Número de publicaciónUS20050208287 A1
Tipo de publicaciónSolicitud
Número de solicitudUS 11/128,778
Fecha de publicación22 Sep 2005
Fecha de presentación13 May 2005
Fecha de prioridad2 Mar 2001
También publicado comoCA2439425A1, CA2439425C, CA2439451A1, CA2439484A1, CA2439484C, CA2439508A1, CA2439513A1, CA2439513C, CN1243615C, CN1254352C, CN1494463A, CN1494473A, CN1498162A, CN1500038A, CN1612847A, CN100391883C, DE60222245D1, DE60222245T2, DE60235531D1, EP1370369A1, EP1370369A4, EP1370369B1, EP1370401A1, EP1370401A4, EP1372952A1, EP1372952A4, EP1373157A2, EP1373157A4, EP1377440A1, EP1377440A4, EP1377440B1, US6692570, US6749897, US6824715, US6893751, US7396402, US7704316, US8153245, US20020170466, US20020170467, US20020175126, US20020179219, US20020179220, US20020189499, US20020189500, US20020192510, US20030000424, US20030070615, US20030165624, US20070077436, US20100124860, WO2002070145A1, WO2002070218A1, WO2002070247A1, WO2002070421A2, WO2002070421A3
Número de publicación11128778, 128778, US 2005/0208287 A1, US 2005/208287 A1, US 20050208287 A1, US 20050208287A1, US 2005208287 A1, US 2005208287A1, US-A1-20050208287, US-A1-2005208287, US2005/0208287A1, US2005/208287A1, US20050208287 A1, US20050208287A1, US2005208287 A1, US2005208287A1
InventoresBasil Naji, John Cottier, Robert Lyons
Cesionario originalBasil Naji, Cottier John S, Robert Lyons
Exportar citaBiBTeX, EndNote, RefMan
Enlaces externos: USPTO, Cesión de USPTO, Espacenet
Composite product
US 20050208287 A1
Resumen
A composite product comprising a substrate layer and one or more functional layers applied thereto. The slurry is applied to the substrate layer to form a functional layer and the functional layer dewatered through the substrate layer. The functional layers can be repeated to build up a laminated composite product. Functional additives may be included in each layer to provide desired properties to that layer and indeed to the subsequent composite product.
Imágenes(7)
Previous page
Next page
Reclamaciones(8)
1. A composite product comprising a substrate layer and one or more functional layers applied thereto, each functional layer including a mixture of hydraulic binder, dewatering agent wherein the quantity of dewatering agent is sufficient to permit de-watering of each functional layer through the substrate layer and any additional functional layer.
2. A composite product according to claim 1, wherein each functional layer includes one or more functional additives to provide desired properties to that layer.
3. A composite product according to claim 1, wherein the substrate layer is a fibre reinforced base material.
4. A composite product according to claim 1, wherein the substrate layer is a reinforced cementitious product.
5. A composite product according to claim 1, wherein the functional layers are added to both sides of the substrate layer.
6. A composite product according to claim 1, wherein the functional layers are added to one side of the substrate layer.
7. A composite product according to claim 1, wherein each functional layer is covered by a reinforcing layer.
8. A composite product according to claim 7, wherein the reinforcing layer comprises fibre mesh or netting.
Descripción
  • [0001]
    This is a continuation application of U.S. patent application Ser. No. 10/090, 406 filed on Mar. 4, 2002, which is hereby incorporated by reference in its entirety. This application also claims priority from the following Australian provisional patent applications, the full contents of which are hereby incorporated by cross-reference.
    Application No Title Date Filed
    PR3474 A Composite Product 2 Mar. 2001
    PR3475 Spattering Apparatus 2 Mar. 2001
    PR3476 Additive for a Dewaterable Slurry 2 Mar. 2001
    PR3477 A Method and Apparatus for Forming a 2 Mar. 2001
    Laminated Sheet Material by Spattering
    PR3478 Coatings for Building Products 2 Mar. 2001
  • BACKGROUND OF THE INVENTION
  • [0002]
    1. Field of the Invention
  • [0003]
    The present invention relates to composites and particularly, but not limited to, fibre reinforced building composites.
  • [0004]
    2. Description of the Related Art
  • [0005]
    Any discussion of the prior art throughout the specification should in no way be considered as an admission that such prior art is widely known or forms part of common general knowledge in the field.
  • [0006]
    Fibre reinforced cement (FRC) is an extremely popular building product.
  • [0007]
    The applicant along with other various parties have developed a variety of techniques for producing fibre reinforced cement building products and tailoring those FRC products to the particular environment of use.
  • [0008]
    There are still, however, certain limitations with regard to FRC products. They have limited acoustic, thermal and fire retardant properties. They can exhibit limited workability and generally lie in the medium density range (around 1300 kg/m3) or higher (compressed densities of around 1700 kg/m3).
  • [0009]
    Generally, the properties of fibre cement are altered by addition of other materials eg different fibres, fillers etc or altered with different production techniques. Such alterations to the FRC formulation, however, can be expensive to develop in order to ensure no detrimental side effects arise from such new formulations. Alterations in production methods or equipment are also expensive and time consuming to develop. Such techniques also do not provide for true “tailoring” of the FRC product. It is, of course, inappropriate to shut down an entire production line, for example, to produce a small batch of FRC product tailored to a specific use.
  • [0010]
    It is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative.
  • SUMMARY OF THE INVENTION
  • [0011]
    In a broad aspect, the present invention provides a composite product comprising a substrate layer and one or more functional layers applied thereto, each functional layer including a mixture of hydraulic binder, dewatering agent wherein the quantity of dewatering agent is sufficient to permit de-watering of each functional layer through the substrate layer and any additional functional layer.
