Búsqueda Imágenes Maps Play YouTube Noticias Gmail Drive Más »
Iniciar sesión
Usuarios de lectores de pantalla: deben hacer clic en este enlace para utilizar el modo de accesibilidad. Este modo tiene las mismas funciones esenciales pero funciona mejor con el lector.

Patentes

  1. Búsqueda avanzada de patentes
Número de publicaciónUSRE39690 E1
Tipo de publicaciónConcesión
Número de solicitudUS 09/998,595
Fecha de publicación12 Jun 2007
Fecha de presentación16 Nov 2001
Fecha de prioridad6 Dic 1993
TarifaPagadas
También publicado comoDE69425636D1, DE69425636T2, EP0657925A1, EP0657925B1, US5435888, US5633534, US5837613, US5986330
Número de publicación09998595, 998595, US RE39690 E1, US RE39690E1, US-E1-RE39690, USRE39690 E1, USRE39690E1
InventoresAlex Kalnitsky, Yih-Shung Lin
Cesionario originalStmicroelectronics, Inc.
Exportar citaBiBTeX, EndNote, RefMan
Enlaces externos: USPTO, Cesión de USPTO, Espacenet
Enhanced planarization technique for an integrated circuit
US RE39690 E1
Resumen
A method for planarizing integrated circuit topographies, wherein, after a first layer of spin-on glass is deposited, a layer of low-temperature oxide is deposited before a second layer of spin-on glass.
Imágenes(5)
Previous page
Next page
Reclamaciones(29)
1. An integrated circuit manufactured by the method comprising the acts of:
(a.) providing a partially fabricated integrated circuit structure;
(b.) applying and curing spin-on glass, to form a first dielectric layer;
(c.) depositing dielectric material, to form a second dielectric layer over said first dielectric layer;
(d.) applying and curing spin-on glass, to form a third dielectric layer, to produce a stack including said third dielectric layer over said first and second dielectric layers;
(e.) performing a global etchback to substantially remove portions of said dielectric stack from high points of said partially fabricated structure, wherein at least a portion of said third dielectric layer remains after said global etchback;
(f.) deposition of an interlevel dielectric at least over said remaining third dielectric layer;
(g.) etching holes in said interlevel dielectric in predetermined locations; and
(h.) depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.
2. The integrated circuit of claim 1, wherein said deposition step (c.) is plasma-enhanced.
3. The integrated circuit of claim 1, wherein said deposition step (c.) uses TEOS as a source gas.
4. The integrated circuit of claim 1, comprising the additional step of applying a passivating dielectric, under vacuum conditions, after said step (a.) and Am before said deposition step (b.).
5. The integrated circuit of claim 1, Hi wherein said deposition step (b.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
6. The integrated circuit of claim 1, wherein said deposition step (d.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
7. The integrated circuit of claim 1, wherein said interlevel dielectric is a doped silicate glass.
8. An integrated circuit manufactured by the method comprising the acts of:
(a.) providing a partially fabricated integrated circuit structure;
(b.) applying and curing spin-on glass, to form a first dielectric layer;
(c.) depositing silicon dioxide, to form a second dielectric layer over said first dielectric layer;
(d.) applying and curing spin-on glass, to form a third dielectric layer to produce a dielectric stack including said third dielectric layer over said first and second layers;
(e.) performing a global etchback to substantially remove said dielectric stack from high points of said partially fabricated structure, wherein at least a portion of said spin-on glass of said third dielectric layer remains after said global etchback;
(f.) deposition of an interlevel dielectric at least over said remaining spin-on glass of said third dielectric layer;
(g.) etching holes in said interlevel dielectric in predetermined locations; and
(h.) depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.
9. The integrated circuit of claim 8, wherein said deposition step (c.) is plasma-enhanced.
10. The integrated circuit of claim 8, wherein said deposition step (c.) uses TEOS as a source gas.
11. The integrated circuit of claim 8, comprising the additional step of applying a passivating dielectric, under vacuum conditions, after said step (a.) and before said deposition step (b.).
12. The integrated circuit of claim 8, wherein said deposition step (b.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
