US20100255379A1 - Battery plate - Google Patents
Battery plate Download PDFInfo
- Publication number
- US20100255379A1 US20100255379A1 US12/816,873 US81687310A US2010255379A1 US 20100255379 A1 US20100255379 A1 US 20100255379A1 US 81687310 A US81687310 A US 81687310A US 2010255379 A1 US2010255379 A1 US 2010255379A1
- Authority
- US
- United States
- Prior art keywords
- grid
- battery
- lead
- alloy
- battery plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A battery grid includes a grid network bordered by a frame element and includes a plurality of spaced apart grid wire elements. Each grid wire element has opposed ends joined to one of a plurality of nodes to define a plurality of open spaces in the grid network. In various embodiments, at least a portion of a plurality of the grid wire elements are deformed such that the deformed grid wire elements have a first transverse cross-section at a point intermediate their opposed ends that differs from a second transverse cross-section taken at least one of their opposed ends. In various embodiments, the battery grid also includes a lead alloy coating applied to the battery grid, and a battery paste applied to the battery grid.
Description
- This application is a Continuation of U.S. patent application Ser. No. 12/135,903, filed Jun. 9, 2008 and currently pending, which is a Continuation of U.S. patent application Ser. No. 10/996,168, now U.S. Pat. No. 7,398,581, filed Nov. 23, 2004, which is a Divisional of U.S. application Ser. No. 09/755,337, now U.S. Pat. No. 6,953,641, filed Jan. 5, 2001, each of which are incorporated herein by reference in their entirety.
- The present application relates to the modification of battery grids of the type used in lead-acid storage batteries, and more particularly, it relates to a modification of the surface finish of the battery grids of a lead-acid storage battery to improve paste adhesion and the service life of the battery.
- Lead-acid storage batteries typically comprise several cell elements which are encased in separate compartments of a container containing sulfuric acid electrolyte. Each cell element includes at least one positive plate, at least one negative plate, and a porous separator positioned between each positive and negative plate. The positive and negative plates each comprise a lead or lead alloy grid that supports an electrochemically active material. The active material is a lead based material (i.e., PbO, PbO2, Pb or PbSO4 at different charge/discharge stages of the battery) that is pasted onto the grid. The grids provide an electrical contact between the positive and negative active materials which serves to conduct current.
- Lead-acid battery manufacturing technologies and materials have improved in the last few decades. For example, because pure lead may be too soft for the manufacturing processes used to form battery grids, various alloying elements have been added to lead over the years to produce battery grids of sufficient strength to withstand battery manufacturing processes. For example, antimony was added to lead as lead-antimony alloys were found to be capable of being formed into battery grids at acceptable commercial rates by way of gravity casting techniques. However, it was discovered that when a lead antimony alloy is used in battery grids, water loss occurs because of gassing. Therefore, batteries having lead-antimony grids required periodic maintenance, i.e., the addition of water to the battery.
- In order to lower the gassing rate of batteries, lead-calcium battery grids were developed. Batteries using lead-calcium alloy grids have relatively low gassing rates, and therefore, do not require the addition of water.
- Another development in lead-acid battery manufacturing has been the manufacturing of battery plates in a continuous process, instead of traditional methods in which battery grids are made using a conventional gravity cast book mold operation and the cast grids are later pasted in a separate step. In a typical continuous battery plate making method, a lead alloy strip is manufactured, either by casting (namely, cast strip) or by casting and rolling (namely, wrought strip), and the strip is subsequently expanded or punched to generate the desired grid pattern in a strip of interconnected battery grids.
- Typically, lead alloys having a relatively high level of calcium are used in continuous grid making processes as higher calcium levels tend to increase the hardness of the battery grids, which is beneficial in punching and expansion processes. Previously prepared active material battery paste (which may be prepared by mixing lead oxide, sulfuric acid, water, and optionally dry additives, such as fiber and expander) is then applied to the strip of interconnected battery grids and the strip is parted into single battery plates. Advantages of continuous battery plate making are improved production rate, improved dimensional control, thinner plates, lower scrap rate and lower manufacturing costs.
- The pasted plates are next typically cured for many hours under elevated temperature and humidity to oxidize free lead (if any) and adjust the crystal structure of the plate. After curing, the plates are assembled into batteries and electrochemically formed by passage of current to convert the lead sulfate or basic lead sulfate(s) to lead dioxide (positive plates) or lead (negative plates). This is referred to as the “formation” process.
- It is well known that lead-acid batteries will eventually fail in service through one or more of several failure modes. One such failure mode is failure due to corrosion of the grid surface. Electrochemical action corrodes the grid surface and reduces the adhesion between the active material and the grid (e.g., failure of the battery occurs when the grids are no longer able to provide adequate structural support or current flow due to the separation of the active material from the grid).
- The formation efficiency of lead-acid batteries also may depend on the positive plate, in particular, to the extent of conversion of lead monoxide (PbO) to lead dioxide (PbO2) in the active positive material. The high electrical potential required for formation appears to be related to the transformation of non-conductive paste materials to PbO2. A low formation efficiency of positive plates requires a high formation charge. Inefficient charging also leads to deficiencies in the resulting batteries assembled with such plates. Typically, the initial capacity (performance) of the battery is low if the battery is not completely formed, requiring additional cycling to reach specific performance values. It is believed that by increasing the adhesion between the paste mixture and the grid, formation efficiency can be improved. Among other things, the increased adhesion between the grid and the paste provides for improved interfacial contact between the grid and paste thereby improving current flow between the grid and paste.
- There is a need in the battery manufacturing field for even more effective methods for improving the service life of a battery. More particularly, there is a need for a method that can more greatly increase the adherence of active material to a battery grid produced by a continuous process.
- The present invention relates to a method of making a plurality of battery plates that includes forming a strip including a plurality of battery grids. Each battery grid includes a grid network bordered by a frame element and includes a plurality of spaced apart grid wire elements. Each grid wire element has opposed ends joined to one of a plurality of nodes to define a plurality of open spaces in the grid network. The method also includes deforming at least a portion of a plurality of the grid wire elements such that the deformed grid wire elements have a first transverse cross-section at a point intermediate their opposed ends that differs from a second transverse cross-section taken at least one of their opposed ends. The method also includes applying a lead alloy coating to the strip, applying battery paste to the strip, and cutting the strip to form a plurality of battery plates.