  • [0012]
    In a second aspect, the present invention provides a method of manufacturing a composite product comprising:
      • (i) providing a substrate layer,
      • (ii) providing a slurry formulation including an hydraulic binder and dewatering agent,
      • (iii) applying said slurry to said substrate layer to form a functional layer,
      • (iv) dewatering the functional layer, and
      • (v) optionally repeating steps (ii) through (iv), wherein the quantity of dewatering agent is sufficient to maintain porosity and thereby permit de-watering of each functional layer through the substrate layer and any additional functional layer.
  • [0018]
    Preferably, the substrate layer is a fibre reinforced base material such as fibre reinforced cement. This substrate layer provides a structural base on which additional functional layers may be added.
  • [0019]
    The functional layers may be added to both sides of the substrate layer but most preferably are added to one side which generally expose one side of the building board during production. Such a technique allows the aforementioned method to be applied to current FRC production techniques such as Hatschek.
  • DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
  • [0020]
    The present applicants have developed a process for manufacture of a composite article to virtually any desired specification or use. To explain, the present inventive composite and method starts with a simple water permeable substrate layer such as conventional fibre reinforced building board. To this base layer are added one or more functional layers, each functional layer being specifically tailored to provide the desired functionality. For example, if it is desired to provide an insulating layer, the slurry formulation from which the functional layer is formed can include insulating materials such as rubber crumbs, vermiculite, perlite, gypsum, etc.
  • [0021]
    Similarly, water permeability may be decreased by including water resistant polymers eg silanes, siloxane blends etc or pozzalanic materials such as silica fume, metakaoline, ultrafine fly ash etc.
  • [0022]
    Density modification of the functional layer can be accomplished by addition of suitable light weight materials such as cenospheres (ceramic hollow spheres), expanded polystyrene, vermiculite, perlite etc.
  • [0023]
    The inventive process enables various functional layers to be integrated into a single composite by appropriate slurry modification.
  • [0024]
    In a preferred embodiment, each functional layer has a reinforcing layer positioned therebetween. The reinforcing layer may comprise fibre mesh or netting, and serves to improve the strength and durability of the composite product.
  • [0025]
    In some instances, the reinforcing layer may comprise a thin fibre reinforced cementitious layer similar for instance to the base material. This provides for more efficient utilisation of such fibre reinforced layers, similar to sandwich composite technology. It will be appreciated by a person skilled in the art, that there are areas of a composite which require less fibre reinforcement ie the core. Such a core area can be formed as the aforementioned functional layer with low fibre reinforcement. Areas which require high fibre reinforcement due to high tensile strength ie surface or skin areas, can be covered by a fibre reinforced cementitious layer. The thus formed fibre reinforced layers act as sandwich skins with a de-watered slurry functional layer acting as a sandwich core.
  • [0026]
    As a result, the described composite provides significant advantages over monolithic fibre reinforced composites. Firstly, by the aforementioned composite action, fibres can be positioned in areas where they are most required. This will, of course, lead to a reduction in the fibre reinforced volume of the product.
  • [0027]
    Secondly, such a reduced fibre volume will lead to an improvement in non-combustibility and thermal insulation performance of the composite. Production of a non-combustible composite has, in the past, been difficult to achieve due the high cost of non-combustible fibres and specialised processes required for their use.
  • [0028]
    Further, one of the most important advantages arising from preferred embodiments of the present invention is the ability to concentrate a particular functionality into a single layer. To explain, in large monolithic structural layers, particularly fibre reinforced cement building products, any adjustments to the functional or structural aspects of the product ,au be diluted or diminished or unevenly spread throughout the product. There is also the possibility of adverse side reactions occurring during production of such a monolithic product which may diminish the structural or functional attributes required. With the present invention, on the other hand, it is possible to concentrate or target specific functional or structural attributes within a single functional layer thereby assuring the attribute is provided to the resultant composite product.
  • [0029]
    Indeed, various optional additives and filler can be incorporated for specific purposes, ie acoustic, thermal or fire performance, density modification, cost or production efficiency.
  • [0030]
    A top or finish coating layer can also be provided for the composite product by a fibre reinforced cementitious layer, a material similar or identical to the functional layer or any other product. In one particularly preferred embodiment, the top or finishing coating can be primarily an “aesthetic” layer of, say, ultrafine particle size or made from a sandable material to smooth the exterior surface of the composite product and thereby provide a finish/paint ready surface.
  • [0031]
    Unless the context clearly requires otherwise, throughout the description and the claims, the words ‘comprise’, ‘comprising’, and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense; that is to say, in the sense of “including, but not limited to”.
  • [0032]
    The dewatering agent serves to maintain sufficient porosity in the slurry and product to be coated to permit dewatering of the slurry through the product to be coated. Preferably, the dewatering agent is a particulate material such as fly ash, alumina trihydrate, silica flour, cenospheres (ceramic hollow spheres) or similar.
  • [0033]
    Fly ash is particularly preferred as it permits dewatering of the slurry within a few minutes. Other particulate dewatering agents such as alumina trihydrate or silica flour may also be used, however, they increase the time required for dewatering of the slurry through the product to be coated.
  • [0034]
    In a preferred embodiment, the slurry applied to the product to be coated has a high water content. Preferably, the water content can be up to about 50%. This is in contrast to previous cementitious formulations which generally have a very high solids content.
  • [0035]
    By combining the various components of the formulation described above, a self levelling dewaterable slurry is obtained which can be applied to the substrate layer, dewatered through the substrate layer and thereby provide a uniform coating over this substrate layer.
  • [0036]
    Normally, after application of the coating, the resultant product would be normally cured, steam cured or hydrothermally cured, ie autoclaved, and if required, sanded to a smooth flat finish.
