US20050263403A1 - Method for electrodeposition of bronzes - Google Patents

Method for electrodeposition of bronzes Download PDF

Info

Publication number
US20050263403A1
US20050263403A1 US11/105,947 US10594705A US2005263403A1 US 20050263403 A1 US20050263403 A1 US 20050263403A1 US 10594705 A US10594705 A US 10594705A US 2005263403 A1 US2005263403 A1 US 2005263403A1
Authority
US
United States
Prior art keywords
electrolyte
thioether
concentration
wetting agent
thiobis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/105,947
Other versions
US20060260948A2 (en
Inventor
Katrin Zschintzsch
Joachim Heyer
Marlies Kleinfeld
Stefan Schafer
Ortrud Steinius
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MacDermid Enthone Inc
Original Assignee
Enthone Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Enthone Inc filed Critical Enthone Inc
Priority to US11/105,947 priority Critical patent/US20060260948A2/en
Publication of US20050263403A1 publication Critical patent/US20050263403A1/en
Priority to KR1020077026291A priority patent/KR101361431B1/en
Priority to EP06750231.0A priority patent/EP1874982B1/en
Priority to CN2006800208357A priority patent/CN101194049B/en
Priority to TW095113445A priority patent/TWI391534B/en
Priority to JP2008506756A priority patent/JP2008537017A/en
Priority to PCT/US2006/014141 priority patent/WO2006113473A1/en
Publication of US20060260948A2 publication Critical patent/US20060260948A2/en
Abandoned legal-status Critical Current

Abstract

A method for electrodeposition of bronzes, with which the substrate to be coated is plated in an acid electrolyte that contains at least tin and copper ions, an alkylsulfonic acid and a wetting agent, and the preparation of such an electrolyte.

Description

    CROSS REFERENCE TO RELATED APPLICATIONS
  • This application is a continuation-in-part from U.S. app. Ser. No. ______ entitled METHOD FOR ELECTRODEPOSITION OF BRONZES filed Apr. 11, 2005, the entire disclosure of which is explicitly incorporated by reference.
  • FIELD OF THE INVENTION
  • This invention concerns a method for electrodeposition of bronzes, with which the substrate to be coated is plated in an acid electrolyte that contains at least tin and copper ions, an alkylsulfonic acid and a wetting agent, and the preparation of such an electrolyte.
  • BACKGROUND OF THE INVENTION
  • Methods for deposition of tin and tin alloys on the basis of various types of electrolytes are known from the prior art and are already widely used in practice. Methods for deposition of tin and/or tin alloys from cyanide electrolytes are very common. Such electrolytes, however, are highly toxic, which makes their use problematic from the environmental standpoint, so that for some years there has been a push to develop cyanide-free electrolytes, for example electrolytes based on pyrophosphates or oxalates, which operate in a pH region of 5-9. However, such methods have both economic and technical disadvantages, of which the relatively slow deposition rates may be mentioned here.
  • For these reasons development is currently going mostly in the direction of making available methods for deposition of tin and/or tin alloys from acid electrolytes, since, for one thing, divalent tin can be very easily reduced to metallic tin in acid electrolytes, which leads to better deposition rates while having qualitatively equivalent coatings, and for another the disadvantageous effect of alkaline electrolytes on substrates, for example ceramic structural elements, is prevented by this.
  • Thus, acid electrolytes and methods for deposition of qualitatively high grade tin or tin alloys with a higher deposition rate are known from EP 1 111 097 A2 and U.S. Pat. No. 6,176,996 B1. These are electrolytes that contain at least two divalent metal salts of an organic sulfonic acid and from which are deposited solderable and corrosion resistant coatings that can be used, for example, as substitutes for lead-containing solderable coatings in electronics for manufacture of circuit boards, etc.
  • However, such methods have their limits in the deposition of tin-copper alloys with high copper contents, such as the so-called “true” bronzes, which have a copper content of at least 10%. For example, due to the high difference of potential between tin and copper higher rates of oxidation of the divalent tin can occur, due to which it very easily becomes oxidized to tetravalent tin in acid electrolytes. However, in this form tin can no longer be electrolytically deposited in an acid and thus is withdrawn from the process, which leads to uneven deposition of the two metals and to a decrease of the deposition rate. In addition, oxidation to tetravalent tin leads to increased sludge formation, which can prevent stable operation and long lifetime of the acid electrolyte. Moreover, because of such contaminated of a firmly bonding and pore-free coating is no longer guaranteed.
