US20070295243A1 - Use of hydroxyl-functional polyalkylorganosiloxanes as solvents for cationic photoinitiators for use in radiation-curable silicones - Google Patents
Use of hydroxyl-functional polyalkylorganosiloxanes as solvents for cationic photoinitiators for use in radiation-curable silicones Download PDFInfo
- Publication number
- US20070295243A1 US20070295243A1 US11/851,521 US85152107A US2007295243A1 US 20070295243 A1 US20070295243 A1 US 20070295243A1 US 85152107 A US85152107 A US 85152107A US 2007295243 A1 US2007295243 A1 US 2007295243A1
- Authority
- US
- United States
- Prior art keywords
- radical
- functional
- hydroxyl
- radicals
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims priority to German application Ser. No. 103 41 137.2, filed Sep. 6, 2003, herein incorporated by reference.
- 1. Field of the Invention
- The present invention relates to the use of hydroxyl-functional polyalkylorganosiloxanes as solvents for cationic photoinitiators and compositions comprising cationic photoinitiators, to hydroxyl-functional polyalkylorganosiloxanes as solvents and to their use in cationically radiation-curable silicones.
- 2. Description of Related Art
- Since the 1980s cationically radiation-curing abhesive coating materials have been known on the market. They are composed of organopolysiloxanes which contain reactive groups and which cure under UV radiation by a cationic mechanism. Said reactive groups may be epoxy groups, vinyl ether groups or alkenyloxy groups such as vinyloxy groups or propenyloxy groups. Such substances are described for example in U.S. Pat. No. 5,057,549; U.S. Pat. No. 5,231,157; U.S. Pat. No. 4,421,904; U.S. Pat. No. 4,547,431; U.S. Pat. No. 4,952,657; U.S. Pat. No. 5,217,805; U.S. Pat. No. 5,279,860; U.S. Pat. No. 5,340,898; U.S. Pat. No. 5,360,833; U.S. Pat. No. 5,650,453; U.S. Pat. No. 5,866,261 and U.S. Pat. No. 5,973,020.
- Cationic photopolymerization is a rapid, efficient and environmentally benign way to cure catonically polymerizable monomers. Particularly efficient photoinitiators are diaryliodonium salts (I) and triarylsulfoniun salts (II)
where Ar represents identical or different aromatic radicals which if desired may contain heteroatoms and/or further substituent radicals. - Diaryliodonium salts (I) in particular are known from the patent literature (GB-A-1 516 352, U.S. Pat. No. 4,279,717, EP-A-0 334 056, U.S. Pat. No. 5,468,890) and are used as photoinitiators for polymerizing cationically polymerizable substances.
- One important requirement for the utility of the photoinitiators is their miscibility in the cationically radiation-curable organopolysiloxanes. In order to ensure such miscibility the photoinitiators are prepared or modified with a hydrophobic radical, as described for example in U.S. Pat. No. 4,310,469; U.S. Pat. No. 6,365,643 and U.S. Pat. No. 6,380,277.
- In pure form, however, such photoinitiators are solids or at least waxlike or viscous compounds and hence are difficult to incorporate into cationically radiation-curable organopolysiloxanes. For example the commercially available cationic photoinitiator bis(dodecylphenyl)iodonium hexafluoroantimonate (III),
has a waxlike consistency at room temperature. - In order to ensure ease of incorporation of such photoinitiators into the cationically radiation-curable compositions, the photoinitiators are generally supplied in dissolved form. Used for this purpose are solvents such as toluene, xylene, isopropanol, propylene glycol, palkylphenols, propylene carbonate, glycidyl ethers and butyrolactone.
- One important requirement for the utility of such solvents is that the cationic photoinitiators form clear solutions therein and form clear mixtures with the cationically radiation-curable organopolysiloxanes. With propylene carbonate, ethylene glycol or propylene glycol, for example, it is the case, however, that the frequently very hydrophobic cationically curable organopolysiloxanes are generally unable to form clear mixtures. Other solvents such as C12/C14 glycidyl ethers, for example, are environmentally hazardous.
