US20070098492A1 - Temporary marking material and pavement marker - Google Patents
Temporary marking material and pavement marker Download PDFInfo
- Publication number
- US20070098492A1 US20070098492A1 US10/595,854 US59585404A US2007098492A1 US 20070098492 A1 US20070098492 A1 US 20070098492A1 US 59585404 A US59585404 A US 59585404A US 2007098492 A1 US2007098492 A1 US 2007098492A1
- Authority
- US
- United States
- Prior art keywords
- thermally
- expansible
- marking material
- pavement
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A temporary marking material comprises a thermally-expansible layer containing a binder, a pigment and thermally-expansible microballs, and a pavement marker comprises the temporary marking material. Both the temporary marking material and the pavement maker hardly peel off or move during the use, and when they become unnecessary, they can be easily peeled off by heating from the structure in a short time by virtue of the expanded microballs. When the temporary marking material is in practical use, the thermally-expansible layer is disposed on the surface of a structure. The pavement marker is disposed on the pavement as part of a surface of the structure.
Description
- The present invention relates to a temporary marking material and a pavement marker, and more particularly to a temporary marking material and a pavement marker which can be easily peeled off when they become unnecessary after being disposed on a structure such as a surface of pavement.
- Temporary marking materials which are disposed on the surface of a structure are generally used for the formation of pavement markers for temporary marking. After being used, such temporary marking materials must be removed from the surface of the structure or must be made invisible for observers.
- The pavement markers for temporary marking are used, for example, for marking border lines such as white lines which show temporary traffic lanes different from real lanes during road construction. The border lines for indication of temporary traffic lanes must be visible for observers during road construction, but they must be made invisible for observers after completion of the construction. Therefore, if the pavement markers for temporary marking are formed using, for example, paints or fusible sheets, in order to restore the state of the surface of the pavement to the original state after completion of the construction, (1) the border lines are covered with a paint of the same color as of the pavement (black or gray color) or (2) the material of the border lines is scraped off to make the border lines invisible for the observers. In this case, the operation for the removal of the border lines is very difficult and requires prodigious labor, and, besides, the operation of (2) might damage the surface of the pavement.
- On the other hand, it is known to use marking materials of peeling type comprising adhesive tapes. As such marking materials, Scotch-Lane (trademark for a pavement marker for temporary construction manufactured by 3M Co.) is commercially available. The marking materials of peeling type can be removed by peeling the border lines (such as white lines) comprising tapes adhered to the surface of the pavement after completion of the construction.
- Furthermore, JP-A-11-321817 and JP-A-5-319405 disclose use of rubber-like elastic materials as pavement markers for temporary marking, but use of them on a road of much traffic has the problem that the markers are apt to be peeled off from the surface of the road or apt to get out of position.
- Moreover, JP-A-11-349211 discloses a paint which foams or expands at a predetermined temperature and becomes easily peelable, though it is not intended to be used as temporary marking materials. This paint is coated on a material body, and is foamed (expanded) by heating after a lapse of service period and can be easily peeled from the material body. Thus, the material body can be reused.
- The conventional marking materials of peeling type are relatively low in adhesive force and must be subjected to a primer treatment for enhancing the adhesive force depending on the state of the pavement surface. However, in case the primer treatment is carried out, a large force is needed for peeling the tape, and the removal operation tends to become difficult. On the other hand, there is known a means to coat a material body such as metal, glass or plastic with a paint and then foam or expand the primer of the paint to make easy the peeing of the paint. However, there is no report that this means has been practically applied for temporary marking materials. Moreover, the above means much labor and high cost since the expansible layer should be formed by coating firstly the primer and then the facing paint thereon.
- Therefore, the present invention has been made in an attempt to solve the above problems in the conventional technologies and has provided a temporary marking material and pavement marker which hardly peel off or shift during use and can easily be peeled from the structure in a short time by heating when they become unnecessary.
- According to the present invention, there is provided a temporary marking material comprising a thermally-expansible layer containing a binder, a pigment, and thermally-expansible microballs, wherein said thermally-expansible layer is adhered to surface of a structure for use by virtue of the binder contained in the thermally-expansible layer.