  • Because of such technical process disadvantages, there is currently no large area of use for electrolytically deposited bronze coatings. occasionally bronze coatings are used in the jewelry industry as a substitute for expensive silver or allergy-triggering nickel. In the same way methods for electrodeposition of bronzes are also gaining importance in some technical fields, for example in electronics for coating electronic components or in mechanical engineering and/or in process technology for coating bearing overlays and friction layers. However, in this case chiefly white bronzes or the so-called “false bronzes,” whose copper content can be kept quite low due to process conditions, are deposited as nickel substitutes.
  • SUMMARY OF THE INVENTION
  • Therefore, the invention is based on the task of providing a method for deposition of bronzes that, in contrast to the methods known from the prior art, enables uniform deposition of at least tin and copper side by side from an acid electrolyte at considerably higher deposition rates. Moreover, with this method firmly bonding and pore-free bronze coatings with high copper contents as well as various decorative and mechanical properties are said to be deposited.
  • In addition, an acid electrolyte that can have a high content of divalent copper ions, is stable with respect to oxidation-caused sludge formation, and is both economical and environmentally friendly when used over a long period of time, is to be made available.
  • DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
  • The task is solved in accordance with the invention by a method of the kind mentioned at the start, which is characterized by the fact that an aromatic, nonionic wetting agent is added to the electrolyte.
  • With this invention a method for electrodeposition of bronzes is made available, where an anode of a copper-tin alloy and a cathode are connected to the substrate that is to be coated by means of an electrolyte, and coating takes place by passing a direct current through them. In addition, with the invention an electrolyte that is usable in particular for this method and the coatings that are obtainable by this method are made available.
  • Through the method in accordance with the invention the disadvantages known in the prior art are remedied with the offering of a new electrolyte composition and in this way considerably better deposition results are achieved. Moreover, the conduct of the method is made to be simpler and more economical. This, too, is chiefly based on the advantageous composition of the electrolyte. For example, the method is carried out at room temperature, or between 17 and 25° C., and the substrate to be coated is plated in a highly acid environment at a pH <1. The electrolyte is particularly stable in this temperature range. In addition, there are no longer any costs for heating the electrolyte and the plated substrates also do not have to be cooled very much, with large expenditures of time and money. Moreover, deposition rates of 0.25 im/min at a current density of 1 A/dm2 are achieved due to, among other things, the pH value and the advantageous addition of at least one aromatic non-ionic wetting agent. By increasing the metal content this rate can be raised up to 7 A/dm2 in rack operation and even up to 120 A/dm2 for continuous plants. Thus, usable current densities in a range from 0.1-120 A/dm2 are reached in each case according to plant type.
  • Surprisingly, the wetting of the surfaces to be plated, above all those of more complex substrates, is considerably improved in particular through the addition of at least one nonionic wetting agent to the electrolyte. This advantageously has the result that not only are the considerably higher deposition rates achieved through the use of the method in accordance with the invention, but moreover the coatings produced by the method are uniform and qualitatively high grade, have very good adhesion and are generally pore-free.
  • Another advantage of the nonionic wetting agent that is used is that because of the advantageous wetting properties the electrolyte and/or the substrate in the electrolyte need to be agitated only a little or even not at all, in order to achieve the desired deposition results, so that additional devices for agitation of the electrolyte can be omitted. In addition, because of the advantageous use of the aromatic nonionic wetting agent, electrolyte residues drain from the plated substrate better when it is removed from the electrolyte, which leads to reduced entrainment losses and thus to lower process costs.
  • The addition of 2-40 g/L of one or more aromatic nonionic wetting agents is especially advantageous, with â-napththol ethoxylate and/or nonylphenol ethoxylate are especially preferably used.
  • The proposed method is therefore advantageously economical and environmentally friendly compared to the cyanide processes.
  • The additional or alternative use of one or more anionic and/or aliphatic nonionic wetting agent that is known from the prior art is also optionally possible, provided these wetting agents support or even enhance the advantageous effects of the aromatic nonionic wetting agent. In this regard polyethylene glycols and/or anionic surfactants are preferably added to the electrolyte as anionic and/or aliphatic nonionic wetting agents. Additional exemplary aliphatic nonionic wetting agents include aliphatic fatty alcohol ethoxylates.