- The present invention also relates to a method of making a plurality of battery plates that includes melting a lead alloy grid material and continuously casting the grid material to form a continuous strip. The method also includes punching grid material out of the strip to form interconnected battery grids, each interconnected battery grid including a grid network bordered by a frame. The grid network includes a plurality of spaced apart grid wire elements. Each grid wire element includes opposed ends, each opposed end being joined to one of a plurality of nodes to define a plurality of open spaces in the grid network. The method also includes deforming a portion of a plurality of the grid wire elements such that a first transverse cross-section intermediate its opposed ends differs from a second transverse cross-section taken at least one of its opposed ends. The method also includes applying a lead alloy coating to the interconnected battery grids and cutting the interconnected battery grids to form a plurality of battery plates.
- The present invention also relates to a method of making a plurality of battery grids that includes forming a strip of interconnected battery grids from a lead alloy grid material, each interconnected battery grid including a grid network bordered by at least one frame element. The grid network includes a plurality of spaced apart grid wire elements, each grid wire element having opposed ends. The method also includes deforming a portion of a plurality of the grid wire elements such that a first transverse cross-section intermediate its opposed ends differs from a second transverse cross-section taken at least one of its opposed ends. The method also includes applying a lead alloy coating to the strip of interconnected battery grids and cutting the strip to form a plurality of battery plates.
-
FIG. 1 shows a battery grid made in accordance with an exemplary embodiment. -
FIG. 2 shows a cross-section of a grid wire section taken along line 2-2 ofFIG. 1 . -
FIG. 3 shows a cross-section of a grid wire section taken along line 3-3 ofFIG. 1 . -
FIG. 4 shows a cross-section of a grid wire section taken along line 4-4 ofFIG. 1 . -
FIG. 5 shows a cross-section of a grid wire section taken along line 5-5 ofFIG. 1 . -
FIG. 6A shows a cross-section of a grid wire section taken along line 6-6 ofFIG. 1 . -
FIG. 6B shows a cross-section of a grid wire section without an alloy coating taken along line 6-6 onFIG. 1 . -
FIG. 6C shows a cross-section of a grid wire section having a partial alloy coating taken along the line 6-6 ofFIG. 1 . -
FIG. 7A is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 7B is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 7C is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 7D is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 8A is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 8B is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 8C is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 8D is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 9A is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 9B is a schematic illustration of an apparatus for producing a battery grid according to an exemplary embodiment. -
FIG. 1 shows a front view of a battery grid made in accordance with an exemplary embodiment. The grid is a stamped grid made of a lead alloy grid material coated with a lead alloy, and functions in the same manner as other battery grids known in the art. It should be noted that an infinite number of grid designs may result from the present invention and therefore, it is not the intent of the following description to limit the invention to the grid design shown inFIG. 1 , which is presented for the purposes of illustration. - Referring now to
FIG. 1 , thegrid 10 comprises a frame that includes atop frame element 12, first and secondside frame elements 14 and 16, and abottom frame element 18. Thegrid 10 includes a series of grid wires that defineopen areas 20 that hold the electrochemical paste (not shown) that provides the current generation. Acurrent collection lug 22 is integral with thetop frame element 12 and is offset from the center of thetop frame element 12. Thetop frame element 12 includes an enlargedconductive section 24 directly beneath thelug 22, and has the shape shown to optimize current conduction to thelug 22. - A series of radially extending vertical
grid wire elements 26 a-26 o form part of thegrid 10. Thevertical wire elements 26 c-26 n are connected to thetop frame element 12 and thebottom frame element 18, thevertical wire elements 26 a-26 b are connected to thetop frame element 12 and to the first side frame element 14, and the vertical wire element 26 o is connected to thetop frame element 12 and theside frame element 16, as shown. Thevertical wire element 26 i is parallel to theside elements 14 and 16, and the remainingvertical wire elements 26 a-26 h and 26 j-26 o extend radially toward an imaginary intersecting point along a radius line running through thevertical element 26 i. Thevertical wire elements 26 a-26 o become closer together when moving from thebottom element 18 towards thetop element 12 and get farther apart when moving towards the left element 14 or theright element 16 from thevertical element 26 i. - The
grid 10 also includes a plurality of horizontal or cross wire elements. The cross wire elements include a set of parallelhorizontal wire elements 30 positioned in a middle portion of thegrid 10. Additionally, thegrid 10 includes a first set ofcross wire elements 32 connected between the left frame element 14 and thevertical element 26 a that are parallel to each other, a second set ofcross wire elements 34 connected between thevertical elements 26 a and 26 b that are parallel to each other, and a third set ofcross wire elements 36 connected between thevertical elements 26 b and 26 c that are parallel to each other at the left side of thegrid 10. Also, thegrid 10 includes a fourth set ofcross wire elements 38 connected between thevertical elements 26 n and 26 o that are parallel to each other and a fifth set ofcross wire elements 40 connected between the vertical element 26 o and theright frame element 16 that are parallel to each other at the right side of the grid, as shown. A series ofshort support wires 42 are connected to thebottom frame member 18 as shown. - Individual sections of the
vertical wire elements 26 a-26 o and thehorizontal wire elements 30 or the cross wire elements 32-40 have opposed ends 43 which are joined at a plurality ofnodes 44 that define theopen areas 20 that support the electrochemical paste for conduction. - The grid wire cross-sections shown in