  • [0037]
    The substrate layer to which the functional layers can be applied is virtually limitless provided the slurry can be dewatered through the substrate layer. Cementitious and gypsum building boards are typical examples of suitable building products on which the coating can be applied.
  • [0038]
    The thickness of the functional layers would range from around 0.1 to 10 mm, preferably about 0.5 to 5 mm and most preferably about 1 to 3 mm.
  • [0039]
    After optional sanding, the layer may have a depth of around 0.05 to 5 mm, preferably about 1 to 2 mm and most preferably about 0.5 to 1 mm. The thus produced composite is comparable in its workability to monolithic (single layer) composites. It can be flexed, cut, drilled and fixed by nails etc to a frame without surface cracking or chipping.
  • [0040]
    The applicants have found an extremely good interlaminer bond and compatibility between the dewatered slurry layer and base layer resulting in excellent composite action, compatibility and resistance to delamination.
  • [0041]
    The term ‘hydraulic binder’ as used throughout the specification refers to a pulverised material in the solid, dry state which, when mixed with water, yields plastic mixtures that are able to set and harden, for example a cement. Included within the definition are white, grey or pigmented cements and hydraulic limes.
  • [0042]
    The term ‘cement’ includes hydraulic and alite cements such as portland cement, blended cements such as portland cement blended with fly ash, blast-furnace slag, pozzalans and the like and mixtures thereof, masonry cement, oil well cement, natural cement, alumina cement, expansive cements and the like, or mixtures thereof.
  • [0043]
    The quantity of binder in the formulation is preferably between about 10 to 50 wt % based on the total dry ingredients, more preferably about 15 to 40 wt % and most preferably about 20 to 30 wt %.
  • [0044]
    The fly ash used in the preferred embodiments provides a number of advantages including, particularly, as an aid to dewatering of the slurry as defined above.
  • [0045]
    The term ‘fly ash’ as used herein refers to a solid powder having a chemical composition similar to or the same as the composition of material that is produced during combustion of powdered coal, ie about 25 to 60 wt % silica, about 10 to 30 wt % A1203, about 5 to 25 wt % Fe2O3, about 0 to 20 wt % CaO and about 0 to 5 wt % MgO.
  • [0046]
    In another preferred embodiment, the dewatering agent may include a coarse fraction fly ash which is greater than about 100 microns. This coarse fraction fly ash includes bottom ash or similar products from coal combustion. There is an advantage to using these products over the aforementioned particle size fly ash since it is cheaper. Of course, as will be clear to persons skilled in the art, some reformulation of the slurry may be required to provide a suitable coating and appropriate dewatering characteristics when the dewatering agent is such a coarse fraction fly ash.
  • [0047]
    Fly ash particles are typically spherical and range in diameter from about 1 to 100 microns. In a preferred embodiment, the fly ash comprises two components. A first ‘larger’ size particles of fly ash with preferably about a 100 micron maximum size. This size range of fly ash is used in the slurry to aid in improving the dewatering characteristics of the slurry but also as a moderately reactive pozzalan.
  • [0048]
    The second ‘smaller’ fly ash size zone which preferably has about a 10 micron maximum size also adds an improving dewatering characteristic but is a more highly reactive pozzalan. This ‘smaller’ fly ash particle zone also improves the sanded surface quality of the finish layer.
  • [0049]
    In a preferred embodiment, the first fly ash comprises about 10 to 60 wt % of the formulation based on total dry ingredients, more preferably about 20 to 50 wt % and most preferably about 30 to 40 wt %.
  • [0050]
    The second fly ash component preferably provides about 5 to 30 wt % of the formulation based on total dry ingredients, more preferably about 10 to 25 wt % and most preferably about 15 to 20%.
  • [0051]
    The functional layers may optionally contain other additives such as fillers. Such fillers may also be used to improve the dewatering characteristics of the slurry. For example, cenospheres (hollow ceramic microspheres) diatomite, wollastonite, ground rice hulls, ground perlite or the like, are particularly suitable for this purpose.
  • [0052]
    These and other fillers may also be used to provide additional benefits, for example calcium carbonates or alumina hydrates improve sandability and flexibility of the coated layer respectively. Silica flour improves hardness of the sanded surface of the coating layer and the acoustic/thermal insulation properties of the layer can be improved by including rubber particles, vermiculite, perlite, shredded or expanded polystyrene or gypsum.
  • [0053]
    The fillers preferably comprise about 5 to 30 wt % of the formulation based on total dry ingredients, more preferably about 10 to 25 wt % and most preferably about 25 to 20 wt %.
  • [0054]
    The functional layers may also contain other organic additives. Cement plasticising agents, for example, may be used to alter the rheology of the slurry. Suitable cement plasticising agents include melamine sulphonate formaldehyde condensates, naphthalene sulphonate formaldehyde condensates, naphthalene sulphonates, calcium lignosulphonates, sodium lignosulphonates, saccharose, sodium gluconate, sulphonic acids, carbohydrates, amino carboxylic acids, polyhydroxycarboxilic acids, sulphonated melomine and the like.
  • [0055]
    The amount of cement plasticiser of course will depend upon the fluidising ability of the particular plasticisers. Generally the quantity of plasticiser will be in the range of about 0.3 to 3 wt % and more preferably about 0.5 to 2 wt % based on the total of dry ingredients in the formulation.
  • [0056]
    Particularly preferred cement plasticisers are Melment F-10, a melamine formaldehyde sodium bisulphate polymer dispersant marketed by SKW-Trostburg in the form of a fine white powder. Another suitable plasticiser is Neosyn, a condensed sodium salt of sulphonated naphthalene formaldehyde available from Hodgson Chemicals.