13. The integrated circuit of claim 8, wherein said deposition step (d.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
14. The integrated circuit of claim 8, wherein said interlevel dielectric is a doped silicate glass.
15. An integrated circuit manufactured by the method comprising the acts of:
(a.) providing a partially fabricated integrated circuit structure;
(b.) applying and curing spin-on glass, to form a first dielectric layer;
(c.) depositing dielectric material, to form a second dielectric layer over said first dielectric layer, said second dielectric layer having a thickness equal to or less than said first dielectric layer;
(d.) applying and curing spin-on glass, to form a third dielectric layer to produce a dielectric stack including said third dielectric layer over said first and second dielectric layers, said third dielectric layer having a thickness equal to or greater than said second layer;
(e.) performing a global etchback to substantially remove said dielectric stack from high points of said partially fabricated structure, wherein at least a portion of said third dielectric layer remains after said global etchback;
(f.) deposition of an interlevel dielectric at least over said remaining second dielectric layer;
(g.) etching holes in said interlevel dielectric in predetermined locations; and
(h.) depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.
16. The integrated circuit of claim 15, wherein said deposition step (c.) is plasma-enhanced.
17. The integrated circuit of claim 15, wherein said deposition step (c.) uses TEOS as a source gas.
18. The integrated circuit of claim 15, comprising the additional step of applying a passivating dielectric, under vacuum conditions, after said step (a.) and before said deposition step (b.).
19. The integrated circuit of claim 15, wherein said deposition step (b.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
20. The integrated circuit of claim 15, wherein said interlevel dielectric is a doped silicate glass.
21. The integrated circuit of claim 15, wherein said deposition step (d.) applies said spin-on glass with a thickness in the range of 1000-5000 Å inclusive.
22. An integrated circuit, comprising:
(a.) an active device structure, including therein a substrate, active device structures, isolation structures, and one or more patterned thin film conductor layers including an uppermost conductor layer; and
(b.) a planarization structure, overlying recessed portions of said active device structure, comprising a layer of sol-gel-deposited dielectric overlain by a layer of vacuum-deposited dielectric overlain by a further layer of sol-gel-deposited dielectric;
(c.) an interlevel dielectric overlying said planarization structure and said active device structure, and having via holes therein which extend to selected locations of said uppermost conductor layer; and
(d.) an additional thin-film patterned conductor layer which overlies said interlevel dielectric and extends through said via holes to said selected locations of said uppermost conductor layer.
23. A semiconductor structure, comprising:
a substrate;
a first layer of inorganic spin-on glass disposed on the substrate;
a first dielectric disposed on the first layer; and
a planarized second layer of inorganic spin-on glass disposed on the first dielectric.
24. The semiconductor structure of claim 23, further comprising:
a second dielectric disposed on the substrate; and
wherein the first layer of spin-on glass is disposed on the second dielectric.
25. The semiconductor structure of claim 23, further comprising:
a metal layer disposed on the substrate; and
wherein the first layer of spin-on glass is disposed on the metal layer.
26. The semiconductor structure of claim 23, further comprising:
a metal layer disposed on the substrate;
a second dielectric disposed on the metal layer; and
wherein the first layer of spin-on glass is disposed on the second dielectric.
27. The semiconductor structure of claim 23 wherein the first dielectric comprises a low-temperature oxide.
28. The semiconductor structure of claim 23, further comprising a planarized boundary that includes the planarized second layer of spin-on glass and a planarized portion of the first dielectric.
29. The semiconductor structure of claim 23, further comprising a planarized boundary that includes the planarized second layer of spin-on glass, a planarized portion of the first dielectric, and a planarized portion of the first layer of spin-on glass.
Descripción

