WO1994008078A1 - A melt-stable lactide polymer fabric and process for manufacture thereof - Google Patents

A melt-stable lactide polymer fabric and process for manufacture thereof Download PDF

Info

Publication number
WO1994008078A1
WO1994008078A1 PCT/US1993/009308 US9309308W WO9408078A1 WO 1994008078 A1 WO1994008078 A1 WO 1994008078A1 US 9309308 W US9309308 W US 9309308W WO 9408078 A1 WO9408078 A1 WO 9408078A1
Authority
WO
WIPO (PCT)
Prior art keywords
lactide
poly
polymer
melt
fibers
Prior art date
Application number
PCT/US1993/009308
Other languages
French (fr)
Inventor
Patrick Richard Gruber
Jeffrey John Kolstad
Christopher M. Ryan
Original Assignee
Cargill, Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=26752403&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO1994008078(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority claimed from US07/955,690 external-priority patent/US5338822A/en
Priority to DE1993630046 priority Critical patent/DE69330046T2/en
Priority to AT93923176T priority patent/ATE199944T1/en
Priority to BR9305661A priority patent/BR9305661A/en
Priority to CA 2124842 priority patent/CA2124842C/en
Priority to EP19930923176 priority patent/EP0615555B1/en
Priority to AU52948/93A priority patent/AU5294893A/en
Application filed by Cargill, Incorporated filed Critical Cargill, Incorporated
Priority to KR1019940701868A priority patent/KR100290012B1/en
Priority to DK93923176T priority patent/DK0615555T3/en
Priority to JP50930694A priority patent/JP3447289B2/en
Publication of WO1994008078A1 publication Critical patent/WO1994008078A1/en
Priority to FI942560A priority patent/FI106047B/en
Priority to NO942036A priority patent/NO308957B1/en
Priority to GR20010400957T priority patent/GR3036108T3/en

Abstract

A nonwoven fabric comprised of a lactide polymer. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 2% and water in concentration of less than about 2000 parts-per-million. A process for manufacturing a nonwoven fabric with the lactide polymer composition is also disclosed.

Description

A MELT-STABLE LACTIDE POLYMER FABRIC
AND PROCESS FOR MANUFACTURE THEREOF
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to fabrics comprising a melt-stable, biodegradable lactide polymer composition and a process for manufacturing such fabrics from a melt-stable, biodegradable lactide polymer.
2. Description of the Prior Art
The need for and uses of fabrics, particularly nonwoven fabrics, have increased tremendously in recent years. Production of nonwoven roll goods was estimated at 2.5 billion pounds in 1992. Nonwoven fabrics are presently used for coverstock, interlinings, wipes, carrier sheets, furniture and bedding construction, filtration, apparel, insulation, oil cleanup products, cable insulating products, hospital drapes and gowns, battery separators, outerwear construction, diapers and feminine hygiene products.
There are basically three different manufacturing industries which make fabrics, such as nonwovens; the textile, paper and extrusion industries. The textile industry garnets, cards or aerodynamically forms textile fibers into oriented webs. The paper industry employs technology for converting dry laid pulp and wet laid paper systems into nonwoven fabrics. The extrusion industry uses at least three methods of nonwoven
manufacture, those being the spunbond, melt blown and porous film methods . The melt blown method involves extruding a thermoplastic resin through a needle thin die, exposing the extruded fiber to a jet of hot air and depositing the "blown" fiber on a conveyor belt. These fibers are randomly orientated to form a web. The spunbond method also utilizes a needle thin die, but orients or separates the fibers in some manner. The porous film method employs both slit and annular dies. In one method, a sheet is extruded and drawn,
fibrillization occurs and a net-like fabric results. A problem associated with current fabric materials is that recycling of the articles containing the
fabrics, such as nonwovens, is generally not cost effective. In addition, disposal generally involves creating non-degradable waste. A vivid example is the disposal of diapers. Disposable diapers rely heavily on the use of nonwovens in their construction. Millions of diapers are disposed of each year. These disposable diapers end up in landfills or compost sites. The public is becoming increasingly alarmed over diapers that are not constructed of biodegradable material. In order to address the public's concern over the
environment, diaper manufacturers are turning to
biodegradable materials for use in their diapers.
Currently, biodegradable materials made from starch based polymers, polycaprolactones, polyvinyl alcohols, and polyhydroxybutyrate-valerate-copolymers are under consideration for a variety of different uses in the disposable article market. However, to date, there has not been a satisfactory fabric made from a biodegradable material which has properties that can withstand the present requirements of nonwoven fabrics.
Although not believed to be known as a precursor for fabrics such as nonwovens, the use of lactic acid and lactide to manufacture a biodegradable polymer is known in the medical industry. As disclosed by Nieuwenhuis et al. (U.S. Patent No. 5,053,485), such polymers have been used for making biodegradable sutures, clamps, bone plates and biologically active controlled release devices. Processes developed for the manufacture of polymers to be utilized in the medical industry have incorporated techniques which respond to the need for high purity and biocompatability in the final product. These processes were designed to produce small volumes of high dollar-value products, with less emphasis on manufacturing cost and yield . In order to meet projected needs for biodegradable packaging materials, others have endeavored to optimize lactide polymer processing systems. Gruber et al. (U.S. Pat. No. 5,142,023) disclose a continuous process for the manufacture of lactide polymers with controlled optical purity from lactic acid having physical
properties suitable for replacing present petrochemical-based polymers.
Generally, manufacturers of polymers utilizing processes such as those disclosed by Gruber et al. will convert raw material monomers into polymer beads, resins or other pelletized or powdered products. The polymer in this form may then be then sold to end users who convert, i.e., extrude, blow-mold, cast films, blow films, thermoform, injection-mold or fiber-spin the polymer at elevated temperatures to form useful
articles. The above processes are collectively referred to as melt-processing. Polymers produced by processes such as those disclosed by Gruber et al., which are to be sold commercially as beads, resins, powders or other non-finished solid forms are generally referred to collectively as polymer resins.
Prior to the present invention, it is believed that there has been ho disclosure of a combination of
composition control and melt stability requirements which will lead to the production of commercially viable lactide polymer nonwoven fabrics.
It is generally known that lactide polymers or poly(lactide) are unstable. The concept of instability has both negative and positive aspects. A positive aspect is the biodegradation or other forms of
degradation which occur when lactide polymers or
articles manufactured from lactide polymers are
discarded or composted after completing their useful life. A negative aspect of such instability is the degradation of lactide polymers during processing at elevated temperatures as, for example, during melt- processing by end-user purchasers of polymer resins. Thus, the same properties that make lactide polymers desirable as replacements for non-degradable
petrochemical polymers also create undesirable effects during processing which must be overcome.
Lactide polymer degradation at elevated temperature has been the subject of several studies, including: I. C. McNeill and H. A. Leiper, Polymer Degradation and Stability, vol. 11, pp. 267-285 (1985); I. C. McNeill and H. A. Leiper, Polymer Degradation and Stability, vol. 11, pp. 309-326 (1985); M. C. Gupta and V. G.
Deshmukh, Colloid & Polymer Science, vol. 260, pp. 308311 (1982); M. C. Gupta and V. G. Deshmukh, Colloid & Polymer Science, vol. 260, pp. 514-517 (1982); Ingo Luderwald, Dev. Polymer Degradation, vol. 2, pp. 77-98 (1979); Domenico Garozzo, Mario Giuffrida, and Giorgio Montaudo, Macromolecules, vol. 19, pp. 1643-1649 (1986); and, K. Jamshidi, S. H. Hyon and Y. Ikada, Polymer, vol. 29, pp. 2229-2234 (1988).
It is known that lactide polymers exhibit an
equilibrium relationship with lactide as represented by the reaction below:
Figure imgf000007_0001
No consensus has been reached as to what the primary degradation pathways are at elevated processing
temperatures. One of the proposed reaction pathways includes the reaction of a hydroxyl end group in a
"back-biting" reaction to form lactide. This
equilibrium reaction is illustrated above. Other proposed reaction pathways include: reaction of the hydroxyl end group in a "back-biting" reaction to form cyclic oligomers, chain scission through hydrolysis of the ester bonds, an intramolecular beta-elimination reaction producing a new acid end group and an
unsaturated carbon-carbon bond, and radical chain decomposition reactions. Regardless of the mechanism or mechanisms involved, the fact that substantial
degradation occurs at elevated temperatures, such as those used by melt-processors, creates an obstacle to use of lactide polymers as a replacement for
petrochemical-based polymers. It is apparent that degradation of the polymer during melt-processing must be reduced to a commercially acceptable rate while the polymer maintains the qualities of biodegradation or compostability which make it so desirable. It is believed this problem has not been addressed prior to the developments disclosed herein.
As indicated above, poly(lactide)s have been
produced in the past, but primarily for use in medical devices. These polymers exhibit biodegradability, but also a more stringent requirement of being bioresorbable or biocompatible. As disclosed by M. Vert, Die
Ingwandte Makromolekulare Chemie, vol. 166-167, pp. 155- 168 (1989), "The use of additives is precluded because they can leach out easily in body fluids and then be recognized as toxic, or, at least, they can be the source of fast aging with loss of the properties which motivated their use. Therefore, it is much more
suitable to achieve property adjustment through chemical or physical structure factors, even if aging is still a problem." Thus, work aimed at the bioresorbable or biocompatible market focused on poly(lactide) and blends which did not include any additives.
Other disclosures in the medical area include
Nieuwenhuis (European Patent No. 0 314 245), Nieuwenhuis (U.S. Patent No. 5,053,485), Eitenmuller (U.S. Patent No. 5,108,399), Shinoda (U.S. Patent No. 5,041,529), Fouty (Canadian Patent No. 808,731), Fouty (Canadian Patent No. 923,245), Schneider (Canadian Patent No.
863,673), and Nakamura et al., Bio. Materials and
Clinical Applications, Vol. 7, p. 759 (1987). As disclosed in these references, in the high value, low volume medical specialty market, poly(lactide) or lactide polymers and copolymers can be given the
required physical properties by generating lactide of very high purity by means of such methods as solvent extraction or recrystallization followed by
polymerization. The polymer generated from this high purity lactide is a very high molecular weight product which will retain its physical properties even if substantial degradation occurs and the molecular weight drops significantly during processing. Also, the polymer may be precipitated from a solvent in order to remove residual monomer and catalysts. Each of these treatments add stability to the polymer, but clearly at a high cost which would not be feasible for lactide polymer compositions which are to be used to replace inexpensive petrochemical-based polymers in the
manufacture of nonwoven products.
Furthermore, it is well-known that an increase in molecular weight generally results in an increase in a polymer's viscosity. A viscosity which is too high can prevent melt-processing of the polymer due to
physical/mechanical limitations of the melt-processing equipment. Melt-processing of higher molecular weight polymers generally requires the use. of increased
temperatures to sufficiently reduce viscosity so that processing can proceed. However, there is an upper limit to temperatures used during processing.
Increased temperatures increase degradation of the lactide polymer, as the previously-cited studies
disclose.
Jamshidi et al., Polymer, Vol. 29, pp. 2229-2234 (1988) disclose that the glass transition temperature of a lactide polymer, Tg, plateaus at about 57°C for poly(lactide) having a number average molecular weight of greater than 10,000. It is also disclosed that the melting point, Tm, of poly (L-lactide) levels off at about 184°C for semi-crystalline lactide polymers having a number average molecular weight of about 70,000 or higher. This indicates that at a relatively low
molecular weight, at least some physical properties of lactide polymers plateau and remain constant.
Sinclair et al. (U.S. Patent No. 5,180,765) disclose the use of residual monomer, lactic acid or lactic acid oligomers to plasticize poly(lactide) polymers, with plasticizer levels of 2-60%. Loomis (U.S. Patent No. 5,076,983) discloses a process for manufacturing a self- supporting film in which the oligomers of hydroxy acids are used as plasticizing agents. Loomis and Sinclair et al. disclose that the use of a plasticizer such as lactide or lactic acid is beneficial to produce more flexible materials which are considered to be
preferable. Sinclair et al., however, disclose that residual monomer can deposit out on rollers during processing. Loomis also recognizes that excessive levels of plasticizer can cause unevenness in films and may separate and stick to and foul processing equipment. Thus, plasticizing as recommended, negatively impacts melt-processability in certain applications.
Accordingly, a need exists for a lactide polymer composition which is melt-stable under the elevated temperatures common to melt-processing resins in the manufacture of fabrics, such as nonwovens. The needed melt-stable polymer composition must also exhibit sufficient compostability or degradability after its useful life as a fabric. Further, the melt-stable polymer must be processable in existing melt-processing equipment, by exhibiting sufficiently low viscosities at melt-processing temperatures while polymer degradation and lactide formation remains below a point of
substantial degradation and does not cause excessive fouling of processing equipment. Furthermore, the polymer lactide must retain its molecular weight, viscosity and other physical properties within
commercially-acceptable levels through the fabric manufacturing process. It will be further appreciated that a need also exists for a process for manufacturing fabrics such as nonwoven fabrics. The present invention addresses these needs as well as other problems
associated with existing lactide polymer compositions and manufacturing processes. The present invention also offers further advantages over the prior art, and solves other problems associated therewith. SUMMARY OF THE INVENTION
According to the present invention, a fabric, such as a nonwoven fabric, comprising poly(lactide) fibers is provided. A first portion of the fibers comprises a melt-stable lactide polymer composition comprising:
poly(lactide) chains having a number average molecular weight of at least 10,000, and preferably from about 10,000 to about 300,000; lactide in a concentration of less than about 2% by weight; and optionally water in a concentration of less than about 2,000 parts per
million. A process for the manufacture of the fabric is also provided. For the purposes of the present
invention, the fabric may be manufactured from any number of methods and is not to be limited by the particular method.
