and comprises an etchant that removes at least a portion of the contaminant copper ions from the exposed surface of the workpiece; and
(c) supplying a second fluid to the second chamber portion to expose the front side to the second fluid.
51. A process for treating a semiconductor workpiece having their front side on which a plurality of metallized devices are formed, an opposing back side and a peripheral edge defined between the front and back sides, the back side and/or peripheral edge being contaminated with copper ions, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion that receives the back side and including a first fluid inlet and a second chamber portion receiving the front side and including a second fluid inlet; and
(b) supplying a first fluid to the first chamber portion to expose the back side to the first fluid while excluding at least a major portion of the front side from exposure to the first fluid, wherein the first fluid is supplied for a sufficient time and comprises an etchant that removes at least a portion of the contaminant copper ions from the exposed surface of the workpiece.
52. A process for treating a workpiece, the workpiece having a first side, an opposing second side and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber; and
(b) supplying a first fluid to the chamber to expose the first side and the peripheral edge to the first fluid while excluding at least a major portion of the second side from exposure to the first fluid.
53. A process for treating a workpiece, the workpiece having a first side, an opposing second side, and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion receiving the first side of the workpiece, a second chamber portion receiving the second side of the workpiece, and a perimeter portion receiving the peripheral edge, further comprising at least one fluid outlet defined proximate the perimeter portion; and
(b) supplying a first fluid to the first chamber portion to expose the first side to the first fluid while excluding at least a major portion of the second side from exposure to the first fluid, the first fluid flowing from the reaction chamber through the outlet in the perimeter edge portion of the chamber.
54. The process of claim 53 , wherein the peripheral edge of the workpiece is exposed to the first fluid before the first fluid flows through the outlet.
55. The process of claim 53 , wherein a perimeter edge portion of the second side of the workpiece is exposed to the first fluid before the first fluid flows out through the fluid outlet.
56. A process for treating a workpiece, the workpiece having a first side, an opposing second side, and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber that includes a first chamber portion receiving the first side of the workpiece, a second chamber portion receiving the second side of the workpiece, and a perimeter portion receiving the peripheral edge; and
(b) supplying a first fluid to the first chamber portion to expose the first side to the first fluid while excluding at least a major portion of the second side from exposure to the first fluid, the first fluid flowing from the reaction chamber out the outlet in the perimeter edge portion of the chamber.
57. The process of claim 56 , wherein the first fluid is excluded from the second side by providing at least one outlet defined in the reaction chamber proximate to the perimeter edge portion of the chamber, through which outlet the first fluid flows.
58. The process of claim 56 , wherein the first fluid is excluded from the second side by providing a seal included in the reaction chamber and sealing against the peripheral edge of the workpiece.
59. The process of claim 56 , wherein the first fluid is excluded from the second side by supplying a second fluid to the second side of the workpiece while supplying the first fluid to the first side of the workpiece.
60. An etchant solution for use in etching metal and oxides from an electroplating workpiece, comprising hydrofluoric acid in an amount sufficient to solubilize the oxide or an oxide of the metal, and ozone, in an aqueous carrier.
61. The etchant solution of claim 60 , wherein the hydrofluoric acid is included at a level of 0.2 to 0.6% by volume.
62. The etchant solution of claim 61 , wherein the hydrofluoric acid is included at a level of 0.4% by volume.
63. The etchant solution of claim 60 , wherein the ozone is present in solution at a level of 10 parts per million to an ozone saturated solution.
64. The etchant solution of claim 63 , wherein the ozone is present in solution at a level of 20 parts per million.
65. A process for treating a workpiece, the workpiece having a first side, an opposing second side, and a peripheral edge defined between the first and second sides, comprising:
(a) placing the workpiece in a reaction chamber;
(b) supplying a first fluid to the chamber to expose the first side f the workpiece to the first fluid while excluding at least a major portion of the second side of the workpiece from exposure to the first fluid; and
(c) supplying a second fluid to the chamber to expose the second side of the workpiece to the second fluid, wherein at least one of the first and second fluids comprises an etchant for removal of a metal or oxide film from an exposed surface portion of the workpiece.
66. The method of claim 65 , further comprising spinning the workpiece while applying at least one of the fluids to the workpiece.