This application is a continuation of patent application Ser. No. 08/456,343, filed Jun. 1, 1995 now abandoned which is a continuation of Ser. No. 08/163,043 filed on Dec. 6, 1993 now U.S. Pat. No. 5,435,888.

BACKGROUND AND SUMMARY OF THE INVENTION

The present invention relates to formation and structures for interlevel dielectrics in integrated circuit fabrication.

A high degree of planarization is essential in the fabrication of integrated circuits with multiple levels of interconnect. Application of spin-on glass,1 followed by global etch-back, is widely used in the industry to achieve the desired level of surface planarity. However, spin on glass (“SOG”) and SOG etch-back technique are inadequate in a variety of situations where topologies with high aspect ratio and/or more topologies are encountered due to lack of planarization and/or sog cracks.

1Spin-on glass deposition is an example of a “sol-gel” process, which has been used in the semiconductor industry for many years. The unprocessed spin-on-glass material (available in numerous formulations) is a fluid material (actually a gel). After the liquid material is coated onto the face of a wafer, the wafer is rotated at high speed to throw off the excess material. The surface tension and adhesion of the material provides a flat (planarized) surface with a controlled thickness. The liquid material is then baked, to drive off solvents and provide a stable solid silicate glass. See generally, e.g., Dauksher et al., “Three ‘low Dt’ options for planarizing the pre-metal dielectric on an advanced double poly BiCMOS process,” 139 J. Electrochem Soc 532-6 (1992), which is hereby incorporated by reference.

In most cases, successful planarization of severe topologies is achieved by a single or double SOG deposition+etchback step in the following sequence:

  • a) a layer of dielectric is applied between the underlying surface and SOG.
  • b) application of a layer of SOG and SOG cure;
  • c) application of a second layer of SOG and SOG cure (optional); and
  • d) SOG etchback.

However, in extreme topologies, when the volume of SOG is very large, shrinkage of SOG during planarization and post-planarization processing leads to formation of undesirable cracks or voids.

The proposed method seeks to alleviate the problem of SOG cracking by performing the following operations:

  • a) Conventional dielectric deposition is applied (optional);
  • b) Application of a layer of SOG and SOG cure (as in prior art);
  • c) deposition of a layer of dielectric (e.g. TEOS/ozone deposition, or simple plasma-enhanced-TEOS,2 or plasma-enhanced-silane oxide) with or without dopant can be used to adjust for etch back selectivity between SOG and dielectric. Thicknesses between 1000 Å to 5000 Å can be used.

2“TEOS,” or tetraethoxysilane, is a popular and convenient feedstock for deposition of oxides from the vapor phase.

  • d) application of a second layer of SOG and/or SOG cure: and
  • e) SOG etchback.

This process will leave a layer of dielectric between the 1st and the 2nd SOG layers in locations where conventional planarization technique are likely to crack or void. This provides enhanced reliability.

The thickness of the first SOG layer can be reduced to avoid any undesired effects, such as field inversion of underlying devices or enhanced hot-carrier injection.3

3See, e.g., Lifshitz et al., “Hot-carrier aging of the MOS transistor in the presence of spin-on glass as the interlevel dielectric,” 12 IEEE ELECTRON DEVICE LETTERS 140-2 (March 1991), which is hereby incorporated by reference.

A positive sloped valley is produced for second dielectric deposition. The step coverage will be enhanced due to this positive slope.

The structure provided by these steps has improved resistance to cracking, and improved resistance to other undesirable possible effects of thick spin-on glass layers.

According to a disclosed class of innovative embodiments, there is provided: An integrated circuit fabrication method, comprising the steps of: providing a partially fabricated integrated circuit structure; applying and curing spin-on glass, to form a first dielectric; depositing dielectric material under vacuum conditions, to form a second dielectric layer over said first layer; applying and curing spin-on glass, to form a dielectric stack including a third dielectric layer over said first and second layers; performing a global etchback to substantially remove said dielectric stack from high points of said partially fabricated structure; deposition of an interlevel dielectric; etching holes in said interlevel dielectric in predetermined locations; and depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.

According to a disclosed class of innovative embodiments, there is provided: An integrated circuit fabrication method, comprising the steps of: providing a partially fabricated integrated circuit structure; applying and curing spin-on glass, to form a first dielectric; depositing silicon dioxide under vacuum conditions, to form a second dielectric layer over said first layer; applying and curing spin-on glass, to form a dielectric stack including a third dielectric layer over said first and second layers; performing a global etchback to substantially remove said dielectric stack from high points of said partially fabricated structure; deposition of an interlevel dielectric; etching holes in said interlevel dielectric in predetermined locations; and depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.