Optionally, stabilizing agents in the form of anti-oxidants and water scavengers may be added. Further, plasticizers, nucleating agents and/or anti-blocking agents may be added. The resultant fabric is
biodegradable and may be disposed of in an
environmentally sound fashion.
Poly(lactide) is a polymeric material which offers unique advantages as a fiber for nonwovens not only in the biodegradable sense, but in the manufacturing process as well.
Poly(lactide) offers advantages in the formation of the nonwoven fabric in a melt extrusion process. One problem that is sometimes encountered in the extrusion of fibers into a nonwoven web is poor adhesion of the fibers to one another upon cooling. Two characteristics of poly(lactides) lend themselves to enhanced adhesion: low viscosity and high polarity. Mechanical adhesion, the interlocking of fibers at adjoining points,
increases as the viscosity decreases. An advantage of poly(lactide) is that the viscosity lends itself well to fiber formation. Thus, poly(lactide) fibers adhere to one another well, resulting in a web with added strength. Also, because the surface is typically polar for most fibers, the high polarity of the poly(lactide) offers many dipole-dipole interactions, further
resulting in enhanced adhesion.
In melt blown processes, the fibers of the present invention have small diameters which are beneficial for many applications. The present fibers can have
diameters of less than about 5 μm.
The fibers of a nonwoven web of the present
invention are superior to typical polypropylene nonwoven webs in diaper construction. The typical construction of a diaper comprises an outer, water impervious back sheet, a middle, absorbent layer and an inner layer, which is in contact with the diaper wearer. The inner layer is typically made from a soft, nonwoven material such as a polypropylene nonwoven web. However,
polypropylene, due to its low polarity, has to be surface modified such that the urine passes through the inner layer, rather than being repelled. A significant advantage of the present invention is that the polarity of the poly(lactide) (without surface treatment) is ideally suited such that urine readily passes through the nonwoven web, but is not absorbed by the layer.
Thus, the poly(lactide) web of the present invention is a superior inner layer for diaper construction. The present invention may also be employed in incontinent and feminine hygiene products.
A fabric, such as a nonwoven, of the present
invention also may be used in packaging and bagging operations. Food packaging which does not require water tight packaging but requires breathability is an example of a use of the present invention. Bags such as leaf or yard bags may also be made from a nonwoven fabric of the present invention. The fabric is porous to allow air to enter the bag to begin decomposing the leaves. This is advantageous over present leaf bags, which do not allow air to penetrate into the leaf cavity. Further, the present nonwoven fabric, when used as a leaf bag, decomposes along with the leaves, thus minimizing the adverse environmental impact of the leaf bags.
Poly(lactide) processes at lower temperatures which allows the fiber to be extruded at lower temperatures than traditional polymers. This results in a cost savings to the converter because the extrusion equipment will not require as much power when run at lower
temperatures. There is also increased safety associated with lower temperatures.
A significant advantage of poly(lactide) over many fabrics used today such as polypropylene is its
biodegradability. The continued depletion of landfill space and the problems associated with incineration of waste have led to the need for development of a truly biodegradable fabric to be utilized as a substitute for non-biodegradable or partially biodegradable
petrochemical-based nonwoven fabrics. Furthermore, a poly(lactide) nonwoven web, unlike other biodegradable polymers, is believed not to support microbial growth. Starch or other biodegradable polymers, when exposed to warm, damp environments, will promote the growth of unhealthy microbes. This is undesirable in the diaper industry. Thus the present invention has yet another advantage over prior biodegradable polymers.
The above described features and advantages along with various other advantages and features of novelty are pointed out with particularity in the claims of the present application. However, for a better
understanding of the invention, its advantages, and objects attained by its use, reference should be made to the drawings which form a further part of the present application and to the accompanying descriptive matter in which there is illustrated and described preferred embodiments of the present invention. BRIEF DESCRIPTION OF THE DRAWINGS
In the drawings, in which like reference numerals indicate corresponding parts or elements of preferred embodiments of the present invention throughout the several views;
Fig. 1 is a schematic representation of a preferred process for the manufacture of a melt-stable lactide polymer composition; and
Fig. 2 is a graph showing the equilibrium
relationship between lactide and poly(lactide) at various temperatures.
Fig. 3 is a graph showing the relationship between meso-lactide concentration and energy of melting. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT(S)
The lactide polymer compositions used in fabrics disclosed herein focus on meeting the requirements of the end user melt-processor of a lactide polymer resin such as that produced from a process disclosed by Gruber et al. However, the present invention is directed to a poly(lactide) fiber and is not limited to the lactide polymer composition or process of Gruber et al. Any lactide polymer composition, which comes within the scope of this invention, may be used as a fiber for a fabric, particularly a nonwoven fabric. As disclosed herein, the problems of degradation, fouling, and lactide formation during melt-processing of lactide polymers are addressed through suggested ranges of molecular weights and compositional limits on impurities such as residual monomer, water and catalyst along with the use of stabilizing agents and catalyst-deactivating agents.
In general, according to the present invention, a melt-stable lactide polymer fabric and a process for manufacturing a melt-stable lactide polymer fabric from a melt-stable lactide polymer are disclosed. Lactide polymers are useful due to their biodegradable nature. Furthermore, lactide polymers are compostable as
illustrated in Example 15 below. Applicants believe the hydrolysis of the ester may be the key to or the first step in degradation of a lactide polymer composition. The mechanism of degradation is not key to the fabric of the present invention, however it must be recognized that such degradation makes lactide polymers desirable as replacements for presently-utilized non-degradable petrochemical-based polymers used for fabrics, such as nonwovens.
Applicants have found that the instability of lactide polymers which leads to the beneficial
degradation discussed above also creates processing problems. These processing problems include generation of lactide monomer at elevated temperatures and loss in molecular weight believed due to chain scission
degradation of the ester bonds and other
depolymerization reactions which are not completely understood. No consensus has been reached as to what are the primary degradation pathways at elevated
processing temperatures. As previously disclosed, these may include such pathways as equilibrium-driven
depolymerization of lactide polymers to form lactide and chain scission through hydrolysis of the ester bonds along with other pathways. For purposes of the present invention, the exact mechanism of degradation at
elevated temperatures is not critical.
It is to be understood, however, that degradation of lactide polymers is both beneficial and detrimental.
Benefits derive from degradability when articles
manufactured from such polymers are discarded. The same or similar types of degradation are detrimental if they occur during processing or prior to the end of the article's useful life. Melt-Processing
It is believed that a manufacturer of lactide polymers from a lactide monomer will produce a lactide polymer resin which is in the form of beads or pellets. The melt-processor will convert the resin to a fiber for a fabric by elevating the temperature of the resin above at least its glass transition temperature but normally higher and extruding the fiber into a fabric, such as a nonwoven. It is to be understood that the conditions of elevated temperatures used in melt-processing cause degradation of lactide polymers during processing.
Degradation under melt-processing conditions is shown experimentally in Example 7 based on equilibrium,
Example 10 based on catalyst concentration, Example 11 based on catalyst activity, Example 13 based on use of stabilizers and Example 14 based on moisture content. As can be seen in these examples, it is understood that several factors appear to affect the rate of degradation during melt-processing. Applicants have addressed these factors in a combination of compositional requirements and the addition of stabilizing or catalyst-deactivating agents to result in a polymer of lactide which is melt-stable.
In addition, melt-processing frequently produces some proportion of trimmed or rejected material.
Environmental concerns and economical efficiencies dictate that this material be reused, typically by regrinding and adding back the material into the polymer feed. This introduces additional thermal stress on the polymer and increases the need for a melt-stable polymer composition.
Melt Stability
The lactide polymers of the present invention are melt-stable. By "melt-stable" it is meant generally that the lactide polymer, when subjected to melt-processing techniques, adequately maintains its physical properties and does not generate by-products in sufficient quantity to foul or coat processing
equipment. The melt-stable lactide polymer exhibits reduced degradation and/or reduced lactide formation relative to known lactide polymers. It is to be understood that degradation will occur during melt-processing. The compositional requirements and use of stabilizing agents as disclosed herein reduces the degree of such degradation to a point where physical properties are not significantly affected by melt-processing and fouling by impurities or degradation by-products such as lactide does not occur. Furthermore, the melt-stable polymer should be melt-processable in melt-processing equipment such as that available
commercially. Further, the polymer will preferably retain adequate molecular weight and viscosity. The polymer should preferably have sufficiently low
viscosity at the temperature of melt-processing so that the extrusion equipment may create an acceptable
nonwoven fabric. The temperature at which this
viscosity is sufficiently low will preferably also be below a temperature at which substantial degradation occurs.
Polymer Composition
The melt-stable lactide polymer fabric of the present invention comprises poly(lactide) polymer chains having a number average molecular weight of at least 10,000 and preferably from about 10,000 to about
300,000. In a preferred composition for a melt blown nonwoven, the number average molecular weight ranges from about 15,000 to about 100,000. In the most
preferred composition, the number average molecular weight ranges from about 20,000 to about 80,000. In a spunbond nonwoven fabric, the preferred number average molecular weight range is from about 50,000 to about 250,000. In a most preferred embodiment, the number average molecular weight range is from about 75,000 to about 200,000. As detailed in Example 9 , it appears that the physical properties such as modulus, tensile strength, percentage elongation at break, impact strength, flexural modulus, and flexural strength remain
statistically constant when the lactide polymer samples are above a threshold molecular weight. The lower limit of molecular weight of the polymer compositions of the present invention is set at a point above the threshold of which a fiber has sufficient diameter and density. In other words, the molecular weight cannot be lower than is necessary to achieve a targeted fiber diameter and density. As detailed in Example 22, there is a practical upper limit on molecular weight based on increased viscosity with increased molecular weight. In order to melt-process a high molecular weight lactide polymer, the melt-processing temperature must be
increased to reduce the viscosity of the polymer. As pointed out in the Examples, the exact upper limit on molecular weight must be determined for each melt-processing application in that required viscosities vary and residence time within the melt-processing equipment will also vary. Thus, the degree of degradation in each type of processing system will also vary. Based on the disclosure of Example 22, it is believed that one could determine the suitable molecular weight upper limit for meeting the viscosity and degradation requirements in any application.
Lactide polymers can be in either an essentially amorphous form or in a semi-crystalline form. For various applications it will be desirable to have the polymer in one of these configurations. As detailed in Example 24, the desired range of compositions for semi-crystalline poly(lactide) is less than about 12% by weight meso-lactide and the remaining percent by weight either L-lactide or D-lactide, with L-lactide being more readily available. A more preferred composition
contains less than about 9% by weight meso-lactide with the remainder being substantially all L-lactide.
For applications where an amorphous polymer is desired, the preferred composition of the reaction mixture is above 9% by weight meso-lactide and a more preferred composition contains above 12% by weight meso- lactide with the remaining lactide being substantially all L-lactide mixture, or D-lactide can be used to control the potential crystallinity in a predominantly L-lactide mixture.
Addition of even small amounts of meso-lactide to the polymerization mixture results in a polymer which is even slower to crystallize than polymerization mixtures having lesser amounts of meso-lactide, as detailed in Example 23. Beyond about 12% meso content the polymer remains essentially amorphous following a typical annealing procedure. This contrasts with the behavior of D,L-lactide, which can be added at a concentration of 20% to the polymerization mixture and still produce a semi-crystalline polymer following the annealing
procedure. These results are detailed in Example 24.
There are three main methods to increase the rate of crystallization. One is to increase chain mobility at low temperatures, by adding, for example, a plasticizing agent. The plasticizer must be selected carefully, however, and preferably will be of limited compatibility so that it will migrate to the amorphous phase during crystallization. Dioctyl adipate is an example of a plasticizer which helps crystallization rates in
poly(lactide), as detailed in Example 25. A second method to increase the rate of crystallization is to add a nucleating agent, as detailed in Example 26. A third method is to orient the polymer molecules. Orientation can be accomplished by drawing during film casting, drawing of fibers, blowing films, stretching of film or sheet after it is cast (in multiple directions, if desired), or by the flow of polymer through a small opening in a die. The alignment generated helps to increase the rate of crystallization, as detailed in Example 27.
Heat setting may also be employed to increase the degree of crystallinity in the fibers. Heat setting involves exposing the fabric to elevated temperatures, as shown in Plastics Extrusion Technology, F. Hensen (ed), Hanser Publishers, New York, 1988, pp 308, 324. It is preferred to heat set with the fiber or nonwoven fabric under tension to reduce shrinkage during the setting process.
Applicants recognize that an essentially amorphous lactide polymer may have some crystallinity.
Crystalline poly L-lactide exhibits an endotherm of roughly 92 Joules per gram at its melting temperature of 170°-190°C. The melting point changes with composition. The degree of crystallinity is roughly proportional to the endotherm on melting. For purposes of the present invention, it is meant by an amorphous or non-crystalline poly(lactide) to be a poly(lactide) or lactide polymer which exhibits a melting endotherm of less than about 10 Joules per gram in the temperature range of about 130-200°C. Semi-crystalline
poly(lactide) exhibits a melting endotherm above about 10 joules per gram.
