WO1997023448A1

WO1997023448A1 - Preparation of bis(fluoroalkylenesulfonyl)imides and (fluoroalkylsulfonyl) (fluorosulfonyl)imides

Info

Publication number: WO1997023448A1
Application number: PCT/US1996/019532
Authority: WO
Inventors: Richard D. Howells; William M. Lamanna; Alan D. Fanta; Jennifer E. Waddell
Original assignee: Minnesota Mining And Manufacturing Company
Priority date: 1995-12-22
Filing date: 1996-12-09
Publication date: 1997-07-03
Also published as: ES2155632T3; DE69612573T2; US5874616A; AU1130197A; EP0904265B1; DE69612573D1; EP0904265A1

Abstract

A method for preparing fluoroalkylsulfonyl imides by reacting a fluoroalkylsulfonamide with a fluoroalkylsulfonyl halide or a fluorosulfonyl halide in the presence of a non-nucleophilic base. One reaction is: Z-Rf-SO2NH2 + Z-R'f-SO2-X + 2B ∊ (Z-Rf-SO2)(Z-R'f-SO2)N-.BH+ + BHX, where each Z is a fluorine atom or a polymerizable organic functional group, R¿f? and R'f are fluoroalkylene groups optionally containing catenary oyxgen or nitrogen, X is a halogen atom, and B is a non-nucleophilic base. Unsymmetrical imides and polymeric imides can be prepared.

Description

Preparation of Bis (fluoroalkylenesulfonyl) Imides and (Fluoroalkylsulfonyl) (Fluorosulfonyl) Imides

Technical Field

This invention relates to a method for preparing bis (fluoroalkylsulfonyl) imides,

(fluoroalkylsulfonyl) (fluorosulfonyl) imides and derivatives thereof.

Background Bis (Fluoroalkylsulfonyl) imides,

(fluoroalkylsulfonyl) (fluorosulfonyl) imides and derivatives thereof are known to be useful in many chemical processes and formulations. In solution, the imides behave as strong acids due to the presence of the electron-withdrawing fluoroalkylsulfonyl or fluorosulfonyl groups and exhibit exceptional stability under a variety of conditions. These compounds have been found to be useful, for example, as fuel cell electrolytes, as esterification catalysts and as polymerization catalysts for cationically-sensitive monomers such as epoxy resins.

The salts of bis (fluoroalkylsulfonyl) imides and (fluoroalkylsulfonyl) (fluorosulfonyl) imides have been found useful as electrolytes in advanced high voltage batteries. In particular, lithium bis (trifluoromethylsulfonyl) imide (CF₃S0 ) ₂N^"Li⁺, shows excellent conductivity and stability, but can be corrosive toward aluminum. Certain higher homologues of this compound show comparable performance as battery electrolytes, and have decreased the corrosion toward aluminum.

There are several known methods for preparing some classes of bis (fluoroalkylsulfonyl) imides . Bis (perfluoroalkylsulfonyl) imides can be prepared by 3448 the reaction of an alkali metal salt of an N- trimethylsilyl perfluoroalkylsulfonamide with a perfluoroalkylsulfonyl fluoride in a polar organic solvent. This route requires several synthetic steps, with the isolation of intermediate compounds, and the overall yields are often low. A second method involves the reaction of an alkali metal salts of a perfluoroalkylsulfonamide with perfluoroalkylsulfonyl fluoride in a polar organic solvent. Here too, the yields are low. A third method involves reacting a perfluorinated sulfonic anhydride with urea and a sulfonic acid. The products of this reaction are then dissolved in water and the addition of tetrabutylammonium bromide precipitates the tetrabutylammonium i ide. This method is not satisfactory for the large scale production of imides IH^,..7HI..O l. ovr.r.'il l yi lcJ.'. arc low ,ιiifl I ho suJfon.c anhydride precursors are not easily accessible. A fourth method o f making metal salts o f suJ fσnimides involves the reaction of a metal nitride with perfluoroalkyl suJ fonyl halide. However this method cannot be used to make unsymmetrical imides and requires handling metal nitrides which are sensitive to air. Thus there remains a need for an efficient method of preparing bis (fluoroalkylsulfonyl) imides, (fluoroalkylsulfonyJ ) (fluorosulfonyl) imides, and derivatives thereof.

Disclosure of the Invention

The present invention provides an efficient, high yield method of preparing bis (fluoroalkylsulfonyl) imides,

(fluoroalkylsulfonyl) (fluorosulfonyl) imides as well as derivatives such as the organic or inorganic salts, and N-halo, N-alkyl or N-silyl compounds; hereinafter described as "imides" for the sake of brevity. The method uses readily available starting materials and allows the preparation of the imides in a single step, without the isolation and purification of intermediate compounds. The method of this invention also features the preparation of unsymmetrical imides and polymers having imide groups in the polymer chain.

By this method, a fluoroalkylsulfonamide is contacted with a fluoroalkylsulfonyl halide or a fluorosulfonyl halide, in the presence of a sufficient amount of a non-nucleophilic base at a temperature and for a time sufficient to yield the imide salt. Preferably, the fluoroalkylsulfonamide is prepared i n si tu by contacting a fluoroalkylsulfonyl halide with anhydrous ammonia.

Detailed Description

In one aspect, the method of the invention may be represented by the following Scheme 1:

Scheme 1 Z-R_f-S0₂NH₂ + Z-R'_r-SO_?-X + 2B => (Z-R_f-S0₂) (Z-R' _f-S0₂)N^" ^■BH' + BHX, wherein R_f and R_f' are fluoroalkylene groups having from 1 to 12 carbon atoms, optionally containing one or more catenary oxygen or nitrogen atoms, each Z is a fluorine atom or a polymerizable organic functional group, X is a halogen atom and B is a non-nucleophilic base. BH^* represents an cation derived from the non- nucleophilic base B, e.g. an ammonium cation, but other cations may be used. In the case of symmetrical imides, the sulfonamide is preferably generated i n si t u by the reaction of a sulfonyl halide with anhydrous ammonia. The sulfonamide then reacts with another

-3- molecule of sulfonyl halide to produce the bis(fluoroalkylenesulfonyl)imide as shown in Scheme 2.

Scheme 2 2 Z-R_fS0₂X + NH₃ + 3 B = (Z-R_£S0₂)₂N^"-BH^* + 2BΗX, when sulfonamides are used as the starting compounds in the preparation of bis (fluoroalkylenesulfonyl)imides according the method of this invention, either the sulfonamide per se, or a salt of the sulfonamide may be used. As used herein, the term "sulfonamide" represents both the sulfonamides and the salts thereof. Thus, the use of fluoroalkylenesulfonamide salts may be represented in Scheme 3.

