US20050220160A1 - Vertical cavity surface emitting semiconductor laser device - Google Patents
Vertical cavity surface emitting semiconductor laser device Download PDFInfo
- Publication number
- US20050220160A1 US20050220160A1 US11/138,424 US13842405A US2005220160A1 US 20050220160 A1 US20050220160 A1 US 20050220160A1 US 13842405 A US13842405 A US 13842405A US 2005220160 A1 US2005220160 A1 US 2005220160A1
- Authority
- US
- United States
- Prior art keywords
- layer
- type
- layers
- reflectivity
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A vertical cavity surface emitting semiconductor laser (VCSEL) device has p-type and n-type DBRs sandwiching therebetween a resonant cavity including an active layer. Each the DBRs has a plurality of layer pairs each including a Alx1Ga1-x1As high-reflectivity layer and an Alx2Ga1-x2As low-reflectivity layer and an Alx3Ga1-x3As slope content layer interposed between each of the high-reflectivity layers and adjacent low-reflectivity layer. The slope content layers in the vicinity of the active layer has an Al content x3 wherein 0<x3≦0.3 and 0.55≦x3<1 and an impurity concentration of 3×1017 cm−3 or above.
Description
- (a) Field of the Invention
- The present invention relates to a vertical cavity surface emitting semiconductor laser device (VCSEL device) and, more particularly, to a VCSEL device for use as a light source in the field of optical data transmission and optical communications.
- (b) Description of the Related Art
- The VCSEL devices have attracted attentions in the data transmission field. The VCSEL device includes a pair of semiconductor multi-layer reflectors (referred to as DBRs hereinafter) overlying a semiconductor substrate, and a resonant cavity sandwiched between the DBRs and including an active layer for laser emission and a pair of cladding layers sandwiching therebetween the active layer. Each DBR includes a plurality of Al(Ga)As/(Al)GaAs layer pairs, and one of the DBRs passes therethrough a laser beam in the direction perpendicular to the substrate surface.
-
FIG. 11 shows a conventional VCSEL device, which includes an n-type GaAs (n-GaAs)substrate 111, and a layer structure formed thereon by an epitaxial growth process. The layer structure includes consecutively, as viewed from the n-GaAs substrate 111, an n-typelower DBR 112, an n-typelower cladding layer 113, an active layer oractive layer structure 114, a p-typelower cladding layer 115, acurrent confinement layer 116, a p-typeupper DBR 117, and a p-typeGaAs cap layer 118. The VCSEL device further includes a p-side electrode 119 formed on the layer structure and an n-side electrode 120 formed on the bottom surface of the n-GaAs substrate 111. The active layer (or active layer structure) 114 emits light by recombination of positive holes and electrons injected from the p-side electrode 19 and theaside electrode 20, respectively. -
FIG. 12 shows the structure of the n-type DBR 112 as well as the p-type DBR 117. Each of the lower andupper DBRs reflectivity layer 112A and an Alx12Ga1-x12As low-reflectivity layer 112B, and an Alx13Ga1-x13Asslope content layer 112C sandwiched between each of the high-reflectivity layer 112A and each adjacent low-reflectivity layer 112B, wherein 0≦x11<1, 0≦x12≦1, x11<x12, x11<x13<x12. One of the Alx13Ga1-x13Asslope content layers 112C has a stepwise increasing Al content x13 between x11 and x12 as viewed from the high-reflectivity layer 112A toward the low-reflectivity layer 112B, and another of Alx13Ga1-x13Asslope content layers 112C has a stepwise decreasing Al content x13 between x12 and x11 as viewed from the low-reflectivity layer 112C toward the high-reflectivity layer 112A. The pair ofDBRs active layer 114 to lase between theDBRs upper DBR 117 as a laser beam having a desired output power. - The
current confinement layer 116 is disposed between the p-type cladding layer 115 and theupper DBR 117, has anon-oxidized area 116A as a current injection area and an oxidized-Al area 116B as a current confinement area, and implements a current injection path for injecting current into theactive layer 114 from the p-side electrode 119. Thecurrent confinement layer 116 may be. formed by replacing the Alx12Ga1-x12As low-reflectivity layer 112B of theupper DBR 17 with an AlAs layer in the vicinity of theactive layer 114 and selectively oxidizing the Al content in the AlAs layer. - In the conventional VCSEL device as described above, it is observed that the VCSEL device reduces its optical output power during a continuous laser emission operation thereof. The reduction of the optical output power sometimes results in halt of the laser emission itself and degrades the reliability of the optical data transmission.
