US20080110245A1 - Methods Relating to Molding Optical Lenses - Google Patents
Methods Relating to Molding Optical Lenses Download PDFInfo
- Publication number
- US20080110245A1 US20080110245A1 US11/932,736 US93273607A US2008110245A1 US 20080110245 A1 US20080110245 A1 US 20080110245A1 US 93273607 A US93273607 A US 93273607A US 2008110245 A1 US2008110245 A1 US 2008110245A1
- Authority
- US
- United States
- Prior art keywords
- piece
- cavity
- sealing material
- opening
- instrument
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method that includes providing a cavity defined by at least a portion of a mold and a closure member attached to the portion of the mold, the portion of the mold being oriented vertically and having a top and a bottom, and a sealing material being positioned near the bottom and attached to the closure member; puncturing the sealing material and the closure member with an instrument near the bottom, the puncturing creating an opening in the sealing material; and introducing a polymerizable composition into the cavity through the instrument. A method useful in testing sealing materials. Other methods are also disclosed.
Description
- 1. Field of the Invention
- The invention relates to testing materials for possible use during the molding of optical lenses. The invention also relates to molding optical lenses, particularly ophthalmic lenses, from polymerizable compositions.
- 2. Description of Related Art
- The traditional mold comprises a molding cavity defined by two mold pieces, each typically made of mineral glasses, and an annular closure member, such as a gasket or an adhesive tape, disposed around the periphery of the two mold pieces and attached to them. The conventional way to fill such a two-piece mold is by causing the molding material to flow into the molding cavity through a casting opening provided for this purpose in the closure member. In at least a partly automated process, the molding cavity to be filled is vertically aligned with a filling device that is adapted to deliver a particular quantity of molding material through a nozzle.
- One way to fill such a vertically oriented mold is by filling the molding cavity through a nozzle disposed at the top of the mold periphery, which nozzle introduces molding material into the molding cavity by gravity only. See, for example, U.S. Pat. No. 5,110,514. Experience has shown that in the case of a relatively long waiting time (for example, on the order of two hours) between filling the mold and starting polymerization, unless special measures are implemented, the optical lenses obtained frequently have localized optical defects of greater or lesser severity, which leads to relatively high reject rates.
- To overcome such problems, U.S. Pat. Nos. 5,547,618 and 5,662,839 propose filling the molding cavity of a vertically oriented two-piece mold through a casting opening formed in a lower part of the closure member and using a pumping mechanism adapted to cause the molding material to flow without significantly pressurizing it. Typically, filling of the molding cavity in this manner is effected using a pipe connected to a pressurized molding material reservoir and applied, like a filling nozzle, to the casting opening. With such a method, it is possible to start polymerization immediately after filling. However, in the case of molding material that reacts at room temperature in less than ten minutes, such as the formulations disclosed in U.S. Pat. No. 5,973,098, the pipe will quickly clog.
- One solution to this problem involves the use of a check valve provided in the closure member as disclosed in U.S. patent application Ser. No. 09/814,318, the inventors of which are Gabriel Keita and Yassin Yusef Turshani. While use of a check valve, which may be a duck bill valve as disclosed in the referenced application, addresses the aforementioned clogging problem, use of such valves may be expensive.
- Another way of filling a vertically oriented mold is disclosed in Japanese Patent Application No. 8-308223 (Unexamined Japanese Patent 10-146846). The Japanese application discloses molding cavity A defined by two molding pieces 1 and annular closure member comprising adhesive tape 2. An elastic body with a rubber-like elasticity 3 is attached to the adhesive tape at the top of the vertically oriented mold. As an alternative to the elastic body 3, the Japanese application also discloses a coating 4 that has a rubber-like elasticity. The Japanese application discloses introducing molding material into the cavity A through an injection needle placed through both the elastic body 3 or coating 4 and the adhesive tape 2 while using an exhaust tube placed into the molding cavity A through another opening in the elastic body 3 or coating 4 and the adhesive tape 2. The Japanese application discloses withdrawing the nozzle and the exhaust tube after filling the cavity A with the molding material. The Japanese application notes that two holes formed by the introduction of the nozzle (an example of which is an injection needle) and the exhaust tube are closed after those items are removed by virtue of the rubber-like elasticity of elastic body 3 or coating 4. Next, the molding material is cured in a heating furnace for about 10 to 15 hours at about 100° C. The filling method disclosed in the Japanese application is not confronted with, and therefore does not address, the problem of molding material leaking out of the molding cavity A around the injection needle or exhaust tube. This follows because those two instruments enter cavity A from the top of the vertically oriented mold. In addition, problems with encountering localized optical defects due, for example, to microbubbles that form in the molding material as it fills up cavity A may be present with the method disclosed in the Japanese application unless special measures are implemented.