  • [0057]
    Another preferred component in the coating is a biopolymer which acts to enhance the flowability, segregation resistance and self levelling qualities of the cementitious slurry. Particularly suitable bioplymers are xanathan gum and/or whelan gum, eg KELCO-CRETE, K1C 376 manufactured by Monsanto.
  • [0058]
    Latex may also be included in the formulation to improve adherence, elasticity, stability and impermeability of the functional layers. The latex also improves flexibility of the formed composite.
  • [0059]
    The latex may be selected from the group consisting of acrylic latex, styrene latex, butadiene latex or mixtures thereof and is provided preferably in an amount between about 0.5 to 20%, more preferably about 1 to 15% and most preferably about 10% by weight of cement (on polymer solids basis) solids.
  • [0060]
    Vinyl polymers may also be incorporated into the formulation either in addition or as a substitute to the latex emulsions. Such vinyl polymers or equivalent polymeric materials enhance adhesion, resilience and flexural strength and abrasion resistance of the functional layer.
  • [0061]
    Preferred vinyl polymers include polyvinyl acetate or a copolymer vinyl acetate with another monomer such as ethylene. A particularly preferred vinyl acetate resin is VINNAPAS LL5044 thermo plastic resin powder which contains a vinyl acetate-ethylene copolymer available from Wacker. Such powdered vinyl polymer is preferably provided in quantities similar to the latex emulsion referred to above.
  • [0062]
    In addition to the above, conventional other additives such as mineral oxides, hydroxides and clays, metal oxides and hydroxides, fire retardants such as magnesite, thickeners, silica fume or amorphous silica, water sealing agents, water reducing agents, setting modifiers, hardeners, dispersants, foaming agents or flocculating agents, water-proofing agents and density modifiers are suitable for use with the present invention.
  • [0063]
    In this regard, one particular advantage arising from the preferred embodiments is the ability to treat the product to be coated by providing additives in the functional layer. To explain, since the slurry is dewatered through the product to be coated, it is possible to provide additives to the base layer by incorporation in the slurry. For instance, a waterproofing agent such as silane may be included in the formulation in excess of the functional layer requirements. During dewatering, the silane will be drawn into and through the base layer being coated thereby treating the base layer. This simultaneous treatment of the base layer as well as providing a functional attribute via the deposited layer is a valuable additional benefit arising from the aforedescribed method.
  • EXAMPLES
  • [0064]
    The present invention will now be described by way of example only with reference to the following embodiments.
  • [0065]
    In each of the following examples, the product was produced as follows.
  • [0000]
    Step 1 Slurry Preparation
  • [0066]
    A slurry of the formulation is prepared by mixing the hydraulic binder, fly ash and other optional components with water. The solids content in the slurry is preferably between about 50 and 90%, more preferably about 55 to 80% and most preferably about 60 to 70%.
  • [0000]
    Step 2 Slurry Application/Dewatering
  • [0067]
    The slurry is applied to the base layer by any convenient means such as brushes rollers, knives or sprays etc. The slurry is designed to self level and form a uniform coating on the product. The building product to be coated exhibits s certain degree of porosity causing the slurry to dewater and form a uniform deposited cementitious layer. Time for dewatering can vary quite dramatically but normally occurs between about 10 and 90 seconds, depending on the porosity of the material to be coated, its water content and thickness and viscosity of the slurry formulation. A vacuum may be used to reduce the slurry dewatering time if required. This is particularly useful when tailoring the coating process to the speed of a building product forming process, eg between about 40 to 45 seconds on a Hatschek production line.
  • [0000]
    Step 3 Curing
  • [0068]
    After forming, the green laminate article comprising the building product plus coating is preferably precured for a short time, eg up to about 48 hours, then cured by air/moist curing at room temperature, steam curing between about 40 and 90° C. or autoclaving in a steam pressure vessel between about 120 and 200° C.
  • [0069]
    For either of these three curing techniques, a curing time range between about 6 and 72 hours, preferably up to about 48 hours, is suitable. Of course, as will be clear to persons skilled in the art, the length of time chosen for curing is dependent on the formulation, the manufacturing process and form of the article.
  • [0070]
    The following examples relate to specific formulation compositions.
  • Example 1 Sandable Dewatered Slurry Composition
  • [0000]
    Function: Sandable, Durable Finishing Layer for Facade Applications.
  • [0071]
    The low viscosity slurry (drainage time in 50 ml volume funnel=3.4 seconds) was applied on the base layer (Hardiform™ 12 mm thick cellulose fibre reinforced cement-based green sheet manufactured by James Hardie Industries). The slurry dewatered in 90 seconds (un-aided by vacuum) forming a 1.25 mm thick coating. The coated sheet was autoclave-cured for 8 hrs at 180 ° C. temperature and 0.80 MPa pressure. It was then sanded flat to 0.60 mm thick using industrial sanders equipped with 100 grit sand paper belts.
    % by total
    Slurry weight of
    Composition solids (S) Weight in gm
    Dewatered Cementitious Composition
    Portland Cement 30 12000
    Silica Flour 10 4000
    (400 G grade)
    Fly ash 40 16000
    (larger size fraction)
    Fly ash 20 8000
    (smaller size fraction)
    Total 100 40000
    Water (W) 14000
    Water/Solids (W/S 0.35
    ratio)
    Solids Content 0.74
    (W/W + S)
    Organic Additives
    Welan Gum 0.0075 3.0
    (Kelcocrete)
    naphthalene 0.25 100.0
    formaldehyde
    Plasticising Agent
    (Neosyn)
    Acrylic Emulsion 1.0 400.0
    Rhoplex MC1934
  • Example 2 Rubberised Dewatered Slurry Composition
  • [0000]
    Function: In Skid-Resistant Flooring, Hard Wearing Static Dissipative Flooring and Acoustic Insulating Ceiling Panels.