- It is preferable that the thermally-expansible microballs are expandable at a predetermined temperature or higher, and expanded thermally-expansible microballs makes thermally-expansible layer expanded in such an extent that the temporary marking material becomes peelable from the surface of said structure due to expansion of the thermally-expansible layer caused by expanded thermally-expansible microballs when heated at said predetermined temperature or higher while the temporary marking material is adhered to the surface of the structure at a temperature of working atmosphere.
- It is further preferable that the thermally-expansible microballs have an expandability of at least 10 times in term of volume, compared with the volume thereof at temperature of working atmosphere. It is more preferable that the marking material further comprises a bead layer containing transparent beads; said bead layer being provided on a side of the thermally-expansible layer opposite to a side which contacts with the structure.
- According to the present invention, there is also provided a pavement marker comprising a temporary marking material which comprises a thermally-expansible layer containing a binder, a pigment and thermally-expansible microballs, wherein the pavement marker is disposed, for use, on a pavement as a surface of the structure by virtue of the binder contained in the thermally-expansible layer. The present pavement maker may contain the thermally-expansible microballs being expandable at a predetermined temperature or higher in such an extent that the thermally-expansible layer becomes peelable due to the expansion thereof caused by expansion of the heated thermally-expansible microballs. The pavement maker should adhere to the surface of the structure at a temperature of working atmosphere and become peelable from the surface of the structure due to the expansion of the thermally-expansible layer at said predetermined temperature or higher. Anyhow, the present temporary marking material mentioned above can be used for the present pavement marker, inclusive of any one of the preferable embodiments thereof.
- As mentioned above, the temporary marking material of the present invention has a thermally-expansible layer containing a binder, a pigment and thermally-expansible microballs. Therefore, when the temporary marking material is disposed on the surface of a structure as a pavement marker or the like and thereafter the pavement marker becomes unnecessary, the pavement marker can be easily peeled off from the surface of the structure since upon heating of the pavement marker, the thermally-expansible microballs thermally expand to result in expansion of the thermally-expansible layer, thereby causing reduction of adhesive force between the pavement marker and the structure.
- Furthermore, the pavement marker of the present invention comprises the temporary marking material of the present invention. Therefore, when the pavement marker is disposed on the surface of a structure and after the use, when the pavement marker becomes unnecessary, the pavement marker can be easily peeled off from the surface of the structure because upon heating of the pavement marker, the thermally-expansible microballs thermally expand to result in expansion and deformation of the thermally-expansible layer, thereby causing reduction of adhesive force between the pavement marker and the structure.
- The embodiments of the present invention will be explained in detail. These embodiments should not be construed as limiting the present invention in any manner, and changes and modifications may be made without departing from the spirit and scope of the invention.
- One embodiment of the temporary marking material of the present invention is as follows: the temporary marking material has a thermally-expansible layer containing a binder, a pigment and thermally-expansible microballs; the volume of the thermally-expansible microballs expand at a predetermined temperature or higher; the thermally-expansible layer expands in accordance with the expansion of the thermally-expansible microballs; and when the temporary marking material is disposed on the surface of a structure as a marker for temporary marking at a temperature of working atmosphere in such a manner that the thermally-expansible layer contacts with and adheres to the surface of the structure, the thermally-expansible layer adheres to the surface of the structure at a temperature of working atmosphere and upon being heated at a predetermined temperature or higher, the thermally-expansible layer expands and the temporary marking material becomes easily peelable from the surface of the structure. Therefore, when the temporary marking material becomes unnecessary, it can be peeled from the surface of the structure by heating the thermally-expansible layer to a predetermined temperature or higher. Here, the term “peelable” denotes such a state that the temporary marking material which adheres to the surface of the structure can be easily peeled off by man power, without using a special mechanical means.
- The temporary marking material of this embodiment has a thermally-expansible layer containing a binder, a pigment and thermally-expansible microballs. The binder serves to bind the pigment and the thermally-expansible microballs to maintain the thermally-expansible layer in the form of a layer. When the thermally-expansible layer is directly adhered to a structure such as the surface of pavement, the binder allows the temporary marking material and the structure to adhere to each other. The binder includes those which are conventionally used for paving marking materials. Examples of the binder are transparent materials such as epoxy resins, acrylic resins, urethane resins and silicone varnishes. The binder may contain a curing agent and/or a curing accelerator. The pigment and the thermally-expansible microballs may bind with the binder so as not to fall off from the thermally-expansible layer during use, and are not needed to be uniformly dispersed in the binder.