The residual monomer concentration in the melt-stable lactide polymer composition is less than about 2% by weight. In a preferred composition, the lactide concentration is less than about 1% by weight, and a most preferred composition has less than about 0.5% by weight of lactide. Contrary to disclosures in the art. Applicants have found that the monomer cannot be used as a plasticizing agent in the resin of the present
invention due to significant fouling of the extrusion equipment. As detailed in Example 16, it is believed the low levels of monomer concentration do not
plasticize the final polymer. The water concentration within the melt-stable lactide polymer composition is less than about 2,000 parts-per-million. Preferably this concentration is less than 500 parts-per-million and most preferably less than about 100 parts-per-million. As detailed in
Example 14, the polymer melt-stability is significantly affected by moisture content. Thus, the melt-stable polymer of the present invention must have the water removed prior to melt-processing. Applicants recognize that water concentration may be reduced prior to
processing the polymerized lactide to a resin. Thus, moisture control could be accomplished by packaging such resins in a manner which prevents moisture from
contacting the already-dry resin. Alternatively, the moisture content may be reduced at the melt-processor's facility just prior to the melt-processing step in a dryer. Example 14 details the benefit of drying just prior to melt-processing and also details the problems encountered due to water uptake in a polymer resin if not stored in a manner in which moisture exposure is prevented or if not dried prior to melt-processing. As detailed in these examples, Applicants have found that the presence of water causes excessive loss of molecular weight which may affect the physical properties of the melt-processed polymer.
In a preferred composition of the present invention, a stabilizing agent is included in the polymer
formulation to reduce degradation of the polymer during production, devolatilization, drying and melt processing by the end user. The stabilizing agents recognized as useful in the present nonwoven fibers may include antioxidants and/or water scavengers. Preferred
antioxidants are phosphite-containing compounds,
hindered phenolic compounds or other phenolic compounds. The antioxidants include such compounds as trialkyl phosphites, mixed alkyl/aryl phosphites, alkylated aryl phosphites, sterically hindered aryl phosphites, aliphatic spirocyclic phosphites, sterically hindered phenyl spirocyclics, sterically hindered
bisphosphonites, hydroxyphenyl propionates, hydroxy benzyls, alkylidene bisphenols, alkyl phenols, aromatic amines, thioethers, hindered amines, hydroquinones and mixtures thereof. As detailed in Example 13, many commercially-available stabilizing agents have been tested and fall within the scope of the present melt- stable lactide polymer nonwoven fabric composition.
Biodegradable antioxidants are particularly preferred.
The water scavengers which may be utilized in preferred embodiments of the melt-stable lactide polymer nonwoven fiber include: carbodiimides, anhydrides, acyl chlorides, isocyanates, alkoxy silanes, and desiccant materials such as clay, alumina, silica gel, zeolites, calcium chloride, calcium carbonate, sodium sulfate, bicarbonates or any other compound which ties up water. Preferably the water scavenger is degradable or
compostable. Example 19 details the benefits of
utilizing a water scavenger.
In a preferred composition of the present invention, a plasticizer is included in the polymer formulation to improve the nonwoven fiber quality of the lactide polymer. More particularly, plasticizers reduce the melt viscosity at a given temperature of poly( lactide), which aides in processing and extruding the polymer at lower temperatures and may improve flexibility and reduce cracking tendencies of the finished fabric.
Plasticizers also lower the melt viscosity of
poly(lactide), thereby making it easier to draw-down the fibers to a small diameter.
A plasticizer is useful in concentration levels of about 1 to 35%. Preferably, a plasticizer is added at a concentration level of about 5 to 25%. Most preferably, a plasticizer is added at a concentration level of about 8 to 25%. Selection of a plasticizing agent requires screening of many potential compounds and consideration of several criteria. For use in a biodegradable nonwoven fabric the preferred plasticizer is to be biodegradable, non- toxic and compatible with the resin and relatively nonvolatile.
Plasticizers in the general classes of alkyl or aliphatic esters, ether, and multi-functional esters and/or ethers are preferred. These include alkyl phosphate esters, dialkylether diesters, tricarboxylic esters, epoxidized oils and esters, polyesters,
polyglycol diesters, alkyl alkylether diesters,
aliphatic diesters, alkylether monoesters, citrate esters, dicarboxylic esters, vegetable oils and their derivatives, and esters of glycerine. Most preferred plasticizers are tricarboxylic esters, citrate esters, esters of glycerine and dicarboxylic esters. Citroflex A4 ® from Morflex is particularly useful. These esters are anticipated to be biodegradable. Plasticizers containing aromatic functionality or halogens are not preferred because of their possible negative impact on the environment.
For example, appropriate non-toxic character is exhibited by triethyl citrate, acetyltriethyl citrate, tri-n-butyl citrate, acetyltri-n-butyl citrate,
acetyltri-n-hexyl citrate, n-butyltri-n-hexyl citrate and dioctyl adipate. Appropriate compatibility is exhibited by acetyltri-n-butyl citrate and dioctyl adipate. Other compatible plasticizers include any plasticizers or combination of plasticizers which can be blended with poly(lactide) and are either miscible with poly(lactide) or which form a mechanically stable blend. Corn oil and mineral oil were found to be incompatible when used alone with poly(lactide) because of phase separation (not mechanically stable) and migration of the plasticizer. Volatility is determined by the vapor pressure of the plasticizer. An appropriate plasticizer must be sufficiently non-volatile such that the plasticizer stays substantially in the resin formulation throughout the process needed to produce the nonwoven fabric.
Excessive volatility can lead to fouling of process equipment, which is observed when producing fabrics by melt processing poly(lactide) with a high lactide content. Preferred plasticizers should have a vapor pressure of less than about 10 mm Hg at 170°C, more preferred plasticizers should have a vapor pressure of less than 10 mm Hg at 200°C. Lactide, which is not a preferred plasticizer, has a vapor pressure of about 40 mm Hg at 170°C. Example 6 highlights useful
plasticizers for the present invention.
In a preferred composition, nucleating agents may be incorporated during polymerization. Nucleating agents may include selected plasticizers, finely divided minerals, organic compounds, salts of organic acids and imides and finely divided crystalline polymers with a melting point above the processing temperature of poly(lactide). Examples of useful nucleating agents include talc, sodium salt of saccharin, calcium
silicate, sodium benzoate, calcium titanate, boron nitride, copper phthalocyanine, isotactic polypropylene, low molecular weight poly(lactide) and polybutylene terephthalate.
In a preferred composition, fillers may be useful to prevent blocking or sticking of layers or rolls of the nonwoven fabric during storage and transport. Inorganic fillers include clays and minerals, either surface modified or not. Examples include talc, diatomaceous earth, silica, mica, kaolin, titanium dioxide, and wollastonite. Preferred inorganic fillers are
environmentally stable and non-toxic. Organic fillers include a variety of forest and agricultural products, either with or without
modification. Examples include cellulose, wheat, starch, modified starch, chitin, chitosan, keratin, cellulosic materials derived from agricultural products, gluten, nut shell flour, wood flour, corn cob flour, and guar gum. Preferred organic fillers are derived from renewable sources and are biodegradable. Fillers may be used either alone or as mixtures of two or more fillers. Example 5 highlights useful anti-blocking fillers for the present invention.
Surface treatments may also be used to reduce blocking. Such treatments include corona and flame treatments which reduce the surface contact between the poly(lactide) based fabric and the adjacent surface.
For certain applications, it is desirable for the fabric to be modified to alter the water transport properties. Surfactants may be incorporated into the web of the present invention to increase the water transport properties.
Surfactants which are useful can be subdivided into cationic, anionic, and nonionic agents.
With regard to cationic compounds, the active molecule part generally consists of a voluminous cation which often contains a long alkyl residue (e.g. a quaternary ammonium, phosphonium or sulfonium salt) whereby the quaternary group can also occur in a ring system (e.g. imidazoline). In most cases, the anion is the chloride, methosulfate or nitrate originating from the quaternization process.
In the anionic compounds, the active molecule part in this class of compounds is the anion, mostly an alkyl sulfonate, sulfate or phosphate, a dithiocarbamate or carboxylate. Alkali metals often serve as cations.
Nonionic antistatic agents are uncharged, surface-active molecules of a significantly lower polarity than the above mentioned ionic compounds and include polyethylene glycol esters or ethers, fatty acid esters or ethanolamides, mono-or diglycerides or ethyoxylated fatty amines. The above surfactants may also act as antistatic agents, which may be desirable.
Pigments or color agents may also be added as necessary. Examples include titanium dioxide, clays, calcium carbonate, talc, mica, silica, silicates, iron oxides and hydroxides, carbon black and magnesium oxide.
In the manufacture of the melt-stable lactide polymer compositions of the present invention, the reaction to polymerize lactide is catalyzed. Many catalysts have been cited in literature for use in the ring-opening polymerization of lactones. These include but are not limited to: SnCl2, SnBr2, SnCl4, SnBrA, aluminum alkoxides, tin alkoxides, zinc alkoxides, SnO, PbO, Sn (2-ethyl hexanoates), Sb (2-ethyl hexanoates), Bi (2-ethyl hexanoates), Na (2-ethyl hexanoates)
(sometimes called octoates), Ca stearates, Mg stearates, Zn stearates, and tetraphenyltin. Applicants have also tested several catalysts for polymerization of lactide at 180°C which include: tin(II) bis (2-ethyl hexanoate) (commercially available from Atochem, as Fascat 2003, and Air Products as DABCO T-9), dibutyltin diacetate (Fascat 4200®, Atochem), butyltin tris(2-ethyl hexanoate) (Fascat 9102®, Atochem), hydrated monobutyltin oxide (Fascat 9100®, Atochem), antimony triacetate (S-21,
Atochem), and antimony tris(ethylene glycoxide) (S-24, Atochem). Of these catalysts, tin(II) bis (2-ethyl hexanoate), butyltin tris (2-ethyl hexanoate) and
dibutyltin diacetate appear to be most effective.
Applicants have found the use of catalysts to polymerize lactide significantly affects the stability of the resin product. It appears the catalyst as incorporated into the polymer also is effective at catalyzing the reverse depolymerization reaction.
Example 10 details the effect of residual catalyst on degradation. To minimize this negative effect, in a preferred composition, the residual catalyst level in the resin is present in a molar ratio of initial monomer-to-catalyst greater than about 3,000:1,
preferably greater than about 5,000:1 and most
preferably greater than about 10,000:1. Applicants believe a ratio of about 20,000:1 may be used, but polymerization will be slow. Optimization of catalyst levels and the benefits associated therewith are
detailed in Example 20. Applicants have found that when the catalyst level is controlled within these
parameters, catalytic activity is sufficient to
polymerize the lactide while sufficiently low to enable melt-processing without adverse effect when coupled with low residual monomer level and low water concentration as described above in polymers of molecular weight between 10,000 to about 300,000. It is believed in most applications the addition of a stabilizing agent may be unnecessary if catalyst level is optimized.
Applicants have also found that catalyst
concentration may be reduced subsequent to
polymerization by precipitation from a solvent. Example 21 demonstrates potential catalyst removal by
precipitation from a solvent. This produces a resin with reduced catalyst concentration. In an alternative embodiment, the catalyst means for catalyzing the polymerization of lactide to form the poly(lactide) polymer chains which was incorporated into the melt-stable lactide polymer composition during polymerization is deactivated by including in the melt-stable lactide polymer composition a catalyst deactivating agent in amounts sufficient to reduce catalytic depolymerization of the poly(lactide) polymer chains. Example 11 details the benefits of utilizing a catalyst deactivating agent. Such catalyst-deactivating agents include hindered, alkyl, aryl and phenolic hydrazides, amides of aliphatic and aromatic mono- and dicarboxylic acids, cyclic amides, hydrazones and bishydrazones of aliphatic and aromatic aldehydes, hydrazides of aliphatic and aromatic mono- and dicarboxylic acids, bis-acylated hydrazine derivatives, and heterocyclic compounds. A preferred metal deactivator is Irganox® MD1024 from Ciba-Geigy. Biodegradable metal deactivators are particularly preferred.
In an alternative embodiment, the catalyst
concentration is reduced to near zero by utilizing a solid-supported catalyst to polymerize lactide. The feasibility of utilizing such a catalyst is detailed in Example 8. It is believed catalysts which may be utilized include supported metal catalysts, solid acid catalysts, acid clays, alumina silicates, alumina, silica and mixtures thereof.
In a preferred composition, the catalyst usage and/or deactivation is controlled to reduce
depolymerization of the poly(lactide) polymer during melt-processing to less than about 2% by weight
generation of lactide from a devolatilized sample in the first hour at 180°C and atmospheric pressure. More preferably, the amount of lactide generated is less than about 1% by weight in the first hour and most preferably less than about 0.5% by weight in the first hour.
A preferred melt-stable lactide polymer composition is the reaction product of polymerization of lactide at a temperature greater than about 160°C. Applicants have found that polymerization at higher temperatures result in a characteristically different polymer which is believed to have improved melt stability due to
increased transesterification during polymerization.