  • [0072]
    The low viscosity slurry (drainage time in 50 ml volume funnel =4.2 seconds) was applied on the base layer (Hardiform™ 12 mm thick cellulose fibre reinforced cement-based green sheet manufactured by James Hardie Industries). The slurry dewatered in 60 seconds (un-aided by vacuum) forming a 1.25 mm thick coating. The coated sheet was autoclave-cured for 8 hrs at 180 ° C. temperature and 0.80 MPa pressure. It was then sanded flat to 0.60 mm thick using industrial sanders equipped with 100 grit sand paper belts.
    % by total
    Slurry weight of
    Composition solids (S) Weight in gm
    Dewatered Cementitious Composition
    Portland Cement 30 12000
    Recycled Rubber crumbs 10 4000
    (minus 30 mesh)
    Fly ash 40 16000
    (larger size fraction)
    Fly ash 20 8000
    (smaller size fraction)
    Total 100 40000
    Water 13000
    Water/Solids (W/S 0.325
    ratio)
    Solids Content 0.755
    (W/W + S)
    Organic Additives
    Welan Gum (Kelcocrete) 0.0075 3.0
    naphthalene 0.25 100.0
    formaldehyde
    Plasticising Agent
    (Neosyn)
    Acrylic Emulsion 1.0 400.0
    Rhoplex MC1934
  • Example 3 Flexible & Sandable Dewatered Slurry Composition
  • [0000]
    Function: Flexible & Sandable Layer on Thin Fibre Cement Reinforced Cement-Based Lining.
  • [0073]
    The low viscosity slurry (drainage time in 50 ml volume funnel =2.8 seconds) was applied on the base layer (Hardiflex™ 4.5 mm thick cellulose fibre reinforced cement-based green sheet manufactured by James Hardie Industries). The slurry dewatered in 120 seconds (un-aided by vacuum) forming a 1.25 mm thick coating. The coated sheet was precured for 48 hours then was autoclave-cured for 8 hrs at 180 ° C. temperature and 0.80 MPa pressure. It was then sanded flat to 0.60 mm thick using industrial sanders equipped with 100 grit sand paper belts.
    % by total
    Slurry weight of
    Composition solids (S) Weight in gm
    Dewatered Cementitious Composition
    Portland Cement 20 8000
    Calcium Carbonate 10 4000
    Grade 10 (40 um avg.
    size)
    Alumina Tri-hydrate 5 2000
    (80 um avg. size)
    Fly ash 45 18000
    (larger size fraction)
    Fly ash 20 8000
    (smaller size fraction)
    Total 100 40000
    Water 12000
    Water/Solids (W/S 0.30
    ratio)
    Solids Content 0.77
    (W/W + S)
    Organic Additive
    Welan Gum (Kelcocrete) 0.0075 3.0
    naphthalene 0.25 100.0
    formaldehyde
    Plasticising Agent
    (Neosyn)
    Styrene Acrylic Latex 5 2000
    Emulsion (56% solids)
  • Example 4 Flexible & Sandable Dewatered Slurry Composition (Low Cement)
  • [0000]
    Function: Flexible & Sandable Layer on Thin Fibre Cement Reinforced Cement-Based Lining.
  • [0074]
    The low viscosity slurry (drainage time in 50 ml volume funnel=4.5 seconds) was applied on the base layer (Hardiflex™ 4.5 mm thick cellulose fibre reinforced cement-based green sheet manufactured by James Hardie Industries). The slurry dewatered in 90 seconds (un-aided by vacuum) forming a 1.25 mm thick coating. The coated sheet was autoclave-cured for 8 hrs at 180 ° C. temperature and 0.80 MPa pressure. It was then sanded flat to 0.60 mm thick using industrial sanders equipped with 100 grit sand paper belts.
    % by
    total
    Slurry weight of
    Composition solids (S) Weight in gm
    Dewatered Cementitious Composition
    Portland Cement 10 4000
    Calcium Carbonate 20 8000
    Grade 10 (40 um avg.
    size)
    Alumina Tri-hydrate 5 2000
    (80 um avg. size)
    Fly ash 40 18000
    (larger size fraction)
    Fly ash 25 10000
    (smaller size fraction)
    Total 100 40000
    Water 16000
    Water/Solids (W/S 0.40
    ratio)
    Solids Content 0.715
    (W/W + S)
    Organic Additives
    Welan Gum (Kelcocrete) 0.0075 3.0
    naphthalene 0.25 100.0
    formaldehyde
    Plasticising Agent
    (Neosyn)
    Vinyl acetate-ethylene 1.625 650
    powdered copolymer
    (Vinnapas LL5004)
  • [0075]
    The aforementioned examples provide a composite comparable in workability to monolithic or single layer composites. They can be flexed, cut, drilled or fixed by nails or the like to a frame without surface cracking or chipping.
  • [0076]
    The surface is ‘finish-ready’ and remains smooth, flat, crack-free and with low permeability even when used in a curved configuration.
  • [0077]
    Each example provided excellent interlaminer bond between the base sheet and coating exhibiting good composite action, compatibility and resistance to delamination.
  • [0078]
    The applicants have developed a unique process which allows them to combine fibre reinforced layers with functional dewatered slurry layers optional reinforced with a wide range of synthetic or natural fibres, eg polypropylene, glass, PVA, cellulose fibres etc. The outcome of the aforementioned method is to produce a fibre reinforced composite with strength, water resistance, incombustibility of fibre cement with a low density, surface finish and insulation properties of, for example, gypsum board.