According to a disclosed class of innovative embodiments, there is provided: An integrated circuit fabrication method, comprising the steps of: providing a partially fabricated integrated circuit structure; applying and curing spin-on glass, to form a first dielectric layer; depositing dielectric material under vacuum conditions, to form a second dielectric layer over said first layer, said second dielectric layer having a thickness equal to or less than said first layer; applying and curing spin-on glass, to form a dielectric stack including a third dielectric layer over said first and second layers, said third dielectric layer having a thickness equal to or greater than said second layer; performing a global etchback to substantially remove said dielectric stack from high points of said partially fabricated structure; deposition of an interlevel dielectric; etching holes in said interlevel dielectric in predetermined locations; and depositing and patterning a metallization layer to form a desired pattern of connections, including connections through said holes.

According to a disclosed class of innovative embodiments, there is provided: An integrated circuit, comprising: an active device structure, including therein a substrate, active device structures, isolation structures, and one or more patterned thin film conductor layers including an uppermost conductor layer; and a planarization structure, overlying recessed portions of said active device structure, comprising a layer of sol-gel-deposited dielectric overlain by a layer of vacuum-deposited dielectric overlain by a further layer of sol-gel-deposited dielectric; an interlevel dielectric overlying said planarization structure and said active device structure, and having via holes therein which extend to selected locations of said uppermost conductor layer; and an additional thin-film patterned conductor layer which overlies said interlevel dielectric and extends through said via holes to said selectred locations of said uppermost conductor layer.

BRIEF DESCRIPTION OF THE DRAWING

The present invention will be described with reference to the accompanying drawings, which show important sample embodiments of the invention and which are incorporated in the specification hereof by reference, wherein:

FIGS. 1A-1C show steps in a conventional process;

FIGS. 2A-2C show steps in a first embodiment of the invention;

FIGS. 3A-3C show steps in a second embodiment of the invention.

FIG. 4 shows a sample device structure incorporating a planarization layer according to the disclosed innovations.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The numerous innovative teachings of the present application will be described with particular reference to the presently preferred embodiment. However, it should be understood that this class of embodiments provides only a few examples of the many advantageous uses of the innovative teachings herein. In general, statements made in the specification of the present application do not necessarily delimit any of the various claimed inventions. Moreover, some statements may apply to some inventive features but not to others.

The disclosed process steps can be applied, for example, after fabrication of the first metal layer. Thus, the starting structure would be patterned metallization lines running over an interlevel dielectric which includes contact holes, and also has topographical excursions due to the underlying polysilicon layer(s) and field oxide layer. The maximum topographical excursion will include contributions from all of these. (However, the disclosed innovations can also be applied after fabrication of the second metal layer, before deposition of a third metal layer.)

FIGS. 1A-1C show steps in a conventional process. The starting structure will of course be defined by the previous process steps; but assume, for example, that the recesses have widths of 0.8 μm each, are spaced on a minimum pitch of 1.6 μm, and have a maximum depth of 1 μm. (Of course, these numbers are merely illustrative.)

As shown in FIG. 1A, a first layer 1 of SOG would be spun on and cured, to a thickness of e.g. 3000 Å in flat areas. (The thickness is substantially more in recessed areas ) As is well known to those of ordinary skill, the thickness of the SOG is determined by the individual composition and by the spin rate. As seen in FIG. 1A, a single deposition of SOG is not enough to fill the recesses.

As shown in FIG. 1B, a second layer 2 of SOG would then be spun on and cured, to provide an additional thickness of e.g. 3000 Å in flat areas.

A global etchback step is then performed, to remove the SOG from flat areas. The resulting surface contour, as shown in FIG. 1C, is susceptible to cracking.

FIGS. 2A-2C show steps in a first embodiment of the invention. Assume that the same recess dimensions are used as in FIGS. 1A-1C. Again, the specific dimensions and parameters given here are merely illustrative, and do not delimit the invention.