Scheme 3

Z-R.-S0₇Nir-BH' -I Z-R'f-SOz-X + B =>

(Z-R.-SO?) (Z-R'r-S0₂)N^"-BH^* + BH'X^",

In another aspect of the invention, polymeric bis (fluoroalkyJenesul onyl) imides may be prepared by contacting equimolar amounts of difunctional fluoroalkylene sulfonyl halides and fluoroalkylene sulfonamides in the presence of a non-nucleophilic base. The difunctional su] fonyl halides or sulfonamides may be fluoroalkylene disulfonyl halides or fluoroalkylene disulfonamides. Alternatively, a difunctional sulfonamidofluoroalkylenesulfonyl halide may be used. The preparation of poJymeric imides is shown in Schemes 4-6.

Scheme 4 nCX-S0₂-R_f-S0₂NH_?)+ 2B =_> -SO?-R_f-S0₂N^" ,,- [BH⁴] + B'HX, where n is an integer greater than 1 , and X is preferably a fluorine atom.

-4- 3448

Scheme 5 H₂NS0₂-R_f-S0₂NH₂ + X-S0₂-R' _tS0₂-X + 4B --> -fS0₂-R_f-S0₂N^~- S0₂-R'_f-Sθ₂N^" -^#2[BH'_ + 2B^'HX.

Scheme 6 X-S0₂-R_f-S0₂-X + NH₃ + 3B => - S0₂-R_f-S0₂-N^" _n- [BH⁺] + 2B'HX.

In Scheme 6, the sulfonamide is generated in si t u by the reaction between a sulfonyl halide and ammonia in the presence of a non-nucleophilic base B. The sulfonamide thus produced reacts with a sulfonyl halide from another molecule of X-SO?-R_f-S0₂-X to produce the imide. Where sulfonamides are used as starting compounds, ei her the sulfonamide per se can be used, or a salt as previously described. Preferably X-SO--R_f-SO^-X is chosen so that the R, group is sufficiently large to make intramolecular cyclization unfavorable. Cyclization would be unfavorable when the resulting cyclic compound would have a ring size < four ring atoms or nine ring atoms.

In the preparation of polymeric imides according to Schemes 4-6 it is preferable that the reagents be of the highest possible purity (e.g., > 99?. by weight) and have a high level of difunctionality (e.g., > 99ft) so that the reaction proceeds to high levels of conversion (e.g., >98ft) with minimal side reactions in order to maximize the molecular weight of the final polymer.

(Fluoroalkylsulfonyl) (fluorosulfonyl) imides can be prepared by the method of this invention using a fluoroalkylsulfonamide and a fluorosulfonyl halide according to Scheme 7.

Scheme 7 Z-R_f-S0₂NH_z + F-SO_?-X + 2B =- (Z-R.-SO?) (F-S0₂)N^"ΕH^* + BHX.

The fluoroalkylsulfonamide is preferably generated in si t u by the reaction between a fluoroalkylsulfonyl halide and ammonia, and subsequently reacted with the fluorosulfonyl halide to produce the imides. As previously described, the fluoroalkylsulfonamide per se may be used, or a salt as shown in Scheme 8.

Scheme 8 Z-R_f-SO_?NH^"-BH⁴ + F-SCv-X + B =

(Z-R.-SO?) (F-SCv)N^'-BH' + BHX.

Difunc ional f1 uoroal ylono ul fonamidos may also be reacted with monofunctional fluoroalkylenesul fonyl halides, or conversely, difunctional luoroal kylenesulfonyl halides may be reacted w h monofιιικ-1 ional fluoroalkylonosulfonamidos to produce dimeric bis (fluoroalkylenesulfonyl) imides, as shown in Schemes 9 and 10.

Scheme 9 X-S0₇-R_c-S0₂X + 2 Z-R' _fS0₂NH₂ + 4B => Z-R' _fS0₂N^~S02-Rf-S0₂N^" -SC -R'_f-Z- [2BH'] + 2BΗX

Scheme 10 H₂N-SO_?-R_f-S0₂NH? + 2 Z-R' _f-S0₇-X + 4B => Z-R' _fS0₂N^~S02-Rf- SO/N^'-SOy-R' r-Z- [2BH'] + 2B HX

The fluoroalkylene groups, R_f and R_f' , of the fluoroalkylenesulfonyl halides and the fluoroalkylenesulfona ides may be linear, branched, cyclic or acyclic, or combinations thereof. Additionally one or more of the fluorine or hydrogen atoms of the fluoroalkylene group may be replaced by chlorine or bromine atoms. In the above formulae shown in Schemes 1 to 10, one or more non-adjacent carbon atoms of the fluoroalkylene groups R_f and R' _t may be replaced by catenary divalent oxygen or trivalent nitrogen atoms.

When the fluoroalkylene group is acyclic it has the general formula C_mH₍₂m-8)F_a, where m is 1 to 12 and a is at least one. When the fluoroalkylene group contains a cyclic group it has the general formula C_mH(₂m-₂-_a)F_a, where is 1 to 12 and a is at least one. Preferably the sum of carbon atoms in the two fluoroalkylene groups of tre bis (fluoroalkylenesulfonyl) imide is 3 to 12 carbon atoms

Prcforr'ibl y, t o fluoroalkyJonc group is substantially fluorinated so that the number of fluorine atoms is greater than the number of hydrogen atoms present. Most preferably the fluoroalkylene group is a linear oi branched, cyclic or acyclic perfluoroalkylene group containing 1 to 10 carbon atoms and the sum of carbon atoms, in the two fluoroalkylene groups of the bis (fluoroalkylenesulfonyl) imide is 3 to 12 carbon atoms.

The halide X may be F, Br or I, but is preferably F. When Z is a polymerizable organic functional group it allows the preparation of polymers having pendant bi ( f Juoroalkyl enesuJ fonyl) imide moieties on the polymer chain.

Fluoroalkylenesui fonyl iuorides having polymerizable functional groups have been described by Gard et al., J. Fluorine Chem. 66, 105(1994), Gard et al . , Coordination Chemistry Reviews 112, 47(1992), Gard et al., J. Fluorine Chem. 4J3, 331(1990), Gard et al. J. Fluorine Chem. £3, 329(1989), Gard et al . , J. Fluorine Chem. ^7, 27(1994), Gard et al. J. Fluorine Chem. 55, 313(1991), Gard et al. J. Fluorine Chem. 3J3, 3(1988), Gard et al., Inorg. Chem., 29, 4588(1990) U.S. 5,414,117 (Armand) and U.S. 5,463,005 (Desmarteau) . Polymers prepared from fluσroalkylenesulfonylfluorides having polymerizable functional groups have been described in DesMarteau, Novel Fluorinated Acids for Phosphoric Acid Fuel Cells, Gas Research Institute Report flGRI-92/0385, July 1992, and J. Fluorine Chem. 72,203 (1995) .