  • It has also been discovered that substituted dithioglycols act advantageously as wetting agents and brighteners. Therefore, certain embodiments of the invention include substituted dithioglycols, such as, for example, those selected from the group consisting of:
    • (1) Thiobis(diethyleneglycol)represented by H—(OCH2CH2)2—S—(CH2CH2O)2—H,
    • (2) Thiobis(hexaethylene glycol),
    • (3) Thiobis(pentadecaglycelol) represented by H—(OCH2CH (OH)CH2)15—S—(CH2CH (OH)CH2O)15—H,
    • (4) Thiobis(icosaethyleneglycol) represented by H—(OCH2CH2)20—S—(CH2CH2O)20—H, (5) Thiobis(pentacontaethyleneglycol),
    • (6) 4,10-dioxa-7-thiatridecane-2,12-diol represented by HO—CH (CH3)CH2 —OCH2CH2 —SCH2CH2—OCH2CH (CH3)—OH,
    • (7) Thiodiglycerin represented by HOCH2CH (OH) CH2—S—CH2CH (OH) CH2OH,
    • (8) Thiobis(triglycerin) represented by H—(OCH2CH (OH) CH2)3—S—(CH2CH (OH) CH2O)—H,
    • (9) 2,2′-thiodibutanolbis(octaethyleneglycolpentaglycerol) ether represented by H—(OCH2CH (OH) CH2)—(OCH2CH2) 8—OC4H8—SC4H8—O—(CH2CH2O)8—(CH2CH (OH)CH2O)—H,
    • (10) Thiobis(octaethyleneglycol)bis(2-chloroethyl)ether represented by Cl—CH2CH2CH2—(OCH2CH2) 8—S —(CH2CH2O)8—CH2CH2CH2 —Cl,
    • (11) Thiobis(decaethyleneglycol)bis(carboxymethyl)ether,
    • (12) Thiobis(dodecaethyleneglycol)bis(2-nitroethyl)ether,
    • (13) Thiodiglycolbis(carboxymethyl)ether represented by HOOCCH2OCH2CH2—S—CH2CH2OCH2COOH,
    • (14) Dithiodiglycolbis(carboxymethyl)ether represented by HOOCCH2OCH2CH2—S—S—CH2CH2OCH2COOH,
    • (15) Thiobis(dodecaethyleneglycol) represented by H—(OCH2CH2)12—S—(CH2CH2O)12—H,
    • (16) Dithiobis(hentetracontaethyleneglycol) represented by H—(OCH2CH2)41—S—S—(CH2CH2O)41—H,
    • (17) Dithiobis(icosaethyleneglycolpentapropyleneglycol) represented by H—(OC3H6)5—(OC2H4)20—S—S—(OC2H4)20—(OC3H6)5—H,
    • (18) Dithiobis(triglycerol) represented by H—(OCH2CH(OH)CH2)3—S—S—(CH2CH (OH) CH2O)3—H,
    • (19) Dithiobis(decaglycelol),
    • (20) 3,6-Dithiaoctane-1,8-diol represented by HOCH2CH2S —CH2CH2 —SCH2CH2OH,
    • (21) 1,3-Propanedithiolbis(decaethyleneglycol)thioether represented by H—(OC2H4)10—S—C3H6—S—(OC2H4)10—H,
    • (22) 1,4-Buthanedithiolbis(pentadecaglycerol)thioether represented by H—(OCH2CH(OH)CH2)15—S—C4H8—S—(CH2CH (OH) CH2O)15—H,
    • (23) 1,3-Dithioglycerolbis(pentaethyleneglycol)thioether represented by H—(OCH2CH2)5—SCH2CH (OH) CH2S—(CH2CH2O)5—H,
    • (24) 1,2-Ethanedithiolbis(penta(1-ethyl)ethyleneglycol)thioether represented by H—(OCH(C2H5)CH2)5—SC2H4S—(CH2CH(C2H5)O)5—H,
    • (25) 1,3-Dithioglycerolbis(di(1-ethyl)ethyleneglycol)thioether represented by H—(OCH (CH3)CH2)2—SCH2CH(OH) CH2S—(CH2CH (CH3)O)2—H,
    • (26) 2-Mercaptoethylsulfide bis(hexatriacontaethylene-glycol) represented by H—(OC2H4)18—SC2H4—SC2H4—S—(C2H4O)18—H,
    • (27) 2-Mercaptoethylsulfidebis(icosaethyleneglycol)dimethylether represented by CH3—(OC2H4)10—SC2H4—SC2H4—S—(C2H4O)10—CH3,
    • (28) 2-Mercaptoethyletherbis(diethyleneglycol) represented by H—(OC2H4)2—S —CH2CH2OCH2CH2 —S —(C2H4O)2—H,
    • (29) Thiodiglyceroltetra(decaethyleneglycol)ether represented by the above formula (6),
    • (30) Diethyleneglycolmonomethylthioether represented by CH3—S—(CH2CH2O)2—H,
    • (31) Decaglycerolmono(6-methylthiohexyl)thioether represented by CH3—S—C6H12—S—(CH2CH (OH) CH2O)10—H,
    • (32) 2-Mercaptoethylsulfide-ω-{(2-bromoethyl)icosaethyleneglycol}thioethe r-ω′-{(2-bromoethyl)hectaethyleneglycol}thioether represented by BrCH2CH2—(OCH2CH2)20—(S—CH2CH2) 3—(OCH2CH2)100—OCH2CH2Br,