The benefits of higher temperature polymerization are detailed in Example 12.
Melt-Stable Lactide Polymer Process
The process for the manufacture of a melt-stable lactide polymer comprises the steps of first providing a lactide mixture wherein the mixture contains about 0.5% by weight to about 50% by weight meso-lactide and about 99.5% by weight or less L-lactide and/or D-lactide.
Such purified lactide stream may be such as that
produced in the process disclosed by Gruber et al., although the source of lactide is not critical to the present invention.
The lactide mixture is polymerized to form a lactide polymer or poly(lactide) with some residual unreacted monomer in the presence of a catalyst means for
catalyzing the polymerization of lactide to form
poly( lactide). Catalysts suitable for such
polymerization have been listed previously. The
concentration of catalysts utilized may be optimized as detailed in the following examples and discussed
previously.
In a preferred embodiment, a stabilizing agent, which may be an antioxidant and/or a water scavenger is added to the lactide polymer. It is recognized that such stabilizing agents may be added simultaneously with or prior to the polymerization of the lactide to form the lactide polymer. The stabilizing agent may also be added subsequent to polymerization.
As previously disclosed, the catalyst usage is adjusted and/or deactivation agent is added in a
sufficient amount to reduce depolymerization of
poly(lactide) during melt-processing to less than 2% by weight generation of lactide from a devolatilized sample in the first hour at 180°C and atmospheric pressure.
More preferably, the stabilizing agent controls lactide generation to less than 1% by weight and most preferably less than 0.5% by weight in the first hour at 180°C and atmospheric pressure. Alternatively, the control of catalyst concentration to optimize the balance between necessary catalytic activity to produce poly(lactide) versus the detrimental effects of catalytic
depolymerization or degradation of the lactide polymer may be utilized to obviate the need for adding a
stabilizing agent. The lactide polymer is then devolatilized to remove unreacted monomer which may also be a by-product of decomposition reactions or the equilibrium-driven depolymerization of poly(lactide). Any residual water which may be present in the polymer would also be removed during devolatilization, although it is
recognized that a separate drying step may be utilized to reduce the water concentration to less than about 2,000 parts-per-million. The devolatilization of the lactide polymer may take place in any known
devolatilization process. The key to selection of a process is operation at an elevated temperature and usually under conditions of vacuum to allow separation of the volatile components from the polymer. Such processes include a stirred tank devolatilization or a melt-extrusion process which includes a devolatilization chamber and the like. An inert gas sweep is useful for improved devolatization.
In a preferred process for manufacture of a melt- stable lactide polymer composition, the process also includes the step of adding a molecular weight control agent to the lactide prior to catalyzing the
polymerization of the lactide. For example, molecular weight control agents include active hydrogen-bearing compounds, such as lactic acid, esters of lactic acid, alcohols, amines, glycols, diols and triols which function as chain-initiating agents. Such molecular weight control agents are added in sufficient quantity to control the number average molecular weight of the poly(lactide) to between about 10,000 and about 300,000.
Next referring to Figure 1 which illustrates a preferred process for producing a melt-stable lactide polymer composition. A mixture of lactides enters a mixing vessel (3) through a pipeline (1). A catalyst for polymerizing lactide is also added through a
pipeline (13). Within mixing vessel (3) a stabilizing agent may be added through a pipeline (2). A water scavenger may also be added through the pipeline (2). The stabilized lactide mixture is fed through a pipeline (4) to a polymerization process (5). The polymerized lactide or lactide polymer leaves the polymerization process through a pipeline (6). The stream is fed to a second mixing vessel (8) within which a stabilizing agent and/or catalyst deactivating agent may be added through a pipeline (7). The stabilized lactide polymer composition is then fed to a devolatilization process (10) through a pipeline (9). Volatile components leave the devolatilization process through a pipeline (11) and the devolatilized lactide polymer composition leaves the devolatilization process (10) in a pipeline (12). The devolatilized lactide composition is fed to a resin-finishing process (14). Within the resin-finishing process the polymer is solidified and processed to form a pelletized or granular resin or bead. Applicants recognize the polymer may be solidified and processed to form resin or bead first, followed by devolatilization. The resin is then fed to a drying process (16) by conveyance means (15). Within the drying process (16) moisture is removed as a vapor through pipeline (17). The dried lactide polymer resin leaves the drying process (16) by a conveyance means (18) and is fed to a melt-processing apparatus (19). Within the melt-processing apparatus (19) the resin is converted to a useful article as disclosed above. The useful article leaves the melt-processing apparatus (19) through a conveyance means (20).
The following examples further detail advantages of the system disclosed herein:
Example 1
Melt Spinning of Poly(lactide)
Melt spinning of poly(lactide) having a weight average molecular weight of 140,000, a residual lactide content of about 1.1% and an original lactide mixture of about 7% by weight meso-lactide was performed on a 13 mm. single screw extruder with a gear pump and fitted with a 7 hole multifilament spinning head. The hole diameter was 0.4 mm. The spinline length, the distance from the spinning head to the take-up roll, was 1.7 meters. Polymer throughput was 1 g/min/hole. Filaments were drawn down by drawing through a circular aspirator which makes use of high velocity air to apply a force downward on the fibers. Post drawing of the fibers was also done on a draw stand or heated godet.
The process conditions were varied to find
conditions under which fibers could be made from
poly(lactide). Extrusion temperatures were varied from 150 to 170°C and the take up velocity was varied from 500 to 6,000 meters/min. Fiber diameters were measured and are shown in Table 1 for the various fiber spinning conditions. With a microscope equipped with a light polarizer, birefringence was measured to assess the extent of polymer orientation within the fiber as a function of spinning conditions. Table 1 shows
birefringence as a function of take-up velocity and fiber diameter as a function of take-up velocity
respectively.
Table 1
Take-up Extrusion Fiber
Velocity Temperature Diameter Birefringence
(meters/min) (°C) (microns) ×1000
2674 170 19.0 13.84
6179 160 12.5 15.84
4656 160 14.4 12.71
3177 160 17.6 9.09
4656 150 14.4 14.94
3421 150 16.8 8.04
3117 150 17.6 11.82
478 150 45.0 0.91 Fibers collected at a take-up velocity of 478 meters/min were post drawn on a heated godet. This apparatus is a series of rolls, including an unwind roll on the front and a take-up roll on the back. With the take up roll rotating faster than the unwind roll, the fiber is stretched. The rolls in between the unwind and take-up are heated to a temperature of 50°C to soften the polymer and allow the fiber to be drawn. Measuring fiber diameter allows calculation of the draw ratio and birefringence relates to the degree of orientation of the polymer chains. Table 2 summarizes the drawing data. The data illustrates it is possible to postdraw the fibers to increase the orientation of the fibers.
Table 2
Initial Final Draw Birefringence
Diameter Diameter Ratio × 1000
45.00 26.00 3.00 16.64
45.00 25.10 3.18 19.73
45.00 24.80 3.32 21.94
45.00 24.00 3.50 19.58
Example 2
Properties of Poly(lactide) Melt Spun Fibers.
In an apparatus similar to that used in Example 1, poly(lactide) having a weight average molecular weight of about 100,000, a residual lactide content of less than about 1% and an original lactide mixture of about 10% by weight of meso-lactide was melt spun into a fiber. The optical composition was such that upon annealing, (the sample was held at 100°C for 90 minutes, the oven was turned off and was allowed to cool to room temperature), the polymer exhibited an endothermic melt peak with a peak temperature of 140°C with an endotherm of 36.1 joules/gram. The poly(lactide) fibers were post drawn as in Example 1. The thermal and mechanical properties are shown in Table 3. The results compare favorably to standard fiber resins such as polypropylene and nylon. The elongation and modulus compare favorably to
commercial fibers. Further, poly(lactide) exhibited an affinity to crystallize under the conditions of fiber spinning.
Table 3
Properties Resin As-Spun Drawn Polyprop. Nylon 6,6 Melt Temp (°C) 133 140 140 170 265
Heat of Fusion (J/g) 2.4 14.2 26.4 105 xxxxx Denier (g/9000m) xxxxx 162 57 xxxxx xxxxx Tenacity (g/den) xxxxx 0.97 2.75 6.5 5.4 Break Elongation xxxxx 165% 38% 34% 20% Young's Modulus (g/den) xxxxxxxxxx 22 44 68 34
Example 3
Melt Blown Fabrics from Poly(lactide)
On a six inch melt blown nonwoven line equipped with a single screw extruder, poly(lactide) of a weight average molecular weight of about 80,000, a residual lactide content of about 0.6%, an original lactide mixture of about 9% by weight of meso-lactide and a water content of about 70 ppm was converted into melt blown nonwoven webs. This process involves feeding resin pellets into a feeding hopper of an extruder having a one inch single screw and extruding molten polymer through a die containing many small holes out of which emerges small diameter fiber. The fiber diameter is attenuated at the die as the fiber emerges using high velocity hot air. Three inches from the die exit is a rotating collection drum on which the fibrous web is deposited and conveyed to a wind up spool. The melt blown line is of standard design as in Malkan et al.
(Nonwovens: An Advanced Tutorial, TAPPI press, Atlanta, 1989, pp 101-129). The die used had 121 holes with a diameter of 0.020 inch per hole.
Conditions were varied to find conditions under which poly(lactide) could be made into a useful nonwoven fabric. The die temperature was varied from 380 to 480°F, the air temperature was varied from 458 to 500°F, the die-to-collector distance varied from 6 to 14 inches and the air velocity varied from approximately 12 to 18 cu-ft/min/inch web.
The resultant poly(lactide) webs were tested for performance using standard tests for melt blown fabrics. The basic weight of all webs was 1 oz/sq-yd. Fiber
diameter and fiber diameter variability were measured using a scanning electronic microscope. Tensile stress-strain properties were measured using ASTM method D-1682-64.
Bursting strength was measured using the Mullen Bursting Tester and ASTM method D-3387. Filtration efficiency was assessed using an aerosol having 0.1 micron sodium chloride particles. The filtration test involved making a 20 gram/liter NaCl solution and making an aerosol of the solution with a concentration of 100 milligram per cubic meter. The aerosol was thereafter passed through the fabric at 31 liters/minute. Sensors were placed both upstream and downstream of the fabric, with the difference reflecting the amount remaining in the filter. Air
permeability, another feature important to filtration, was measured according to ASTM D737-75 and reported as cubic feet of air per square feet of fabric per minute. All of these performance measures were compared to standard polypropylene fabrics. The data illustrates poly(lactide) processes as well as polypropylene. Poly(lactide) is capable of forming fine or small diameter fibers. Fibers having diameters of less than about 5 μm are shown.
Further, poly(lactide) nonwoven webs have a high filtration efficacy as well as good air permeability. The results are shown in Table 4.
Figure imgf000038_0001
Example 4
Melt Blow Nonwovens made from Poly(lactide).
Melt blown fabrics were made with poly(lactide) using the same equipment and procedure as in Example 3. The extrusion temperature was 320°F, screw speed was 8 rpm, die temperature was 315°F, air temperature and air velocity were at 400°F and 12 cu ft/min/inch web respectively. Die-to-collector distance was 13 inches.
The poly(lactide) used in this test had a weight average molecular weight of about 66,000, a residual lactide concentration of about 1.3% and an original lactide mixture of about 9% by weight of meso-lactide. This lower molecular weight resulted in softer nonwoven fabrics than Example 3 and had good hand. Fiber diameters were measured and found to be 11.57 μm. Other tests done on this fabric was the air permeability test having a value of 4.26, bursting strength having a value of 5.4, and filtration efficiency having a value of 14.0%.
Example 5
Anti-Blocking Agents
Two injection molded disks, 2.5 inch diameter, were placed together with a 94 gram weight on top and held at 50ºC for 24 hours. The disks had the following agents compounded therein. The disks were then cooled to room temperature and pulled apart by hand and ranked for
blocking characteristics (considerable, slight and none). The following are the results:
Table 5
AGENTS
Poly(lactide) control considerable
22% wheat gluten none
10% wheat gluten slight
22% pecan shell none
15% pecan shell slight
23% wollastonite slight
28% Ultratalc 609 none
23% Ultratalc 609 none
28% Microtuff F talc slight
22% Microtuff F talc slight
14% Microtuff F talc slight
2% Microtuff F talc considerable
Example 6
Plasticizer Agents
Dried pellets of devolatilized poly(lactide) were processed in a twin screw extruder to allow compounding of various plasticizing agents. The strands leaving the extruder were cooled in a water trough and chopped into pellets. Samples of the pellets were heated at 20°C/minute to 200°C in a DSC apparatus, held at 200°C for 2 minutes and rapidly cooled to quench the samples. The quenched samples were then reheated in the DSC apparatus increasing at 20°C/minute to determine the glass transition
temperature. These samples were compared to a polymer with no plasticizer. The effect of the plasticizer on the glass transition temperature is shown in the table below. Glass transition temperatures are taken at the mid-point of the transition. Table 6
Change in Tg/wt.