- In view of the above, it is an object of the present invention to provide a VCSEL device which is capable of suppressing the reduction of the output power during a continuous laser emission operation and removing the resultant halt of the laser emission.
- The present inventors found that the reduction of the output power could be suppressed by optimizing the Al content and/or the dopant concentration of the slope content layers of the n-type DBR disposed in the vicinity of the active layer, i.e., disposed within a distance from the active layer which was equivalent to the effective cavity length of the laser device.
- Thus, the present invention provides, in a first aspect thereof, a vertical cavity surface emitting semiconductor laser (VCSEL) device comprising a semiconductor substrate, and a layer structure formed thereon, the layer structure including an active layer, p-type and n-type cladding layers sandwiching therebetween the active layer, p-type and n-type semiconductor multilayer mirrors (DBRs) sandwiching therebetween the p-type and n-type cladding layers and the active layer, and a current confinement layer for injecting therethrough current to the active layer, each of the p-type and n-type DBRs including a plurality of layer pairs each including an Alx1Ga1-x1As high-reflectivity layer (0≦x1<1) and an Alx2Ga1-x2As low-reflectivity layer (0<x2≦1, and x1<x2) and an Alx3Ga1-x3As slope content layer (x1<x3<x2) interposed between each of the high-reflectivity layers and each of the low-reflectivity layers, each of the slope content layer having a slope Al-content profile for Al content x3, wherein the Al content x3 in the Al content profiles of the slope content layers of the n-type DBR disposed within a distance from the active layer which is equivalent to an effective cavity length of the VCSEL device is such that 0<x3 ≦0.3 and 0.55≦x3<1 in the slope content profile.
- According to the VCSEL device of the first aspect of the present invention, the density of the point defects and dislocations which constitute crystal defects that cause the reduction of the laser output power in the VCSEL device can be reduced, thereby suppressing the reduction of the laser output power during the continuous laser emission.
- The present invention also provides a vertical cavity surface emitting semiconductor laser (VCSEL) device comprising a semiconductor substrate, and a layer structure formed thereon, the layer structure including an active layer, p-type and n-type cladding layers sandwiching therebetween the active layer, p-type and n-type semiconductor multilayer mirrors (DBRs) sandwiching therebetween the p-type and n-type cladding layers and the active layer, and a current confinement layer for injecting therethrough current to the active layer, each of the p-type and n-type DBRs including a plurality of layer pairs each including an Alx1Ga1-x1As high-reflectivity layer (0≦x1<1) and an Alx2Ga1-x2As low-reflectivity layer (0<x2≦1, and x1<x2) and an Alx3Ga1-x3As slope content layer (x1<x3<x2) interposed between each of the high-reflectivity layers and each of the low-reflectivity layers, each of the slope content layers having a slope Al-content profile for Al content x3, wherein the slope content layers of the n-type DBR disposed within a distance from the active layer which is equivalent to an effective cavity length of the VCSEL device has an impurity concentration of 3×1017 cm−3 or above.
- According to the VCSEL device of the second aspect of the present invention, the electric resistance of the VCSEL device falls within a suitable range, which suppresses the dislocations occurring during the laser emission, thereby stabilizing the laser output power during the continuous laser emission.
- The above and other objects, features and advantages of the present invention will be more apparent from the following description, referring to the accompanying drawings.
-
FIG. 1 is a sectional view of a VCSEL device according to an embodiment of the present invention. -
FIG. 2 is an enlarged partial sectional view of the upper and lower DBRs shown inFIG. 1 . -
FIGS. 3A and 3B are Al content profiles in slope content layers disposed far from the active layer, andFIGS. 3C and 3D are Al content profiles in the slope content layers disposed in the vicinity of the active layer. -
FIG. 4 is an impurity concentration profile of the slope content layers in the n-type DBR of the VCSEL device of the embodiment. -
FIG. 5 is a graph showing optical output-injection current characteristics for the sample VCSEL devices of the embodiment and the conventional VCSEL. -
FIG. 6 is a graph showing injection current-applied voltage characteristics for the sample VCSEL devices of the embodiment and the conventional VCSEL. -
FIG. 7 is a graph showing an optical output power characteristic of the conventional VCSEL with respect to the operating time. -
FIG. 8 is a graph showing an optical output power characteristic of the first sample VCSEL of the embodiment with respect to the operating time. -
FIG. 9 is a graph showing an optical output power characteristic of the second sample VCSEL of the embodiment with respect to the operating time. -
FIG. 10 is a graph showing an optical output power characteristic of the third sample VCSEL of the embodiment with respect to the operating time. -
FIG. 11 is a sectional view of a conventional VCSEL. -
FIG. 12 is an enlarged partial sectional view of the upper and lower DBRs shown inFIG. 11 . - Before describing preferred embodiments of the present invention, the principle of the present invention will be described for a better understanding of the present invention.