    • (33) 1,4-Butanediol-ω-{(2-benzyloxy-1-methyl)ethyl}thioether-ω′-(de capropyleneglycoloctacontaethyleneglycol)thioether represented by PhCH2OCH2CH (CH3)—S—4H8—S—(CH2CH2O)80—(CH2CH (CH3)O)10—H,
    • (34) Dithiobis(icosaethyleneglycol)bis(2-methylthioethyl)ether represented by CH3—S—CH2CH2—(OCH2CH2)20—S—S—(CH2CH2O)20—CH2CH2—S—CH3,
    • (35) 1,2-Ethanediol-ω-(4-methoxybenzyl)thioether-ω′-(pentacontaethy leneglycol)thioether represented by CH3O—Ph—CH2S—CH2CH2—(CH2CH2O)50—H,
    • (36) Triacontaethyleneglycolmono(4-cyanobenzyl)thioether represented by NC—Ph—CH2—S—(CH2CH2O)30—H,
    • (37) Thiobis(pentadecaethyleneglycol)bisallylether represented by CH2═CHCH2—(OCH2CH2)15—S—(CH2CH2O)15—CH2CH═CH2,
    • (38) Tricosaethyleneglycolmono(4-formylphenetyl)thioether represented by OHC—Ph—CH2CH2—S—(CH2CH2O)23—H,
    • (39) Pentadecaethyleneglycolmono{(acetylmethyl)thioethyl}thioether represented by CH3COCH2—S—CH2CH2—S—(CH2CH2O)15—H,
    • (40) 1,2-Ethanediol-ω-(glycidyl)thioether-ω′-icosaethyleneglycolthioether represented by
      Figure US20050263403A1-20051201-C00001
    • (41) Octadecaethyleneglycolbis(2-methylthioethyl)ether represented by CH3—S—CH2CH2CO—(CH2CH2O)18—CH2CH2S—CH3,
    • (42) Hexadecaethyleneglycolmono(2-methylthioethyl)thioether represented by CH3—S—CH2CH2—S—(CH2CH2O)16—H,
    • (43) Icosaethyleneglycolmonomethylthioether represented by CH3—S—(CH2CH2O)20—H,
    • (44) Undecaethyleneglycoldi(n-propyl)thioether represented by C3H7—S—(CH2CH2O)10—CH2CH2S—C3H7,
    • (45) Dodecaethyleneglycolbis(2-hydroxyethyl)thioether represented by HOCH2CH2—S—(CH2CH2O)11—CH2CH2—S—CH2CH2OH,
    • (46) Undecaethyleneglycoldimethylthioether,
    • (47) Pentatriacontaethyleneglycolmono(2-n-butyldithioethyl)dithioether represented by C4H9—S—S—CH2CH2—S—S—(CH2CH2O)35—H,
    • (48) 4,8,12-trithiapentadecane-1,2,6,10,14,15-hexaol represented by HOCH2CH (OH) CH2—S—CH2CH (OH) CH2—S—CH2CH (OH) CH2—S—CH2CH (OH) CH2OH,
    • (49) Icosaglycerolmono(2-ethylthioethyl)thioether represented by C2H5—S—CH2CH2—S—(CH2CH(OH)CH2O)20—H, (50) Triacontaethyleneglycolmono(2-methylthioethyl)thioether represented by CH3—S—CH2CH2—S—(C2H40)30—H,
    • (51) Dithiobis(icosaethyleneglycol)dibenzylether represented by Ph—CH2—(OC2H4)20—S—S—(C2H4O)20—CH2—Ph,
    • (52) Tridecaethyleneglycolmonomethylthioether represented by CH3—S—(CH2CH2O)10—H,
    • (53) Hexadecaethyleneglycol dimethylthioether represented by CH3—S—(CH2CH2O)15—CH2CH2—S—CH3,
    • (54) 1,2-Ethanedithiolbis(icosaethyleneglycol)thioether represented by H—(OCH2CH2)20—S—CH2CH2—S—(CH2CH2O)20—H,
    • (55) Dithiobis(pentadecaethyleneglycol) represented by H—(O CH2CH2)15—S—S—(CH2CH2O)15—H, and
    • (56) 3,3′-thiodipropanol represented by HO—CH2CH2CH2—S—CH2CH2CH2—OH. In the above-listed structural formulae, Ph represents a phenyl group.
  • As already mentioned above, the method in accordance with the invention is characterized in particular by the special composition of the electrolyte. It contains essentially tin and copper ions, an alkylsulfonic acid and an aromatic nonionic wetting agent. In addition, stabilizers and/or complexing agents, anionic and/or nonionic, aliphatic and/or substituted dithioglycol wetting agents, oxidation inhibitors, brighteners, and other metal salts can optionally be contained in the electrolyte.