SAMPLE Tg(C) percent additive
Control 54.8 ┄
8% Dioctyl adipate 35.0 2.5
Control+40% silica 54.5 ┄
Control+40% silica+
5% dioctyl adipate 36.0 3.7
Control 54.6 ┄
6% Citroflex A-4* 42.6 2.0
12% Citroflex A-4 31.4 1.9
Control 59.3 ┄
1.6% Citroflex A-4 56.3 1.9
2.9% Citroflex A-4 53.1 2.1
Control 58.4 ┄
2.1% Citroflex A-4 56.1 1.1
3.4% Citroflex A-4 50.5 2.3
Control 61.6 ┄
18.6% Citroflex A-2 54.7 0.4
13.1% Citroflex B-6 52.4 0.7
12.6% Citroflex A-6 53.8 0.6
*Citroflex is a registered trademark of Morflex, Inc., Greensboro, NC. A-4 is the designation of acetyltri-n-butyl citrate. A-2 is the designation of acetyltriethyl citrate, A-6 is the designation of acetyltri-n-hexyl citrate, and B-6 is the designation of n-butyryltri-n-hexyl citrate.
These results show the effectiveness of these
plasticizers in reducing the glass transition temperature of poly(lactide).
The procedure above was tried using corn oil as a plasticizer. Visual observation showed the corn oil to be not compatible, forming a film on the surface. Corn oil and mineral oil were both not effective as a primary plasticizer with poly(lactide). They may still be useful as a secondary plasticizer, in combination with a
compatible primary plasticizer. Example 7
Lactide and Poly(lactide) Equilibrium Concentrations Experiments were conducted to determine the equilibrium concentration of lactide and poly(lactide) at different temperatures. In these experiments a sample of lactide was polymerized in the presence of a catalyst (tin (II) bis(2- ethyl hexanoate)) and held at a fixed temperature for 18 hours or greater. Beyond this time the residual monomer concentration is believed essentially constant. The content of residual monomer was determined by GPC analysis. GPC analysis was conducted with an Ultrastyragel® column from Waters Chromatography. The mobile phase was
chloroform. A refractive index detector with molecular weight calibration using polystyrene standards was used. The GPC temperature was 35°C. Data analysis was completed using the software package Baseline, model 810, version 3.31.
The results of tests conducted on several samples at various temperatures are summarized in the graph of Fig. 2 as indicated by X's on such graph. Also plotted on the graph of Fig. 2 are data points cited in A. Duda and S. Penczek, Macromolecules, vol. 23, pp. 1636-1639 (1990) as indicated by circles on the graph. As can be seen from the graph of Fig. 2, the equilibrium concentration, and thus the driving force behind the depolymerization of
poly(lactide) to form lactide, increases dramatically with increased temperature. Thus, melt-processing at elevated temperatures results in degradation of the lactide polymer to form lactide on the basis of equilibrium alone. For example, lactide concentrations below about 2% cannot be directly obtained at temperatures of 140°C or above due to the identified equilibrium relationship between lactide and poly(lactide). Example 8
Lactide Polymerization in the Presence of a Solid Supported Catalyst
Tin (II) Oxide
24 grams of L-lactide (melting point about 97°C) and 6 grams of D,L-lactide (for the purposes of this invention, D,L-lactide has a melting point of about 126°C) were combined in a round bottom flask with 0.033 grams of Tin (II) oxide, as a fine powder. This corresponds to the catalyst level of 852:1, molar ratio lactide to tin. The flask was then purged with dry nitrogen 5 times. This was lowered into an oil bath at 160°C with magnetic stirring. Polymerization time was 8 hours.
Amberlyst 36
24 grams of L-lactide and 6 grams of D,L-lactide were combined in a round bottom flask with 1.06 grams of
Amberlyst 36 resin beads. The flask was purged 5 times with dry nitrogen. The flask was lowered into an oil bath at 140°C with magnetic stirring. Polymerization time was 8 hours. The resin had a stated proton content of 1 meq/gram dry weight resin. The resin was prepared by rinsing 2 times with 10 volumes dry methanol, then dried for several hours under high vacuum for several hours at 40°C.
The polymerization results are shown below:
TABLE 7
Sample Mn Mw PDI % Conversion Tin (II) Oxide 77,228 103,161 1.34 54.0
Amberlyst 1,112 1,498 1.34 73.5 Example 9
Molecular Weight Relationship to Physical Properties of Lactide Polymers
Poly(lactide) samples with various molecular weights and optical compositions were prepared by polymerizing blends of L-lactide and meso-lactide at 180°C under
nitrogen in a 1-gallon sealed reactor. Tin(II) bis(2-ethyl hexanoate) catalyst was added at a monomer-to-catalyst ratio of 10,000:1. After about 1 hour the molten polymer was drained from the reactor using nitrogen pressure. The sample was poured into a pan and placed in a vacuum oven at about 160°C for about 4 hours to bring the reaction to near equilibrium levels.
Portions of the samples were then dried under vacuum and processed in an injection molding apparatus (New
Britain 75 from New Britain Machine Co.) to produce
standard test bars for physical property testing. The results of physical property testing are shown in the following Table 8. The physical property tests were made according to ASTM methods D 638, D 256, and D 790. The reported results are the averages of several tests.
Samples of the test bars after injection molding were analyzed by GPC for molecular weight. Other portions of the test bars were reground and tested in a capillary viscometer to determine the melt-viscosity. These results are also included in Table 8.
Statistical analysis of the data revealed no
correlations which were statistically significant between either optical composition or molecular weight and the mechanical properties of modulus, tensile strength,
percentage elongation at break, notched Izod impact
strength, flexural modulus, or flexural strength. The independence of these properties on molecular weight indicates that all of these samples were above a
"threshold" molecular weight required to achieve the intrinsic properties of the polymer in a preferred composition.
The viscosity data show significant correlations with molecular weight. This dependence documents the practical limitation and necessity of controlling polymer molecular weight below an upper limit at which it is impractical to melt-process the polymer. At high molecular weight, high viscosity prevents processing by standard melt-processing equipment. Increases in temperature to reduce viscosity dramatically increase polymer degradation and lactide formation which is also unacceptable.
TABLE 8
Molecular Viscosity at 173ºC (Pa·S)
Weight After
Sample Meso Lactide Injection Final Shear Rate Shear Rate
I.D. In Blend, Wt% Weight IV (dl/e) 100 S-1 1000 S-1
6 A0 A1000 0.86 5.5 2.9
5 10 5A000 0.88 10. A 7.2
A 20 59000 0.91 10. A 7.2
8 10 6A000 1.02 15.7 10.0
9 40 68000 0.97 12.6 8.1
7 20 Dataproducts LZR-1230 *M&G* /HGCDALZR12A .PRSies ; of Injection Molded Samples
Tensile Flexural Flexural
Sample Modulus Strength % Elongat:ion IZOD Impact Modulus Strength
I.D. MPSI (Yld) PSI at Break ft · lb. /in MPSI PSI
6 0.55 6600 3.3 0.39 0.53 11300
5 0.56 7800 3.5 0.46 0.54 12500
4 0.56 7600 3.9 0.32 0.53 12500
8 0.55 7700 3.4 0.47 0.53 12400
9 0.59 6700 3.1 0.40 0.52 10600
7 0.56 7400 3.3 0.45 0.51 12400
10 0.55 6700 3.0 0.47 0.52 9900
Example 10
Effect of Residual Catalyst on Polymer Degradation
Polymer samples were prepared at four levels of
catalyst, corresponding to monomer to catalyst molar ratios of 5,000:1, 10,000:1, 20,000:1, and 40,000:1. The catalyst utilized was tin (II) bis(2-ethyl hexanoate). These samples were then subjected to heating in a TGA apparatus (TA Instruments, Inc., model 951 thermogravometric analyzer with a DuPont 9900 computer support system) with a nitrogen purge. Isothermal conditions of 200°C for 20 minutes were used. The samples were then analyzed by GPC with a
viscosity-based detector and a universal calibration curve to determine the extent of breakdown in molecular weight. The GPC apparatus for this test was a Viscotek Model 200 GPC and a Phenomenex column. The TGA analysis typically resulted in about a 5% loss in weight and molecular weight drops of 0 to 70%.
The number average molecular weights were converted to a milliequivalent per kilogram basis (1,000, 000/Mn) in order to calculate a rate of chain scission events. The results below represent averages of 2-4 replicates on each of the four samples.
TABLE 9
Catalyst level Scission Rate
(monomer/catalyst) (meq/kg*min)
5,000 1.33
10,000 0.62
20,000 0.44
40,000 0.12
The rate of chain scission was directly proportional to the residual catalyst level, demonstrating the detrimental effect of catalyst activity on melt-stability under
conditions similar to melt-processing. This instability, however, is distinguished from the instability due to the equilibrium relationship between lactide and poly(lactide) detailed in Example 7, in that loss of molecular weight due to catalytic depolymerization by chain scission is evident.
EXAMPLE 11
Catalyst Deactivation Experiment
Two runs were made in a laboratory Parr reactor.
Lactide feed was 80% L-lactide and 20% D,L-lactide.
Molecular weight was controlled by adding a small quantity of lactic acid, the target molecular weight was 80,000 Mn.
Lactide was charged to the reactor as a dry mix, the reactor was purged 5 times with nitrogen, and heated up to 180°C. At this point catalyst (5000:1 initial monomer to catalyst molar ratio, Fascat® 2003) was charged through a port in the top of the reactor. The reaction was allowed to proceed for 70 minutes at 180°C, with mechanical
agitation. Conversion at this point was 93-94%, close to the equilibrium value at 180°C of 96% poly(lactide) from Figure 2. This point is considered t-zero, designating the completion of the polymerization reaction and the beginning of the mixing time.
In the control experiment, a sample was taken and the mixture was held at temperature with continued agitation. Samples were taken periodically through a port in the reactor bottom. After 4 hours the reactor was drained.
In the example experiment, a sample was taken and 0.25 weight % of a metal deactivator (Irganox® MD 1024®) was added through the catalyst addition port. The mixture was held at temperature with continued agitation and samples were withdrawn periodically. The reactor was drained after 4 hours.
GPC analysis (utilizing the method of Example 7) for these samples was divided into three parts: polymer with molecular weight over 4,000 (for which the Mn and Mw numbers are reported), the percent oligomers (comprising the region with molecular weight greater than lactide but less than 4,000, as distinguished from oligomers as defined by Loomis to include only oligomers up to a molecular weight of 450), and percent lactide (residual monomer). The structure of the oligomers was not certain, but it is believed they were primarily cyclic structures. It is also believed that the metal deactivator, if unreacted, will elute with the oligomer fraction. Quantification of the oligomer fraction is difficult, because the GPC trace is near the baseline in this region.
The analysis of the polymer samples as withdrawn from the reactor at various time intervals for the control and experimental compositions are shown below in Table 10.
TABLE 10
Control Mn Mw % Polymer % Oligomer % Monomer t-zero 67,100 119,500 94 0 6.0
0.5 hr 62,500 119,000 95 0.7 3.9
1.0 hr 61,500 116,100 96 0 3.6
1.5 hr 56,000 111,600 95 1.5 3.3
2.0 hr 57,600 110,900 96 0.9 3.1
4.0 hr 51,400 105,400 94 3.3 3.1
Test Mn Mw % Polymer % Oligomer % Monomer t-zero 63,200 110,700 93 3.5 3.8
0.5 hr 52,100 108,600 92 4.6 2.9
1.0 hr 52,700 109,200 92 4.9 2.8
1.5 hr 53,400 107,200 93 4.0 3.1
2.0 hr 59,700 111,100 94 0.6 5.8
4.0 hr 51,200 107,300 91 6.1 3.3
The samples were then ground and placed in a 120°C oven under vacuum (pressure 0.1 inch Hg) for 14 hours.
Sample analyses after this treatment are shown below in Table 11.
TABLE 11
Control Mn Mw % Polymer % Oligomer % Monomer t-zero 45,500 88,500 98 2.2 0.0
0.5 hr 45,000 88,700 98 2.0 0.0
1.0 hr 43,900 87,200 98 2.0 0.0
1.5 hr 42,600 84,000 98 2.2 0.0
2.0 hr 42,000 85,200 97 3.2 0.0
4.0 hr 41,900 82,800 98 2.0 0.0
Test Mn Mw % Polymer % Oligomer % Monomer t-zero 39,300 76,700 96 4.0 0.0
0.5 hr 43,900 85,100 98 2.4 0.0
1.0 hr 55,300 98,600 96 3.8 0.0
1.5 hr 48,400 96,200 95 4.5 0.0
2.0 hr 48,900 101,900 95 5.0 0.0
4.0 50,600 101,900 94 5.6 0.0 In all cases the polymer was completely devolatilized (0.0% residual lactide monomer). The data also clearly show that the metal deactivator reduced the degradation of polymer during the devolatilization step (as indicated by the greater loss in Mn for the control samples from Table 9 to Table 10 versus the Test samples). One hour of mixing appears to be long enough to develop most of the benefit.
The samples were stored at room temperature under nitrogen for about 1 week and reanalyzed, as shown below in Table 12.