- We provide methods and compositions that may be used to mold optical lenses, especially ophthalmic lenses, in a fast and cost-efficient manner. In one such method, a cavity is provided that is defined by at least a portion of a mold and by a closure member attached to the portion of the mold. The mold is oriented vertically and has a top and a bottom. A sealing material is positioned near the bottom and attached to the closure member. This method also includes puncturing the sealing material and the closure member with an instrument near the bottom. The puncturing creates an opening in the sealing material. This method further includes introducing a polymerizable composition into the cavity through the instrument. Through the use of suitable sealing materials in connection with this and other disclosed methods, the expense of a check or other similar valve may be avoided because such sealing materials tend to conform well to the outside of the instrument used to introduce the polymerizable composition. Further, once the puncturing instrument is removed, such sealing materials tend to minimize (or even eliminate) the size of the opening that is created as a result of the puncture, thereby minimizing (or even eliminating) the formation of microbubbles within the polymerizable composition.
- We also provide methods for evaluating the self-sealing nature of various materials, in order to determine if those materials are suited for use as sealing materials in, for example, the method described above. In one such method, a cavity is provided that has at least one opening over which a piece of sealing material is positioned. The cavity contains (but is not necessarily filled with) liquid. The method also includes puncturing the piece of sealing material with an instrument, thereby creating a sealing material opening for a period of time; applying a vacuum to the cavity; and noting a cavity pressure approximately when a first bubble forms around gas entering the liquid through the sealing material opening. The lower the cavity pressure noted, the better, or more well-suited, the tested material is for use as a sealing material in, for example, the method described above.
- The following drawings demonstrate certain, but not necessarily all, aspects of the present methods and compositions. The drawings illustrate by way of example and not limitation, and they use like references to indicate similar elements.
-
FIG. 1 is a cross-sectional view of a mold and a pumping system. -
FIG. 2 is a front view of a mold. -
FIG. 3 is a front view of a mold that has been rotated, and shows the migration pattern of bubbles formed within the polymerizable composition. -
FIG. 4 is a front view of a mold that has not been rotated, and shows the migration pattern of a bubble formed within the polymerizable composition. -
FIGS. 5A and 5B are front and side views, respectively, of a testing system used to test pieces of material to determine their suitability for use as sealing materials. - The terms “comprise” (and any form of comprise, such as “comprises” and “comprising”), “have” (and any form of have, such as “has” and “having”), “contain” (and any form of contain, such as “contains” and “containing”), and “include” (and any form of include, such as “includes” and “including”) are open-ended linking verbs. As a result, a method, or a step in a method, that “comprises,” “has,” “contains,” or “includes” one or more steps or elements possesses those one or more steps or elements, but is not limited to possessing only those one or more steps or elements.
- Thus, and by way of example, a method “comprising” providing a cavity defined by at least a portion of a mold and a closure member attached to the portion of the mold, the portion of the mold being oriented vertically and having a top and a bottom, and a sealing material being positioned near the bottom and attached to the closure member; puncturing the sealing material and the closure member with an instrument near the bottom, the puncturing creating an opening in the sealing material; and introducing a polymerizable composition into the cavity through the instrument, has, but is not limited to having only, the recited steps. That is, the method possesses at least the recited steps, but does not exclude other steps that are not expressly recited. For example, the method also covers retracting the instrument and/or rotating the mold.
- While the present methods may be adaptable to various modifications and alternative forms, specific embodiments have been shown by way of example. However, it should be understood that the present methods are not intended to be limited to the particular forms disclosed. Rather, they are is to cover all modifications, equivalents, and alternatives falling within the scope of the claims.