  • [0079]
    The applicants have found that using the techniques described herein, functional layers can be added to the substrate layer with no delamination or incompatibility between the layers, ie no differential shrinking, warping or similar properties.
  • [0080]
    It will be understood by persons skilled in the art that the present invention may be embodied in other forms without departing form the spirit or scope of the inventive idea as described herein. In particular, it will be appreciated that the formulations, coatings, additives, methods and composite products of the present invention are suitable or may be adapted for use in conjunction with the methods and apparatus as described in the various priority documents.
Citas de patentes
Patente citada Fecha de presentación Fecha de publicación Solicitante Título
US2987408 *27 Mar 19586 Jun 1961Corson G & W HPozzolanic material
US3782958 *7 Feb 19721 Ene 1974Us Air ForceGlass showing electrical switching phenomena
US3865779 *5 May 197211 Feb 1975Hiromichi MurataProcess for preparing reinforcing additives to be applied to inorganic cements
US3873025 *6 May 197425 Mar 1975Stora Kopparbergs Bergslags AbMethod and apparatus for atomizing a liquid medium and for spraying the atomized liquid medium in a predetermined direction
US3932275 *29 Ago 197413 Ene 1976Amax Resource Recovery Systems, Inc.Process for the treatment of mineral slimes
US4009135 *4 Oct 197422 Feb 1977Hoechst AktiengesellschaftAdditive for mortar and concrete
US4066723 *19 Mar 19763 Ene 1978Caterpillar Tractor Co.Method and apparatus for making fibrous concrete
US4070199 *27 Oct 197624 Ene 1978Imperial Chemical Industries LimitedCementitious compositions
US4088804 *16 Feb 19779 May 1978Cornwell Charles ECementitious coatings and method
US4102697 *8 Jul 197625 Jul 1978Sumitomo Chemical Company, LimitedFluid plaster composition
US4134773 *3 Oct 197716 Ene 1979Centralna Laboratoria Po Physiko-Chimicheska Mechanika Pri BanMethod of accelerated hardening and strength-increasing of different cements
US4188231 *17 Jun 197712 Feb 1980Valore Rudolph CMethods of preparing iron oxide mortars or cements with admixtures and the resulting products
US4204644 *25 Oct 197727 May 1980Asahi Glass Company, LimitedSpraying apparatus for preparing glass fiber reinforced cementitious product
US4250134 *20 Jun 197910 Feb 1981L. John MinnickMethod for the production of cementitious compositions and aggregate derivatives from said compositions
US4256504 *16 Oct 197917 Mar 1981The United States Of America As Represented By The Secretary Of The InteriorFly ash-based cement
US4256584 *25 Jul 197917 Mar 1981Mold-Masters LimitedInjection molding filter assembly
US4261286 *9 Jul 197914 Abr 1981Maschinenfabrik Max KroenertApparatus for coating of moving sheets with a contact adhesive
US4265674 *7 Ago 19795 May 1981Hoechst AktiengesellschaftAdditive for concrete or mortar and the use thereof
US4268316 *27 Jul 197919 May 1981Martin Marietta CorporationMasonry cement composition
US4328145 *26 Oct 19794 May 1982American Admixtures And Chemicals CorporationAdditive for air-entrained super plasticized concrete, concrete produced thereby and method of producing air-entrained super plasticized concrete
US4339289 *25 Ago 198013 Jul 1982Battelle Development CorporationConcrete overlay construction
US4344804 *21 Nov 197917 Ago 1982Stamicarbon B.V.Process and apparatus for the manufacture of fiber-reinforced hydraulically bound articles such as cementitious articles
US4374672 *19 Oct 198122 Feb 1983The Detroit Edison CompanyMethod of and composition for producing a stabilized fill material
US4379729 *7 Ago 198012 Abr 1983Tarmac Industrial Holdings LimitedMethod and apparatus for the production of composite sheet material and a sheet material produced thereby
US4383960 *4 Jun 198117 May 1983Adrien DelcoigneProcess and mechanism for the elimination of excess water from a mixture of plaster and water, and the product obtained
US4394175 *7 May 198119 Jul 1983Cheriton Leslie WSelf-levelling cementitious mixes
US4403006 *13 Mar 19806 Sep 1983United States Gypsum CompanySag-resistant gypsum board containing coal fly ash and method for making same
US4441723 *13 Abr 198210 Abr 1984General Connectors Corp.Duct seal
US4441944 *31 Dic 198110 Abr 1984Pmp CorporationBuilding board composition and method of making same
US4495301 *6 Abr 198322 Ene 1985Dresser Industries, Inc.Insulating refractories
US4507154 *12 Oct 198226 Mar 1985Sika Ag, Vorm. Kaspar Winkler & Co.Chloride-free setting accelerator for hydraulic binding agents
US4721160 *19 Ago 198526 Ene 1988Dowell Schlumberger IncorporatedComposition for a lightweight cement slurry for cementing oil and gas wells
US4746364 *10 Jul 198624 May 1988Shimizu Construction Co., Ltd.Flowing concrete and process of producing the same
US4759802 *31 Oct 198626 Jul 1988Kao CorporationCement dispersion agent
US4767491 *14 Feb 198630 Ago 1988Moplefan S.P.A.Device for the continuous production of manufactured articles reinforced with mixtures of hydraulic binders
US4772328 *18 Dic 198620 Sep 1988Basf CorporationHydraulic cementitious compositions reinforced with fibers containing polyacrylonitrile