A first layer 1 of SOG is deposited as in FIG. 1A. That is, for example, a siloxane-based spin-on glass4 is spun on to a thickness of 2000 Å over flat areas, and is then cured for 60 minutes at 425° C.

4Such materials may be obtained, for example, from Ohka America™ or Allied Signal™ or other suppliers.

A layer 3 of low-temperature oxide is then deposited, to a thickness of 2000 Å. (For example, this may be done by plasma-enhanced deposition of TEOS.) This produces the structure shown in FIG. 2B.

A second layer 2 of SOG is then be spun on and cured, to provide an additional thickness of e.g. 3000 Å in flat areas.

A global etchback step is then performed, to remove the SOG and TEOS from flat areas. The resulting surface contour, as shown in FIG. 2C, provides improved filling of the recessed areas. Moreover, the combination of slightly different materials (SOG and low-temperature oxide) reduces susceptibility to cracking.

For simplicity, the drawing of FIG. 2C shows exactly 100% etchback, but of course the degree of etchback can be varied if desired.

FIGS. 3A-3C show steps in a second embodiment of the invention. This may be particularly advantageous with more extreme topologies. In this embodiment, assume, for example, that the recessed areas have widths of 0.8 μm each, are spaced on a minimum pitch of 1.6 μm, and have a maximum depth of 2 μm. (Of course, these numbers are merely illustrative.)

A first layer 1 of SOG is spun on and cured to produce a thickness of 2000 Å over flat areas, as shown in FIG. 3A.

A layer 3 of low-temperature oxide is then deposited, to a thickness of 3000 Å. (For example, this may be done by plasma-enhanced deposition of TEOS.) This produces the structure shown in FIG. 3B.

A second layer 2 of SOG is then be spun on and cured, to provide an additional thickness of e.g. 2000 Å in flat areas.

A global etchback step is then performed, to remove the SOG and TEOS from flat areas. The resulting surface contour, as shown in FIG. 3C, provides improved filling of the recessed areas, even under extreme topologies. Moreover, the combination of slightly different materials (SOG and low-temperature oxide) reduces susceptibility to cracking.

For simplicity, the drawing of FIG. 3C shows exactly 100% etchback, but of course the degree of etchback can be varied if desired.

In alternative embodiments, it is also possible to deposit a plasma oxide before the first layer of spin-on glass. (This is commonly done to prevent direct contact between the SOG and the underlying metallization.) In this embodiment, 1000 Å-5000 Å of (for example) TEOS oxide would be deposited before the first layer of SOG.

Processing then continues with deposition of an interlevel dielectric, such as PSG, and conventional further processing steps.

One particular advantage of the disclosed invention is that it can be very easily implemented (in at least some processes) by a simple transposition of steps (depositing the low-temperature oxide before, rather than after, the second layer of spin-on glass).

FIG. 4 shows a sample device structure incorporating a planarization layer according to the disclosed innovations. In this example, the partially fabricated device structure included active devices 12 in a substrate 10, including polysilicon lines 14. Field oxide 13 provides lateral separation active devices. Metal lines 18 overlie a first interlevel dielectric 16 (e.g. of BPSG over TEOS), and make contact to active device areas at contact locations 20. (This provides the starting structure on which planarization is performed as described above.) A planarization layer 22 is then deposited, by the techniques described above, to reduce or eliminate the topographical excursions of the structure. An interlevel dielectric 24 overlies the planarization layer 22 (and the rest of the planarized structure), and includes via holes 25 through which a second metal layer 26 contacts the first metal layer 18. The structure shown can be topped by a protective overcoat (not shown) through which holes are etched to expose locations of contact pads in the second metal layer.

FURTHER MODIFICATIONS AND VARIATIONS

It will be recognized by those skilled in the art that the innovative concepts disclosed in the present application can be applied in a wide variety of contexts. Moreover, the preferred implementation can be modified in a tremendous variety of ways. Accordingly, it should be understood that the modifications and variations suggested below and above are merely illustrative. These examples may help to show some of the scope of the inventive concepts, but these examples do not nearly exhaust the full scope of variations in the disclosed novel concepts.