- Moreover, the different aspects of the disclosed methods may be utilized in various combinations and/or independently. Thus the present methods and compositions are not limited to only those combinations disclosed, but rather may include other combinations. Those of skill in the art will understand that numerous other modifications may be made to the disclosed methods and compositions, and that such similar substitutes and modifications are within the scope of the claims.
-
FIG. 1 shows amold 10 in cross-section.Mold 10 includes two mold pieces—afront mold piece 12 and aback mold piece 14. The two mold pieces may be made of any suitable material such as, for example, glass. More specifically, mineral glass may be used for these mold pieces. Other suitable mold piece materials are metal and plastic. The facing inside surfaces of front andback mold pieces FIG. 1 , the two molding pieces are intended for molding a minus ophthalmic lens. - Front and
back mold pieces FIG. 1 in the practice of usingmold 10. Such additional parts may include, for example, a frame in which front andback mold pieces -
Mold 10 has a top, generally designated by 30, and a bottom, generally designated by 32. -
Front mold piece 12 has anedge 22, and backmold piece 14 has anedge 24. As shown inFIG. 1 ,closure member 16 is attached to a portion of mold 10 (e.g., to front andback mold pieces 12 and 14). Suitable closure members may be characterized as sleeves (e.g., a rubber gasket), and may be disposed around and engaged with the edges of the front and back mold pieces ofmold 10. For example,FIG. 1 showsclosure member 16 disposed around and attached toedges back mold pieces Closure member 16 may also be a strip that is wrapped around the edges of the mold pieces. A machine may be used to effect this. For example, a machine may be configured to holdmold pieces closure member 16 around edges 22 and 24 whilemold pieces closure member 16 toedges -
Closure member 16 may comprise any suitable material, including, for example, an adhesive synthetic material or a heat-shrink synthetic material. One example of a suitable closure member is Niponzeon Sliontec 6263, which is commercially available from Sliontec Corporation (3819 Noborito, Tama-ku, Kawasaki, Kanagawa, 214-0014 Japan). Another example of a suitable material forclosure member 16 is Barnier tape reference no. 8055 (produced by Scapa Tapes France; 9-11 Rue Edouard Branly 26000 Valence). 3M produces tapes that are also suitable forclosure member 16—3M Composite Bonding Tape 8905 and 3M Polyester Film Tape 8412 (available from 3M's Industrial Tape and Specialties Division, St. Paul, Minn.). -
Mold 10 also includes sealingmaterial 18, which is positioned near bottom 32 and attached toclosure member 16. By “near bottom 32,” we mean either atbottom 32 or close to bottom 32. All the present uses of “near” carry the same meaning: at or close to. A description of a suitable method for testing the suitability of materials to serve as sealingmaterial 18 shown inFIG. 1 is included below in the example. Some suitable sealing materials are also provided below as the results of an experiment. - Together, front and
back mold pieces closure member 16 definecavity 40, which may be characterized as a molding cavity.Cavity 40 comprises an upper half and a lower half, which halves may be symmetrically arranged about a central horizontal axis HH ofmold 10. As shown inFIG. 1 ,mold 10 may be held vertically or at least substantially vertically, or on edge, withcavity 40 extending in the direction of a vertical axis VV, which may be oriented perpendicular to central horizontal axis HH. - Consistent with certain of the present methods, which may be characterized as methods for molding optical lenses, after
mold 10 is provided and preferably oriented vertically (as shown inFIG. 1 ),instrument 50 may be used to puncture sealingmaterial 18 andclosure member 16, thereby forming an opening (e.g., a hole) in sealingmaterial 18, and more specifically in sealingmaterial 18 and inclosure member 16. In one embodiment,instrument 50 may puncture sealingmaterial 18 andclosure member 16 at the lowest point ofmold 10. As shown inFIG. 1 ,instrument 50 may be a needle, such as a hypodermic needle. However, any hollow structure (such as tubing) with a sharp tip may be used forinstrument 50; preferably, the angle of the tip should be between 10 and 80 degrees. - A polymerizable composition may then be introduced into