  • The metals that are primarily added to the electrolyte for deposition of bronzes in accordance with the invention—tin and copper—can first and foremost be in the form of salts of alkylsulfonic acids, preferably as methanesulfonates, or as salts of mineral acids, preferably as sulfates. Tin methanesulfonate is especially preferably used as tin salt in the electrolyte preferably in an amount of 5-195 g/L of electrolyte, preferably 11-175 g/L of electrolyte. This corresponds to a use of 2-75 g/L, preferably 4-57 g/L divalent tin ions. Copper methanesulfonate is especially preferably used in the electrolyte as the copper salt, which is advantageously added to the electrolyte in an amount of 8-280 g/L of electrolyte, preferably 16-260 g/L of electrolyte. This corresponds to the use of 2-70 g/L, preferably 4-65 g/L divalent copper ions.
  • Since the deposition is clearly higher in an acid environment, an acid, preferably a mineral and/or an alkylsulfonic acid, is added to the electrolyte in amounts of 140-382 g/L of electrolyte, preferably 175-245 g/L of electrolyte. The use of methanesulfonic acid turned out to be especially advantageous, since for one thing this produces advantageous solubility of metal salts and for another, because of its acid strength, it produces or facilitates the adjustment of the pH needed for the process. In addition, methanesulfonic acid has the advantageous property of contributing considerably to the stability of the bath.
  • In accordance with an additional characteristic of the invention at least one additional metal and/or chloride is added to the electrolyte. Advantageously, the metals are in the form of their soluble salts. In particular, the addition of zinc and/or bismuth has a considerable effect on the properties of the deposited coatings. The metals zinc and/or bismuth added to the electrolyte can namely be in the form of salts of alkylsulfonic acids, preferably as methanesulfonates or as salts of mineral acids, preferably as sulfates. Zinc sulfate is especially preferably uses in the electrolytes as zinc salt, and is advantageously added in an amount of 0-25 g/L of electrolyte, preferably 15-20 g/L of electrolyte. Bismuth methane sulfate is especially preferably used in the electrolyte as bismuth salt and is advantageously added to the electrolyte in an amount of 0-5 g/L of electrolyte, preferably 0.05-0.2 g/L of electrolyte.
  • In addition, various additives, for example stabilizers and/or complexing agents, oxidation inhibitors and brighteners, that are usually used in acid electrolytes for deposition of tin alloys can be added to the electrolyte.
  • In particular, the use of suitable compounds for stabilizing the electrolyte is an important condition for rapid as well as qualitative high grade deposition of bronzes. Gluconates are advantageously added to the electrolyte and stabilizers and/or complexing agents. Here in the method in accordance with the invention the preferred use of sodium gluconate turned out to be especially advantageous. The concentration of the stabilizers and/or complexing agents is 0-50 g/L of electrolyte, preferably 20-30 g/L of electrolyte. Compounds from the class of the dihydroxybenzenes, for example mono- or polyhydroxyphenyl compounds like pyrocatechol or phenolsulfonic acid are preferably used as oxidation inhibitors. The concentration of oxidation inhibitors is 0-5 g/L of electrolyte. Advantageously, the electrolyte contains hydroquinone as oxidation inhibitor.
  • The conduct of the method in accordance with the invention enables the deposition of bronzes onto various substrates. For example, all of the usual methods for making electronic components can be used. In the same way especially hard and wear-resistant bronze coatings can be deposited on materials like bearings, etc., to the method in accordance with the invention. The method in accordance with the invention is advantageously also used in the fields of decorative coating of, for example, fixtures and jewelry, etc., where the deposition of multi-component alloys that contain tin, copper, zinc and bismuth is particularly advantageous in these areas.
  • A really special advantage is that the so-called “true” bronzes that have a copper content >60% can be deposited with the method in accordance with the invention, where the copper content can be up to 95 wt % in each according to the desired properties. In addition, the ratio of the amount of copper to the amount of tin in the electrolyte has a considerable effect of properties like hardness and color of the bronze coatings. For instance, at a tin/copper ratio of 40/60 silver-colored coatings, the so-called white bronzes, which are relatively soft, are deposited. At a tin/copper ratio of 20/80 yellow gold colored coatings result, the so-called yellow bronzes, and at a tin/copper ratio of 10/90 red gold colored coatings are formed, the so-called red bronzes.
  • Moreover, the deposition of high-tin white bronzes with a copper content=10% is also possible.