FIGS. 2-6A illustrate versions of a grid wire section formed by various exemplary embodiments described below. In the battery grid, each grid wire section may have a different cross-sectional configuration, or each grid wire section may have the same cross-sectional configuration. It is also important to note that although certain features have been illustrated inFIGS. 2-6A by way of cross-sectional views of vertical grid wires, the same cross-sectional views could apply when taking a cross-section of horizontal grid wires. In other words, the similar deformation methods as illustrated inFIGS. 2 to 6A can also be applied to the horizontal wire elements. Depending on the needs, a grid can be deformed at the vertical wire elements only, or at both the vertical and horizontal wire elements, or not deformed at any of the wire elements. -
FIG. 2 shows a cross-section of a section ofvertical wire element 26 h taken at a position between the opposed ends of the grid wire section. It can be seen that at the position between the opposed ends of this grid wire section, the cross-section of the grid wire includes a grid wire base 90 a which is substantially an octagon, and an alloy coating 92 a. Also shown in phantom at 93 is the interface between the grid wire base 90 a and the alloy coating 92 a below the opposed flatplanar surfaces 33 of the grid. It can be appreciated by those in the art that a battery grid wire section or node will not have a perfect geometric configuration and that the rounding of edges and corners of a grid wire section, base, coating surface, or node is often the result of a manufacturing operation. For this reason, the description of cross-sectional shapes in the specification will be proceeded by the word “substantially” to indicate that the cross-sectional shape may vary somewhat from a perfect geometric shape. -
FIG. 3 shows a cross-section of a section ofvertical wire element 26 i taken at a position between the opposed ends of the grid wire section. It can be seen that at the position between the opposed ends of this grid wire section, the cross-section of the grid wire includes a grid wire base 90 b has been rotated 45 degrees in relation to the node and has a substantially rectangular cross-section. The cross-section of the grid wire also shows an alloy coating 92 b. Also shown in phantom at 93 is the interface between the grid wire base 90 b and the alloy coating 92 b below the opposed flatplanar surfaces 33 of the grid. -
FIG. 4 shows a cross-section of a section of vertical wire element 26 j taken at a position between the opposed ends of the grid wire section. It can be seen that at the position between the opposed ends of this grid wire section, the cross-section of the grid wire includes agrid wire base 90 c which is substantially a hexagon and analloy coating 92 c. Thegrid wire base 90 c has opposed surfaces which are coplanar with the surface of the adjacent nodes. Also shown in phantom at 93 is the interface between thegrid wire base 90 c and thealloy coating 92 c below the opposed flatplanar surfaces 33 of the grid. -
FIG. 5 shows a cross-section of a section ofvertical wire element 26 k taken at a position between the opposed ends of the grid wire section. It can be seen that at the position between the opposed ends of this grid wire section, the cross-section of the grid wire includes agrid wire base 90 d which is substantially a diamond and analloy coating 92 d. Also shown in phantom at 93 is the interface between thegrid wire base 90 d and thealloy coating 92 d below the opposed flatplanar surfaces 33 of the grid. -
FIG. 6A shows a cross-section of a section of vertical wire element 26 l taken at a position between the opposed ends of the grid wire section. This figure shows the configuration of a conventional stamped battery grid wherein the cross section of the node and the cross-section at all positions along the grid wire section are substantially rectangular and the surfaces of the node and grid wire section (which includes a grid wire base 90 e) include an alloy coating 92 e. Also shown in phantom at 93 is the interface between the grid wire base 90 e and the alloy coating 92 e below the opposed flatplanar surfaces 33 of the grid. -
FIG. 6B shows another version of the cross-section of a section of vertical wire element 26 l taken at a position between the opposed ends of the grid wire section wherein the grid does not include an alloy coating. It can be seen that the cross-section of the node and the cross-section at all positions along the grid wire section are substantially rectangular and the cross-sectional area of each grid wire does not extend above or below opposed flatplanar surfaces 33 of the grid. -
FIG. 6C shows yet another version of the cross-section of a section of vertical wire element 26 l taken at a position between the opposed ends of the grid wire section. In this cross-section of the grid wire, there is shown agrid wire base 90 g and analloy coating 92 g. Thealloy coating 92 g is disposed on the flatplanar surfaces 33 of the grid; however, no alloy coating is present on surfaces 91 g of the grid wire element that are transverse to the flat planar surfaces 33. - One advantage of the battery grid construction shown in
FIGS. 2-6A can be best understood with reference toFIGS. 6A and 6B .FIG. 6A shows the configuration of a conventional stamped battery grid that has been coating with an alloy coating 92 e after stamping. The cross section of the node and the cross-section at all positions along the grid wire section comprising the grid wire base 90 e are substantially rectangular. However, the surface of the alloy coating 92 e is slightly rounded at the regions near the four corners of the grid wire base 90 e. When applying battery paste to a grid as inFIG. 6A , the slightly rounded grid wires allow the paste to flow around the wire. The rough surface of the wires provide a mechanical graft and interlock of paste particles. Therefore, the contact between the grid and the battery paste is good and the plate is strong. -
FIG. 6B shows the configuration of a conventional stamped battery grid wherein the cross section of the node and the cross-section at all positions along the grid wire section 90 f are substantially rectangular. When applying battery paste to a grid as inFIG. 6B , it is much more difficult to make good contact between the battery paste and the surface of the wire moving in a direction perpendicular to the direction in which the paste is applied because the flow of paste must change in a 90 degree step. This is analogous to the situation where water flows down a 90 degree cliff, and the surface right below the edge of the cliff is not contacted by the falling water. With a grid wire orientation other than 90 degrees, the change of paste flow is gradual and continuous and therefore, provides better paste coverage. When the battery paste is cured and dried, it will shrink and generate tensile force at the paste/grid interface. The tensile force at the paste/grid wire interface is at a maximum when the wire surface is perpendicular to the grid surface and at a minimum when the wire surface is parallel to the grid surface. As a result, a gap is formed between the grid wire and the paste at the location where the tensile force is the maximum. Because of a lack of contact between the paste and the grid, a battery made with this type of plate is much more difficult to form, performs poorly in certain reserve capacity tests, and does not exhibit satisfactory cycle life. - In