cavity 40 throughinstrument 50. Suitable polymerizable compositions include polymerizable synthetic compositions, such as room temperature compositions and, in particular, fast curing compositions. Examples of fast curing compositions are compositions that cures within 10 minutes or less, 7 minutes or less, or 4 minutes or less at room temperature. An example of a composition that cures in 10 minutes or less at room temperature is disclosed in U.S. Pat. No. 5,973,098, which is incorporated by reference. Polymerizable compositions that are particularly well-suited for use with certain of the present methods include those that tend to shrink minimally (e.g., preferably less than 15% by volume, and more preferably in the range of 0 to 8% by volume) because minimal shrinkage will lessen the chance of bubble formation during either filling of the mold or curing of the composition. Other suitable polymerizable compositions that may be used are the acrylic ultra-violet polymerizable compositions provided in U.S. Pat. Nos. 5,741,831 and 5,702,825, both of which are incorporated by reference. - The introduction of a polymerizable composition into
cavity 40 throughinstrument 50 may be facilitated through the use of a pumping system. One embodiment of a suitable pumping system is shown inFIG. 1 . Pumpingsystem 62 includes apressure source 54 on the upstream side of astorage vessel 60 containing thepolymerizable molding material 58.Storage vessel 60 may be connected by aconduit 52 toinstrument 50 and applied like a filling nozzle. Pressuresource 54 may be, for example, a compressed air vessel, and may be connected tostorage vessel 60 by aconduit 64 controlled byvalve 56.Valve 56 may be opened and controlled to obtain the desired flowrate ofpolymerizable molding material 58 intocavity 40 progressively from bottom 32 ofmold 10.Valve 56 may be adjusted such thatcavity 40 is fed continuously withpolymerizable molding material 58. For example,valve 56 may be adjusted such thatpolymerizable molding material 58 flows smoothly intocavity 40. A smooth flow may be achieved at a volumetric rate of between 0.4 and 1.3 milliliters/minute. -
FIG. 2 is a front view ofmold 10. As shown inFIG. 2 , a piece ofvent tape 70 may be positioned neartop 30 ofmold 10. The piece of vent tape may be attached toclosure member 16 and cover an opening inclosure member 16. The piece of vent tape may be configured to allow air, but not the polymerizable composition that will fillcavity 40, to pass through it. An example of a suitable material that may be used forvent tape 70 is 3M Venting Tape 394 (available from 3M's Industrial Tape and Specialties Division). A discussion of suitable vent tapes for use with the present methods is found in U.S. patent application Ser. No. 10/212,629, filed Aug. 5, 2002, the inventors of which are James A. Reed and Joseph Boryslawski. This application is incorporated by reference. - After
cavity 40 has been completely filled (i.e., filled to the satisfaction of the operator) with the polymerizable composition,instrument 50 may be retracted fromcavity 40. In one embodiment,mold 10 may then be rotated. This rotation may occur as soon afterinstrument 50 is retracted as possible. The rotation may take place by rotatingmold 10 about its central horizontal axis HH. The rotation may take place in either a clockwise or a counterclockwise direction. The degree of rotation may range from between 0° to 180°, but preferably is 90° or at least approximately 90°. “Approximately” and “substantially” are both defined as at least close to a given value (e.g., preferably within 10% of, more preferably within 1% of, and most preferably within 0.1% of). Thus, “approximately 90 degrees” includes any angle from 81 to 99 degrees, including 81, 82, 83, 84, 85, 86, 87, 88, 89, 90, 91, 92, 93, 94, 95, 96, 97, 98, and 99 degrees, as well as any derivative of any angle between 81 and 99 degrees. “Substantially vertically” includes vertically. - The purpose of the rotation is to reduce or eliminate the possibility that any microbubbles that form within the polymerizable composition after entering the same through the openings in sealing