- The thermally-expansible microballs comprise a nearly spherical hollow shell of an elastic material in which a thermally-expansible gas and/or liquid is encapsulated. The elastic material is not particularly limited, and examples thereof are acrylic copolymers, vinyl chloride-based copolymers, etc. The gas and liquid enclosed in the shell include, for example, isobutane, isopentane, isooctane, n-pentane, etc. The thermal expansion coefficient of the thermally-expansible microballs is such that when the microball is heated to a predetermined temperature or higher, the volume thereof increases by 10 times or more, especially 15 times or more the volume of the microball at a temperature of working atmosphere. This is for markedly lowering the adhesion of the temporary marking material to the structure due to the expansion and easily peeling the temporary marking material from the structure. Here, the thermal expansion coefficient of the thermally-expansible balls means a ratio of the volume of the microball after expansion to the standard volume of the microball, that is, the volume before thermal expansion.
- The expression “temperature of working atmosphere” in this specification means an average temperature (atmospheric temperature) during temporary arrangement of the marking material on the structure. The environmental temperature of the surface of the pavement on which the marking material of the present invention is mainly used varies depending on seasons and extends over a wide range of about −20° C. to about 40° C. Therefore, it is preferred to select thermally-expansible microballs having a thermal expansion coefficient suitable for the environmental temperature at which the marking material is used.
- The average particle diameter of the thermally-expansible microballs is about 5 μm to about 50 μm. As the commercially available thermally-expansible microballs, there may be used EXPANCEL microspheres manufactured by Japan Phyllite Co., Ltd, MATSUMOTO microspheres manufactured by Matsumoto Yushi Co., Ltd., KUREHA microspheres manufactured by Kureha Chemical Co., Ltd., and the like. The shape of the thermally-expansible microballs may not necessarily be true sphere, and may be distorted or dented. The particle diameter of the deformed microball is a diameter of a sphere which is assumed to have the same volume as of the deformed microball.
- The pigment used has a color different from that of the surface of the structure and is selected so that it gives markers which are clearly visible for observers. There may be used, for example, titanium dioxide, carbon black, titanium yellow, phthalocyanine blue, phthalocyanine green, perylene red, etc.
- The content of the thermally-expansible microballs based on 100 parts by weight of the binder is usually 10-300 parts by weight, suitably 50-150 parts by weight. If the content of the thermally-expansible microballs is too small, the marker cannot be easily peeled by heating, and if it is too large, the thermally-expansible microballs are apt to fall off during temporary marking operation.
- The content of the pigment based on 100 parts by weight of the binder is usually 0.1-100 parts by weight, suitably 1-50 parts by weight. If the content of the pigment is too small, the temporary marking material tends to be light in color, and if it is too large, the pigment might fall off from the temporary marking material during use.
- The heating temperature at peeling of the marker, that is, the predetermined temperature, is usually not lower than 80° C., suitably not lower than 100° C., especially suitably 100-150° C. If the heating temperature is too low, the peeling operation requires a long time, and this would cancel out the simplicity of the operation. If it is too high, gas is sometimes generated. Therefore, for safety's sake, it is preferred to use heat sources such as infrared heaters and far infrared heaters rather than fire such as gas burner. From these viewpoints, the temporary marking material preferably becomes easily peelable after it is heated at a temperature of usually 80-200° C., preferably 100-150° C. for 1 second to 10 minutes.
- The thermally-expansible layer preferably comprises a dry film of a coloring paint comprising a vehicle containing a solvent and a binder dissolved or dispersed in the solvent, and thermally-expansible microballs and pigment dispersed in the vehicle. In this case, the thermally-expansible layer can be easily formed in the form of a layer.
- The thickness of the thermally-expansible layer is usually 1-5000 μm, suitably 10-500 μm. If the layer is too thin, the color of the thermally-expansible layer tends to be seen pale, and if it is too thick, there is the possibility of the thermally-expansible layer being damaged upon contact with cars or the like during use.
- The thermally-expansible layer may further contain other materials than those mentioned hereinabove. For example, it may contain transparent beads having a refractive index of 1.5-2.3 for the purpose of enhancing the visibility at night. The transparent beads include glass beads, ceramic beads, etc. Moreover, the thermal-expansible layer may contain aggregates such as natural stones, artificial stones, ceramics, etc. for improving the wear resistance of the layer.