  • In each case according to the desired appearance of the bronze coatings additives such as brighteners are added to the electrolyte, in addition to it having a varying copper content. Advantageously, the electrolyte contains brighteners from the class of the aromatic carbonyl compounds and/or á,â-unsaturated carbonyl compounds. The concentration of brighteners is 0-5 g/L of electrolyte.
  • Some preferred embodiments are presented below for illustration of the invention in more detail, but the invention is not limited to these embodiments.
  • Electrolyte Composition:
  • The base electrolyte of the highly acid electrolyte in accordance with the invention contains essentially (per liter of electrolyte)
      • 2-75 g divalent tin,
      • 2-70 g divalent copper,
      • 2-40 g of an aromatic nonionic wetting agent, and
      • 140-382 g of a mineral and/or alkylsulfonic acid.
  • Optionally, other components can be added to the electrolyte (per liter of electrolyte):
      • 0-10 g of an anionic and/or aliphatic nonionic wetting agent,
      • 0-50 g of a stabilizer and/or complexing agent,
      • 0-5 g of an oxidation inhibitor,
      • 0-5 g of a brightener
      • 0-5 trivalent bismuth
      • 0-25 g divalent zinc.
  • In order to achieve a specific color of the deposited bronze coatings the electrolyte is prepared by varying the individual components, as given below as a matter of example. Additional information about the corresponding process conditions as well as other properties of the individual coatings can be seen in Table 1.
  • Example 1 (Red Bronze)
      • 4 g/L Sn2+
      • 18 g/L Cu2+
      • 286 g/L methanesulfonic acid
      • 3 g/L aromatic nonionic wetting agent
      • 0.4 g/l aliphatic nonionic wetting agent
      • 2 g/L oxidation inhibitor
      • 20 mg/L complexing agent
  • Example 2a (Yellow Bronze)
      • 4 g/L Sn2+
      • 18 g/L Cu2+
      • 240 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 2 g/L oxidation inhibitor
      • 25 mg/L stabilizer/complexing agent
  • Example 2b (Yellow Bronze)
      • 4 g/L Sn2+
      • 18 g/L Cu2+
      • 286 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 6 mg/Lbrightener
      • 2 g/L oxidation inhibitor
      • 50 mg/L stabilizer/complexing agent
  • Example 3 (White Bronze)
      • 5 g/L Sn2+
      • 10 g/L Cu2+
      • 240 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 6 mg/Lbrightener
      • 2 g/L oxidation inhibitor
      • 25 mg/L stabilizer/complexing agent
  • Example 4 (Matte White Bronze)
      • 18 g/L Sn2+
      • 2 g/L Cu2+
      • 258 g/L methanesulfonic acid
      • 9 g/L aromatic nonionic wetting agent
  • To improve the hardness and/or ductility of the deposited bronze coatings the contents of zinc and/or bismuth indicated below as examples are added to the electrolyte. Additional data on the corresponding process conditions and other properties of the individual coatings can be seen in Table 1.
  • Example 5 (High Ductility)
      • 4 g/L Sn2+
      • 18 g/L Cu2+
      • 238 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 3 mg/Lbrightener
      • 2 g/L oxidation inhibitor
      • 25 mg/L stabilizer/complexing agent
      • 20 g/L ZnSO4
  • Example 6 (Hardness)
      • 4 g/L Sn2+
      • 18 g/L Cu2+
      • 238 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 2 g/L oxidation inhibitor
      • 25 mg/L stabilizer/complexing agent
      • 0.1 g/L Bi3+
  • Example 7 (Yellow Bronze)
      • 14.5 g/L Sn2+
      • 65.5 g/L Cu2+
      • 382 g/L methanesulfonic acid
      • 32.2 g/L aromatic nonionic wetting agent
      • 4 g/L oxidation inhibitor
      • 25 mg/L stabilizer/complexing agent
      • 20 g/L ZnSO4
  • Example 8 (Yellow Bronze)
      • 2 g/L Sn2+
      • 8 g/L Cu2+
      • 400 g/L methanesulfonic acid
      • 2.5 g/L aromatic nonionic wetting agent
      • 1 g/L fatty alcohol ethoxylate
      • 4 g/L oxidation inhibitor
  • Example 9 (White Bronze)
      • 4 g/L Sn2+
      • 8 g/L Cu2+
      • 400 g/L methanesulfonic acid
      • 1 g/L aromatic nonionic wetting agent
      • 40 mg/L substituted dithioglycol
      • 4 g/L oxidation inhibitor
  • With these exemplary electrolyte compositions coatings with specific properties were deposited under the process conditions listed in the following table.