material 18 andclosure member 16 that remain afterinstrument 50 is removed, or through the openings in piece ofvent tape 70 and closure member 16 (which openings are designed to vent the gas displaced by the polymerizable composition during the filling process) migrate to the central portion of the lens. For example, as shown inFIG. 3 , by rotatingmold 10 in this fashion, anybubbles 110, which may be microbubbles, that form within the polymerizable composition after rotation will migrate along the outermost edge of the polymerizable composition (i.e., near closure member 16) and up to the new top ofmold 10, as shown by the arrows. In this way, bubbles that form in a fast-curing polymerizable composition will remain at the edges of the resulting lens, and will not foul the utility of the central portion of the lens, which is the portion used as the final lens in a pair of eyeglasses. - By contrast, as shown in
FIG. 4 , thebubble 110 that forms near the openings remaining in sealingmaterial 18 andclosure member 16 in the polymerizable composition inmold 10 could migrate to or near the center of the lens as it is curing or being polymerized and remain there once the lens is cured, thereby rendering the cured lens useless. This problem is especially acute in instances where the polymerizable composition cures rapidly, such as on the order of 10 minutes or less at room temperature. - After polymerization is complete,
mold 10 may be disassembled. Because a sealing material is utilized instead of a valve as disclosed in U.S. patent application Ser. No. 09/814,318, no special machining is required to remove a valve from the finished lens. This results in a savings of time and money. - Another of the present methods is a method for evaluating, or testing, the self-sealing nature of a piece of material. The method includes providing a cavity that has an opening over which a piece of material, such as sealing material, is positioned. The cavity may take the form, for example, of the space within a glass tube and the opening may be positioned near the bottom of the tube. The cavity may be partially filled with a liquid, such as water. The piece of material may be punctured with an instrument. The force that it takes to puncture the piece of material may be recorded via a load cell positioned on the instrument. The instrument may be driven with a robotic arm. The recording may take place on a computer with an acquisition card. Suitable forces for puncturing the piece of material being tested include those at or below 30 Newtons (N). A vacuum may be applied to the cavity through, for example, a conduit communicating with the cavity near, for example, the top of cavity. The vacuum may be applied after the instrument—which may, as in the example described above, comprise a needle (such as a hypodermic needle)—is retracted from the cavity. The vacuum may be applied using a venturi and adjusted using a vacuum balance valve. The opening left by the instrument in the piece of material should reduce in size in those materials suitable for use as sealing materials once the instrument is retracted. During the testing, the value of the vacuum (e.g., in inches of mercury) should be noted when, or approximately when, the first microbubble forms near the opening left by the instrument in the piece of material. That vacuum value may then be translated to a pressure value, which is one manner of noting a pressure. Alternatively, a pressure may be noted directly, without the translation from a vacuum value. The best results are obtained when the pressure at which the first bubble forms around gas (such as air) that enters the liquid in the cavity is low.
- Some characteristics of suitable sealing materials include, in one embodiment, the following: good adhesion to the closure member; the ability to be pierced by an instrument with less than 30 N of force; resilience resulting in the material sealing quickly after piercing such that leakage and spillage are minimized or avoided; the ability to withstand a vacuum (i.e., low pressure) and permit only minimal or no gas to pass through the opening formed by the instrument.
- The following example is included to demonstrate a specific embodiment of the present testing methods. It should be appreciated by those of skill in the art that the techniques disclosed in the example that follows represent techniques discovered by the inventors to function in the practice of the present testing methods, and thus can be considered to constitute a specific mode for their practice. However, those of skill in the art should, in light of this disclosure, appreciate that many changes can be made in the specific embodiment that is disclosed, and still obtain a like or similar result without departing from the scope of the present testing methods.