The disclosed innovative steps have been described in the context of via formation (e.g. forming connections from second metal to first metal, or third metal to second metal). Due to the accumulated topographical excursions, planarization is especially desirable at these stages. However, the disclosed innovative concepts can also be applied to planarization of lower levels as well.

The disclosed innovative concepts can also be applied to other spin-on materials, such as polyimide or polymethylmethacrylate.

As will be recognized by those skilled in the art, the innovative concepts described in the present application can be modified and varied over a tremendous range of applications, and accordingly the scope of patented subject matter is not limited by any of the specific exemplary teachings given.

Citas de patentes
Patente citada Fecha de presentación Fecha de publicación Solicitante Título
US4253907 *28 Mar 19793 Mar 1981Western Electric Company, Inc.Anisotropic plasma etching
US4354896 *5 Ago 198019 Oct 1982Texas Instruments IncorporatedFormation of submicron substrate element
US4384938 *3 May 198224 May 1983International Business Machines CorporationReactive ion etching chamber
US4654112 *26 Sep 198431 Mar 1987Texas Instruments IncorporatedOxide etch
US4657628 *7 Mar 198614 Abr 1987Texas Instruments IncorporatedProcess for patterning local interconnects
US4660278 *26 Jun 198528 Abr 1987Texas Instruments IncorporatedProcess of making IC isolation structure
US4676867 *6 Jun 198630 Jun 1987Rockwell International CorporationPlanarization process for double metal MOS using spin-on glass as a sacrificial layer
US4707218 *28 Oct 198617 Nov 1987International Business Machines CorporationLithographic image size reduction
US4721548 *13 May 198726 Ene 1988Intel CorporationSemiconductor planarization process
US4755476 *17 Nov 19865 Jul 1988Siemens AktiengesellschaftProcess for the production of self-adjusted bipolar transistor structures having a reduced extrinsic base resistance
US4792534 *15 Dic 198620 Dic 1988Kabushiki Kaisha ToshibaMethod of manufacturing a semiconductor device involving sidewall spacer formation
US4801350 *29 Dic 198631 Ene 1989Motorola, Inc.Method for obtaining submicron features from optical lithography technology
US4801560 *2 Oct 198731 Ene 1989Motorola Inc.Semiconductor processing utilizing carbon containing thick film spin-on glass
US4824767 *2 Jun 198725 Abr 1989Intel CorporationDual glass contact process
US4894351 *16 Feb 198816 Ene 1990Sprague Electric CompanyMethod for making a silicon IC with planar double layer metal conductors system
US4912061 *4 Abr 198827 Mar 1990Digital Equipment CorporationMethod of forming a salicided self-aligned metal oxide semiconductor device using a disposable silicon nitride spacer
US4962414 *8 Jun 19899 Oct 1990Sgs-Thomson Microelectronics, Inc.Method for forming a contact VIA
US4986878 *19 Jul 198822 Ene 1991Cypress Semiconductor Corp.Process for improved planarization of the passivation layers for semiconductor devices
US5003062 *19 Abr 199026 Mar 1991Taiwan Semiconductor Manufacturing Co.Semiconductor planarization process for submicron devices
US5063176 *30 May 19905 Nov 1991Hyundai Electronics Industries Co., Ltd.Fabrication of contact hole using an etch barrier layer
US5068711 *19 Mar 199026 Nov 1991Fujitsu LimitedSemiconductor device having a planarized surface
US5110763 *22 Ene 19915 May 1992Yamaha CorporationProcess of fabricating multi-level wiring structure, incorporated in semiconductor device