- Low molecular mass, highly volatile compounds in particular are of only limited suitability as solvents for the cationic photoinitiators, since they burden the environment by odors and/or volatile solvent constituents (VOCs, volatile organic compounds) and harbor the risk of formation of explosive gas mixtures.
- In order to prevent the environment being burdened by odors and/or VOCs the aim is to use high-boiling solvents which additionally by way of functional groups can be incorporated into the cationically curable coating and hence do not remain as a migrateable constituent in the cured silicone release coating. High-boiling solvents of this kind may be, for example, allylphenols or alkyl epoxides, as described in EP-A-0 522 703.
- Particularly in the case of coatings produced from organopolysiloxanes containing epoxy groups, however, it is observed that polar solvents, such as isopropanol, propylene glycol and alkylphenols, may adversely affect the release activity of the organopolysiloxane coating. U.S. Pat. No. 4,954,364 describes for example the addition of alkylphenols to organopolysiloxanes containing epoxy groups as a controlled release additive (CRA) in order deliberately to detract from the release property of the organopolysiloxane coating. The addition of just 0.1 part of nonylphenol to the organopolysiloxane containing epoxy groups produces a doubling in the release force as compared with a nonylphenol-free coating. The release force (or release value) is the force required to peel the respective adhesive tape from the substrate. Generally speaking, however, the aim when using an organopolysiloxane coating is to obtain a very good release effect, i.e., low release force.
- It is therefore desirable to find high-boiling solvents which do not burden the environment with odors and/or volatile solvent constituents (VOCs, volatile organic compounds) and which do not adversely affect the release activity of organopolysiloxane coatings.
- A further important requirement for the utility of such solvents is that the mixtures of solvent and photoinitiator exhibit at least six months' storage stability. It is desirable, in other words, to find solvents which form clear solutions with the cationic photointiator and which have a storage stability of at least six months.
- For the preparation of cationic photoinitiators, as described in applications U.S. Pat. No. 6,365,643 and U.S. Pat. No. 6,380,277, the substances used are in some cases toxic, corrosive and/or environmentally hazardous, such as isocyanates, acid chlorides or chlorosilanes, for example. For reasons of the reaction r process these substances are used in excess, an excess which it is then impossible to remove sufficiently by distillation afterward, owing to the thermal liability of the iodonium salts.
- It is therefore also desirable to find solvents which together with the remnant excesses are consumed by reaction to form nonhazardous, polymeric substances.
- Therefore, it is an object of the present invention to provide solvents for diaryliodonium salts in particular as photoihitiators for the cationic curing of radiation-curable organopolysiloxanes, these solvents forming clear mixtures with the cationically curable organopolysiloxanes and having a storage stability of at least six months. The solvents reduce the burden on the environment due to odors and/or volatile solvent constituents (VOCs, volatile organic compounds), do not adversely affect the release activity of organopolysiloxane-based coatings, can be incorporated into the coating by polymerization and can react with excesses of reactive substances to form nonhazardous, polymeric compounds.
- Surprisingly it has been found that the aforementioned object is achieved through the use of hydroxyl-functional polyalkylorganosiloxanes as solvents. Other objects include mixtures comprising these hydroxy-function polyalkyl organosiloxanes and cation photoinitiators. These and other objects will be apparent from the following Description of the Invention.
- The invention therefore firstly provides mixtures which comprise:
A) hydroxyl-functional polyalkylorganosiloxanes of the general formula (IV)
where
a is from 0 to 200,
b is from 0 to 50,
R1 is identical or different at each occurrence in the molecule and denotes alkyl radicals, preferably having from 1 to 4 carbon atoms,
R2, R2* and R2** are identical or different and have the following definition: - R2a independently at each occurrence denotes selected, optionally substituted alkyl radicals preferably having from 1 to 20 carbon atoms, optionally substituted aryl or aralkyl radicals,
- R2b independently at each occurrence denotes selected radicals of the general formula
—R3[—O—(CnH2nO—)xH]z
where - R3 is a z+1-valent hydrocarbon radical which optionally is substituted and/or contains ether bridges and preferably has from 2 to 20 carbon atoms or is an aryl radical or aralkyl radical which optionally is substituted and/or contains ether bridges,
- n is 2, 3 or 4,
- x is from 0 to 100,
- z is from 1 to 6,
- with the proviso that in the average molecule in each case at least one radical R2, R2*, R2** has the definition R2b, and
- B) at least one cationic photoinitiator.