FIG. 7A , there is shown one apparatus, indicated generally at 50, for forming a battery grid according to an exemplary embodiment. Theapparatus 50 includes aheated lead pot 61 a, which contains themolten lead alloy 62 that forms the base of the battery grids, and an internally cooled rotating casting drum 63. In operation, themolten lead alloy 62 contacts the cooled drum surface and freezes to form a solidlead alloy strip 65 of substantially constant width and thickness. Thelead alloy strip 65 may optionally be rolled byrollers 64 to change the thickness and grain structure of thestrip 65. Thecontinuous strip 65 is then fed into a punchingstation 71 wherein a series of interconnected battery grids is formed by punching grid material out of thecontinuous strip 65. - During punching operations in the punching
station 71, thestrip 65 is maintained as a continuous strip and preferably the interconnected battery grid shapes and formed in a progressive punching operation, i.e., features are added to the battery grid through several punching operations. The punchingstation 71 may form a strip of interconnected battery grids, each of which has a configuration such as that shown inFIG. 1 . - After the strip exits the punching
station 71, the battery grid wire sections of the strip may optionally be processed in a coiningstation 73. The coiningstation 73 is used to deform or coin the grid wires so that the grid wires have a cross-section similar to one of the grid wire cross-sections 90 a, 90 b, 90 c or 90 d shown inFIGS. 2-5 . For instance, the coiningstation 73, may include a die or dies that deform the rectangular cross-section of the grid wires of the punched grid into an octagonal cross-section 90 a as shown inFIG. 2 . The other exemplary wire cross-sections shown inFIGS. 3-5 may also be formed. The strip of punched (and optionally, coined)interconnected battery grids 74 exiting the punching station 71 (and optionally, the coining station 73) is fed through analloy coating bath 76 that contains amolten lead alloy 77 to form a strip of alloy coatedinterconnected battery grids 79. The length of thealloy coating bath 76 may vary with the composition of themolten lead alloy 77, the thickness of the alloy coating to be deposited, and the rate at which the strip of punchedinterconnected battery grids 74 moves through thealloy coating bath 76. The strip of alloy coatedinterconnected battery grids 79 is then fed through a quenchbath 83 containing quench fluid 84 (preferably water) and is coiled onto a take upreel 85. The quenching preserves the resolutionized grains of the strip of alloy coatedinterconnected battery grids 79 in a much more stable condition. The reel of alloy coatedinterconnected battery grids 79 may then be age hardened. While the reel of alloy coatedinterconnected battery grids 79 can be age hardened at room temperature (i.e., 25° C.), it is preferred to age harden the reel of alloy coatedinterconnected battery grids 79 at an elevated temperature (i.e., above 25° C.). Thereafter, the reel of alloy coatedinterconnected battery grids 79 may be uncoiled and fed to a paster and parted into battery plates (as is known in the art) for assembly into a battery. Alternatively, the reel of alloy coatedinterconnected battery grids 79 may be uncoiled and divided into individual battery grids which are subsequently pasted to form battery plates. - In
FIG. 7B , there is shown another apparatus, indicated generally at 51, for forming a battery grid according to an exemplary embodiment. In theapparatus 51, a strip of alloy coatedinterconnected battery grids 79 is produced using the casting drum 63, the punchingstation 71, the coining station 73 (if desired), thealloy coating bath 76 and the quenchtank 83 as in theapparatus 50 ofFIG. 7A . However, in theapparatus 51 ofFIG. 7B , the strip of alloy coatedinterconnected battery grids 79 enters anoven 86 after exiting the quenchtank 83 in order to immediately age harden the strip of alloy coatedinterconnected battery grids 79 after quenching. After age hardening in theoven 86, the strip of alloy coatedinterconnected battery grids 79 is fed through apaster 87 where conventional battery paste is applied to the strip of alloy coatedinterconnected battery grids 79. A strip of pasted alloy coated interconnected battery grids 79 a exits thepaster 87 and is separated into individual battery plates in aparter 88 before assembly into a battery. - In
FIG. 7C , there is shown another apparatus, indicated generally at 52, for forming a battery grid according to an exemplary embodiment. In the apparatus 52, alead alloy strip 65 is formed using the casting drum 63 as in theapparatus 50 ofFIG. 7A . Thelead alloy strip 65 is then expanded into a strip ofinterconnected battery grids 75 in anexpander 72. After the strip ofinterconnected battery grids 75 exits theexpander 72, the battery grid wire sections of the strip may optionally be processed in a coiningstation 73 as described above with reference to theapparatus 50 ofFIG. 7A . The strip ofinterconnected battery grids 75 is then fed through thealloy coating bath 76 to form a strip of alloy coatedinterconnected battery grids 80 which is quenched in quenchtank 83 and coiled onto take upreel 85. The reel of alloy coatedinterconnected battery grids 80 may then be heated to age harden theinterconnected battery grids 80. The strip ofinterconnected battery grids 80 may be uncoiled and fed to a paster and parted into battery plates that are assembled into a battery. Alternatively, the reel of alloy coatedinterconnected battery grids 80 may be uncoiled and divided into individual battery grids which are subsequently pasted to form battery plates. - In
FIG. 7D , there is shown another apparatus, indicated generally at 53, for forming a battery grid according to an exemplary embodiment. In theapparatus 53, a strip of alloy coatedinterconnected battery grids 80 is produced using the casting drum 63, theexpander 72, the coiningstation 73, thealloy coating bath 76 and the quenchtank 83 as in the apparatus 52 ofFIG. 7C . However, in theapparatus 53 ofFIG. 7D , the strip of alloy coatedinterconnected battery grids 80 enters anoven 86 immediately after exiting the quenchtank 83 in order to age harden the strip of alloy coatedinterconnected battery grids 80. After age hardening in theoven 86, the strip of alloy coatedinterconnected battery grids 80 is fed through apaster 87 where conventional battery paste is applied to the strip of alloy coatedinterconnected battery grids 80. A strip of pasted alloy coatedinterconnected battery grids 80 a exits thepaster 87 and is separated into individual battery plates in apatter 88 before assembly into a battery. - While the apparatus 52 of