Z may be any organic functional group that may undergo grafting or polymerization by an addition or step-growth mechanism, including cationic, anionic, free-radical and Z-N polymerization or poJ ycondensation . 7, may be chosen from those groups con i^'i in i ικj double bond.;, for examp.I c vinyl, allyl, vinyl-benzyl or acryloyl groups. Z may also be chosen from those groups containing oxirane, oxetane, azetidine, or aziridine functional groups. Z may also bo chosen from those groups containing alcohol, amine, isocyanate, or trialkoxysilyl functional groups.

When Z contains functional groups whose reactivity could interfere with reactions for preparing the imides, Z can be protected by reactants that are reversibly bound to it. For example, a double bond may be protected as a di-halo derivative and subsequently dehalogenated. Examples of Z include CH^CH-, CH_?=CHO-, CH₇=CHCH,0-, CU_?=CHCO -, (CH?=CHCH_?) ₇NC0- (prepared as described in Armand et.al, US 5,414,117),

(CH_?=CHCH_?)₇NSO_?- CF-=CFO-, CF₂=CF-, CH₇=CHC0₂CH₂CH_?-, -0- C₆H<,-CH=CH_;, -C(0)OCH_?CH,OC (0)C(CH )=CH,.,

-C(0)NCH₂CH_?OC(0)C(CH,)=CH₂, -S0₂0-C₆H₄-CH=CH_?, -OCH₂CHOH- CH?OH, -C(0)C(CH₃)=CH_?, -C (0)OCH_?CH=CH₇, and -OCH₂CsCH. 448

Perfluoroalkylsulfonyl fluorides and perfluoroalkylened ulfonyl fluorides used as precursors to the imide salts of this invention can be prepared by a variety of methods known in the art as described, for example, in U.S. Patents 3,542,864;

5,318,674; 3,423,299; 3,476,753, 3,776,960, 2,519,983, 3,951,762; 3,623,963; 2,732,398 S. Temple, J.Org. Chem., 33(1), 344 (1968), D.D. DesMarteau, Inorg. Chem., 32, 5007 (1993), and Chemistry of Organic Fluorine Compounds, M. Hudlicky, ed., 2nd ed. PTR Prentice Hall (New York), pp. 73-6.

Perfluoroalkylsulfonyl fluorides are available by the electrochemical fluorination of the corresponding alkylsulfonyl- fluorides as described in U.S. 2,732,398 (Brice et al.) . See also T. Abe et al., in Preparation, Properties and Industrial Applications of Ori-jriuor ior i no Compounds, R. . Banks (Kd), pages 37- 9, John Wiley & Sons, New York (1982) . Routes to perfluoroalkanesu1 fonyl chlorides are described by P.J. Stag et al. in Synthesis 1982, 85 and by R.N.

HaszeJdJne ot aJ . , in J. Chem. Soc. 1955, 2901. The chlorides of ω-hydrof1 uorinated sulfonic acids are described by Coffman and Raasch in J. Org. Chem, . 14, 747 (1949), by Weiyuan et al. in Chemistry 2, 31 (1987), and by Huang, J. Fluorine Chem. _32' ¹⁷⁹ (1986) . Ammonia, when used in the method of this invention, should be anhydrous to prevent side reactions from occurring. To avoid the hazards of handling liquid ammonia, it is often convenient to generated anhydrous ammonia in si tu by reacting ammonium salts of the formula NH X^" with one equivalent of a non-nucleophilic base. Here X may be any halide, or any other non-reactive anion.

For purposes of this description, the term "non-nucleophilic base" B means a base which does not undergo an irreversible reaction with the sulfonyl halide group. This reaction, when it occurs will reduce the yields of the desired imide. The non- nucleophilic base may be an organic or inorganic base, but is preferably an organic aprotic base. Examples of suitable organic non-nucleophilic bases include alkylamines, for example triethyl amine, trimethyl amine, tripropyl amine and diisopropylethyl amine, pyridines, alkyl pyridines and dialkyla inopyridines, alkyl piperadines, dialkyi piperazines, N-alkyl pyrrolidines, N-alkylpyrroles N-alkylimidazoles, amidines, for example 1, 5-diazabicyclo[4.3.0]non-5-ene (DBN) or 1, 8-diazabicyclo[5.4.0]dec-7-ene (DBU) , or guanidines. It is preferable to prepare the bis (fluoroalkylenesulfonyl) imides neat, i.e. in the absence of any πolvont.. Generally a solvent is not necessary, the reactants are sufficiently soluble in each other to produce the imides. In some cases, solvents may be added to enhance the solubility of the reactants, such as when preparing polymeric imides from difunctional sulfonyl halides and/or sulfonamides. Any solvent that is non-reactive toward the starting sulfonyl halides and sulfonamides may be used, but polar aprotic solvents are preferred. Any solvent used should be anhydrous, (e.g., less than 1 % water) to avoid competing hydrolysis of the sulfonyl halides. Examples of suitable aprotic liquids include linear ethers such as diethyl ether, diethylene glycol dimethyl ether, and 1, 2-dimethoxyethane; cyclic ethers such as tetrahydrofuran, 2-methyltetrahydrofuran, dioxane, dioxolane, and 4-methyldioxolane; nitriles such as acetonitrile and benzonitrile; nitro compounds such as nitromethane or nitrobenzene; amides such as N,N-dimethylformamide, N,N-diethylformamide, and N- methylpyrrolidinone; sulfoxides such as dimethyl sulfoxide; sulfones such as dimethylsulfone, tetramethylene sulfone, and other sulfolanes; oxazolidinones such as N-methyl-2-oxazolidinone and mixtures thereof.

The method of this invention can be carried out by introducing the reactants into a vessel, which can be made of glass or other corrosion-resistant material. Preferably the vessel is suitable for use at elevated pressures caused by the high vapor pressure (s) of certain reagents (e.g., NH₃) . The method of this invention can generally by carried out by heating the contents of the vessel at temperatures from about -25°C to about 150°C, preferably from 25°C to about 100°C and at a pressure equal to or greater than atmospheric.

Generally pressures i.n excess of those generated by the vapor pressures of t e reagents at the reaction temperatures is not required.

