WO1997047370A1 - Microfabricated filter and method of making same - Google Patents
Microfabricated filter and method of making same Download PDFInfo
- Publication number
- WO1997047370A1 WO1997047370A1 PCT/US1997/010034 US9710034W WO9747370A1 WO 1997047370 A1 WO1997047370 A1 WO 1997047370A1 US 9710034 W US9710034 W US 9710034W WO 9747370 A1 WO9747370 A1 WO 9747370A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- bulk substrate
- openings
- thin film
- containment
- etch
- Prior art date
Abstract
Description
Claims