- In order to enable the inventors to screen materials for use as sealing materials, the test set-up shown in
FIGS. 5A and 5B was created. As shown inFIG. 5A ,testing system 100 includesglass site tube 84, which is 6 inches long, has an outer diameter of 0.625 inches and an inner diameter of 0.500 inches. The glass tube permitted the testers to view the water level within the tube (i.e., within the cavity) such that those materials that were inefficient at self-sealing would be apparent (e.g., because the water would leak out and the water level would drop). In addition, the glass tube permitted the testers to view the formation of any bubbles in cases in which the material being tested was not sealing completely against the vacuum applied. The glass tube had an opening at its bottom end, which was covered with a piece of the material to be tested 99. - The piece of material to be tested was pierced by
needle 96, which was a 16-gauge by 1-inch Becton-Dickinson insertion needle.Needle 96 was advanced and retracted usingcylinder 80, which was an Intelligent Actuator Inc. (2690 W. 237th St., Torrance, Calif. 90505) Robot Cylinder, model RCP-RSA1-H-100-S.A load cell 82, which was a GS sensor 2-pound, model XFTC101-M5M-2 (available from GS Sensors Inc.; 24 Rue Des Dames B17 78340 Les Clayes Sous Bois France), was attached toneedle 96 to record the load while piercing. - As shown in
FIG. 5A , a vacuum inlet fitting 86, to which a vacuum source was connected, was in communication withtube 84.Vacuum gauge 88 for measuring a value of the vacuum applied to tube 84 (in inches of mercury) was in communication with vacuum inlet fitting 86.Vacuum balance valve 90 was in communication with the vacuum source, for adjusting the vacuum applied totube 86. - An
electric panel box 94 contained a 24-volt DC power supply for poweringcontroller 95, which comprised an Intelligent Actuator Inc. controller model RCP-C. Usingoperator control box 92, a tester could actuate controller 95 (in preset fashion if desired) to advance and retractneedle 82 usingcylinder 80. All of these components were supported byframe structure 98. - To carry out the testing method, different pieces of material were attached to the bottom of
tube 84, thereby covering its opening.Tube 84 was then filled partially with water. An operator then causedneedle 96 to advance such that the tip of the needle pierced the piece of material. This was done by actuating a button oncontrol box 92. The load force used bycylinder 80 to causeneedle 96 to pierce the piece of material was sensed byload cell 82, and recorded on computer with an acquisition card. In all cases, the value of the piercing load force was less than 30 N. The speed of penetration and the depth of penetration were fixed at 20 millimeters per second and 10 millimeters, respectively. The needle was then retracted by another button oncontrol box 92. - An operator tracked any water loss for 10 minutes. Any tape that leaked at atmospheric pressure was characterized as failing the test. A vacuum was then applied using a series ZH venturi made by SMC Corporation of America (Indianapolis, Ind.) and adjusting
vacuum balance valve 90 to gradually increase the value of the vacuum in inches of mercury. The vacuum value was read onvacuum gauge 88. As the vacuum was adjusted, an operator checked for microbubbles forming at the puncture point ofneedle 96. For a given piece of material, the test was stopped when the first microbubble was seen; at this time, or at approximately this time, the value of the vacuum was also recorded. - The results of this testing appear below in Table 1. The vacuum values that were noted during the test have been converted to pressure values. The different materials screened for use as sealing materials are described by company and model. The column heading “Lowest pressure without bubble apparition (mm Hg)” means the lowest pressure in
tube 84 that was noted prior to the formation of a microbubble in the water in tube 84 (note that normal atmospheric pressure is ˜760 mm Hg). -
TABLE 1 Lowest pressure Leaking without after bubble Thickness needle apparition Company Model (mm) Structure retraction (mm Hg) 1 Secon PN4701-40 3.18 Foam Yes 735 Rubber and Plastics 2 Kapco Co. VHB4910 3.18 Foam Yes 735 3 Industrial ⅛″ foam tape 3.18 Foam Yes 735 Tape 4 Carolina ⅛″ foam tape 3.18 Foam Yes 735 Tape Co. 5 Saint-Gobain N4704 3.18 Foam Yes 735 Co. 6 Adchem 4423-60 3.18 Foam Yes 735 Corp. 7 Saint-Gobain N4504 3.18 Foam Yes 735 Co. 8 Adhesive Arclad 561 6 mils Non-foam Yes 735 Research 9 Tape-Rite closed cell 3.18 Foam Yes 735 Co. rubber 10 New #3120 3.18 Foam Yes 735 Dimension W/GRC-700 & RB PSA 1- Side 11 Stik II ½″ foam tape 12.70 Foam Yes 735 Products 12 R. H. Hughes PH4992 0.79 Neoprene No 735 Co. neoprene 13 3M Co. Can- ⅛″ foam tape 3.18 Foam Yes 735 Do Tapes 14 3M VHB 4618 0.90 Foam Yes 735 15 Tape-Rite ⅛″ foam tape 3.18 Foam Yes 735 Co. Inc. 16 Adchem ⅛″ foam tape 4.18 Foam Yes 735 Corp. 17 Nott Co. Silicone 303.18 Silicone No 75 Durometer ⅛″ thick 18 Nott Co. Silicone 301.59 Silicone No 630 Durometer ⅛″ thick 19 Nott Co. Neoprene 303.18 Neoprene No 75 Durometer 1/16″ thick 20 Nott Co. Neoprene 301.59 Neoprene No 75 Durometer 1/16″ thick 21 3M 8300 2.00 Non-foam No 735 22 Aero Rubber PN 3.18 Rubber No 735 Co. S0034213308 23 Carolina ⅛″ foam tape 3.18 Foam Yes 735 Tape 24 Avery UHA3099 2.00 Acrylic No 735 25 3M 8500T-0125 2.00 Acrylic No 75 26 3M 8100 2.00 Acrylic No 505 - A polymerizable composition was prepared from two pre-polymers. Different materials were then tested for use as sealing materials in the creation of lenses from the polymerizable composition.