When preparing non-polymeric imides from fluoroalkylsulfonamides generally at least one molar equivalent of the sulfonyl halide is used. Preferably a slight stoichiometric excess of the sulfonyl halide is used. When preparing imides from ammonia, as shown in Scheme 2, a stoichiometric excess of sulfonyl halide, relative to the amount of ammonia, is generally preferred. The amount of non-nucleophilic base used is generally in excess of the stoichiometric amount shown in Schemes 1 through 6. Preferably the amount of base is less than a 100V. excess of the stoichiometric amount shown in the Schemes. Most preferably amount of base is less than a 50V, excess of the stoichiometric amount shown in the Schemes to maximize the volume efficiency of the reaction.

Representative imides that can be prepared by the method of this Jnvention include: 3448

^"N(S0₇CF₃)2 ^"N(S0₂C2F₅)2 N(S0₂C₄F₉)₂ ^"N(S0,C„F,,)₇ ^~N(S0₇CF?CF₇CFC1CF_?C1)₇ ^•"N(S0₂CF₂-c-C₆F₁₁)₂ ^"N {SO2CF2CF2OCFCICF₂CI ) ₂ ^~N(SO?C₃F_flCF₂Cl)₇ ^"N(S0_?C₃F₆CF₂H)₂ ^■ (S0₂C₂F₄N(CF₃)₇)₇

) ₂ -N(S0₂CF₃) (SO_?C₇F,) ^~N(SO_?CF₃) (S0₇C₄F₉) ^"N(S0₂CF₃) (S0₂C₈F₁₇) ^~N(S0₂C₂F₅) (SO2CF9) ^■N(S0₂CF₃) (S0₂F) ^■N(S0₂C₄F₉) (SO₂F) ^"N(S0₂CF₃) (S0₇CF₇H)

^'N(S0₂CF₃) (S0₂C₂F₄N(CF₃)₇)₇ ^"N(S0₂CF₃) (S0₂C₂F₄CFC1CF₂C1) ^"N(S0₇CF₃) (S02C2F40CFC1CF2C1) ^"N(S0₇CF₃) (S0₂C₂F₄OCF=CF₇) ^~N(S0_?CF₃) (S0₇C₇F₁0CF₁) ^~N(SO_?CF₃) (S0₂C₂F₄CF=CF_?) ^"N (S0₇CF,) (S0₂C₂F₄0CH?CH=CH₂) ^"N(SO_?CF₃) (S0₂C₃F₆CF₂H) ^~N(SO_?CF₃) (S0₇C_?F₄OC,.F,,CH=CH₇) ^~N (SO?CF,) (S0₂C₇F₄CON (C..₇CH=CH,) ₇; ^~N (S0₇CF,) (SO_?C_?F,,OClI,.CHOHCH..OH) ^~N(SO?CF,) (S0₇C F₄COC (CH,) = CH.)

N(.'.o..(.τ,) (so/:.-'/: (o) (jιι.(;ιι-cιι₇) ^"N(SO CF,) (SO,C_?F₄OCH/ CH)

CF₃S0_?N^~S0₇C₄FnS0₇N^~S0 CF, C?Fr,SO..N^"S0₇ (CF_?) ₆S0₇N^~S0₇C-F<,

^■N(SO.,CF ) (SO_nCF.CF,OCII, . / \ ) ^"N(S0₂CF₃) S0₂CF₂CF₂ -- i . 0

CF SO N^'SO CF CF- -N F N- -CF CF SO -SO CF.

3 2 2 2 2 2 2 2 2 3

CF₃SO₇N^"SO₇CF₇CF_?OCH₇CH.OCF₇CF₇SO₇N^"S0₂CFj CH₇=CHCH₇OC₇F₄SO_?N^~SO- (CF,.) ₄S0₇N^'SO₂C₇F₄OCH₇CH=CH₂ SO₇CF₇CF₇N(CF-,)CF₇CF₇SO.N^"S0₇(CF₇)_ftS0₇N „ S0₇ (CF_?) ₃S0₂N~SO? (CF ) ,S0₇N _n - SO_? ( CF_? ) _?OCH_?CH_?0 ( CF ■ ) .S0₇N _n -ISO₂C ₂SO₂ -SO₂ (CF_?) _fiSO_?N _n - SO_? (CF₂) ?OCF_?0 (CF?) ?SO?N^"f_n

S0₂CF₂CF₂-N^F -CF₂CF₂S0₂N^" -_n

^"N(S0₂CF₃) (S0₂C₃F₈C (0) 0CH₂CH₂0C (0) C (CH,) =CH₂) ^"N(S0₂CF₃) (SO₂CF₂C(O)NCH?CH₂0C(O)C(CH₃)=CH₂)

The imides shown (without a corresponding cation for illustrative purposes) can be used to prepare derivatives such as alkali, alkaline earth and other metal salts, N-silyl imides, N-alkyl and N-fluoro imides. For example, conjugate acids of the imides may be treated with an inor'ganic base having the desired cation M', such as NaOH, LiOH, KOH, NH₄0H, Λg?C0₍ or CuO, to produce the corresponding N-Na, N-Li, N-K, N-NJ.j,, N-Λy or N- u ..rilLs. The jmides may be contacted with fluorine under dαrect fluorination conditions to produce the N-F dor 1 vaIives . The silver imide salts may be contacted with a trialkylsilyl chloride, trialkylstannyl chloride, or an alkyl halide to produce the N-trialkylsilyl, N-trialkylstannyl or N-alkyl derivatives respectively. Other derivatives can be prepared by means known to those skilled in the art. The invention is further illustrated by the following Examples. In the examples, the term "reduced pressure" means the vacuum obtained by means of a commercially available laboratory distillation apparatus using an aspirator connected to a water pipe or other fluid stream for aspiration, such as a rotary evaporator apparatus.