US4816091 *24 Sep 198728 Mar 1989Miller Robert GMethod and apparatus for producing reinforced cementious panel webs
US4818595 *24 Abr 19874 Abr 1989Delphic Research Laboratories, Inc.Fire barrier coating and fire barrier plywood
US4840688 *1 Sep 198820 Jun 1989Pfleiderer Industrie Gmbh & Co., KgMethod for the production of fibrous plaster boards
US4846889 *2 Feb 198811 Jul 1989The Dow Chemical CompanyPolymeric blend useful in thin-bed mortar compositions comprising a water-soluble cellulose ether and a water-insoluble, but water-dispersible polymer
US4904503 *29 Sep 198727 Feb 1990W. R. Grace & Co.-Conn.Rapid setting cementitious fireproofing compositions and method of spray applying same
US4915740 *24 Sep 198710 Abr 1990Denki Kagaku Kogyo Kabushiki KaishaHydraulic material composition having high strength
US4933013 *7 Sep 198812 Jun 1990Denki Kagaku Kogyo Kabushiki KaishaHydraulic material composition having high strength
US4933031 *17 Sep 198712 Jun 1990Elkem A/S And Den Norske Stats Oljeselskap A.S.Hydraulic cement slurry
US4935060 *16 Nov 198919 Jun 1990Elkem A/SHydraulic cement slurry
US4946505 *17 Jul 19897 Ago 1990Chemische Werke Brockhues AgProcess for dyeing concrete
US4981740 *21 Mar 19891 Ene 1991Kkkk A/SAcid resistant concrete articles, especially sulfur concrete pipes, and a method of manufacturing said articles
US4994113 *6 Feb 199019 Feb 1991Core-Guard Industries, Inc.Mixture for the preparation of building materials
US5032548 *27 Feb 199016 Jul 1991Marathon Oil CompanyConstruction material containing catalytic cracking catalyst particles
US5047086 *28 Abr 198910 Sep 1991Shin-Etsu Chemical Co., Ltd.Cement composition for extrusion
US5108510 *18 May 199028 Abr 1992Sika Ag, Vorm. Kaspar WinklerHighly reactive hydraulic binder for the preparation of building, construction and raw materials
US5108679 *2 Nov 199028 Abr 1992Redland Roof Tile LimitedProcess for the production of concrete building products
US5192366 *4 Dic 19909 Mar 1993Denki Kagaku Koygo Kabushiki KaishaCement admixture and cement composition
US5236773 *25 Oct 199117 Ago 1993The United States Of America As Represented By The Secretary Of The NavyFire-resistant barriers for composite materials
US5294255 *23 Sep 199215 Mar 1994Specrete-Ip IncorporatedPumpable backfill grout
US5338357 *3 Ago 199216 Ago 1994Polyfibre S.A.Fibre reinforced shaped solid articles
US5346012 *1 Feb 199313 Sep 1994Halliburton CompanyFine particle size cement compositions and methods
US5383521 *1 Abr 199324 Ene 1995Halliburton CompanyFly ash cementing compositions and methods
US5385764 *21 Jul 199331 Ene 1995E. Khashoggi IndustriesHydraulically settable containers and other articles for storing, dispensing, and packaging food and beverages and methods for their manufacture
US5387283 *29 Jun 19947 Feb 1995Kirkpatrick; William D.Process for producing a hydraulic cement binder for both general and special applications
US5387626 *28 Abr 19947 Feb 1995Hoechst AktiengesellschaftAdditive combination for improving the processing properties of water-containing mixtures of building materials
US5403394 *24 Feb 19944 Abr 1995Burgand; YvesSelf-leveling floor coating material
US5432212 *4 Abr 199411 Jul 1995W. R. Grace & Co.-Conn.Dispersant composition for cement having excellent property in inhibition of slump-loss
US5439518 *6 Ene 19938 Ago 1995Georgia-Pacific CorporationFlyash-based compositions
US5453123 *16 Dic 199326 Sep 1995Sika Ag, Vorm. Kaspar Winkler & Co.Thixotroping and set-accelerating additive for mixtures containing a hydraulic binder, process using the additive, apparatus for preparing the mixtures containing a hydraulic binder as well as the additive
US5453310 *17 Feb 199326 Sep 1995E. Khashoggi IndustriesCementitious materials for use in packaging containers and their methods of manufacture
US5484480 *19 Oct 199316 Ene 1996Jtm Industries, Inc.Use of alumina clay with cement fly ash mixtures
US5490889 *20 Ene 199513 Feb 1996Kirkpatrick; William D.Blended hydraulic cement for both general and special applications
US5508072 *19 Nov 199316 Abr 1996E. Khashoggi IndustriesSheets having a highly inorganically filled organic polymer matrix
US5536310 *6 Oct 199416 Jul 1996Sandoz Ltd.Cementitious compositions containing fly ash
US5556458 *6 Oct 199417 Sep 1996Sandoz Ltd.Cementitious compositions
US5728458 *16 Ago 199617 Mar 1998Diversitech CorporationLight-weight high-strength composite pad
US5888322 *14 Jul 199730 Mar 1999Nalco Chemical CompanyPolymeric oxyalkylate viscosity modifiers for use in gypsum wallboard production
US5900053 *15 Ago 19974 May 1999Halliburton Energy Services, Inc.Light weight high temperature well cement compositions and methods
US6030447 *25 Jul 199729 Feb 2000James Hardie Research Pty. LimitedCement formulation
US6204214 *29 Jul 199820 Mar 2001University Of ChicagoPumpable/injectable phosphate-bonded ceramics
US6346146 *9 Abr 199812 Feb 2002James Hardie Research Pty LimitedBuilding products
US6387175 *5 Oct 200014 May 2002Bethlehem Steel CorporationRoadway base intermediate, roadway base, and methods of manufacture
US6506248 *17 Jul 200114 Ene 2003James Hardie Research Pty LimitedBuilding products