- The two pre-polymers were prepared according to following procedure, which is described fully in U.S. patent application Ser. No. 10/012,727, filed Nov. 5, 2001 by Gabriel Keita, Joey 0. Obordo, Pamela Anne McClimans, and Yusef Turshani, and which is incorporated by reference:
- Part A—NCO
- A reactor equipped with a condenser, a thermal probe, and an agitator was charged with a determined amount of xylylene diisocyanate (XDI). The monomer XDI was heated to 115° C. Next, 3-(2-sulfanylethylthio)-2-(2-sulfanlethylthio)propane 1-thiol was introduced and mixed with polyisocyanate in amounts such that the molar ratio of isocyanate functions to the thiol function
-
- was 8:1.
- The reaction was complete after 3 to 4.5 hours. The final Part A prepolymer with isocyanate end groups had a viscosity at 25° C. of 0.071 Pascal seconds (Pa.s).
- Part B—SH Ending
- The reactor was charged with a determined amount of 3-(2-sulfanylethylthio)-2-(2-sulfanlethylthio)propane 1-thiol. That monomer was heated to 90° C. Next, xylylene diisocyanate was introduced and mixed with polythiol in amounts such that the molar ratio of thiol functions to the isocyanate function
-
- was 8:1.
- The reaction was complete after 3 hours. The final Part B prepolymer with thiol end groups was cooled to 35° C. and had a viscosity of 0.543 Pa.s at 25° C.
- A catalyst solution was added to 10,000 grams (g) of part B. The catalyst solution was made of the following: 71.88 g of 18-crow-6 ether; 17.97 g of potassium thiocyanate (KSCN); and 119.8 of thioethanol.
- Part A and Part B (plus the catalyst solution) were then dispensed through two metering gear pumps at a volume ratio of A/B=1.18. The two parts were then blended together using a dynamic mixer.
- After the polymerizable composition was created, a molding cavity created in accordance with
cavity 40 inFIG. 1 was filled in the manner shown inFIG. 1 . That is, a hypodermic needle was used to puncture, from the bottom, a material attached to a closure member made of Barnier tape reference no. 8055. The polymerizable composition was introduced into the molding cavity at a rate of approximately 2 grams/second. A lens was obtained after 10 minutes at room temperature and one hour of curing at 120° C. The lens was then visually inspected with a high-intensity lamp (an arc lamp) for the presence of bubbles or microbubbles. - This process was used to create many different lenses, and different materials were tested. The results, including the materials used and the number of lenses created, are provided below in Table 2. The vacuum values that were converted to the pressure values provided below were measured using the series ZH venturi identified above in Example 1. The heading “Percentage of lenses with microbubbles” indicates the percentage of lenses created in which microbubbles were formed. As the data in Table 2 shows, there was a good correlation between the “Lowest pressure” values and the percentage of microbubbles found: that is, the lower the pressure value, the lower the percentage of microbubbles found. Certain lenses were rotated 90 degrees after filling as described above, and this even further reduced the percentage of lenses in which microbubbles were formed.
- The inventors have found that the materials best suited for use as sealing materials are those that resulted in no more than 10% of lenses with microbubbles, whether the lenses were rotated 90° after filling or not.