- The inventive mixtures can contain from about 1 weight % to 99 weight % of compound A and from about 99 weight % to about 1 weight % of component B, based upon total weight of the mixture provided that the resulting mixture is a liquid (flowable) at room temperature. Preferred amounts of component A are from about 10 weight % to about 90 weight %, with about 30 weight o/% to about 70 weight % being especially preferred.
- This invention further provides for the use of the polyalkylorganosiloxanes of the formula (IV) as solvents for cationic photoinitiators.
- The invention further provides mixtures consisting of
A) at least one hydroxyl-functional polyalkylorganosiloxane of the general formula (IV)
where
a is from 0 to 200,
b is from 0 to 50,
R1 is identical or different at each occurrence in the molecule and denotes alkyl radicals, preferably having from 1 to 4 carbon atoms,
R2, R2* and R2** are identical or different and have the following definition: - R2a independently at each occurrence denotes selected, optionally substituted alkyl radicals having from 1 to 20 carbon atoms, aryl or aralkyl radicals which optionally are substituted and/or contain ether bridges,
- R2b independently at each occurrence denotes selected radicals of the general formula
—R3[—O—(CnH2nO—)xH]z
where -
- R3 is a z+1-valent hydrocarbon radical which optionally is substituted and/or contains ether bridges and preferably has from 2 to 20 carbon atoms or is an optionally substituted aryl radical or aralkyl radical,
- n is 2, 3 or 4,
- x is from 0 to 100,
- z is from 1 to 6,
with the proviso that in the average molecule in each case at least one radical R2, R2*, R2** has the definition R2b, and
B) at least one cationic photoinitiator, preferably diaryliodonium salts.
- In one preferred embodiment of the present invention the hydroxyl-functional polyalkylorganosiloxanes are such that
- a is a number in the range from 5 to 100, in particular from 5 to 80,
- b is a number in the range from 0 to 10, in particular from 0 to 5,
- n is a number in the range from 2 to 3,
- x is a number in the range from 0 to 30, in particular from 0 to 10,
- z is a number from 1 to 3.
- The values of the indices a, b and x are mean values, the respective increments being present in random or blockwise distribution in the molecule.
- In the moiety —R3[—O—(CnH2nO—)xH]z it is possible for “n” identically or differently to adopt one or more of the values from 2 to 4, it being possible for the distribution within the range of repetition “x” to be blockwise or random.
- Particular preference is given in accordance with the present invention to hydroxyl-functional polyalkylorganosiloxanes where the radical R1 in the general formula (IV) is a methyl radical.
- Examples of the radical R2a are alkyl radicals, such as the methyl, ethyl, butyl, dodecyl and/or hexadecyl radical; aryl radicals, such as the phenyl and/or naphthyl radical; and aralkyl radicals, such as the (methyl)ethylphenyl radical.
- Examples of the radical R3 are divalent alkyl radicals, such as —CH2—, —(CH2)2—, —(CH2)3—, —(CH2)4—, —(CH2)6, —(CH2)10—, —CH2CH2CH(OCH3)CH2—; aryl radicals, such as the phenyl, naphthyl or anthryl radical; and aralkyl radicals, such as
and radicals containing ether bridges, such as
Particularly preferred examples of the radical R3 are —(CH2)3—, —(CH2)6—,
Examples of hydroxyl-functional polyalkylorganosiloxanes used in accordance with the invention are - Cationic photoinitiators for the purposes of the present invention are diaryliodonium salts (I) and triarylsulfonium salts (II).