- In general, degradation of a typical facet emission semiconductor laser device occurs due to the dislocation of a semiconductor layer caused by meltdown thereof at the rear facet of the laser device, which is generally called catastrophic optical damage (COD), or occurs due to the defect called dark line defect (DLD). On the other hand, since generation of a dislocation loop has been observed in the cross section of a degraded VCSEL device by using a transmission electron microscope, the degradation of the VCSEL device is considered to occur due to the point defects or combination thereof, the latter being generally called dislocation, in the crystal structure of the layer structure of the laser device.
- For improved reliability of a specific type of the VCSEL having an oxidized current confinement layer, the degradation in the VCSEL device may be suppressed by using an Al0.98Ga0.02As layer instead of the AlAs layer which is generally employed as the oxidized current confinement layer. More specifically, it is known that the AlAs layer causes after oxidation thereof a 30 to 40% reduction in the volume thereof to thereby generate a high internal stress. Thus, the use of the Al0.98Gao0.02As layer instead of the AlAs layer may be expected to reduce the dislocations due to a lower internal stress. However, the use of the Al0.98Ga0.02As layer itself cannot in fact reduce the density of the point defects or the dislocations, although it significantly reduces the rate of such degradation.
- Thus, the present inventors attempted to experimentally find the layer structure which inherently reduced the density of the point defects and the dislocations. The principle of the present invention which allows reduction of the point defects and the dislocations by employing the configurations as recited above is such that the specific slope content layer having the specific slope Al content has a considerably reduced density of the crystal defects which cause the point defects or the dislocations, and such that the specific dopant concentration of the specific slope content layer reduces the device resistance and allows the laser device to lase at a higher output power.
- The present invention achieve remarkable advantages in a specific VCSEL device having a longer emission wavelength range such has 1000 nm or longer. This is because the VCSEL device having a longer emission wavelength has a higher absorption loss due to free electrons, and has a larger thickness in each layer of the DBRs corresponding to the longer emission wavelength. In general, for a VCSEL device having a longer emission wavelength, an optimum GaAs layer can be used for each high-reflectivity layer of the DBRs in the VCSEL device, and it is desired that the optimum GaAs high-reflectivity layer and the adjacent low-reflectivity layer be coupled via a slope content layer disposed therebetween to achieve a continuous Al content profile, for the purpose of obtaining a smooth reflectivity profile between the GaAs high-reflectivity layer and the low-reflectivity layer.
- To the contrary, however, based on the above findings, the present invention uses the specific slope content layer having a specific slope content profile for the Al content x3 which resides other than the range between 0.3 and 0.55, as will be detailed below.
- Now, the present invention is more specifically described with reference to accompanying drawings, wherein similar constituent elements are designated by similar or related reference numerals.