-
TABLE 2 Lowest pressure 90° Total without Leaking rotation number Percentage of bubble after after of lenses lenses with apparition needle Material filling created microbubbles (mm Hg) retraction 1 3M 8500T-0125 No 150 9 75 No 2 3M 8100 No 625 22.3 505 No 3 Nott Co No 225 28 630 No Silicone 30 Durometer 1/16″ thick 4 Avery No 775 28 735 No UHA3099 5 Aero Rubber No 950 37.4 735 No Co. PN S0034213308 tape 6 Aero Rubber Yes 450 3.3 735 No Co. PN S0034213308 tape 7 3M 8500T-0125 Yes 3000 0 75 No - Materials capable of withstanding a cavity pressure that is less than or equal to 505 millimeters of mercury or less are examples of materials suitable for use with the present methods. The same is true for materials capable of withstanding a cavity pressure that is less than or equal to: 450 millimeters of mercury or less, 400 millimeters of mercury or less, 350 millimeters of mercury or less, 300 millimeters of mercury or less, 250 millimeters of mercury or less, 200 millimeters of mercury or less, 150 millimeters of mercury or less, and 100 millimeters of mercury or less. Materials capable of withstanding pressures greater than or equal to 75 millimeters of mercury and less than or equal to 505 millimeters of mercury also are suitable for use with the present methods. The same is true of materials capable of withstanding pressures: greater than or equal to 100 millimeters of mercury and less than or equal to 450 millimeters of mercury, greater than or equal to 150 millimeters of mercury and less than or equal to 400 millimeters of mercury, greater than or equal to 200 millimeters of mercury and less than or equal to 350 millimeters of mercury, and greater than or equal to 250 millimeters of mercury and less than or equal to 300 millimeters of mercury.
- It is believed that, based on the test results above in Tables 1 and 2, materials capable of withstanding pressures greater than or equal to 10 millimeters of mercury and less than or equal to 505 millimeters of mercury also are suitable for use with the present methods.
Claims (15)
1. A method comprising:
providing a cavity having at least one opening over which a piece of sealing material is positioned, the cavity containing liquid;
puncturing the piece of sealing material with an instrument, thereby creating a sealing material opening for a period of time;
applying a vacuum to the cavity; and
noting a cavity pressure approximately when a first bubble forms around gas entering the liquid through the sealing material opening from outside the cavity.
2. The method of claim 1 , where the cavity pressure is greater than or equal to 10 millimeters of mercury and less than or equal to 505 millimeters of mercury.
3. The method of claim 1 , where the cavity pressure is greater than or equal to 75 millimeters of mercury and less than or equal to 505 millimeters of mercury.
4. The method of claim 1 , where the cavity pressure is less than or equal to 505 millimeters of mercury.
5. The method of claim 1 , further comprising:
retracting the instrument from the piece of sealing material; and
where the sealing material opening possesses a size that decreases after the instrument is retracted.
6. The method of claim 1 , where the providing comprises:
providing a cylinder having a sealed top opening, a bottom opening, an inner wall defining a cavity, and a piece of sealing material positioned over the bottom opening.
7. The method of claim 1 , where the instrument is controlled using a robot.
8. The method of claim 1 , where the method is a method for testing the utility of a piece of sealing material for a lens molding operation, and where the method further comprises:
repeating the providing, puncturing, applying, and noting for at least a second piece of sealing material; and
selecting a piece of sealing material among those tested for use in the lens molding operation.
9. The method of claim 8 , where the piece of sealing material includes silicone and the second piece of sealing material includes neoprene.
10. The method of claim 1 , further comprising:
tracking any liquid loss through the sealing material opening.
11. The method of claim 1 , where the applying a vacuum comprises applying a vacuum using a venturi.
12. The method of claim 1 , where the providing comprises:
providing a cylinder having a sealed top opening, a bottom opening, an inner wall defining a cavity, and a piece of sealing material positioned over the bottom opening, and where the at least some liquid is introduced into the cavity after the piece of sealing material is positioned over the bottom opening.
13. The method of claim 1 , where the piece of sealing material comprises silicone.
14. A method of evaluating the self-sealing nature of a piece of material, the method comprising:
piercing a piece of material with an instrument, the piece of material being positioned over an opening to a cavity containing liquid, the piercing creating a puncture opening;
retracting the instrument from the piece of material;
applying a vacuum to the cavity; and
noting a cavity pressure approximately when a first bubble of gas from outside the cavity forms within the liquid near the puncture opening.
15-33. (canceled)