WO1996036665A1 - Curable resin sols - Google Patents
Curable resin sols Download PDFInfo
- Publication number
- WO1996036665A1 WO1996036665A1 PCT/US1996/005438 US9605438W WO9636665A1 WO 1996036665 A1 WO1996036665 A1 WO 1996036665A1 US 9605438 W US9605438 W US 9605438W WO 9636665 A1 WO9636665 A1 WO 9636665A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin
- microparticles
- curable resin
- sol
- composition
- Prior art date
Abstract
Description
Claims