TABLE 12
Control Mn Mw % Polymer % Oligomer % Monomer t-zero 33,500 71,000 100 0.1 0.0
0.5 hr 43,400 95,800 99 1.0 0.0
1.0 hr 44,900 96,300 100 0.1 0.0
1.5 hr 45,900 95,000 100 0.0 0.0
2.0 hr 45,900 94,100 100 0.2 0.0
4.0 hr 43,100 90,100 99 1.3 0.0
Test Mn Mw % Polymer % Oligomer % Monomer t-zero 44,600 84,900 100 0.0 0.0
0.5 hr 45,300 90,600 99 1.2 0.0
1.0 hr 47,800 100,000 98 2.4 0.0
1.5 hr 46,600 98,900 96 3.5 0.0
4.0 57,700 110,200 96 4.0 0.3
Equilibrium lactide levels are estimated to be less than 0.2 weight % at room temperature. Consistent with that, essentially no lactide was observed in any of the samples (detection limit about 0.1 weight %). The oligomer content in the non-stabilized samples declined and some increase in molecular weight was noted, perhaps due to reincorporation of the (cyclic) oligomers into the polymer. The oligomer depletion reaction was inhibited in the stabilized polymers, with the extent of inhibition
dependent on the length of time that the additive was mixed.
The samples were then reheated to 180°C in sealed vials and held for one hour as a simulation of melt-processing. Analysis of the samples after the heat treatment is given below in Table 13.
TABLE 13
Control Mn Mw % Polymer % Oligomer % Monomer t-zero 23,900 60,000 88 8.4 4.0
0.5 hr 23,900 59,600 90 7.7 2.7
1.0 hr 23,700 58,800 88 9.3 2.7
1.5 hr 24,700 58,000 86 10.0 3.8
2.0 hr 26,100 56,400 90 6.8 2.7
4.0 hr 24,800 58,700 92 6.6 1.9
Test Mn Mw % Polymer % Oligomer % Monomer t-zero 33,900 64,300 95 2.2 3.1
0.5 hr 17,900 34,600 94 4.8 1.7
1.0 hr 21,200 42,900 94 4.6 1.8
1.5 hr 29,200 56,900 98 0.5 1.8
2.0 hr missing
4.0 hr 35,700 71,400 95 3.7 1.7
The data for molecular weight show that if the metal deactivator is not mixed into the system long enough then it can have a detrimental impact on stability in the melt. The samplesDataproducts LZR-1230 *M&G* /HGCDALZR124.PRSight alone. More importantly, the metal deactivator samples show significantly less lactide reformation than the control samples. This effect is gained even in the samples which were mixed for only 0.5 hour. The metals deactivated samples averaged only 1.8% lactide after one hour at 180°C, compared to an average of 3.0% lactide for the controls. The equilibrium level at 180°C is about 3.6% from Figure 2. Thus, the use of metal deactivators can reduce the
troublesome reformation of lactide during melt-processing of the finished polymer. Example 12
Effect of Increased Polymerization Temperature on Polymer Characteristics
L-lactide (Boeringer Ingleheim, S-grade) was used as received, meso-lactide (PURAC) was purified by distillation to remove traces of D- and L-lactide. The melting point of the purified meso-lactide was 54°C. Lactide mixtures were made up to the following ratios: 100% L-lactide, 90/10 L-lactide/meso-lactide, 70/30 L-lactide/meso-lactide, 50/50 L-lactide/meso-lactide, and 100% meso-lactide. Catalyst level was 2,500:1 molar ratio of initial monomer to tin with the tin being tin(II) bis (2-ethyl hexanoate) (Fascat® 9002). Lactic acid was added as a molecular weight control agent to target a number average molecular weight of 50,000 (the same amount was added to all samples). Polymerization times were estimated to obtain conversions of 50% and 90%. For 120°C this was 4 hours and 16 hours, respectively. For 180°C these times were 10 minutes and 50 minutes,
respectively. Below in Table 9 are the GPC results (method of Example 7) of tests on the polymer samples produced by this procedure.
TABLE 14
L/meso Temp Mn Mw PDI %Conv
1002 L 120°C 31,014 33,774 1.09 53.2
45,864 52,574 1.15 87.1
1002 L 180°C 27,785 32,432 1.17 46.7
56,839 98,125 1.73 93.3
90/10 120°C 34,541 38,586 1.12 62.3
29,222 34,466 1.18 89.3
90/10 180°C 31,632 35,713 1.13 48.5
57,925 110,841 1.91 94.8
70/30 120°C 41,211 45,222 1.10 60.1
58,284 71,257 1.22 89.1
70/30 180°C 32,292 37,401 1.16 53.8
51,245 107,698 2.10 96.5
50/50 120°C 15,888 17,969 1.13 57.8
25,539 31,834 1.25 90.6
50/50 180°C 34,375 42,018 1.22 62.5
44,590 98,028 2.20 95.5
1002 meso 120°C 33,571 40,635 1.21 73.4
45,237 68,142 1.51 94 . 3
1002 meso 180°C 30 , 976 42 , 987 1.39 67.6
40,038 83,815 2.09 96.6
The results show that the ultimate number average molecular weight was not significantly affected by the temperature of polymerization, with an average of 41,000 at 120°C and 50,000 at 180°C. This implies that each lactic acid molecule initiates about one polymer chain, regardless of temperature. The ultimate weight average molecular weight is, however, significantly affected by temperature. At 120°C the weight average molecular weight averaged
52,000 and at 180°C the average was 100,000. This is believed to be due to a relative increase in the rate of transesterification at 180°C. The polydispersity index (PDI) at high conversion also reflects this, averaging 1.3 at 120°C and 2.0 at 180°C. It is believed these
differences would have a significant effect on the melt- processing characteristics of the polymer, with the higher weight average molecular weight of the polymer produced at 180°C expected to translate into better melt strength and processability.
These experiments show that polymerization at a higher temperature results in a polymer that is characteristically different. Further, the glass transition temperature for the samples polymerized at higher temperature is higher.
Example 13
Experiments with Stabilizing Agents
and Metal Deactivators
Test 1
Conditions: vial polymerization, (Lactide is melted under a nitrogen-purged atmosphere in a round bottom flask with stirring. Catalyst and additives are added and aliquots of the mixtures are pipetted into silanized glass vials. Typically 5-10 grams of reaction mixture are used in a 16 ml. vial. The vials are tightly capped and placed into a preheated oil bath.) 10,000:1 molar ratio of
lactide-to-tin, tin(II) bis (2-ethyl hexanoate) catalyst, 0.2 wt% Ultranox®626 in tetrahydrofuran (THF). 180°C.
Time was 90 minutes.
The control with tin only polymerized to 84% conversion and reached a MWn of 31,700. The example with tin and Ultranox® polymerized to 83% conversion and reached a number average molecular weight (MWn) of 39,800; an
increase of 26% over the control.
The control sample turned light yellow, the sample with stabilizer remained colorless. Test 2
Conditions: vial polymerization, 5000:1 molar ratio of lactide to tin, tin(II) bis (2-ethyl hexanoate) catalyst, 0.25 wt % Ultranox®626 (in THF) . 180°C. Time was 60 minutes. Lactide was used from the above described Gruber et al. process.
The control with tin alone polymerized to 67%
conversion and reached a MWn of 62,900. The example with tin and Ultranox® polymerized to 66% conversion and reached a MWn of 75800; an increase of 21% over the control.
A second example with tin(II) bis (2-ethyl hexanoate), Ultranox®, and 0.50% of Irganox® 1076, which is a phenolic antioxidant, polymerized to 66% conversion and reached a number average molecular weight (MWn) of 74500; an increase of 18% over the control.
All samples were a dark yellow color, although the samples with stabilizer had a slightly lower absorbance at 300 nm.
Test 3
Conditions: vial polymerization, 10,000:1 molar ratio of lactide to tin, tin(II) bis (2-ethyl hexanoate) catalyst, 180°C, 80% L-lactide and 20% D,L-lactide purchased from Henley and Aldrich, respectively. Lactic acid was added to control molecular weight to about 75,000 at full
conversion. One sample included 0.25% Ultranox® 626 phosphite stabilizer, one included 0.25% Irganox® 1076 antioxidant, and one control sample.
Samples were taken at various times and analyzed by GPC for conversion and molecular weight (the method of Example 7). The results are summarized in Table 15 below. TABLE 15
Time Cont .rol Irganox® Ultranox®
(hrs) Mn %conv Mn %conv Mn % conv
1 31,000 46 35,900 41 66,500 61
2 45,400 74 56,800 74 102,700 83
4 69,600 93 74,100 93 97,200 91
11 52,900 95 60,700 95 71,500 94
The sample with phosphite stabilizer polymerized faster, shown by the higher conversion at 1 and 2 hours, and went to a higher molecular weight than the control or the sample with Irganox . The phosphite stabilized sample had a molecular weight more than 30% higher than the control for all time periods.
Test 4
The experiment above was repeated to compare the control to the phosphite-stabilized polymer, as summarized in Table 16 below.
TABLE 16
Time Control Ultranox®
(hrs) Mn %conv Mn %conv
1 36,600 37 71,500 59
2 51,700 70 95,200 85
4 64,400 91 103,700 94
8 58,100 96 95,700 94
The sample with phosphite stabilizer again polymerized faster and went to a higher molecular weight than the non-stabilized sample. The phosphite stabilized sample had a molecular weight more than 60% higher than the control for all time periods.
Test 5
Conditions: vial polymerization, 5,000:1 molar ratio of lactide to tin, tin(II) bis (2-ethyl hexanoate) catalyst, 180°C, 80% L-lactide and 20% D,L-lactide purchased from Henley and Aldrich. Lactic acid was added to control number average molecular weight to an estimated 80,000 at full conversion. One sample was run with 0.25% Ultranox® 626 phosphite stabilizer, one with 0.25% Irganox® 1076 antioxidant, and one control sample.
Samples taken at various times and analyzed by GPC (the method of Example 1) for conversion and molecular weight. The results are tabulated in Table 17 below.
TABLE 17
Time Cont :rol Irganox® Ultranox®
(hrs) Mn %conv Mn %conv Mn % conv
1 83,600 76 121,900 83 162,300 87
4 74,400 93 104,300 95 123,900 96
24 40,200 96 52,000 96 96,900 97
48 34,200 97 30,400 96 56,500 96
72 25,000 96 22,400 96 69,500 96 The phosphite-stabilized sample had a molecular weight more than 60% higher than the control for all time periods. After 72 hours it had a molecular weight 2.8 times higher than the control. The sample with antioxidant showed an initial increase in molecular weight, relative to the control, but the effect disappeared after 48 hours.
The phosphite stabilized sample was significantly lighter in color than the control or the antioxidant treated sample. Test 6
Conditions: vial polymerization, 5000:1 molar ratio of lactide to tin, tin(II) bis (2-ethyl hexanoate) catalyst, 0.25 wt % Ultranox®626 (in THF). 180°C. Time was two hours. Gruber et al. process lactide washed with isopropyl alcohol was used.
The control with tin alone polymerized to 95%
conversion and reached a number average molecular weight of 118,000. The example with tin and Ultranox® polymerized to 93% conversion and reached a number average-molecular weight of 151,000, an increase of 28% over the control.
Test 7
Conditions: vial polymerization at 180°C. 5000:1 molar ratio of lactide to tin, tin(II) bis (2-ethyl
hexanoate) catalyst. Lactide was 80% L-lactide and 20% D,L-lactide, purchased from Henley and from Aldrich.
Lactic acid was added to target the molecular weight to an Mn of 80,000. All stabilizers were added at 0.25 weight%. Molecular weight (number average) was determined for samples pulled at 3 hours, while rate constants were based on samples pulled at 1 hour. The results of these
screening tests on many stabilizing agents following the above procedure are detailed below in Table 18. Product designations in Table 18 are tradenames or registered trademarks.
TABLE 18
Relative
Sample MWn % Conversion Rate
Control 1 65,000 95.9 90 Control 2 85,000 95.9 100 Control 3 76,000 96.6 100 Control 4 69,000 96.2 100 Control 5 74,000 96.8 110 Control 6 70,000 97.2 110
PHOSPHITES
Ultranox 626 (GE) 103,000 96.8 100 Weston TDP (GE) 64,000 70.0 60 Weston PDDP (GE) 67,000 76.7 60 Weston PNPG (GE) 92,000 94.1 100 Irgafos 168 (Ciba-Geigy) 95,000 95.3 120 Weston 618 (GE) 99,000 95.1 100
Sandostab P-EPQ (Sandoz) 108,000 94.7 110 Weston TNPP (GE) 88,000 97.9 130 PHENOLIC ANTIOXIDANTS
Irganox 1010 (Ciba-Geigy) 95,000 97.5 110
Cyanox 1790 (Cyanamid) 98,000 96.9 120
BHT 87,000 96.5 130
Irganox 1076 (Ciba-Geigy) 121,000 97.8 130
Topanol CA (ICI) 84,000 96.6 160
AMINES
Tinuvin 123 (Ciba-Geigy) 65,000 94.8 70
Tinuvin 622 (Ciba-Geigy) 82,000 95.7 80
Naugard 445 (Uniroyal) 93,000 98.2 120
THIOETHER
Mark 2140 (Witco) 77,000 97.0 120
METAL DEACTIVATORS
Irganox MD1024 (Ciba-Geigy) 34,000 65.7 10 Naugard XL-1 (Uniroyal) 91,000 95.8 110 Note, that with a few exceptions, the phosphites and the phenolic antioxidants provide increased molecular weight with no reduction in polymerization rate. Of the amines, only Naugard® 445 provided stabilization without a rate decrease. The metal deactivators are expected to deactivate the catalyst, as was observed for Irganox®
MD1024. The Naugard® XL-1 did not accomplish deactivation.