FIG. 7C and theapparatus 53 ofFIG. 7D provide suitable results when used to practice the present invention, theapparatus 50 ofFIG. 7A and theapparatus 51 ofFIG. 7B are particularly advantageous in that complex battery grid shapes (such as that shown inFIG. 1 ) may be produced, using the punchingstation 71 and optionally, the coiningstation 73. Specifically, theexpander 72 used in the apparatus 52 ofFIG. 7C and theapparatus 53 ofFIG. 7D produces a continuous length of expanded metal grids that are limited in wire pattern, wire shape, and lead distribution. In contrast, theapparatus 50 ofFIG. 7A and theapparatus 51 ofFIG. 7B produce a continuous length of punched grids having optimized grid wire patterns, asymmetric and offset grid wire patterns, improved grid wire thickness control (grid wire aspect ratios), improved grid wire shape control, improved lead distribution in the grid (percent lead distribution from the top to the bottom of the grid), and grain control. As a result, the corrosion performance is enhanced because of the relatively stress free grain structure and low porosity of the punched sheet. In addition, the punching process does not substantially deform the grain or add other stresses into the grid which might lead to corrosion initiation sites. The electrical performance is enhanced as a result of unique and optimized grid wire patterns, improved control of grid wire size and optimized lead distribution within the grid. Thus, theapparatus 50 ofFIG. 7A and theapparatus 51 ofFIG. 7B produce a battery grid that has the advantages of optimized grid wire patterns and the advantages of an alloy coating. - In
FIG. 8A , there is shown another apparatus, indicated generally at 54, for forming a battery grid according to an exemplary embodiment. Theapparatus 54 includes a heated lead pot 61 b, which contains themolten lead alloy 62 that forms the base of the battery grids, and a pair oftwin casting rollers 66. In operation, themolten lead alloy 62 contacts the roller surfaces and freezes to form a solidlead alloy strip 68 of substantially constant width and thickness. Thelead alloy strip 68 may optionally be further rolled byrollers 67 to change the thickness and grain structure of thestrip 68. Thecontinuous strip 68 is then fed into a punchingstation 71 wherein a series of interconnected battery grids is formed by punching grid material out of thecontinuous strip 68. - During punching operations in the punching
station 71, thestrip 68 is maintained as a continuous strip and preferably the interconnected battery grid shapes and formed in a progressive punching operation, i.e., features are added to the battery grid through several punching operations. The punchingstation 71 may form a strip of interconnected battery grids, each of which has a configuration such as that shown inFIG. 1 . - After the strip exits the punching
station 71, the battery grid wire sections of the strip may optionally be processed in a coiningstation 73. The coiningstation 73 is used to deform or coin the grid wires so that the grid wires have a cross-section similar to one of the grid wire cross-sections 90 a, 90 b, 90 c or 90 d shown inFIGS. 2-5 . For instance, the coiningstation 73, may include a die or dies that deform the rectangular cross-section of the grid wires of the punched grid into an octagonal cross-section 90 a as shown inFIG. 2 . The other exemplary wire cross-sections shown inFIGS. 3-5 may also be formed. The strip of punched (and optionally, coined)interconnected battery grids 74 exiting the punching station 71 (and optionally, the coining station 73) is then fed through analloy coating bath 76 that contains amolten lead alloy 77 to form a strip of alloy coatedinterconnected battery grids 79, as described with reference toFIG. 7A . The strip of alloy coatedinterconnected battery grids 79 is then fed through a quenchfluid 84 and is coiled onto a take upreel 85. The reel of alloy coatedinterconnected battery grids 79 may then be heated to age harden theinterconnected battery grids 79. The reel of alloy coatedinterconnected battery grids 79 may be uncoiled and fed to a paster and parted into battery plates that are assembled into a battery. Alternatively, the reel of alloy coatedinterconnected battery grids 79 may be uncoiled and divided into individual battery grids which are subsequently pasted to form battery plates. - In
FIG. 8B , there is shown another apparatus, indicated generally at 55, for forming a battery grid according to an exemplary embodiment. In theapparatus 55, a strip of alloy coatedinterconnected battery grids 79 is produced using thetwin roll caster 66, the punchingstation 71, the coining station 73 (if desired), thealloy coating bath 76 and the quenchtank 83 as in theapparatus 54 ofFIG. 8A . However, in theapparatus 55 ofFIG. 8B , the strip of alloy coatedinterconnected battery grids 79 enters anoven 86 after exiting the quenchtank 83 in order to age harden the strip of alloy coatedinterconnected battery grids 79. After age hardening, the strip of alloy coatedinterconnected battery grids 79 is fed through apaster 87 where conventional battery paste is applied to the strip of alloy coatedinterconnected battery grids 79. A strip of pasted alloy coated interconnected battery grids 79 a exits thepaster 87 and is separated into individual battery plates in aparter 88. - In
FIG. 8C , there is shown another apparatus, indicated generally at 56, for forming a battery grid according to an exemplary embodiment. In the apparatus 56, alead alloy strip 68 is formed using thetwin roll caster 66 as in theapparatus 54 ofFIG. 8A . Thelead alloy strip 68 is then expanded into a strip ofinterconnected battery grids 75 in anexpander 72. After the strip ofinterconnected battery grids 75 exits theexpander 72, the battery grid wire sections of the strip may optionally be processed in a coiningstation 73 as described above with reference to theapparatus 50 ofFIG. 7A . The strip ofinterconnected battery grids 75 is then fed through thealloy coating bath 76 to form a strip of alloy coatedinterconnected battery grids 80 which is quenched in quenchtank 83 and coiled onto take upreel 85. The reel of alloy coatedinterconnected battery grids 80 may then be heated to age harden theinterconnected battery grids 80. The strip ofinterconnected battery grids 80 may be uncoiled and fed to a paster and parted into battery plates that are assembled into a battery. Alternatively, the reel of alloy coatedinterconnected battery grids 80 may be uncoiled and divided into individual battery grids which are subsequently pasted to form battery plates. - In