- Examples of cationic photoinitiators in the sense of the present invention may be found in J. V. Crivello and K Dietliker, Photoinitiators for Free Radical Cationic & Anionic Photopolymerisation 2nd Edition, John Wiley and Sons, New York, 1998, pp. 379-466 and in U.S. Pat. No. 6,365,643. The cationic photoinitiators preferred in accordance with the invention are diaryliodonium salts of the general formula (V):
Ar—I+—Ar X− (V)
in which
I is the element iodine,
Ar represents identical or different aromatic radicals which if desired may contain heteroatoms and/or further substituent radicals
and
X is the anion of a complex metal salt or of a strong acid.
Particularly preferred examples of diaryliodonium salts in the sense of the present invention are
Comparative Experiments: - The solution behavior of the hydroxy-functional polyalkylorganosiloxanes used in accordance with the invention was compared with that of noninventive compounds. For this purpose, 50% by weight each of solvent and of diaryliodonium salt were mixed with one another and the storage stability (180 days at 5 25° C.) of the mixture was observed. The results are summarized in Table 1:
TABLE 1 Solution Solution Diaryliodonium after after Solvent salt 1 day 180 days Toluene Ex. 10 cloudy two phases Toluene Ex. 11 clear two phases Toluene Ex. 12 clear two phases Toluene Ex. 13 clear clear Isopropanol Ex. 10 clear clear Dodecylphenol Ex. 13 clear clear Polyethylene glycol 200 Ex. 10 clear clear Silicone oil 100 Ex. 12 cloudy two phases C12/C14 glycidyl ether Ex. 14 clear clear Propylene carbonate Ex. 14 clear clear Ex. 1 Ex. 10 clear clear Ex. 2 Ex. 13 clear clear Ex. 3 Ex. 13 clear clear Ex. 4 Ex. 15 clear clear Ex. 5 Ex. 14 clear clear Ex. 6 Ex. 11 clear clear Ex. 7 Ex. 13 clear clear - It is apparent that the hydroxy-functional polyalkylorganosiloxanes used in accordance with the invention form clear solutions with diaryliodonium salts and produce solutions which are still stable even after a 180-day storage period.
- In order to determine the burden on the environment as a result of odors and/or volatile solvent constituents (VOCs, volatile organic compounds) 4% by weight of a photoinitiator solution composed of 50% by weight solvent and 50% by weight photoinitiator were mixed with 96% by weight of a cycloaliphatic epoxy silicone having a viscosity of 125 mPas and an epoxy value of 3.5% and the mixture was then applied using a five-roll applicator in a pilot plant to a standard BOPP (biaxially oriented polypropylene) film. The application weight was 1 g/m2. The coating was subsequently cured using a microwave-excited UV lamp (Fusion, 120 W/cm) at a speed of 20 m/min.
- The odor of the coated film was determined immediately following its departure from the UV lamp. The results are summarized in Table 2.
TABLE 2 Solvent Diaryliodonium salt Odor Toluene Ex. 10 toluene (severe) Toluene Ex. 11 toluene (severe) Toluene Ex. 12 toluene (severe) Toluene Ex. 13 toluene (severe) Isopropanol Ex. 10 isopropanol Dodecylphenol Ex. 13 neutral Polyethylene glycol 200 Ex. 10 neutral Silicone oil 100 Ex. 12 neutral C12/C14 glycidyl ether Ex. 14 acrid Propylene carbonate Ex. 14 neutral Ex. 1 Ex. 10 neutral Ex. 2 Ex. 13 neutral Ex. 3 Ex. 13 neutral Ex. 4 Ex. 15 neutral Ex. 5 Ex. 14 neutral Ex. 6 Ex. 11 neutral Ex. 7 Ex. 13 neutral
It is apparent that the hydroxyl-functional polyalkylorganosiloxanes used in accordance with the invention have a significantly improved odor as compared with the noninventive solvents, particularly toluene and isopropanol. -
- (J. V. Crivello, S. Liu, Journal of Polymer Science: Part A: Polymer Chemistry, Vol. 38, 389-401 (2000)) in the cationic polymerization of cationically polymerizable compositions - in this case epoxides—and hence to be incorporated into the coating in the course of cationic curing.