US5117273 *16 Nov 199026 May 1992Sgs-Thomson Microelectronics, Inc.Contact for integrated circuits
US5158910 *26 Nov 199027 Oct 1992Motorola Inc.Process for forming a contact structure
US5166088 *25 Jun 199124 Nov 1992Sharp Kabushiki KaishaMethod of manufacturing semiconductor device contact vias in layers comprising silicon nitride and glass
US5244841 *10 Dic 199114 Sep 1993Applied Materials, Inc.Method for planarizing an integrated circuit structure using low melting inorganic material and flowing while depositing
US5250472 *3 Sep 19925 Oct 1993Industrial Technology Research InstituteSpin-on-glass integration planarization having siloxane partial etchback and silicate processes
US5266525 *7 Ago 199130 Nov 1993Seiko Epson CorporationMicroelectronic interlayer dielectric structure and methods of manufacturing same
US5310720 *24 Feb 199310 May 1994Fujitsu LimitedProcess for fabricating an integrated circuit device by forming a planarized polysilazane layer and oxidizing to form oxide layer
US5320983 *6 Feb 199114 Jun 1994Mitel CorporationSpin-on glass processing technique for the fabrication of semiconductor devices
US5331117 *12 Nov 199219 Jul 1994Sgs-Thomson Microelectronics, Inc.Method to improve interlevel dielectric planarization
US5399533 *1 Dic 199321 Mar 1995Vlsi Technology, Inc.Method improving integrated circuit planarization during etchback
US5435888 *6 Dic 199325 Jul 1995Sgs-Thomson Microelectronics, Inc.Enhanced planarization technique for an integrated circuit
US5534731 *28 Oct 19949 Jul 1996Advanced Micro Devices, IncorporatedLayered low dielectric constant technology
DE410244C *2 Feb 192426 Feb 1925Friedrich LunowLoseblaetterbuch mit schwingbar gelagerten ineinander eintretenden Aufreihern
EP0111706A1 *3 Nov 198327 Jun 1984International Business Machines CorporationSidewall isolation for gate of field effect transistor and process for the formation thereof
EP0185787A1 *21 Dic 19842 Jul 1986Deutsche ITT Industries GmbHPlastic encapsulated semiconductor component
EP0265638A2 *8 Sep 19874 May 1988International Business Machines CorporationLithographic image size reduction
EP0327412A1 *6 Ene 19899 Ago 1989Sgs-Thomson Microelectronics S.A.Passivation process of a integrated circuit
EP0491408A2 *7 Nov 199124 Jun 1992Consorzio Per La Ricerca Sulla Microelettronica Nel MezzogiornoProcess for making planarized sub-micrometric trenches in integrated circuits
GB2083948A * Título no disponible
GB2167901A * Título no disponible
GB2227452A * Título no disponible
JP31033131A * Título no disponible
JPH0492453A * Título no disponible
JPS6058635A * Título no disponible
JPS6126240A * Título no disponible
JPS61232646A * Título no disponible
JPS62106645A * Título no disponible
JPS63293946A * Título no disponible
Otras citas
Referencia
1 *"A Margin-Free Contact Process Using an AI303 Etch-Stop Layer for High □□Density Devices", Fukase et al., IEDM, p. 837 (1992).
2 *"A New Technology for Oxide Contact and Via Etch", by Pete Singer, □□Semiconductor International, p. 36 (1993). □□.
3 *"A Super Self-Aligned Source/Drain MOSFET," Lau et al., IEDM, p. 358 □□(1987). □□.
4 *"Advantages of Using Spin on Glass Layer in Interconnection Dielectric Planarization", Microelectronic Engineering, vol. 5 (1986).
5 *"Doped Silicon Oxide Deposition by Atmospheric Pressure and Low Temperature Chemical Vapor Deposition Using Tetraethoxysilane and Ozone", Fujino et al., J. Electrochem. Society, vol. 138, No. 10, p. 3019 Oct. 1991.
6 *"Etching Applications and Trends of Dry Etching", Ephrath et al., □□Semiconductor Technology and Computer Systems, Ch. 2, p. 26. 1991. □□.
