US20090061154A1 - Metallic-Colored Thermoplastic Molding Material - Google Patents
Metallic-Colored Thermoplastic Molding Material Download PDFInfo
- Publication number
- US20090061154A1 US20090061154A1 US12/263,714 US26371408A US2009061154A1 US 20090061154 A1 US20090061154 A1 US 20090061154A1 US 26371408 A US26371408 A US 26371408A US 2009061154 A1 US2009061154 A1 US 2009061154A1
- Authority
- US
- United States
- Prior art keywords
- molding material
- glitter
- molded body
- metal
- flow lines
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The invention relates to a metallic-colored thermoplastic molding material, which contains metal glitter in various admixtures. In addition, the invention relates to a method to manufacture this molding material and its use in molded bodies with openings. No visible formation of flow lines occurs with the use of this molding material, so that the quality of the goods manufactured is improved. For this purpose, it is planned that the percentage by weight of the metal glitter in the thermoplastic molding material lies between six and 15%, wherein the size of the glitter is not in a Gaussian distribution, but the molding material to a large extent contains only equally sized glitter particles in glitter mixtures.
Description
- This application is a divisional patent application of U.S. patent application Ser. No. 10/495,099, filed Jan. 21, 2005, now U.S. patent Ser. No. ______, granted ______, and related to prior PCT Patent Application PCT/EPO1/12906, filed Nov. 8, 2001, and claims priority to and incorporates the aforesaid priority applications in their entireties by reference thereto.
- 1. Field of the Invention
- The invention relates to a metallic-colored thermoplastic molding material containing metal glitter in various admixtures.
- In addition, the invention relates to a method for manufacturing this molding material and use of a molding material according to the invention to manufacture molded bodies.
- Metallic-colored thermoplastic molding materials are used, for example, in situations where plastics have displaced metal components, but for reasons of design it is important that the optical appearance of the molded bodies be adapted to the metallic structure of the former metallic components.
- 2. Background of the Prior Art
- In principle, this adaptation can be accomplished in two ways: First, by using an expensive and costly subsequent coloration coating of the molded parts or, second, by using a molding material that already has the desired color effect. The second approach is preferred for economic and ecological reasons.
- Such a metallic-colored thermoplastic molding material, from which the invention departs as prior art, is known from DE 197 28 914 A1.
- What is disadvantageous in the molding material described there is that it tends to form visible flow lines during processing using the injection molding method, particularly when complicated molded parts with openings are manufactured. These flow lines impair the uniform perception of color and produce qualitatively poor molded part surfaces. As a result, not just the quality but also the usability of the molded piece is diminished.
- The objective of the invention is to disclose a molding material with whose use this undesirable formation of flow lines does not occur, in order to thereby improve the quality of the goods manufactured. In addition, an objective of the invention is to disclose a method with which molding materials can be manufactured in which the final product manufactured from it is free of flow lines. Finally, an objective of the invention is to disclose a molded body with openings whose flow lines are not visible.
- This objective is attained by the present invention in that the percentage by weight of metal glitter in the metallic-colored thermoplastic molding material is greater than 5% and less than or equal to 15%. In an especially advantageous embodiment of the invention, the percentage by weight of metal glitter in the metallic-colored molding material is preferably greater than 6%, in particular the percentage lies between 6% and 13%. Surprisingly, molded bodies that are fabricated from this type of molding material with a considerably increased percentage of metal glitter have no visible flow lines. At the same time, the mechanical properties are advantageously retained.
- In a preferred embodiment of the invention, the molding material contains hexagonal metal glitter. The metal-glitter admixture is advantageously any mixture of square, rectangular and hexagonal metal glitters. As a result, the shape of the metal glitter is better adapted to naturally occurring crystalline lattice structures.
- These metal glitters are coated in another embodiment of the invention, in order to intensify bonding to the base material and improve mechanical properties.
- The objective is also attained in that, in an especially favorable embodiment of the invention, the molding material of this type contains a metal-glitter admixture whose edge-length distribution is not a Gaussian distribution.
- It is advantageous if this distribution is at least monomodal, preferably bimodal or multi-modal, whereby “modal” in the sense of the invention means that only metal glitter particles of almost the same size and shape are present. Surprisingly, these types of admixtures produce a situation where the flow lines that are inevitably present no longer emerge optically in the final product and are therefore not visible.