Example 1

Lithiurn(trifluoro ethanesulfonyl) (perfluorobutanesulfonyl) imide

Under a nitrogen atmosphere, a dry, 500 mL Fisher-Porter pressure bottle equipped with a stainless steel pressure head and magnetic stirrer was charged with 35.00 g CF₃S0₂NH? (prepared, e.g., as described in Foropoulos and DesMarteau, Inorg. Chem., 23:3720-23 (1984)), 98 mL anhydrous triethylamine and 74.55 g C₄F₉S0F. The pressure vessel was sealed and the reaction mixture heated to 90°C with stirring for 17 hours. The volatile components of the reaction mixture were evaporated under reduced pressure at 70°C then the reaction mixture was treated with a mixture of 700 mL water and 700 mL methylene 'chloride with stirring to form a two phase mixture. The methylene chloride phase was then separated, washed with two 700 L portions of watci, dried over anhydrous MgS0₄, filtered and then evaporated under reduced pressure to yield a dark red liquid. This liquid was combined with 500 g of polyphosphoric acid (Λldrich Chemical Co.) in a short path vacuum distilla ion apparatus equipped with an ambient air-cooled condenser, and then vacuum distilled at ca. 0.1 Torr. The distillate (96.5 g, corresponding to HN(SO?CF ) (S0?C₄Fn) , which solidified in receiver at 0"C, was further puri ied by sublimation at 70°C, 1.0 Torr and then added in portions to a slurry of 52 g of Li₇CO, (99.997?, purity, from Aldrich Chemical Co.) in 800 mL of methyl t-butyl ether with stirring at room temperature. After about 1 hour CO? evolution subsided and the reaction mixture was heated to about 40°C for 3.5 hours to complete the neutralization. The mixture was filtered by gravity through filter paper and then filtered again by suction through a 0.22 micron Tefsep© Teflon membrane (Micron Separations Inc., estboro, Massachusetts) to remove particulates. The filtrate was evaporated under reduced pressure at 25-80°C to yield a clear, colorless oil. Two 250 mL portions of toluene were combined with the oil and the mixture evaporated at 40-70°C, 20 Torr after each toluene addition, causing the oil to eventually solidify giving a fine white powder. The solid was transferred to a glass jar and dried in vacuo at 100°C, 10^"2 Torr for 24 hours to yield 77.0 g of the anhydrous title salt. The structure of the product was confirmed by H and ¹⁹F NMR spectroscopy which indicated that the purity of the salt was greater than 99% by weight.

Example 2 Lithium (trifluoromethanesulfonyl) (perfluoroethanesulfonyl) imide

Under a nitlogon atmosphere, a dry 3L flask equipped with a dry ice condenser, mechanical stirrer, and a sparging tube was charged with 500 mL anhydrous methyl t-butyl ether (MTBE) and cooled below 0°C in a dry ice bath. To the cold solvent was added 500 g of crude CF₃CF?S0₂F mixture (containing ca. 23% CF₃CF₂SO_?F by weight in C6-C8 perfluoroalkane solvent) . Gaseous anhydrous ammonia (194 g) was gradually introduced through the sparging tube into the resulting mixture at ca. 0°C with vigorous stirring. Once ammonia addition was complete, the reaction was allowed to proceed for an additional hour after which the dry ice bath was removed and the reaction solution gradually warmed to room temperature with stirring. Excess ammonia was allowed to evaporate while stirring overnight at room temperature. The reaction solution was cooled again to 0°C and treated with 83.9 g LiOH-H₂0 dissolved in 750 mL of water with stirring. The mixture was filtered through filter paper by gravity to remove LiF precipitate. To the filtrate was added concentrated aqueous HCl in portions with stirring at 0°C until the pH of the mixture was 0.

The resulting two-phase mixture was separated into separate aqueous and ether phases. The aqueous phase was extracted with two additional 400 mL portions of MTBE. The ether fractions were combined, extracted with two 500 mL portions of water, and then dried over anhydrous MgS0₄ overnight. The ether solution was filtered by gravity through filter paper and then by suction through a 0.22 micron Tefsep^TH membrane (Micron Separations Inc.) . The filtrate was concentrated by rotary evaporation, hexane was added, and the solution concentrated again. This was repeated until the product CF₃CF₇SO?NH? crystallized from solution as a white solid. The product (Crop 1) was isolated by suction fil ra i n through a ylass frit giving 33.0 g. A second crop of crystals (20.2 g) was recovered in the same manner from the filtrate by concentrating further followed by filtration. The remaining filtrate was evaporated to dryner.r; at 40"C , 20 torr to yield a third crop of relatively crude product (26.8 g) . All product fractions (Crops 1-3) were dried at 10^"'^' torr at room temperature for ca . 15 min to give a combined yield of BO.O g. Quantitative Η and ¹³C NMR analysis of the product from Crop 2 indicated that it was the desired product with a purity of 98% by weight.

Under a nitrogen atmosphere, a dry Parr 4560- Series Benchtop Mini Reactor equipped with a 600 mL capacity Monel reactor cylinder, mechanical stirrer, thermocouple and heating mantle was charged with 53 g CF₃CF?SO?NH? (Crops 1 + 2) and 152 mL anhydrous triethylamine. While cooling the reactor at -78°C in dry ice, 55.2 g of gaseous CF₃SO?F (ca. 94% purity) was condensed into the reactor with stirring. The reactor was sealed and the temperature of the reaction mixture gradually raised to 90°C with vigorous stirring, then held at 90°C with stirring for a total of 24 hours. The volatile components of the reaction mixture were evaporated under reduced pressure at 70°C, then the residue was treated with a mixture of 700 L water and 700 mL methylene chloride with stirring to form a two phase mixture. The methylene chloride phase was then separated, washed with two 700 mL portions of water, dried over anhydrous MgS0₄, filtered and then evaporated under reduced pressure to yield a dark red liquid. This liquid was combined with 600 g of polyphosphoric acid (Aldrich Chemical Co.) in a short path vacuum distillation apparatus equipped with an ambient air- cooled condenser, and then vacuum distilled at ca. 15 torr, 85-88°C. The distillate (78.1 g, corresponding to I!N(-.0 CI'"-.) (SOjC,.''.,) ), which solidified in receiver at 0°C, was converted to the corresponding lithium salt, and further purified, using essentially the procedure described in Example 1 to yield 75.0 g of the anhydrous title salt. The structure of the product was confirmed by Η and ^I9F NMR spectroscopy which indicated that the purity of the salt was 98% by weight.

Example 3

Lithium Bis (perfluoroethanesulfonyl) imide

As in Example 2, a dry Parr 4560-Series

Benchtop Mini Reactor was charged with 155 mL anhydrous triethylamine. While cooling the reactor at -78°C in dry ice, gaseous C?F₅S0₂F (100.0 g, > 99% purity) followed by anhydrous ammonia (3.51 g) were condensed into the reactor with stirring. The reactor was sealed and the temperature of the reaction mixture gradually raised to 90°C with vigorous stirring. The reaction mixture was held at 90"C with stirring for a total of 20.5 hours. The intermediate product, HN (SO_?C?F5) _?, was isolated as previously described, then added to a slurry of i^CO, (45.7 g, 99.997% purity) in 800 mL of methyl L-butyl (.t er to produce the l ithium salt. This lithium salt was isolated using essentially the procedure described in Example 1 to yield 73.34 g (92V, yield based upon NH, ) of the anhydrous title salt. The structure of the product was confirmed by Η and ^!9F NMR spectroscopy which indicated that the purity of the salt was 99.9% by weight.