- The temporary marking material may comprise only the thermally-expansible layer, but it is preferred that a beads layer containing the above-mentioned transparent beads is provided on the side of the thermally-expansible layer opposite to the side which contacts with the structure; that is, the side of the thermally-expansible layer which does not contact with the structure and is exposed on the surface of the structure and visible for observers. The transparent bead layer is preferably formed by scattering transparent beads on the thermally-expansible layer before drying.
- The temporary marking material of this embodiment can be produced in the following manner. First, a binder is dissolved or dispersed in a solvent to prepare a vehicle. Then, thermally-expansible microballs and a pigment are dispersed in the vehicle to prepare a coloring paint. The resulting coloring paint is coated on a surface such as the surface of pavement and dried to form a dry paint film which adheres to the surface of pavement. Thus, the thermally-expansible layer is formed. Production of a temporary marking material comprising only the thermally-expansible layer is completed in this way. When a temporary marking material additionally comprising a bead layer is produced, the coloring paint is coated on a surface such as the surface of pavement and then transparent beads are scattered on the surface of the paint film before drying, followed by drying to produce a temporary marking material comprising a thermally-expansible layer and a bead layer provided on the surface of the thermally-expansible layer.
- As a solvent, water is preferred, and there may also be used alcohols, ketones, esters, aliphatic and aromatic solvents. The content of the solvent in the coloring paint is preferably 10-90% by weight. If the content is lower than 10% by weight, concentration and viscosity of the coloring paint are high and hence it sometimes becomes difficult to form the temporary marking material in the desired thickness and shape. If it is higher than 90% by weight, drying properties are inferior and, furthermore, concentration and viscosity of the coloring paint are low and hence it sometimes becomes difficult to form the temporary marking material in the desired thickness and shape.
- The temporary marking material of this embodiment can be used as the pavement marker of the present invention shown below.
- An embodiment of the pavement marker of the present invention will be explained. One embodiment of the pavement marker of the present invention comprises the embodiment of the temporary marking material of the present invention explained hereinabove, and the pavement marker is disposed on the surface of pavement as a surface of the structure. The pavement marker of this embodiment can be produced in the same manner as in the embodiment of the temporary marking material of the present invention as mentioned above.
- The pavement marker of this embodiment comprises the temporary marking material of the present invention mentioned above. Therefore, when the pavement marker is disposed on the surface of a structure, that is, surface of pavement for use and, thereafter, when it becomes unnecessary, the thermally-expansible microballs thermally expand by heating of the pavement marker to bring about expansion and deformation of the thermally-expansible layer. As a result, adhesion between the pavement marker and the structure lowers, and the pavement marker can be easily peeled from the surface of the structure, that is, the surface of pavement.
- Such pavement marker shows a border line of traffic lane during road construction, and after completion of the construction, is peeled from the surface of the pavement and thus can be made invisible for observers. The color of the thermally-expansible layer is usually white, blue or yellow.
- This pavement marker is used for marking border lines such as white lines which are for showing temporary traffic lanes different from the real traffic lanes. These border lines for showing temporary traffic lanes can be easily peeled off to make them invisible for observers after completion of construction, and labor for the peeling operation can be diminished and the possibility of damaging the surface of pavement caused by scraping of the pavement marker can be removed.
- The pavement marker for temporary marking can also be used for drawing letters and/or signs on the surface of pavement for drivers or pedestrians being able to see the guiding information. After the use of the guiding information including letters and/or signs, they can be easily peeled by heating the thermally-expansible layer of the pavement mark to make them invisible for observers.
- The following coloring paint was coated directly on the surface of asphalted road, and glass beads were scattered thereon, followed by drying to form a thermally-expansible layer and a bead layer. Thus, a pavement marker comprising a temporary marking material was obtained. The coating of the coloring paint was carried out using a coating roller to form a marking material in the form of a white line of 20 cm in width and 50 cm in length. The glass beads (trademark: GK-19 manufactured by Japan Electric Glass Co., Ltd.) were scattered before drying of the coated paint, followed by air drying for about 10 minutes to form a film, thereby providing a bead layer on the thermally-expansible layer.