- The skilled worker is aware that the hydroxyl-functional polyalkylorganosiloxanes can react with reactive compounds, such as isocyanates, acid chlorides and/or chlorosilanes, to form less harmful compounds. For example, following the preparation of the diaryliodonium salt (Ex. 13), the hydroxyl-functional polyalkylorganosiloxane (Ex. 2) is able to react with the excess (trifluoromethyl)phenyl isocyanate to form a harmless urethane.
- In order to determine the effect of the solvent used on the release properties of organopolysiloxane-based release coatings, 4% by weight of a photoinitiator solution consisting of 50% by weight solvent and 50% by weight photoinitiator was mixed with 96% by weight of a cycloaliphatic epoxy silicone having a viscosity of 300 mPas (25° C.) and an epoxy value of 1.36%. The mixture was evaluated for clouding as a sign of incompatibilities. The mixture was then applied to a standard BOPP film using a five-roll applicator in a pilot plant. The application weight was 0.5 to 1.0 g/m2. The coating was subsequently cured using a microwave-excited LV lamp (Fusion, 120 W/cm) at a speed of 20 m/min.
- (A) The release value of the release coatings was determined in accordance with FINAT Test Method 10. This test is carried out using the commercially available adhesive tape (25 mm wide) TESA® 7476 from Beiersdorf. In order to measure the adhesiveness, these adhesive tapes are rolled onto the release coating and subsequently stored at 40° C. under a weight of 70 g/cm2. After 24 hours a measurement is made of the force required to peel the respective adhesive tape from the substrate at a peel angle of 180° and at a peel rate of 30 cm/min. This force is termed the release force or release value.
- (B) The subsequent adhesion is determined largely in accordance with FINAT Test Method 11. For this purpose the adhesive tape TESA® 7475 from Beiersdorf was rolled onto the release coating and then stored at 40° C. under a weight of 70 g/cm2. After 24 hours the adhesive tape was separated from the release substrate and rolled onto a defined substrate (steel plate). After one minute a measurement was made of the force required to peel the adhesive tape from the substrate at a peel angle of 1800 and at a peel rate of 30 cm/min. The value thus measured was divided by the value given by an untreated adhesive tape under otherwise identical test conditions. The result was termed the subsequent adhesion and is generally indicated as a percentage. Figures of more than 80% are considered by the skilled worker to be adequate, and suggest effective curing.
- The results are summarized in Table 3.
TABLE 3 Release force Subsequent Diaryl- Mixture with (cN/inch) adhesion (%) No. Solvent iodonium salt epoxy silicone Method (A) Method (B) 1 Toluene Ex. 10 cloudy 40 70 2 Toluene Ex. 11 cloudy 35 72 3 Toluene Ex. 12 clear 55 85 4 Toluene Ex. 13 clear 57 88 5 Isopropanol Ex. 10 cloudy 45 69 6 Dodecylphenol Ex. 13 clear 92 89 7 Polyethylene glycol 200 Ex. 10 cloudy 47 73 8 Silicone oil 100 mPa · s Ex. 12 cloudy 40 65 9 C12/C14 glycidyl ether Ex. 14 clear 55 88 10 Propylene carbonate Ex. 14 cloudy 52 90 11 Ex. 1 Ex. 14 clear 56 87 12 Ex. 2 Ex. 13 clear 58 88 13 Ex. 3 Ex. 13 clear 57 90 14 Ex. 4 Ex. 15 clear 52 91 15 Ex. 5 Ex. 14 clear 50 89 16 Ex. 6 Ex. 14 clear 59 91 17 Ex. 7 Ex. 13 clear 58 90 - Low release values and low subsequent adhesion indicate poor curing of the silicones or migrateable constituents in the coating. This is the case for experiments 1, 2, 5 and 7, owing to the partial incompatibility of the photocatalyst with the epoxy silicone, and in experiment 8, owing to the migrateable solvent (silicone oil, viscosity of 100 mPa.s).
- Release values of around 50-60 cN/in in conjunction with good subsequent adhesion point to a good-quality release coating. The release properties of organopolysiloxane-based release coatings are not adversely affected by the use of hydroxyalkylpolydimethylsiloxanes as solvents for diaryliodonium salts as compared with the prior art mentioned at the outset.