Example 14
Polymer Melt Stability as a Function of Moisture Content Lactide, produced and purified in a continuous (Gruber et al.) process, was fed at a rate of 3 kg/hr to a
continuous polymerization pilot plant. Catalyst was added with a metering pump at the rate of 1 part catalyst to 5000 parts lactide on a molar basis. The reaction system was blanketed with nitrogen. The reactor vessels consist of two continuous stirred tank reactors (CSTR) in series. The first had a 1-gallon capacity and the second had a 5-gallon capacity. The reactors were run 60-80% liquid filled and at 170-180°C. Polymer melt pumps moved the liquid from CSTR 1 to CSTR 2, and from CSTR 2 through a die into a cooling water trough. The polymer strand thus produced was pulled from the trough by a pelletizer and stored as pellets.
The pelletized poly(lactide) was put into a drying hopper and dried at 40°C under flowing dry air. Samples were pulled after one hour and four hours. These samples were then run through a single screw Brabender® extruder, with a retention time of approximately 3 minutes. Samples were analyzed for moisture by an automatic Karl Fischer apparatus and for molecular weight by GPC (the method of Example 7). The results of these tests are documented in Table 19 below. TABLE 19
Extruder Weight Average
Sample Temperature (C ) Molecular Weight
Initial 63 , 000
Dried 1 hour
( 1200 ppm H2O ) 137 44 , 000
145 48 , 000
162 35 , 000
179 30 , 000
Dried 4 hours
(150 ppm H2O ) 140 63 , 000
140 69 , 000
160 65 , 000
178 68 , 000
These results show the detrimental effect of water in the lactide polymer resin during melt polymerization and the need to properly dry the poly( lactide ) before melt-processing .
Example 15
Degradation of Crystalline and
Amorphous Poly(lactide)
Two literature references disclose poly(D,L- lactide) to degrade faster than poly(L-lactide), attributing the result to crystallinity of poly(L-lactide). These are: Kulkarni et al., J. Biomed. Mater. Res., vol. 5, pp. 169-181, (1971); Makino et al., Chem. Pharm. Bull., vol. 33, pp. 1195-1201, (1985). An experiment was conducted to measure the effect of crystallinity on polymer degradation and is detailed below.
An amorphous poly(lactide) sample (clear, and less than 1% crystallinity based on DSC) and a crystalline
poly(lactide) sample (opaque, and approximately 50%
crystallinity based on DSC) were subjected to
biodegradation in a compost test (50°C, with aeration). The DSC apparatus was a TA Instruments, Inc., model 910 differential scanning calorimeter with DuPont 9900 computer support system typically programmed to heating at a rate of 10°C per minute to 200°C. The samples had different optical composition, with the crystalline sample being more than 90% poly(L-lactide) and the amorphous sample being less than 80% poly(L-lactide) with the balance being either poly(D,L-lactide) or poly(meso-lactide). Samples of each polymer were subjected to a compost test (ASTM D 5338) which included mixing a stabilized compost and providing a source of humidified air while maintaining a temperature of about 50°C. The amorphous sample was completely degraded after 30 days of composting. The crystalline sample was only 23% degraded based on carbon dioxide after the same period of time.
Additional samples of these two polymers were subjected to chemical hydrolysis at 50°C (hydrolysis is believed to be the rate-limiting step in the biodegradation process). The chemical hydrolysis procedure included placing 0.1 gram poly(lactide) in 100 ml of 0.2M phosphate buffer (pH = 7.4). The samples were held for 1 week, then filtered, washed with deionized water, and dried at 25°C under vacuum. The initial weight average molecular weight for each sample was about 70,000. After 1 week the amorphous sample had a weight average molecular weight of 10,000 and the crystalline sample had a weight average molecular weight of 45,000, determined by GPC (the method of Example 7). Neither sample had significant weight loss at this time.
Both of these tests demonstrate that degradation of crystalline poly(lactide) is slower than degradation of amorphous poly(lactide). Example 16
Effect of Monomer Concentration on Film Modulus
Poly(lactide) was precipitated in methanol from a chloroform solution in order to remove the residual lactide monomer. GPC analysis (the method of Example 1) showed the precipitated polymer to contain 0.0% lactide.
The polymer was dissolved in chloroform to make a 10 wt% solution, and lactide was added back to make 5 separate solutions which, after removing the chloroform, are
calculated to produce films containing 0.0, 0.2, 0.4, 1.0 and 4.0 weight% lactide in poly( lactide). These solutions were solvent cast onto glass, dried overnight at room temperature in a fume hood, and removed to a vacuum oven. The films were hung in the vacuum oven and dried at 30ºC for 72 hours. GPC analysis of the vacuum-dried films showed measured lactide levels of 0.0, 0.0, 0.4, 0.7 and 3.7 wt%.
The films were then tested for film modulus using ASTM procedure D882.
The results are shown below in Table 20.
TABLE 20
Elastic
% Tensile Std. % Std. Modulus Std. ctide (psi avg.) Dev. Elongation Dev. (psi avg.) Dev.
0 5490 636 2.85 0.14 730,000 103,000
0 6070 123 2.85 0.22 818,000 35,000
0.4 5670 227 2.75 0.27 779,000 44,000
0.7 5690 343 4.04 1.12 749,000 58,000
3.7 5570 458 3.33 1.43 738,000 66,000
Example 17
Rate of Water Uptake Versus Optical Composition
Samples of poly(lactide), made from 80% L-lactide and 20% of either D,L-lactide or meso-lactide, were ground to pass a 20 mesh screen. The samples were dried and
devolatilized under vacuum then removed to a constant humidity chamber maintained at 24°C and 50% relative humidity. The rate of moisture pick-up was determined gravimetrically, with the final results verified by Karl-Fischer water analysis. The rate of moisture pickup is shown below in Table 21.
TABLE 21
Parts Per Million
Time We ight Gain
(Minutes) L/D,L Polymer L/Meso Polymer
10 600 1000
30 1100 1500
60 1500 1800
120 1600 2100
870 2100 2600
Final (Karl -Fischer) 3000 2600
Example 18
Standard Test of Melt Stability
A standard test for determining melt stability is as follows:
A small sample (200 grams or less) of polymer is ground or pelletized and devolatilized by holding under vacuum (about 10 mm Hg) at a temperature of 130°C or less for 18 hours. At this point the residual lactide content should be 1 wt% or less. Portions (1-5 grams) of the
devolatilized sample are then placed in a 16 ml sample vial, tightly capped, and placed in a 180°C oil bath.
Samples are removed at times of 15 minutes and 1 hour and analyzed for lactide content by GPC or other appropriate techniques . Lactide which may collect on the cooler portions of the vial is included in the product work-up and test.
Melt-stabilized poly(lactide) will show less than 2% lactide in the 15 minute sample, and more preferably less than 2% lactide in the 1 hour sample. The most highly stabilized poly( lactide)s will maintain lactide contents of less than 1% in both the.15 minute and 1 hour samples, preferably less than 0.5%. An unstabilized poly(lactide) may reach the equilibrium lactide content at 180°C of 3.6 wt%, or may go even higher as lactide is driven from the polymer melt and collects on the cooler top walls of the vial.
Example 19
Water Scavenger Experiments
Dried poly(lactide) pellets were processed in a twin screw extruder to devolatilize and to prepare a portion with 0.5% by weight of a water scavenger (Stabaxol® P).
The strands leaving the extruder are cooled in a water trough and chopped into pellets. Samples of the control and the test sample were then analyzed by the Karl Fischer technique for moisture content, with no drying. The control sample contained 1700 ppm water, the test sample had 450 ppm water. The control sample was then dried under nitrogen at 40°C, reducing the water content to 306 ppm. A vacuum-dried control sample had 700 ppm water.
The as-produced test sample and the dried control samples were then processed in a 1/2" single screw extruder (Brabender®) at 160°C, with a retention time of 3 minutes. The number average molecular weight for the dried control sample dropped from an initial value of 44,000 to a final value of 33,000 for the 306 ppm water sample and to 28,000 for the 700 ppm water sample. The test sample number average molecular weight dropped from an initial value of 40,000 to a final value of 33,000. This sample shows how the water scavenger protected the polymer from moisture pick-up, imparting the same stability as a thorough drying of the control sample. Combining a water scavenger with appropriate drying is expected to give even greater stability.
Example 20
Optimization of Catalyst Concentration A mixture of 80% L-lactide and 20% D,L-lactide was polymerized using three different levels of tin(II) bis (2-ethyl hexanoate) catalyst. Batches were prepared at initial monomer/catalyst molar ratios of 1000:1, 3000:1, and 20,000:1. Polymerization times were adjusted to reach high conversion without being excessively long and thereby causing degradation in the melt. The reaction times were 1,2 and 20 hours, respectively. The polymerization
temperature was 180°C. The polymers were ground to a coarse powder and devolatilized at 125°C and 10 mm Hg overnight. The samples were then reground and 1-gram portions of each were placed into silanized vials, 16 ml capacity. The vials were sealed and placed into an oil bath at 180°C. Vials were then removed at various times and the samples were analyzed by GPC after dissolution in chloroform. The molecular weights and lactide contents are shown below in Table 22.
TABLE 22
Sample Time Number Average Weight Average Lactide
(min) Molecular Weight Molecular We ight Weight
1000 : 1 0 39,000 81,300 0.8
5 28,100 57,300 2.4
15 25,800 49,700 2.8
30 23,100 43,800 3.7
60 22,800 43,200 3.6
3000 : 1 0 53,100 113,600 0.6
5 39,000 76,400 0.4
15 30,300 65,400 1.9
30 29,000 60,400 2.7
60 28,200 55,200 2.8
20000 : 1 0 89,200 184,000 0.0
5 81,200 165,100 0.0
15 54,300 134,600 0.1
30 51,100 119,600 0.0
60 49,500 111,000 0.0
These results show the benefit of optimizing the catalyst level used in the polymerization process. Note that both lactide reformation and molecular weight
retention benefits are realized from the reduced catalyst levels (higher monomer/catalyst ratio).
It is believed catalyst levels should be limited to 1000:1 for the high end of catalyst usage, with 3000:1 being more preferable and showing somewhat improved stability. Lower levels still, such as 20000:1, show greatly improved stability. Beyond this level it is believed the polymerization rates become too slow to be practical.
Example 21
Removal of Tin Catalyst from Poly(lactide) by Precipitation
45 grams of L-lactide and 13 grams of D,L-lactide were charged with 78 milligrams of crystalline lactic acid to a 200 ml round bottom flask. This was heated to 180°C with magnetic stirring in an oil bath and blanketed with dry nitrogen. Catalyst in the form of tin(II) bis (2-ethyl hexanoate) was added as 0.20 ml of a 0.47 g/ml solution in THF after the molten lactide was at temperature. The mixture was allowed to stir for one minute and then
pipetted into 3 silanized glass vials, which were then sealed and placed into a 180°C oil bath for 75 minutes. The vials were allowed to cool and the polymer recovered by breaking the glass. The polymer was ground to a coarse powder and dissolved in chloroform to make a 10% solution. The polymer contained 3.8% residual monomer and had a number average molecular weight of 70,000 as determined by GPC measurement (the method of Example 9).
500 ml of methanol were placed in a 1-liter glass blender flask. The blender was turned on to medium speed and 50 ml of the polymer in chloroform solution was poured in over a period of three minutes. After one additional minute of blending the mixture was filtered, then rinsed with 100 ml of methanol, and dried overnight under vacuum. The polymer consisted of a fibrous mat. It contained 0.3% residual monomer and had a number average molecular weight of 66,900. The measured tin level in the precipitated polymer was 337 ppm by weight, compared to a calculated value of 466 ppm for the as-produced polymer. This result indicates the feasibility of reducing residual catalyst levels in lactide polymers by solvent precipitation with the benefit of improved stability as detailed in Example 20. Example 22
Samples of devolatilized poly(lactide) were tested in a Rosand Model 14°C capillary rheometer. The die was 1 mm diameter and 16 mm long, with an entry angle of 180°. The table below gives the pressure drop across the die as a function of nominal shear rate (not Rabinowitsch corrected) for various molecular weights and temperatures.
Table 23
Results at 150°C.
Nominal Pressure shear rate Drop
Mn MW Temp. (°C) (s-1) (MPa)
34,000 70,000 150 192 2.0
384 5.5
960 10.0
1920 13.8
4800 19.7
9600 23.7 52,000 108,000 150 192 9.9
384 15.6
960 19.9
1920 23.9
4800 29.4
9600 - - - -
60,000 137,000 150 192 7.4
384 11.1
960 16.6
1920 21.0
4800 - - - -
9600 - - - -
183,000 475,000 150 192 19.1
384 27.0
960 31.4
1920 - - - -
4800 - - - -
9600 - - - -
Results at 175°C.
Nominal Pressure shear rate Drop
Mn MW Temp. (°C) (s-1) (MPa) 34,000 70,000 175 192 0.4
384 0.5
960 3.4
1920 5.5
4800 9.2
9600 12.5
52,000 108,000 175 192 2.2
384 4.6
960 7.6
1920 11.5
4800 17.2
9600 22.1
183,000 475,000 175 192 11.5
384 16.6
960 20.2
1920 24.4
4800 29.9
9600 - - - - Results at 200°C.