    Coating/Amounts
    Example in wt % Properties of coating
    No. Sn Cu Zn Bi Hardness Ductility Gloss Color
    1 10 90 180 HV50 ++ Yes Red
     2a 20 80 283 Hv50 ± Yes Yellow
     2b 20 80 317 HV50 ± Yes Yellow
    3 40 60 360 HV50 ± Yes White
    4 90 10 No White
    5 20 80 <1 +++ Yes Yellow
    6 20 80 <1 345 HV50 Yes Yellow
    7 20 80 <1 ++ Yes Yellow
  • When introducing elements of the present invention or the preferred embodiment(s) thereof, the articles “a,”“an,” “the,” and “said” are intended to mean that there are one or more of the elements. The terms “comprising,” “including,” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements.
  • In view of the above, it will be seen that the several objects of the invention are achieved and other advantageous results attained.
  • As various changes could be made in the above methods and products without departing from the scope of the invention, it is intended that all matter contained in the above description and shown in any accompanying drawings shall be interpreted as illustrative and not in a limiting sense.

Claims (27)

1. A method for electrolytic deposition of bronze onto a substrate, the method comprising:
immersing a substrate in an aqueous acidic electrolyte containing:
a) tin ions;
b) copper ions;
c) an alkylsulfonic acid; and
d) a nonionic wetting agent selected from the group consisting of aliphatic nonionic wetting agents, substituted dithioglycols, and combinations thereof.
2. The method of claim 1 wherein the alkylsulfonic acid is present in the electrolyte at a concentration of from 140 to 382 g/L of electrolyte.
3. The method of claim 1 wherein the alkylsulfonic acid comprises methanesulfonic acid in a concentration of at least about 290 g/L.
4. The method of claim 1 wherein the electrolyte further comprises an oxidation inhibitor.
5. The method of claim 1 wherein the electrolyte further comprises a dihydroxybenzene compound as an oxidation inhibitor.
6. The method of claim 1 wherein the bronze deposited onto the substrate comprises at least about 60% by weight Cu.
7. The method of claim 1 wherein the nonionic wetting agent is present in the electrolyte at a concentration of from about 2 to about 40 g/L.
8. The method of claim 1 wherein tin methanesulfonate is present in the electrolyte in an amount of from about 5 to about 195 g/L of electrolyte, thereby providing the tin ions at a concentration of from about 2 to about 75 g/L of electrolyte.
9. The method of claim 1 wherein copper methanesulfonate is present in the electrolyte in an amount of from about 8 to about 280 g/L of electrolyte, thereby providing the copper ions at a concentration of from about 2 to about 70 g/L of electrolyte.
10. The method of claim 1 wherein the electrolyte has a pH of less than about 1.
11. The method of claim 1 wherein the nonionic wetting agent comprises an aliphatic fatty alcohol ethoxylate.
12. The method of claim 1 wherein the nonionic wetting agent comprises the substituted dithioglycols.
13. An aqueous acidic electrolyte containing:
a) tin ions;
b) copper ions;
c) an alkylsulfonic acid; and
d) a nonionic wetting agent selected from the group consisting of aliphatic nonionic wetting agents, substituted dithioglycols, and combinations thereof.
14. The electrolyte of claim 13 wherein the alkylsulfonic acid is present at a concentration of from about 140 to about 382 g/L of electrolyte.
15. The electrolyte of claim 13 wherein the alkylsulfonic acid comprises methanesulfonic acid in a concentration of at least about 290 g/L.
16. The electrolyte of claim 13 further comprising an oxidation inhibitor.
17. The electrolyte of claim 13 further comprising a dihydroxybenzene compound as an oxidation inhibitor.
18. The electrolyte of claim 13 wherein the nonionic wetting agent is present in the electrolyte at a concentration of from about 2 to about 40 g/L of electrolyte.
19. The electrolyte of claim 13 wherein the tin ions are present at a concentration of from about 2 to about 75 g/L of electrolyte, and the copper ions are present at a concentration of from about 2 to about 70 g/L of electrolyte.
20. The electrolyte of claim 13 wherein the aliphatic nonionic wetting agent comprises an aliphatic fatty alcohol ethoxylate.