- The hydroxyalkylpolydimethylsiloxanes used in accordance with the invention are suitable for use as polymeric solvents for photoinitiators for polymerizing cationically polymerizale organopolysiloxanes.
- The above description is intended to be illustrative and not limiting. Various changes in the embodiments described herein may occur to those skilled in the art. These changes can be made without departing from the scope or spirit of the invention.
Claims (14)
1. A mixture consisting:
—R3[—O—(CnH2nO—)xH]z
A) at least one hydroxyl-functional polyalkylorganosiloxanes of the formula (IV)
where
a is from 0 to 200,
b is from 0 to 50,
R1 is identical or different at each occurrence in the molecule and denotes alkyl radicals,
R2, R2 and R2 are identical or different and have the following definition:
R2a independently at each occurrence denotes optionally substituted alkyl radicals, optionally substituted aryl radicals, or optionally substituted aralkyl radicals,
R2b independently at each occurrence denotes selected radicals of the general formula
—R3[—O—(CnH2nO—)xH]z
where
R3 is a z+1-valent hydrocarbon radical which optionally is substituted and/or contains ether bridges or is an aryl radical or aralkyl radical which optionally is substituted and/or contains ether bridges,
n is 2, 3 or 4,
x is from 0 to 100,
z is from 1 to 6,
with the proviso that in the average molecule in each case at least one radical R2, R2* , R2** has the definition R2b, and
B) at least one cationic photoinitiator.
2. The mixture according to claim 1 wherein the hydroxyl-functional polyalkylorganosiloxane is as follows:
a is a number in the range from 5 to 100,
b is a number in the range from 0 to 10,
n is a number in the range from 2 to 3,
x is a number in the range from 0 to 30,
z is a number from 1 to 3.
3. The mixture according to claim 2 , wherein
a is a number in the range of 5 to 80,
b is a number in the range of 0 to 5, and;
v is a number in the range of 0 to 10.
4. The mixture according to claim 1 wherein R1 in the hydroxyl-functional polyalkylorganosiloxane is a methyl radical.
5. The mixture according to claim 1 , wherein at least one radical R2a in the hydroxyl-functional polyalkylorganosiloxane is a radical selected from the group consisting of methyl, ethyl, butyl, dodecyl, hexadecyl, aryl, and (methyl)ethylphenyl.
7. The mixture as claimed in claim 1 , wherein the cationic photoinitiator is a diaryliodonium salt.
10. The mixture as claimed in claim 1 , wherein the cationic photoinitiator is a triarylsulfonium salt.
11. (canceled)
12. A method for increasing the storage shelf life of a solution comprising of at least one cationic photoinitiator which comprises dissolving the cationic photoinitiator in a solvent comprising at least one hydroxyl-functional polyalkylorganosiloxanes of the formula
where
—R3[—O—(CnH2nO—)xH]z
a is from 0 to 200,
b is from 0 to 50,
R1 is identical or different at each occurrence in the molecule and denotes alkyl radicals,
R2, R2* and R2** are identical or different and have the following definition:
R2a independently at each occurrence denotes selected, optionally substituted alkyl radicals, optionally substituted aryl radicals, or aralkyl radicals,
R2b independently at each occurrence denotes selected radicals of the general formula
—R3[—O—(CnH2nO—)xH]z
where
R3 is a z+1-valent hydrocarbon radical which optionally is substituted and/or contains ether bridges or is an aryl radical or aralkyl radical which optionally is substituted and/or contains ether bridges,
n is 2, 3 or 4,
x is from 0 to 100,
z is from 1 to 6,
with the proviso that in the average molecule in each case at least one radical R2, R2*, R2** has the definition R2b, as solvents for cationic photoinitiators, to form the mixture of claim 1 whereby the solution is stable for at least six months.
13. A cationically curable composition which comprises at least one organopolysiloxanes, which contains at least one UV reactive group and that cures cationically under UV radiation, and the mixture according to claim 1 .
14. An adhesive coating which is obtained by reacting the cationically curable composition according to claim 1 with UV light.