7 *"Etching-Applications and Trends of Dry Etching", by L.M. Eprath and G.S. □□ Mathad, Handbook of Advanced Technology and Computer Systems at 27 ff (1988).
8 *"Hot-Carrier Aging of the MOS Transistor in the Presence of Spin-On Glass as the Interlevel Dielectric", by N. Lifschitz and G. Smolinsky, IEEE Electron Device Letters, vol. 12, No. 3, p. 140 (1991).
9 *"Plasma Etch Anisotrophy", C.B. Zarowin, J. Electrochem. Soc., Solid-State □□Science and Technology, p. 1144 (1983).
10 *"Polysilicon Planarization Using Spin-On Glass", S. Ramaswami and A. Nagy, J. Electrochem. Soc., vol. 139, No. 2, p. 591 (1992).
11 *"Reactive Ion Etching", by B. Gorowitz and R. Saia, 8 VLSI Electronics, □□297ff (1984).
12 *"The Effect of Plasma Cure Temperature on Spin-On Glass", by H. Namatsu and K. Minegishi, J. Electrochem. Soc., vol. 140, No., p. 140 (1991).
13 *"Three 'Low Dt' Options for Planarizing the Premetal Dielectric on an Advanced Double Poly BiCMOS Process", by W. Dauksher, M. Miller, and C. Tracey, J. Electrochem. Soc., vol. 139, No. 2, p. 532 (1992).
14 *Handbook on Semiconductors, (ed. C. Holson), vol. 4, p. 208 (1981).
15 *IBM Technical Disclosure Bulletin, vol. 29, No. 3, p. 1328, Aug. 1986. □□.
16 *IBM Technical Disclosure Bulletin, vol. 30, No. 8, p. 252, Jan. 1988.
17 *Patent Abstracts of Japan, vol. 15, No. 348 (E-1107) Sep. 4, 1991 & JP-A-31 33 131 (Mitsubishi Electric Corp.) Jun. 6, 1991.
18 *Research Disclosure No. 282, Oct. 1987, Havant GB p. 608, "Spin on Glass □□Insulator Enhancement".
19 *VLSI Electronics Microstructures Science, vol. 8, ed. Norman Einspruch, p. □□298 (1984).
Citada por
Patente citante Fecha de presentación Fecha de publicación Solicitante Título
US7737017 *23 Dic 200815 Jun 2010Hynix Semiconductor Inc.Semiconductor device having recess gate and isolation structure and method for fabricating the same
US7833861 *1 Oct 200716 Nov 2010Hynix Semiconductor Inc.Semiconductor device having recess channel structure and method for manufacturing the same
US806779916 Nov 201029 Nov 2011Hynix Semiconductor Inc.Semiconductor device having recess channel structure and method for manufacturing the same
US9252080 *15 Oct 20142 Feb 2016Globalfoundries Inc.Dielectric cover for a through silicon via
US952492414 Dic 201520 Dic 2016Globalfoundries Inc.Dielectric cover for a through silicon via
US20070059898 *30 Mar 200615 Mar 2007Dong-Suk ShinSemiconductor devices including trench isolation structures and methods of forming the same
US20080157191 *1 Oct 20073 Jul 2008Hynix Semiconductor Inc.Semiconductor device having recess channel structure and method for manufacturing the same
US20100078757 *23 Dic 20081 Abr 2010Hynix Semiconductor Inc.Semiconductor device having recess gate and isolation structure and method for fabricating the same
US20110057261 *16 Nov 201010 Mar 2011Hynix Semiconductor Inc.Semiconductor device having recess channel structure and method for manufacturing the same
Clasificaciones
Clasificación de EE.UU.257/644, 257/634, 257/647
Clasificación internacionalH01L21/3105, H01L21/768, H01L23/522, H01L21/316, H01L21/3205, H01L23/58
Clasificación cooperativaH01L21/02274, H01L21/02126, H01L21/02164, H01L21/022, H01L21/02282, H01L21/02216, H01L21/31051, H01L21/31055, H01L21/768, H01L21/76819, H01L21/31612
Clasificación europeaH01L21/768B4, H01L21/316B2B, H01L21/3105B2B, H01L21/768, H01L21/3105B, H01L21/02K2C1L5, H01L21/02K2E3L, H01L21/02K2C3, H01L21/02K2E3B6B, H01L21/02K2C7C4B, H01L21/02K2C1L1
Eventos legales
FechaCódigoEventoDescripción
2 May 2011FPAYFee payment
Year of fee payment: 12