- Referring to
FIG. 1 , a VCSEL device according to a first embodiment of the present invention is similar to the conventional VCSEL device described with reference toFIGS. 11 and 12 except that the n-type DBR in the present embodiment includes slope content layers having a specific Al-content profile and a specific impurity concentration, and that a heavily doped p-GaAs layer 18 is provided as the topmost layer of theupper DBR 17 in the present embodiment in stead of the p-GaAs cap layer 118 inFIG. 11 . - More specifically, the VCSEL device of the present embodiment includes an n-type GaAs (n-GaAs)
substrate 11, and a layer structure formed thereon by an epitaxial growth process. The layer structure includes consecutively, as viewed from the n-type GaAs substrate 11, an n-typelower DBR 12, an n-typelower cladding layer 13, anactive layer 14, a p-typelower cladding layer 15, acurrent confinement layer 16 including anon-oxidized area 16A and an oxidized-Al area 16B, a p-typeupper DBR 17, and the heavily dopedGaAs layer 18. The VCSEL device further includes a p-side electrode 19 formed on the layer structure and an n-side electrode 20 formed on the bottom surface of the n-GaAs substrate 11. - The
active layer 14 and the n-type and p-type cladding layers - Referring to
FIG. 2 , each of the lower andupper DBRs reflectivity layer 12A and an Al2Ga1-x2As low-reflectivity layer 112B, and an Alx3Ga1-x3Asslope content layer 112C sandwiched between each of the high-reflectivity layers 12A and each of the low-reflectivity layers 112B adjacent to the each of the high-reflectivity layer 112A. - Each of the Alx3Ga1-x3As slope content layers of the n-
type DBR 17 disposed in the vicinity of the active layer, i.e., within a distance from the active layer roughly equal to the effective cavity length of the laser device, has an Al content x3, wherein 0<x3≦0.3 or 0.55≦x3<1. In addition, the each of the Alx3Ga1-x3As slope content layers disposed in the vicinity of the active layer has an impurity concentration of 3 ×1017 cm−3 or above. - The VCSEL device of the present embodiment is fabricated by the process as described below. The process begins with the n-
GaAs substrate 11 on which 35.5 pairs of n-type semiconductor layers constituting the n-type DBR 12, n-GaAslower cladding layer 13, GaInNAs/Ga(N)As MQWactive layer structure 14 including three GaInNAs(Sb) QW layers each having a thickness of 7 nm, and p-GaAsupper cladding layer 15 are consecutively grown using a metal-organic chemical vapor deposition (MOCVD) technique. On top of the p-GaAsupper cladding layer 15, 26 pairs of p-type semiconductor layers constituting the p-type DBR 17 are grown, wherein a heavily-doped p-GaAs layer 18 is formed as the topmost GaAs layer of the p-type DBR 17. In addition, one of the low-reflectivity layer of the p-type DBR 17 in the vicinity of theactive layer 14 is replaced by an AlAs layer, the Al content of which is to be selectively oxidized to form acurrent confinement layer 16. Thecurrent confinement layer 16 has a peripheral oxidized-Al area 16B and a centralnon-oxidized area 16A, which acts as a current injection area. - In the specific example of the process, the n-type (or p-type) DBR 12 (17) includes a plurality of GaAs high-
reflectivity layer 12A (17A), a plurality of Al0.9Ga0.1As low-reflectivity layer 12B, and a plurality of Alx3Gax13As slope content layers each sandwiched between a corresponding GaAs high-reflectivity layer 12A and a corresponding low-reflectivity layer 12B. - Referring to
FIGS. 3A and 3B , there are shown Al content profiles for x3 of the Alx3Ga1-x3As slope content layers corresponding to 30.5 layer pairs of the n-type DBR 12, which are disposed far from theactive layer 14. All the Alx3Ga1-x3As slope content layers of the p-type DBR 17 have similar Al content profiles shown inFIGS. 3A and 3B , which are similar to those in the conventional VCSEL device. One of the thirty Alx3Ga3As slope content layers 12C overlying the adjacent GaAs high-reflectivity layer 12A and underlying the adjacent Al0.9Ga0.1As low-reflectivity layer 12B has a stepwise increasing Al content profile from 0.2 to 0.85 as viewed from the bottom toward the top of the Alx3Ga1-x3Asslope content layer 12C, as shown inFIG. 3A . The stepwise increase profile includes 0.4 for x3, which falls between 0.3 and 0.55. - One of the thirty Alx3Ga1-x3As slope content layers 12C overlying the adjacent Al0.9Ga0.1As low-
reflectivity layer 12B and underlying the adjacent GaAs high-reflectivity layer 12A has a stepwise decreasing Al content profile from 0.85 to 0.2 as viewed from the bottom toward the top of the Alx3Ga1-x3Asslope content layer 12C, as shown inFIG. 3B . The stepwise decrease profile includes 0.4 for x3, which falls between 0.3 and 0.55. - Referring to
FIGS. 3C and 3D , there are shown Al content profiles for x3 of the remaining Alx3Ga1-x3As slope content layers of the n-type DBR 12 disposed in the vicinity of theactive layer 14. One of the five Alx3Ga1 -x3As slope content layers 12C overlying the adjacent GaAs high-reflectivity layer 12A and underlying the adjacent Al0.9Ga0.1As low-reflectivity layer has a stepwise increasing Al content profile from 0.2 to 0.85 as viewed from the bottom toward the top of the Alx3Ga1-xAs slope content layer, as shown inFIG. 3C . The stepwise increase profile does not include a value, which falls between 0.3 and 0.55. One of the five Alx3Ga1-x3As slope content layers 12C overlying the adjacent Al0.9Ga0.1As low-reflectivity layer 12B and underlying the adjacent GaAs high-reflectivity layer 12A has a stepwise decreasing Al content profile from 0.85 to 0.2 as viewed from the bottom toward the top of the Alx3Ga1-x3As slope content layer. The stepwise decrease profile does not include a value, which falls between 0.3 and 0.55, as shown inFIG. 3D . - In the step for fabrication of the n-