Nominal Pressure shear rate Drop
Mn MW Temp. (°C) (s-1) (MPa)
60,000 137,000 200 192 0.5
384 1.6
960 3.3
1920 5.3
4800 - - - -
9600 13.2
183,000 475,000 200 192 7.0
384 11.0
960 14.2
1920 17.9
4800 21.6
9600 - - - - Example 23
Effect of Meso-lactide Concentration on Rate of
Crystallization
Polymer samples of various optical composition were prepared by polymerizing mixtures of L-lactide and meso-lactide with Tin II bis (2-ethyl hexanoate) catalyst at a temperature of about 180°C. A portion of each sample was tested in a Mettler Differential Scanning Calorimeter Model 30 (DSC) by heating from -20°C to 200°C at 20°C/minute. The sample was then held at 200°C for 2 minutes to
completely melt any crystals. The sample was thereafter rapidly quenched and reheated with the same procedure. The rapid heat-ups in this method allow a limited time for crystallization to occur, allowing differences in
crystallization rates to be observed. Results are shown in the table below.
Table 24
First upheat
Sample % meso Exotherm Peak Temp. Endotherm Peak Temp.
(J/qm) (°C) (J/qm) (°C)
0 29.1 114 33.7 172 3 4.4 126 5.9 159 6 0 - - - 0 - - - 9 0 - - - 0 - - -
Second upheat
0 14.1 137 12.2 173 3 0 - - - 0 - - - 6 0 - - - 0 - - - 9 0 - - - 0 - - -
The results show that the rate of crystallization for the polymer is decreased dramatically with the addition of small amounts of meso-lactide to the polymerization
mixture.
Example 24
The Effect of Meso-lactide Concentration on Crystallization
Samples of devolatilized poly(lactide) of varying optical composition and with number average molecular weights in the range of 50,000 to 130,000 were prepared in a continuous pilot plant. The samples were dissolved in chloroform to a concentration of 5 grams/100cc and the optical rotation of the samples was measured to determine the concentration of meso-lactide which had been present in the monomer mixture prior to polymerization. Separate optical rotation and gas chromatography analysis of the monomer mixture confirmed that L-lactide and meso-lactide are the predominate components when meso-lactide is present at a concentration of 20% or less, and only a small
correction is required for D-lactide.
Additional samples were made by polymerizing mixtures with known weights of L-lactide and meso-lactide.
All samples were subjected to an annealing procedure to develop crystallinity. The annealing procedure consisted of placing the samples in an oven at 100-105°C for 90 minutes, then lowering the temperature 10°C each 1/2 hour until the temperature reached 45°C. The oven was then shut off and the samples were allowed to cool to room
temperature. The energy of the melting endotherm and the peak melting temperature were then measured using a Mettler Differential Scanning Calorimeter (DSC) apparatus with a scan speed of 20°C/minute. The energy of melting is a measure of crystallinity in the annealed samples. Figure 3 shows the sharp decline in potential
crystallinity between 9 and 12% meso content.
In contrast, a polymer sample made by polymerizing 80% L-lactide and 20% D,L-lactide showed, after annealing, a melting endotherm of 12.3 J/gm. This composition has the same enantiomeric excess in terms of lactide acid R- and S- units as does an 80% L-lactide/20% meso-lactide blend. The 20% meso-lactide containing blend showed no
crystallinity after annealing, as shown by Figure 3.
Example 25
Effect of Plasticizer on Crystallization Rate
Devolatilized polymer samples from a continuous pilot plant were compounded with dioctyl adipate (a plasticizing agent) and/or silica with a twin screw extruder. The samples were then tested for nucleation rates using the DSC method of Example 23. The table below shows that dioctyl adipate (DOA) can increase the rate of crystallization of poly(lactide) or of a filled poly(lactdide).
Figure imgf000076_0001
Example 26
An Evaluation of Nucleating Agents
A devolatilized sample of poly(lactide) polymer was compounded with a variety of potential nucleating agents in a single screw extruder. The candidate nucleating agents were added at a nominal level of 5% by weight. The single screw extruder is not as effective of a mixer as would be used commercially, so failure to observe an effect in these tests does not mean that a candidate agent would not be effective if blended more thoroughly. A positive result in this test demonstrates potential ability to increase crystallization rates. Additives which increased
crystallinity in the second upheat (on a quenched sample) were rated ++, additives which showed an effect only on the first upheat were rated +, and additives which showed no effect were rated 0.
Table 26
Additive Effect
None 0
talc, MP1250 (Pfizer) ++
3-nitro benzoic acid 0
saccharin, sodium salt ++
terephthalic acid,
disodium salt 0
calcium silicate, -200 mesh +
sodium benzoate +
calcium titanate, -325 mesh +
boron nitride +
calcium carbonate, 0.7 micron 0
copper phthalocyanine +
saccharin 0
low molecular weight polyethylene 0
talc, Microtuff-F (Pfizer) ++
talc, Ultratalc (Pfizer) ++
ethylene acrylic acid sodium ionomer 0
(Allied Signal)
isotactic polypropylene +
polyethylene terephthalate 0
low molecular weight poly(L-lactide) ++
Milled 3940 (Milliken) ++
Millad 3905 (Miliken) +
NC-4 (Mitsui) +
polybutylene terephthalate +
talc in polystyrene (Polycom Huntsman +
talc in polyethylene (Advanced ++
Compounding)
Example 27
Orientation and Rate of Crystallization
DSC was used to determine the effectiveness of
orientation as a method of increasing the rate of
crystallization. The method used is the same as in Example 23. An oriented sample will increase crystallization rate primarily on the first upheat. The second upheat, which is on a sample that has been melted and quenched and therefore is no longer oriented is not expected to show
crystallization. The results in the table below show an increase in crystallization rate for the nonwoven fibers of Examples 3 and 4. The melting and quenching procedure
(heating at 200°C for 2 minutes, followed by rapid cooling) reduced the crystallization rate, although the effect of orientation did not disappear. It is believed that a longer hold time in the melt would eliminate the effect of orientation.
Table 27
First upheat
Sample Exotherm Peak Temp. Endotherm Peak Temp.
(J/gm) (°C) (J/qm)
Feed pellet
from Example 3 0 - - - 0.6 147
Nonwoven,
Example 3 19.4 120 19.7 150
Feed pellet
from Example 4 0 - - - 0.2 169
Nonwoven,
Example 4 22.8 118 21.5 148
Second upheat
Feed pellet
from Example 3 0 - - - 0 - - -
Nonwoven,
Example 3 10.5 127 9.6 148
Feed pellet
from Example 4 0 - - - 0 - - -
Nonwoven,
Example 4 7.1 125 7.5 146
It will be understood that even though these
numerous characteristics and advantages of the invention have been set forth in the foregoing description, together with details of the structure and function of the invention, the disclosure is illustrative only, and changes may be made in detail, especially in matters of shape, size and arrangement of the parts or in the sequence or the timing of the steps, within the broad principle of the present invention to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed.

Claims

WHAT IS CLAIMED IS:
1. A fabric including:
(a) poly(lactide) fibers formed from a melt stable lactide polymer composition comprising poly(lactide) chains having a number average molecular weight of at least 10,000; said poly(lactide) chains comprising the polymerization product of a lactide mixture containing 0.5 - 50%, by weight of lactide component, meso-lactide, the remainder of the lactide component in the lactide mixture being selected from the group consisting essentially of: L-lactide, D-lactide and mixtures thereof;
(i) said poly(lactide) fibers further being formed from a melt stable lactide polymer composition including no more than about 2% by weight lactide monomers.
2. A fabric according to claim 1 wherein:
(a) said poly(lactide) fibers comprise a nonwoven fabric.
3. A fabric according to claim 1 wherein:
(a) said poly(lactide) fibers further comprise fibers formed from a melt stable lactide polymer composition comprising poly(lactide) chains having a number average molecular weight from about 20,000 to about
80,000.
4. A fabric according to claim 1 wherein: (a) said poly(lactide) fibers further comprise fibers formed from a melt stable lactide polymer composition comprising
poly(lactide) chains having a number average molecular weight from about 50,000 to about 250,000.
5. A fabric according to claim 1 wherein:
(a) said poly(lactide) fibers are
arranged as a nonwoven fabric;
(b) said poly(lactide) polymer chains have a number average molecular weight of from about 10,000 to about 300,000; and,
(c) said fibers are formed from a melt stable lactide polymer composition including no more than about 2000 parts per million water.
6. The nonwoven fabric of claim 5 wherein said plurality of poly(lactide) polymer chains have a number average molecular weight from about 50,000 to about 250,000.
7. The nonwoven fabric of claim 5 wherein said plurality of poly(lactide) polymer chains have a number average molecular weight from about 20,000 to about 80,000.
8. The nonwoven fabric of claim 5 wherein said polymer chains are reaction products of
polymerizing a lactide mixture comprising about 9 to about 50 percent by weight meso-lactide and the remaining lactide is substantially L-lactide and D-lactide.
9 . The nonwoven fabric of claim 5 wherein said polymer chains are reaction products of polymerizing a lactide mixture comprising about 12 to about 50 percent by weight meso-lactide and the remaining lactide is substantially L-lactide and D- lactide.
10. A diaper comprising the nonwoven fabric of claim 5.
11. The nonwoven fabric of claim 5 further comprising an adhesive binder.
12. The nonwoven fabric of claim 5, wherein said fibers are formed from a melt stable lactide polymer composition including an antioxidant
selected from the group consisting essentially of: trialkyl phosphites, mixed alkyl/aryl phosphites, alkylated aryl phosphites, sterically hindered aryl phosphites, aliphatic spirocyclic phosphites, sterically hindered phenyl spirocyclics, sterically hindered bisphosphonites, hydroxyphenyl propionates, hydroxy benzyls, alkylidene bisphenols, alkyl phenols, aromatic amines, thioethers, hindered amines, hydroquinones and mixtures thereof.
13. The nonwoven fabric of claim 5, wherein said fibers are formed from a melt stable lactide polymer composition including a water scavenger selected from the group consisting essentially of: carbodiimides, anhydrides, acyl chlorides,
isocyanates, alkoxy silanes and mixtures thereof.
14. The nonwoven fabric of claim 5, wherein said fibers are formed from a melt stable lactide polymer composition including a desiccant selected from the group consisting of: clay, alumina, silica gel, zeolites, calcium chloride, calcium carbonates, sodium sulfate, bicarbonates and mixtures thereof.
15. The nonwoven fabric of claim 5 wherein said polymer composition further comprises:
(a) catalyst means for catalyzing the polymerization of lactide to form the
poly(lactide) polymer chains, said catalyst means incorporated into the melt-stable lactide polymer composition during polymerization; and (b) a catalyst deactivating agent in an amount sufficient to reduce catalytic
depolymerization of said poly(lactide) polymer chains.
16. A compostable bag comprising the nonwoven fabric of claim 5.
17. The fabric of claim 1 wherein said
poly(lactide) fibers include melt blown fibers.
18. The fabric of claim 16 wherein said melt blown fibers have a diameter of less than about 5 μm.
19. The fabric of claim 1 wherein said
poly(lactide) fibers include fibers from a spunbond process.
20. The fabric of claim 1 wherein said polymer composition further includes a plasticizer.
21. The fabric of claim 20 wherein said plasticizer is selected from the group consisting essentially of: alkyl phosphate esters,
dialkylether diesters, tricarboxylic esters, epoxidized oils and esters, polymeric polyesters, polyglycol diesters, alkyl alkylether diesters, aliphatic diesters, alkylether monoesters, citrate esters, dicarboxylic esters, esters of glycerine and mixtures thereof.
22. The fabric of claim 1 wherein said polymer composition includes a nucleating agent comprising a crystalline polymer with a melting point greater than a processing temperature of the poly(lactide).
23. The fabric of claim 1 wherein said polymer composition includes a filler selected from the group consisting essentially of: cellulose, wheat, starch, modified starch, chitin, chitosan, keratin, cellulose acetate, cellulosic materials derived from agricultural products, gluten, nut shell flour, wood flour, corn cob flour, guar gum, talc, silica, mica, kaolin, titanium dioxide, wollastonite and mixtures thereof.
24. A process for the manufacture of a fabric, said process comprising the steps of:
(a) providing a melt-stable lactide polymer composition comprising: (i) poly(lactide) polymer chains, said polymer chains being reaction
products of polymerizing a lactide mixture comprising a lactide component including about 0.5 to about 50 percent, by weight, meso-lactide, with the remaining lactide component being selected from the group consisting of L-lactide, D-lactide and mixtures thereof, said polymer chains having a number average molecular weight of at least about 10,000;
(ii) lactide in a concentration of less than about 2 percent by weight; and
(iii) water in a concentration of less than about 2000 parts per million; (b) extruding said polymer composition into fibers; and,
(c) forming the fibers into the fabric.
25. The process of claim 24 wherein said step of extruding is a melt blown process; and the lactide polymer composition comprises poly(lactide) polymer chains having a number average molecular weight of about 20,000 to about 80,000.
26. The process of claim 24 wherein said step of extruding is a spunbond process; and, the lactide polymer composition comprises poly(lactide) polymer chains having a number average molecular weight from about 75,000 to about 200,000.
27. A process according to claim 24 including a step of orienting the fibers.
PCT/US1993/009308 1992-10-02 1993-09-30 A melt-stable lactide polymer fabric and process for manufacture thereof WO1994008078A1 (en)