FIG. 8D , there is shown another apparatus, indicated generally at 57, for forming a battery grid according to an exemplary embodiment. In the apparatus 57, a strip of alloy coatedinterconnected battery grids 80 is produced using thetwin roll caster 66, theexpander 72, the coining station 73 (if desired), thealloy coating bath 76 and the quenchtank 83 as in the apparatus 56 ofFIG. 8C . However, in the apparatus 57 ofFIG. 8D , the strip of alloy coatedinterconnected battery grids 80 enters anoven 86 after exiting the quenchtank 83 in order to age harden the strip of alloy coatedinterconnected battery grids 80. After age hardening, the strip of alloy coatedinterconnected battery grids 80 is fed through apaster 87 where conventional battery paste is applied to the strip of alloy coatedinterconnected battery grids 80. A strip of pasted alloy coatedinterconnected battery grids 80 a exits thepaster 87 and is separated into individual battery plates in aparter 88. - In
FIG. 9A , there is shown another apparatus, indicated generally at 58, for forming a battery grid according to an exemplary embodiment. Theapparatus 58 includes a heated lead pot 61 c, which contains themolten lead alloy 62 that forms the base of the battery grids, and a castingdrum 69. In operation, themolten lead alloy 62 contacts the casting drum surfaces and freezes to form a strip ofinterconnected battery grids 70. A suitable casting device that may be used in theapparatus 58 to form the strip ofinterconnected battery grids 70 is shown and described in U.S. Pat. No. 4,349,067, which is incorporated herein by reference. Optionally, the strip ofinterconnected battery grids 70 removed from the surface of the castingdrum 69 may be fed through one or more sets ofrollers 98 in order to reduce the thickness of the strip ofinterconnected battery grids 70. The strip ofinterconnected battery grids 70 is then fed through analloy coating bath 76 that contains amolten lead alloy 77 to form a strip of alloy coated interconnected battery grids 81, as described with reference toFIG. 7A . The strip of alloy coated interconnected battery grids 81 is then fed through a quenchfluid 84 and is coiled onto a take upreel 85. The reel of alloy coated interconnected battery grids 81 may then be heated to age harden the interconnected battery grids 81. The reel of alloy coated interconnected battery grids 81 may be uncoiled and fed to a paster and parted into battery plates that are assembled into a battery. Alternatively, the reel of alloy coated interconnected battery grids 81 may be uncoiled and divided into individual battery grids which are subsequently pasted to form battery plates. - In
FIG. 9B , there is shown another apparatus, indicated generally at 59, for forming a battery grid according to an exemplary embodiment. In theapparatus 59, a strip of alloy coated interconnected battery grids 81 is produced using the castingdrum 69, optionally therollers 98, thealloy coating bath 76 and the quenchtank 83 as in theapparatus 58 ofFIG. 9A . However, in theapparatus 59 ofFIG. 9B , the strip of alloy coated interconnected battery grids 81 enters anoven 86 after exiting the quenchtank 83 in order to age harden the strip of alloy coated interconnected battery grids 81. After age hardening, the strip of alloy coated interconnected battery grids 81 is fed through apaster 87 where conventional battery paste is applied to the strip of alloy coated interconnected battery grids 81. A strip of pasted alloy coated interconnected battery grids 81 a exits thepaster 87 and is separated into individual battery plates in aparter 88. - Various modifications may be made to the apparatus of
FIGS. 7A-9B . For instance, the strip ofinterconnected battery grids 74 may optionally be fed through a fluxing station (not shown) before entering thealloy coating bath 76 in order to remove oxides from the surface of the strip ofinterconnected battery grids 74. A fluxing station may include a pool of flux in a tray underlying the advancing strip ofinterconnected battery grids 74, a rotating roller that absorbs and picks up flux from the pool and applies it to the underside of the strip ofinterconnected battery grids 74, and a nozzle overlying the strip ofinterconnected battery grids 74 for spraying flux onto the topside of the strip ofinterconnected battery grids 74. Other techniques, e.g. wetted sponges/applicators, for applying the flux to the strip ofinterconnected battery grids 74 may also be used. In another version of the invention, the alloy coating may be applied to the strip ofinterconnected battery grids 74 by spraying the alloy onto the strip ofinterconnected battery grids 74. - Another highly advantageous modification may be made to the apparatus of
FIGS. 7A-9B . Specifically, thealloy coating bath 76 is modified such that a stream of inert gas (e.g., nitrogen or argon) may be purged or blown into themolten lead alloy 77 in thealloy coating bath 76. During coating of the strip ofinterconnected battery grids 74 in thealloy coating bath 76, the inert gas (e.g., nitrogen or argon) is blown into themolten lead alloy 77 such that bubbles form in themolten lead alloy 77. This provides at least three advantages: (1) the alloy coating that forms on the strip ofinterconnected battery grids 74 is porous and therefore, has a much higher surface area, which further enhances the grid/active material adhesion; (2) the alloy coating that forms on the strip ofinterconnected battery grids 74 has a lower mass and lower cost as compared to an alloy coating that forms on the strip ofinterconnected battery grids 74 without the introduction of inert gas into themolten lead alloy 77; (3) the inert gas acts as a shielding film as it is leaving thealloy coating bath 76 which prevents the top of the molten alloy bath from oxidizing thereby reducing dross formation and contamination of thealloy coating bath 76. - The lead alloy used to produce the solid
lead alloy strip 65 in the casting drum 63 of the apparatus of any ofFIGS. 7A-7D is selected in order to provide a cast alloy strip that may be punched or expanded into a strip of interconnected battery grids having an alloy composition suitable for the intended application of the lead-acid battery. For example, if a lead-acid battery is to be sold as a “maintenance-free” battery, a lead-calcium alloy will be selected for use as the lead alloy applied to the casting drum 63. It is well known in the art that an alloy having lead and calcium may also contain other alloyants such as tin, aluminum and silver. Accordingly, as used herein, the term “lead-calcium alloy” is not intended to be limited strictly to binary lead-calcium alloys, but shall also include alloys having lead and calcium as well as other alloying elements which are not deleterious to the battery or the maintenance-free character thereof. The alloying elements in the lead alloy can be varied to provide optimum performance of the casting drum 63 of the apparatus of any ofFIGS. 7A-7D . - Likewise, the lead alloy used to produce the solid