Example 4

Lithium Bis (perfluorobutanesulfonyl) imide

As in Example 1, a dry, 500 ml, Fisher-Porter pressure bottle was charged with anhydrous triethylamine (100.5 g) and C₄F₉S0₂F (145.0 g) . The pressure vessel was sealed, cooled to -78°C in dry ice and then charged with of anhydrous ammonia (3.0 g) with stirring. After warming gradually to room temperature, the reaction mixture was heated to 90"C with stirring for 24 hours. The intermediate product, HN(SO?C₄F₉) _; , was isolated as previously described, then added to a slurry of Li_?C0₃ (40.0 g, 99.997% purity) in 800 mL of methyl t-butyl ether to produce the lithium salt. This lithium salt was isolated using essentially the procedure described in Example 1 to yield 90.8 g (86% yield based upon NH ) of the anhydrous title salt. The structure of the product was confirmed by Η and ¹⁹F NMR spectroscopy which indicated that the purity of the salt was 98% by weight.

Example 5 Lithium Bis (perfluoropropanesulfonyl) imide

As in Example 4, the title compound was prepared using anhydrous triethylamine (100.5 g) ,

CTF/SO_JF (100.0 g, 68:32 i so mormal isomer ratio), and anhydrous ammonia (3.U g) . A total of 40.8 g of the anhydrous title salt was recovered as a light pink solid. Quantitative analysis by 'H and ''F NMR spectroscopy indicated that the product contained the following major components n order of decreasing weight percent: Li' ^"N (S0?C₃F.) ?, 85.1%, 39:61 iso:normal C₃F, ratio; Li^{* "}N (SO, -C,F,) (S0₂F) , 8.7%; Li' ^"N(SO_?n- C₃F₇) (SO?F) ,4.2%.

Example 6

Synthesis of Lithium trifluoromethylsulfonyl perfluoro (dimethylaminoethylsulfonyl) imide Li'^"N(S0_?CF₃) (SO_?C_?F₄N(CF_t)_?)

The hydrocarbon precursor 2- dimethylaminoethylsulfonylfluoride was made by the addition of dimethylamine to vinylsulfonyl fluoride as described in Krutak et al., J. Org. Chem., 44(2) :3847- 58 (1979) . The hydrocarbon was perfluorinated by electrochemical fluorination. An electrochemical cell of the type described in U.S. Patent No. 2,519,983 (Simons) was filled with 1500 cm³ anhydrous HF. The cell was operated at 31 psig (214 Kpa) and at an average temperature of 56°C. During the course of the 129 hour run, 456 grams of fluorinated product was produced from 650 grams (4.2 mole) of starting material. Analysis of the fluorocarbons was done using gas chromatography/FTIR to confirm structures and yields. The resulting fluorochemical was distilled in a 3-plate distillation column to a main cut of 374 grams (1.1 moles, 27% molar yield) corresponding to perfluorodimethylaminoethy1sulfonyl fluoride ( (CF₃)₂NC₇F₄SO?F) .

To a dry flask equipped with a reflux condenser and magnetic stirrer was charged 1.13 g

CF₃SO?NH? (prepared, e.g., as described in Foropoulos /iiul No.'.MnrLoau, IHOMJ. Chem., 23:3720-23 (1984)), 20 ml, anhydrous triethylamine (distilled from LiAlH₄) and 2.67g (CF₃) ₇NC₇F₄SO F. The reaction mixture was heated to 70°C under a nitrogen atmosphere with stirring for 17 hours, after which volatile components were removed under reduced pressure. The residue was treated with a mixture of 40 mL water and 40 mL methylene chloride with stirring to form a two phase mixture. The methylene chloride phase was then separated, washed with two 40 L portions of fresh water to remove water- soluble components, dried over anhydrous MgS0₄, filtered and then evaporated under reduced pressure to yield a dark red liquid. The liquid residue was combined with 20 L of concentrated (at least 98 weight percent H_?S0₄) sulfuric acid in a short path distillation apparatus equipped with a dry-ice cooled condenser, and then vacuum distilled at 10^"' torr, 60°C. The distillate was dissolved in 50 mL of diethyl ether, after which the resulting ether solution was treated with excess lithium carbonate for 2 hours with stirring at room temperature, filtered and the filtrate evaporated under reduced pressure to yield a clear, colorless oil. Approximately 100 mL of toluene were combined with the oil and the mixture evaporated again at 40-70°C, 20 torr, causing the oil to solidify to form the title salt. The structure of the product was confirmed by Η and ¹⁹F NMR.

Example 7

Preparation of Dilithio perfluoro (methyl-bis- trifluoromethylsulfonimidoethyl) amine CF₃N(CF_?CF₂SO₂N^~S0_?CF,).. ' 2Li⁴

A 500 mL flask equipped with an addition funnel, and stir bar was charged with 10 g of CF₃S0₇NH_7/

45 mL of dry THF and 45 mL of dry triethylamine, then coole o 0"C iindci nil ioyori. 1.'. q of CK.N (CF;.CF_?S0,.l') ,. (prepared by electrochemical fluorination of

CH,N(CH_?CH₇SO_?F) .) was then added slowly to the stirred solution. After complete addition, the reaction was al lowed to warm to room temperature and stirred for an additional 92 hours. Next, the mixture was evaporated to a brown oil under reduced pressure, which was then dissolved in 300 ml, of aqueous 1M LiOH. The water, triethylamine and other volatile components were then evaporated under reduced pressure and the remaining solid washed with 100 L of diethyl ether. The ether solution was filtered, then evaporated under reduced pressure to yield a brown oil, which was dissolved in a small amount (quantify just sufficient to dissolve the oil) of diethyl ether, then added to 100 mL of methylene chloride. This solution was again filtered and evaporated to yield 3.5 g of a yellow solid corresponding to the title salt. The structure was confirmed by Η and F NMR. Example 8

Preparation of Lithium bis- perfluoro (dimethylaminoethyl) sulfoni ide Li^{* ~}N(S0₂C₂F₄N(CF₃)₂)₇