- In another embodiment of the invention, the base material for the thermoplastic molding material is composed of polyamide, which preferably contains reinforcing materials, in particular fibers and/or fillers. These types of base materials, which are advantageously mechanically, chemically and thermally resistant, also surprisingly do not form any visible flow structures even in the case of fiber reinforcement, although they otherwise tend to do so in the case of fibers.
- The objective of manufacturing a metallic-colored thermoplastic molding material is attained according to the method by incorporating the metal glitter into the molding material, preferably by using a screw extruder at an admixing point that lies at a ratio of screw length to screw diameter of greater than 5 and less than 60, preferably between 20 and 50, in particular at 40. As a result, the specific energy input that occurs when compounding the molding material is so limited that the admixture of the metal glitter occurs non-destructively while maintaining the at least monomodal edge length distribution as well as maintaining a complete blending of base material and metal glitter, which allows the final product to appear free of flow lines.
- Surprisingly, the use of a molding material according to the invention when manufacturing complicated molded bodies, in particular those with openings, leads to the formation of a uniform surface of the molded body. The formation of visible flow lines does not occur.
- Finally, the objective is attained by a molded body that is composed of a molding material according to one of Claims 1 through 10.
- The invention will be explained, by way of example on the basis of the following example embodiment:
- A polyamide, preferably the applicant's ALCOM™ 6 PA 900/8 GF 10 MR 20 silver metallic 12-778 FF, is used as the base material. The filler system is composed of a 30% hybrid system. This granulate is melted in a double-screw extruder in a known manner at the prescribed temperature, whereby kneading and mixing zones are also normally provided in the double-screw extruder.
- The metal-glitter admixture is composed of various aluminum glitters, wherein the edge length of the glitter is between approximately 100 and 200 μm and its thickness lies between 16 and 54 μm. The metal glitter is added in the flow direction after the kneading and mixing zones. The addition takes place at an admixing point that lies at a ratio of screw length to screw diameter of 35. The temperature of the screw extruder in this process is between approx. 280 and 320° C., in order to guarantee complete and homogenous incorporation of the metal-glitter admixture.
- The molding material obtained in this manner is then cooled in a quenching bath and formed into the shape to be used for subsequent use, for example, granulated.
- This granulate is melted in an injection molding machine and injected through nozzles into a hollow mold that defines the final product. The molded body obtained after cooling features a uniform surface structure; flow lines do not emerge optically and are therefore not visible.
Claims (10)
1. A method for manufacturing a metallic-colored thermoplastic molded body of molding material, said method comprises incorporating metal glitter into the molding material, and then extruding the thermoplastic molding material using a screw extruder at an admixing point, which admixing point lies at a ratio of screw length to screw diameter of greater than 5 and less than 60.
2. The molded body produced according to the method of claim 1 , said molded body being formed with at least one opening, and said molded body being free of flow lines.
3. The method of claim 1 , wherein the screw length to screw diameter ratio is between 20 and 50.
4. The method of claim 1 , said molding material comprises metal glitter in various admixtures, said glitter comprises a square or rectangular shape and having an edge-length distribution of 0.05 to 1 mm, and a characterized in that the percentage by weight of metal glitter in the molding material is greater than 5% and less than or equal to 15% and further characterized in that the edge-length distribution of the metal glitter is not a Gaussian distribution characterized in that the edge length distribution is multi-modal.
5. The method of claim 4 , said molding material comprises a polyamide as a base material.
6. The method of claim 4 , said molding material further comprises reinforcing materials comprising fibers and/or fillers.
7. The molded body produced by the method claim 1 , said molded body comprises a metallic-colored thermoplastic molding material comprising metal glitter, said metal glitter comprises a square or rectangular shape, with an edge-length distribution of 0.05 to 1 mm, and characterized in that the percentage by weight of metal glitter in the thermoplastic molding material is greater than 5% and less than or equal to 15%, and wherein the molded body has no visible flow lines.
8. The molded body of claim 7 , said molded body comprises forming an orifice and said portion has no visible flow lines.
9. The method of claim 1 , said thermoplastic molding material comprises metal glitter configured in a square or rectangular shape with an edge-length distribution of 0.05 to 1 mm, characterized in that the percentage by weight of metal glitter in the thermoplastic molding material is greater than 5% and less than or equal to 15%, and wherein the molded body has no visible flow lines.
10. The method of claim 9 , said method comprises molding a portion forming an orifice, said orifice portion has no visible flow lines.