US6533848 *13 Mar 200118 Mar 2003University Of Kentucky Research FoundationTechnology and methodology for the production of high quality polymer filler and super-pozzolan from fly ash
US6572697 *9 Mar 20013 Jun 2003James Hardie Research Pty LimitedFiber cement building materials with low density additives
US6676745 *2 Oct 200113 Ene 2004James Hardie Research Pty LimitedFiber cement composite materials using sized cellulose fibers
US6682595 *12 Sep 200227 Ene 2004Ronald Lee BarbourSettable composition containing potassium sulfate
US6692564 *6 Jun 200217 Feb 2004Mbt (Schweiz) AgPreparation of concrete accelerator
US6749897 *4 Mar 200215 Jun 2004James Hardie Research Pty LimitedCoatings for building products and methods of using same
US6777103 *2 Oct 200117 Ago 2004James Hardie Research Pty LimitedFiber cement composite material using biocide treated durable cellulose fibers
US6893751 *4 Mar 200217 May 2005James Hardie Research Pty LimitedComposite product
US7028436 *5 Nov 200218 Abr 2006Certainteed CorporationCementitious exterior sheathing product with rigid support member
US20020112827 *2 Oct 200122 Ago 2002Merkley Donald J.Method and apparatus for reducing impurities in cellulose fibers for manufacture of fiber reinforced cement composite materials
US20030164119 *4 Mar 20024 Sep 2003Basil NajiAdditive for dewaterable slurry and slurry incorporating same
US20040083677 *15 Ene 20036 May 2004Bezubic William PaulCementitious exterior sheathing product having improved interlaminar bond strength
US20040145078 *13 Ene 200429 Jul 2004Merkley Donald J.Fiber cement composite materials using sized cellulose fibers
US20040168615 *7 Ene 20042 Sep 2004Caidian LuoFiber cement composite materials using bleached cellulose fibers
US20050005821 *10 Ago 200413 Ene 2005Ciments FrancaisCement composition, its use for the production of a self-leveling liquid casting, and a casting thus obtained
US20050016423 *17 Ago 200427 Ene 2005Merkley Donald J.Fiber cement composite material using biocide treated durable cellulose fibers
US20050045067 *7 Oct 20043 Mar 2005Basil NajiAdditive for dewaterable slurry and slurry incorporating same
US20050126430 *16 Dic 200416 Jun 2005Lightner James E.Jr.Building materials with bioresistant properties
US20070077436 *4 Dic 20065 Abr 2007James Hardie Research Pty LimitedComposite product
Citada por
Patente citante Fecha de presentación Fecha de publicación Solicitante Título
US765879415 Abr 20039 Feb 2010James Hardie Technology LimitedFiber cement building materials with low density additives
US77043164 Mar 200227 Abr 2010James Hardie Technology LimitedCoatings for building products and methods of making same
US772732928 Feb 20081 Jun 2010James Hardie Technology LimitedFiber cement building materials with low density additives
US781584113 Ene 200419 Oct 2010James Hardie Technology LimitedFiber cement composite materials using sized cellulose fibers
US7846244 *15 Mar 20077 Dic 2010Grazyna JanikSealing agent for waterproof barriers
US785790621 Feb 200828 Dic 2010James Hardie Technology LimitedFiber reinforced cement composite materials using chemically treated fibers with improved dispersibility
US79429647 Ene 200417 May 2011James Hardie Technology LimitedFiber cement composite materials using bleached cellulose fibers
US79935707 Oct 20039 Ago 2011James Hardie Technology LimitedDurable medium-density fibre cement composite
US799857111 Jul 200516 Ago 2011James Hardie Technology LimitedComposite cement article incorporating a powder coating and methods of making same
US81333522 Oct 200113 Mar 2012James Hardie Technology LimitedMethod and apparatus for reducing impurities in cellulose fibers for manufacture of fiber reinforced cement composite materials
US81826067 Jun 201022 May 2012James Hardie Technology LimitedFiber cement building materials with low density additives
US820992720 Dic 20073 Jul 2012James Hardie Technology LimitedStructural fiber cement building materials
US826811917 Feb 201218 Sep 2012James Hardie Technology LimitedMethod and apparatus for reducing impurities in cellulose fibers for manufacture of fiber reinforced cement composite materials
US83338367 Abr 201118 Dic 2012James Hardie Technology LimitedFiber cement composite materials using bleached cellulose fibers
US860323925 Abr 201210 Dic 2013James Hardie Technology LimitedFiber cement building materials with low density additives
US899346212 Abr 200731 Mar 2015James Hardie Technology LimitedSurface sealed reinforced building element
US20040145078 *13 Ene 200429 Jul 2004Merkley Donald J.Fiber cement composite materials using sized cellulose fibers
US20070227397 *15 Mar 20074 Oct 2007Grazyna JanikSealing agent for waterproof barriers
Eventos legales
FechaCódigoEventoDescripción
26 Mar 2007ASAssignment
Owner name: JAMES HARDIE INTERNATIONAL FINANCE B.V., NETHERLAN
Free format text: AGREEMENT CONFIRMING ASSIGNMENT OF IP RIGHTS BETWEEN JAMES HARDIE RESEARCH PTY LIMITED AND NV TECHNOLOGY HOLDINGS;ASSIGNOR:JAMES HARDIE RESEARCH PTY LIMITED;REEL/FRAME:019064/0120
Effective date: 20040101
Owner name: JAMES HARDIE RESEARCH PTY LIMITED, AUSTRALIA
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAJI, BASIL;COTTIER, JOHN SYDNEY;LYONS, ROBERT;REEL/FRAME:019064/0476
Effective date: 20020529