A 500 mL Fisher-Porter pressure bottle, equipped with a magnetic stir bar and pressure head, was charged with 30 g of (CF₃) ₂NC2F₄Sθ2NH₂ (prepared by treatment of (CF₃) ?NC₂F₄S0₂F (prepared by electrochemical fluorination of (CH₃) ?NC₂H₄S0₂F) ) with excess ammonia in tetrahydrofuran), 27.4 g of triethylamine and 31.8 g of (CF₃)?NC?F₄S0₂F. The flask was sealed and heated to l0θ°C for 37 hrs with stirring. After cooling, the volatile components of the -reaction mixture were evaporated under reduced pressure. The residue was dissolved in 300 ml, of methylene chloride and extracted l.hr..ι". time:, wi h ^'iHU ml, of water each I iπir.. The methylene chloride solution was then dried over MgSOi, filtered, and the solvent removed under reduced pressure. The residue was then distilled from excess polyphosphoric acid over a temperature and pressure range starting from 105°C and 3 torr and ending at 97°C and 0.2 torr to yield 40.13 g of a pale yellow-orange liquid which solidified on standing. This solid, corresponding to HN (SO,>C?F₄N(CF₃) _?) _?, was dissolved in 300 mL of methyl t-butyl ether, after which 20.6 g of Li₂COτ was added in small portions with stirring. After stirring overnight, a small amount of additional Li?C0, was added and heated briefly until the solution tested neutral to pH paper premoistened with distilled water. The mixture was cooled, filtered and the solvent removed under reduced pressure. Further drying under vacuum at 110°C yielded 33.5 g of a fine white powder corresponding to the title salt. The structure of the product was confirmed by FTIR, and ^,nF and 'H NMR. Example 9 Synthesis of Lithium (trifluoromethylsulfonyl) (allyloxyoctaflurobυtylsulfonyl ) imide (CH₂=CHCH₂OC₄F₈SO₂N(Li)S0₂CF₃)

A 50 mL flask was charged with dry, distilled triethylamine (15mL), dry acetonitrile (15 mL) and CF₃SO_?NH (6.75g, 0.0081 mole), purged with nitrogen, and cooled to about 0°C in an ice bath.

CH_?=CHCH_?OC₄F₀SO₇F (3.0g, 0.0082 mole, prepared essentially as described in Gard et al., J. Fluorine Chem., 4_9, 331(1990) from FC (0) (CF_?) ₃S0₂F, which was prepared as described in U.^«S. 4,425,199) was added dropwise to the solution with stirring, and the reaction mixture was allowed to come to room Lemperaturo overn i g l..

The solvent from the resulting brown mixture was removed under reduced pressure, and aqueous LiOH (30mL of 1M) was added. The mixture was stirred until neutralization was complete. The water was removed under reduced pressure and the resulting oil was dissolved in diethyl ether, then filtered to removed excess LiOH. To the ether solution was added methylene chloride (25mL) and sulfuric acid (15mL of 2M) . The organic layer was separated, neutralized with excess Li?COτ, filtered and the insoluble portion washed with acetonitrile. The volatile components of the combined filtrate solutions were removed under reduced pressure, and the resulting brown oil slowly crystallized to yield clear crystals of the title compound. The structure was confirmed by Η and '⁹F NMR. Yield 2.73g, 71%. Example 10 Preparation of Lithium (trifluoromethylsulfonyl) (fluorosulfonyl ) imide, CF₃S0₂NLiSO₂F.

A dry, 3-necked flask equipped with a nitrogen inlet, stir bar and dry-ice condensor was charged.with dry triethylamine (15mL)and cooled in a dry ice/isopropanol bath. Sulfuryl fluoride S0₂F₂ (7.0g, 6.8mmole) was bubbled into the cooled triethylamine. The reaction mixture was allowed to warm to -30°C, followed by dropwise addition of a solution of triethylamine (lOmL) , acetonitrile (lOmL) and CF₃SO_?NH? (4.0g, 0.027 mole) . The temperature was maintained for an hour, allowed to warm to- room temperature, and then stirred overnight.

The solvent; was removed from the brown reaction miκLuie under reduced pressure. The remaining brown oil was dissolved in methylene chloride (75mL) and washed with water, followed by 3M 11,S0₄, then dried over MgS0₄. The solvent was removed under reduced pressure, and the crude product puri ied by Kugelrohr distillation (80°C at 1 torr) to yield CF₃SO_?NHSO_?F as a clear oil. This imide was dissolved in methyl t-butyl ether, neutralized with excess Li?CO,, filtered and the solvent removed under reduced pressure to yield the title compound. Yield 3.5g, 55%.

Example 11 Preparation of Lithium (difluoromethylsulfonyl) (trifluoromethylsulfonyl) imide, (HCFjSOz) (CF₃SO?)NLi

Difluoromethylsulfonyl chloride (30g, 0.2 mole) was dissolved in diethyl ether (100 mL) and cooled to 0"C. An excess of anhydrous NH, was added until the conversion to the difluoromethylsulfonamide was complete by gas chromatography/mass spectroscopy. The ether solution was evaporated to yield a reddish oil, from which a yellow crystalline solid precipitated. The crystals were washed with diethyl ether, dried and then washed with hot toluene to remove yellow, oil impurities.

A mixture of the purified difluoromethylsulfonamide (26.5g, 0.2 mole), triethylamine (60.6g, 0.6 mole) and trifluoromethylsulfonyl fluoride (85% pure, 39.5g, 0.26 mole) were charged into a stainless steel pressure vessel and heated at 45°C for 24 hours. The lower phase was separated from the upper triethylamine phase, dissolved in methylene chloride, and washed with water. The solvent was removed under reduced pressure to yield (HCF..SO?) (CF,SO?)N^"(Et) ,NH' (38.9g, 0.11 mole, 55%)

This ammoni m salt was acidified with concentrated H_?SO, (20 g)and distilled at 100"C and 5 torr to yield (IICF.SO ) (CF,SO..) NH (9.8 y) . This imide (15.3 g, 0.06 mole from two preparations) was treated with LiOH'H?0 (2.5 g, 0.06 mole in 50 ml, water) . The solution was filtered and dried in a convection oven overnight at 100"C, Yield 14.1 g of (HCF?SO_?) (CF?SO?) N^" Li⁴.

Example 12

Preparation of bis (trifluoromethylsulfonyl) imide

A stainless steel pressure vessel was charged with triethylamine (328 g, 3.25 mole), sealed, and cooled to 0 C. Trifluoromethylsulfonyl fluoride (103.4 g of 85% purity, 0.68 mole) was added to the vessel via a gas inlet, followed by anhydrous ammonia (4.76 g, 0.28 mole) . The mixture was heated at 65°C for 24 hours, cooled and the lower product phase decanted. The upper triethylamine phase was extracted with methylene chloride, then combined with the lower product phase and washed with water to remove by- product salts. The solvent was removed under reduced pressure to yield the crude salt: (CF₃S0₂)N~NH(C₂H₅) ₃ ⁴. The salt was acidified with concentrated sulfuric acid (250 g) , then purified by vacuum distillation to yield the title compound. Yield 64.6 g, b.p. 100°C at 5 torr. This imide was dissolved in water (100 mL) , then treated with LiOH'^O (9.67 g, 0.23 mole) . The solution was filtered, then dried to a white crystalline product in a convection oven at 100"C. Yield 64.9 g of lithium- bis- (trifluoromethylsulfonyl) imide. The structure was confirmed by ¹⁹F NMR.