lead alloy strip 68 in the twinroll casting rollers 66 of the apparatus of any ofFIGS. 8A-8D may be selected in order to provide a cast alloy strip that may be punched or expanded into a strip of interconnected battery grids having an alloy composition suitable for the intended application of the lead-acid battery. If a lead-acid battery is to be sold as a “maintenance-free” battery, a lead-calcium alloy as defined herein will be selected for use as the lead alloy applied to the twinroll casting rollers 66. The alloying elements in the lead alloy can be varied to provide optimum performance of the castingdrum 66. Similarly, the lead alloy used to produce the strip of interconnected battery grids 81 using the castingdrum 69 of the apparatus of any ofFIGS. 9A-9B may be selected in order to provide a strip of interconnected battery grids 81 having an alloy composition suitable for the intended application of the lead-acid battery. If a lead-acid battery is to be sold as a “maintenance-free” battery, a lead-calcium alloy as defined herein will be selected for use as the lead alloy applied to the castingdrum 69. The alloying elements in the lead alloy can be varied to provide optimum performance of the castingdrum 69. One example lead-calcium alloy that is useful in the present invention includes lead, from about 0.060 wt. % to about 0.070 wt. % calcium, and from about 1.20 wt. % to about 1.50 wt. % tin. Another example lead-calcium alloy that is useful in the present invention includes lead, no less than about 0.8% tin, tin in a ratio to calcium of greater than about 12:1, and silver in the range of about 0 to about 0.02%, the percentages being based upon the total weight of the lead-based alloy. This example lead-calcium alloy is fully described in U.S. Pat. No. 6,117,594. - As detailed above, each apparatus shown in
FIGS. 7A-9B produces a strip of interconnected battery grids that is subsequently coated with a lead alloy in thealloy coating bath 76. The lead alloy selected for the coating varies depending on the alloy used to produce the strip of interconnected battery grids. When the strip of interconnected battery grids is formed from a lead-calcium alloy as defined herein, suitable lead alloys for the coating include lead-tin and lead-antimony alloys. The precise composition of the coating is not particularly critical in terms of extending the lives of batteries. On the other hand, there are two general rules applicable to the selection of the lead alloy coating composition. First, the composition of the coating should be selected so as to provide a melt having a melting point which is sufficiently less than the melting point of the lead-calcium alloy strip of interconnected battery grids (e.g., about 620° F. for a typical Pb-0.07 wt. % Ca-1 to 1.5 wt. % tin alloy) so as to preclude complete melting of the strip of interconnected battery grids while it is immersed in the melt. Melting of the surface of the lead-calcium alloy strip of interconnected battery grids is acceptable and, in fact, may be desirable to promote metallurgical bonding of the alloy coating to the strip of interconnected battery grids. Second, the composition of the coating should be such that there is sufficient tin, antimony or other alloying elements present to dope the corrosion layer on the surface of the strip of interconnected battery grids (i.e., at the grid-active material interface) with oxides of the tin, antimony or other alloying elements, and thereby improve the conductivity of the corrosion layer and promote better adhesion of the leady active material to the grid. - Suitable lead-antimony alloys for coating the strip of interconnected battery grids include lead alloys having an antimony content varying from about 1% by weight to about 10% by weight. Other additives such as tin from about 1 wt. % to about 10 wt. % may also be used with the antimonial lead. Hence, the term lead-antimony alloy is not intended to be limited to alloys containing just lead and antimony, but rather is intended to include other low melting alloys thereof which do not negate the intended effects of the antimony or are otherwise deleterious to a battery. For coating a Pb—Ca—Sn alloy (i.e., 0.07 wt. % Ca, and 1 to 1.5 wt. % Sn) strip of interconnected battery grids which melts at about 620° F., the antimony content in the lead alloy coating will preferably be between about 0.5 wt. % and about 3 wt. %, and preferably the tin content in the lead alloy will be between about 2 wt. % and about 5 wt. % so as to have a melting point of about 590° F.
- Similarly, suitable lead-tin alloys may be used as all melt at lower temperatures than the typical lead-calcium alloy strip of interconnected battery grids. Lead-tin alloys will preferably comprise about 1 wt. % to about 10 wt. % tin, but otherwise will be determined primarily on the basis of cost owing to the high cost of tin. One example alloy includes lead and about 4 wt. % to about 6 wt. % tin. Other alloyants could be added and therefore, the term lead-tin alloy is not intended to be limited to alloys containing just lead and tin, but rather intended to include other low melting alloys thereof which do not negate the intended effects of the tin or are otherwise deleterious to a battery or the maintenance-free character thereof.
- The precise temperature of the melt is not particularly critical so long as it is not so hot as to completely melt the strip of interconnected battery grids in the brief time that the strip of interconnected battery grids are immersed in the melt. Hence, the melt temperature will, in many respects, be determined by the composition (and hence melting point) of the strip of interconnected battery grids being coated. Generally speaking, it is preferred that the temperature of the melt be maintained at a temperature that is at least about 20° F. below the melting point of the strip of interconnected battery grids. On the other hand, it is desirable that the temperature be sufficiently high as to melt some low melting phases on the surface of the strip of interconnected battery grids to promote better bonding of the coating to the strip of interconnected battery grids.
- The invention is further illustrated in the following Examples which are presented for purposes of illustration and not of limitation.