type DBR 12, thirty pairs of slope content layers 12C are formed similarly to those in the conventional VCSEL device, and each of the remaining five pairs ofslope content layers 12C is formed to have the slope content profile shown inFIG. 3C or 3D, which does not include a value falling between 0.3 and 0.55 for the Al content x3. - In addition, the n-
type DBR 12 has an impurity concentration profile shown inFIG. 4 . The layers including 30.5 high-reflectivity/low-reflectivity layer pairs disposed far from theactive layer 14 and corresponding slope content layers 12C have an impurity concentration of 4×1018 cm−3, whereas the layers including 5 high-reflectivity/low-reflectivity layer pairs disposed in the vicinity of the active layer and corresponding slope content layers 12C have an impurity concentration of 3×1017 cm−3. The term “vicinity of the active layer” as used herein means that these layers reside within a distance from theactive layer 14 which corresponds to the effective cavity length of the VCSEL device. - After depositing the layer structure including the upper and lower DBRs 12 and 17 and the top p-
GaAs cap layer 18, a SiNx film is deposited on the layer structure, followed by forming thereon a photoresist film. The photoresist film is subsequently patterned by an ordinary photolithographic technique to have a circular opening having a diameter of 45 μm. While using the circular pattern of the photoresist film as an etching mask, the SiNx film is patterned by a reactive ion etching (RIE) technique using a CF4 gas to form a circular SiNx mask. While using the photoresist pattern and the SiNx mask as an etching mask, the layer structure is subjected to RIE until thelower DBR 12 is etched, to thereby form a columnar mesa post. - The entire wafer is subjected to a thermal treatment in a steam ambient at a temperature of 400 degrees C. for twenty minutes, thereby selectively oxidizing the AlAs layer on the
upper DBR 17 to form acurrent confinement layer 16 including an annular oxidized-Al area 16B and a centralnon-oxidized area 16A. In the thermal treatment, the inner diameter of the annular oxidized-Al area 16B is controlled for adjusting the threshold current and the temperature characteristic of the VCSEL device. - Subsequently, the photoresist pattern and the SiNx mask are removed, followed by depositing another SiNx film over the entire area by using a plasma-enhanced CVD technique and patterning thereof, to form an annular opening. The annular opening has an inner diameter equivalent to the diameter of the non-oxidized area or
current injection area 16A, and an outer diameter equal to this inner diameter plus several micrometers. A AuZn p-side electrode 19 is then formed in the annular opening of the SiNx film, whereas an n-side electrode 20 having a AuGeNi/Au layer structure is formed on the bottom surface of the n-GaAs substrate 11. Finally, a pair of Ti/Pt/Au pads for mounting thereon bonding wires are formed in contact with both the p-side and n-side electrodes - For assuring the advantages of the structure in the VCSEL device of the present invention, sample VCSEL devices of the above embodiment and a comparative example of the conventional VCSEL device of
FIG. 11 were manufactured and subjected to characteristic tests. Each sample was similar to the comparative example except for the slope content profile and/or the impurity concentration of the slope content layers. - The samples included a first sample wherein the Al content x3 in the five pairs of Alx3Ga1-x3As slope content layer falls outside the range between 0.3 and 0.55, a second sample wherein the impurity concentration of the five pairs of Alx3Ga1-x3As
slope content layer 12C is 3×1017 cm−3 with the impurity concentration of the other 30.5 pairs of the Alx3Ga1-x3As slope content layers 12C being 4×1018 cm−3, and a third sample wherein the Al content in the five pairs of Ax3Ga1-x3As slope content layer falls outside the range between 0.3 and 0.55, and the impurity concentration of the five pairs of Alx3Ga1-x3As slope content layer is 3×1018 cm−3, with the impurity concentration of the other 30.5 pairs of the Alx3Ga1-x3As slope content layers being 4×1018cm−3. - The results of the optical output-injection current characteristic tests are shown in
FIG. 5 , wherein the results of the first through third samples correspond to curves (A), (B) and (C), respectively, and the result of the comparative example corresponds to curve (D). As understood fromFIG. 5 , the samples of the present embodiment achieved higher output powers compared to the comparative example. - The results of the injection current-applied voltage characteristic tests are shown in
FIG. 6 , wherein designations similar to the designations inFIG. 5 are used. As understood fromFIG. 6 , the sample VCSEL devices of the present embodiment operated at lower voltages compared to the comparative example. - FIGS. 7 to 10 show output power characteristics of the comparative sample and the first through third samples, respectively, each illustrating the output power of the VCSEL device during a continuous operation thereof with the initial output power being set at unit. The tests were conducted at a temperature of 100 degrees C. and at an injection current of 20 mA. As understood from these drawings, the samples of the present embodiment were superior to the comparative example with respect to the output power characteristic, and the third sample was superior to the first sample, which was superior to the second sample. The third sample was capable of operating for 100,000 straight hours or longer at the room temperature.