Example 13

Preparation of [ (-SO? (CF?) ₄S0₇N^"SO? (CF?) ,SO_?N^~-) • 2 (C₇Hs)₃NH⁴]„ Polymer

The reagents H_?NSO_? (CF₂) „SO_?NH_? (1.995 g, 5.539 mmoles; prepared by electrochemical fluorination of FSO_? (CH₂)₄SO_?F followed by amidation) , FSO_? (CF₂) ₃SO_?F (1.751 g, 5.539 mmoles; prepared by electrochemical fluorination of FSO? (CH?) ₃S0_?F) , triethylamine (3.363 g, 33.23 mmoles. dried over activated 3A molecular sieves) and anhydrous acetonitrile (5 mL) were combined in a dry 2 oz (~59.1 mL) jar equipped with a magnetic stir bar and a tight-fitting cap to prevent significant exposure to ambient moisture. Once all reagents were fully dissolved, the contents were heated in an oil bath at 65°C with stirring overnight. The temperature was then increased to 75"C for 8 hours after which the reaction solution was allowed to cool to room temperature. Volatile components of the reaction mixture were removed under vacuum at 70"C. The remaining viscous residue was combined with a mixture of methylene chloride and water and agitated in a separatory funnel to extract by-product salts into the aqueous phase. The polymeric product was only partially soluble in the methylene chloride phase, the remainder separated out as a third viscous brown oil phase. The water fraction was separated and discarded, and the remaining two organic fractions were extracted an additional two times with water. The isolated organic fractions were concentrated under vacuum at 80°C to remove solvent and any other volatile components. A brown viscous residue was obtained weighing 2.2 grams. ^]H, ¹ F and FTIR spectroscopic analysis identified the product as the desired title polymer. Gel permeation c romatoyraphl c anaI ysis in methyl ethyl kcLone revealed a bimodal molecular weight (MW) distribution in which 59% of the product had a number average MW of 19,670 (P.I. = 1.09) and 41% of the product had a number average MW of 4,240 (P.I. - 1.12). End group analysis by ¹⁹F NMR indicated that the overall number average MW was 1,860 and that the polymer chains were terminated with sulfonamide and sulfonate end groups. The lower than expected MW is attributed to partial hydrolysis of the sulfonyl fluoride groups by trace amounts of water in the reaction mixture.

The method shown in the Examples uses relatively inexpensive reagents and provides high yields of imides in a single step, i.e. without the isolation of intermediate reaction products. Furthermore, the method allows unsymmetrical imides (imides having two different fluoroalkyl sulfonyl groups, or fluorosulfonyl groups) to be prepared. The method also allows the preparation of polymeric imides from imides having a polymerizable functional group. The imides prepared using the method of this invention may be used, for example, as electrolytes in fuel cells and batteries and as catalysts for polymerization and esterification.

Claims

What is claimed is:

1. A process for preparing an imide salt selected from bis(fluoroalkylsulfonyl ) imide

and ( fluoroalkylsul fonyl ) (fluorosulfonyl)imide salts comprising the step of contacting a

fluoroalkylsulfonamide with a sulfonyl halide selected from the group consisting of fluoroalkylsulfonyl halides and fluorosulfonyl halides in the presence of a sufficient amount of a non-nucleophilic base at a temperature and for a time sufficient to yield the imide salt.

2. The process of Cl'aim 1 wherein the

fluoroalkylsulfonamide is prepared by contacting a fluoroalkylsulfonyl salt with anhydrous ammonia.

3. The process of Claim 2 wherein the anhydrous ammonia is generated i n si t u by the reaction of an ammonium halide (NH₄'X-) with a non-nucleophilic base.

4. The process of Claim 2 where the temperature is from -25°C to 150"C.

5. The process of Claim 1 characterized by the reaction scheme:

Z-R_f-SO₂NH₂ + Z-R'_f-SO₂-X + 2B ⇒ (Z-R_f-SO₂) (Z-R'_f-SO₂)N- .BH' + BHX,

where each Z is a fluorine atom or a polymerizable organic functional group, R_f and R'_f are fluoroalkylene groups optionally containing catenary oxygen or

nitrogen, X is a halogen atom, and B is a non-nucleophilic base.

6. The process of Claim 5 wherein either or both of R_f and R'_f are perfluoroalkylene groups of the formula -C_mF_2m-, where m is 1 to 12.

7. The process Claim 5 further comprising the step of isolating the bis(fluoroalkylsulfonyl)imide salts of the formula (Z-R_f-SO₂) (Z-R'_f-SO₂)N^-·BH⁺ by evaporating the volatile reaction product components, extracting the remaining reaction product in water and methylene chloride, drying and filtering the methylene chloride phase, and removing residual solvent to yield a concentrated reaction product and acidifying by contacting the concentrated reaction product with a mineral acid to produce a bis(fluoroalkylsulfonyl) imide of the formula (Z-R_f-SO₂) (Z-R'_f-SO₂)N^-.H'.

8. The process of Claim 1 wherein the non-nucleophilic base is an organic base selected from the group of trialkylamines, alkyl aryl amines, and

pyridines.

9. The process of Claim 1 further comprising contacting the bis(fluoroalkylsulfonyl)imide salt with an inorganic base having an alkali metal cation M⁺, volatilizing the non-nucleophilic base, and

isolating the resulting bis(fluoroalkylsulfonyl)imide salt by filtration, evaporating volatile components from the residue, followed by solvent extraction of the filtrate and removal of the solvent.

10. A process for the preparation of

bis(fluoroalkylsulfonyl)imides comprising the step of contacting at least two equivalents of a

fluoroalkylsulfonyl halide with one equivalent of ammonia and at least three equivalents of a non- nucleophilic base at a temperature and for a time sufficient to yield the imide salt.

11. A process for preparing a

bis(fluoroalkylsulfonyl)imide which comprises

contacting a sulfonamidofluoroalkylenesulfonyl halide of the formula X-SO₂-R_f-SO₂NH₂ with a non-nucleophilic base at a temperature and for a time sufficient to produce a polymeric fluoroalkylsulfonimide having the repeat unit

, wherein n is an integer greater than 1 and X is a halogen atom.

12. A process for preparing a polymeric

fluoroalkylsulfonimide characterized by the reaction scheme: o s

than 1 and X is a halogen atom.

13. A process for preparing a polymeric

fluoroalkylsulfonimide characterized by the reaction scheme:

wherein n is an integer greater than 1, R_f is a fluoroalkylene group, B is a non-nucleophilic base and X is a halogen atom.