21. The electrolyte of claim 13 wherein the nonionic wetting agent is the substituted dithioglycol.
22. The electrolyte of claim 21 wherein the substituted dithioglycol is selected from the group consisting of Thiobis(diethyleneglycol), Thiobis(hexaethylene glycol), Thiobis(pentadecaglycelol), Thiobis(icosaethyleneglycol), Thiobis(pentacontaethyleneglycol),4,10-dioxa-7-thiatridecane-2,12-diol, Thiodiglycerin, Thiobis(triglycerin), 2,2′-thiodibutanolbis(octaethyleneglycolpentaglycerol) ether, Thiobis(octaethyleneglycol)bis(2-chloroethyl)ether, Thiobis(decaethyleneglycol)bis(carboxymethyl)ether, Thiobis(dodecaethyleneglycol)bis(2-nitroethyl)ether, Thiodiglycolbis(carboxymethyl)ether, Dithiodiglycolbis(carboxymethyl)ether, Thiobis(dodecaethyleneglycol), Dithiobis(hentetracontaethyleneglycol), Dithiobis(icosaethyleneglycolpentapropyleneglycol), Dithiobis(triglycerol), Dithiobis(decaglycelol), 3,6-Dithiaoctane-1,8-diol, 1,3-Propanedithiolbis(decaethyleneglycol)thioether, 1,4-Buthanedithiolbis(pentadecaglycerol)thioether, 1, 3-Dithioglycerolbis(pentaethyleneglycol)thioether, 1,2-Ethanedithiolbis(penta(1-ethyl)ethyleneglycol)thioether, 1,3-Dithioglycerolbis(di(1-ethyl)ethyleneglycol)thioether, 2-Mercaptoethylsulfide bis(hexatriacontaethylene-glycol), 2-Mercaptoethylsulfidebis(icosaethyleneglycol)di-methylether, 2-Mercaptoethyletherbis(diethyleneglycol), Thiodiglyceroltetra(decaethyleneglycol)ether, Diethyleneglycolmonomethylthioether, Decaglycerolmono(6-methylthiohexyl)thioether, 2-Mercaptoethylsulfide-ω-{(2-bromoethyl) icosaethyleneglycol}thioether-ω′-{(2-bromoethyl) hectaethyleneglycol}thioether, 1,4-Butanediol-ω-{(2-benzyloxy-1-methyl)ethyl}thioether-ω′-(de capropyleneglycoloctacontaethyleneglycol)thioether, Dithiobis(icosaethyleneglycol)bis(2-methyl-thioethyl)ether, 1,2-Ethanediol-ω-(4-methoxybenzyl)thioether-ω′-(pentacontaethy leneglycol)thioether, Triacontaethyleneglycolmono(4-cyanobenzyl)thioether, Thiobis(pentadecaethyleneglycol)bisallylether, Tricosaethyleneglycolmono(4-formylphenetyl)thioether, Pentadecaethyleneglycolmono{(acetylmethyl)thioethyl}thioether, 1,2-Ethanediol-co-(glycidyl)thioether-ω′-icosaethyleneglycolthioether, Octadecaethyleneglycolbis(2-methylthioethyl)ether, Hexadecaethyleneglycolmono(2-methylthioethyl)thioether, Icosaethyleneglycolmonomethylthioether, Undecaethyleneglycoldi(n-propyl)thioether, Dodecaethyleneglycolbis(2-hydroxyethyl)thioether, Undecaethyleneglycoldimethylthioether, Pentatriacontaethyleneglycolmono(2-n-butyldithioethyl)dithioether, 4,8,12-trithiapentadecane-1,2,6,10,14,15-hexaol, Icosaglycerolmono(2-ethylthioethyl)thioether, Triacontaethyleneglycolmono(2-methylthioethyl)thioether, Dithiobis(icosaethyleneglycol)dibenzylether, Tridecaethyleneglycolmonomethylthioether, Hexadecaethyleneglycol dimethylthioether, 1,2-Ethanedithiolbis(icosaethyleneglycol)thioether, Dithiobis(pentadecaethyleneglycol), 3,3′-thiodipropanol, and combinations thereof.
23. The electrolyte of claim 13 further comprising a gluconate.
24. The electrolyte of claim 13 further comprising hydroquinone.
25. The electrolyte of claim 13 having a pH of less than 1.
26. An aqueous acidic electrolyte containing:
a) divalent tin ions at a concentration of from about 2 to about 75 g/L of electrolyte;
b) divalent copper ions at a concentration of from about 2 to about 70 g/L of electrolyte;
c) an aromatic, nonionic wetting agent at a concentration of from about 2 to about 40 g/L of electrolyte;
d) a stabilizer, complexing agent, or mixture thereof at a concentration of less than about 50 g/L of electrolyte;
e) a wetting agent selected from the group consisting of an anionic wetting agent, a nonionic, aliphatic wetting agent, and mixtures thereof at a concentration of less than about 10 g/L of electrolyte;
f) an oxidation inhibitor at a concentration of less than about 5 g/L of electrolyte;
g) a brightener at a concentration of less than about 5 g/L of electrolyte; and
h) an alkylsulfonic acid at a concentration of at least about 140 g/L of electrolyte.
27. The electrolyte of claim 26 wherein the alkylsulfonic acid comprises methanesulfonic acid in a concentration of at least about 290 g/L.
US11/105,947 2005-04-14 2005-04-14 Method for electrodeposition of bronzes Abandoned US20060260948A2 (en)