- The coloring paint used was prepared by dispersing 33.3 parts by weight of thermally-expansible microballs (trademark: M330 manufactured by Kureha Chemical Co., Ltd.) in 66.7 parts by weight of white acrylic emulsion (trademark: HARDLINEAQUA #21 manufactured by Atomix Co., Ltd.) as a binder containing a white pigment.
- After a lapse of 1 month from the formation of the pavement marker of this Example, the white line was heated and expanded using a movable far infrared heater, followed by cleaning by a vacuum type cleaner, and as a result, the white line could be easily removed. Thereafter, when one drove a car on the pavement, the driver recognized no trace of the marker of this Example disposed on the pavement in night and day.
- A pavement marker was obtained in the same manner as in the above Example using the following melting type paint This paint was a melting type pavement marking material. This paint was molten at 200° C. and coated on the surface of pavement, followed by solidification by cooling to form a white line.
- Composition of the paint:
- Titanium dioxide=6.5 parts by weight
- Calcium carbonate=61.0 parts by weight
- Petroleum resin=15.0 parts by weight
- Plasticizer=1.5 parts by weight
- Glass beads=16.0 parts by weight
- When the pavement marker of this Comparative Example was heated at 200-300° C. for 5 minutes by a burner after a lapse of 1 month from the formation of the marker, only the surface resin layer was carbonized and changed to black in its color, but the resin layer under the carbonized resin layer remained white in its color. When after a lapse of 1 week, one drove a car on the pavement on which the marking material was formed and observed the surface of the pavement, the driver saw the original white line exposed by the removal of the carbonized resin layer. Therefore, it was attempted to remove the original white line, that is, the pavement marker of this Comparative Example so as to make it invisible for the driver, but it could be removed only by using a cutting machine and much labor and time were required.
- The temporary marking material and pavement marker of the present invention can be utilized for forming temporary lines, signs, patterns, etc. on the surface of a pavement which can be removed in case they become unnecessary. The temporary marking material and pavement marker of the present invention hardly peel off or move during temporary marking, and when they become unnecessary, they can be easily peeled off by heating from the structure in a short time.
Claims (8)
1. A temporary marking material comprising
a thermally-expansible layer containing a binder,
a pigment, and
thermally-expansible microballs,
wherein said thermally-expansible layer is adhered to surface of a structure for use by virtue of the binder contained in the thermally-expansible layer.
2. A temporary marking material according to claim 1 ,
wherein the thermally-expansible microballs are expandable at a predetermined temperature or higher, and expanded thermally-expansible microballs makes thermally-expansible layer expanded; and
wherein the temporary marking material becomes peelable from surface of said structure due to expansion of the thermally-expansible layer caused by expanded thermally-expansible microballs when heated at said predetermined temperature or higher while the temporary marking material is adhered to the surface of the structure at a temperature of working atmosphere.
3. A temporary marking material according to claim 2 ,
wherein the thermally-expansible microballs have an expandability of at least 10 times in term of volume, compared with the volume thereof at temperature of working atmosphere.
4. A temporary marking material according to claim 1 ,
wherein the marking material further comprises a bead layer containing transparent beads; said bead layer being provided on a side of the thermally-expansible layer opposite to a side which contacts with the structure.
5. A pavement marker comprising a temporary marking material which comprises
a thermally-expansible layer containing a binder,
a pigment and
thermally-expansible microballs,
wherein the pavement marker is disposed, for use, on a pavement as a surface of the structure by virtue of the binder contained in the thermally-expansible layer.
6. A pavement marker according to claim 5 ,
wherein the thermally-expansible microballs are expandable at a predetermined temperature or higher, and expanded thermally-expansible microballs makes thermally-expansible layer expanded; and
wherein the temporary marking material becomes peelable from surface of said structure due to expansion of the thermally-expansible layer caused by expanded thermally-expansible microballs when heated at said predetermined temperature or higher while the temporary marking material is adhered to the surface of the structure at a temperature of working atmosphere.
7. A pavement marker according to claim 5 ,
wherein the thermally-expansible microballs have an expandability of at least 10 times in term of volume, compared with the volume thereof at temperature of working atmosphere.
8. A pavement marker according to claim 5 ,
wherein the marking material further comprises a bead layer containing transparent beads; said bead layer being provided on a side of the thermally-expansible layer opposite to a side which contacts with the structure.