- A second embodiment of the present invention is such that the present invention is applied to a VCSEL device having a relatively shorter wavelength. The VCSEL device of the second embodiment has three 7-nm-thick GaAs QW layers in the GaAs/Al0.2Ga0.8As
QW structure 14 instead of the GaInNAs(Sb) QW layers in the GaInNAs(Sb)/Ga(N)As QW structure in the first embodiment, an n-Al0.3Ga0.7Aslower cladding layer 13 and a p-Al0.3Ga0.7As upper cladding layer instead of the n-GaAs lower cladding layer and the p-GaAs upper cladding layer, respectively, in the first embodiment. - The VCSEL device of the second embodiment also has Al0.2Ga0.8As high-reflectivity layers in each of the n-type and p-
type DBRs GaAs cap layer 18 instead of the heavily-doped p-GaAs layer 18 in the first embodiment. In this configuration, the VCSEL device of the second embodiment has 25 layer pairs in the p-type DBR 17 which is one pair smaller compared to the first embodiment. The other configurations are similar to those in the first embodiment. - The VCSEL device of the second embodiment having a relatively shorter wavelength also achieves advantages similar to those in the first embodiment due to the above configurations. The samples of the second embodiment were manufactured, and subjected to characteristic tests, exhibiting similar excellent characteristics.
- In the above embodiments, the n-type DBR is formed as the
lower DBR 12; however, the p-type DBR may be formed as thelower DBR 12 so long as a p-type substrate is used. In either case, the laser beam is extracted through one of theDBRs active layer 14 in the present invention may have a slope content profile similar to that of the slope content layer in the vicinity of the active layer. - Since the above embodiments are described only for examples, the present invention is not limited to the above embodiments and various modifications or alterations can be easily made therefrom by those skilled in the art without departing from the scope of the present invention.
Claims (3)
1. A vertical cavity surface emitting semiconductor laser (VCSEL) device comprising a semiconductor substrate, and a layer structure formed thereon, said layer structure including an active layer, p-type and n-type cladding layers sandwiching therebetween said active layer, p-type and n-type semiconductor multilayer mirrors (DBRs) sandwiching therebetween said p-type and n-type cladding layers and said active layer, and a current confinement layer for injecting therethrough current to said active layer, each of said p-type and n-type DBRs including a plurality of layer pairs each including an Alx1Ga1-x1As high-reflectivity layer (0≦x1<1) and an A1 x2Ga1-x2As low-reflectivity layer (0<x2≦1, and x1<x2) and an A1 x3Ga1-x3As slope content layer (x1<x3<x2) interposed between each of said high-reflectivity layers and each of said low-reflectivity layers adjacent to said each of said high-reflectivity layers, each of said slope content layers having a slope Al-content profile for Al content x3, wherein said slope content layers of said n-type DBR disposed within a distance from said active layer which is equivalent to an effective cavity length of said VCSEL device has an impurity concentration of 3×1017 cm−3 or above.
2. The VCSEL device of claim 4, wherein said slope content layers are doped with at least one element selected from the group consisting of Si, Se, Sn, Te and S.
3. The VCSEL device of claim 4, wherein each of said slope content layers of said n-type and p-type DBRs other than said slope content layers of said n-type DBR disposed within said distance from said active layer has an impurity concentration of 5×1018 cm−3 or below.