- A continuous strip was prepared from a lead-alloy having the following composition: 0.0425 wt. % calcium, 0.925 wt. % tin, 0.013 wt. % aluminum, 0.0125 wt. % silver and balance lead. A series of interconnected battery grid shapes were then formed in the strip in a progressive punching operation, i.e., features were added to the battery grid through several punching operations. The battery grid wire sections of the strip were then processed in a coining station to coin the grid wires so that the grid wires had a cross-section similar to the grid wire cross-sections 90 c in
FIG. 4 . The interconnected battery grids were then divided into individual grids. The grids were then pasted with a conventional battery paste and formed into battery cells. The battery cells were then cycled in accordance with the SAE J240 life test procedure at a temperature of 75° C. (167° F.) to measure the service life. - A continuous strip was prepared from a lead-alloy having the following composition: 0.0425 wt. % calcium, 0.925 wt. % tin, 0.013 wt. % aluminum, 0.0125 wt. % silver and balance lead. A series of interconnected battery grid shapes were then formed in the strip in a progressive punching operation, i.e., features were added to the battery grid through several punching operations. The battery grid wire sections of the strip were then processed in a coining station to coin the grid wires so that the grid wires had a cross-section similar to the grid wire cross-sections 90 c in
FIG. 4 . The interconnected battery grids were then divided into individual grids. The grids were then hand dipped into a pot of molten 94 wt. % lead-6 wt. % tin coating alloy. The grids were dipped slowly into the melt until they bottomed out in the pot and then slowly withdrawn at the same rate for a total immersion time of about 2 seconds. The coating was uniform with no excess buildup on the grid wires or the edges of the grids. The grids were then pasted with a conventional battery paste and formed into battery cells. The battery cells were then cycled in accordance with the SAE 3240 life test procedure at a temperature of 75° C. (167° F.) to measure the service life. The number of cycles for battery cells having lead-tin alloy coated grids prepared in accordance with Example 2 was 20% higher than the number of cycles for the control battery cells having uncoated grids prepared in accordance with Example 1. This demonstrates that batteries including grids made in accordance with the present invention will have better cycle life performance than batteries including conventional grids. - A continuous strip was prepared from a lead-alloy having the following composition: 0.0425 wt. % calcium, 0.925 wt. % tin, 0.013 wt. % aluminum, 0.0125 wt. % silver and balance lead. A series of interconnected battery grid shapes were then formed in the strip in a progressive punching operation, i.e., features were added to the battery grid through several punching operations. The battery grid wire sections of the strip were then processed in a coining station to coin the grid wires so that the grid wires had a cross-section similar to the grid wire cross-sections 90 c in
FIG. 4 . The interconnected battery grids were then divided into individual grids. The grids were then hand dipped into a pot of molten 94 wt. % lead-3 wt. % tin-3 wt. % antimony coating alloy. The grids were dipped slowly into the melt until they bottomed out in the pot and then slowly withdrawn at the same rate for a total immersion time of about 2 seconds. The coating was uniform with no excess buildup on the grid wires or the edges of the grids. The grids were then pasted with a conventional battery paste and formed into battery cells. The battery cells were then cycled in accordance with the SAE J240 life test procedure at a temperature of 75° C. (167° F.) to measure the service life. The number of cycles for battery cells having lead-tin-antimony alloy coated grids prepared in accordance with Example 3 was 47% higher at the last reading than the number of cycles for the control battery cells having uncoated grids prepared in accordance with Example 1. In addition, the battery cells of Example 3 continue on test as the lower voltage cutoff for the SAE 3240 has not been reached. This demonstrates that batteries including grids made in accordance with the present invention will have better cycle life performance than batteries including conventional grids. - Thus, the present invention provides a method that can increase the adherence of battery active material to a battery grid produced by a continuous process, such as strip expansion, strip punching, or continuous casting. The method of the present invention increases the cycle life of a battery by enhancing the adhesion between the battery paste material and the battery grid. As a result, a battery manufacturer can take advantage of a low cost continuous grid making process without the drawbacks associated with inadequate paste adhesion.
- It is important to note that the method and battery grid as shown in the exemplary embodiments is illustrative only. Although only a few embodiments of the present inventions have been described in detail in this disclosure, those skilled in the art who review this disclosure will readily appreciate that many modifications are possible (e.g., variations in sizes, dimensions, structures, shapes and proportions of the various elements, values of parameters, mounting arrangements, use of materials, colors, orientations, etc.) without materially departing from the novel teachings and advantages of the subject matter recited in the claims. Accordingly, all such modifications are intended to be included within the scope of the present invention as defined in the appended claims. The order or sequence of any process or method steps may be varied or re-sequenced according to other exemplary embodiments. Other substitutions, modifications, changes and omissions may be made in the design, operating conditions and arrangement of the exemplary embodiments without departing from the scope of the present invention as expressed in the appended claims.
Claims (20)
1. A battery plate comprising:
a grid network, the grid network comprising a plurality of spaced apart grid wire elements, each grid wire element having opposed ends joined to one of a plurality of nodes, each node comprising the juncture of one of the opposed ends of a plurality of the grid wire elements, to define a plurality of open spaces in the grid network;
wherein at least one of the grid wire elements has a first transverse cross-section intermediate its opposed ends that is a different shape than a second transverse cross-section at least one of the grid wire element's opposed ends.
2. The battery plate of claim 1 , wherein the first transverse cross-section is generally non-rectangular-shaped and the second transverse cross-section is generally rectangular-shaped.
3. The battery plate of claim 2 , wherein the first transverse cross-section has a shape that is selected from the group consisting of generally octagon-shaped, generally hexagon-shaped, generally diamond-shaped, and generally triangular-shaped.
4. The battery plate of claim 1 , further comprising a lead alloy coating on substantially all surfaces of the grid wire elements.
5. The battery plate of claim 1 , wherein the lead alloy coating is porous.
6. The battery plate of claim 1 , wherein the lead alloy coating comprises a lead-tin alloy.
7. The battery plate of claim 6 , wherein the lead-tin alloy comprises about 90 weight percent to about 99 weight percent lead and about 1 weight percent to about 10 weight percent tin.
8. The battery plate of claim 6 , wherein the lead-tin alloy further includes antimony.
9. The battery plate of claim 8 , wherein the lead-tin alloy comprises about 80 weight percent to about 98 weight percent lead, about 1 weight percent to about 10 weight percent tin, and about 1 weight percent to about 10 weight percent antimony.
10. The battery plate of claim 1 , wherein the battery plate is manufactured in a strip of multiple battery plates and then separated into individual battery plates.
11. The battery plate of claim 10 , wherein the strip of multiple battery plates is continuously cast.
12. The battery plate of claim 1 , wherein the battery plate is coined during manufacture.
13. The battery plate of claim 12 , wherein the at least one grid element has a substantially continuous transverse cross-section between its opposed ends before the battery plate is coined.
14. The battery plate of claim 1 wherein the grid network is comprised of a lead-calcium alloy.
15. The battery plate of claim 14 wherein the lead-calcium alloy comprises between about 0.06 weight percent to about 0.07 weight percent calcium.
16. The battery plate of claim 15 wherein the lead-calcium alloy further comprises about 1.2 weight percent to about 1.5 weight percent tin.
17. The battery plate of claim 16 wherein the lead-calcium alloy comprises tin in a ratio to calcium of greater than 12:1.
18. The battery plate of claim 1 wherein at least a portion of at least one of the grid wire elements is formed via a stamping process at a position intermediate the opposed ends of the grid wire element before applying a lead alloy coating to the battery grid.
19. The battery plate of claim 1 , wherein the battery plate further comprises a frame element bordering the battery grid.
20. The battery plate of claim 1 , further comprising:
a lead alloy coating provided on the plurality of grid wire elements and comprising a lead-tin alloy; and
an active material coupled to the coating and comprising a paste.